Anisotropic biocomposite material, medical implants comprising same and methods of treatment thereof

Information

  • Patent Grant
  • 10869708
  • Patent Number
    10,869,708
  • Date Filed
    Monday, September 7, 2015
    8 years ago
  • Date Issued
    Tuesday, December 22, 2020
    3 years ago
Abstract
Reinforced biocomposite materials. According to at least some embodiments, medical implants are provided that incorporate novel structures, alignments, orientations and forms comprised of such reinforced bioabsorbable materials, as well as methods of treatment thereof.
Description
FIELD OF THE INVENTION

The present invention is of anisotropic biocomposite material, medical implants comprising same and methods of treatment thereof, and in particular to such material, implants and methods of treatment that have medical applications.


BACKGROUND OF THE INVENTION

The mechanical strength and modulus (approximately 3-5 GPa) of non-reinforced resorbable polymers is insufficient to support fractured cortical bone, which has an elastic modulus in the range of approximately 15-20 GPa. For example, in an article the bending modulus of human tibial bone was measured to be about 17.5 GPa (Snyder S M Schneider E, Journal of Orthopedic Research, Vol. 9, 1991, pp. 422-431). Therefore, the indications of existing medical implants constructed from resorbable polymers are limited and their fixation usually requires protection from motion or significant loading. These devices are currently only a consideration when fixation of low stress areas is needed (i.e. non-load bearing applications) such as in pediatric patients or in medial malleolar fractures, syndesmotic fixation, maxillofacial, or osteochondral fractures in adults.


A new class of reinforced composite biomaterials (biocomposites) has been recently introduced wherein a bioabsorbable and biocompatible polymer is reinforced by bioabsorbable, biocompatible glass fibers. These materials can achieve improved mechanical properties. These materials also involve a compatibilizer to bind the polymer to the reinforcing fibers. Examples of such materials are described in the following two patent applications, which are included fully herein by reference as if fully set forth herein:


1. Biocompatible composite and its use (WO2010122098)


2. Resorbable and biocompatible fibre glass compositions and their uses (WO2010122019)


These materials have been further described and characterized in publications associated with these patents including

  • 1. Lehtonen T J et al. Acta Biomaterialia 9 (2013) 4868-4877
  • 2. Lehtonen T J et al. J Mech Behavior BioMed Materials. 20 (2013) 376-386


The development of this class of materials described in the background art has focused on the composition of the materials: the bioabsorbable polymer, the reinforcing mineral fiber, the compatibilizer, and the combinations between them.


These compositions have been demonstrated to be capable of achieving mechanical properties superior to the mechanical properties previously achieved with bioabsorbable polymers alone.


However, while material composition is one parameter that can affect mechanical properties of a medical implant, when it comes to composite materials, the material composition does not by itself ensure mechanical properties that are sufficient for the implant to achieve its desired biomechanical function. In fact, reinforced composite medical implants with identical compositions and identical geometries can have vastly different mechanical properties. Furthermore, even within the same implant, mechanical properties can vary greatly between different mechanical axes and between different types of mechanical strength measurements.


SUMMARY OF THE INVENTION

The background art does not teach or suggest biocomposite materials that have one or more desirable mechanical characteristics. The background are also does not teach or suggest such materials that can achieve a desired biomechanical function.


By “biocomposite material” it is meant a composite material that is biologically compatible or suitable, and/or which can be brought into contact with biological tissues and/or which can be implanted into biological materials and/or which will degrade, resorb or absorb following such implantation.


By “biocompatible” it is meant a material that is biologically compatible or suitable, and/or which can be brought into contact with biological tissues, and/or which can be implanted into biological materials.


The present invention, in at least some embodiments, relates to reinforced biocomposite materials which overcome the drawbacks of the background art. According to at least some embodiments, medical implants are provided that incorporate novel structures, alignments, orientations and forms comprised of such reinforced bioabsorbable materials. These medical implants have unique mechanical properties. They have great clinical benefit in that these implants can have mechanical properties that are significant greater than those of the currently available bioabsorbable polymer implants. The term “mechanical properties” as described herein may optionally include one or more of elastic modulus, tensile modulus, compression modulus, shear modulus, bending moment, moment of inertia, bending strength, torsion strength, shear strength, impact strength, compressive strength and/or tensile strength.


