Amine and Nitroxide Based Additive Composition for Control and Inhibition of Polymerization of Styrene, and Method of Use Thereof

Abstract
The present invention relates to additive composition for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene comprising (a) one or more of nitroxide (i.e. nitroxyl) compounds, and characterized in that the said composition further comprises one or more of (b) aliphatic amines selected from a group comprising tertiary amines, secondary amines and primary amines. In one embodiment, the present invention also relates to method of use of presently provided composition. In another embodiment, the present invention also relates to method of controlling and inhibiting polymerization of aromatic vinyl monomers including styrene by employing presently provided composition. In still another embodiment, the present invention also relates to method of preparation of presently provided composition.
Description
FIELD OF THE INVENTION

The present invention relates to amine and nitroxide based additive composition for control and inhibition of polymerization of aromatic vinyl monomers, wherein aromatic vinyl monomer include styrene.


In one embodiment, the present invention relates to use of amine and nitroxide based additive composition of present invention to control and inhibit polymerization of aromatic vinyl monomers including styrene.


In another embodiment, the present invention relates to method of preparation of amine and nitroxide based additive composition of present invention for control and inhibition of polymerization of aromatic vinyl monomers including styrene.


In still another embodiment, the present invention relates to method of controlling and inhibiting polymerization of aromatic vinyl monomers including styrene by employing amine and nitroxide based additive composition of present invention.


BACKGROUND OF THE INVENTION

The polymerization of aromatic vinyl monomers including styrene during processing is a matter of concern, because it causes formation of unwanted polymers and results in loss of yield of end product and makes the process un-economical.


In the art use of inhibitors and retarders, and combination thereof to overcome problem of polymerization of styrene has been reported.


The problem of using the inhibitors alone is that these are to be added continuously or at regular interval, because once they are consumed, the polymerization will re-start.


The problem of using the retarders alone is that these are not very effective to reduce polymerization of styrene to a level of substantial inhibition or to the acceptable level of inhibition.


The prior art [U.S. Pat. No. 5,254,760 (US'760)] discloses the polymerization inhibition of vinyl monomers using a combination of nitroxides (i.e. nitroxyl compounds) including 1 oxyl-2,2,6,6, tetramethylpiperidin-4-ol (4HT) and aromatic nitro compounds including dinitro-butylphenol [re abstract, Col. 3, lines 26-32; Col. 4, lines 1-2, 12 of US'760] as the polymerization inhibitor.


The US'760 discloses and teaches use of combination of nitroxides (i.e. nitroxyl) compound and aromatic nitro compound. The US'760 discloses and teaches against the use of either of nitroxides (i.e. nitroxyl) compound or of aromatic nitro compound [Re Col. 5, lines 50-56; Col. 6, lines 10-14 and 42-46; Col. 7, lines 36-41 of US'760].


However, the aromatic nitro compounds including DNBP are to be used in higher amounts and/or are also known for their toxic nature for human exposure [re Col. 1, lines 64-68 of US'760].


Therefore, the industry is aiming for additive composition wherein the aromatic nitro compounds can be avoided. Any effort to avoid consumption of aromatic nitro compounds will lessen the problem of industry.


NEED OF THE INVENTION

Therefore, there is still a need of an effective additive composition and method of its use and preparation, and method of controlling and inhibiting polymerization of vinyl aromatic monomers by employing said composition, wherein the additive composition is not only suitable for substantial control and inhibition of polymerization of aromatic vinyl monomers including styrene, but also does not comprise aromatic nitro compounds.


SUMMARY OF THE INVENTION

Therefore, the present invention aims at providing a solution to above-described existing industrial problems by providing effective additive composition and method of its use and preparation, and method of controlling and inhibiting polymerization of vinyl aromatic monomers, wherein the additive composition is not only suitable for substantial control and inhibition of polymerization of aromatic vinyl monomers including styrene, but also does not comprise aromatic nitro compounds.


In addition to above aim, the present invention also aims at providing an effective additive composition and method of its use and preparation, and method of controlling and inhibiting polymerization of vinyl aromatic monomers, wherein the additive composition is not only suitable for substantial control and inhibition of polymerization of aromatic vinyl monomers including styrene, but also comprises reduced or minimized amount of nitroxides (i.e. nitroxyl) compounds.


OBJECTS OF THE INVENTION

Accordingly, the main object of present invention is to provide an effective additive composition and method of its use and preparation, and method of controlling and inhibiting polymerization of vinyl aromatic monomers, wherein the additive composition is not only suitable for substantial control and inhibition of polymerization of aromatic vinyl monomers including styrene, but also does not comprise aromatic nitro compounds.


Another main object of present invention is to provide an effective additive composition and method of its use and preparation, and method of controlling and inhibiting polymerization of vinyl aromatic monomers, wherein the additive composition is not only suitable for substantial control and inhibition of polymerization of aromatic vinyl monomers including styrene, but also comprises reduced or minimized amount of nitroxides (i.e. nitroxyl) compounds.


This is also an object of present invention to provide an effective additive composition and method of its use and preparation, and method of controlling and inhibiting polymerization of vinyl aromatic monomers, wherein the additive composition comprises reduced or minimized amount of one or more of nitroxides (i.e. nitroxyl) compounds, and does not comprise aromatic nitro compounds, and is still suitable for substantial control and inhibition of polymerization of aromatic vinyl monomers including styrene, and is still required in relatively lower dosage as compared to dosage of nitroxides (i.e. nitroxyl) compounds alone for achieving the same or better acceptable level of control and inhibition of polymerization of aromatic vinyl monomers including styrene.


This is also an object of present invention to provide an effective additive composition and method of its use and preparation, and method of controlling and inhibiting polymerization of vinyl aromatic monomers, wherein the additive composition comprises one or more of amines and reduced or minimized amount of one or more of nitroxides (i.e. nitroxyl) compounds, and does not comprise aromatic nitro compounds, and is still suitable for substantial control and inhibition of polymerization of aromatic vinyl monomers including styrene, and is still required in relatively lower dosage as compared to dosage of nitroxides (i.e. nitroxyl) compounds alone for achieving the same or better acceptable level of control and inhibition of polymerization of aromatic vinyl monomers including styrene, and wherein the amine is aliphatic amine.


