Patent Grant
10035187
This application is a U.S. National Phase Application under 35 U.S.C. § 371 of International Patent Application No. PCT/JP2014/054876, filed Feb. 27, 2014, and claims the benefit of Japanese Patent Applications No. 2013-040877, filed Mar. 1, 2013 and No. 2014-028874, filed Feb. 18, 2014, all of which are incorporated by reference in their entirety herein. The International Application was published in Japanese on Sep. 4, 2014 as International Publication No. WO/2014/133079 under PCT Article 21(2).
The present invention relates to an aluminum material for sintering (aluminum sintering material, aluminum material to be sintered, aluminum raw sintering material) that is used for producing a porous aluminum sintered compact in which a plurality of aluminum base materials are sintered together, a method for producing the aluminum sintering material, and a method for producing a porous aluminum sintered compact in which the aluminum sintering material is used.
The above-described porous aluminum sintered compact is used for, for example, electrodes and current collectors in a variety of batteries, heat exchanger components, silencing components, filters, impact-absorbing components, and the like.
In the related art, the above-described porous aluminum sintered compact is produced using, for example, the methods disclosed by Patent Documents 1 to 5.
In Patent Document 1, a mixture is formed by mixing aluminum powder, paraffin wax particles, and a binder, and the mixture is shaped into a sheet shape. This mixture is naturally dried. Next, the mixture is immersed in an organic solvent so as to remove the wax particles, subsequently, drying, defatting, and sintering are carried out; and thereby, a porous aluminum sintered compact is produced.
In addition, in Patent Documents 2 to 4, aluminum powder, sintering aid powder containing titanium, a binder, a plasticizer, and an organic solvent are mixed together so as to form a viscous composition, and the viscous composition is shaped and foamed. Then, the viscous composition is heated and sintered in a non-oxidizing atmosphere; and thereby, a porous aluminum sintered compact is produced.
Furthermore, in Patent Document 5, base powder consisting of aluminum, Al alloy powder used to form bridging portions which contains a eutectic element, and the like are mixed together and the mixture is heated and sintered in a hydrogen atmosphere or a mixed atmosphere of hydrogen and nitrogen; and thereby, a porous aluminum sintered compact is produced. Meanwhile, this porous aluminum sintered compact has a structure in which the particles of the base powder consisting of aluminum are connected together through bridging portions having a hypereutectic structure.
Meanwhile, in the porous aluminum sintered compact and the method for producing the porous aluminum sintered compact described in Patent Document 1, there has been a problem in that it is difficult to obtain a porous aluminum sintered compact having high porosity. Furthermore, in the case in which the aluminum base materials are sintered together, the bonding between the aluminum base materials is hindered by oxide films formed on the surfaces of the aluminum base materials and there has been a problem in that it is not possible to obtain a porous aluminum sintered compact having sufficient strength.
In addition, in the porous aluminum sintered compact and the method for producing the porous aluminum sintered compact described in Patent Documents 2 to 4, there has been a problem in that, since the viscous composition is shaped and foamed, it is not possible to efficiently produce a porous aluminum sintered compact. Furthermore, there has been another problem in that, since the viscous composition contains a large amount of a binder, a long period of time is required for a binder removal treatment, the shrinkage ratio of the compact becomes large during sintering, and it is not possible to produce a porous aluminum sintered compact with excellent dimensional accuracy.
Furthermore, in the porous aluminum sintered compact and the method for producing the porous aluminum sintered compact described in Patent Document 5, there is provided a structure in which the particles of the base powder consisting of aluminum are bonded together through the bridging portions having a hypereutectic structure. In this structure, Al alloy powder having a eutectic composition and a low melting point is melted so as to generate a liquid phase and the liquid phase is solidified among the base powder particles; and thereby, the bridging portions are formed. Therefore, it has been difficult to obtain a porous aluminum sintered compact having high porosity.
