Patent Application
20210269461
Metal-organic frameworks (MOFs) constitute an enormous and growing class of porous (or potentially porous) crystalline materials. By choosing suitable component organic linkers and inorganic nodes, MOFs with desirable pore composition, periodic chemical functionality, ultrahigh specific surface area, and other properties can be obtained. Further, they can be obtained in great variety—both in silico and in real space. The periodic intra-framework functionality of MOFs allows for the high-density installation of well-defined, yet well-separated active species with frameworks functioning as porous supports.
Central to the potential application of MOFs specifically to electrochemical, molecular electronic, or resistive chemical sensing problems is electrical conductivity. Most MOFs, however, are effectively insulating at low bias. Indeed, only a few tens of MOFs have thus far been shown to display appreciable electrical conductivity. Among the experimentally demonstrated routes to engendering electrical conductivity, while retaining molecular-scale porosity, are as follows: formation of π-stacked pathways, formation of two-dimensional MOFs featuring extended π-conjugation, formation of continuous arrays of electron-donor/electron-acceptor complexes (charge-transfer complexes) between MOF hosts and molecular guests, use of sulfur-based ligands to facilitate energy-level matching and charge delocalization into open-shell, node-sited metal ions, and polymerization of tethered oligomers or, at low loading, adsorbed monomers, within MOF pores to yield MOF/conducting-polymer composites. Yet another approach is linker-to-linker hopping at the redox potentials of selected organic linkers (or molecule-to-molecule hopping at the redox potentials of species installed in the pores of MOFs) under electrochemical conditions.
What the above approaches have in common is a reliance upon organic species/components to sustain, or help sustain, charge transport. To the extent that these species possess radical character, diminished chemical stability and eventual loss of conductivity may be anticipated.
MOF materials, methods of making the materials, and chemical sensors incorporating the materials are provided.
One embodiment of a metal-organic framework material includes: a porous metal-organic framework comprising inorganic nodes connected by organic linkers; and a plurality of continuous strands comprising an inorganic oxide running through the metal-organic framework. The metal-organic framework material is porous.
One embodiment of a method of forming a metal-organic framework material starts with a porous metal-organic framework that includes inorganic nodes connected by organic linkers, wherein the inorganic nodes are capped by hydroxo ligands, aquo ligands, oxo ligands, or a combination thereof. The method includes the steps of: (a) reacting the hydroxo ligands, aquo ligands, and/or oxo ligands on the inorganic nodes with organometallic complexes in a liquid solution to graft the organometallic complexes onto the inorganic nodes, the organometallic complexes comprising a metal ion bound to one or more organic ligands; (b) exposing the organometallic complexes grafted to the inorganic nodes to steam to replace the organic ligands in the organometallic complexes with secondary hydroxo ligands, aquo ligands, oxo ligands, or a combination thereof to provide metal oxide species grafted to the inorganic nodes; (c) reacting the secondary hydroxo ligands, aquo ligands, oxo ligands, or combination thereof with organometallic complexes in a liquid solution to graft the organometallic complexes to the metal oxide species; (d) exposing the organometallic complexes grafted to the metal oxide species to steam to replace the organic ligands in the organometallic complexes with secondary hydroxo ligands, aquo ligands, oxo ligands, or a combination thereof, and (e) repeating steps (c) and (d) a sufficient number of times to form continuous metal oxide strands from the metal oxide species.
One embodiment of a method of detecting hydrogen uses a metal-organic framework material that includes: a porous metal-organic framework, the metal-organic framework comprising inorganic nodes connected by organic linkers; and continuous strands of an electrically conductive material comprising an inorganic oxide running through the metal-organic framework, wherein the metal-organic framework material is porous and electrically conductive. The method includes the steps of: exposing the metal-organic framework material to an environment comprising hydrogen; and measuring an increase in the conductance of the metal-organic framework material.
Illustrative embodiments of the invention will hereafter be described with reference to the accompanying drawings.
MOF materials, methods of making the materials, and chemical sensors incorporating the materials are provided.
