1. Field of the Invention
The present invention relates to a method for analyzing the properties of an organic material such as a thermosetting resin and an apparatus therefor, in particular to an analysis method for analyzing the change of structure dimensions caused by reaction hardening and moisture absorption and to an apparatus therefor.
2. Description of the Related Art
Simulation methods for predicting the behavior of a resin formed by injection molding and “warping” deformation of a molded product have hitherto been known (refer to Patent documents 1 and 2, for example).
The technologies described in such Patent documents 1 and 2 are those that predict the behavior of molten resin in a metal mold at the processes of filling, pressure keeping and cooling and thereafter predict the warping deformation of the resultant molded product on the basis of a fundamental expression formulated by the Finite Element Method.
Here, the Finite Element Method (FEM) is a means of predicting the overall behavior (in this case, deformation and stress distribution) of an object actually having complicated shape and properties by decomposing the object into small parts (elements) each having simplified shape and properties, approximately expressing the properties of each element by using each mathematical equation, combining the equations, and obtaining a solution that is compatible with all the equations.
The technologies described in the aforementioned Patent documents 1 and 2 are those that predict the behavior of a resin formed by injection molding and the “warping” deformation of a molded product and the warping or the like of a material for an electronic component or a printed circuit board is generally analyzed by using the aforementioned Finite Element Method as shown in
(i) To measure the properties (hardness, a Young's modulus, the amounts of expansion and contraction at each temperature, and others) of a material that composes an electronic component, a printed circuit board or the like to be analyzed and then obtain the material property data.
(ii) To give the material property data and the structure data of a printed circuit board or the like to be analyzed and obtain structure model data (meshed element data and node data) and the material property data corresponding to each meshed element by a meshing means 10.
(iii) To give process data that defines the constraint conditions of a model, temperature, humidity, forced displacement, load, time, etc. and the changes of those, the structure model data and the material property data to a numerical analysis means 20, apply numerical analysis, and obtain the analysis results of the changes of the structure dimensions such as the “warping” deformation or the like of the printed circuit board or the like to be analyzed.
Patent document 1: JP-A No. 7-186228
Patent document 2: JP-A No. 8-230008
Thermosetting resin is used as a material for an electronic component or a printed circuit board in many cases.
The thermosetting resin is subjected to cross-linking reaction by moisture absorption or the radiation of ultraviolet ray, electron beam, laser beam or the like and hardens as a result of the cross-linking reaction. The cross-linking reaction is an irreversible process and forms a network structure that hinders the free motion of a polymer chain regardless of the temperature of the material. Further, the material contracts when cross-linking occurs.
Such cross-linking reaction contraction is determined by a temperature and a retention time at the temperature. For that reason, a polymer component under thermal load causes contraction warping during its use.
Further, the mechanical properties of such an organic material, such as hardness, a Young's modulus and a linear expansion coefficient, are changed by moisture absorption and also the volume thereof is increased by moisture absorption.
As shown in the figure, reaction contraction occurs at the temperature rise of the first cycle but does not occur at the temperature rise of the second and subsequent cycles.
As mentioned above, in the case of thermosetting resin used as a material for printed circuit boards and LSIs, the structure change is not necessarily the same between the first cycle and the second and subsequent cycles and the dimensions after once subjected to temperature rise and drop do not necessarily return to the previous dimensions.
This is presumably because some portions that are not cross-linked remain and the cross-linking proceeds with the lapse of time at the portions.
As a result, there have been phenomena wherein, for example, unexpected dimensions are obtained when a printed circuit board is fabricated and then subjected to a temperature rise or the dimensions do not return to the original dimensions when it is subjected to a temperature drop again. Further, even in the state of retaining a material at a constant temperature, if some portions that are not cross-linked remain, the resin hardens and contracts with the lapse of time and resultantly the dimensions thereof change or deformation such as warping occurs. Furthermore, in addition to the aforementioned expansion and contraction caused by the temperature change, as mentioned above, the mechanical properties such as hardness, a Young's modulus, a linear expansion coefficient and the like are changed by moisture absorption and the volume also increases.
Up to now, the structure analysis that takes into consideration the properties of a material during temperature rise and drop processes, the properties thereof at each temperature and retention time, and the properties thereof such as expansion caused by the moisture absorption of a resin as mentioned above has not been implemented. As a consequence, the problem has been that an electronic component, a printed circuit board or the like deforms unexpectedly after it is fabricated and resultantly desired performances are not secured.
The present invention has been established in view of the above situation and the object thereof is to make it possible to analyze the change of the structure dimensions of an organic material in consideration of the change of the material properties corresponding to temperature rise and drop processes, temperature and a retention time and an absorbed moisture amount as described above.