Patent Document 1: Japanese Unexamined Patent Application, First Publication No. 2009-256788
Patent Document 2: Japanese Unexamined Patent Application, First Publication No. 2010-280951
Patent Document 3: Japanese Unexamined Patent Application, First Publication No. 2011-023430
Patent Document 4: Japanese Unexamined Patent Application, First Publication No. 2011-077269
Patent Document 5: Japanese Unexamined Patent Application, First Publication No. H08-325661
The present invention has been made in consideration of the above-described circumstances and the present invention aims to provide an aluminum sintering material that makes it possible to efficiently produce, at low cost, a high-quality porous aluminum sintered compact having a small shrinkage ratio during sintering, excellent dimensional accuracy, and sufficient strength, a method for producing the aluminum sintering material, and a method for producing a porous aluminum sintered compact in which the aluminum sintering material is used.
In order to solve the above-described problems and achieve the above-described object, the aluminum sintering material of the present invention is an aluminum sintering material that is used for producing a porous aluminum sintered compact in which a plurality of aluminum base materials are sintered together, the aluminum sintering material includes: the aluminum base materials; and a plurality of titanium powder particles fixed to outer surfaces of the aluminum base materials, wherein the titanium powder particles are composed of either one or both of metallic titanium powder particles and hydrogenated titanium powder particles.
In the case in which the aluminum sintering material of the present invention provided with the above-described features is heated at a temperature near the melting point of aluminum during sintering, the aluminum base materials are melted. However, since oxide films are formed on the surfaces of the aluminum base materials, the molten aluminum is held by the oxide films and the shapes of the aluminum base materials are maintained. The oxide films are broken by the reaction with titanium powder particles which are fixed to the surfaces of the aluminum base materials, the molten aluminum inside the aluminum sintering material is ejected outwards, and the ejected molten aluminum reacts with titanium and thus a compound having a higher melting point is generated and solidified. Thereby, a plurality of columnar protrusions protruding outwards are formed on the outer surfaces of the aluminum base materials.
In addition, since the aluminum base materials are bonded together through the columnar protrusions formed on the outer surfaces of the aluminum base materials, it is possible to obtain a porous aluminum sintered compact having high porosity without separately carrying out a foaming step and the like. Therefore, it becomes possible to efficiently produce a porous aluminum sintered compact at low cost.
Furthermore, unlike when a viscous composition is used, a large amount of a binder is not present between the aluminum base materials; and therefore, the shrinkage ratio during sintering is small and it becomes possible to obtain a porous aluminum sintered compact having excellent dimensional accuracy.
In addition, since the oxide films are broken by titanium, the aluminum base materials can be reliably bonded together and it is possible to obtain a porous aluminum sintered compact having sufficient strength.
Furthermore, since the molten aluminum is solidified by titanium, it is possible to prevent the gaps between the aluminum base materials from being filled with the molten aluminum and it is possible to obtain a porous aluminum sintered compact having high porosity.
Here, the amount of the titanium powder particles is preferably set to be in a range of 0.5 mass % to 20 mass %.
In this case, since the amount of the titanium powder particles is set to be in a range of 0.5 mass % or more, the columnar protrusions are sufficiently formed on the outer surfaces of the aluminum base materials, the aluminum base materials can be reliably bonded together, and it is possible to obtain a porous aluminum sintered compact having sufficient strength. In addition, since the amount of the titanium powder particles is set to be in a range of 20 mass % or less, the columnar protrusions are not formed on the outer surfaces of the aluminum base materials more than necessary (a minimal amount of columnar protrusions are formed on the outer surfaces of the aluminum base materials) and it is possible to ensure high porosity.
Furthermore, the aluminum base materials are preferably composed of either one or both of aluminum fibers and aluminum powder.
In the case in which aluminum fibers are used as the aluminum base materials, it is easy to maintain gaps when the aluminum fibers are bonded together through the columnar protrusions, and there is a tendency for the porosity to increase. Therefore, when aluminum fibers and aluminum powder are used as the aluminum base materials and the mixing ratio thereof is adjusted, it becomes possible to control the porosity of the porous aluminum sintered compact.
The method for producing an aluminum sintering material of the present invention is a method for producing the above-described aluminum sintering material, the method includes: a mixing step of mixing the aluminum base materials and the titanium powder with a binder; and a drying step of drying a mixture obtained in the mixing step.
According to the method for producing an aluminum sintering material having the above-described features, since the mixing step of mixing the aluminum base materials and the titanium powder with a binder and the drying step of drying a mixture obtained in the mixing step are included, the titanium powder particles are dispersed and fixed to the outer surfaces of the aluminum base materials and the above-described aluminum sintering material is produced.