According to at least some embodiments, the implants have improved mechanical properties in at least one mechanical axis or parameter as compared with at least one other mechanical axis or parameter within the same implant. The implants can therefore be considered anisotropic. A mechanical axis as defined herein can be any line drawn through the implant, optionally passing through the center of the implant. A mechanical parameter as defined herein can include bending strength and stiffness (resistance to bending force), tensile strength and stiffness (resistance to tensile force), compression strength and stiffness (resistance to compression force), shearing strength and stiffness (resistance to shearing force), or torsional strength and stiffness (resistance to torsional force).


Optionally, the improved mechanical properties in one axis or parameter are increased by at least 50% as compared with another axis or parameter and are preferably increased by at least 100%, more preferably by at least 200%, 300%, 400%, and most preferably by at least 500% or any integral value in between.


Optionally, the improved mechanical properties in one axis or parameter of the implant are alternatively or additionally increased by at least 50% as compared with an implant of identical composition but with amorphous or non-aligned internal structure and are preferably increased by at least 100%, more preferably by at least 200%, 300%, 400%, and most preferably by at least 500% or any integral value in between.


Optionally, the improved mechanical property is strength and the strength in one axis or parameter is increased by at least 50 MPa as compared with another axis or parameter. Preferably, the strength is increased by at least 100 MPa, more preferably by at least 200 MPa, 300 MPa, 400 MPa, and most preferably by at least 500 MPa or any integral value in between.


Optionally, the improved mechanical property is strength and the strength in one axis or parameter of the implant is alternatively or additionally increased by at least 50 MPa as compared with an implant of identical composition but with amorphous or non-aligned internal structure, and preferably are increased by at least 100 MPa, more preferably by at least 200 MPa, 300 MPa, 400 MPa, and most preferably by at least 500 MPa or any integral value in between.


Optionally, the improved mechanical property is elastic modulus and the modulus in one axis or parameter is increased by at least 3 GPa as compared with another axis or parameter. Preferably, the modulus is increased by at least 5 GPa, more preferably by at least 8 GPa, 12 GPa, 16 GPa, and most preferably by at least 20 GPa or any integral value in between.


Optionally, the improved mechanical property is elastic modulus and the modulus in one axis or parameter of the implant is alternatively or additionally increased by at least 3 GPa as compared with an implant of identical composition but with amorphous or non-aligned internal structure. Preferably, the modulus is increased by at least 5 GPa, more preferably by at least 8 GPa, 12 GPa, 16 GPa, and most preferably by at least 20 GPa or any integral value in between.


According to at least some embodiments, anisotropocity of one or more segments of implant in one mechanical axis as compared with amorphous (non-aligned) material is preferably greater than 10%, 50%, 100%, 200%, 300%, 500% or any integral value in between.


According to at least some embodiments, anisotropocity of one or more segments of implant in one mechanical axis as compared with another axis is preferably greater than 10%, 50%, 100%, 200%, 500%, 1000% or any integral value in between.


According to at least some embodiments, there is provided relative higher strength in one mechanical axis as compared with another (e.g. bending over tensile) of 10%, 50%, 100%, 200%, 300% or any integral value in between.


According to at least some embodiments, there is provided relative higher elastic modulus as measured in one mechanical axis as compared with another of 10%, 30%, 50%, 100%, 200% or any integral value in between.


Without wishing to be limited by a closed list or a single hypothesis, the biocomposite implants described herein represent a significant benefit over metal or other permanent implants (including non absorbable polymer and reinforced polymer or composite implants) in that they are absorbable by the body of the subject receiving same, and thus the implant is expected to degrade in the body following implantation. Again without wishing to be limited by a closed list or a single hypothesis, they also represent a significant benefit over prior absorbable implants since they are stronger and stiffer than non-reinforced absorbable polymer implants in at least one mechanical axis. In fact, these reinforced composite polymer materials can even approach the strength and stiffness of cortical bone, making them the first absorbable materials for use in load bearing orthopedic implant applications.


