Patent Grant
8969506
This disclosure relates to amorphous, high glass transition temperature copolyester compositions, methods of manufacture, and articles thereof.
Thermoplastic polyesters are readily molded into useful articles, and articles comprising such polyesters have valuable characteristics, including strength, toughness, high gloss, and solvent resistance. Polyesters therefore have utility in a wide range of applications, including automotive parts, electric appliances, and electronic devices.
Although polyesters can have a range of desirable performance properties, most of the commercially available amorphous polyesters, such as polyethylene terephthalate (PET), glycol-modified polyethylene terephthalate (PETG), and glycol-modified polycyclohexylenedimethylene terephthalate (PCTG), have useful impact properties, but low glass transition temperatures. This can significantly limit the range of applications for the polyesters. There accordingly remains a need in the marketplace for a new class of amorphous polyesters with better heat performance than those currently available.
An amorphous copolyester is disclosed, comprising the reaction product of:
wherein R1, R2, R3, and R5 are each independently a C1-3 alkyl group, a is 0-1, b is 0-4, c is 0-4 and d is 0-3, and each R4 is independently a hydrogen or a C1-3 alkyl group;
the residue of monomer (a) is present in an amount from 7 to less than 12 mole % of the copolyester based on the total moles of repeat units in the polyester; and
the copolyester has a glass transition temperature of at least 107° C., an intrinsic viscosity of at least 0.7 dl/g, and a molded sample has a Notched Izod value of at least 290 J/m determined in accordance with ASTM D256 at 25° C.
In another embodiment, the method for the manufacture of the copolyester composition is disclosed, which comprises polymerizing the components in the presence of an esterification catalyst.
Compositions comprising the amorphous polyester are also disclosed.
Further disclosed are articles comprising the copolyester composition. Methods of manufacturing an article comprise extruding, shaping, calendaring, molding, or injection molding the copolyester composition.
The described and other features are exemplified by the following detailed description.
Our invention is based on the discovery that it is now possible to make an amorphous copolyester composition having a combination of high glass transition temperature, high strength, and good flow. These properties are achieved using a specific combination of monomer units, including a combination of 1-phenylindane dicarboxylic acid and a terephthalyl component, together with 1,4-cyclohexanedimethanol. In a particularly advantageous feature, the terephthalyl component is a virgin monomer selected from terephthalic acid, a di(C1-3 alkyl) terephthalate, and combinations thereof.
The prefix “bio-”, “bio-based” or “bio-derived” as used herein means that the compound or composition is ultimately derived, in whole or in part, from a biological source, e.g., “bio-based terephthalic acid” is derived from a biological (e.g., plant or microbial source) rather than a petroleum source. Similarly, the prefix “petroleum-” or “petroleum-derived” means that the compound or composition is ultimately derived from a petroleum source, e.g., a “petroleum-derived poly(ethylene terephthalate) is derived from reactants that are themselves derived from petroleum. For example, U.S. patent application Ser. No. 12/347,423, filed Dec. 31, 2008 and published as US 2010/0168371 A1 on Jul. 1, 2010, describes bio-based polyesters produced from a biomass containing a terpene or terpenoid, such as limonene, as well as the process of making these products. The bio-based polyesters include poly(alkylene terephthalate)s such as bio-based poly(ethylene terephthalate) (bio-PET), bio-based poly(trimethylene terephthalate) (bio-PTT), bio-based poly(butylene terephthalate), bio-based poly(cyclohexylene terephthalate) (bio-PCT), bio-based poly(cyclohexylene terephthalate glycol) (bio-PCTG), bio-based (polyethylene terephthalate glycol) (bio-PETG).
As used herein the singular forms “a,” “an,” and “the” include plural referents. “Or” means “and/or.” The term “combination” is inclusive of blends, mixtures, alloys, reaction products, and the like. Unless defined otherwise, technical and scientific terms used herein have the same meaning as is commonly understood by one of skill. Compounds are described using standard nomenclature. The term “and a combination thereof” is inclusive of the named component and/or other components not specifically named that have essentially the same function.
Other than in the operating examples or where otherwise indicated, all numbers or expressions referring to quantities of ingredients, reaction conditions, and the like, used in the specification and claims are to be understood as modified in all instances by the term “about.” Various numerical ranges are disclosed in this patent application. Because these ranges are continuous, they include every value between the minimum and maximum values. The endpoints of all ranges reciting the same characteristic or component are independently combinable and inclusive of the recited endpoint. Unless expressly indicated otherwise, the various numerical ranges specified in this application are approximations. The term “from more than 0 to” an amount means that the named component is present in some amount that is greater than 0, and up to and including the higher named amount.
Polyesters are generally manufactured by polymerization of a dicarboxylic acid or reactive derivative thereof and a diol or reactive derivative thereof. The copolyesters herein are manufactured by polymerization of two dicarboxylic acids (a) a phenyl indane dicarboxylic acid or a reactive derivative thereof; and (b) a virgin terephthalic acid or reactive derivative thereof. The diol is 1,4-cyclohexanedimethanol or a reactive derivative thereof.
The 1-phenylindane dicarboxylic acid monomer is a monomer of formula I:
wherein R1, R2, R3, and R5 are each independently a C1-3 alkyl group, a is 0-1, b is 0-4, c is 0-4 and d is 0-3, and each R4 is independently a hydrogen or a C1-3 alkyl group. The acid or its C1-3 alkyl ester can be used.
One skilled in the art will recognize this general class of monomers as the dicarboxylic acid derivatives of phenyl indane. Among these dicarboxylic acids are 3-(4-carboxyphenyl)-1,1,3-trimethyl-5-indan carboxylic acid; 3-(4-carboxyphenyl)-1,3-diethyl-1-methyl-5-indan carboxylic acid; 3-(4-carboxyphenyl)-1,3-dipropyl-1-methyl-5-indan carboxylic acid; and the like.
In a specific embodiment the monomers are of the formula II
wherein R1, R2, and R4 are each independently hydrogen or a C1-3 alkyl group.
Monomers of formula III can be specifically mentioned
wherein R4 is each independently hydrogen or a C1-3 alkyl group. In an embodiment, each R4 is the same and is a methyl or ethyl group, specifically a methyl group. This monomer is known in the literature, and when R4 is hydrogen, is also known as 1,3,3-trimethyl-1-phenylindan-4′,5-dicarboxylic acid; 1,1,3-trimethyl-5-carboxy-3-(p-carboxy-phenyl)indan; 1,1,3-trimethyl-5-carboxy-3-(4-carboxyphenyl)indan; and 3-(4-carboxyphenyl)-1,1,3-trimethyl-5-indan carboxylic acid. As described in U.S. Pat. No. 3,859,364, the diacid of monomer III is a commercially available material, generally referred to as phenylindan dicarboxylic acid, or, abbreviated, PIDA. The Preparation of PIDA have been disclosed by Petropoulous in, for example, U.S. Pat. Nos. 2,780,609; 2,830,966; and 2,873,262 and 3,102,135. Copolyesters of PIDA with terephthalic acid and ethylene glycol have been described in Belgian 731,258 and Netherlands 6905547. Alternatively, the monomer I, II, or III is a bio-based material, i.e., derived wholly or in part from a biological material, which excludes organic material that has been transformed by geological processes into petroleum, petrochemicals, and combinations thereof.
