Aluminum welding process and mixture of reactants for use in such process

Abstract

The invention provides a method and means of producing weld metal for use in joining two or more aluminum containing pieces. The method includes the steps of providing a novel mixture of reactants comprising silicon, a reducing agent, a metallic compound which is exothermically reduced by the reducing agent, and a filler metal that does not react with the metallic compound. The mixture of reactants is then exothermically reacted so as to form the weld metal for joining the metallic pieces. At least about 90 percent by weight of the weld metal is produced by the silicon and the filler metal and at least about 90 percent by weight of the weld metal has a chemical composition substantially similar to that of at least one of the metallic pieces being joined.

Description

TECHNICAL DISCLOSURE

This invention relates generally to the art of welding. More particularly, the invention concerns a unique welding process and a novel mixture of reactants for use in such process. Specifically, the invention concerns a novel application of the thermite reaction to the welding of aluminum.

BACKGROUND OF INVENTION

The thermite reaction has been utilized for a long period of time in order to provide weldments normally associated with the railroad industry and in electric power transmission. The thermite reaction is comprised of a reaction between aluminum (Al) and a metal oxide wherein the metal oxide is reduced providing a filler metal, i.e., the source of the filler metal is the oxide on reduction. The "Goldschmidt" reaction is the basis of the application of the process described in U.S. Pat. No. 2,229,045 to Charles A. Cadwell. This reaction is as follows: ##STR1##

The "Goldschmidt" reaction has been successfully utilized over the years to weld or join metals such as iron (Fe) and copper (Cu). However, the process is not particularly well adapted for use in joining metals such as aluminum (Al) wherein the use of a copper (Cu) or iron (Fe) filler metal is generally unacceptable.

U.S. Pat. No. 3,020,610 to Rejdak discloses a method of welding aluminum (Al) and other metals, and provides a listing of various reactions which can be utilized to produce reaction products which may be utilized to provide a weldment. Unfortunately, in the method disclosed by Rejdak the weld which is formed is not suitable for some applications. More particularly, the weld metal formed by the Rejdak method is not chemically pure enough for some applications. For example, a weldment produced by the Rejdak method in some environments may be susceptible to a high level of corrosion due to the presence of impurities or unwanted elements in the resultant weldment.

U.S. Pat. No. 2,569,956 to Schiltknecht discloses a process wherein a thermite reaction is utilized to join together a pair of non-ferrous metal pieces by melting a sleeve about the metal pieces. This process is usually referred to as the "Alusuisse Process" referring to a welding system produced by Swiss Aluminum Ltd. of Zurich. Unfortunately, the "Alusuisse Process" is an indirect welding process (i.e., the heat generated by the thermite reaction does not produce a weld filler metal by chemical reaction) and it is not suitable for use in some joining applications.

SUMMARY OF THE INVENTION

The present invention provides a new and improved method and means for producing molten weld metal for use in welding or joining two or more metallic pieces or sections which affords various distinct advantages over the prior art. More particularly, the invention provides a direct thermite welding process that is capable of producing weld metal that is substantially similar in chemical composition to the metallic pieces being joined and is thus capable of being used to join non-ferrous metals such as aluminum. Additionally, the process provides for the use of a filler metal in the mixture of reactants utilized to produce the molten weld metal having a chemical composition substantially similar to that of the metallic pieces being joined. This filler metal does not take part in the thermite reaction and it serves to produce the resultant weld metal. The invention thus allows for the use of coarser filler metals (which are generally less expensive than the finer metals required in prior art processes) and results in a slower burning reaction that evolves fewer gases.

In general the process includes the steps of providing a mixture of reactants comprising a reducing agent, a metallic compound which is exothermically reduced by the reducing agent, and a filler metal that does not react with the metallic compound. Upon exothermically reacting the reducing agent and the metallic compound heat, a metal oxide slag, evolving gases and molten weld metal are produced.

As used herein this specification and the claims below the term "weld metal" means the metal which is the resultant product of the thermite reaction exclusive of any slags or evolving gases produced by the reaction. The weld metal serves to weld or hold together the metal pieces being joined. The filler metal produces at least about 90 percent by weight of the resultant weld metal. Preferably, at least about 95 percent by weight, and more preferably at least about 97 percent by weight of the resultant weld metal is produced by the filler metal.

At least about 90 percent by weight of the weld metal has a chemical composition substantially similar to that of at least one of the metallic pieces being joined. Preferably, at least about 95 percent by weight, and more preferably at least about 97 percent by weight of the weld metal has a chemical composition substantially similar to that of at least about one of the metallic pieces being joined.