Here, the drying step is preferably either one of low-temperature drying conducted at a temperature of 40° C. or lower or reduced-pressure drying conducted at a pressure of 1.33 Pa or less.
In this case, in the drying step, it is possible to suppress (limit) the forming of thick oxide films on the surfaces of the aluminum base materials, and the sinterability of the aluminum sintering material can be improved.
In addition, the method for producing a porous aluminum sintered compact of the present invention is a method for producing a porous aluminum sintered compact in which the above-described aluminum sintering material is used, the method includes: a material distributing step of distributing the aluminum sintering material to a holding body; and a sintering step of heating and sintering the aluminum sintering material held by the holding body.
According to the method for producing a porous aluminum sintered compact having the above-described features, since the above-described aluminum sintering material is used, the oxide films on the aluminum base materials are broken by the titanium powder particles fixed to the outer surfaces of the aluminum base materials during sintering and the molten aluminum inside the aluminum base materials is ejected outwards. The molten aluminum reacts with titanium and thus a compound having a higher melting point is generated and solidified. Thereby, a plurality of columnar protrusions protruding outwards are formed on the outer surfaces of the aluminum base materials.
In addition, a plurality of the aluminum base materials are bonded together through the columnar protrusions and it is possible to produce a porous aluminum sintered compact having high porosity and sufficient strength.
According to the present invention, it is possible to provide an aluminum sintering material that makes it possible to obtain a high-quality porous aluminum sintered compact, a method for producing the aluminum sintering material, and a method for producing a porous aluminum sintered compact in which the aluminum sintering material is used. By using the aluminum sintering material of the present invention, it is possible to efficiently produce a porous aluminum sintered compact at low cost, and the produced porous aluminum sintered compact has a small shrinkage ratio during sintering, excellent dimensional accuracy, and sufficient strength.
Hereinafter, an aluminum sintering material, a method for producing the aluminum sintering material, and a method for producing a porous aluminum sintered compact in which the aluminum sintering material is used, which are embodiments of the present invention, will be described.
First, a porous aluminum sintered compact 10 produced using the aluminum sintering material according to the present embodiment will be described.
As shown in
In the present embodiment, as shown in
In addition, a plurality of columnar protrusions 12 protruding outwards are formed on the outer surfaces of the aluminum base materials 11 (the aluminum fibers 11a and the aluminum powder 11b), and a structure is provided in which a plurality of the aluminum base materials 11 and 11 (the aluminum fibers 11a and the aluminum powder 11b) are bonded together through the columnar protrusions 12. As shown in
As shown in
Next, an aluminum sintering material 20 according to the present embodiment will be described.
As shown in
In the aluminum sintering material 20, the amount of the titanium powder particles 22 is set to be in a range of 0.5 mass % to 20 mass %, preferably in a range of 0.5 mass % to 15 mass %, and still more preferably in a range of 1.0 mass % to 10 mass %. In the present embodiment, the amount thereof is set to 5 mass %.
In addition, the particle diameters of the titanium powder particles 22 are set to be in a range of 1 μm to 50 μm and preferably set to be in a range of 5 μm to 30 μm. In addition, since it is possible to make the particle diameters of the hydrogenated titanium powder particles smaller than those of the metallic titanium powder particles, the hydrogenated titanium powder particles are preferably used in the case in which it is necessary to decrease the particle diameters of the titanium powder particles 22 that are fixed to the outer surfaces of the aluminum base materials 11.
Furthermore, the intervals between the titanium powder particles 22 and 22 fixed to the outer surface of the aluminum base material 11 are preferably set to be in a range of 5 μm to 100 μm and more preferably set to be in a range of 5.0 μm to 70 μm.
As the aluminum base materials 11, as described above, the aluminum fibers 11a and the aluminum powder 11b are used. As the aluminum powder 11b, atomized powder can be used.
The fiber diameters of the aluminum fibers 11a are set to be in a range of 40 μm to 300 μm and preferably set to be in a range of 50 μm to 200 μm. In addition, the fiber lengths of the aluminum fibers 11a are set to be in a range of 0.2 mm to 20 mm and preferably set to be in a range of 1 mm to 10 mm.
In addition, the particle diameters of the aluminum powder 11b are set to be in a range of 20 μm to 300 μm and preferably set to be in a range of 20 μm to 100 μm.