To solve the aforementioned problems, as one preferred mode, the present invention comprises the steps:
(1) to read out the property data of an organic material to be analyzed at each temperature from a material property database that stores the property data of organic materials including the linear expansion coefficient of the organic material at each temperature during a temperature rise process and the linear expansion coefficient thereof at each temperature during a temperature drop process, and numerically analyze the expansion and contraction properties of the organic material during the temperature rise and drop processes on the basis of the property data of the organic material including the linear expansion coefficients at each temperature,
(2) in the above item (1), to store in the material property database the linear expansion coefficient corresponding to the temperature gradient of the organic material to be analyzed or the linear expansion coefficient corresponding to a temperature and a retention time at the temperature of the organic material, read out the linear expansion coefficient corresponding to the temperature gradient or the linear expansion coefficient corresponding to the temperature and the retention time at the temperature from the material property database, and numerically analyze the expansion and contraction properties corresponding to the temperature gradient or the expansion and contraction properties of the organic material when the organic material is kept at a given temperature for a certain period of time, and
(3) in the above items (1) and (2), to store the moisture absorption expansion coefficient corresponding to each absorbed moisture amount in the material property database, read out the moisture absorption expansion coefficient corresponding to each absorbed moisture amount from the material property database, revise the linear expansion coefficient in accordance with the moisture absorption expansion coefficient, and numerically analyze the expansion and contraction properties of the organic material.
The present invention has made it possible: to numerically analyze the expansion and contraction properties of an organic material such as thermosetting resin during the temperature rise and drop processes, the expansion and contraction properties thereof corresponding to a temperature gradient, the expansion and contraction properties of the organic material when the organic material is kept at a given temperature for a certain period of time, or the expansion and contraction properties corresponding to a temperature and an absorbed moisture amount; and resultantly to analyze the warping and deformation of a structure including resin with a high degree of accuracy.
As a consequence, it becomes possible to prevent the occurrence of such a problem that an electronic component, a printed circuit board or the like that contains a resin material deforms unexpectedly after it is fabricated and thus desired performances cannot be obtained.
Other and further objects, features and advantages of the invention will appear more fully from the following description.
The analysis processing of an embodiment according to the present invention is explained in reference to
Firstly, material property data are obtained by measuring the properties (hardness, a Young's modulus, the amounts of expansion and contraction at each temperature, etc.) of a material composing an electronic component, a printed circuit board or the like to be analyzed as mentioned earlier. Here, in the embodiment according to the present invention, in addition to the aforementioned material properties which used to have been measured in the prior art, property data necessary to analyze the change of the material properties in accordance with temperature rise and drop processes, a temperature and a retention time and an absorbed moisture amount, such as “the amounts of expansion and contraction during the temperature rise and drop at the first cycle or the second and subsequent cycles,” “the amounts of expansion and contraction corresponding to a temperature and a retention time at the temperature,” “the amounts of expansion and contraction corresponding to a temperature and a temperature gradient,” “a moisture absorption expansion coefficient corresponding to an absorbed moisture amount,” “a Young's modulus corresponding to an absorbed moisture amount,” and the like are measured.
A numerical analysis model is produced by using a meshing means 10 by giving the aforementioned material property data and the structure data of an electronic component, a printed circuit board or the like to be analyzed.
That is, an analyzer, while having a conversation with the processing unit via an I/O unit 40, divides the structure data into elements, relates the above measured material properties to each of the elements, and produces a numerical analysis model comprising a structure model data (meshed element data and node data) and the material property data corresponding to each element. The material property data corresponding to each element is stored in a material property database 30. Here, the property data necessary to analyze the change of the material properties in accordance with temperature rise and drop processes, a temperature and a retention time, and an absorbed moisture amount as mentioned above are allocated to each element.
An example of data stored in the aforementioned material property database is shown in
In addition, other various property data required for analysis, such as a moisture absorption expansion coefficient for each absorbed moisture amount, a Young's modulus for each absorbed moisture amount, expansion and contraction amounts for each temperature and retention time, a linear expansion coefficient for each temperature and temperature gradient, and the like are stored as shown in
As shown in
(i) Process Data
Data that define the state of environment surrounding a material to be analyzed, such as the constraint conditions of a model, temperature, humidity, forced displacement, load, time and others, and the changes of those.
(ii) Analysis Definition Data
Data that define the material properties and the like necessary to analyze the changes of the material properties and the like corresponding to temperature rise and drop processes, a temperature and a retention time and an absorbed moisture amount.