The process is particularly well suited for use with joining two or more pieces of non-ferrous metal such as aluminum (Al) or aluminum alloys. When aluminum (Al) or aluminum alloy pieces are being joined the mixture of reactants may comprise from about 20 percent to about 50 percent by weight of a metal sulfate such as, for example, magnesium sulfate (MgSO.sub.4), barium sulfate (BaSO.sub.4) or calcium sulfate (CaSO.sub.4), from about 40 percent to about 70 percent by weight aluminum (Al), from about 0.1 percent by weight to about 45 percent by weight silicon (Si), up to about 10 percent by weight of a chloride salt such as, for example, sodium chloride (NaCl) or calcium chloride (CaCl) and up to 10 percent by weight of a suitable flux such as, for example, calcium fluoride (CaF.sub.2). Preferably, the mixture of reactants comprises from about 30 percent by weight to about 45 percent by weight metal sulfate, from about 42 percent by weight to about 60 percent by weight aluminum (Al), from about 0.2 percent by weight to about 9 percent by weight silicon (Si), from about 2 percent by weight to about 7 percent by weight of a chloride salt and from about 2 percent by weight to about 10 percent by weight flux. More preferably, the mixture of reactants comprises from about 35 percent by weight to about 42 percent by weight metal sulfate, from about 45 percent by weight to about 52 percent by weight aluminum (Al), from about 0.2 percent by weight to about 9 percent by weight silicon (Si), from about 4 percent by weight to about 5 percent by weight of a chloride salt and from about 5 percent by weight to about 7 percent by weight flux.

The foregoing and other features of the invention are hereinafter more fully described and particularly pointed out in the claims. The following descriptions setting forth in detail certain illustrative embodiments of the invention, these being indicative, however, of but a few of the various ways in which the principles of the invention may be employed.

BRIEF DESCRIPTION OF DRAWING

FIG. 1 is a cross-sectional view of a welding apparatus suitable for use in the present invention.

DETAILED DESCRIPTION

In accordance with this invention it has been found that a plurality of filler metals may be utilized via the thermite reaction to produce weldments but without having the filler metals actually enter into the reaction. Thus, in accordance with this invention, a filler metal for use in a weldment is provided into a mixture with a metallic compound which is exothermically reduced by the reducing agent to produce heat to melt the filler metal which then flows from the reactant and product mixture as weld metal to provide a weldment. Other product components are left behind in a slag with reaction gases released. The process is generally summarized as follows: ##STR2##

In accordance with this invention it has been found with the above reaction that the reducing agent may be selected from the group consisting of aluminum (Al), magnesium (Mg), zirconium (Zr) and equivalent metals which exhibit compounds which have a high thermodynamic heat of formation with respect to the reaction product between the metal and the metallic compound to be reduced. For example, aluminum (Al) can reduce a metal oxide or sulfate forming aluminum oxide (Al.sub.2 O.sub.3) which exhibits a heat of formation of 399 kcal/mole at 25.degree. Celsius. Such a reaction is highly exothermic providing sufficient heat to raise the temperature of the filler metal beyond its melting point so that the molten filler metal can be directed into a weld cavity, i.e., the mold, to affect the weld and join two or more metallic pieces or sections.

The metallic compound may generally be selected from the group consisting of magnesium sulfate (MgSO.sub.4), calcium sulfate (CaSO.sub.4), and barium sulfate (BaSO.sub.4), fluoride compounds, and equivalent materials which upon reduction contribute one or more elements to exothermically form a compound with the reducing agent. Preferably, the metallic compound is utilized in an anhydrous form and preferably all of the reactants are protected from moisture prior to use. Moisture contamination may suppress the exothermic reaction.

The reaction between aluminum (Al) and metal compounds containing oxygen, such as oxides and sulfates, is particularly useful because of the high amount of heat liberated when aluminum oxide (Al.sub.2 O.sub.3) is formed. However, other exothermic reactions may be employed such as the one between magnesium (Mg) and polytetrafluoroethylene (C.sub.2 F.sub.4).sub.n, forming magnesium fluoride (MgF.sub.2) and providing heat to melt the filler metal. Magnesium fluoride (MgF.sub.2) exhibits a heat of formation of 264 kcal/mole at 25.degree. Celsius. The metallic compounds used in this invention generally do not, on reduction via reaction with the reducing agent, provide for a metallic phase which serves as the filler metal or becomes a part of the resultant weld metal. In fact, the metallic compounds of the present invention upon reduction via reaction with the reducing agent usually form minerals associated with the slag or oxide residual. This is in contrast to the method disclosed in Cadwell U.S. Pat. No. 2,229,045 wherein the metallic compound (i.e., iron oxide (Fe.sub.2 O.sub.3) provides a metallic phase on reduction to become the filler metal or resultant weld metal (i.e., iron (Fe)).