The terephthalate group is provided by copolymerization with terephthalic acid, a dialkyl terephthalate monomer, or a combination thereof, particularly a virgin di(C1-3)alkyl ester of terephthalic acid, preferably the diethyl ester (DET) or dimethyl ester (DMT). The terephthalyl-containing polyester can contain virgin monomers, recycle monomers, including petroleum-based monomers and bio-based monomers. Thus, the terephthalyl component can be bio-based, i.e., derived in whole or in part from a biological material, which excludes organic material that has been transformed by geological processes into petroleum, petrochemicals, and combinations thereof.
In addition to the monomers I, II, or III and the terephthalyl component, the copolyester is manufactured from 1,4-cyclohexane dimethanol. In an embodiment, the 1,4-cyclohexane dimethanol has an isomer distribution of 60 to 80% trans and 20 to 40% cis isomers. In a specific embodiment, the amorphous copolyester comprises reacted 1,4-cyclohexane dimethanol in an amount of 50 mole %, based on the total moles of repeat units in the copolyester. The CHDM can be virgin monomer, derived from a polyester, or bio-based. For example, one skilled in the art will recognize that DMT or DET derived from a terephthalic-containing polyester homopolymer, terephthalic-containing copolymer, or a combination thereof can be further hydrogenated to 1,4-CHDM. In this instance, the resulting 1,4-CHDM will also contain 1,3-CHDM by-product generated by DMI hydrogenation. Accordingly, where 1,4-CHDM derived from recycle DMT or DET is used, the copolyester can further comprise units derived from 1,3-CHDM. For example, the copolyester can comprise from 0.01 to 5 mole %, from 0.01 to 1 mole %, or from 0.01 to 0.5 mole % of 1,3-cyclohexane dimethanol units, based on the total moles of repeat units in the copolyester.
Methods for the manufacture of the copolyesters from virgin terephthalic acid or di(C1-3)alkyl terephthalic esters, 1-phenylindane monomers I, II, or III, in particular PIDA and 1,4-cyclohexane dimethanol are known and can be used. For example, the copolyesters can be obtained by melt-process condensation, or solution phase condensation in the presence of an acid catalyst. The catalyst facilitates the transesterification reaction, and can be selected from antimony compounds, tin compounds, titanium compounds, combinations thereof as well as many other metal catalysts and combinations of metal catalysts that have been disclosed in the literature. The amount of catalyst required to obtain an acceptable polymerization rate at the desired polymerization temperature will vary, and can be determined by experimentation. The catalyst amount can be 1 to 5000 ppm, or more. It is possible to prepare a branched polyester in which a branching agent, for example, a glycol having three or more hydroxyl groups or a trifunctional or multifunctional carboxylic acid has been incorporated. Furthermore, it is sometimes desirable to have various concentrations of acid and hydroxyl end groups on the polyester, depending on the ultimate end use of the composition.
In an advantageous feature, the copolyesters have an advantageous combination of properties, including an improved Tg, good intrinsic viscosity, and good impact strength.
The copolyesters manufactured from 1,4-cyclohexane dimethanol, 1-phenylindane I, II, or III, in particular PIDA and the virgin terephthalic acid/dialkyl terephthalate have a Tg of at least 107° C., specifically 107 to 117° C.
In general, the copolyester manufactured from 1,4-cyclohexane dimethanol, 1-phenylindane I, II, or III, in particular PIDA and the virgin terephthalic acid/dialkyl terephthalate will have an intrinsic viscosity of at least 0.7 deciliters per gram (dL/g), as measured in a 60:40 by weight phenol/1,1,2,2-tetrachloroethane mixture at 23° C.
The copolyester further has good impact strength, in particular, a molded sample has a Notched Izod value of at least 290 J/m, at least 400 J/m, or at least 600 J/m, determined in accordance with ASTM D256 at 25° C.
The copolyester can have a weight average molecular weight of 10,000 to 200,000 atomic mass units (amu), specifically 50,000 to 150,000 atomic mass units (amu) as measured by gel permeation chromatography (GPC) using polystyrene standards. The copolyester can also comprise a mixture of different batches of copolyester prepared under different process conditions in order to achieve different intrinsic viscosities and/or weight average molecular weights.
The copolyester can be clear or translucent. In an embodiment, the copolyesters are clear. For example, molded sample of the copolyester can have a haze less of less than 20%, less than 15%, less than 10%, less than 5%, or less than 3%, and a transmission greater than 70%, greater than 80%, greater than 85%, or greater than 90%, each measured according to ASTM D 1003-07 using illuminant C at a 0.062 inch (1.5 mm) thickness.
The copolyester can be used as a component in thermoplastic compositions for a variety of purposes. The copolyester can be present in the thermoplastic composition in an amount from 20 to 99.99 wt. %, or from 20 to 95 wt. %, or from 30 to 80 wt. % based on the total weight of the composition. Within this range, at least 50 wt. %, specifically at least 70 wt. %, of the copolyester can be present. In an embodiment, the polyester is present in an amount from 50 to 99 wt. %, based on the total weight of the thermoplastic composition, specifically from 60 to 98 wt. %, more specifically from 70 to 95 wt. %, each amount based on the total weight of the thermoplastic composition. The remaining components of the thermoplastic compositions can be other additives, including other polymers as further described below.
Such thermoplastic composition can optionally comprise other polyesters and/or other polymers, for example other polyesters or polycarbonates. As used herein, “polyesters” is inclusive of homopolymers and copolymers comprising ester units, and “polycarbonate” is inclusive of homopolymers and copolymers comprising carbonate units. Exemplary polyesters include poly(ethylene terephthalate) (“PET”), poly(1,4-butylene terephthalate), (“PBT”), poly(ethylene naphthalate) (“PEN”), poly(butylene naphthalate), (“PBN”), poly(1,3-propylene terephthalate) (“PPT”), poly(cyclohexane-1,4-dimethylene terephthalate) (“PCT”), poly(cyclohexane-1,4-dimethylene cyclohexane-1,4-dicarboxylate) also known as poly(l, 4-cyclohexane-dimethanol 1,4-dicarboxylate) (“PCCD”), and poly(cyclohexylene-1,4-dimethylene-co-ethylene terephthalate), also known as cyclohexanedimethanol-terephthalic acid-ethylene glycol (“PCTG” or “PETG”) copolymers. When the molar proportion of cyclohexanedimethanol is higher than that of ethylene glycol the polyester is termed PCTG. When the molar proportion of ethylene glycol is higher than that of cyclohexane dimethanol the polyester is termed PETG. As is known in the art, the foregoing polyesters can further comprise units derived from isophthalic acid. Combinations of the foregoing polymers can be used. The other polymer can be present in an amount of from more than 0.01 to 80 wt. %, or from 5 to 80 wt. %, or from 30 to 70 wt. %, each based on the total weight of the copolyester and the other polymers in the thermoplastic polyester composition. For example, a thermoplastic polyester composition comprising copolyester manufactured from combination of the monomer I, II, or III, virgin terephthalic acid or dialkyl terephthalate and the CHDM, can comprise from 1 to 30 wt. % percent, based on the total weight of the polyesters and other polymers in the thermoplastic polyester composition, of a second polyester, for example poly(ethylene terephthalate), poly(ethylene naphthalate), poly(1,4-butylene naphthalate), poly(trimethylene terephthalate), poly(1,4-cyclohexanedimethylene 1,4-cyclohexanedicarboxylate), poly(1,4-cyclohexanedimethylene terephthalate), poly(1,4-butylene-co-1,4-but-2-ene diol terephthalate), poly(1,4-cyclohexanedimethylene-co-ethylene terephthalate), or a combination comprising at least one of the foregoing polyesters. Alternatively, the thermoplastic polyester composition can comprise 1 to 50 wt. %, or 1 to 30 wt. %, or 1 to 10 wt. %, based on the total weight of the polyester and other polymers in the composition, of a polycarbonate and/or an aromatic copolyester carbonate. In a specific embodiment, the polymer component of the thermoplastic composition consists only of the copolyester. In another embodiment, the polymer component comprises at least 70 wt. % of the copolyester.
