Amorphous carbon coated tool and fabrication method thereof

Abstract

An amorphous carbon coated tool includes a base material of WC base cemented carbide, and an amorphous carbon film formed on this base material. The cobalt content in the base material is at least 12% by mass. The maximum thickness of the amorphous carbon film is at least 0.05 μm and not more than 0.5 μm at the cutting edge. The amorphous carbon film is deposited with graphite as the source material by physical vapor deposition in an atmosphere substantially absent of hydrogen. The amorphous carbon film coated tool superior in wear resistance and adhesion resistance is preferably applicable to rotating tools such as drills, end mills and reamers, indexable inserts used for milling cutters and turning tools, and cutting-off tools such as cutters, knives, or slitters.

Description

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a tool having a wear-resistant and adhesion-resistant amorphous carbon film formed at the surface of rotating tools (drills, end mills, reamers, and the like), an indexable insert used for milling cutters and turning tools, and cutting-off tools (cutters, knives, slitters and the like). The present invention also relates to a method of fabricating such a tool.

[0003] 2. Description of the Background Art

[0004] The conventional requirements with respect to cutting tools include the capability of increasing the lifetime of the tool by minimizing any damage at its surface and carrying out machining at high efficiency as well as finishing the workplace with high quality (maintaining the surface configuration, the hardness of the parent material, the dimension accuracy and the like).

[0005] Recently, there is a strong demand for the development of a tool that reduces the cutting resistance and a tool without degradation in the lifetime and cutting efficiency even if the amount of oil agents for cutting is reduced from the standpoint of protecting the environment and saving energy.

[0006] The material of the workpiece now includes a variety of types. In the case where the workpiece includes soft metal such as aluminum alloy, a non-ferrous metal such as titanium, magnesium, or copper, an organic material, or a material including hard particles such as graphite, or in the case of working on a printed circuit board or bimetallic cutting of an iron type material and aluminum, problems are noted such as residuals adhering to the cutting edge of the cutting tool to increase the cutting resistance, and, in some cases, cause chipping at the cutting edge. The wear of the tool used on such specific workpieces has become more significant.

[0007] The demand for reducing the cost drastically without degrading the performance is strong in the field of metal machining.

[0008] In the specific field of working on aluminum, aluminum alloy, or organic material, the diamond tool has been traditionally used. As to such tools having a diamond film formed on the base, the growing rate of the diamond film differs greatly depending upon the crystal orientation. The surface asperity is so great that the complex shape of the tool must be polished if the tool is to be used for high-precision processing.

[0009] Since diamond is the hardest available material, grinding of a diamond film requires the usage of diamond that is extremely expensive. This attributes to the increase in cost.

[0010] Furthermore, since a crystal growth speed varies in the crystal direction drastically, to get a smooth grinding surface, a film of 20-30 μm in thickness must be prepared in the case of a diamond film, as compared to the general thickness of 2-3 μm for a ceramics coated film such as TiN, obtained by PVD (Physical Vapor Deposition) coating. Formation of a diamond film is carried out while graphite that is deposited at the same time is removed by etching. Therefore, the film growth rate becomes as slow as less than {fraction (1/10)} the rate of normal PVD coating. There was a problem that the fabrication cost including the coating process is extremely high.

[0011] As to tools made by brazing a diamond sintered compact on a base, it is difficult to fabricate the tools of complicated shape or the tools as fine as several millimeters in diameter.

[0012] Japanese Patent Laying-Open No. 2000-176705 discloses a tool member having a hard material including TiN, TiCN, TiAlN, Al2O3 or a combination thereof coated, and then further coated with a hard carbon type lubricating film. In order to form an economic hard carbon type lubricated film that has stable durability and suitable for mass production, the inventors in this publication propose formation of an intermediate layer of a component including silicon and carbon or silicon, carbon and nitrogen, followed by a formation of a silicon layer of at least 0.02 μm and not more than 0.5 μm in thickness under and in contact with the bottom of the intermediate layer.

[0013] The hard carbon coated film at the outermost surface layer disclosed in this publication inevitably includes hydrogen atoms in the film since formation is conducted through ion plating and plasma CVD (Chemical Vapor Deposition) using hydrocarbon type gas. It is generally known that hydrogen atoms in hard carbon film are desorbed from the film at the temperature of at least approximately 350° C. in the atmosphere. Following desorption of hydrogen, the hard carbon coated film is modified into graphite. The hardness is significantly degraded. Such a coated film is not suitable for usage in a severe cutting environment.

SUMMARY OF THE INVENTION

[0014] In view of the foregoing, a main object of the present invention is to provide an amorphous carbon coated tool less vulnerable to adhesion of residual and chipping at the cutting edge when used in cutting soft metal, non-ferrous metal, organic material, material including hard particles, printed circuit boards, and in bi-metallic cutting of iron base material and soft metal material, and having temperature increase at the cutting edge suppressed by coating with amorphous carbon that has high heat conductivity to allow usage even under a severe cutting environment such as in dry cutting and high speed machining.

[0015] Another object of the present invention is to provide a method of fabricating such an amorphous carbon coated tool.

[0016] The above objects of the present invention are achieved by specifying the component of the base material and the thickness of the amorphous carbon film.

[0017] The amorphous carbon coated tool of the present invention includes a base material of WC base cemented carbide, and an amorphous carbon coated film covering at least the cutting edge on the base material. The base material has a cobalt content of not more than 12% by mass. The amount of hydrogen in the amorphous carbon film is not more than 5% by mass. The maximum film at the cutting edge of the amorphous carbon film is at least 0.05 μm and not more 0.5 μm.

[0018] The amorphous carbon coated tool of the present invention includes a base material of WC base cemented carbide, and an amorphous carbon coated film covering at least the cutting edge on the base material. The base material has a cobalt content of not more than 12% by mass. The amorphous carbon film is formed by physical vapor deposition with graphite as the source material under an atmosphere that is substantially absent of hydrogen. The maximum thickness at the cutting edge of the amorphous carbon film is at least 0.05 μm and not more 0.5 μm.

[0019] The method of fabricating an amorphous carbon coated tool of the present invention includes the steps of supporting in a vacuum vessel a base material of WC base cemented carbide, and applying zero or negative direct-current bias to the base material and vaporizing the graphite that is the source material to form an amorphous carbon film. The maximum thickness of the amorphous carbon film at the cutting edge is controlled to be 0.05 to 0.5 μm.

BRIEF DESCRIPTION OF THE DRAWINGS

[0020] FIG. 1 is a schematic diagram of a film deposition apparatus of the present invention.