The filler metal of the present invention may be any metal which is desired to be utilized in a welding process. Because of their use in electric transmission applications, aluminum (Al) and copper (Cu) are particularly useful as filler metals to weld aluminum (Al) or copper (Cu) articles respectively. In the case of aluminum (Al) welds wherein one or more sections of aluminum (Al) are being joined, the filler metal and the reducing agent are both aluminum (Al). Whereas, in the case of copper (Cu) welds where one or more sections of copper (Cu) are being joined, mixtures or alloys of copper (Cu) and aluminum (Al) can be used to provide for the reduction process and to provide for the filler metal. Additional filler metals may be selected from the group consisting of iron (Fe), iron alloys, non-ferrous metals and alloys, solders and brazing filler metals or others where the heat from the exothermic reaction is sufficient to raise the temperature of the filler metal beyond its melting point and to provide additional superheat to the filler metal such that it is useful in producing a weld metal for joining metallic pieces.

The mixture of reactants may additionally include a flux to lower the melting point of the mixture and products. Commonly utilized fluxes such as calcium fluoride (CaF.sub.2), magnesium fluoride (MgF.sub.2), cryolite (Na.sub.3 AlF.sub.6), and other substances such as alkali compounds, particularly alkali silicates and fluorosilicates, can be used to lower the fusion point and increase the fluidity of the reaction products (i.e., "slag") such that the molten filler metal can readily be separated from the slag and flow into the mold cavity.

An unexpected advantage has been found with regard to the particle sizes of reactants utilized in the process of this invention. In the prior art of thermite welding, the materials utilize aluminum (Al) at a particle size smaller than 325 Mesh (i.e., less than 44 micrometers in diameter). The metal oxide is normally utilized at a larger particle size than 325 Mesh. In accordance with this invention, when the reducing agent aluminum (Al) is employed it may be utilized at a particle size of greater than 325 Mesh for greater than 90% of the aluminum (Al) by weight. This has two unexpected advantages. This brings about a reaction rate which exhibits a uniformly slow burning rate with low gaseous emissions. A second advantage is that the coarser aluminum (Al) is less expensive than the finer materials normally required.

An additional unexpected advantage of this invention is that the filler metals can produce weld metal comprising 97% or greater of the desired element or alloy. There is believed to be currently no direct thermite process in existence for welding aluminum (Al) conductors providing for this kind of purity in the weld metal. Since much of the world's power transmission is accomplished with aluminum (Al) conductors, this means that the process of this invention is a more effective and efficient substitute for mechanical connectors which must be maintained or eliminates the requirement for expensive TIG (gas tungsten-arc welding) or MIG (metal inert-gas welding) welding.

The process of this invention also helps to eliminate segregation in the weld metal caused by limited solubility of constituents such as aluminum (Al) and tin (Sn) as found in the prior art thermite process for welding aluminum (Al) conductors. The process also helps to eliminate the presence of elements causing galvanic corrosion thus providing outdoor connections for power transmission and grounding. The process also eliminates additional steps or equipment as required with the "Alusuisse Process" or furnaces used in foundry welding operations.

The process of this invention also allows for the use of permanent steel molds when welding aluminum (Al) or its alloys. The reactant mixtures of this invention require high temperatures for initiation of the reaction thus helping to provide for safety in use. The reactions are slow and steady thus helping to prevent violence and the slag materials should not present a disposal problem.

The process of this invention is particularly well adapted for use with the welding apparatus formed from two graphite blocks or various other materials as shown in U.S. Pat. No. 3,020,610 to Rejdak. The entire disclosure of the Rejdak U.S. Pat. No. 3,020,610 is incorporated herein by reference. FIG. 1 is an example of a welding apparatus 1 which may be utilized with the present invention. Welding apparatus 1 comprises a pair of blocks 2 which are hollowed out to provide an upper crucible portion 3 and a mold cavity portion 4. Blocks 2 are releasably connected or clamped using any one of a variety of means. Metallic pieces, or more particularly, cable ends 5 and 6 are clamped in the mold cavity portion 4 with their opposed ends located substantially vertically below sprue 7 which is closed by means of a small metal disc 8. The mixture of reactants 9 is then placed in the crucible portion 3 and a starting material 10 may then be placed on top of the mixture of reactants 9. The starting material 10 may then be ignited with a flint gun, which in turn ignites the exothermically reacting mixture of reactants 9 to produce molten metal which melts through disc 8 and drops into mold cavity portion 4 thereby contacting and joining the ends of the cables 5 and 6. It will be appreciated that in addition to a flint gun alternative ignition means may be employed such as an electrical ignition system as disclosed in Amos et al. U.S. Pat. No. 4,885,452. The disclosure of the Amos et al. U.S. Pat. No. 4,885,452 is incorporated herein by reference.