Furthermore, the aluminum base materials 11 are preferably made of pure aluminum having a purity of 99.5 mass % or more and, furthermore, the aluminum base materials 11 are preferably made of 4N aluminum having a purity of 99.99 mass % or more.
In addition, it becomes possible to adjust the porosity by adjusting the mixing ratio between the aluminum fibers 11a and the aluminum powder 11b. That is, when the ratio of the aluminum fibers 11a is increased, it becomes possible to increase the porosity of the porous aluminum sintered compact 10. Therefore, as the aluminum base materials 11, the aluminum fibers 11a are preferably used and, in the case in which the aluminum powder 11b is mixed, the ratio of the aluminum powder 11b is preferably set to be in a range of 10 mass % or less and more preferably set to be in a range of 1.0 mass % to 5.0 mass %.
Next, a method for producing an aluminum sintering material and a method for producing a porous aluminum sintered compact, which are the present embodiments, will be described with reference to the flowchart of
First, as shown in
The aluminum base materials 11 and titanium powder are mixed together at normal temperature (Mixing Step S01). At this time, a binder solution is sprayed. As the binder, a binder that is combusted and decomposed when heated at 500° C. in air atmosphere is preferable and, specifically, an acryl-based resin or a cellulose-based macromolecular body is preferably used. In addition, as a solvent for the binder, a variety of solvents such as water-based solvents, alcohol-based solvents, and organic solvents can be used.
In the Mixing Step S01, the aluminum base materials 11 and the titanium powder are mixed while being made to flow using a variety of mixers such as an automatic mortar, a pan-type tumbling granulator, a shaker mixer, a pot mill, a high-speed mixer, and a V-type mixer.
Next, a mixture obtained in the Mixing Step S01 is dried (Drying Step S02). In the Drying Step S02, the mixture is subjected to drying at a low temperature of 40° C. or lower or drying at a reduced pressure of 1.33 Pa or less (10−2 Torr or less) so as to prevent thick oxide films from being formed on the surfaces of the aluminum base materials 11. The temperature of the low-temperature drying is preferably in a range of 25° C. to 30° C. and the pressure of the reduced-pressure drying is preferably in a range of 0.5 Pa to 1.0 Pa.
Through the Mixing Step S01 and the Drying Step S02, the titanium powder particles 22 are dispersed and fixed to the outer surfaces of the aluminum base materials 11 as shown in
Next, the porous aluminum sintered compact 10 is produced using the aluminum sintering material 20 obtained in the above-described manner.
In the present embodiment, for example, a long sheet-shaped porous aluminum sintered compact 10 having a width of 300 mm, a thickness in a range of 1 mm to 5 mm, and a length of 20 m is produced using a continuous sintering device 30 shown in
The continuous sintering device 30 includes: a powder distributing apparatus 31 that uniformly distributes the aluminum sintering material 20; a carbon sheet 32 that holds the aluminum sintering material 20 supplied from the powder distributing apparatus 31; a transportation roller 33 that drives the carbon sheet 32; a defatting furnace 34 that heats the aluminum sintering material 20 that is transported together with the carbon sheet 32 so as to remove the binder; and a sintering furnace 35 that heats and sinters the aluminum sintering material 20 from which the binder has been removed.
First, the aluminum sintering material 20 is distributed from the powder distributing apparatus 31 toward the carbon sheet 32 (Material Distributing Step S03).
The aluminum sintering material 20 distributed on the carbon sheet 32 spreads in the width direction of the carbon sheet 32 so as to have a uniform thickness and is shaped into a sheet shape while moving in the travelling direction F. At this time, since no load is applied, gaps are formed between the aluminum base materials 11 and 11 in the aluminum sintering material 20.
Next, the aluminum sintering material 20 that is formed into a sheet shape on the carbon sheet 32 is loaded into the defatting furnace 34 together with the carbon sheet 32 and is heated at a predetermined temperature; and thereby, the binder is removed (Binder Removal Step S04).