Note that, in the above process data, the temperature, humidity, load, displacement that are mentioned above are set so as to be constant or increase or decrease gradually, the aforementioned subroutine 21 is called up during the implementation of numerical analysis, and the analysis proceeds on the basis of the analysis definition data defined in the above item (ii).
That is, as shown in
Further, in the case where analysis is carried out in consideration of an absorbed moisture amount, the numerical analysis means 20 obtains an absorbed moisture amount at each time and gives it together with the temperature to the subroutine 21. The subroutine 21 reads material property data based on a temperature and an absorbed moisture amount from the material property database 30 on the basis of the analysis definition data of the item (ii), obtains a linear expansion coefficient and others at each temperature and absorbed moisture amount, and gives them to a numerical analysis program.
The numerical analysis means 20 obtains the displacement of each element for temperature change, absorbed moisture amount change and others on the basis of the linear expansion coefficient and others and outputs the change of the structure dimensions as the analysis result as shown in
In
Next, the measured data are arranged and material properties under each combined condition of temperature, humidity and time are obtained (step S2). The obtained data are registered in the material property database 30 (step S3).
Subsequently, a numerical analysis model comprising structure model data and material property data is produced in reference to the material property database 30 as mentioned earlier (step S4) and numerical analysis input data are defined by using resin reaction contraction and moisture absorption expansion as material properties of linear expansion coefficient (step S5).
That is, whether or not the influences of reaction contraction and moisture absorption are taken into consideration is judged and, when analysis is carried out while the influences are taken into consideration, for example, following definitions are employed.
In the same way, parameters necessary for analysis, such as each linear expansion coefficient during a temperature drop process, the moisture absorption expansion coefficient for each absorbed moisture amount, the Young's modulus for each absorbed moisture amount, the amounts of expansion and contraction for each temperature and retention time, and others, as mentioned earlier are allocated. Likewise, also in the case where input temperature is the passage temperature of the second cycle, parameters are allocated respectively in the same way.
On the basis of the above definitions, the document on the definition of the analysis procedure is added to the numerical analysis program and the numerical analysis processing is carried out (steps S6 and S7).
In the numerical analysis processing, the numerical analysis program calls up the subroutine 21 as shown in
Firstly, the temperature increment ΔT is obtained from the numerical analysis program and whether the temperature rises or lowers is judged (steps S1 and S2).
If the temperature rises, the linear expansion coefficient corresponding to the temperature T at the time of the temperature rise is obtained from the material property database 30. On the other hand, if the temperature lowers, the linear expansion coefficient corresponding to the temperature T at the time of the temperature drop is obtained from the material property database 30 (steps S3 and S4). In this event, the relevant linear expansion coefficient is obtained in accordance with whether the temperature rise and drop defined in the aforementioned analysis definition are of the first cycle or the second and subsequent cycles.
Successively, whether or not the influence of moisture absorption expansion is taken into consideration is determined on the basis of the aforementioned analysis definition (step S5) and, when the influence of moisture absorption expansion is not taken into consideration, the procedure goes to the step S9 and the aforementioned linear expansion coefficient is given to the numerical analysis program.
On the other hand, when the influence of moisture absorption expansion is taken into consideration, the absorbed moisture amount is obtained from the numerical analysis program and the moisture absorption expansion coefficient and Young's modulus corresponding to the absorbed moisture amount are obtained from the material property database 30 (steps S6 and S7).
Thereafter, the linear expansion coefficient is revised with the moisture absorption expansion coefficient and Young's modulus corresponding to the absorbed moisture amount and the revised linear expansion coefficient is obtained (step S8) and given to the numerical analysis program (step S9).
Here, though the numerical analysis corresponding to the temperature rise and drop processes and the absorbed moisture amount is shown in the above flowchart, it is also acceptable to obtain, from the material property database 30, the property data such as the amounts of expansion and contraction corresponding to a retention time at a temperature, the amounts of expansion and contraction corresponding to a temperature gradient and others on the basis of the analysis definition defined as mentioned above and to numerically analyze the change of the structure dimensions of a resin corresponding to a temperature and a retention time, the change of the structure dimensions of a resin corresponding to the change of a temperature gradient and others.
As shown in the figure, by the embodiment according to the present invention, it has become possible to numerically analyze deformation such as warping caused by the hardening and contraction of the resin material 53 with a high degree of accuracy and to analyze beforehand unexpected deformation caused by the hardening and contraction of an electronic component, a printed circuit board or the like.
The foregoing invention has been described in terms of preferred embodiments. However, those skilled, in the art will recognize that many variations of such embodiments exist. Such variations are intended to be within the scope of the present invention and the appended claims.