Claims
- 1. A process for preparing an amphoteric starch derivative which comprises:
- (a) providing an aqueous slurry of a non-degraded starch derivative containing tertiary amino or quaternary ammonium cationic substituent groups having a D.S. of from about 0.010 to 0.080,
- (b) adjusting the pH level of the slurry to about pH 5.5-8.5,
- (c) adding to the aqueous starch slurry a phosphate salt selected from the group consisting of tripolyphosphate, hexametaphosphate, and pyrophosphate alkali metal salts, while maintaining the pH level at 5.5-8.5,
- (d) filtering the slurry,
- (e) drying the resultant cake to a moisture of 9.0% or below,
- (f) heat reacting the dried starch at a temperature of about 110.degree.-140.degree. C. for a period of 0.1 to 4.0 hours, and
- (g) recovering the amphoteric starch derivative, wherein the resultant starch derivative has a bound phosphorus content of at least 0.12%, a viscosity of at least 800 cps, and a ratio of anionic to cationic groups of from about 0.12 to 0.55.
- 2. The process of claim 1 wherein step (a) the starch derivative contains tertiary amino groups and is a diethylaminoethyl ether of starch.
- 3. The process of claim 1 where in step (a) the starch derivative contains quaternary ammonium groups and is a 2-hydroxypropyl trimethylammonium ether of starch.
- 4. The process of claim 1 wherein the starch derivative employed in step (a) is waxy maize, corn, tapioca or potato starch.
- 5. The process of claim 1 wherein step (c) the slurry is adjusted to a pH level of 6.0-8.0, and the starch derivative of step (g) has a bound phosphorus content of at least 0.14% and a viscosity of at least 1,000 cps.
- 6. The process of claim 5 wherein the starch derivative of step (a) contains tertiary amino groups and is a diethylaminoethyl ether of starch.
- 7. The process of claim 5 wherein the starch derivative of step (a) contains quaternary amino groups and is a 2-hydroxypropyl trimethylammonium ether of starch.
- 8. A process for preparing an amphoteric starch derivative which comprises:
- (a) providing an aqueous slurry of a non-degraded starch derivative containing tertiary amino or quaternary ammonium cationic substituent groups having a D.S. of from about 0.010 to 0.080,
- (b) adjusting the pH level of the slurry to about pH 5.5-8.5,
- (c) filtering the slurry to provide a starch cake containing no more than 45% of moisture,
- (d) forming a reagent solution of an alkali metal tripolyphosphate or hexametaphosphate salt which comprises water and 20-36% by weight of said salt,
- (e) adding 2-30% by weight of said reagent solution based on the weight of the starch to said starch cake to achieve efficient impregnation of the starch cake,
- (f) drying the resultant cake and heat reacting the dried starch-salt mixture which has a pH of 5.5 to 8.5 at a temperature of about 110.degree.-140.degree. C. for a period of 0.1 to 4.0 hours, and
- (g) recovering the amphoteric starch derivative, wherein the resultant starch derivative has a bound phosphorus content of at least 0.12%, a viscosity of at least 800 cps, and ratio of anionic to cationic groups of from 0.12 to 0.55.
- 9. The process of claim 8 wherein step (a) the starch derivative contains tertiary amino groups and is a diethylaminoethyl ether of starch.
- 10. The process of claim 8 wherein step (a) the starch derivative contains quaternary ammonium groups and is a 2-hydroxypropyl trimethylammonium ether of starch.
- 11. The process of claim 8 wherein the starch derivative employed in step (a) is waxy maize, corn, tapioca or potato starch.
- 12. An amphoteric starch derivative containing tertiary amino or quaternary ammonium cationic groups and anionic phosphate groups wherein said starch derivative has a D.S. of cationic groups of from about 0.010-0.080, a bound phosphorus content of at least 0.12%, a viscosity of at least 800 cps, and the ratio of anionic to cationic groups is within the range of from about 0.12 to 0.55 moles of phosphate groups per mole of cationic group.
- 13. The starch derivative of claim 12 wherein the starch is substituted with diethylaminoethyl ether groups and contains a bound phosphorus content of at least 0.14%.
- 14. The starch derivative of claim 12 wherein the starch is substituted with 2-hydroxypropyl trimethylammonium ether groups and contains a bound phosphorus content of at least 0.14%.
- 15. The amphoteric starch derivative of claim 12 wherein the starch is waxy maize, corn, tapioca or potato starch.
BACKGROUND OF THE INVENTION
This application is a continuation-in-part of Ser. No. 896,546 filed Aug. 13, 1986 and now abandoned.
US Referenced Citations (8)
Non-Patent Literature Citations (2)
Entry |
K. W. Britt, TAPPI Journ., Jan. 1984, pp. 102-103, "Water Removal During Paper Sheet Formation". |
A. M. Springer et al., TAPPI Journ., Feb. 1984, pp. 104-108, "The Influence of Starch on Drainage and Retention in Paperboard Mill Systems". |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
896546 |
Aug 1986 |
|