In the Binder Removal Step S04, the aluminum sintering material is held in air atmosphere at a temperature in a range of 350° C. to 500° C. for 0.5 minutes to 30 minutes; and thereby, the binder in the aluminum sintering material 20 is removed. The heating temperature is preferably in a range of 350° C. to 450° C. and the holding time is preferably in a range of 10 minutes to 15 minutes. In the present embodiment, since the binder is used in order to fix the titanium powder particles 22 to the outer surfaces of the aluminum base materials 11 as described above, the amount of the binder is much smaller than that in a viscous composition and it is possible to sufficiently remove the binder within a short period of time.
Next, the aluminum sintering material 20 from which the binder has been removed is loaded into a sintering furnace 35 together with the carbon sheet 32 and is heated at a predetermined temperature so as to be sintered (Sintering Step S05).
In the Sintering Step S05, the aluminum sintering material is held in an inert gas atmosphere at a temperature in a range of 655° C. to 665° C. for 0.5 minutes to 60 minutes. The heating temperature is preferably in a range of 657° C. to 662° C. and the holding time is preferably set to be in a range of 1 minute to 20 minutes.
By using an inert gas atmosphere such as Ar gas and the like as the sintering atmosphere in the Sintering Step S05, it is possible to sufficiently decrease the dew point. A hydrogen atmosphere or a mixed atmosphere of hydrogen and nitrogen is not preferable since it is difficult to decrease the dew point. In addition, since nitrogen reacts with Ti so as to form TiN, the sintering acceleration effect of Ti is lost, which is not preferable.
Therefore, in the present embodiment, as the atmosphere gas, an Ar gas having a dew point of −50° C. or lower is used. The dew point of the atmosphere gas is more preferably set to be in a range of −65° C. or lower.
In the Sintering Step S05, since the aluminum sintering material is heated at a temperature in a range of 655° C. to 665° C., which is approximate to the melting point of aluminum, the aluminum base materials 11 in the aluminum sintering material 20 are melted. Since oxide films are formed on the surfaces of the aluminum base materials 11, the molten aluminum is held by the oxide films and the shapes of the aluminum base materials 11 are maintained.
In addition, when the aluminum sintering material is heated at a temperature in a range of 655° C. to 665° C., the oxide films are broken by the reaction with the titanium powder particles 22 which are fixed in the outer surfaces of the aluminum base materials 11 and the molten aluminum inside the aluminum sintering material is ejected outwards. The ejected molten aluminum reacts with titanium and thus a compound having a higher melting point is generated and solidified. Thereby, as shown in
In the case in which hydrogenated titanium is used as the titanium powder particles 22, the hydrogenated titanium is decomposed at a temperature within or in the vicinity of 300° C. to 400° C. and the generated titanium reacts with the oxide films on the surfaces of the aluminum base materials 11.
At this time, adjacent aluminum base materials 11 and 11 are bonded together by being integrated together in a molten state or solid-phase sintering through the columnar protrusions 12 on both of the aluminum base materials and, as shown in
According to the aluminum sintering material 20, which is the present embodiment having the above-described features, when the aluminum sintering material is heated at a temperature of 655° C. to 665° C. which is near the melting point of aluminum in the Sintering Step S05, the oxide films formed on the surfaces of the aluminum base materials 11 are broken at the portions to which the titanium powder particles 22 are fixed and molten aluminum is ejected. When the ejected molten aluminum reacts with titanium and thus a compound having a higher melting point is generated and solidified, a plurality of columnar protrusions 12 protruding outwards are formed on the outer surfaces of the aluminum base materials 11. At this time, adjacent aluminum base materials 11 and 11 are bonded together by being integrated together in a molten state or solid-phase sintering through the columnar protrusions 12 on both of the aluminum base materials, and thus it becomes possible to produce the porous aluminum sintered compact 10 in which the a plurality of aluminum base materials 11 and 11 are bonded together through the columnar protrusions 12 as shown in
As described above, since a structure is provided in which the aluminum base materials 11 and 11 are bonded together through the columnar protrusions 12 formed on the outer surfaces of the aluminum base materials 11, it is possible to obtain a porous aluminum sintered compact 10 having high porosity without separately carrying out a foaming step and the like. Therefore, it becomes possible to efficiently produce the porous aluminum sintered compact 10 according to the present embodiment at low cost.
Furthermore, unlike the case in which a viscous composition is used, a large amount of a binder is not present between the aluminum base materials 11 and 11, and thus it becomes possible to obtain a porous aluminum sintered compact 10 having a small shrinkage ratio during sintering and excellent dimensional accuracy.
