Claims
- 1. A process of reducing the free aldehyde content of an amino resin, said process comprising steps of:
- (i) providing an initial amino resin dispersion containing from 0.10 to about 0.35% by weight based on the weight of the initial dispersion of free aldehyde;
- (ii) mixing, either sequentially or simultaneously, with the initial amino resin dispersion provided in step (i):
- (a) an amount of modifying reagent molecules that are soluble in the initial amino resin dispersion and include a structure according to formula I: ##STR4## in which each of Q.sup.1 and Q.sup.3 independently is one of .dbd.O, .dbd.NH, or .dbd.N; Q.sup.2 is C or N, such that the ratio of the stoichiometric equivalent as acetoacetamide of the total amount of said modifying reagent added to the content of free aldehyde of the resin provided in step (i) is from 0.5:1.0 to 50:1.0; and
- (b) an amount of a component selected from molecules that do not belong to component (a) but do contain at least one amino moiety that can react with an aldehyde molecule to form a single molecule product in which the nitrogen atom from the amino moiety has become covalently bonded to the carbon atom from the aldehydo moiety, such that the ratio by weight of the total stoichiometric equivalent as urea of component (b) to the total stoichiometric equivalent as acetoacetamide of component (a) is from about 1:100 to about 1.0:0.40; and
- (iii) allowing the mixture formed in step (ii) to undergo spontaneous chemical reaction, at a temperature at which the mixture is liquid, to produce a modified amino resin dispersion in which the concentration of free aldehyde in the modified amino resin dispersion is not greater than about 0.20% by weight based on the weight of the modified amino resin dispersion and is not greater than about 80% by weight of the concentration of free aldehyde in the initial amino resin dispersion provided in step (i).
- 2. A process according to claim 1 of reducing the free formaldehyde content of a melamine-formaldehyde resin dispersion in water, said process comprising steps of:
- (i) providing an initial aqueous resin dispersion containing from about 1 to about 20% by weight based on the weight of the initial dispersion of dispersed melamine-formaldehyde polymer solids and from about 0.10 to about 0.35% by weight based on the weight of the initial dispersion of free formaldehyde;
- (ii) mixing with the initial aqueous resin dispersion provided in step (i) an amount of component (ii) (a) and an amount of component (ii) (b) such that the ratio by weight of the total stoichiometric equivalent as urea of component (ii) (b) to the total stoichiometric equivalent as acetoacetamide of component (ii) (a) is from about 1:100 to about 1.0:0.40; and
- (iii) allowing the mixture formed in step (ii) to undergo spontaneous chemical reaction, at a temperature at which the mixture is liquid, to produce a modified resin dispersion in which the concentration of free formaldehyde is not greater than about 0.20% by weight based on the weight of the modified resin dispersion and is not greater than about 80% by weight of the concentration of free formaldehyde in the initial resin dispersion provided in step (i).
- 3. A process according to claim 2, wherein: the dispersion provided in step (i) contains from about 6.0 to about 12.0% by weight based on the weight of the initial dispersion of dispersed melamine-formaldehyde polymer solids and has a pH in the range from about 1.5 to about 2.3; the ratio of the stoichiometric equivalent as acetoacetamide of component (ii) (a) to the free formaldehyde content of the resin provided in step (i) is from about 1.2:1.0 to about 11:1.0; the ratio by weight of the total stoichiometric equivalent as urea of component (ii) (b) to the total stoichiometric equivalent as acetoacetamide of component (ii) (a) is from about 1:20 to about 1.0:1.2; the free formaldehyde content of the modified resin dispersion is not greater than about 0.11% by weight based on the weight of the modified resin dispersion; and the pH of the modified resin dispersion is from about 1.5 to about 2.3.
- 4. A process according to claim 3, wherein: the dispersion provided in step (i) contains from about 7.0 to about 10.0% by weight based on the weight of the initial dispersion of dispersed melamine-formaldehyde polymer solids; the ratio of the total stoichiometric equivalent as acetoacetamide of component (ii) (a) to the free formaldehyde content of the resin provided in step (i) is from about 1.3:1.0 to 8.0:1.0; the ratio by weight of the total stoichiometric equivalent as urea of component (ii) (b) to the total stoichiometric equivalent as acetoacetamide of component (ii) (a) is from about 1:9.0 to about 1.0:2.8; and the free formaldehyde content of the modified resin dispersion is not greater than about 0.10% by weight based on the weight of the modified dispersion.