Some embodiments of the MOF materials are electrically conductive. The electrically conductive MOF materials are formed from mesoporous MOF crystals having continuous strands of electrically conductive inorganic oxides within their porous structures. Non-conductive MOF materials are formed from mesoporous MOF crystals having continuous strands of non-electrically conductive inorganic oxides within their porous structures. The inorganic strands are formed by the condensed-phase grafting of molecular metal species onto MOF nodes via reactions with hydroxyl, aqua ligands, and/or oxo ligands present at the nodes' surfaces. This self-limiting SIM process provides a robust inorganic approach that permits retention of the MOF's crystallinity and porosity.
MOFs are hybrid, crystalline, porous materials made from metal-ligand networks that include inorganic nodes connected by organic linkers. The inorganic nodes or vertices in the framework can be composed of metal ions or clusters. By convention, carboxylates (or other linker terminal groups or atoms) are often represented as components of the nodes. These nodes are connected by coordination bonds to organic linkers, which commonly contain carboxylate, phosphonate, pyridyl, and imidazolate or other azolate functional groups. In the zirconium MOFs, the nodes comprise zirconium atoms or zirconium clusters.
The SIM process can be carried out on MOFs having hydroxyl and/or aquo ligands present on their nodes. Examples of such MOFs include, but are not limited to, zirconium MOFs (i.e., MOFs having zirconium-based nodes), hafnium MOFs, cerium MOFs, and thorium MOFs. Notable characteristics of zirconium MOFs include high thermal, mechanical, and chemical stability (e.g., stability toward H2S, ammonia, steam, aqueous acid, and/or hydrogen peroxide), as well as the ability to present well-defined, node-based grafting sites for chemical and structural elaboration and, thus, for introduction of specific functional properties.
The MOFs include channel-type MOFs that present a hierarchical pore structure comprising a first set of large hexagonal channels and a second set of smaller triangular channels, running alongside of the large hexagonal channels. The hexagonal channels impart the MOFs with mesoporosity and typically have channel diameters in the range from about 20 Å to about 70 Å.
By way of illustration, MOFs having a framework with a csq-net topology characterized by large hexagonal channels and smaller triangular channels may be used to immobilize various enzymes. MOFs of this type are described in Mondloch et al., J. Am. Chem. Soc. 135, 10294-10297 (2013) and include the MOF designated NU-1000. NU-1000 has hexagonal channels with a diameter of 3.1 nm as well as triangular channels with an edge length of 1.5 nm, with windows connecting the two channels.
The zirconium MOFs having a csq-net topology include mesoporous zirconium MOFs having eight Zr6 cluster nodes connected by tetratropic linkers, where a Zr6 cluster node has the structure Zr6(μ3-O)4(μ3-OH)4(OH)4(H2O)4 or a variation of that structure in which some or all of the hydroxo ligands are replaced with oxo and/or aquo ligands. For example, one family of such MOFs has pyrene-based tetratopic linkers connecting the metal cluster nodes. The pyrene-based linkers can include various aryl groups in their linker chains, including phenyl groups, bi-phenyl groups, and napthyl groups. The structure of these types of MOFs are illustrated in FIGS. 5A, 5B, 5C, 5D, and 5E of PCT application number WO/2017213871, which show MOFs designated NU-1006, NU-1005, NU-1004, NU-1003, and NU-1000, respectively. Other csq-net topology MOFs include those having eight Zr6 cluster nodes connected by ethene-1,1,2,2-tetrayl)tetrakis-(([1,1′-biphenyl]-4-carboxylic acid))) (ETTC) linkers. The structure of the PCN-128 MOF is shown in FIG. 6 of PCT application number WO/2017213871 and described in Zhang et al., J. Am. Chem. Soc., 2015, 137, 10064-10067. Still other csq-net topology MOFs have Zr6 cluster nodes connected by parylene-based tetratopic linkers. The structure for one such MOF, UMCM-313, is shown in FIG. 7 of PCT application number WO/2017213871 and described in Ma et al., Cryst. Growth Des., 2016, 16 (7), pp 4148-4153. MOFs having a csq-net topology formed from Zr6 clusters connected by porphyrin-based linkers can also be used. FIG. 8 of PCT application number WO/2017213871 shows the structure on one such MOF, denoted PCN-222. Methods for making these MOFs are illustrated in PCT application number WO/2017213871, the disclosure of which in incorporated herein by reference.