Having generally described the process of this invention, the following specific Examples are given:

EXAMPLE 1

A thermite reaction per the teachings of this disclosure was conducted as follows in a ceramic crucible set over a steel mold which holds cables to be joined and provides for a casting mold at the cable junction using the following thermite mixture:

______________________________________Constituent Weight Percent______________________________________Magnesium Sulfate (MgSO.sub.4) 38.6Aluminum (Al) Powder 57.6Calcium Fluoride (CaF.sub.2) 3.8______________________________________Particle Size Distributions of Materials Used in ExamplesMAGNESIUM SULFATE (MgSO.sub.4)>44 micron - 100%ALUMINUM (Al) POWDER+ 20 Mesh >840 microns 100% (by weight)-20 + 40 Mesh 420-840 microns 5% Max-40 + 50 Mesh 300-420 microns 1-10%-50 + 80 Mesh 180-300 microns 15-30%-80 + 140 Mesh 100-180 microns 35-50%-140 + 325 Mesh 44-180 microns 25-45%-325 Mesh <44 microns 5 MaxCALCIUM FLUORIDE (CaF.sub.2)+ 50 Mesh >300 microns 2% Max (by weight)-50 + 100 Mesh 150-300 microns 0-10%-100 + 140 Mesh 100-150 microns 5-20%-140 + 200 Mesh 74-100 microns 10-25%-200 + 325 Mesh 44-74 microns 20-40%-325 Mesh <44 microns Balance______________________________________

A weld metal nugget is subjected to chemical analysis and the following welding metal composition was found (weight percent):

______________________________________Aluminum (Al) Powder 97.2Silicon (Si) 0.1Magnesium (Mg) 0.2Sulfur (S) 1.7______________________________________

The weldments made by this process were further tested by sequentially dipping them in simulated seawater (3.5% sodium chloride (NaCl) in distilled water) followed by drying. In a one month process, welds made by this method do not exhibit signs of corrosion whereas those made per existing technology and disclosed in Rejdak U.S. Pat. No. 3,020,610 and containing tin (Sn) and copper (Cu) all exhibit signs of corrosion.

EXAMPLE 2

Two pieces of 250 MCM aluminum (Al) cable (19 strand--diameter 0.575 in. were welded together using the process of Example 1.

EXAMPLE 3

Two pieces of 2/0 aluminum (Al) cable (7 strand--diameter 0.419 inches) were joined by the process of Example 1 obtaining a resistance of 100 micro-ohms (note that total resistance is greatly affected by the measuring technique with stranded cable and, therefore, comparative values are very important when a common technique has been used.)

EXAMPLE 4

Thermite reactions per the teachings of this disclosure were conducted in a graphite crucible and mold using the following mixture to affect welds in 2/0 aluminum (Al) cable segments;

______________________________________Constituent Weight Percent______________________________________Calcium Sulfate (CaSO.sub.4) 35.67Aluminum (Al) Powder 57.49Calcium Fluoride (CaF.sub.2) 6.84______________________________________Particle Size Distributions of Materials Used in ExamplesCALCIUM SULFATE (CaSO.sub.4)<20 micron 100% (by weight) <10 95% <5 63% <2 23% <1 9%ALUMINUM (Al) POWDER+ 20 Mesh >840 microns 100% (by weight)-20 + 40 Mesh 420-840 microns 5% Max-40 + 50 Mesh 300-420 microns 1-10%-50 + 80 Mesh 180-300 microns 15-30%-80 + 140 Mesh 100-180 microns 35-50%-140 + 325 Mesh 44-180 microns 25-45%-325 Mesh >44 microns 5% MaxCALCIUM FLUORIDE (CaF.sub.2)+ 50 Mesh >300 microns 2% Max (by weight)-50 + 100 Mesh 150-300 microns 0-10%-100 + 140 Mesh 100-150 microns 5-20%-140 + 200 Mesh 74-100 microns 10-25%-200 + 325 Mesh 44-74 microns 20-40%-325 Mesh <44 microns Balance______________________________________

The joined cables were tested for resistance and ultimate tensile strength. Duplicate welds were sectioned to detect the presence of porosity and to evaluate fusion of cable ends. Results were as follows:

A. Resistance and Tensile Strength

______________________________________ Resistance Tensile Strength (micro-ohms, 12" gauge) (lb/in.sup.2)______________________________________Unsectioned Cable 139 6348Welded Cable 132-137 1670-2387______________________________________

B. Porosity

Results ranged from no voids visible to the naked eye to less than three voids located near the top of the weld nugget.

C. Fusion of Cable Ends

Cable ends, including central strands, were fused to the filler metal.

EXAMPLE 5

Thermite reactions per the teachings of this disclosure were conducted using a ceramic crucible set over a graphite mold using the following thermite mixture to affect welds in 2/0 aluminum (Al) cable:

______________________________________Constituent Weight Percent______________________________________Barium Sulfate (BaSO.sub.4) 49.32%Aluminum (Al) Powder 44.46%Calcium Fluoride (CaF.sub.2) 6.22%______________________________________Particle Size Distributions of Materials Used in ExampleBARIUM SULFATE (BaSO.sub.4)<11 micron 100% (by weight) <6 87 <2 29ALUMINUM POWDER (Al)+ 20 Mesh >840 microns 100% (by weight)-20 + 40 Mesh 420-840 microns 5% Max-40 + 50 Mesh 300-420 microns 1-10%-50 + 80 Mesh 180-300 microns 15-30%-80 + 140 Mesh 100-180 microns 35-50%-140 + 325 Mesh 44-180 microns 25-45%-325 Mesh <44 microns 5% MaxCALCIUM FLUORIDE (CaF.sub.2)+ 50 Mesh >300 microns 2% Max (by weight)-50 + 100 Mesh 150-300 microns 0-10%-100 + 140 Mesh 100-150 microns 5-20%-140 + 200 Mesh 74-100 microns 10-25%-200 + 325 Mesh 44-74 microns 20-40%-325 Mesh <44 microns Balance______________________________________

Good quality welds were obtained with acceptable fusion of cable ends with a small amount of porosity in the weld cavity.