The present invention particularly aims at providing an effective additive composition and method of its use and preparation, and method of controlling and inhibiting polymerization of vinyl aromatic monomers, wherein the additive composition comprises one or more of amines and reduced or minimized amount of one or more of nitroxides (i.e. nitroxyl) compounds, and does not comprise aromatic nitro compounds, and is still suitable for substantial control and inhibition of polymerization of aromatic vinyl monomers including styrene, and is still required in relatively lower dosage as compared to dosage of nitroxides (i.e. nitroxyl) compounds alone for achieving the same or better acceptable level of control and inhibition of polymerization of aromatic vinyl monomers including styrene, and wherein the amine is aliphatic amine, which is selected from a group comprising tertiary amines, secondary amines and primary amines, preferably the amine is tertiary amine, and therefore, the composition of present invention is not only economical, but is also environment friendly.


The present invention also aims at improving the performance of nitroxide (i.e. nitroxyl) compounds at a wider range of temperature including the higher temperature and in presence of air, wherein the composition further comprises one or more aliphatic amines.


Other objects and advantages of present invention will become more apparent from the following description when read in conjunction with examples, which are not intended to limit scope of present invention.







DETAILED DESCRIPTION OF THE INVENTION

With aim to overcome above-described problems of prior art and to achieve above-described objects of the invention, the inventor has found that when an aliphatic amine is added to composition consisting of nitroxide (i.e. nitroxyl) compounds even without aromatic nitro compounds, then not only polymerization controlling and inhibiting efficiency of nitroxides is substantially improved, but polymerization of aromatic vinyl monomers including styrene, surprisingly and unexpectedly, is also controlled and inhibited to the acceptable level at substantially reduced dosages of composition comprising one or more of nitroxide compounds and one or more of aliphatic amine compounds, which makes the composition economical as well as environment friendly.


With aim to overcome above-described problems of prior art and to achieve above-described objects of the invention, the inventor has found that when one or more of aliphatic tertiary amines, or aliphatic tertiary amines containing one or more hydroxyl groups or one or more of secondary amines or one or more of primary amines or mixture thereof is added to composition consisting of one or more of nitroxide (i.e. nitroxyl) compounds without aromatic nitro compounds, then not only polymerization controlling and inhibiting efficiency of nitroxides is substantially improved, but polymerization of aromatic vinyl monomers including styrene, surprisingly and unexpectedly, is also controlled and inhibited to the acceptable level at substantially reduced dosages of composition comprising nitroxide and aliphatic amine compounds, which makes the composition economical as well as environment friendly.


Accordingly, the present invention relates to additive composition for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene comprising:


(a) one or more of nitroxides (i.e. nitroxyls) compounds; and


characterized in that the said composition further comprises one or more of


(b) aliphatic amines selected from a group comprising tertiary amines, secondary amines and primary amines, preferably the amine is tertiary amine.


Accordingly, in one embodiment, the present invention relates to additive composition for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene comprising:


(a) one or more of nitroxides (i.e. nitroxyls) compounds; and


characterized in that the said composition further comprises one or more of


(b) tertiary amines.


Accordingly, in another embodiment, the present invention relates to additive composition for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene comprising:


(a) one or more of nitroxides (i.e. nitroxyls) compounds; and


characterized in that the said composition further comprises one or more of


(b) amines selected from a group consisting of primary amines and secondary amines.


In accordance with present invention, the aliphatic amine is an aliphatic tertiary amine, which contains one or more hydroxyl groups in the alkyl chain of the tertiary amine, preferably it contains three hydroxyl groups in the alkyl chain of the tertiary amine, more preferably the hydroxyl groups are hydroxyalkyl groups.


In accordance with one of the most preferred embodiments of the present invention, the said amine is hydroxyl alkyl tertiary amine.


In accordance with one of the preferred embodiments of the present invention, the said amine is ethylene oxide treated amine.


In accordance with one of the preferred embodiments of the present invention, the said amine is propylene oxide treated amine.


In accordance with one of the preferred embodiments of the present invention, the said amine is tertiary alkyl amine.


In accordance with one of the preferred embodiments of the present invention, the said amine is mixture of one or more of hydroxyl alkyl tertiary amines, ethylene oxide treated amines, propylene oxide treated amines, tertiary alkyl amines.


In accordance with one of the most preferred embodiments of the present invention, the said hydroxyl alkyl tertiary amine is tris(2-hydroxypropyl)amine (TIPA).


In accordance with one of the preferred embodiments of the present invention, the said ethylene oxide treated amine is N,N,N′,N′-Tetrakis(2-hydroxyethyl)ethylene-diamine) (THEED).


In accordance with one of the preferred embodiments of the present invention, the said propylene oxide treated amine is N,N,N′,N′-Tetrakis(2-hydroxypropyl)ethylene-diamine) (Quadrol).


In accordance with one of the preferred embodiments of the present invention, the said hydroxyl alkyl tertiary amine is triethanolamine (TEA).


In accordance with one of the preferred embodiments of the present invention, the said tertiary alkyl amine is Tris[N-butylamine] (TBA).


In accordance with one of the embodiments of the present invention, the said primary amine is selected from a group comprising hydroxyl alkyl primary amine and alkyl primary amine.


In accordance with one of the embodiments of the present invention, the said secondary amine is alkyl secondary amine.


In accordance with one of the embodiments of the present invention, the said hydroxyl alkyl primary amine is monoethanolamine (MEA).


In accordance with one of the embodiments of the present invention, the said alkyl primary amine is octyl amine (OA).


In accordance with one of the embodiments of the present invention, the said alkyl secondary amine is dibutyl amine (DBA).


It has been found that when composition of present invention comprises one or more of said amines, the efficiency of nitroxide compounds to control and inhibit polymerization of aromatic vinyl monomers including styrene is, surprisingly and unexpectedly, substantially improved to the acceptable level that's too at substantially reduced dosages of nitroxide compounds and that's too without aromatic nitro compounds, thereby making the composition of present invention relatively more economical and environment friendly.