Other suitable MOFs include MOFs that are isostructural with the Zr-based MOF, but are based on different transition metals, lanthanides, and actinides. These include isostructural Hf-, Ce-, and Th-based MOFs. Illustrative examples of hafnium-based MOFs are described in Hassan, et al. “A hafnium-based metal-organic framework as an efficient and multifunctional catalyst for facile CO2 fixation and regioselective and enantioretentive epoxide activation.” Journal of the American Chemical Society 136.45 (2014): 15861-15864 and in Ting, et al. “Fast and scalable synthesis of uniform zirconium-, hafnium-based metal-organic framework nanocrystals.” Nanoscale 9.48 (2017): 19209-19215. Illustrative examples of cerium-based MOFs are described in Islamoglu, Timur, et al. “Cerium (IV) vs zirconium (IV) based metal-organic frameworks for detoxification of a nerve agent.” Chemistry of Materials 29.7 (2017): 2672-2675 and in Dalapati, Rana, et al. “A cerium-based metal-organic framework having inherent oxidase-like activity applicable for colorimetric sensing of biothiols and aerobic oxidation of thiols.” CrystEngConn 19.39 (2017): 5915-5925. Illustrative examples of thallium-based MOFs, zirconium-based MOFs, hafnium-based MOFs, and cerium-based MOFs are also described in Xingjie, et al. “Vanadium Catalyst on Isostructural Transition Metal, Lanthanide, and Actinide Based Metal-Organic Frameworks for Alcohol Oxidation.” Journal of the American Chemical Society (2019).
The SIM process is carried out on MOFs that have hydroxo, aquo, and/or oxo ligands bound their nodes. One embodiment of a SIM process includes the step of reacting the hydroxo ligands, aquo ligands, and/or oxo ligands on their nodes with organometallic complexes in the condensed phase to graft the organometallic complexes onto the nodes. The organometallic complexes include a metal ion bound to one or more organic ligands. It is the metal ion of the organometallic complexes that will be converted into the inorganic oxide strands after multiple SIM cycles. The product of this initial reaction can then be removed from solution and, optionally dried. The organometallic complexes that are grafted to the MOF nodes are then exposed to steam to replace the organic ligands in the organometallic complexes with secondary hydroxo ligands, aquo ligands, oxo ligands, or a combination thereof. This provides metal-oxy clusters composed of hydroxo-, aquo-, and/or oxo-functionalized metal oxide species grafted to the nodes. For the purpose of this disclosure, such SIM-synthesized clusters will be referred to as metal oxides, although the metal ion-containing species ligate hydroxide, and possibly also water, in addition to O2. The term “secondary” is used here to distinguish the hydroxo ligands, aquo ligands, oxo ligands that are initially present on the nodes of the MOF (primary hydroxo ligands, aquo ligands, and oxo ligands) from the hydroxo ligands, aquo ligands, oxo ligands that become bound to the grafted metal ions during the SIM process.
In subsequent cycles of the process, the newly formed secondary hydroxo ligands, aquo ligands, oxo ligands, or combination thereof are reacted with additional organometallic complexes in liquid solution to graft the organometallic complexes to the metal oxide species. The organometallic complexes in the subsequent cycles may be the same as or different from the organometallic complexes used in previous cycles. The resulting, newly grafted organometallic complexes are then exposed to steam to replace their organic ligands with a new set of secondary hydroxo ligands, aquo ligands, and/or oxo ligands. By introducing the new O—H presenting ligands on the modified-MOF nodes, the steam step serves to reset the material to reactive form, thus enabling a second self-limiting metal grafting step to be run. Thus, the cycle can be repeated one or more times until the metal ion loading on the nodes is sufficiently high to form continuous metal oxide strands that are electrically conductive.