In a specific embodiment, the other polymer includes one or more impact modifiers. The thermoplastic copolyester composition can thus optionally comprise the amorphous copolyester and an impact modifier.
For example, the thermoplastic composition can optionally further comprise an impact modifier in an amount from 0.25 to 40 wt. %, or from 0.5 to 25 wt. %, or from 1 to 10 wt. %, based on the total weight of the composition. In other embodiments, the impact modifier is present in an amount from 0.5 to 8 wt. %, specifically from 1.0 to 6 wt. %, still more specifically 0 to 1.0 wt. %, based on the total weight of the composition. In another embodiment, the thermoplastic composition does not include an impact modifier or does not contain appreciable amounts of an impact modifier. In such embodiments, the impact modifier is present in an amount, based on wt. %, ranging from 0 to less than an integer selected from the group consisting of 40, 39, 38, 37, 36, 35, 34, 33, 32, 31, 30, 29, 28, 27, 26, 25, 24, 23, 22, 21, 20, 19, 18, 17, 16, 15, 14, 13, 12, 11, 10, 9, 8, 7, 6, 5, 4, 3, 2, 1 wt. %, and combinations thereof.
Useful impact modifiers include olefin-containing copolymers such as olefin acrylates and olefin diene terpolymers. An example of an olefin acrylate copolymer impact modifier is ethylene ethyl acrylate copolymer available from Union Carbide as DPD-6169. Other higher olefin monomers can be employed as copolymers with alkyl acrylates, for example, propylene and n-butyl acrylate. Olefin diene terpolymers known in the art and generally fall into the EPDM (ethylene propylene diene monomer) family of terpolymers. They are commercially available such as, for example, EPSYN® 704 from Copolymer Rubber Company. Examples of such rubber polymers and copolymers that can be used as impact modifiers are polybutadiene, polyisoprene, and various other polymers or copolymers having a rubbery dienic monomer, for example random copolymers of styrene and butadiene (SBR).
Other thermoplastic impact modifiers are unit copolymers, for example, A-B diblock copolymers and A-B-A triblock copolymers having of one or two alkenyl aromatic units A, which are typically styrene units, and a rubber unit, B, which is typically an isoprene or butadiene unit. The butadiene unit can be partially hydrogenated. Mixtures of these diblock and triblock copolymers are especially useful. Examples of A-B and A-B-A copolymers include polystyrene-polybutadiene, polystyrene-poly(ethylene-propylene), polystyrene-polyisoprene, poly(α-methylstyrene)-polybutadiene, polystyrene-polybutadiene-polystyrene (SBS), polystyrene-poly(ethylene-propylene)-polystyrene, polystyrene-polyisoprene-polystyrene and poly(alpha-methylstyrene)-polybutadiene-poly(alpha-methylstyrene), as well as the selectively hydrogenated versions thereof, and the like. Mixtures of the aforementioned unit copolymers are also useful. Styrene-containing polymers can also be used as impact modifiers.
Other copolymers containing vinyl aromatic compounds, for example styrene, para-methyl styrene, or alpha methyl styrene and vinyl cyanides, for example acrylonitrile or methacrylonitrile, can also be useful as impact modifiers. One example is styrene-acrylonitrile (SAN), comprising 15 to 30 percent by weight acrylonitrile (AN) with the remainder styrene. The SAN can be further modified by grafting to a rubbery substrate such as a 1,4-polybutadiene to produce a rubber graft polymer, e.g., acrylonitrile-butadiene-styrene (ABS), and methacrylonitrile-butadiene-styrene (MBS). High rubber content (greater than about 50 wt %) resins of this type (e.g., HRG-ABS) can be especially useful.
These types of polymers are often available as core-shell polymers. The core usually consists substantially of an acrylate rubber or a butadiene rubber, wherein one or more shells have been grafted on the core. Usually these shells are built up from a vinyl aromatic compound, a vinyl cyanide, an alkyl acrylate or methacrylate, acrylic acid, methacrylic acid, or a combination of the foregoing. The core and/or the shell(s) often comprise multi-functional compounds that can act as a cross-linking agent and/or as a grafting agent. These polymers are usually prepared in several stages. Still other impact modifiers include various elastomeric materials such as organic silicone rubbers, elastomeric fluorohydrocarbons, elastomeric polyesters, random unit polysiloxane-polycarbonate copolymers, and the like.
Specific examples of useful impact modifiers include acrylonitrile-butadiene-styrene, methacrylate-butadiene-styrene, high impact polystyrene, and combinations thereof. With the proviso that desired properties, such as high heat properties, mold shrinkage, tensile elongation, heat deflection temperature, and the like are not adversely affected, the thermoplastic compositions comprising the copolyester can optionally further comprise other known additives used in thermoplastic polyester compositions such as reinforcing fillers, non-reinforcing fillers, stabilizers such as antioxidants, thermal stabilizers, radiation stabilizers, and ultraviolet light absorbing additives, as well as mold release agents, plasticizers, quenchers, lubricants, antistatic agents, dyes, pigments, laser marking additives, and processing aids. A combination comprising one or more of the foregoing or other additives can be used. A specific example of an additive combination is a hindered phenol stabilizer and a waxy mold release agent such as pentaerythritol tetrastearate. When used, the additives are generally present in an amount of 0.01 to 5 wt. %, specifically 0.05 to 2 wt. % each. Alternatively, such additives may be absent from the composition. In one embodiment, such additives are present in an amount ranging from 0 to a number selected from the group consisting of 5, 4, 3, 2, 1, wt. %,
The thermoplastic copolyester compositions can be prepared by blending the components of the composition so that they are homogeneously dispersed in a continuous matrix of the polyester. A number of blending processes can be used. In an exemplary process, the copolyester, other optional polymers, and/or other additives are mixed in an extrusion compounder and extruded to produce molding pellets. In another process, the components, including any reinforcing fibers and/or other additives, are mixed with the copolyester by dry blending, fluxed on a mill and either comminuted or extruded and chopped. The components can also be mixed and directly molded, e.g. by injection or transfer molding. All of the components are dried as much as possible prior to blending. In addition, compounding is carried out with as short a residence time in the machine as possible and at the lowest possible temperature to minimize loss of components by decomposition or volatilization. The temperature is carefully controlled, and friction heat is utilized.