In accordance with one of the embodiments of the present invention, the composition of present invention comprises:

    • a) about 40 to about 99.75% by weight of I) said nitroxide (i.e. nitroxyl) compounds; and
    • b) about 0.25 to about 60% by weight of II) said amines or mixture thereof.


In accordance with one of the preferred embodiments of the present invention, the composition of present invention is added to the stream containing aromatic vinyl monomers including styrene in an amount varying from about 0.01 ppm to about 2000 ppm, preferably from about 1 ppm to about 2000 ppm by weight of the stream of monomer including styrene.


In accordance with present invention, the nitroxide (or nitroxyl) compound is selected from the group comprising di-tert-butylnitroxyl, 1-oxyl-2,2,6,6-tetramethylpiperidine, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-ol, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-one, and derivatives thereof; and di-nitroxides and derivatives comprising bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)sebacate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yesuccinate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)adipate, and mixture thereof.


In accordance with preferred embodiment of the present invention, the nitroxide (or nitroxyl) compound is selected from the group comprising bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)sebacate and 1 oxyl-2,2,6,6, tetramethylpiperidin-4-ol or 4-hydroxy-2,2,6,6-tetramethylpiperidin-1-oxyl (or 4 Hydroxy Tempo or 4-HT), and mixture thereof.


In accordance with most preferred embodiment of the present invention, the nitroxide (or nitroxyl) compound is 1 oxyl-2,2,6,6, tetramethylpiperidin-4-ol (or 4 Hydroxy Tempo or 4-HT).


In accordance with one of the preferred embodiments of the present invention, the present composition does not comprise aromatic nitro compound.


Accordingly, in another embodiment, the present invention also relates to method of using amine and nitroxide based additive composition of present invention described herein, a reference to which is drawn in entirety, to control and inhibit polymerization of aromatic vinyl monomers including styrene, wherein the stream comprising aromatic vinyl monomer including styrene is treated with an additive composition comprising one or more of nitroxides (i.e. nitroxyls) compounds and one or more of said amines.


In particular, in second embodiment, the present invention relates to a method of using additive composition of the present invention described herein, a reference to which is drawn in entirety, for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene, wherein said composition comprises:


(a) one or more of nitroxides (i.e. nitroxyls) compounds; and


characterized in that the said composition further comprises one or more of


(b) aliphatic amines selected from a group comprising tertiary amines, secondary amines and primary amines, preferably the amine is tertiary amine; and


said monomers are treated with said composition.


Accordingly, in this second embodiment, the present invention particularly relates to a method of using additive composition of the present invention described herein, a reference to which is drawn in entirety, for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene, wherein said composition comprises:


(a) one or more of nitroxides (i.e. nitroxyls) compounds; and


characterized in that the said composition further comprises one or more of


(b) tertiary amines; and


said monomers are treated with said composition.


Accordingly, in this second embodiment, the present invention also relates to a method of using additive composition of the present invention described herein, a reference to which is drawn in entirety, for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene, wherein said composition comprises:


(a) one or more of nitroxides (i.e. nitroxyls) compounds; and


characterized in that the said composition further comprises one or more of


(b) amines selected from a group consisting of primary amines and secondary amines; and


said monomers are treated with said composition.


It may be noted that the stream comprising aromatic vinyl monomers including styrene may be referred to as stream or monomers stream or as aromatic vinyl monomers stream.


In accordance with one of the embodiments of the present invention, the method of using said additive composition of the present invention comprises treating said monomers stream with about 0.01 ppm to about 2000 ppm, preferably from about 1 ppm to about 2000 ppm of said composition based on weight of monomers.


It may be noted that all the features of the composition of the present invention described herein, a reference to which is drawn in entirety, are deemed to have been included in present method of using said additive composition of the present invention.


Accordingly, in third embodiment, the present invention also relates to method for controlling and inhibiting polymerization of aromatic vinyl monomers including styrene by employing amine and nitroxide based additive composition of present invention described herein, a reference to which is drawn in entirety, wherein the stream comprising aromatic vinyl monomers including styrene is treated with an additive composition comprising one or more of nitroxides (i.e. nitroxyls) compounds and one or more of said amines.


In particular, in third embodiment, the present invention relates to a method for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene by employing additive composition of the present invention described herein, a reference to which is drawn in entirety, wherein said composition comprises:


(a) one or more of nitroxides (i.e. nitroxyls) compounds; and


characterized in that the said composition further comprises one or more of


(b) aliphatic amines selected from a group comprising tertiary amines, secondary amines and primary amines, preferably the amine is tertiary amine; and


said composition is added to said monomers.


Accordingly, in this third embodiment, the present invention particularly relates to a method for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene by employing additive composition of the present invention described herein, a reference to which is drawn in entirety, wherein said composition comprises:


(a) one or more of nitroxides (i.e. nitroxyls) compounds; and


characterized in that the said composition further comprises one or more of


(b) tertiary amines; and


said composition is added to said monomers.


Accordingly, in this third embodiment, the present invention also relates to a method for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene by employing additive composition of the present invention described herein, a reference to which is drawn in entirety, wherein said composition comprises:


(a) one or more of nitroxides (i.e. nitroxyls) compounds; and


characterized in that the said composition further comprises one or more of


(b) amines selected from a group consisting of primary amines and secondary amines; and


said composition is added to said monomers.


It may be noted that the stream comprising aromatic vinyl monomers including styrene may be referred to as stream or monomers stream or as aromatic vinyl monomers stream.


In accordance with one of the embodiments of the present invention, the method for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene by employing said additive composition of the present invention comprises adding from about 0.01 ppm to about 2000 ppm, preferably from about 1 ppm to about 2000 ppm of said composition to the aromatic vinyl monomers stream including styrene based on weight of monomers.


It may be noted that all the features of the composition of the present invention described herein, a reference to which is drawn in entirety, are deemed to have been included in present method for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene by employing said additive composition of the present invention.


In accordance with one of the embodiments of the present invention, the composition of present invention may be mixed with or added to the monomers stream containing aromatic vinyl monomers including styrene either before the stream enters into processing system or after the stream has entered into processing system, but preferably the composition is added to the stream containing aromatic vinyl monomers before its processing starts so that polymerization of aromatic vinyl monomers is avoided.