For the synthesis of electrically conductive MOF materials, the metal ion of the organometallic complexes should be a metal having an electrically conductive oxide. Tin ions, including tin(IV) ions are examples of ions that can be used in the organometallic compounds for the formation of tin oxide strands. The tin oxide strands may comprise fluorine-doped tin oxide, indium-doped tin oxide, and/or may take the form of tin oxide nanowires. Doped metal oxide strands can be made by running a small number of SIM cycles using the selected dopant element, such as indium, among the multiple SIM cycles used to form the strands. The number of dopant SIM cycles used would depend on the desired level of doping. The synthesis of an electrically conductive NU-1000 MOF having continuous strands of oxy-tin(IV) oriented exclusively along its c-axis is illustrated in the Example. Other metal ions that can be used to form the electrically conductive metal oxide strands include indium and cerium. Metal ions that can be used to form non-electrically conductive MOFs include cobalt, nickel, and copper.
Various aspects of the inventions described herein are based, at least in part, on the inventors' discovery that continuous electrically conducting strands can be formed by enshrouding electrically insulating nodes in the MOFs with conductive oxides when the organometallic compound deposition is carried out from a condensed phase (i.e., for a liquid solution), rather than in vacuum. Without intending to be bound to any particular theory, it is believed that heat is released at a much slower rate during the reactions in the condensed phase relative to the heat release in a vacuum based deposition. This slower heat release prevents the reactive ligands from boiling off and allows the organometallic compounds to graft over the surface of the nodes to such an extent that a continuous electrically conductively pathway is created through the MOF. The continuous strands formed within the pores of the MOFs can be parallel, running along the same axis within the MOF.
The condensed-phase reactions between the organometallic complexes and the MOFs nodes in the initial SIM cycle and the secondary hydroxo, aquo, and/or oxo ligands in subsequent SIM cycles can be carried by dissolving the MOFs and the organometallic complexes in an organic solvent, such as heptane. Suitable organometallic compounds that can be used in the SIM synthesis include bis(N,N′-di-i-propylacetamidinato)tin(II). Other illustrative examples of organometallic compounds that can be used in the SIM synthesis include bis(N,N′-di-i-propylacetamidinato)cobalt, bis(N,N′-di-i-propylacetamidinato)nickel, and bis(dimethylamino-2-propoxy)copper. Guidance regarding the selection of other organometallic compounds can be found in the existing literature for atomic layer deposition of metal-containing materials.
The electrically conductive strands formed via SIM can be effectively one-dimensional, having widths of 5 nm or less, 2 nm or less, and 1 nm or less and can be oriented along a single axis of the MOF crystal, such as the c-axis. As a result, the electrical conductivity can be highly anisotropic—and this behavior can extend to thermal conductivity. In addition, because the electrically conductive MOFs retain their mesoporosity, they can be used in aqueous electrocatalysis and other applications where electrical conductivity and high internal surface areas are desirable. By way of illustration, the porosity of the electrically conductive MOFs is typically reduced by 50% or less relative to the MOF starting crystals, with channel diameters that are reduced by, for example, less than 20%.
Embodiments of the electrically conductive MOF materials can have electrical conductivities of 1×10−6 S/cm or higher. This includes embodiments of the MOF materials that have electrical conductivities of 1×10−7 S/cm or higher and 2×10−7 S/cm or higher.
Embodiments of the electrically conductive MOF materials can have BET surface areas of 300 m2/g or higher. This includes embodiments of the MOF materials that have BET surface areas of 500 m2/g or higher.
Methods of measuring electrical conductance and BET surface area are described in the Example. Unless otherwise indicated, measured and measurable values recited herein refer to those values at room temperature (˜25° C.) and atmospheric pressure.
Hydrogen sensing is an example of an application for the electrically conductive MOFs. Such sensors take advantage of the reversible H2 doping of the inorganic oxide (e.g., metal oxide) strands in the MOFs. In a hydrogen sensor, an electrically conductive MOF of the type described herein, is exposed to an environment containing (or suspected of containing) hydrogen. As a result of this exposure, the metal oxide becomes reversibly doped and an increase in the conductance of the electrically conductive MOF material can be measured. The conductance increase can be measured directly or it can be measured indirectly by measuring a decrease in the material's resistance.