Methods of manufacture of articles include molding, extruding, shaping, injection molding, or calendaring the amorphous copolyester, in particular thermoplastic compositions comprising the amorphous copolyester. In one embodiment, the components are pre-compounded, pelletized, and then molded. Pre-compounding can be carried out in known equipment. For example, after pre-drying the polyester composition (e.g., for four hours at 120° C.), a single screw extruder can be fed with a dry blend of the ingredients, the screw employed having a long transition section to ensure proper melting. Alternatively, a twin-screw extruder with intermeshing co-rotating screws can be fed with polyester and other components at the feed port and reinforcing fibers (and other additives) can optionally be fed downstream. In either case, a generally suitable melt temperature will be 230° C. to 300° C. The pre-compounded components can be extruded and cut up into molding compounds such as granules, pellets, and the like by standard techniques. The granules or pellets can then be molded in any known equipment used for molding thermoplastic compositions, such as a Newbury or van Dorn type injection-molding machine with cylinder temperatures at 230° C. to 280° C., and mold temperatures at 55° C. to 95° C. The granules and pellets can also be extruded into films or sheets. The articles formed by molding or extrusion of the thermoplastic polyester compositions possess an excellent balance of properties.
In particular, the thermoplastic copolyester composition can be molded into useful articles such as heat resistant containers by a variety of means for example, injection molding, blow molding, extruding, and the like. The thermoplastic copolyester composition can also be used to form at least parts in articles such as a wire, an optical fiber, a cable, an automotive part, an outdoor product, a biomedical intermediate or product, a composite material, a melt-spun mono- or multi-filament fiber, an oriented or un-oriented fiber, a hollow, porous or dense component; a woven or non-woven fabric (e.g., a cloth or a felt), a filter, a membrane, a sheet, a film (thin and thick, dense and porous), a multi-layer- and/or multicomponent film, a barrier film, a container, a bag, a bottle, a rod, a liner, a vessel, a pipe, a pump, a valve, an O-ring, an expansion joint, a gasket, a heat exchanger, an injection-molded article, a see-through article, a sealable packaging, a profile, heat-shrinkable film, a thermoplastically welded part, a generally simple and complex part, such as rods, tubes, profiles, linings and internal components for vessels, tanks, columns, pipes, fittings, pumps and valves; an O-ring, a seal, a gasket, a heat exchanger, a hose, an expansion joint, a shrinkable tube; a coating, such as protective coatings, electrostatic coatings, cable and wire coatings, optical fiber coatings; and the like. Articles that can be made from our compositions include and not limited food containers and medical devices, which may be FDA approved. Other articles include houseware articles such as utensils, water bottles, beer bottles, juice containers, soft drink containers, and combinations thereof. Medical articles can include hemodiafilteration housings, medical devices housings for Gamma radiation, e-beam, and ethylene oxide sterilization devices. Infant care articles include baby bottles, pacifier housings, baby food makers, and combinations thereof. Consumer durable articles include and are not limited to chair mats. Small appliance articles can include blending jars, juice maker jars, frozen beverage dispensers, food maker jars, coffee cups, hot drink cups and containers, and sports drink bottles.
In a specific embodiment, a thermoplastic composition comprising the copolyester, or comprising the copolyester and an impact modifier, are formed into a container such as a bottle, having a wall thickness from 1.0 mm 10.0 mm, and an internal volume from 1 to 10,000 mL, from 10 to 5,000 mL, or from 250 to 5,000 mL.
In another specific embodiment, a thermoplastic composition comprises an amorphous copolyester comprising the polymerization reaction product of: (a) a monomer of formula III
wherein R4 is each the same and is methyl or ethyl; (b) a virgin monomer selected from dimethyl or diethyl terephthalate, and combinations thereof, and (c) 1,4-cyclohexane dimethanol having an isomer distribution of 60 to 80% trans and 20 to 40% cis isomers; wherein the residue of monomer (a) is present in an amount from 7 to less than 12 mole % of and the residue of monomer (b) is present in an amount from more than 38 to 43 mol %, each based on moles of repeat units in the polyester; and the copolyester has a glass transition temperature of at least 107° C., an intrinsic viscosity of at least 0.7 dl/g, and a molded sample has a Notched Izod value of at least 290 J/m determined in accordance with ASTM D256. This thermoplastic composition can further comprise an additive is selected from reinforcing fillers, non-reinforcing fillers, antioxidants, thermal stabilizers, radiation stabilizers, ultraviolet light absorbing additives, mold release agents, plasticizers, quenchers, lubricants, antistatic agents, dyes, pigments, laser marking additives, processing aids, and combinations thereof, and optionally a polymer selected from polycarbonate, poly(ethylene terephthalate), poly(butylene terephthalate), poly(butylene naphthalate), poly(1,2-propylene terephthalate), poly(cyclohexylene-1,4-dimethylene terephthalate), poly(ethylene terephthalate), poly(1,3-propylene terephthalate), poly(cyclohexylene-1,4-dimethylene cyclohexylene-1,4-dicarboxylate), poly(cyclohexylene-1,4-dimethylene-co-ethylene terephthalate), poly(cyclohexylene-1,4-dimethylene-co-1,3-cyclobutylene terephthalate), and combinations thereof. In another specific embodiment, this thermoplastic composition, optionally comprising an impact modifier, are formed into a container such as a bottle, having a wall thickness from 1.0 mm 10.0 mm, and an internal volume from 1 to 10,000 mL, from 10 to 5,000 mL, or from 250 to 5,000 mL.
The materials in Table 1 were used in the Examples.
Molding Procedures
The polymers were injection molded on a BOY molding machine. The pellets were dried for 3 hours at 82° C. in a forced air-circulating oven prior to injection molding. The zone temperature was set to 260° C. The nozzle temperature was also set at 260° C. The mold temperature was 54° C. The screw speed was 100 rpm. The injection, holding, cooling and cycle time were 1.5, 6, 18, and 32 seconds, respectively. All standard parts were 0.125 inches (3.12 mm) thick.
Testing Procedures
Glass transition temperature (Tg) was determined according to ASTM D3418 by Differential Scanning calorimetry (DSC) using Perkin Elmer DSC 7 equipped with Pyris DSC 7 software. In a typical procedure, polymer sample (10-20 mg) was heated from 40° C. to 290° C. (20° C./min), held at 290° C. for 1 min, cooled back to 40° C. (20° C./min), then held at 40° C. for 1 min, and the above heating/cooling cycle was repeated. The second heating cycle is usually used to obtain the Tg data.
Intrinsic viscosity (IV) was determined by automatic Viscotek Microlab® 500 series Relative Viscometer Y501. In a typical procedure, 0.5000 g of polymer sample was fully dissolved in 60/40 mixture (by vol) of % phenol/1,1,2,2-tetrachloroethane solution (Harrell Industries). Two measurements were taken for each sample, and the result reported was the average of the two measurements.