[0021] FIG. 2 is a sectional view of a cutting edge of a tool of the present invention.

[0022] FIG. 3 represents the Raman spectrum of an amorphous carbon coated film of the present invention.

[0023] FIG. 4 represents a Raman spectrum of a conventional amorphous carbon coated film.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0024] The structural elements of the present invention will be described in detail hereinafter.

[0025] WC Base Cemented Carbide Base Material

[0026] The WC base cemented carbide is formed of a hard phase with tungsten carbide (WC) as the main component, and a bonded phase with iron group metal such as cobalt as the main component. The reason why the amount of cobalt included in the WC base cemented carbide is defined is set forth below. If the amount of cobalt is great, the toughness of the base material is increased to improve the chipping resistance property at the cutting edge of the cemented base material. However, if a great external force is applied on the cutting edge, the hard amorphous carbon film cannot follow the deformation of the base material. The amorphous carbon film will peel off from the cemented base material at the interface. In order to stabilize the cutting performance without any delamination, the amount of cobalt is preferably set to not more than 12% by mass. Further preferably, the cobalt content in the base material is at least 3% by mass and not more than 7% by mass.

[0027] The average crystal grain size of tungsten carbide after the base material is subjected to sintering is preferably at least 0.1 μm and not more than 3 μm. Any particle smaller than 0.1 μm in average crystal grain size cannot be easily identified by the current evaluation method. If the average crystal grain size exceeds 3 μm, the large tungsten carbide particles in the base material will fall off to induce large chipping when the film is abraded.

[0028] Also, preferably in the base material is included at least 0.01% by mass and not more than 3% by mass a compound formed of at least one type of element selected from the group consisting of a metal element from Groups IVa, Va, and VIa of the periodic table, and at least one type of element selected from the group consisting of carbon and nitrogen. By containing such elements, the crystal particle growth of tungsten carbide during sintering can be suppressed. A specific example of preferable added compound includes (Ta, Nb) C, VC, Cr2C2 and NbC.

[0029] Amorphous Carbon Film

[0030] An amorphous carbon film includes films such as a hard carbon film, diamond-like carbon film, DLC film, and a-C:H, i-carbon film. The amorphous carbon film of the present invention is characterized in the following issues.

[0031] Deposition Method

[0032] In the present invention, an amorphous carbon film is formed with graphite as the source material by physical vapor deposition under an atmosphere absent of hydrogen. The film has a high hardness equal to that of diamond, and superior in wear resistance for a cutting tool. An amorphous carbon film with hydrogen carbon as the source material will include hydrogen, and differs from the amorphous carbon film of the present invention.

[0033] The amorphous carbon film of the present invention is formed only of carbon atoms with the exception of impurities inevitably included during film deposition. Since the ratio of sp3 bonding becomes higher than that of an amorphous carbon film including hydrogen, the hardness is improved. Also, the oxidation resistance is improved up to approximately 600° C. equal to that of diamond. Even if film deposition is effected under an atmosphere that if substantially absent of hydrogen, a slight amount of hydrogen, not more than 5% by atom, may be included in the resulting amorphous carbon film. It is likely that this is caused by the hydrogen and moisture remaining in the film deposition apparatus being introduced into the amorphous carbon film due to the vacuum during deposition.

[0034] Regarding the physical vapor deposition method with graphite as the original material, the cathode arc ion plating method, laser abrasion method, sputtering method and the like generally used in the field of industry are suitable by virtue of the high deposition rate. The problem of the fabrication cost noted in the case where the conventional diamond film is used is eliminated. The cathode arc ion plating method is particularly preferable for film deposition from the standpoint of the adherence and the hardness of the coated film. It is noted that the ionization of the source material is high in the cathode arc ion plating method. Therefore, an amorphous carbon film is formed by directing carbon ions onto the base material. Thus, a film of high sp3 bond ratio that is compact and that has high hardness is obtained. Accordingly, the lifetime of the tool can be improved greatly.

[0035] It is desirable that temperature of the base material on the occasion of forming film is more than 50° C., and less than 350° C., more desirably less than 200° C., and most desirably less than 150° C. When temperature of the base material exceeds 350° C., graphite tends to be easily deposited. The temperature of the base material rises when carbon ion is irradiated on the base material to form the amorphous carbon film. Therefore, the temperature may rise to the efficient degree without heating. The temperature of the base material can also be adjusted by heating and cooling.

[0036] Macro-Particle Density

[0037] Hard particles called “macro-particle” are present at the surface of an amorphous carbon film formed by cathode arc ion plating. A smaller macro-particle density at the surface of the film is desirable since the cutting resistance will become lower. The macro-particle density is not more than 3×105 particles/mm2, more preferably not more than 1.5×105 particles/mm2. The optimum macro-particle density is of course 0 particle/mm2. If the macro-particle density is greater than 3×105 particles/mm2, the residual of the workpiece will adhere to the macro-particles to increase the cutting resistance.

[0038] The density of the macro-particles can be evaluated by observation through an SEM (Scanning Electron Microscope). In order to facilitate observation of the macro-particles, SEM observation should be conducted after vapor deposition of noble metal such as Pt or Pd on the surface of the sample by ion-sputtering. The density is to be obtained by counting the number of macro-particles on a photograph of the sample surface taken at the magnification of at least 1000 times.

[0039] FIG. 2 is a sectional view of an amorphous carbon coated plane 20 to show the growth of a macro-particle 21. Amorphous carbon 20 is applied on a cutting edge 23 of a tool. Graphite particles 22 float and adhere to the coated plane during the process. Round particles 21 of various diameters can be observed at the surface through an SEM. However, such particles are not desirable in the present invention. It is assumed that graphite particles 22 are present at various thickness sites of amorphous carbon 20 as shown in FIG. 2, since graphite particles 22 are scattered in the film deposition process.

[0040] Furthermore, in order to improve the surface roughness of the amorphous carbon film, appropriate measures to prevent scattering of particles from the graphite material can be taken. For example, growing a film through low energy or using a filter by a magnetic field can be used.

[0041] Surface Roughness

[0042] The surface roughness of the amorphous carbon film is desirably at least 0.002 μm and not more than 0.05 μm in Ra representation defined by the standards of JIS B0601. From the standpoint of a cutting tool, the surface roughness Ra should be as small as possible. In practice, a surface roughness Ra of zero cannot be achieved. It is found that the adhesion at the cutting edge is improved to increase the cutting performance when Ra is 0.05 μm or below as a result of various cutting experiments. Furthermore, the surface roughness is preferably at least 0.02 μm and not more than 0.5 μm in Ry representation defined by the standards of JIS B0601. If Ry exceeds 0.5 μm, any projection on the amorphous carbon film will become the adhesion origin of residuals to result in higher cutting resistance.