This Example illustrates an inorganic approach to engendering electrical conductivity within a representative mesoporous Zr-MOF, NU-1000. (See, e.g., Mondloch et al., 2013) Briefly, the multiple reactive aqua and hydroxo ligands of the eight-connected nodes of NU-1000 and the compound's mesoporosity (31 Å diameter hexagonal pores) were used to install tin(IV) ions via the SIM process and fabricate continuous, transparent strands of tin-oxide—essentially, conductive glass (cf, fluorine-doped (bulk) tin oxide, indium-doped (bulk) tin-oxide, arrays of tin-oxide nano-wires, etc.). The self-limiting nature of SIM chemistry was relied upon to avoid over-filling MOF channels and thereby eliminate the material's inherent mesoporosity. Indeed, MOF channel functionalization with conductive tin oxide is accompanied by a decrease of effective mesopore diameter of only a few angstroms (˜31→27 Å). Finally, this Example shows how the engendered conductivity can be used to render the MOF functional as a rapidly responding, resistive sensor for hydrogen gas.
Chemicals. All chemicals including N,N-dimethylformamide (DMF) (Fisher Chemical, ≥99.8%), benzoic acid (Sigma-Aldrich, ≥99.5%), zirconyl chloride octahydrate (Sigma-Aldrich, 98%), hydrochloric acid (HCl) (36.5-38.0%, Avantor), acetone (Fisher Chemical, ≥99.5%), bis(N,N′-di-i-propylacetamidinato)tin(II) (Sn(amd)2) (Strem, 99%), and heptane (Sigma-Aldrich, anhydrous, 99%) were used as received. Deionized water was used for preparing aqueous solutions. The chemicals for synthesizing the 1,3,6,8-tetrakis(p-benzoic acid)pyrene (H4TBAPy) linkers were all the same as those reported in a previous work. (See, e.g., Wang, T. C., et al., Nat. Protocols 2016, 11 (1), 149-162.)
Synthesis of tin oxide installed in NU-1000 (Sn-SIM). NU-1000 was synthesized according to the procedures reported in a previous study. (See, e.g., Wang, et al., 2016) Thereafter, 120 mg of Sn(amd)2 was dissolved in 20 mL of anhydrous heptane in an argon-filled glove box, and 80 mg of NU-1000 was added in to the obtained solution. The mixture was kept for 24 h in the glove box at room temperature. The mixture was then decanted, and the powder was washed with 20 mL of heptane two times, waiting at least 6 h in between each washing step. Fresh heptane (20 mL) was then added, and the mixture was kept overnight. After the final decantation, the obtained sample was removed from the glove box and dried in an oven at 100° C. in air overnight to remove the residual heptane. Thereafter, equal or less than 50 mg of the obtained powder was packed in a custom-made stainless steel powder sample holder, and the holder was placed in an atomic layer deposition (ALD) chamber (Savanah S100 system, Ultratech Cambridge Nanotech) held at 120° C. The water dosing was conducted by utilizing the following ALD sequence (time in s): t1-t2-t3, where t1 is the water pulse time, t2 is the exposure time (i.e., the time without pumping), and t3 is the pumping time. The water source was kept at room temperature, and the deposition was conducted by utilizing 100 cycles of 0.015-120-120 sequences. The nitrogen flow rate in the ALD chamber was 5 sccm during the whole process. The sample obtained after this process was designated “Sn-SIM (1 cycle).” Thereafter, NU-1000 was replaced by 80 mg of Sn-SIM (1 cycle) and all the experimental steps mentioned above were conducted again, resulting in the sample designated “Sn-SIM (2 cycle).” The whole process was conducted again starting with 80 mg of Sn-SIM (2 cycle) to synthesize the sample designated “Sn-SIM (3 cycle),” and again starting with 80 mg of Sn-SIM (3 cycle) to make “Sn-SIM (4 cycle).”
Preparation of electrodes. IDEs with 180 pairs of platinum fingers and a 5-μm gap (MicruX Technologies, ED-IDE3-Pt) were used for all current-voltage (I-V) and gas sensing measurements. NU-1000 and all the Sn-SIM materials were first dispersed in acetone to make suspensions by sonication, with a concentration of 10 mg/mL. Thereafter, NU-1000/IDE, Sn-SIM (1 cycle)/IDE, Sn-SIM (2 cycle)/IDE, Sn-SIM (3 cycle)/IDE, and Sn-SIM (4 cycle)/IDE were prepared by successively drop-casting 2 μL of corresponding suspensions on bare IDEs until full coverage was achieved. For conductivity measurements, 2 μL of diluted suspensions (0.1 mg/mL) were drop-casted once on bare IDEs to deposit bridging crystals between the gaps of IDEs. All the obtained electrodes were dried at room temperature before any measurement.