Weight average molecular weight (Mw) and number average molecular weight (Mn) were determined by GPC. A Waters 2695 separation module equipped with a single PL HFIP gel (250×4.6 mm) and a Waters 2487 Dual 2, Absorbance Detector (signals observed at 273 nm) was used for GPC analysis. The mobile phase was a mixture of 5/95% HFIP/Chloroform solution. Typically, samples were prepared by dissolving 50 mg of the polymer pellets in 50 mL of 5/95% HFIP/Chloroform solution. The results were processed using Millennium 32 Chromatography Manager V 4.0. Reported molecular weights are relative to polystyrene standards
Injection molded parts as described were tested in accordance with the ASTM and ISO procedures in Table 2.
Notched Izod testing is done on 3×½×⅛ inch (76.2×12.7×3.2 mm) bars using ASTM method D256. Bars were notched prior to oven aging; samples were tested at room temperature, 25° C.
Laboratory synthesis of copolyesters from DMT as shown in Table 3 and further described was conducted in the presence of 250 ppm of titanium (TPT) as the catalyst.
A mixture of 83.42 g (0.43 mol) of DMT, 22.68 g (0.07 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After 5 minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 270° C. After the reaction temperature reached 270° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 47 minutes. A pressure of less than 1 torr was maintained for a total time of 112 minutes. During this period, the stirring speed was reduced to 60 RPM, then maintained for 20 minutes, and subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are listed in Table 4.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) dialkyl terephthalate and (c) 1,4-cyclohexane dimethanol and wherein the 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount from 7 to less than 12 mol %, based on the repeat unit of polymer, the polymer exhibited a combination of the following useful properties: (i) the polymer had a Tg of at least 107° C.; and (ii) the polymer had a Notched Izod of at least 290 Joules/m, and (iii) the polymer had an intrinsic viscosity IV of at least 0.7 dl/g.
A mixture of 83.42 g (0.43 mol) of DMT, 22.68 g (0.07 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After 5 minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 270° C. After the reaction temperature reached 270° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 47 minutes. A pressure of less than 1 torr was maintained for a total time of 78 minutes. During this period, the stirring speed was reduced to 60 RPM, was maintained for 20 minutes, and subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are listed in Table 5.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) dialkyl terephthalate and (c) 1,4-cyclohexane dimethanol and wherein the 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount from 7 to less 12 mol %, based on the repeat unit of polymer, the polymer exhibited a combination of the following useful properties: (i) the polymer had a Tg of at least 107° C.; and (ii) the polymer had a Notched Izod of at least 290 Joules/m, and (iii) the polymer had an intrinsic viscosity IV of at least 0.7 dl/g.
A mixture of 83.42 g (0.43 mol) of DMT, 22.68 g (0.07 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After 5 minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 270° C. After the reaction temperature reached 270° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 47 minutes. A pressure of less than 1 torr was maintained for a total time of 63 minutes. During this period, the stirring speed was reduced to 60 RPM, was maintained for 20 minutes, and subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are listed in Table 6.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) a dialkyl terephthalate and (c) 1,4-cyclohexane dimethanol and wherein the 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount from 7 to less 12 mol %, based on the repeat unit of polymer, the polymer did not exhibit a combination of the following useful properties: (i) the polymer had Tg of at least 107° C.; and (ii) the polymer did not have a Notched Izod of at least 290 Joules/m, and (iii) the polymer did not have an intrinsic viscosity IV of at least 0.7 dl/g.
A mixture of 77.6 g (0.4 mol) of DMT, 32.4 g (0.1 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After 5 minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 275° C. After the reaction temperature reached 275° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 15 minutes. A pressure of less than 1 torr was maintained for a total time of 40 minutes. During this period, the stirring speed was reduced to 60 RPM, was maintained for 20 minutes was subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are shown in Table 7.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) dialkyl terephthalate and (c) cyclohexane dimethanol and the 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount from 7 to less 12 mol %, based on the repeat unit of polymer, the polymer did not exhibit a combination of the following useful properties: (i) the polymer had Tg of at least 107° C.; and (ii) the polymer did not have a Notched Izod of at least 290 Joules/m, and (iii) the polymer did not have an intrinsic viscosity IV of at least 0.7 dl/g.
A mixture of 77.6 g (0.4 mol) of DMT, 32.4 g (0.1 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After 5 minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 275° C. After the reaction temperature reached 275° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 15 minutes. A pressure of less than 1 torr was maintained for a total time of 44 minutes. During this period, the stirring speed was reduced to 60 RPM, was maintained for 20 minutes was subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are shown in Table 8.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) dialkyl terephthalate and (c) cyclohexane dimethanol and the 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount from 7 to less 12 mol %, based on the repeat unit of polymer, the polymer did not exhibit a combination of the following useful properties: (i) the polymer had a Tg of at least 107° C.; and (ii) the polymer did not have a Notched Izod of at least 290 Joules/m, and (iii) the polymer did not have an intrinsic viscosity IV of at least 0.7 dl/g.
A mixture of 77.6 g (0.4 mol) of DMT, 32.4 g (0.1 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After 5 minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 275° C. After the reaction temperature reached 275° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 15 minutes. A pressure of less than 1 torr was maintained for a total time of 62 minutes. During this period, the stirring speed was reduced to 60 RPM, was maintained for 20 minutes was subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are shown in Table 9.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) dialkyl terephthalate and (c) cyclohexane dimethanol and the 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount from 7 to less 12 mol %, based on the repeat unit of polymer, the polymer exhibited a combination of the following useful properties: (i) the polymer had Tg of at least 107° C.; and (ii) the polymer had a Notched Izod of at least 290 Joules/m, and (iii) the polymer had an intrinsic viscosity IV of at least 0.7 dl/g.
A mixture of 77.6 g (0.4 mol) of DMT, 32.4 g (0.1 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After 5 minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 275° C. After the reaction temperature reached 275° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 15 minutes. A pressure of less than 1 torr was maintained for a total time of 50 minutes. During this period, the stirring speed was reduced to 60 RPM, was maintained for 20 minutes was subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are shown in Table 10.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) dialkyl terephthalate and (c) cyclohexane dimethanol and the 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount from 7 to less 12 mol %, based on the repeat unit of polymer, the polymer did not exhibit a combination of the following useful properties: (i) the polymer had a Tg of at least 107° C.; and (ii) the polymer did not have a Notched Izod of at least 290 Joules/m, and (iii) the polymer did not have an intrinsic viscosity IV of at least 0.7 dl/g.
A mixture of 77.6 g (0.4 mol) of DMT, 32.4 g (0.1 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After five minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 275° C. After the reaction temperature reached 275° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 15 minutes. A pressure of less than 1 torr was maintained for a total time of 97 minutes. During this period, the stirring speed was reduced to 60 RPM, was maintained for 20 minutes was subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are shown in Table 11.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) dialkyl terephthalate and (c) cyclohexane dimethanol and the a 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount from 7 to less 12 mol %, based on the repeat unit of polymer, the polymer exhibited a combination of the following useful properties: (i) the polymer had Tg of at least 107° C.; and (ii) the polymer had a Notched Izod of at least 290 Joules/m, and (iii) the polymer had an intrinsic viscosity IV of at least 0.7 dl/g.