[0043] Thickness

[0044] The reason why the maximum film thickness of the amorphous carbon film at the cutting edge of a tool is set to 0.05 μm to 0.5 μm is set forth below. If the maximum film thickness is less than 0.05 μm, the wear resistance is degraded. If the maximum film thickness exceeds 0.5 μm, the internal stress accumulated at the coated film will be increased to facilitate delamination, or cause chipping of the coated film. By setting the film thickness to not more than 0.5 μm, the size and density of the macro-particles at the surface can be reduced. There is the advantage that the surface roughness can be suppressed to not more than 0.05 μm in Ra representation and not more than 0.5 μm in Ry representation. The amorphous carbon film is thicker at the cutting edge of the tool as indicated by T in FIG. 2. The performance is improved by reducing this thickness. Thus, the maximum thickness T at the cutting edge of the amorphous carbon film corresponding to cutting is preferably at least 0.05 μm and not more than 0.25 μm from the standpoint of lower adhesion.

[0045] Hardness

[0046] The Knoop hardness of the amorphous carbon film is preferably at least 20 GPa and not more than 50 GPa. If the hardness is lower than 20 GPa, the wear resistance is degraded. If the hardness exceeds 50 GPa, the chipping resistance at the cutting edge is reduced. Further preferably, the Knoop hardness of the amorphous carbon film is at least 25 GPa and not more than 40 GPa.

[0047] Raman Spectrum

[0048] It is extremely difficult to identify the film structure of the amorphous carbon film due to the amorphous characteristic thereof. As a result of evaluating various amorphous carbon films, it was found that there is difference in the obtained Raman spectrum reflecting the change in structure by Raman spectroscopic analysis.

[0049] FIG. 3 represents the Raman spectrum of the amorphous carbon of the present invention whereas FIG. 4 represents the Raman spectrum of conventional amorphous carbon that includes hydrogen. These spectra are obtained by Raman spectroscopic analysis using argon gas laser having a wavelength of 514.5 nm. In FIG. 4, the solid line indicates the measured result. A bulge is observed in the vicinity of 1340 cm−1. There is no peak in the vicinity of 700 cm−1.

[0050] In order to divide the obtained spectrum into two, the background is removed from the spectral waveform. Assuming that the spectral with a bulge has two Gaussian functions added, approximation is conducted by the nonlinear least-square method to obtain two separated peaks. The chain dotted line indicates the result. The height of the peak with the center about 1340 cm−1, is indicated by I1340 whereas the height of the peak about 1560 cm−1 is indicated by I1560. Referring to the Raman spectrum of the present invention shown in FIG. 3, a bulge in the vicinity of 1340 cm−1 is not easily perceivable in the solid line. There is a wide peak in the vicinity of 700 cm−1. The chain dotted line in FIG. 3 shows the peak separation result carried out in a manner similar to that described above. It is appreciated that the height of the peak of I1340 is lower than that of FIG. 3. The height of the peak in the vicinity of 700 cm−1 is indicated by I700. Similarly, the value corresponding to integration of respective peaks is represented as, for example, S700.

[0051] The total of three peaks are observed in the amorphous carbon film of the tool of the present invention, i.e. between wave number 400 cm−1 to 1000 cm−1, in the vicinity of 1340 cm−1, and in the vicinity of 1560 cm−1. In contrast, no peak is observed at the lower wave number side of 400 cm−1 to 1000 cm−1 in the conventional coated film containing hydrogen. By taking a coated film structure having a peak in the range between 400 cm−1 and 1000 cm−1 in wave number, hardening is induced to improve the wear resistance. Therefore, it is desirable to have a peak in the range of at least 400 cm−1 and not more 1000 cm−1 in wave number.

[0052] When the intensity ratio (I700/I1340) of the peak intensity located between at least 400 cm−1 and 1000 cm−1 in wave number (I700) to the peak intensity located in the vicinity of 1340 cm−1 (I1340) is at least 0.01 and not more than 2.5, the wear resistance is improved. It is possible that the film hardness is improved by the small-size sp2 bond and the increase of sp3 bond with distortion.

[0053] Although the peak intensity (height) is used here, the same applies to the peak integrated intensity ratio. The intensity ratio (S700/S1340) of the integrated intensity of the peak located in the range between 400 cm−1 to 1000 cm−1 in wave number (S700)to the integrated intensity of the peak located in the vicinity of 1340 cm−1 (S1340) is preferably at least 0.01 and not more than 2.5. If the peak intensity ratio is less than 0.01, the wear resistance is equal to that of the conventional coated film. Although various film deposition experiments were carried out, a peak intensity ratio exceeding 2.5 could not be obtained by the experiments carried out, as will be described afterwards.

[0054] If the intensity ratio (I1340/I1560) of the peak intensity located in the vicinity of 1560 cm−1 (I1560) to the peak intensity located in the vicinity of 1340 cm−1 (I1340) is at least 0.1 and not more than 1.2, high wear resistance is exhibited. The ratio of the intensity (I1560) of the peak located in the vicinity of 1560 cm−1 to the intensity (S1340) of the peak located in the vicinity of 1340 cm−1 is also referred to as sp2/sp3, representing the presence of the carbon bond status in the coated film. Although these values of the peak intensity ratio do not directly indicate the containing amount of sp2, relative classification of the coated film structure can be conducted. It was found that the hardness is increased when the intensity of the peak located in the vicinity of 1560 cm−1 is high. In other words, the wear resistance is improved when the sp3 bond characteristic is stronger. In addition to the peak intensity, the intensity ratio (S1340/S1560) of the integrated intensity of the peak located in the vicinity of 1560 cm−1 (S1560) to the integrated intensity of the peak located in the vicinity of 1340 cm−1 (S1340) is to be at least 0.3 and not more than 3.

[0055] When the peak located in the vicinity of 1560 cm−1 is present in a range of at least 1560 cm−1 and not more than 1580 cm−1, high wear resistance can be realized. The peak position in the Raman spectrum is affected by the stress in the coated film. In general, the peak in the Raman spectrum shifts to the higher wave number side when the stress in the coated film is high at the compressive side. In contrast, the peak in the Raman spectrum shifts to the lower wave number side when the stress in the coated film is high at the extension side. It was found that the wear resistance is improved when the stress in the coated film is high at the compressive side.