- 5. A process according to claim 4, wherein the dispersion provided in step (i) contains from about 8.0 to about 9.0% by weight based on the weight of the initial dispersion of dispersed melamine-formaldehyde polymer solids; the ratio of the total stoichiometric equivalent as acetoacetamide of component (ii) (a) to the free formaldehyde content of the resin provided in step (i) is from about 1.3:1.0 to about 7.0:1.0; the ratio by weight of the total stoichiometric equivalent as urea of component (ii) (b) to the total stoichiometric equivalent as acetoacetamide of component (ii) (a) is from about 1.0:9.0 to about 1.0:2.4; and the free formaldehyde content of the modified resin dispersion is not greater than about 0.095% by weight based on the weight of the modified dispersion.
- 6. A process according to claim 5, wherein the ratio of the total stoichiometric equivalent as acetoacetamide of component (ii) (a) to the free formaldehyde content of the resin provided in step (i) is from about 1.5:1.0 to about 1.8:1.0, component (ii) (b) is urea, the ratio of urea to the total stoichiometric equivalent as acetoacetamide of component (ii) (a) is from about 1.0:8.0 to about 1.0:4.0, the free formaldehyde content of the modified resin dispersion is not greater than about 0.090% by weight based on the weight of the modified dispersion, and the pH of the modified resin dispersion is from about 1.7 to about 2.1.
- 7. A process of detackifying paint entrained in a first aqueous liquid composition by mixing with said first aqueous composition a detackifying effective amount of a second aqueous liquid composition which is a dispersion consisting essentially of water and:
- (A') from about 1 to about 20% by weight based on the weight of the dispersion of dispersed melamine-formaldehyde polymer solids;
- (B') from about 0.005 to about 0.20% by weight based on the weight of the dispersion of free formaldehyde;
- (C') at least one product of reaction between free formaldehyde and water soluble modifying reagent molecules selected from the group consisting of diketo compounds and their nitrogen analogs; and
- (D') at least one product of reaction between free formaldehyde and molecules that are not diketo compounds or their nitrogen analogs but do contain at least one formaldehyde-reactive amino moiety; and, optionally one or both of the following:
- (E') unreacted modifying reagent molecules selected from the group consisting of diketo compounds and their nitrogen analogs; and
- (F') unreacted molecules that are not diketo compounds or their nitrogen analogs but do contain at least one formaldehyde-reactive amino moiety;
- the total stoichiometric equivalent as acetoacetamide value in said dispersion being from about 0.05 to about 17.5% by weight based on the weight of said dispersion; said dispersion having a total stoichiometric equivalent as urea value and a total stoichiometric equivalent as acetoacetamide value such that the ratio of the total stoichiometric equivalent as urea value to the total stoichiometric equivalent as acetoacetamide value is at least about 1.0:30.
- 8. A process according to claim 7, wherein in said second aqueous liquid composition which is a dispersion the amount of free formaldehyde in the dispersion is from about 0.01 to about 0.16% by weight based on the weight of said dispersion, the total stoichiometric equivalent as acetoacetamide is from about 0.08 to about 6% by weight based on the weight of said dispersion, the ratio of the total stoichiometric equivalent as urea to the total stoichiometric equivalent as acetoacetamide is from about 1.0:30 to 1.0:1.6, and the ratio of the amount of said second aqueous liquid composition which is a dispersion added to the amount of paint entrained in said first aqueous liquid composition is from about 0.05:1.0 to about 1.5:1.0.