A mixture of 67.9 g (0.35 mol) of DMT, 48.6 g (0.15 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After 5 minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 275° C. After the reaction temperature reached 275° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 15 minutes. A pressure of less than 1 torr was maintained for a total time of 76 minutes. During this period, the stirring speed was reduced to 60 RPM, was maintained for 20 min was subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are shown in Table 12.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) dialkyl terephthalate and (c) cyclohexane dimethanol and the 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount more than 12 mol %, based on the repeat unit of polymer, the polymer did not exhibit a combination of the following useful properties: (i) the polymer had Tg of at least 107° C.; and (ii) the polymer did not have a Notched Izod of at least 290 Joules/m, and (iii) the polymer did not have an intrinsic viscosity IV of at least 0.7 dl/g.
A mixture of 67.9 g (0.35 mol) of DMT, 48.6 g (0.15 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After 5 minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 275° C. After the reaction temperature reached 275° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 15 minutes. A pressure of less than 1 torr was maintained for a total time of 95 minutes. During this period, the stirring speed was reduced to 60 RPM, was maintained for 20 minutes was subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are shown in Table 13.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) dialkyl terephthalate and (c) cyclohexane dimethanol and the a 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount more than 12 mol %, based on the repeat unit of polymer, the polymer did not exhibit a combination of the following useful properties: (i) the polymer had a Tg of at least 107° C.; and (ii) the polymer did not have a Notched Izod of at least 290 Joules/m, and (iii) the polymer did not have an intrinsic viscosity IV of at least 0.7 dl/g.
A mixture of 67.9 g (0.35 mol) of DMT, 48.6 g (0.15 mol) of PIDA and 72 g (0.5 mol) of as obtained CHDM were placed into a 500 mL, three neck round bottom flask equipped with a nitrogen inlet, glass stirrer with a metal blade, and a short distillation column. The flask was placed in an oil bath already heated to 180° C. with the stirring speed set at 260 RPM. After five minutes, 250 ppm of titanium catalyst was added to the reaction mixture, and the temperature was gradually increased to 220° C. at a rate of 2° C./minute while stirring under nitrogen. The reaction mixture was heated at 220° C. for 23 minutes and then the temperature of reaction was increased to 275° C. After the reaction temperature reached 275° C., pressure inside the reactor was gradually reduced to 0.2 mm Hg (less than 1 torr) over the next 15 minutes. A pressure of less than 1 torr was maintained for a total time of 105 minutes. During this period, the stirring speed was reduced to 60 RPM, was maintained for 20 minutes was subsequently reduced to 30 RPM for the remainder of polymerization stage. The reaction was stopped and product was collected for analysis. The results for this example are shown in Table 14.
The results indicate that when the copolyester having a repeat unit comprising the reaction product of (a) a 1-phenylindane dicarboxylic acid or ester, in particular PIDA, (b) dialkyl terephthalate and (c) cyclohexane dimethanol and the 1-phenylindane dicarboxylic acid or ester, in particular PIDA is present in an amount more than 12 mol % based on the repeat unit of polymer, the polymer did not exhibit a combination of the following useful properties: (i) the polymer had a Tg of at least 107° C.; and (ii) the polymer did not have a Notched Izod of at least 290 Joules/m, and (iii) the polymer did not have an intrinsic viscosity IV of at least 0.7 dl/g.
Table 15 shows the results of a compositional analysis of terephthalate, PIDA, and CHDM units in the Examples as determined by proton nuclear magnetic spectroscopy.
All cited patents, patent applications, and other references are incorporated herein by reference in their entirety.
Although the present invention has been described in detail with reference to certain preferred versions thereof, other variations are possible. Therefore, the spirit and scope of the appended claims should not be limited to the description of the versions contained therein.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2012267 | Carothers | Aug 1935 | A |
| 2780609 | Petropoulos | Feb 1957 | A |
| 2830966 | Petropoulos | Apr 1958 | A |
| 2873262 | Petropoulos | Feb 1959 | A |
| 3102135 | Petropoulos et al. | Aug 1963 | A |
| 3522215 | Sardessai et al. | Jul 1970 | A |
| 3535286 | Stow et al. | Oct 1970 | A |
| 3547888 | Sardessai et al. | Dec 1970 | A |
| 3634089 | Hamb | Jan 1972 | A |
| 3769264 | Wilson et al. | Oct 1973 | A |
| 3833685 | Wambach | Sep 1974 | A |
| 3856752 | Bateman et al. | Dec 1974 | A |
| 3951886 | Miyake et al. | Apr 1976 | A |
| 3953539 | Kawase et al. | Apr 1976 | A |
| 3989664 | Kawase et al. | Nov 1976 | A |
| 4128526 | Borman | Dec 1978 | A |
| 4178277 | Gebauer et al. | Dec 1979 | A |
| 4328059 | Horlbeck et al. | May 1982 | A |
| 4401804 | Wooten et al. | Aug 1983 | A |
| 4452933 | McCready | Jun 1984 | A |
| 4482700 | Kuhnrich et al. | Nov 1984 | A |
| 4500575 | Taira et al. | Feb 1985 | A |
| 4617373 | Pruett et al. | Oct 1986 | A |
| 4659615 | Ishii et al. | Apr 1987 | A |
| 5266601 | Kyber et al. | Nov 1993 | A |
| 5268420 | Nishimura et al. | Dec 1993 | A |
| 5271985 | Tsunashima et al. | Dec 1993 | A |
| 5378796 | George et al. | Jan 1995 | A |
| 5391362 | Reinalda et al. | Feb 1995 | A |
| 5413681 | Tustin et al. | May 1995 | A |
| 5446079 | Buchanan et al. | Aug 1995 | A |
| 5451611 | Chilukuri et al. | Sep 1995 | A |
| 5453479 | Borman et al. | Sep 1995 | A |
| 5466777 | Caruso et al. | Nov 1995 | A |
| 5554657 | Brownscombe et al. | Sep 1996 | A |
| 5559159 | Sublett et al. | Sep 1996 | A |