[0056] Interference Colors

[0057] The amorphous carbon film coated in conventional art is opaque in the visible region and has the color of brown to black. The amorphous carbon film of the tool of the present invention is transparent in the visible region, and exhibits interference color.

[0058] Exhibiting interference color implies that sp3 bond component in the amorphous carbon film is extremely great, and physical properties such as the refractive index, the optical bandgap and elastic modulus are closer to those of diamond than of the conventional amorphous carbon film. When the amorphous carbon film of the present invention is used for the tool, superior wear resistance and heat resistance are exhibited due to the high film hardness. Since the WC base cemented carbide which is the base material of the tool of the present invention is silver or gray close to silver in color, the tool of the present invention is characterized in the appearance of exhibiting interference color.

[0059] The interference color of the amorphous carbon film changes from (1) brown→(2) magenta→(3) violet→(4) blue-violet→(5) blue→(6) silver→(7) yellow→(8) red→(9) blue→(10) green→(11) yellow→(12) red, and then repeats the change from (8) red to (12) red thereafter, as a function of thicker film. The change of these colors is continuous with respect to difference in the film thickness. When the film is of a thickness intermediate therebetween, the color exhibited is the intermediate color therebetween.

[0060] The inventors of the present invention studied the results and found that the coated film exhibited the colors between (2) magenta to (10) green when the range of 0.05 μm to 0.5 μm is selected for the maximum film thickness at the cutting edge of the tool. The color of the coated film may be the rainbow color corresponding to a plurality of color tones instead of a single color. The tool of the present invention may have a conventional amorphous carbon film of the brown to black color formed on the amorphous carbon film presenting the above-described interference colors.

[0061] Interlayer

[0062] The tool of the present invention preferably has an interlayer provided between the base material and the amorphous carbon film to enhance the adherence of the amorphous carbon film.

[0063] Material

[0064] For the interlayer, at least one type of element selected from the group consisting of an element from Groups IVa, Va, VIa and IIIb of the periodic table and from Group IVb of the periodic table excluding C, or carbide of at least one type of element selected from the group consisting of these elements is suitable.

[0065] It is further desirable that the interlayer includes at least one type of element selected from the group consisting of elements Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W and Si, or carbide of at least one type of element selected from the group consisting of these elements. Since these metal elements facilitate a strong bond with carbon, the formation of an amorphous carbon film on the interlayer of these metal elements or metal carbide produces stronger adherence.

[0066] Thickness

[0067] The thickness of the interlayer is at least 0.5 nm and less than 10 nm. Is the film thickness is thinner than this range, the interlayer cannot play its role. If the thickness exceeds this range, adherence of only a level equal to that of conventional art can be obtained. By forming such an extremely thin interlayer, significant adherence not achieved in prior art can be obtained. Thus, the lifetime of the tool can be extremely improved.

[0068] Mixed Composition Layer•Gradient Composition Layer

[0069] Adhesion can further be improved by providing a mixed composition layer whose composition of each coated film is mixed or a gradient composition layer whose composition is continuously varied between the interlayer and the amorphous carbon film. The mixed composition layer and the gradient composition layer are not necessarily distinguishable. When the fabrication conditions are switched from those of forming an interlayer to those for forming an amorphous carbon film, mixture occurs of the compositions of the interlayer and the amorphous carbon layer, whereby a mixed composition layer or gradient composition layer is formed. Although it is difficult to directly confirm such a composition layer, the results of XPS (X-ray Photo-electronic Spectroscopy), AES (Auger Electron Spectroscopy), and the like sufficiently support this presumption.

[0070] Tool Application

[0071] The amorphous carbon coated tool of the present invention is particularly suitable for working on aluminum and alloy thereof by virtue of the wear resistance and adhesion resistance. The tool of the present invention is most suitable to be used on non-ferrous material such as titanium, magnesium and copper. The tool of the present invention is also effective for cutting materials including hard particles such as graphite, organic material, and working on printed circuit boards and bi-metallic cutting of iron type material and aluminum. Furthermore, the tool of the present invention can be used in working on steel such as stainless steel and cast metal in addition to non-ferrous material by virtue of the high hardness of the amorphous carbon film.

[0072] Specific Examples of Tool

[0073] The amorphous carbon coated tool of the present invention can be used in an application including one type selected from the group consisting of a drill, an end mill, an indexable insert for end mill working, an indexable insert for a milling cutter, an indexable insert for a turning tool, a metal saw, a gear cutter, a reamer and a tap.

[0074] The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.

[0075] An embodiment of an amorphous carbon coated tool of the present invention will be described specifically according to examples. It is to be understood that the method is not limited to that described here. An arbitrary method can be used as long as the film is deposited by PVD using graphite.

EXAMPLE 1

[0076] As the base, a φ8 mm drill made of WC base cemented carbide was prepared. This base includes 1% by mass of (Ta, Nb) C, and Co of a content indicated in Table 1 that will be described afterwards. The surface of this base was subjected to the well-known cathode arc ion plating method, whereby Samples 1-38 of amorphous carbon coated drills of the present invention shown in Table 1-Table 4 were prepared.

[0077] Referring to FIG. 1, a plurality of targets 2 and 3 are disposed in a film deposition apparatus 1. A drill formed of cemented carbide is attached to a base holder 4 that rotates between targets about the center point of respective targets. Power supplies 7 and 8 are adjusted to alter the discharging current of the cathode to coat amorphous carbon while controlling the vaporization of the target material.

[0078] The vacuum level in deposition apparatus 1 was set to an atmosphere of 2×10−3 Pa while heating up to 100° C. using a base heater 6. Argon gas is then introduced. A voltage of −1000V is applied to base holder 4 through a bias power supply 9 while maintaining the atmosphere at 2×10−1 Pa. Following an argon plasma cleaning process, the argon gas is discharged. The gas is introduced into deposition apparatus 1 through an inlet 10 and output through an outlet 11. By vaporizing and ionizing the graphite target through the vacuum arc discharge while introducing argon gas into deposition apparatus 1 at the rate of 100 cc/min., an amorphous carbon film is formed in contact on the cemented carbide drill. Here, the voltage from the bias power supply 9 was set to—several hundred V. At this time, the temperature of the base material was set up in 100° C.

[0079] Prior to deposition of amorphous carbon, some samples had the voltage of −1000V applied to base holder 4 through bias power supply 9 while the target of the metal element from Groups IVa, Va and VIa of the periodic table are vaporized and ionized to conduct metal ion bombardment. This surface etching process is effected to improve the adherence of the coated film.