In accordance with one of the embodiments of the present invention, the nitroxide compounds and the amine compounds may be mixed with or added to the monomers stream individually or after mixing.


In accordance with one of the embodiments of the present invention, the present composition may be used in or employed with or added to monomers stream over a wide range of temperature varying from about 50 degree C. to about 180 degree C., preferably from about 60 degree C. to about 180 degree C.


The composition of present invention may be prepared in any known manner to prepare the compositions.


Accordingly, in fourth embodiment, the present invention also relates to method of preparing amine and nitroxide based additive composition of present invention described herein, a reference to which is drawn in entirety, for controlling and inhibiting polymerization of aromatic vinyl monomers including styrene, wherein the nitroxide and said amine compounds are added individually or after mixing.


In particular, in fourth embodiment, the present invention relates to a method for preparation of additive composition of the present invention described herein, a reference to which is drawn in entirety, for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene, wherein the method comprises:


(A) mixing one or more of said nitroxide (i.e. nitroxyl) compounds,


characterized in that said nitroxide compound or mixture thereof is further mixed with one or more of


(B) aliphatic amines selected from a group comprising tertiary amines, secondary amines and primary amines, preferably the tertiary amines.


Accordingly, in this fourth embodiment, the present invention particularly relates to a method for preparation of additive composition of the present invention described herein, a reference to which is drawn in entirety, for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene, wherein the method comprises:


(A) mixing one or more of said nitroxide (i.e. nitroxyl) compounds,


characterized in that said nitroxide compound or mixture thereof is further mixed with one or more of


(B) tertiary amines.


Accordingly, in this fourth embodiment, the present invention also relates to a method for preparation of additive composition of the present invention described herein, a reference to which is drawn in entirety, for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene, wherein the method comprises:


(A) mixing one or more of said nitroxide (i.e. nitroxyl) compounds,


characterized in that said nitroxide compound or mixture thereof is further mixed with one or more of


(B) amines selected from a group consisting of primary amines and secondary amines.


It may be noted that the stream comprising aromatic vinyl monomers including styrene may be referred to as stream or monomers stream or as aromatic vinyl monomers stream.


It may be noted that all the features of the composition of the present invention described herein, a reference to which is drawn in entirety, are deemed to have been included in present method for preparation of additive composition of the present invention.


In one of the embodiments, the inventor has found that when present composition comprises any one of the amines selected from a group consisting of N,N,N′,N′-Tetrakis(2-hydroxyethyl)ethylene-diamine) (THEED) and N,N,N′,N′-Tetrakis(2-hydroxypropyl)ethylene-diamine) (Quadrol), then efficiency for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene of the nitroxides is substantially improved, however, the efficiency improvement is not as substantial as for the composition comprising tris(2-hydroxypropyl)amine (TIPA). Therefore, as per most preferred embodiment of the present invention, tris(2-hydroxypropyl)amine (TIPA) is most preferred amine.


In another embodiment, the inventor has found that when present composition comprises any one of the amines selected from a group consisting of triethanolamine (TEA), Tris[N-butylamine] (TBA), monoethanolamine (MEA), octyl amine (OA), dibutyl amine (DBA), then efficiency for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene of the nitroxides is improved, however, the efficiency improvement is not as substantial as for the composition comprising N,N,N′,N′-Tetrakis(2-hydroxyethyl)ethylene-diamine) (THEED) or N,N,N′,N′-Tetrakis(2-hydroxypropyl)ethylene-diamine) (Quadrol). Therefore, as per more preferred embodiment of the present invention, N,N,N′,N′-Tetrakis(2-hydroxyethyl)ethylene-diamine) (THEED) and N,N,N′,N′-Tetrakis(2-hydroxypropyl)ethylene-diamine) (Quadrol) are the more preferred amines. It has been found that dibutyl amine (DBA), surprisingly and unexpectedly, demonstrates better efficiency when used in compositions of dosages of about 200 ppm or more.


In still another embodiment, the inventor has found that when present composition comprises any one of the amines selected from a group consisting of N,N,disec-butyl-para-phenylene diamine (UOP5), ethylene diamine (EDA), tetraethylenepentamine (TEPA), dipropyl amine (DPA), or diethanol amine (DEA), then efficiency for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene of the nitroxides is not improved. Therefore, in one embodiment, the present composition does not comprise any one of the amines selected from a group consisting of N,N,disec-butyl-para-phenylene diamine (UOP5), ethylene diamine (EDA), tetraethylenepentamine (TEPA), dipropyl amine (DPA), or diethanol amine (DEA). It may be noted that some of these amines result in very marginal improvement in efficiency of nitroxides, but same is not commercially viable.


EXAMPLES

Further advantages and embodiments of the present invention will become more apparent from the following examples.


The present invention is now described with the help of following examples, which are not intended to limit scope of the present invention, but have been incorporated to illustrate mode and best mode of performing the present invention.


EXPERIMENTS
Main Experiment

In the following experiments, weighed amount of distilled styrene and additives were taken in a reactor (tube reactor or round bottom reactor) equipped with thermometer and nitrogen inlet and outlet. In these experiments a tube reactor was used without any mechanical stirrer, and enough N2 flow was maintained to ensure proper agitation. The reactions were carried out at about 120° C. for about 2 hours. After the selected duration, the reactor was cooled to below about 10° C. by immersing in crushed ice. The contents of the reactor were then poured in a beaker. To this same beaker, approximately for 1.5-2 g chilled polymerization mixture, about 80 g methanol was used to precipitate the polymer formed in the styrene solution. The precipitate obtained was filtered, dried to remove methanol, and weighed.


The weight of the precipitate was reported as % polymer formed in following tables.


It may be noted that styrene was purified before use to remove the stabilizers.


In the following examples, the prior additive is a nitroxide, which is 1 oxyl-2,2,6,6, tetramethylpiperidin-4-ol (or 4 Hydroxy Tempo or 4-HT), which was taken in an amount of about 100, 200, 300, 500, or 1000 ppm by weight of styrene.