Instrumentation. Powder XRD (PXRD) patterns were collected on a Rigaku ATX-G workstation. Nitrogen adsorption isotherms were collected on an ASAP 2020 (Micromeritics). Inductively coupled plasma optical emission spectroscopy (ICP-OES) measurements were conducted on a Thermo iCAP 7600 and utilized to obtain the Sn loadings of all samples; the procedure for digesting MOF samples for ICP-OES measurements has been reported previously. (See, e.g., Mondloch et al., 2013) X-ray photoelectron spectroscopy (XPS) was measured on ESCALAB 250Xi, Thermo Scientific. SEM and EDS measurements were conducted on a Hitachi SU8030. Thermogravimetric analysis (TGA) was performed using a TA Instruments Q500 under air flow at a ramp rate of 10° C./min from 25 to 600° C.
Synchrotron PXRD data suitable for DED analysis were collected at beamline 17-BM at the Advanced Photon Source using 17.0 keV (0.45220 Å). (See, e.g., Yakovenko, A. A. et al., J. Appl. Crystallogr. 2013, 46 (2), 346-353.) Data were collected using an amorphous silicon-based area detector. Geometric corrections and reduction to one-dimensional data used GSAS-II. (See, e.g., Toby, B. H., et al., J. Appl. Crystallogr. 2013, 46 (2), 544-549.) Lattice parameters and peak intensities were extracted from diffraction patterns via Le Bail whole-pattern fitting using Jana2006 based on the reported structural model for NU-1000 (csq topology, P61mmm, a˜40 Å, c˜17 Å). (See, e.g., Mondloch et al., 2013; Le Bail, A., J. Non-Cryst. Solids 1995, 183 (1), 39-42; and Petricek, V., et al., Zeitschrift fur Kristallographie—Crystalline Materials, 2014; Vol. 229, p 345.) Lattice and pseudo-Voigt profile parameters were refined over a 0.5-10° 20 range. Structure envelopes were generated using the intensities of low-index reflections. DED maps were then obtained via subtraction of the envelope for pristine NU-1000 from the envelope for Sn-SIM materials.
IV curves of the IDEs deposited with NU-1000 and Sn-SIM materials were measured on a CHI 660 potentiostat (CH Instruments, Inc., USA), with a two-electrode setup connected to a drop-cell connector (MicruX Technologies, ED-DROP-CELL) with the IDE. All IV curves were measured in air at room temperature. Gas sensing experiments were conducted in a sealed glass cell installed with one gas inlet, one gas outlet, and two copper wires which connected the IDE inside the cell to a portable potentiostat (CHI 1200, CH Instruments, Inc., USA). 5% hydrogen in nitrogen or air continuously flowed into the cell through the gas inlet. A constant voltage of 1 V was applied to the IDE during all gas sensing experiments.
Estimation of volumetric surface area. The volume of the unit cell in NU-1000 is 22145.3 Å3 according to the crystal structure, including three hexa-zirconium nodes and six TBAPy linkers. The molecular weight of the atoms presented in each unit cell was calculated by considering the atoms presented in NU-1000 and the installed Sn atoms, as the number of Sn on each node had been obtained by ICP-OES. Two new oxo ligands were considered with each Sn atom. Thereafter, according to the molecular weight and the volume of unit cell, the densities of NU-1000, Sn-SIM (1 cycle), Sn-SIM (2 cycle), and Sn-SIM (3 cycle) were estimated to be 0.49, 0.63, 0.80, and 0.96 g/cm3, respectively. The galvanometric BET surface areas of these materials can then be converted into volumetric BET surface areas by multiplying their densities.