[0080] Also, for some samples, a target selected from the group consisting of an element from Groups IVa, Va, VIa and IIIb of the periodic table and an element of Group IVb of the periodic table excluding C was vaporized and ionized, with or without hydrocarbon gas introduced, and a voltage of—several hundred V was applied to base holder 4 by bias power supply 9. As a result, an interlayer of this metal or of metal carbide was formed. The formation of an amorphous carbon film from an interlayer was effected by switching the target and atmosphere. At the time of this switching, slight mixture of the components of both layers generally occurs. It is therefore presumed that a mixed composition layer or gradient composition layer of the source material is present between the layers.

[0081] For the sake of comparison, coating drills of Comparative Examples 1-7 shown in Tables 5 and 6 were also prepared. Comparative Example 4 was deposited an amorphous carbon film at the surface of a cemented carbide drill identical to that described above using a general plasma CVD.

[0082] Each of the drills fabricated by the above-described method was used in a boring test according to the conditions in Table 7 (wetting condition by external oil feed). The thrust reduction with respect to a non-coat drill (evaluated based on the thrust resistance of Comparative Example 26) and the status of adhesion at the cutting edge were measured. The results of respective cutting tests are shown in Tables 2, 4 and 6. In Tables 1, 3 and 5, “Crystal grain size of WC” refers to the average grain size of WC after the base is sintered. The film thickness at the cutting edge was evaluated through SEM at the cutting edge cross section.

	TABLE 1
	Maximum film	Cutting	Cobalt	Crystal	Surface	Surface	Macro-particle	Knoop	Metal ion
	thickness at	edge film	content	grain size	roughness	roughness	density	hardness	bombard
	cutting edge (μm)	color	(mass %)	of WC	Ra (μm)	Ry (μm)	(particles/mm2)	GPa	process	Interlayer
Sample 1	0.05	Magenta	5	1.2	0.002	0.02	24000	35	No	No
Sample 2	0.15	Yellow	6	1.1	0.007	0.08	77000	34	Yes	CrCx
Sample 3	0.25	Blue	5	1	0.015	0.12	125000	35	Yes	Cr
Sample 4	0.50	Green	5	1.5	0.030	0.30	260000	34	No	No
Sample 5	0.07	Violet	3	1.3	0.002	0.03	93000	32	Yes	TiCx
Sample 6	0.20	Red	7	1.3	0.010	0.10	98000	29	No	No
Sample 7	0.08	Blue	12	1.2	0.003	0.04	114000	31	Yes	Ti
		Violet
Sample 8	0.18	Red	6	0.1	0.009	0.09	82000	30	No	No
Sample 9	0.10	Blue	5	1	0.005	0.07	73000	35	Yes	ZrCx
Sample 10	0.16	Yellow	5	2	0.007	0.06	77000	34	No	No
Sample 11	0.07	Violet	5	3	0.003	0.04	73000	33	Yes	Zr
Sample 12	0.21	Red	4	1	0.018	0.11	98000	30	No	No
Sample 13	0.08	Blue	6	1.2	0.003	0.03	99500	34	Yes	HfCx
		Violet
Sample 14	0.22	Red	6	1.1	0.020	0.18	112000	31	No	No
Sample 15	0.10	Blue	5	1	0.005	0.06	84000	20	Yes	Hf
Sample 16	0.16	Yellow	5	0.9	0.007	0.08	72000	25	No	No
Sample 17	0.12	Silver	7	1.4	0.007	0.09	110000	50	Yes	VCx
Sample 18	0.19	Red	5	1.1	0.015	0.12	98000	33	No	No
Sample 19	0.10	Blue	5	1.3	0.005	0.07	96000	32	Yes	V
Sample 20	0.20	Red	6	1.2	0.018	0.20	110000	30	No	No

[0083]

	TABLE 2
						Peak position	Thrust
						in vicinity of	resistance (%)	Adhesion
	Peak below					1560 cm−1	(Non-coated:	status at
	1000 cm−1	I700/I1340	S700/S1340	I1340/I1560	S1340/S1560	(cm−1)	100%)	cutting edge
Sample 1	Yes	0.21	0.09	0.6	1.5	1571	61	No adhesion
Sample 2	Yes	0.2	0.21	0.8	1.4	1570	54	No adhesion
Sample 3	Yes	0.22	0.22	0.8	1.6	1570	55	No adhesion
Sample 4	Yes	0.23	0.1	0.7	1.5	1569	64	No adhesion
Sample 5	Yes	0.21	0.05	0.9	1.4	1568	62	No adhesion
Sample 6	Yes	0.2	0.03	0.9	1.7	1570	59	No adhesion
Sample 7	Yes	0.2	0.22	0.9	1.6	1571	68	No adhesion
Sample 8	Yes	0.24	0.11	0.8	1.5	1572	63	No adhesion
Sample 9	Yes	0.26	0.03	0.8	1.5	1570	52	No adhesion
Sample 10	Yes	0.21	0.02	1	1.5	1570	56	No adhesion
Sample 11	Yes	0.22	0.18	1	1.5	1570	66	No adhesion
Sample 12	Yes	0.22	0.16	1.1	1.6	1570	57	No adhesion
Sample 13	Yes	0.2	0.07	1	1.6	1569	61	No adhesion
Sample 14	Yes	0.21	0.14	0.4	1.4	1567	60	No adhesion
Sample 15	Yes	0.21	0.12	0.6	1.7	1570	69	No adhesion
Sample 16	Yes	0.22	0.09	0.6	1.7	1571	64	No adhesion
Sample 17	Yes	0.24	0.12	0.8	1.7	1571	61	No adhesion
Sample 18	Yes	0.02	0.11	0.9	1.8	1570	62	No adhesion
Sample 19	Yes	1.5	0.11	0.5	1.6	1571	65	No adhesion
Sample 20	Yes	2.5	0.2	1	1.5	1569	63	No adhesion

[0084]