EXAMPLE 6

Weldments of 1/4".times.4" aluminum (Al) busbar in a straight splice were made using the process disclosed in Rejdak U.S. Pat. No. 3,020,610, the method disclosed above in EXAMPLE 4 and utilizing the following formula:

______________________________________ Approximate MeanConstituent Weight Percent Particle Size______________________________________Calcium Sulfate (CaSO.sub.4) 34.2 10 micronsAluminum (Al) Powder 55.1 150 micronsCalcium Fluoride (CaF.sub.2) 6.6 20 micronsSilicon (Si) 4.2 150 microns______________________________________ Thus, the process of the present invention may be successfully utilized with an alloying element such as silicon (Si) incorporated in the mixture of reactants.

In some applications incorporating silicon into the mixture of reactants can be highly desirable. Specifically, it has been found that the silicon provides a range of temperatures over which the weld metal will solidify thus allowing the molten weld metal to feed the solidifying interface, substantially eliminating hot cracking, wetting the pieces that are being joined and allowing gases to escape during solidification thereby reducing porosity especially in larger welds. Silicon also has the effect of strengthening the weld metal.

When silicon is employed in the mixture of reactants it has been found to be beneficial to also include a chloride salt. The chloride salt appears to act as a degassing agent, possibly combining with the hydrogen in solution.

Either calcium chloride or sodium chloride can be used. Sodium chloride is preferred because it is readily available, inexpensive, is available in many different particle size ranges, and is not hygroscopic. It is believed that the sodium chloride breaks down in the extreme heat of the reaction and the chlorine combines with the hydrogen in the molten aluminum weld metal to form minute amounts of hydrogen chloride gas, which bubbles away.

When silicon is utilized in the mixture of reactants it has also been found that the particle size of the metal sulfate is important. Specifically, it has been determined through SEM analysis that the finer sulfate powders (less than 3 .mu.m) tended to agglomerate the mixture of reactants. When calcium sulfate of a finer particle size (average .about.1.4 .mu.m) was added to the mixture, it was seen that the mixture of reactants agglomerated into very fine spheroids in the mixer, allowing the material to flow much better. The flowability of the powder was determined to be very important to the consistency of the welding process. When using a crucible and mold configuration similar to that used in the process disclosed in Rejdak U.S. Pat. No. 3,020,610, powder which does not flow in the crucible results in inconsistent burning and "tunneling", where the material does not all react before the actual welding begins. If the mixed powder does not flow well, air pockets may be left in the crucible and this results in an uneven reaction of the material. This uneven reaction results in "cold shuts", where weld metal drops, solidifies, and more metal drops over it, and also results in poor weld metal/slag separation. It was also determined that too much of the finer metal sulfate resulted in reactions that were too violent and the weld metal tended to blow out of the crucible rather than drop to make the weld.

Additional Examples illustrating the use of silicon in the mixture of reactants are set forth below. In each of such Examples below, the particle sizes of the constituents is as follows:

______________________________________Calcium Sulfate (CaSO.sub.4): Type A Type B______________________________________-44 .mu.m 100% 99%-20 .mu.m 100% 98%-10 .mu.m 95% 95%-5 .mu.m 63% 79%-2 .mu.m 23% 60%-1 .mu.m 9% 40%average size (.mu.m) 3.75-4.4 1.4______________________________________Aluminum (Al) Powder: Silicon (Si) -1% Iron (Fe):______________________________________-20 Mesh 100% +30 Mesh 1% max.-20 + 40 Mesh 95% min. -30 + 40 Mesh 1% max.-40 + 50 Mesh 1-10% -40 + 50 Mesh 1-10%-50 + 80 Mesh 15-30% -50 + 100 Mesh 45-75%-80 + 140 Mesh 35-50% -100 + 200 Mesh 20-45%-140 + 325 Mesh 25-45% -200 Mesh 5% max.-325 Mesh 5% max.______________________________________Calcium Fluoride (CaF.sub.2): Calcium Chloride (CaCl):______________________________________+50 Mesh 2% max. +35 Mesh bal.-50 + 100 Mesh 10% max. -35 + 50 Mesh 15%-100 + 140 Mesh 5-20% -50 + 80 Mesh 12%-140 + 200 Mesh 10-25% -80 + 100 Mesh 3%-200 + 325 Mesh 20-40% -100 + 140 Mesh 7%-325 Mesh bal. -140 + 200 Mesh 7% -200 + 325 Mesh 9% -325 Mesh 10%______________________________________Sodium Chloride (NaCl): Type A Type B______________________________________+35 Mesh bal. 1% max.-35 + Mesh 67% 2%-50 + Mesh 16% 67%-80 + 100 Mesh 1% 12%-100 + 140 Mesh 2% 15%-140 Mesh trace 19%______________________________________