In addition, since the oxide films are broken by titanium, the aluminum base materials 11 and 11 can be reliably bonded together and it is possible to obtain the porous aluminum sintered compact 10 having sufficient strength.
Furthermore, since the molten aluminum is solidified by titanium, it is possible to prevent the gaps between the aluminum base materials 11 and 11 from being filled with the molten aluminum, and it is possible to obtain the porous aluminum sintered compact 10 having high porosity.
In addition, in the aluminum sintering material 20 of the present embodiment, since the amount of the titanium powder particles 22 is set to be in a range of 0.5 mass % to 20 mass %, it is possible to form the columnar protrusions 12 at appropriate intervals on the outer surfaces of the aluminum base materials 11, and it is possible to obtain a porous aluminum sintered compact 10 having sufficient strength and high porosity.
In addition, in the present embodiment, since the aluminum fibers 11a and the aluminum powder 11b are used as the aluminum base materials 11, it becomes possible to control the porosity of the porous aluminum sintered compact 10 by adjusting the mixing ratio thereof.
In addition, in the porous aluminum sintered compact 10 of the present embodiment, since the porosity is set to be in a range of 30% to 90%, it becomes possible to provide a porous aluminum sintered compact 10 having the optimal porosity for a particular use.
In addition, in the present embodiment, since the intervals between the titanium powder particles 22 and 22 fixed to the outer surface of the aluminum base material 11 are set to be in a range of 5 μm to 100 μm, the intervals between the columnar protrusions 12 are optimized, and it is possible to obtain a porous aluminum sintered compact 10 having sufficient strength and high porosity.
Furthermore, in the present embodiment, since the fiber diameters of the aluminum fibers 11a, which are the aluminum base materials 11, are set to be in a range of 40 μm to 300 μm, the particle diameters of the aluminum powder 11b are set to be in a range of 20 μm to 300 μm, and the particle diameters of the titanium powder particles 22 are set to be in a range of 1 μm to 50 μm, it is possible to reliably disperse and fix the titanium powder particles 22 to the outer surfaces of the aluminum base materials 11 (the aluminum fibers 11a and the aluminum powder 11b).
Furthermore, according to the method for producing the aluminum sintering material 20 which is the present invention, since the Mixing Step S01 of mixing the aluminum base materials 11 and the titanium powder with a binder through spraying and the Drying Step S02 of drying a mixture obtained in the Mixing Step S01 are included, the titanium powder particles 22 are dispersed and fixed to the outer surfaces of the aluminum base materials 11 and the above-described aluminum sintering material 20 can be produced.
Here, since low-temperature drying which is conducted at a temperature of 40° C. or lower or reduced-pressure drying which is conducted at a pressure of 1.33 Pa or less is applied in the Drying Step S02, it is possible to suppress (limit) the forming of thick oxide films on the surfaces of the aluminum base materials 11 in the Drying Step S02, and the sinterability of the aluminum sintering material 20 can be improved.
In addition, according to the method for producing a porous aluminum sintered compact which is the present embodiment, since the above-described aluminum sintering material 20 is used, a plurality of columnar protrusions 12 protruding outwards are formed on the outer surfaces of the aluminum base materials 11 and a plurality of the aluminum base materials 11 and 11 are bonded together through the columnar protrusions 12. Therefore, it is possible to produce a porous aluminum sintered compact 10 having high porosity and sufficient strength.
In addition, in the present embodiment, since the continuous sintering device 30 shown in
Furthermore, since the carbon sheet 32 is used as the holding body that holds the aluminum sintering material 20, it is possible to favorably remove the porous aluminum sintered compact 10 from the carbon sheet 32 after sintering.
In addition, in the porous aluminum sintered compact 10 produced using the aluminum sintering material 20 according to the present embodiment, since the Ti—Al-based compound 16 is present in the bonding portions 15 between the aluminum base materials 11 and 11, the oxide films formed on the surfaces of the aluminum base materials 11 are broken by the Ti—Al-based compound 16 and the aluminum base materials 11 and 11 are favorably bonded together. Therefore, it is possible to obtain a porous aluminum sintered compact 10 having sufficient strength.