	TABLE 3
	Maximum film	Cutting	Cobalt		Surface	Surface	Macro-particle	Knoop	Metal ion
	thickness at	edge film	content	Grain size	roughness	roughness	density	hardness	bombard
	cutting edge (μm)	color	(mass %)	of WC	Ra (μm)	Ry (μm)	(particles/mm2)	GPa	process	Interlayer
Sample 21	0.12	Silver	5	1.2	0.006	0.06	105000	29	Yes	NbCx
Sample 22	0.21	Red	5	1.5	0.015	0.12	98000	31	No	No
Sample 23	0.20	Red	7	1.8	0.018	0.20	103000	33	Yes	Nb
Sample 24	0.19	Red	6	1.3	0.016	0.13	93000	32	No	No
Sample 25	0.19	Red	6	1.7	0.012	0.10	94000	31	Yes	TaCx
Sample 26	0.18	Red	5	1.2	0.010	0.08	78000	30	No	No
Sample 27	0.16	Yellow	5	1.5	0.008	0.07	74000	30	Yes	Ta
Sample 28	0.22	Red	5	1.4	0.015	0.13	120000	31	No	No
Sample 29	0.20	Red	5	1.5	0.022	0.23	112000	32	Yes	MoCx
Sample 30	0.23	Blue	5	0.08	0.021	0.20	108000	31	No	No
Sample 31	0.22	Red	6	4	0.018	0.15	112000	31	Yes	Mo
Sample 32	0.21	Red	5	1.5	0.016	0.15	96000	31	No	No
Sample 33	0.16	Yellow	5	1.3	0.008	0.09	73000	33	Yes	WCx
Sample 34	0.22	Red	6	1.2	0.021	0.18	112000	32	No	No
Sample 35	0.20	Red	5	1	0.015	0.16	124000	34	Yes	W
Sample 36	0.23	Blue	5	1.1	0.022	0.19	140000	31	No	No
Sample 37	0.22	Red	6	1.5	0.018	0.16	96000	30	Yes	SiCx
Sample 38	0.21	Red	6	1.2	0.017	0.15	98000	30	No	No

[0085]

	TABLE 4
						Peak position	Thrust
						in vicinity of	resistance (%)	Adhesion
	Peak below					1560 cm−1	(Non-coated:	status at
	1000 cm−1	I700/I1340	S700/S1340	I1340/I1560	S1340/S1560	(cm−1)	100%)	cutting edge
Sample 21	Yes	0.24	0.01	0.3	1.5	1569	68	No adhesion
Sample 22	Yes	0.22	1.5	0.7	1.6	1569	68	No adhesion
Sample 23	Yes	0.25	2.5	0.4	1.8	1571	67	No adhesion
Sample 24	Yes	0.22	0.06	0.1	1.3	1568	59	No adhesion
Sample 25	Yes	0.22	0.03	0.5	1.5	1569	62	No adhesion
Sample 26	Yes	0.23	0.02	1.2	1.4	1567	63	No adhesion
Sample 27	Yes	0.22	0.11	1.1	0.3	1569	66	No adhesion
Sample 28	Yes	0.2	0.08	1	1.5	1571	65	No adhesion
Sample 29	Yes	0.21	0.08	0.9	3	1571	68	No adhesion
Sample 30	Yes	0.22	0.09	1	1.4	1560	62	No adhesion
Sample 31	Yes	0.19	0.15	0.9	1.5	1570	61	No adhesion
Sample 32	Yes	0.2	0.14	0.8	1.4	1580	59	No adhesion
Sample 33	Yes	0.59	0.5	0.7	1.3	1569	74	No adhesion
Sample 34	Yes	0.48	1.11	0.8	1.2	1570	68	No adhesion
Sample 35	Yes	0.79	0.69	0.8	1.2	1570	66	No adhesion
Sample 36	Yes	1.11	0.79	0.6	1.2	1571	71	No adhesion
Sample 37	Yes	1.23	1.11	0.7	1.1	1573	69	No adhesion
Sample 38	Yes	1.49	1.08	0.3	1.1	1577	66	No adhesion

[0086]

	TABLE 5
	Maximum film	Cutting	Cobalt		Surface	Surface	Macro-particle	Knoop	Metal ion
	thickness at	edge film	content	Grain size	roughness	roughness	density	hardness	bombard	Interface
	cutting edge (μm)	color	(mass %)	of WC	Ra (μm)	Ry (μm)	(particles/mm2)	GPa	process	Layer
Comparative	0.03	Brown	5	1.5	0.002	0.03	21000	30	Yes	Ti
Example 1
Comparative	0.60	Red	5	1.4	0.065	0.62	35000	31	No	No
Example 2
Comparative	0.20	Red	13	1.5	0.017	0.18	96000	32	Yes	CrCx
Example 3
Comparative	0.22	Red	5	1.4	0.020	0.21	—	18	No	Si
Example 4
Comparative	TiN3 μm	Gold	6	1.5	0.200	0.80	—	20	Yes	No
Example 5
Comparative	TiAlN3	Copper	5	1.6	0.180	1.20	—	23	Yes	No
Example 6	μm	Red
Comparative	non-coat	—	5	1.7	—	—	—	—	—	—
Example 7

[0087]

	TABLE 6
						Peak position	Thrust
						in vicinity of	resistance (%)	Adhesion
	Peak below					1560 cm−1	(Non-coated:	status at
	1000 cm−1	I700/I1340	S700/S1340	I1340/I1560	S1340/S1560	(cm−1)	100%)	cutting edge
Comparative	Yes	0.22	0.11	0.9	1.4	1569	99	Adhesion at
Example 1								cutting edge
Comparative	Yes	0.2	0.08	0.3	1.5	1571	101	Adhesion at
Example 2								cutting edge
Comparative	Yes	0.21	0.08	0.5	1.4	1571	98	Adhesion at
Example 3								cutting edge
Comparative	No	0	—	1	1.5	1571	97	Adhesion at
Example 4								cutting edge
Comparative	No	—	—	—	—	—	135	chipping
Example 5
Comparative	No	—	—	—	—	—	140	chipping
Example 6
Comparative	—	—	—	—	—	—	100	chipping
Example 7

[0088]

TABLE 7
Workpiece material A5052P
Cutting speed      100 m/min
Feed               0.5 mm/rev
Depth              40 mm
Number of worked   1000 holes
holes

[0089] The composition of A5052 in Table 7 is defined in the standards of JIS H4000.

[0090] It is appreciated from the results of Tables 2, 4 and 6 that the conventional TiN film (Comparative Example 5), the TiAlN film (Comparative Example 6), Comparative Example 4 corresponding to a hydrogenated amorphous carbon film containing 35 atomic % hydrogen formed by CVD and other comparative examples have a thrust resistance equal to that of a noncoated sample and is inferior in adhesion resistance. All the drills of the present invention (Samples 1-38) had a hydrogen content of 5 atomic % in the amorphous carbon coated film. This amount of hydrogen was evaluated by ERDA (Elastic Recoil Detection Analysis). It is appreciated that the drills of the present invention exhibited superior wear resistance as well as superior adhesion resistance in the process of aluminum boring. The accuracy of the bore after the boring process was extremely high. It is appreciated that the lifetime of the tool can be increased.

