Patent Application
20230391046
This invention pertains to an impact protective composite material. More particularly, but not exclusively, this invention pertains to an impact protective composite material for a flexible bulletproof garment.
Protective garments such as bulletproof vests that contain high strength fibres or material are known. Fibres used in the construction of these known bulletproof vests include aramid synthetic fibres such as poly (p-phenylene terephthalamide) and ultra-high molecular weight polyethylene.
The conventionally used aramid synthetic fibres or material are typically formed into layers by interlacing yarns of the synthetic fibres or sintering a powder of the synthetic material. These layers have high energy absorption properties and is also reasonably light in weight and flexible.
Overlying layers are typically incorporated into the structure of a bulletproof vest to provide a flexible bulletproof vest. These flexible bulletproof vests provide excellent stopping power to a ballistic threat. However, the known flexible bulletproof vests do not sufficiently protect a wearer thereof from suffering trauma from an impact of a ballistic threat. Trauma suffered by a wearer of the known flexible bulletproof vests include significant contusions and broken ribs or bones.
It is an object of the present invention to provide an impact protective composite material for a flexible bulletproof garment with which the applicant believes the above disadvantage may at least be alleviated or which may provide a useful alternative to known impact protective composite materials for a bulletproof garment.
According to a first aspect of the invention there is provided an impact protective composite material including:
The elastomer may be polyurea.
The layers of the first element and the second element may be formed by interlacing yarn of fibres selected from the group consisting of a meta-aramid fibre, a para-aramid fibre, an ultra-high molecular weight polyethylene fibre, a polyethylene terephthalate fibre, a cellulose fibre, a polyamide fibre, a mixture of para-aramid fibres and meta-aramid fibres and a mixture of para-aramid fibres and carbon fibres, and a combination thereof.
Alternatively, the layers of the first element and the second element may be formed by sintering a powder of a material selected form the group consisting of meta-aramids, para-aramids, ultra-high molecular weight polyethylene, polyethylene terephthalate, cellulose, polyamide, a mixture of para-aramids and meta-aramids and a mixture of para-aramids and carbon, and a combination thereof.
Preferably the layers comprise ultra-high molecular weight polyethylene that are formed into a layer having an area density of between 50±8 gram per square metre (g/m2) and 300±8 gram per square metre (g/m2). The ultra-high molecular weight polyethylene layers may each have a thickness of between 0.07±0.02 millimetres (mm) and 0.40±0.02 millimetres (mm).
The first element may comprise at least 14, preferably at least 24 ultra-high molecular weight layers. The plurality of ultra-high molecular weight layers may be grouped into sets, wherein a number of sets forms the first element. The ultra-high molecular weight layers of each set may be attached to one another. The second element may have a thickness of between 0.5 millimetre (mm) and millimetres (mm).
The impact protective composite material may include a third element comprising a layer of high-density foam. The layer of high-density foam may have a thickness of between 1 millimetre (mm) and 7 millimetres (mm).
According to a second aspect of the invention, there is provided for the use of the impact protective composite material in a flexible bulletproof garment.
According to a third aspect of the invention, there is provided a flexible bulletproof garment which incorporates the impact protective composite material.
The invention will now be described further, by way of example only, with reference to the accompanying drawings in which:
With reference to the accompanying drawings, an impact protective composite material according to the invention is generally indicated by reference numeral 10.
The impact protective composite material 10 includes a first element 20, a second element 30 and a third element 40.
The first element 20 comprises a plurality of overlying ultra-high molecular weight polyethylene layers 22.1 to 22.n. Each of the ultra-high molecular weight polyethylene layers has an area density of approximately 160±8 grams per square metre (g/m2) and a thickness of approximately 0.21±0.02 millimetres. The plurality of ultra-high molecular weight polyethylene layers 20.1 to 20.n are typically grouped into sets (not shown), where a number of sets form the first element 20. To form a set, a number of ultra-high molecular weight polyethylene layers are attached to one another at a peripheral region of each of the ultra-high molecular weight polyethylene layers forming the set. The number of ultra-high molecular weight polyethylene layers are typically stitched to one another at a peripheral region of each of the ultra-high molecular weight polyethylene layers. As an example, a first element 20 having 32 ultra-high molecular weight polyethylene layers are grouped into four sets, where each set comprises eight ultra-high molecular weight polyethylene layers.
The second element 30 comprises at least one ultra-high molecular weight polyethylene layer that is encased in polyurea. The polyurea encasing is the reaction product of an aromatic or aliphatic isocyanate component and a synthetic resin. The reaction product contains between 60% and 100% solids.