In the following examples, the present additive is a composition comprising nitroxide which is 1-oxyl-2,2,6,6, tetramethylpiperidin-4-ol (4 Hydroxy Tempo or 4-HT), and aliphatic tertiary amine, which is tri-isopropanol amine (TIPA) containing three hydroxyl groups, wherein from about 1 to about 20 ppm of TIPA is added to the weighed amount of nitroxide.


Experiment 1

The results of above Main Experiment when performed with 10 g of distilled styrene by heating to 120° C. for 2 h are provided in Table-I.













TABLE I





Active






Dosage of
% polymer
Active Dosage


Prior Art
formed
of Present
% polymer


Additive
with Prior
Additive
formed with


Composition
art
Composition
Present
Technical Effects of


(ppm) ↓
Additive
(ppm) ↓
composition
present composition



















100 ppm
13.19
100 + 4 TIPA
11.22
Polymerization




100 + 10
10.9
inhibition efficiency of




TIPA

nitroxide is improved,




100 + 15
6.28
and % polymer formed




TIPA

is reduced substantially




100 + 20
4.3
on addition of aliphatic




TIPA

tertiary amine in


200 ppm
9.38
100 + 15
6.28
nitroxide




TIPA




100 + 20
4.3




TIPA


300 ppm
5.1
100 + 20
4.3




TIPA









It is understood from above Table-I that when just 4 ppm to 20 ppm of TIPA is added to 100 ppm of 4HT (prior art additive), the efficiency of 4-HT to control and inhibit polymerization of styrene is, surprisingly and unexpectedly, improved substantially.


It can also be seen from Table-I that polymerization of styrene is, surprisingly and unexpectedly, substantially reduced just on addition of 4 to 20 ppm of TIPA in 100 ppm of 4HT (prior art additive).


It may be noted, the % polymer formed with 100 ppm of 4-HT alone is substantially reduced from 13.19% to 11.22%, to 10.9%, to 6.28%, and to 4.3%, respectively when 4 ppm (3.85% of total composition), 10 ppm (9.09% of total composition), 15 ppm (13.04% of total composition) and 20 ppm (16.67% of total composition) of TIPA is added to 100 ppm of 4HT.


It can also be seen from Table-I that for composition comprising 100 ppm of 4HT and 15 ppm of TIPA (13.04% of TIPA of total composition), the % polymer formed is, surprisingly and unexpectedly, substantially less than % polymer formed with composition consisting of 200 ppm of 4-HT, meaning thereby, the present composition results in saving of half of dosage of 4-HT, and hence is economical and environment friendly.


It can also be seen from Table-I that for composition comprising 100 ppm of 4HT and 20 ppm of TIPA (16.67% of TIPA of total composition), the % polymer formed is, surprisingly and unexpectedly, substantially less than % polymer formed with composition consisting of 300 ppm of 4-HT, meaning thereby, the present composition results in saving of two-third of dosage of 4-HT, and hence, is economical and environment friendly.


Experiment 2

The results of above Main Experiment when performed with 10 g of distilled styrene by heating to 135° C. for 2 h are provided in Table-II.













TABLE II





Active






Dosage of
% polymer
Active Dosage


Prior Art
formed
of Present
% polymer


Additive
with Prior
Additive
formed with


Composition
art
Composition
Present
Technical Effects of


(ppm) ↓
Additive
(ppm) ↓
composition
present composition



















 500 ppm
16.7
500 + 5 TIPA
6.45
Polymerization




500 + 10
6.05
inhibition efficiency of




TIPA

nitroxide is improved,




500 + 15
5.72
and % polymer formed




TIPA

is reduced substantially




500 + 20
4.9
on addition of aliphatic




TIPA

tertiary amine in


1000 ppm
6.13
500 + 10
6.05
nitroxide




TIPA




500 + 15
5.72




TIPA




500 + 20
4.9




TIPA









It is understood from above Table-II that when just 5 ppm to 20 ppm of TIPA is added even to higher dosage of 500 ppm of 4HT (prior art additive) and styrene stream with additive is treated even at higher temperature of 135° C., the efficiency of 4-HT to control and inhibit polymerization of styrene is, surprisingly and unexpectedly, improved substantially.


It can also be seen from Table-II that polymerization of styrene is, surprisingly and unexpectedly, substantially reduced just on addition of 5 to 20 ppm of TIPA in 500 ppm of 4HT (prior art additive).


It may be noted the % polymer formed with 500 ppm of 4-HT alone is substantially reduced even at higher temperature of about 135° C. from 16.7% to 6.45%, to 6.05%, to 5.72%, and to 4.9%, respectively when 5 ppm (just 0.99% of total composition), 10 ppm (just 1.96% of total composition), 15 ppm (just 2.91% of total composition) and 20 ppm (just 3.85% of total composition) of TIPA is added to 500 ppm of 4HT. The reduction achieved is even greater than about 3 times.


It can also be seen from Table-II that for composition comprising 500 ppm of 4HT and 10 ppm of TIPA (just 1.96% of TIPA of total composition), the % polymer formed is, surprisingly and unexpectedly, less than % polymer formed with composition consisting of 1000 ppm of 4-HT, meaning thereby, the present composition results in saving of half of dosage of 4-HT, and hence is economical and environment friendly.


Experiments 3 to 5

In the following examples, for above Main Experiment, the prior art additive composition is 4HT, which is taken in an amount of about 100, 200, and 300 ppm, and the present additive composition is a composition comprising 4HT being nitroxide, and additionally comprising TIPA, THEED, Quadrol, TEA, TBA, MEA, OA, DBA being amines of the present invention, which are taken in weight ratio of 99:1, 98:2, 95:5, 90:10, 85:15, 80:20, 70:30 and 50:50, the composition is made to 100, 200 and 300 ppm.


The inventor has further compared the results of present compositions with additive compositions comprising 4HT and amine selected from a group consisting of UOP5, EDA, TEPA, DPA, or DEA for comparative purposes.


As can be seen from data in Tables III, IV and V, with addition of about 1 to about 150 ppm of TIPA, THEED, Quadrol, TEA, TBA, MEA, OA or DBA to 4HT making total of 100, 200 and 300 ppm of the composition so as to have 4HT:Amine in a weight ratio of 99:1, 98:2, 95:5, 90:10, 85:15, 80:20, 70:30 and 50:50, the efficiency of prior art additive composition consisting of 4HT to control and inhibit polymerization of styrene is, surprisingly and unexpectedly, generally improved.