- 9. A process according to claim 8, wherein in said second aqueous liquid composition which is a dispersion the concentration of melamine-formaldehyde polymer solids in the dispersion is from about 6.0 to about 12.0 by weight based on the weight of the dispersion, the amount of free formaldehyde in the dispersion is from about 0.022 to about 0.12% by weight based on the weight of said dispersion, the total stoichiometric equivalent as acetoacetamide is from about 0.15 to about 2.0% by weight based on the weight of said dispersion, the ratio of the total stoichiometric equivalent as urea to the total stoichiometric equivalent as acetoacetamide is from about 1.0:15 to 1.0:2.0; and the ratio of the amount of said second aqueous liquid composition which is a dispersion added to the amount of paint entrained in said first aqueous liquid composition is from about 0.09:1.0 to about 1.0:1.0.
- 10. A process according to claim 9, wherein in said second aqueous liquid composition which is a dispersion the amount of free formaldehyde in the dispersion is from about 0.027 to about 0.10% by weight based on the weight of said dispersion, the total stoichiometric equivalent as acetoacetamide is from about 0.22 to about 1.8% by weight based on the weight of said dispersion the ratio of the total stoichiometric equivalent as urea to the total stoichiometric equivalent as acetoacetamide is from about 1.0:12.0 to 1.0:2.8; and the ratio of the amount of said second aqueous liquid composition which is a dispersion added to the amount of paint entrained in said first aqueous liquid composition is from about 0.11:1.0 to about 0.70:1.0.
- 11. A process according to claim 10, wherein in said second aqueous liquid composition which is a dispersion the concentration of melamine-formaldehyde polymer solids in the dispersion is from about 6.0 to about 10.0% by weight based on the weight of said dispersion, the amount of free formaldehyde in the dispersion is from about 0.030 to about 0.095% by weight based on the weight of said dispersion, the total stoichiometric equivalent as acetoacetamide is from about 0.22 to about 1.5% by weight based on the weight of said dispersion, and the ratio of the total stoichiometric equivalent as urea of component (ii) (b) to the total stoichiometric equivalent as acetoacetamide is from about 1.0:9.0 to 1.0:4.0; and the ratio of the amount of said second aqueous liquid composition which is a dispersion added to the amount of paint entrained in said first aqueous liquid composition is from about 0.13:1.0 to about 0.40:1.0.
- 12. A process according to claim 11, wherein in said second aqueous liquid composition which is a dispersion the concentration of melamine-formaldehyde polymer solids in the dispersion is from about 6.8 to about 9.0% by weight based on the weight of said dispersion, the amount of free formaldehyde in the dispersion is from about 0.030 to about 0.090% by weight based on the weight of said dispersion, the total stoichiometric equivalent as acetoacetamide is from about 0.27 to about 1.0% by weight based on the weight of said dispersion the ratio of the total stoichiometric equivalent as urea to the total stoichiometric equivalent as acetoacetamide is from about 1.0:8.0 to 1.0:4.8; and the ratio of the amount of said second aqueous liquid composition which is a dispersion added to the amount of paint entrained in said first aqueous liquid composition is from about 0.14:1.0 to about 0.31:1.0.
- 13. A process according to claim 12, wherein in said second aqueous liquid composition which is a dispersion, the concentration of melamine-formaldehyde polymer solids is from about 6.8 to about 8.5% by weight based on the weight of said dispersion, the total stoichiometric equivalent as acetoacetamide is from about 0.27 to about 0.50% by weight based on the weight of said dispersion, and the ratio of the total stoichiometric equivalent as urea to the total stoichiometric equivalent as acetoacetamide is from about 1.0:7.6 to 1.0:6.0; and the ratio of the amount of said second aqueous liquid composition which is a dispersion added to the amount of paint entrained in said first aqueous liquid composition is from about 0.15:1.0 to about 0.28:1.0.
CROSS-REFERENCE TO RELATED APPLICATIONS
This application is a continuation-in-part of application Ser. No. 08/219,058 filed Mar. 29, 1994, now U.S. Pat. No. 5,454,516 which was a continuation-in-part of application Ser. No. 970,727 filed Nov. 3, 1992 and now abandoned.
US Referenced Citations (3)
Non-Patent Literature Citations (2)
Entry |
CHEMetrics Vacu-Vials.RTM. self-filling ampoules for photometric analysis No. K-4203. |
Eastman Chemicals BKB (beta-Ketobutyramide or Acetoscetemide). |
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
215098 |
Mar 1994 |
|
Parent |
970727 |
Nov 1992 |
|