Particularly, in the present embodiment, since Al3Ti is present as the Ti—Al-based compound 16 in the bonding portions 15 between the aluminum base materials 11 and 11, the oxide films formed on the surfaces of the aluminum base materials 11 are reliably broken, the aluminum base materials 11 and 11 are favorably bonded together, and it is possible to ensure the strength of the porous aluminum sintered compact 10.
In addition, in the present embodiment, since the aluminum base materials 11 are made of pure aluminum having a purity of 99.5 mass % or more and, furthermore, the aluminum base materials 11 are made of 4N aluminum having a purity of 99.99 mass % or more, it is possible to improve the corrosion resistance of the porous aluminum sintered compact 10.
Furthermore, in the present embodiment, since the aluminum fibers 11a and the aluminum powder 11b are used as the aluminum base materials 11 and the mixing ratio of the aluminum powder lib is set to be in a range of 10 mass % or less, it is possible to obtain a porous aluminum sintered compact 10 having high porosity.
Thus far, the embodiment of the present invention has been described, but the present invention is not limited thereto and can be appropriately modified within the scope of the technical features of the invention.
For example, the method in which the porous aluminum sintered compacts are continuously produced using the continuous sintering device shown in
In addition, in the present embodiment, the sheet-shaped porous aluminum sintered compact has been described, but the shape is not limited thereto and the porous aluminum sintered compact may be, for example, a bulk-shaped porous aluminum sintered compact produced through production steps shown in
As shown in
A porous aluminum sintered compact can be efficiently produced at low cost using the aluminum sintering material of the present invention and the produced porous aluminum sintered compact has a small shrinkage ratio during sintering, excellent dimensional accuracy, and sufficient strength. Therefore, the porous aluminum material of the present invention can be preferably used in production steps of porous aluminum sintered compacts that are applied to electrodes and current collectors in a variety of batteries, heat exchanger components, silencing components, filters, impact-absorbing components, and the like.
10, 110 POROUS ALUMINUM SINTERED COMPACT
11 ALUMINUM BASE MATERIAL
11
a ALUMINUM FIBER
11
b ALUMINUM POWDER
12 COLUMNAR PROTRUSION
15 BONDING PORTION
16 Ti—Al-BASED COMPOUND
20 ALUMINUM SINTERING MATERIAL
22 TITANIUM POWDER PARTICLE
32 CARBON SHEET (HOLDING BODY)
132 CARBON CONTAINER (HOLDING BODY)
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013-040877 | Mar 2013 | JP | national |
| 2014-028874 | Feb 2014 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2014/054876 | 2/27/2014 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2014/133079 | 9/4/2014 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20030200837 | Matsuura et al. | Oct 2003 | A1 |
| 20110151181 | Liu | Jun 2011 | A1 |
| 20120094142 | Hoshino et al. | Apr 2012 | A1 |
| 20120135142 | Yang et al. | May 2012 | A1 |
| Number | Date | Country |
|---|---|---|
| 1762909 | Apr 2006 | CN |
| 101985084 | Mar 2011 | CN |
| 102305564 | Jan 2012 | CN |
| 2939762 | Nov 2015 | EP |
| 2962791 | Jan 2016 | EP |
| 61084351 | Apr 1986 | JP |
| 08-325661 | Dec 1996 | JP |
| 2009-256788 | Nov 2009 | JP |
| 2010-280951 | Dec 2010 | JP |
| 2011-023430 | Feb 2011 | JP |
| 2011-077269 | Apr 2011 | JP |
| 2011-175934 | Sep 2011 | JP |
| 2011-214049 | Oct 2011 | JP |
| 2012-507464 | Mar 2012 | JP |
| 2012-195182 | Oct 2012 | JP |
| WO-2010051292 | May 2010 | WO |
| WO-2010116679 | Oct 2010 | WO |
| Entry |
|---|
| International Search Report dated Apr. 1, 2014 for the corresponding PCT Application No. PCT/JP2014/054876. |
| Office Action dated May 3, 2016 for the corresponding Chinese Patent Application No. 201480004359.4. |
| Office Action dated Dec. 30, 2016 for the corresponding Chinese Patent Application No. 201480004359.4. |
| Extended European Search Report dated Jul. 19, 2016 for the corresponding European Patent Application No. 14756420.7. |
| Number | Date | Country | |
|---|---|---|---|
| 20160008884 A1 | Jan 2016 | US |