As can be seen, when present composition comprises any one of the amines selected from a group consisting of N,N,N′,N′-Tetrakis(2-hydroxyethyl)ethylene-diamine) (THEED) and N,N,N′,N′-Tetrakis(2-hydroxypropyl)ethylene-diamine) (Quadrol), then efficiency for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene of the nitroxides is substantially improved, however, the improvement is not as substantial as for the composition comprising tris(2-hydroxypropyl)amine (TIPA). Therefore, as per most preferred embodiment of the present invention, tris(2-hydroxypropyl)amine (TIPA) is most preferred amine.


As can also be seen, when present composition comprises any one of the amines selected from a group consisting of triethanolamine (TEA), Tris[N-butylamine] (TBA), monoethanolamine (MEA), octyl amine (OA), dibutyl amine (DBA), then efficiency for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene of the nitroxides is improved, however, the improvement is not as substantial as for the composition comprising N,N,N′,N′-Tetrakis(2-hydroxyethyl)ethylene-diamine) (THEED) or N,N,N′,N′-Tetrakis(2-hydroxypropyl)ethylene-diamine) (Quadrol). Therefore, as per more preferred embodiment of the present invention, N,N,N′,N′-Tetrakis(2-hydroxyethyl)ethylene-diamine) (THEED) and N,N,N′,N′-Tetrakis(2-hydroxypropyl)ethylene-diamine) (Quadrol) are the more preferred amines.


As can be seen, dibutyl amine (DBA), surprisingly and unexpectedly, demonstrates better efficiency when used in compositions of dosages of about 200 ppm or more.


As can also be seen, when the composition comprises any one of the comparative amines selected from a group consisting of N,N,disec-butyl-para-phenylene diamine (UOP5), ethylene diamine (EDA), tetraethylenepentamine (TEPA), dipropyl amine (DPA), or diethanol amine (DEA), then efficiency for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene of the nitroxides is not improved. Therefore, in one embodiment, the present composition does not comprise any one of the amines selected from a group consisting of N,N,disec-butyl-para-phenylene diamine (UOP5), ethylene diamine (EDA), tetraethylenepentamine (TEPA), dipropyl amine (DPA), or diethanol amine (DEA). It may be noted that some of these amines result in very marginal improvement in efficiency of nitroxides, but same is not commercially viable.


It may be noted that, surprisingly and unexpectedly, with increase in concentration of amine, i.e. when about 20% or more of the amine is added to 4HT, the polymerization inhibition efficiency of present additive composition reduces marginally, the reasons for which are not know at present.


Accordingly, in view of above experimental data and analysis thereof, it can be concluded that only the additive compositions of the present invention comprising 4HT and amine selected from a group consisting of TIPA, THEED, Quadrol, TEA, TBA, MEA, OA and DBA, surprisingly and unexpectedly, result in improvement of control and polymerization inhibition efficiency of prior art additive composition consisting of 4HT, and these findings confirm synergistic effect of present compositions.

























TABLE III





Active

Active
















Dosage
Total
Dosage







4HT/


Ratio of
Dosage
4HT +


4HT/
4HT/
4HT/
4HT/
4HT/
Octyl
4HT/
4HT/
4HT/
4HT/
4HT/
4HT/


4HT:Amine
(ppm)
Amine
4HT
4HT/TIPA
THEED
Quadrol
TEA
MEA
TBA
amine
DPA
DEA
UOP5
DBA
EDA
TEPA































99:1
100
99 + 1
13.9
11.15
11.65
11.57
12.86
12.50
12.95
12.82
12.27
12.83
13.04
13.33
13.65
13.85


98:2
100
98 + 2
13.9
10.61
11.16
11.23
12.25
12.18
12.61
12.35
11.86
12.32
13.22
13.58
13.91
14.22


95:5
100
95 + 5
13.9
8.84
9.81
9.95
11.06
12.08
11.82
11.95
11.68
12.52
13.55
13.78
14.1
14.08


90:10
100
90 + 10
13.9
7.52
9.15
9.25
10.38
11.83
11.5
11.25
11.58
12.9
13.69
14.01
14.2
14.5


85:15
100
85 + 15
13.9
7.34
8.89
8.80
9.31
11.25
11.0
10.86
11.94
13.35
13.92
14.25
14.4
14.67


80:20
100
80 + 20
13.9
7.4
8.45
8.43
9.05
11.05
11.2
11.56
12.60
14.0
14.21
14.4
14.61
14.75


70:30
100
70 + 30
13.9
8.10
9.26
9.16
9.97
11.20
11.68
12.15
13.24
15.6
14.68
14.64
14.86
15.15


50:50
100
50 + 50
13.9
8.30
9.92
9.82
10.87
11.98
13.05
13.11
14.56
16.8
15.59
15.11
15.96
16.27
































TABLE IV







Active
















Active

Dosage


Dosage
Total
(ppm)








4HT/


Ratio of
Dosage
of 4HT +

4HT/
4HT/
4HT/
4HT/
4HT/
4HT/
4HT/
Octyl
4HT/
4HT/
4HT/
4HT/
4HT/


4HT:Amine
(ppm)
Amine
4HT
TIPA
THEED
Quadrol
TEA
MEA
DBA
TBA
amine
DPA
DEA
UOP5
EDA
TEPA































99:1
200
198 + 2
9.38
3.05
4.49
4.5
8.86
8.2
6.47
9.09
8.8
9.10
9.21
9.33
9.52
9.64


98:2
200
196 + 4
9.38
2.5
3.87
3.94
7.08
7.87
6.66
8.83
8.33
8.53
9.08
9.67
9.8
9.92


95:5
200
190 + 10
9.38
2.14
3.47
3.53
5.26
7.41
6.90
8.45
8.03
8.39
9.27
9.82
9.91
10.20


90:10
200
180 + 20
9.38
1.91
3.12
3.06
4.11
7.21
7.25
8.08
7.42
8.11
9.54
10.02
10.22
10.55