Estimation of conductivity. For conductivity measurements, a dilute suspension (0.1 mg/mL) of each sample was coated on a bare IDE, and the I-V curve of each coated IDE was measured in air after drying. The number of bridging crystals between the gaps of each IDE was estimated via SEM after the I-V measurements. The approach for measuring electrical conductivity by bridging microcrystals between the five-micrometer gaps prevented the estimation of conductivity contributed from the tin oxide installed in the NU-901-like second phase in the middle (about 20%) of those crystals. The electrical conductivity (a) of each sample was then estimated by the following equation,
where G is the electrical conductance estimated from the slope within the linear region of the I-V curve between +0.5 V and −0.5 V, l is the gap width of the IDE, which is 5 μm, n is the number of bridging crystals between the gaps of the full IDE, and A is the average cross-section area of single MOF crystal, which is 5.7 μm2 estimated by assuming that the cross section of the crystal is a regular hexagon with an average maximal diameter of 2.96 μm.
PXRD measurements (
The persistence of MOF crystallinity makes possible the collection of high resolution (synchrotron derived) PXRD data for various Sn-SIM NU-1000 samples. Subsequent DED analysis can provide information about the siting of SIM-installed tin ions. Briefly, however, DED maps were obtained by subtracting the X-ray derived structure envelope for pristine NU-1000 from that for a tin-modified version.
DED mapping with extra electron density from tin oxide was obtained with Sn-SIM (3 cycle), as shown in
To gauge the porosity of the MOF following tin-oxide installation of tin, N2 adsorption-desorption experiments were conducted at 77K; the gravimetric isotherms of NU-1000, Sn-SIM (1 cycle), Sn-SIM (2 cycle), and Sn-SIM (3 cycle) were obtained. The corresponding volumetric isotherms are shown in
The nitrogen isotherms returned BET surface areas of 2100, 1410, 1130, and 680 m2/g, for NU-1000, Sn-SIM (1 cycle), Sn-SIM (2 cycle), and Sn-SIM (3 cycle), respectively. The significant decrease in gravimetric surface area can be attributed, in part, to the aforementioned mass gain due to tin incorporation; the unit-cell mass of Sn-SIM (3 cycle) is about double of that of NU-1000 due to the presence of 14 tin ions (and charge-balancing oxy ligands) for each Zr6 node. Volumetric parameters, therefore, may be more instructive than gravimetric parameters. (For simplicity, and in the absence of more detailed information, the samples were treated as if each tin ion was accompanied by two new oxo ligands.) The volumetric BET surface areas were 1020, 890, 900, and 650 m2/cm3, for NU-1000, Sn-SIM (1 cycle), Sn-SIM (2 cycle), and Sn-SIM (3 cycle), respectively. In other words, roughly two-thirds of the initial surface area, and slightly more than half the total initial pore volume (
To investigate electrical conductivity of NU-1000 and the modified MOFs, MOF suspensions were drop-casted on IDEs featuring electrode spacings of 5 μm, which can be spanned by the microcrystals of ˜10 μm in length. The drop-casted MOF suspensions were then allowed to dry in air at room temperature.
The combined results indicate that the presence of tin-oxide and continuous c-axis strands of the added oxide resulted in the conductivity; see
It was reasoned that the conductivity of Sn-SIM would be susceptible to modulation by hydrogen and that Sn-SIM/IDE assemblies could function as H2 sensors.
The word “illustrative” is used herein to mean serving as an example, instance, or illustration. Any aspect or design described herein as “illustrative” is not necessarily to be construed as preferred or advantageous over other aspects or designs. Further, for the purposes of this disclosure and unless otherwise specified, “a” or “an” means “one or more.”
The foregoing description of illustrative embodiments of the invention has been presented for purposes of illustration and of description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed, and modifications and variations are possible in light of the above teachings or may be acquired from practice of the invention. The embodiments were chosen and described in order to explain the principles of the invention and as practical applications of the invention to enable one skilled in the art to utilize the invention in various embodiments and with various modifications as suited to the particular use contemplated. It is intended that the scope of the invention be defined by the claims appended hereto and their equivalents.
The present application claims priority to U.S. provisional patent application No. 62/701,131 that was filed Jul. 20, 2018, the entire contents of which are incorporated herein by reference.
This invention was made with government support under DE-SC0001059 awarded by the U.S. Department of Energy. The government has certain rights in the invention.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US19/42366 | 7/18/2019 | WO | 00 |