| 5744503 | Smith et al. | Apr 1998 | A |
| 5817721 | Warzelhan et al. | Oct 1998 | A |
| 5844023 | Tomka | Dec 1998 | A |
| 5866710 | Ridland et al. | Feb 1999 | A |
| 5869543 | Boos et al. | Feb 1999 | A |
| 6020393 | Khemani | Feb 2000 | A |
| 6066714 | Putzig et al. | May 2000 | A |
| 6096809 | Lorcks et al. | Aug 2000 | A |
| 6120895 | Kowitz et al. | Sep 2000 | A |
| 6166170 | Putzig | Dec 2000 | A |
| 6201034 | Warzelhan et al. | Mar 2001 | B1 |
| 6231970 | Andersen et al. | May 2001 | B1 |
| 6235815 | Loercks et al. | May 2001 | B1 |
| 6303738 | Putzig et al. | Oct 2001 | B1 |
| 6383729 | Ohnuma et al. | May 2002 | B1 |
| 6384129 | Lowry | May 2002 | B1 |
| 6472497 | Loercks et al. | Oct 2002 | B2 |
| 6472557 | Pell, Jr. et al. | Oct 2002 | B1 |
| 6518322 | West | Feb 2003 | B1 |
| 6521717 | Itoh | Feb 2003 | B1 |
| 6649731 | Hori et al. | Nov 2003 | B2 |
| 6706843 | Ishihara et al. | Mar 2004 | B1 |
| 6713595 | Chung et al. | Mar 2004 | B2 |
| 6998462 | Duan et al. | Feb 2006 | B2 |
| 7129301 | Wu et al. | Oct 2006 | B2 |
| 7160977 | Hale et al. | Jan 2007 | B2 |
| 7214414 | Khemani et al. | May 2007 | B2 |
| 7241832 | Khemani et al. | Jul 2007 | B2 |
| 7241838 | Shelby et al. | Jul 2007 | B2 |
| 7354653 | Germroth et al. | Apr 2008 | B2 |
| 7368503 | Hale | May 2008 | B2 |
| 7368511 | Hale et al. | May 2008 | B2 |
| 7737246 | Crawford | Jun 2010 | B2 |
| 7910645 | Ahmed et al. | Mar 2011 | B2 |
| 8088834 | Agarwal et al. | Jan 2012 | B2 |
| 20010014388 | Bastioli et al. | Aug 2001 | A1 |
| 20020111409 | Talibuddin | Aug 2002 | A1 |
| 20040092672 | Bastioli et al. | May 2004 | A1 |
| 20040254330 | Duan et al. | Dec 2004 | A1 |
| 20050113534 | Agarwal et al. | May 2005 | A1 |
| 20050137304 | Strand et al. | Jun 2005 | A1 |
| 20060004151 | Shaikh et al. | Jan 2006 | A1 |
| 20060257676 | Itada et al. | Nov 2006 | A1 |
| 20070010648 | Partridge et al. | Jan 2007 | A1 |
| 20070066794 | Jernigan | Mar 2007 | A1 |
| 20070079945 | Noda et al. | Apr 2007 | A1 |
| 20070082573 | Noda et al. | Apr 2007 | A1 |
| 20070082981 | Noda et al. | Apr 2007 | A1 |
| 20070093634 | Salsman et al. | Apr 2007 | A1 |
| 20070208160 | Agarwal et al. | Sep 2007 | A1 |
| 20070244242 | Agarwal et al. | Oct 2007 | A1 |
| 20070264460 | Del Tredici | Nov 2007 | A1 |
| 20070275242 | Gopal et al. | Nov 2007 | A1 |
| 20070276069 | Agarwal et al. | Nov 2007 | A1 |
| 20080039571 | Cohoon et al. | Feb 2008 | A1 |
| 20080274320 | Yokoyama et al. | Nov 2008 | A1 |
| 20080311385 | Miyazaki et al. | Dec 2008 | A1 |
| 20090169772 | Yamada et al. | Jul 2009 | A1 |
| 20090274885 | Egawa | Nov 2009 | A1 |
| 20090275698 | Ravi et al. | Nov 2009 | A1 |
| 20100041831 | Chung et al. | Feb 2010 | A1 |
| 20100168317 | Cahoon-Brister | Jul 2010 | A1 |
| 20100168336 | Cohoon-Brister | Jul 2010 | A1 |
| 20100168371 | Berti et al. | Jul 2010 | A1 |
| 20110039999 | Witt et al. | Feb 2011 | A1 |
| 20110071235 | Kannan et al. | Mar 2011 | A1 |
| 20110120346 | Reisacher et al. | May 2011 | A1 |
| 20110178265 | Tanaka et al. | Jul 2011 | A1 |
| 20120232191 | Auffermann et al. | Sep 2012 | A1 |
| 20130030116 | Okaniwa et al. | Jan 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 19638488 | Mar 1998 | DE |
| 0103531 | Mar 1984 | EP |
| 0331746 | Jun 1984 | EP |
| 0272417 | Jun 1988 | EP |
| 0573680 | Dec 1993 | EP |
| 0634435 | Jan 1995 | EP |
| 0736557 | Oct 1996 | EP |
| 0575349 | Aug 2003 | EP |
| 1344765 | Sep 2003 | EP |
| 1426404 | Jun 2004 | EP |
| 1473324 | Nov 2004 | EP |
| 1627893 | Feb 2006 | EP |
| 0950678 | Dec 2006 | EP |
| 1862507 | Dec 2007 | EP |
| 2003159 | Dec 2008 | EP |
| 2042548 | Apr 2009 | EP |
| 1947145 | Dec 2009 | EP |
| 1507358 | Apr 1978 | GB |
| 2101617 | Jan 1983 | GB |
| 0185824 | Nov 2001 | WO |
| 2005017034 | Feb 2005 | WO |
| 2007076384 | Jul 2007 | WO |
| 2007089598 | Aug 2007 | WO |
| 2007089600 | Aug 2007 | WO |
| 2008042384 | Apr 2008 | WO |
| 2008085396 | Jul 2008 | WO |
| 2009127556 | Oct 2009 | WO |
| 2010034711 | Apr 2010 | WO |
| 2010077809 | Jul 2010 | WO |
| 2011054786 | May 2011 | WO |
| 2013012706 | Jan 2013 | WO |
| 2013012707 | Jan 2013 | WO |
| 2013033285 | Mar 2013 | WO |
| Entry |
|---|
| U.S. Appl. No. 13/409,898, filed Mar. 1, 2012. |
| U.S. Appl. No. 13/409,983, filed Mar. 1, 2012. |
| U.S. Appl. No. 13/432,638, filed Mar. 29, 2012. |
| U.S. Appl. No. 13/433,390, filed Mar. 29, 2012. |
| U.S. Appl. No. 13/435,865, filed Mar. 30, 2012. |
| Chang et al.; “Copolyesters, VII. Thermal Transitions of Poly(butylene terephthalate-co-isophthalate-co-adipate)s”; vol. 51; Issue 6; Feb. 1994; pp. 999-1004. |
| English Abstract of EP0007445; Date of Publication Feb. 6, 1980; 1 page. |
| International Search Report for International Application No. PCT.JP2009/064418; International Date of Publication Nov. 10, 2009; Date of Mailing Nov. 17, 2009; 2 pages. |
| International Search Report for International Application No. PCT/US2012/026046; Date Mailed May 18, 2012; 5 pages. |
| Written Opinion of the International Search Report for International Application No. PCT/US2012/026046; Date of Mailing May 18, 2012; 8 pages. |
| International Search Report for International Application No. PCT/US2012/026048; Date Mailed May 18, 2012; 5 pages. |
| Written Opinion for International Application No. PCT/US2012/026048; Date Mailed May 18, 2012; 8 pages. |
| International Search Report for International Application PCT/US2012/026051; International Filing Date Feb. 22, 2012; Date of Mailing Aug. 3, 2012; 5 pages. |
| Written Opinion of the International Search Report for PCT/US2012/026051; International Filing Date Feb. 22, 2012; Date of Mailing Aug. 3, 2012; 9 pages. |
| Ukielski et al.; “Effect of Chemical Modification of Poly(butylene terephthalate) on elastic properties”; International Polymer Science and Technology, vol. 31, No. 3; Jan. 2004; 6 pages. |
| Witt et al.; “New Biodegradable Polyester-Copolymers from Commodity Chemicals with Favorable Use Properties”; Journal of Environmental Polymer Degradation; vol. 3; No. 4; no month, 1995; pp. 215-223. |