EXAMPLE 7

Twenty weldments were made using the process described in Rejdak U.S. Pat. No. 3,020,610, welding two 1/4.times.4" aluminum busbars in a straight splice with the following formula:

I.

______________________________________Constituent Weight Percent______________________________________Calcium sulfate (CaSO.sub.4) 34.6% - half Type A, half Type BAluminum (Al) powder 51.7%Calcium fluoride (CaF.sub.2) 5.2%Silicon (Si) 4.3% - (theoretically resulting in 12.2% Si in he resultant weld metal)Sodium chloride (CaCl) 4.2% - type A______________________________________

II.

Six additional weldments welding two 1/4.times.4" aluminum busbars in a straight splice were made using the process described in Rejdak U.S. Pat. No. 3,020,610 with the following formula:

______________________________________Constituent Weight Percent______________________________________Calcium sulfate (CaSO.sub.4) 35.7% - Type AAluminum (Al) powder 57.5%Calcium fluoride (CaF.sub.2) 6.8%______________________________________

The average tensile load value of the twenty splices made above pursuant to the formula of section I was 15,040 pounds, and the sample standard deviation was 880 pounds. The average of the six splices made pursuant to the formula of section II was 6960 pounds and the sample standard deviation was 2150 pounds.

Six splices welding two 1/4.times.4" aluminum busbars into a straight splice were also made using a prior art Rejdak type formulation. The Rejdak type formulation resulted in an average tensile load of 13,330 pounds and a sample standard deviation of 1400 pounds. The details of the Rejdak type formulation are as follows:

______________________________________Constituent Weight Percent______________________________________Aluminum (Al) powder 42.8%Tin oxide (SnO.sub.2) 39.5%Copper oxide (Cu.sub.2 O) 13.4%Calcium Fluoride (CaF.sub.2) 4.3%______________________________________

The particle size of the constituents is as follows:

______________________________________Aluminum (Al) powder: Tin oxide (SnO.sub.2):______________________________________-100 Mesh 100% 99% <10 .mu.m-100 + 325 Mesh 80% average size = 0.3 .mu.maverage size (.mu.m) 19______________________________________Copper oxide (Cu.sub.2 O): Calcium Fluoride (CaF.sub.2):______________________________________-140 Mesh 100% +50 Mesh 2% max. -5 + 100 Mesh 10% max. -100 + 140 Mesh 5-20% -140 + 200 Mesh 10-25% -200 + 325 Mesh 20-40% -325 Mesh bal.______________________________________

EXAMPLE 8

Twenty 100 g reactions were made in a "pencil" mold which is designed to accentuate porosity in the weld metal. The reaction is made in an appropriately sized crucible, and the molten weld metal drops into a 1/2" diameter hole set at a 25.degree. angle. Ten reactions of each of the formulations from sections I and II of Example 7 were made. The bulk density was calculated for each of the twenty pencils, and that value was divided by the appropriate theoretical density to obtain a value for the theoretical porosity. The average theoretical porosity of the weld metal using the formula from section I of Example 7 was 9.5% with a sample standard deviation of 1.0% and the reaction appeared consistent. The average theoretical porosity of the weld metal using the formula from section II of Example 7 was 12.1% (27% higher) with a sample standard deviation of 1.1% and the reaction varied considerably.

EXAMPLE 9

Commercial 2/0 aluminum cable was welded in a straight splice according to the process disclosed in Rejdak U.S. Pat. No. 3,020,610 using the formulations shown in sections I, II and III of Example 7. These welds were tested for resistance to corrosion by exposing them to salt spray for three months. The welds were visually examined and tested in tension. The average strength of three welds made using the formulations of section III of Example 7, section II of Example 7, and section I of Example 7 was 980 pounds, 1050 pounds and 1230 pounds respectively. After three months in salt spray, the welds made using the formulation of section III of Example 7 showed obvious signs of corrosion at the interface between the weld and the cable, whereas the other two (formulations of section I and II of Example 7) did not. The tensile strength of welds made using the formulations of section III of Example 7, section II of Example 7 and section I of Example 7 after three months were 820 pounds, 960 pounds and 1250 pounds respectively. A weld made using the formulation of section III of Example 7 completely separated after six months in salt spray.