85:15
200
170 + 30
9.38
1.74
2.75
2.86
3.58
7.08
7.55
7.60
7.11
8.62
9.76
10.33
10.5
10.77


80:20
200
160 + 40
9.38
1.80
2.42
2.49
3.22
7.25
7.82
7.96
7.66
9.35
10.2
10.52
10.71
11.88


70:30
200
140 + 60
9.38
2.53
3.22
3.18
4.06
7.64
8.21
8.24
8.11
9.91
10.9
11.0
11.14
12.07


50:50
200
100 + 100
9.38
3.10
3.65
3.62
4.98
8.25
9.02
9.65
8.95
10.28
11.5
11.5
11.26
12.79
































TABLE V







Active
















Active

Dosage


Dosage
Total
(ppm) of







4HT/


Ratio of
Dosage,
4HT +

4HT/
4HT/
4HT/
4HT/
4HT/
4HT/
Octyl
4HT/
4HT/
4HT/
4HT/
4HT/
4HT/


4HT:Amine
ppm
Amine
4HT
TIPA
THEED
Quadrol
TEA
MEA
TBA
amine
DBA
UOP5
DEA
DPA
EDA
TEPA































99:1
300
297 + 3
5.1
1.35
2.28
2.23
4.74
3.95
4.8
4.53
4.15
5.05
5.06
4.91
5.2
5.5


98:2
300
294 + 6
5.1
1.07
1.50
1.55
4.05
3.24
4.09
3.92
3.53
5.24
4.95
4.63
5.64
5.75


95:5
300
285 + 15
5.1
0.88
1.41
1.44
3.22
3.08
3.78
3.8
3.30
5.62
5.56
4.23
6.08
6.17


90:10
300
270 + 30
5.1
0.77
1.17
1.25
2.44
2.84
3.5
3.29
3.15
5.90
5.77
4.05
6.20
6.45


85:15
300
255 + 45
5.1
0.62
0.95
1.02
2.23
3.04
2.7
2.92
3.04
7.51
6.10
4.35
6.34
6.62


80:20
300
240 + 60
5.1
0.51
0.79
0.83
1.95
3.55
3.25
3.2
3.41
7.7
7.5
4.65
6.91
7.09


70:30
300
210 + 90
5.1
0.68
1.09
1.12
2.55
4.22
3.68
3.56
3.9
8.9
8.8
5.26
8.18
8.96


50:50
300
150 + 150
5.1
0.75
1.70
1.66
3.22
4.82
4.36
4.33
4.55
9.9
9.7
6.55
9.26
10.05









Experiment 6

The above Main Experiment was also carried out with round bottom reactor for prior art additive composition consisting of 4HT; and present additive composition comprising 4HT and TIPA, and it has been found that with addition of present amine additives, the efficiency of prior art additive composition to control and inhibit polymerization of styrene is, surprisingly and unexpectedly, generally improved even in round bottom reactor.













TABLE VI








Dosage,





active,



Composition
ppm
% Polymer




















4HT
100
13.27



4HT
200
9.11



4HT
300
6.79



4HT
400
2.32



4HT + TIPA (90:10)
100
10.17



4HT + TIPA (90:10)
200
4.42



4HT + TIPA (95:5)
200
5.15










The above experimental data confirms the synergistic effects, and the surprising and unexpected technical effects and advantages of the additive composition of the present invention over the prior art additive composition and comparative compositions.


All of above findings confirm synergistic, surprising and unexpected effects of present composition at lower as well as at higher temperatures.


All of above findings also confirm that there is successive increase in efficiency of prior art additive to control and inhibit polymerization of styrene.


All of above findings also confirm that present composition is capable of achieving far better efficiency to control and inhibit polymerization of styrene with same dosage of the prior art additive, meaning thereby, the present invention results in economical and environmental benefits.


Above experimental results confirm that presently provided composition is far superior than prior art additive, and hence, has technical advantages and surprising effects over the prior art additive.


It may be noted that the term “about” as employed herein is not intended to enlarge scope of claimed invention, but has been incorporated only to include experimental errors permissible in the field of the art.