On an underlying level, there is a great difference between the reinforced biocomposite implants and previous implants from metal, plastic, and other traditional medical implant materials. Traditional medical implant materials are isotropic such that their mechanical properties are identical in all axes. This simplifies implant design as the mechanical strength of the implant is determined solely based on the geometry of the implant and the inherent material properties of the material. Without wishing to be limited by a closed list or a single hypothesis, for reinforced biocomposite implants, the inherent material properties of the biocomposite (i.e. the biocomposite in amorphous or non-aligned form) are actually quite low and can approximate the mechanical properties of the polymer alone. As such, implant geometries for implants constructed from these biocomposite materials does not inherently determine implants that are mechanically strong or stiff.


However, the medical implants of the present invention in at least some embodiments are able to exceed the mechanical properties of previous bioabsorbable implants, including previous biocomposite implants in one or more mechanical axes and in one or more mechanical parameters. Preferably these implants feature structures and forms in which the reinforcing fibers are aligned within the implant in order to provide the implant load bearing strength and stiffness in the axes in which these properties are biomechanically required. Thus, either the entire implant or segments of the implant are anisotropic (i.e. they have different mechanical properties in different axes). With these anisotropic implants, the implant mechanical design cannot rely solely on the geometry of each part. Rather, the specific alignment of the reinforcing fibers within the implant and the resulting anisotropic mechanical profile are a key parameter in determining the biomechanical function of the implant.


Aside from the mechanical considerations related to the anisotropic medical implants, there are additional limitations in that medical implants using these reinforced biocomposite materials cannot be designed according to existing implant designs due to the limitations associated with producing parts from these composite materials.


For example, metal implants or permanent polymer implants may be produced by machining. Even fiber-reinforced permanent polymer implants may be machined without adversely affecting the mechanical properties. However, absorbable, reinforced composite material implants cannot be machined without causing damage to the underlying material since machining will expose reinforcing fibers from the polymer, thus causing their strength to degrade quickly once they are directly exposed to body fluid following implantation.


At the other end of the spectrum, pure polymer or very short (<4 mm) fiber-reinforced polymer implants may be manufactured using straightforward injection molding processes. Injection molding of these materials does not, however, result in sufficiently strong implants. Therefore, specialized designs and production methods are required in order to design and produce an implant that can benefit from the superior mechanical properties of the previously described reinforced bioabsorbable composite materials.


The term “biodegradable” as used herein also refers to materials that are degradable, resorbable or absorbable in the body.


The term “load bearing” optionally also includes partially load bearing. According to various embodiments, the load bearing nature of the device (implant) may optionally include flexural strengths above 200 MPa, preferably above 300 MPa, more preferably above 400 MPa, 500 MPa, and most preferably above 600 MPa or any integral value in between.


Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. The materials, methods, and examples provided herein are illustrative only and not intended to be limiting.





BRIEF DESCRIPTION OF THE DRAWINGS

The invention is herein described, by way of example only, with reference to the accompanying drawings. With specific reference now to the drawings in detail, it is stressed that the particulars shown are by way of example and for purposes of illustrative discussion of the preferred embodiments of the present invention only, and are presented in order to provide what is believed to be the most useful and readily understood description of the principles and conceptual aspects of the invention. In this regard, no attempt is made to show structural details of the invention in more detail than is necessary for a fundamental understanding of the invention, the description taken with the drawings making apparent to those skilled in the art how the several forms of the invention may be embodied in practice.


In the drawings:



FIG. 1 shows some exemplary plates according to at least some embodiments of the present invention;



FIG. 2 shows the anisotropic properties of a bio-composite plate as demonstrated by the large difference in mechanical properties of samples with identical compositions, but with a majority of layers aligned at either 0° (Parallel) or 90° (Perpendicular) to the longitudinal axis of the implant sample (n=4);



FIGS. 3A and 3B show representative examples of samples. FIG. 3A shows a sample with majority of layers with fiber orientation perpendicular to implant longitudinal axis. FIG. 3B shows a sample with majority of layers with fiber orientation parallel to implant longitudinal axis;



FIG. 4 shows that the anisotropic properties of a bio-composite plate are directly affected by fiber orientation, as demonstrated by the large difference in mechanical properties of samples with identical compositions, but with non-aligned layers (Amorphous) or with layers aligned at either 0° (Parallel) or 90° (Perpendicular) to the longitudinal axis of the implant sample (n=4);