| WO 2011054786 A1 English Abstract; Date of Publication May 12, 2011; 1 page. |
| DE 19638488 A1 English Abstract; Date of Publication Mar. 26, 1998 2 pages. |
| JP19840003496 English Abstract; Date of Publication Aug. 3, 1985; 2 pages. |
| International Search Report for International Application No. PCT/US2012/071902; International Filing Date: Dec. 28, 2012; Date of Mailing Jun. 24, 2013; 5 pages. |
| Written Opinion of the International Search Report for International Application No. PCT/US2012/071902; International Filing Date: Dec. 28, 2012; Date of Mailing Jun. 24, 2013; 7 pages. |
| International Search Report for International Application No. PCT/US2012/071904; International Filing Date Dec. 28, 2012; Date of Mailing Jun. 24, 2013; 5 pages. |
| Written Opinion of the International Search Report for International Application No. PCT/US2012/071904; International Filing Date Dec. 28, 2012; Date of Mailing Jun. 24, 2013; 6 pages. |
| International Search Report for International Application No. PCT/US2012/071908; International Date of Filing Dec. 28,2012; Date of Mailing May 7, 2013; 5 pages. |
| Written Opinion of the International Search Report for International Application No. PCT/US2012/071908; International Date of Filing Dec. 28,2012; Date of Mailing May 7, 2013; 8 pages. |
| WO 2009127556 A1 English Abstract; Date of Publication Oct. 22, 2009; 2 pages. |
| Machine Translation of JP2004098321; Apr. 2004; 6 pages. |
| Kleeberg et al.; “Biodegradation of Aliphatic-Aromatic copolyesters by Thermomonospora fusca and Other Thermophilic Compost Isolates”; Applied and Environmental Microbiology; vol. 64, No. 5; 1998, American Society for Microbiology; pp. 1731-1735. |
| International Search Report for International Patent Application No. PCT/US2012/068913; International Filing Date Dec. 11, 2012; Date of Mailing Mar. 25, 2013; 5 pages. |
| International Search Report of International Patent Application No. PCT/US2012/068907; International Date of Filing Dec. 11, 2012; Date of Mailing Mar. 25, 2013; 5 pages. |
| Written Opinion of the International Search Report for International Patent Application No. PCT/US2012/068907; International Date of Filing Dec. 11, 2012; Date of Mailing Mar. 25, 2012; 8 pages. |
| International Search Report of International Patent Application No. PCT/US2012/068909; International Filing Date Dec. 11, 2012; Date of Mailing Mar. 21, 2013; 5 pages. |
| Written Opinion of the International Search Report for International Patent Application No. PCT/US2012/068909; International Filing Date Dec. 11, 2012; Date of Mailing Mar. 21, 2013; 7 pages. |
| Written Opinion of the International Search Report for International Patent Application PCT/US2012/068913; International Date of Filing Dec. 11, 2012; Date of Mailing Mar. 25, 2013; 8 pages. |
| U.S. Appl. No. 13/032,051, filed Feb. 22, 2011. |
| U.S. Appl. No. 13/032,091, filed Feb. 22, 2011. |
| U.S. Appl. No. 13/032,121, filed Feb. 22, 2011. |
| U.S. Appl. No. 13/183,786, filed Jul. 15, 2011. |
| U.S. Appl. No. 13/183,807, filed Jul. 15, 2011. |
| U.S. Appl. No. 13/183,821, filed Jul. 15, 2011. |
| U.S. Appl. No. 13/221,159, filed Aug. 30, 2011. |
| U.S. Appl. No. 13/397,189, filed Feb. 15, 2012. |
| U.S. Appl. No. 13/397,210, filed Feb. 15, 2012. |
| JP59138222A with English Abstract; Date of Publication Aug. 8, 1984; 7 pages. |
| JP60147430 Abstract; 1 page; Aug. 3, 1985. |
| JP9087370A with English Abstract; Date of Publication Mar. 31, 1997; 6 pages. |
| International Search Report for International Application No. PCT/US2012/046625; International Filing Date Jul. 13, 2012; Date of Mailing Dec. 20, 2012; 4 pages. |
| Written Opinion of the International Search Report for International Application No. PCT/US2012/046625; International Filing Date Jul. 13, 2012; Date of Mailing Dec. 20, 2012; 6 pages. |
| International Search Report for International Application No. PCT/US2012/046627; International Filing Date Jul. 13, 2012; Date of Mailing Dec. 12, 2012. |
| Written Opinion of the International Search Report for International Application No. PCT/US2012/046627; International Filing Date Jul. 13, 2012; Date of Mailing Dec. 12, 2012. |
| International Search Report for International Application No. PCT/US2012/046629; International Filing Date Jul. 13, 2012; Date of Mailing Dec. 20, 2012; 4 pages. |
| Written Opinion of the International Search Report for International Application No. PCT/US2012/046629; International Filing Date Jul. 13, 2012; Date of Mailing Dec. 20, 2012; 6 pages. |
| International Search Report for International Patent Application No. PCT/US2012/052971; International Filing Date Aug. 30, 2012; Date of Mailing Dec. 10, 2012; 5 pages. |
| Written Opinion of the International Search Report for International Patent Application No. PCT/US2012/052971; International Filing Date Aug. 30, 2012; Date of Mailing Dec. 10, 2012; 7 pages. |
| Patent Cooperation Treaty; International Preliminary Report on Patentability; PCT/US2012/052971; Date of mailing: Mar. 13, 2014, 7 pages. |
| Scheirs et al.; “Modern Polyesters: Chemistry and Technology of Polyesters and Copolyesters”; 2003; pp. 293-321. |
| English Abstract of EP0519367 A1; Date of Publication Dec. 23, 1992; 2 pages. |
| English Abstract of EP2258545 A1; Date of Publication Dec. 8, 2010; 2 pages. |
| English Abstract of JP2000109665 A; Date of Publication Apr. 18, 2000; 1 page. |
| English Abstract of JP2003220645 A; Date of Publication Aug. 5, 2003; 1 page. |
| English Abstract of JP2004050769 A; Date of Publication Feb. 19, 2004; 1 page. |
| English Abstract of JP2004098321 A; Date of Publication Apr. 2, 2004; 2 pages. |
| English Abstract of JP2004204038 A; Date of Publication; 1 page, Jul. 22, 2004. |
| English Abstract of JP2005052479 A; Date of Publication Mar. 3, 2005; 2 pages. |
| English Abstract JP2005220278 A; Aug. 18, 2005; 1 page. |
| English Abstract JP2008045117 A; Date of Publication Feb. 28, 2008; 2 pages. |
| English Abstract of JP3776578 B2; Date of Publication May 17, 2006; 1 page. |
| Number | Date | Country | |
|---|---|---|---|
| 20130206636 A1 | Aug 2013 | US |