EXAMPLE 2

[0091] By means of a method identical to that of Example 1, the surface of a φ4 mm reamer made of cemented carbide was coated with an amorphous carbon film (film of Sample 2). The cemented carbide base of Example 2 includes 1% by mass of (Ta, Nb) C, and 7% by mass of Co. The hydrogen content in the amorphous carbon film is not more than 5 atomic %. As comparative examples, a hydrogenated amorphous carbon film by CVD (Comparative Example 4), a TiN film (Comparative Example 5) and a TiAlN film (Comparative Example 6) were deposited. Each of the surface coated reamers fabricated by the above-described method were used in the boring process of an aluminium die cast (ADC 12) under the conditions shown in Table 8. The number of bores produced and the status of the cutting edge were evaluated.

TABLE 8
Workpiece     ADC12
material
Cutting speed 230 m/min
Feed          0.15 mm/rev
Depth         15 mm

[0092] The composition of ADC12 in Table 8 is defined in the standards of JIS H5302.

[0093] Variation in the diameter of bores formed in the workpiece was noted after forming 600 bores using the conventional surface coated reamer (hydrogenated amorphous carbon film by CVD (Comparative Example 4)) and the metal nitride film formed by PVD (Comparative Examples 5 and 6). Upon checking the status of the reamer, it was found that the cutting edge was subject to wear and chipping was identified at the tip.

[0094] No problem was observed in the machining status of the workpiece even after forming 900 bores using the amorphous carbon coated reamer of Sample 2 of the present invention. No wear or chipping was identified at the cutting edge of the reamer of the present invention.

EXAMPLE 3

[0095] The surface of a φ7 mm end mill made of cemented carbide was coated with an amorphous carbon film (film of Sample 3 of the present invention), fabricated by a method identical to that of Example 1. The cemented carbide base contains 1% by mass of (Ta, Nb) C and 7% by mass of Co. The hydrogen content in the amorphous carbon film is not more than 5 atomic %. As comparative examples, a hydrogenated amorphous carbon film by CVD (Comparative Example 4), a TiN film (Comparative Example 5), and a TiAlN film (Comparative Example 6) were deposited. Using each of the surface coated end mills fabricated by the above-described method, end milling is effected on an aluminium die cast (ADC12) under conditions shown in Table 9. The cutting length and the status of the cutting edge before deviation from the tolerance of the surface roughness of the workpiece were evaluated. In Table 9, Ad (axial depth of cut) is the depth of cut in the axial direction whereas Rd (radial depth of cut) is the depth of cut in the radial direction.

TABLE 9
Workpiece     ADC12
material
Cutting speed 300 m/min
Feed          0.1 mm/rev
Depth of cut  Ad = Rd = 5 mm

[0096] The composition of ADC 12 in Table 9 is defined in the standards of JIS H5302.

[0097] Among the conventional surface coated end mills, the hydrogenated amorphous carbon film by CVD (Comparative Example 4) and the metal nitride films formed by PVD (Comparative Examples 5 and 6) exhibited deviation from the tolerance in surface roughness at 20 m, 5 m and 6 m, respectively. Therefore, determination was made that the lifetime of these tools has expired. Aluminum adhering to the leading edges of the surface coated end mills that had expired lifetime was removed and studied. It was found that the coated film is no longer present, and the WC base cemented carbide of the base was exposed.

[0098] In contrast, the surface roughness of the workpiece was maintained within the tolerance even after 800 m was cut using the end mill of Sample 3 of the present invention. It was expected that the lifetime is further increased.

EXAMPLE 4

[0099] The back side of an indexable insert was coated with an amorphous carbon film (coated film of Sample 2 of present invention) according to a method identical to that of EXAMPLE 1. The cemented base included 1% by mass of (Ta, Nb) C and 6% by mass of Co. The hydrogen content in the amorphous carbon film was not more than 5 atomic %. As comparative examples, a hydrogenated amorphous carbon film by CVD (Comparative Example 4), TiN film (Comparative Example 5) and TiAlN film (Comparative Example 6) were coated. Each of the surface coated indexable insert 1 fabricated by the above-described method was attached to a holder having a tool diameter of 32 mm and used for an end mill process on an aluminium die cast (A390) under the conditions shown in Table 10. The cutting length and status of the cutting edge before the surface roughness of the workpiece deviated from the tolerance were evaluated. In Table 10, Ad (axial depth of cut) is the depth of cut in the axial direction, and Rd (radial depth of cut) is the depth of cut in the radial direction).

TABLE 10
Workpiece     A390
material
Cutting speed 200 m/min
Feed          0.1 mm/rev
Depth of cut  Ad = Rd = 3 mm

[0100] A390 in Table 10 has the composition of Al-16˜18% (m/m) Si.

[0101] As to the conventional surface coated end mills, the surface roughness of the hydrogen amorphous carbon film by CVD (Comparative Example 4), and the metal nitride film formed by PVD (Comparative Examples 5 and 6) deviated from the surface roughness tolerance at 15 m, 4 m and 2 m, respectively. Accordingly, determination was made that the lifetime of the tools has expired. Aluminum adhering to the tip of the surface coated insert determined as having expired lifetime was removed and examined. It was found that the coated film is no longer present and the WC base cemented carbide of the base was exposed.

[0102] The end mill of Sample 2 of the present invention exhibited deviation in the surface roughness tolerance of the workpiece when cutting has been effected for 900 m. Accordingly, determination was made that the lifetime of that tool has expired when the length of 900 m has been cut.

[0103] It will be understood that the above description is merely exemplary, and is also applicable to rotating tools of other configuration (drills, end mills, reamer, and the like), indexable inserts used for milling cutters and turning tools, and cutting-off tools (cutters, knives, splitters, and the like).

[0104] By defining the composition of the base material and the thickness of the amorphous carbon film in the coated tool of the present invention, the tool of the present invention maintains wear resistance and exhibits superior adhesion resistance. Thus, the cutting and wear resistance of the tool of the present invention can be greatly increased. Particularly, by using an amorphous carbon film absent of hydrogen, the wear resistance and adhesion resistance can further be improved. Thus, the potential of effective usage towards rotating tools (drills, end mills, reamers and the like), and indexable insert used for milling cutters and turning tools, and cutting-off tools (cutters, knives, slitters, and the like) exist.

[0105] Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims.