FIG. 5A-C show representative sample examples. FIG. 5A shows an amorphous fiber orientation sample; FIG. 5B shows a sample with majority of layers with fiber orientation perpendicular to implant longitudinal axis. FIG. 5C shows a sample with majority of layers with fiber orientation parallel to implant longitudinal axis;



FIG. 6 shows elastic modulus after exposure of exemplary biocomposite samples to forced degradation;



FIG. 7 shows flexural strength after exposure of exemplary biocomposite samples to forced degradation;



FIGS. 8A and 8B are photographs of a representative hollow pin implant, 5 cm length, 2 mm OD, 1 mm ID. FIG. 8A is a photo of the pin along its length; FIG. 8B is a photo of the cross-section of the pin;



FIGS. 9A and 9B are photographs of a representative pin, 5 cm length, 2 mm OD. FIG. 9A is a photo of the pin along its length; FIG. 9B is a photo of the cross-section of the pin.



FIG. 10 shows the decrease in mechanical properties due to incubation under conditions that force degradation; and



FIGS. 11A and 11B demonsrate a graphical finite elements simulation. FIG. 11A shows force distribution on a hollow cylinder pin implant with a wall thickness made of 5 layers as demonstrated in FIG. 11B.





DETAILED DESCRIPTION OF SOME EMBODIMENTS

A medical implant according to at least some embodiments of the present invention is suitable for load-bearing orthopedic implant applications and comprises one or more bioabsorbable materials where sustained mechanical strength and stiffness are critical for proper implant function.


According to at least some embodiments of the present invention, there is provided orthopedic implants, such as those for bone fixation, made from reinforced bioabsorbable composite materials. Specifically, implants according to at least some embodiments incorporate characteristics, features, or properties that can either only be achieved using the reinforced bioabsorbable composite materials or are specifically advantageous for implants comprised of these types of materials, or optionally a combination of both in a single implant.


Without wishing to be limited by a closed list, the material-specific design benefits are optionally provided by one or more of the following unique characteristics of implants manufactured from this material:


1. Absorbable structural implants wherein strength and stiffness properties are anisotropic. The bending resistance and other mechanical properties of these implants depends greatly on the specific design of the part and of the alignment of reinforcing fibers within the part. It is therefore possible to design such implants efficiently such that they provide sufficient support in the necessary axes (for example, flexural stiffness) without comprising an excessive amount of material that would provide equivalent support in the remaining axes (for example, tensile stiffness).


2. Low profile/minimally invasive/material efficient design for absorbable implant that take advantage of the strength and stiffness characteristics of the reinforced absorbable composite material to create implants that achieve bone fixation with minimal profile. By “minimal profile”, it is meant that the implant is reduced in size in at least one dimension in comparison with an equivalent currently available implant that is not made from such composite material.


3. Load bearing absorbable bone implants, as opposed to previous absorbable implants which did not approach the stiffness of cortical bone.


4. Small functional features, such as anchors, ridges, teeth, etc that require the reinforcement in order to be strong enough to be functional. Previous absorbable materials may not have had sufficient strength for such features.


5. The capability of being produced according to fiber-reinforced composite specific manufacturing techniques such as compression molding, pultrusion, etc.


6. Reduced damage to surrounding tissues, including both soft tissues and bone tissues, as compared with the trauma of stress risers or stress shielding that can arise from use of high modulus (such as metal) implants.


The present invention, according to at least some embodiments, thus provides medical implants that are useful as structural fixation for load-bearing purposes, exhibiting sustained mechanical properties.


The present invention, according to at least some embodiments, further comprises a biodegradable composite material in which the drawbacks of the prior art materials can be minimized or even eliminated, i.e. the composite retains its strength and modulus in vivo for a time period sufficient for bone healing for example. Mechanical strength as used here includes, but is not limited to, bending strength, torsion strength, impact strength, compressive strength and tensile strength.


The presently claimed invention, in at least some embodiments, relate to a biocomposite material comprising a biocompatible polymer and a plurality of reinforcing fibers, wherein said reinforcing fibers are oriented in a parallel orientation.