EXAMPLE 10

Three straight splice weldments were made between pieces of 1/4.times.4" aluminum busbar using the following composition:

______________________________________Constituent Weight Percent______________________________________Calcium sulfate (CaSO.sub.4) 36.7% - 75% Type A, 25% Type BAluminum (Al) powder 44.5%Calcium fluoride (CaF.sub.2) 7.4%Silicon (Si) 8.3% (theoretically resulting in 33% Si in the resultant weld metal)Sodium chloride (NaCl) 3.1%______________________________________

All the bars were welded, and the average tensile strength was 12,450 pounds. This shows that a weld can be made with a very high silicon content. After the welds were pulled, each was hit with a hammer to see if the weld was brittle. Each deformed at the edges rather than breaking.

EXAMPLE 11

Three more welds were made using the following formula:

______________________________________Constituent Weight Percent______________________________________Calcium sulfate (CaSO.sub.4) 34.6% - 25% Type A, 75% Type BAluminum (Al) powder 43.4%Calcium fluoride (CaF.sub.2) 6.9%Silicon (Si) 10.0% (theoretically resulting in 40% Si in the resultant weld metal)Sodium chloride (NaCl) 5.0%______________________________________

All the bars were welded, and the average tensile strength was 10,860 pounds. However, the welds were brittle and shattered when hit with a hammer.

EXAMPLE 12

Three straight-splice weldments were made between pieces of 1/4.times.4" aluminum busbar using each of the two following formulas:

I.

______________________________________Constituent Weight Percent______________________________________Calcium sulfate (CaSO.sub.4) 39.7% - half type A, half type BAluminum (Al) powder 49.9%Calcium fluoride (CaF.sub.2) 6.0%Silicon (Si) 0.9% (theoretically resulting in 3% Si in the resultant weld metal)Sodium chloride (NaCl) 3.6%______________________________________

II.

______________________________________Constituent Weight Percent______________________________________Calcium sulfate (CaSO.sub.4) 38.9% - half Type A, half Type BAluminum (Al) powder 49.4%Calcium fluoride (CaF.sub.2) 5.8%Silicon (Si) 2.3% (theoretically resulting in 8% Si in the resultant weld metal)Sodium chloride (NaCl) 5.0%______________________________________

The welds made using the formulation of section I were tensile tested. The average tensile strength was 11,600 pounds. The average tensile strength using the formulation of section II was 13,000 pounds. Although the formulation of section I probably gave adequate strength, an examination of the fracture surface revealed that the bar was incompletely welded and large gas bubbles had been trapped in the weld. In the weld made with the formulation of section II, the bubbles were substantially smaller and the interface was completely welded. The interface is critical to the electrical properties of the weld.

It is thus seen that the process of this invention provides a novel process for producing weldments and a novel process for the utilization of the thermite reaction to produce weldments.

Although the invention has been shown and described with respect to certain preferred embodiments, it is obvious that equivalent alterations and modifications will occur to others skilled in the art upon their reading and understanding of this specification. The present invention includes all such equivalent alterations and modifications, and is limited only by the scope of the following claims.

Claims

1. A process for producing weld metal for use in joining at least two aluminum (Al) containing pieces comprising:

(A) providing a mixture of reactants comprising a reducing agent, a metallic compound which is exothermically reduced by such reducing agent, silicon and a filler metal that does not chemically react with such metallic compound or such reducing agent upon the exothermic reaction of such reducing agent and such metallic compound; and

(B) exothermically reacting such reducing agent and such metallic compound so as to generate sufficient heat to melt such filler metal and form such molten weld metal for joining such aluminum pieces, at least 90 percent by weight of such molten weld metal being formed by such filler metal and such silicon.

2. A process as set forth in claim 1 wherein at least about 90% by weight of such weld metal includes a chemical composition which is substantially similar to that of at least one of such aluminum containing pieces being joined.

3. A process as set forth in claim 1 wherein such mixture of reactants includes a flux and such flux comprises at least one compound selected from the group consisting of calcium fluoride (CaF.sub.2), magnesium fluoride (MgF.sub.2), cryolite (Na.sub.3 AlF.sub.6), alkali silicates and fluorosilicates.

4. A process as set forth in claim 1 wherein at least about 95% by weight of such weld metal is formed by such filler metal.

5. A process as set forth in claim 1 wherein such mixture of reactants comprises from about 20 percent by weight to about 50 percent by weight of a metal sulfate, from about 40 percent by weight to about 70 percent by weight aluminum (Al), from about 0.1 percent by weight to about 45 percent by weight of silicon (Si), up to about 10 percent by weight of a chloride salt and up to about 10 percent by weight of a flux.

6. A process as set forth in claim 5 wherein said chloride salt is selected from the group consisting of calcium chloride (CaCl) or sodium chloride (NaCl), such metal sulfate is selected from the group consisting of magnesium sulfate (MgSO.sub.4), barium sulfate (BaSO.sub.4) or calcium sulfate (CaSO.sub.4) and such flux is selected from the group consisting of calcium fluoride (CaF.sub.2), magnesium fluoride (MgF.sub.2) or cryolite (Na.sub.3 AlF.sub.6).