The second element 30 has a thickness of between 0.5 millimetre (mm) and 5 millimetres (mm). As an example, a polyurea layer having a thickness of approximately 0.5 millimetre (mm) may locate on each side of the ultra-high molecular weight polyethylene layer which is encased in polyurea. The polyurea which encases the ultra-high molecular weight polyethylene layer, surrounds the said ultra-high molecular weight polyethylene layer on all sides and around its edges.
The third element 40 comprises a layer of high-density foam. The layer of high-density foam typically has a thickness of between 1 millimetre (mm) and 7 millimetres (mm).
In use, the impact protective composite material 10 is incorporated into the structure of a flexible bulletproof vest, with the first element 20 forming the strike face. That is, the first element 20 is arranged in the flexible bulletproof vest to face an incoming ballistic threat.
The number of overlying ultra-high molecular weight polyethylene layers 20.1 to used in the first element 20 depends on the level of protection sought. As an example, for a Level II (as classified by the United States National Institute of Justice) bulletproof vest, the first element 20 will comprise between 14 and 26 overlying ultra-high molecular weight polyethylene layers. As a further example, for a Level IIIA (as classified by the United States National Institute of Justice), the first element 20 will comprise between 20 and 34 overlying ultra-high molecular weight polyethylene layers.
Advantageously, a bulletproof vest that incorporates the impact protective composite material 10 of the invention provides excellent stopping power to a ballistic threat and protection against trauma as the result of an impact of the ballistic threat. More particularly, the first element 20 provides the stopping power and the second element 30 provides the protection against trauma. Furthermore, the third element 40 and the flexibility of the sets forming the first element 20 provides for a comfortable bulletproof vest.
It is significant that a bulletproof vest that incorporates the impact protective composite material 10 provides the above-described protection whilst remaining flexible and light in weight. In this regard, a bulletproof vest that incorporates the impact protective composite material 10 is typically lighter in weight than conventional bulletproof vests that provide comparable protection against a ballistic threat.
Test Results which Showcase the Advantages of the Impact Composite Material 10.
Comparative test results which showcase the advantages of the impact protective composite material 10 are provided below.
All tests were performed by the South African Bureau of Standards (“SABS”). The tests were performed according to the prescriptions of South African National Standard 1658:2007 entitled “Ballistic resistance of body armour” and was tested for level IIIA (as classified by the United States National Institute of Justice) ballistic resistance. South African National Standard 1658:2007 is based on the National Institute of Justice Standard 0101.04.
A bulletproof vest which incorporates the impact protective composite material 10 was compared to a bulletproof vest described and claimed in international application number PCT/162017/000572 entitled “Protective garments” (hereinafter “Comparative Bulletproof Vest”). The bulletproof vests tested were all sized “large” and so-called tactical bulletproof vests. That is, the bulletproof vests which were tested were not concealed bulletproof vests which are meant to be worn underneath the clothes of a wearer.
The Comparative Bulletproof Vest which was used during the tests weighed 5.9 kilogram and comprised:
The tests were performed on a 5-metre range. An average temperature of 23.4 degrees Celsius (° C.) and a relative humidity of 38% were recorded.
Results of tests performed on the Comparative Bulletproof Vest:
Below follows the results of tests performed on a first version of a bulletproof vest incorporating the impact protective composite material 10. This first version of the bulletproof vest weighed 4.8 kilogram and comprised:
Below follows the results of tests performed on a second version of a bulletproof vest incorporating the impact protective composite material 10. This second version of the bulletproof vest weighed 3.7 kilogram and comprised:
24 overlying ultra-high molecular weight polyethylene layers; and
As is clear from the above test results, a bulletproof vest which incorporates the impact protective composite material 10 is not only lighter in weight, but also has a significantly lower average back face signature (i.e., deformation) than the Comparative Bulletproof Vest. The significantly lower average back face signature (i.e., deformation) of a bulletproof vest incorporating the impact protective composite material 10 lessens trauma suffered from an impact of a ballistic threat by a wearer of the bulletproof vest.
It will be appreciated by those skilled in the art that the invention is not limited to the precise details as described herein and that many variations are possible without departing from the scope of the invention. As an example, the impact protective composite material 10 described herein is suitable for any flexible impact protective garment, not only bulletproof vests.
The description is presented by way of example only in the cause of providing what is believed to be the most useful and readily understood description of the principles and conceptual aspects of the invention. In this regard, no attempt is made to show more detail than is necessary for a fundamental understanding of the invention. The words which have been used herein are words of description and illustration, rather than words of limitation.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2020/06465 | Oct 2020 | ZA | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2021/055665 | 6/25/2021 | WO |