Claims
  • 1. Additive composition for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene comprising: (a) one or more of nitroxide (i.e. nitroxyl) compounds; andcharacterized in that the said composition further comprises one or more of(b) amines, wherein said amine is aliphatic amine, and wherein the aliphatic amine is tertiary amine.
  • 2. Additive composition as claimed in claim 1, wherein said amine is selected from the group comprising hydroxyl alkyl tertiary amine, ethylene oxide treated amine, propylene oxide treated amine, and tertiary alkyl amine, or combination thereof.
  • 3. The additive composition as claimed in claim 1, wherein said hydroxyl alkyl tertiary amine is tris(2-hydroxypropyl)amine (TIPA).
  • 4. The additive composition as claimed in claim 1, wherein said ethylene oxide treated amine is N,N,N′,N′-Tetrakis(2-hydroxyethyl)ethylene-diamine) (THEED).
  • 5. The additive composition as claimed in claim 1, wherein said propylene oxide treated amine is N,N,N′,N′-Tetrakis(2-hydroxypropyl)ethylene-diamine) (Quadrol).
  • 6. The additive composition as claimed in claim 1, wherein said hydroxyl alkyl tertiary amine is triethanolamine (TEA).
  • 7. The additive composition as claimed in claim 1, wherein said tertiary alkyl amine is Tris[N-butylamine](TBA).
  • 8. Additive composition for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene comprising: (a) one or more of nitroxide (i.e. nitroxyl) compounds; andcharacterized in that the said composition further comprises(b) one or more of amines, wherein said amine is aliphatic amine, and wherein the aliphatic amine is selected from a group consisting of primary and secondary amines.
  • 9. Additive composition as claimed in claim 8, wherein said primary amine is selected from a group comprising hydroxyl alkyl primary amine and alkyl primary amine.
  • 10. The additive composition as claimed in claim 8, wherein said secondary amine is alkyl secondary amine.
  • 11. The additive composition as claimed in claim 8, wherein said hydroxyl alkyl primary amine is monoethanolamine (MEA).
  • 12. The additive composition as claimed in claim 8, wherein said alkyl primary amine is octyl amine (OA).
  • 13. The additive composition as claimed in claim 8, wherein said alkyl secondary amine is dibutyl amine (DBA).
  • 14. The additive composition as claimed in claim 1, wherein said composition comprises: a) about 40 to about 99.75% by weight of I) said nitroxide (i.e. nitroxyl) compounds; andb) about 0.25 to about 60% by weight of II) said amines, or mixture thereof.
  • 15. The additive composition as claimed in claim 1, wherein about 0.01 to about 2000 ppm of said composition is added to aromatic vinyl monomers stream based on weight of monomer.
  • 16. The additive composition as claimed in claim 1, wherein said nitroxide (i.e. nitroxyl) compound is selected from the group comprising di-tert-butylnitroxyl, 1-oxyl-2,2,6,6-tetramethylpiperidine, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-ol, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-one, and derivatives thereof; and di-nitroxides and derivatives comprising bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)sebacate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)succinate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)adipate, and mixture thereof.
  • 17-18. (canceled)
  • 19. The additive composition as claimed in claim 1, wherein said composition does not comprise aromatic nitro compound.
  • 20. A method for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene by adding additive composition as claimed in claim 1 to monomers stream, wherein said composition comprises: (a) one or more of nitroxide (i.e. nitroxyl) compounds; andcharacterized in that the said composition further comprises one or more of(b) said amines; andsaid composition is added to said monomers.
  • 21. The method as claimed in claim 20, wherein about 0.01 to about 2000 ppm of said composition is added to aromatic vinyl monomers stream based on weight of monomer.
  • 22. A method of using additive composition as claimed in claim 1 for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene, wherein said composition comprises: (a) one or more of nitroxide (i.e. nitroxyl) compounds; andcharacterized in that the said composition further comprises one or more of(b) said amines,and said monomers are treated with said composition.
  • 23. The method as claimed in claim 22, wherein said aromatic vinyl monomers stream is treated with about 0.01 to about 2000 ppm of said composition based on weight of monomer.
  • 24. A method for preparing additive composition as claimed in claim 1 for controlling and inhibiting polymerization of aromatic vinyl monomers including styrene, wherein the method comprises: (A) mixing one or more of said nitroxide (i.e. nitroxyl) compounds,characterized in that said nitroxide (i.e. nitroxyl) compound or mixture thereof is further mixed with one or more of(B) said amines.
  • 25. The method as claimed in claim 24, wherein said one or more of nitroxide compounds, and said one or more amines are added to monomer stream individually.
  • 26. The method as claimed in claim 20, wherein said composition is used over a range of temperature varying from about 50 degree C. to about 180 degree C.
  • 27. The additive composition as claimed in claim 8, wherein said composition comprises: a) about 40 to about 99.75% by weight of I) said nitroxide (i.e. nitroxyl) compounds; andb) about 0.25 to about 60% by weight of II) said amines, or mixture thereof.
  • 28. The additive composition as claimed in claim 8, wherein about 0.01 to about 2000 ppm of said composition is added to aromatic vinyl monomers stream based on weight of monomer.
  • 29. The additive composition as claimed in claim 8, wherein said nitroxide (i.e. nitroxyl) compound is selected from the group comprising di-tert-butylnitroxyl, 1-oxyl-2,2,6,6-tetramethylpiperidine, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-ol, 1-oxyl-2,2,6,6-tetramethylpiperidin-4-one, and derivatives thereof; and di-nitroxides and derivatives comprising bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)sebacate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)succinate, bis(1-oxyl-2,2,6,6-tetramethylpiperidin-4-yl)adipate, and mixture thereof.
  • 30. The additive composition as claimed in claim 8, wherein said composition does not comprise aromatic nitro compound.
  • 31. A method for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene by adding additive composition as claimed in claim 8 to monomers stream, wherein said composition comprises: (a) one or more of nitroxide (i.e. nitroxyl) compounds; andcharacterized in that the said composition further comprises one or more of(b) said amines; andsaid composition is added to said monomers.
  • 32. The method as claimed in claim 31, wherein about 0.01 to about 2000 ppm of said composition is added to aromatic vinyl monomers stream based on weight of monomer.
  • 33. A method of using additive composition as claimed in claim 8 for controlling and inhibition of polymerization of aromatic vinyl monomers including styrene, wherein said composition comprises: (a) one or more of nitroxide (i.e. nitroxyl) compounds; andcharacterized in that the said composition further comprises one or more of(b) said amines,and said monomers are treated with said composition.
  • 34. The method as claimed in claim 33, wherein said aromatic vinyl monomers stream is treated with about 0.01 to about 2000 ppm of said composition based on weight of monomer.
  • 35. A method for preparing additive composition as claimed in claim 8 for controlling and inhibiting polymerization of aromatic vinyl monomers including styrene, wherein the method comprises: (A) mixing one or more of said nitroxide (i.e. nitroxyl) compounds,characterized in that said nitroxide (i.e. nitroxyl) compound or mixture thereof is further mixed with one or more of(B) said amines.
  • 36. The method as claimed in claim 35, wherein said one or more of nitroxide compounds, and said one or more amines are added to monomer stream individually.
  • 37. The method as claimed in claim 22, wherein said composition is used over a range of temperature varying from about 50 degree C. to about 180 degree C.
  • 38. The method as claimed in claim 31, wherein said composition is used over a range of temperature varying from about 50 degree C. to about 180 degree C.
  • 39. The method as claimed in claim 33, wherein said composition is used over a range of temperature varying from about 50 degree C. to about 180 degree C.
Priority Claims (1)
Number Date Country Kind
3383/MUM/2011 Dec 2011 IN national
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a filing under 35 U.S.C. 371 of International Application No. PCT/IN2012/000758 filed Nov. 21, 2012, entitled “Amine and Nitroxide Based Additive Composition for Control and Inhibition of Polymerization of Styrene, and Method of Use Thereof,” which claims priority to Indian Patent Application No. 3383/MUM/2011 filed Dec. 2, 2011, which applications are incorporated by reference herein in their entirety.

PCT Information
Filing Document Filing Date Country Kind 371c Date
PCT/IN2012/000758 11/21/2012 WO 00 5/30/2014