7. A process as set forth in claim 1 including the steps of placing such mixture of reactants into the crucible portion of a welding apparatus and placing a portion of such aluminum (Al) containing pieces into the mold cavity portion of such welding apparatus.

8. A mixture of reactants which upon initiation of an exothermic reaction forms a molten weld metal for use in joining two or more aluminum or aluminum alloy pieces, said mixture of reactants comprising:

silicon;

a reducing agent;

a metallic compound; and

a filler metal that does not chemically react with said metallic compound upon initiation of the exothermic reaction between said reducing agent and said metallic compound, the exothermic reaction producing sufficient heat for melting said filler metal and forming the resultant molten weld metal, at least about 90 percent by weight of the resultant molten weld metal being formed by said filler metal and said silicon.

9. A mixture of reactants as set forth in claim 8 wherein said reducing agent comprises aluminum (Al).

10. A mixture of reactants as set forth in claim 8 wherein said metallic compound comprises a metal sulfate, at least a portion of said metal sulfate having an average particle size of about 1.4 microns.

11. A mixture of reactants as set forth in claim 8 wherein said filler metal comprises aluminum (Al).

12. A mixture of reactants as set forth in claim 8 comprising from about 20 percent by weight to about 50 percent by weight reducing agent, from about 40 percent by weight to about 70 percent by weight aluminum (Al), from about 0.1 percent by weight to about 45 percent by weight silicon (Si) and up to about 10 percent by weight flux.

13. A mixture of reactants as set forth in claim 8 comprising from about 30 percent by weight to about 45 percent by weight reducing agent, from about 42 percent by weight to about 60 percent by weight aluminum (Al), from about 0.2 percent by weight to about 9 percent by weight silicon (Si), from about 2 percent by weight to about 10 percent by weight of a chloride salt and from about 2 percent by weight to about 10 percent by weight flux.

14. A mixture of reactants as set forth in claim 8 comprising from about 35 percent by weight to about 42 percent by weight reducing agent, from about 45 percent by weight to about 52 percent by weight aluminum (Al), from about 0.2 percent by weight to about 9 percent by weight silicon (Si), from about 4 percent by weight to about 5 percent by weight of a chloride salt and from about 5 percent by weight to about 7 percent by weight flux.

15. A mixture of reactants which upon initiation of an exothermic reaction form a molten weld metal for use in joining two or more aluminum containing pieces, said mixture of reactants comprising silicon, a first and a second portion of aluminum (Al) and a metal sulfate; said aluminum (Al) being present in a sufficient amount such that said first portion of said aluminum (Al) does not chemically react with said metallic sulfate upon the initiation of the exothermic reaction between said metal sulfate and said second portion of said aluminum (Al), the exothermic reaction between said metal sulfate and said second portion of said aluminum (Al) producing sufficient heat for melting said first portion of said aluminum (Al), said first portion of aluminum (Al) and said silicon (Si) upon melting forming such resultant molten weld metal such that at least about 90 percent by weight of such resultant molten weld metal comprises aluminum (Al) and silicon (Si).

16. A mixture of reactants as set forth in claim 15 wherein said aluminum (Al) of said mixture of reactants comprises aluminum (Al) powder.

17. A mixture of reactants which upon initiation of an exothermic reaction form a weld metal for use in joining two or more metallic pieces comprising from about 20 percent by weight to about 50 percent by weight of a metal sulfate, from about 40 percent by weight to about 70 percent by weight aluminum and from about 0.1 percent by weight to about 45 percent by weight silicon.

18. A mixture of reactants as set forth in claim 17 including up to about 10 percent by weight of a chloride salt and up to about 10 percent by weight of a flux.

19. A mixture of reactants as set forth in claim 18 wherein said chloride salt is selected from the group consisting of sodium chloride or calcium chloride and said flux is selected from the group consisting of calcium fluoride, magnesium fluoride or cryolite.

20. A mixture of reactants as set forth in claim 19 comprising from about 30 percent by weight to about 45 percent by weight metal sulfate, from about 42 percent by weight to about 60 percent by weight aluminum, from about 2 percent by weight to about 9 percent by weight silicon, from about 2 percent by weight to about 10 percent by weight chloride salt and from about 2 percent by weight to about 10 percent by weight flux.

21. A mixture of reactants as set forth in claim 18 wherein said metal sulfate is selected from the group consisting of magnesium sulfate, barium sulfate or calcium sulfate.

22. A mixture of reactants as set forth in claim 17 comprising from about 35 percent by weight to about 42 percent by weight metal sulfate, from about 45 percent by weight to about 52 percent by weight aluminum, from about 0.2 percent by weight to about 9 percent by weight silicon, from about 4 percent by weight to about 5 percent by weight chloride salt and from about 5 percent by weight to about 7 percent by weight flux.