Claims

1. An amorphous carbon coated tool comprising: a base of WC base cemented carbide, and an amorphous carbon coated film covering at least a cutting edge on said base material, wherein said base material has a cobalt content of not more than 12% by mass, hydrogen in said amorphous carbon film is not more than 5 atomic %, and a maximum thickness of said amorphous carbon film at a cutting edge is at least 0.05 μm and not more than 0.5 μm.

2. The amorphous carbon coated tool according to claim 1, wherein said amorphous carbon film is formed of substantially only carbon.

3. The amorphous carbon coated tool according to claim 1, wherein a density of macro-particles present at a surface of said amorphous carbon film is not more than 3×105 particles/mm2.

4. The amorphous carbon coated tool according to claim 1, wherein the maximum thickness of said amorphous carbon film at a cutting edge corresponding to cutting is at least 0.05 μm and not more than 0.25 μm.

5. The amorphous carbon coated tool according to claim 1, wherein said base material has a cobalt content of at least 3% by mass and not more than 7% by mass.

6. The amorphous carbon coated tool according to claim 1, wherein an average crystal grain size of tungsten carbide after said base material is sintered is at least 0.1 μm and not more than 3 μm.

7. The amorphous carbon coated tool according to claim 1, wherein, in said base material, at least 0.01% by mass and not more than 3% by mass is included of a compound comprising at least one type of element selected from the group consisting of a metal element from Groups IVa, Va and VIa of the periodic table, and at least one type of element selected from the group consisting of carbon and nitride.

8. The amorphous carbon coated tool according to claim 1, wherein a surface roughness Ra of said amorphous carbon film is at least 0.002 μm and not more than 0.05 μm.

9. The amorphous carbon coated tool according to claim 1, wherein a surface roughness Ry of said amorphous carbon film is at least 0.02 μm and not more than 0.5 μm.

10. The amorphous carbon coated tool according to claim 1, wherein a Knoop hardness of said amorphous carbon film is at least 20 GPa and not more than 50 GPa.

11. The amorphous carbon coated tool according to claim 1, wherein said amorphous carbon film has a peak in a range of a wave number of at least 400 cm−1 and not more than 1000 cm−1 in a Raman spectrum obtained by Raman spectroscopic analysis using an argon ion laser of 514.5 nm in wavelength.

12. The amorphous carbon coated tool according to claim 11, wherein an intensity ratio (I700/I1340) of the intensity of a peak located in a range of at least 400 cm−1 and not more than 1000 cm−1 in wave number (I700) to the intensity of a peak located in a neighborhood of 1340 cm−1 (I1340) is at least 0.02 and not more than 2.5.

13. The amorphous carbon coated tool according to claim 11, wherein an intensity ratio (S700/S1340) of an integrated intensity of a peak located in a range of at least 400 cm−1 and not more than 1000 cm−1 in wave number (S700) to the integrated intensity of a peak located in a neighborhood of 1340 cm−1 (S1340) is at least 0.01 and not more than 2.5.

14. The amorphous carbon coated tool according to claim 11, wherein an intensity ratio (I1340/I1560) of the intensity of a peak located in a neighborhood of 1560 cm−1 (I1560) to the intensity of a peak located in a neighborhood of 1340 cm−1 (I1340) is at least 0.1 and not more than 1.2.

15. The amorphous carbon coated tool according to claim 11, wherein an intensity ratio (S1340/S1560) of an integrated intensity of a peak located in a neighborhood of 1560 cm−1 (S1560) to the integrated intensity of a peak located in a neighborhood of 1340 cm−1 (S1340) is at least 0.3 and not more than 3.

16. The amorphous carbon coated tool according to claim 11, wherein a peak located in a neighborhood of 1560 cm−1 includes a peak in a range of at least 1560 cm−1 and not more than 1580 cm−1.

17. The amorphous carbon coated tool according to claim 1, wherein said amorphous carbon film is transparent in a visible region, and exhibits an interference color.

18. The amorphous carbon coated tool according to claim 17, wherein said amorphous carbon film exhibits at least one interference color selected from the group consisting of magenta, violet, blue violet, violet, blue, silver, yellow, red, and green.

19. The amorphous carbon coated tool according to claim 1, wherein a coating of said amorphous carbon is directly applied on the base material.

20. The amorphous carbon coated tool according to claim 1, wherein an interlayer is present between said base material and said amorphous carbon film, said interlayer being formed of at least one type of element selected from the group consisting of an element from Groups IVa, Va, VIa and IIIb of the periodic table and an element from Group IVb excluding C, or carbide of at least one type of element selected from said element group, said interlayer having a thickness of at least 0.5 nm and less than 10 nm.

21. The amorphous carbon coated tool according to claim 20, wherein said interlayer includes at least one type of element selected from the group consisting of elements Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W and Si, or carbide of at least one type of element selected from said element group.

22. The amorphous carbon coated tool according to claim 20, wherein a mixed composition layer having a composition of each coated film mixed or a gradient composition layer having a composition continuously changing is present between said interlayer and said amorphous carbon film.

23. The amorphous carbon coated tool according to claim 1, wherein said amorphous carbon coated tool is a tool to work on soft metal material, non-ferrous material, organic material, material including hard particles, a printed circuit board, or for bimetallic cutting of iron type material and soft metal material.

24. The amorphous carbon coated tool according to claim 1, wherein said amorphous carbon coated tool is one type of tool selected from the group consisting of a drill, a micro-drill, an end mill, an indexable insert for end mill processing, an indexable insert for milling cutting, an indexable insert for turning, a metal saw, a gear cutter, a reamer, and a tap.

25. A tool comprising a base material of WC base cemented carbide, and an amorphous carbon film covering at least a cutting edge on said base material, characterized in that: said base material has a cobalt content of not more than 12% by mass, said amorphous carbon film is formed with graphite as a source material by physical vapor deposition under an atmosphere substantially absent of hydrogen, and a maximum thickness of said amorphous carbon film at the cutting edge is at least 0.05 μm and not more than 0.5 μm.

26. A method of fabricating an amorphous carbon coated tool, comprising the steps of: supporting a base material of WC base cemented carbide in a vacuum vessel, and applying a zero or negative direct-current bias to the base material, and vaporizing graphite that is a source material to form an amorphous carbon film, wherein a maximum thickness of the amorphous carbon film is controlled to be 0.05-0.5 μm at a cutting edge.

27. The fabrication method of an amorphous carbon coated tool according to claim 26, wherein said step of forming an amorphous carbon film is carried out by cathode arc ion plating.