The biocomposite material has one or more mechanical properties which feature an increased extent or degree as compared to such a material with reinforcing fibers oriented in a non-parallel orientation. Optionally such a non-parallel orientation is a perpendicular or amorphous (non-oriented) orientation, elastic modulus, tensile modulus, compression modulus, shear modulus, bending moment, moment of inertia, bending strength, torsion strength, shear strength, impact strength, compressive strength and/or tensile strength. The increased extent or degree may optionally be at least twice as great, at least five times as great, at least ten times as great, at least twenty times as great, at least fifty times as great, or at least a hundred times as much, or any integral value in between.


Optionally the mechanical properties can comprise any one of Flexural strength, Elastic modulus and Maximum load, any pair of same or all of them. Optionally density and/or volume are unchanged or are similar within 5%, within 10%, within 15%, within 20%, any integral value in between or any integral value up to 50%.


Optionally the biocomposite implant as described herein is swellable, having at least 0.5% swellability, at least 1%, 2% swellability, and less than 20% swellability, preferably less than 10% or any integral value in between.


Optionally, the swellability in one mechanical axis is greater than the swellability in a second mechanical axis. Preferably the difference in swelling percentage (%) between axes is at least 10%, at least 25%, at least 50%, or at least 100%, or any integral value in between.


After exposure to biological conditions for 1 hour, 12 hours, 24 hours, 48 hours, five days, one week, one month, two months or six months or any time value in between, the biocomposite material implants preferably retain at least 10%, at least 20%, at least 50%, at least 60%, at least 75%, at least 85% or up to 100% of flexural strength, Modulus and/or Max load, and/or volume, or any integral value in between. By “biological conditions” it is meant that the temperature is between 30-40 C but preferably is at 37 C. Optionally, fluid conditions replicate those in the body as well, under “simulated body fluid” conditions.


The flexural strength of the implant or segment of the implant is preferably at least 200 MPA, at least 400 mPa, at least 600 mPA, at least 1000 mPA or any integral value in between.


Relevant implants may include bone fixation plates, intramedullary nails, joint (hip, knee, elbow) implants, spine implants, and other devices for such applications such as for fracture fixation, tendon reattachment, spinal fixation, and spinal cages.


According to at least some embodiments, there are provided medical implants for bone or soft tissue fixation comprising a biodegradable composite, wherein said composite optionally and preferably has the following properties:


(i) wherein biodegradable composite comprises one or more biodegradable polymers and a resorbable, reinforcement fiber; and


(ii) wherein one or more segments comprising the medical implant have a maximum flexural modulus in the range of 6 GPa to 30 GPa and flexural strength in the range of 100 MPa to 1000 MPa; and


(iii) wherein the average density of the composite is in the range of 1.1-3.0 g/cm3.


Preferably, average density of the composite is in the range of 1.2-2.0 g/cm3.


More preferably, average density of the composite is in the range of 1.3-1.6 g/cm3.


Preferably, flexural modulus is in the range of 10 GPa to 28 GPa and more preferably in the range of 15 to 25 GPa.


Preferably, flexural strength is in the range of 200-800 MPa. More preferably, 400-800 MPa.


In a preferred embodiment of the present invention, at least 50% of elastic modulus is retained following exposure to simulated body fluid (SBF) at 50° C. for 3 days. More preferably at least 70% is retained, and even more preferably at least 80% is retained.


In a preferred embodiment of the present invention, at least 20% of strength is retained following exposure to simulated body fluid (SBF) at 50° C. for 3 days. More preferably at least 30% is retained, and even more preferably at least 40% is retained.


In a preferred embodiment of the present invention, at least 50% of elastic modulus is retained following exposure to simulated body fluid (SBF) at 37° C. for 3 days. More preferably at least 70%, and even more preferably at least 85%.


In a preferred embodiment of the present invention, at least 30% of strength is retained following exposure to simulated body fluid (SBF) at 37° C. for 3 days. More preferably at least 45%, and even more preferably at least 60%.


Specifically regarding medical implants described herein that contain one or more segments that can be anisotropic, this anisotropicity reflects a significant divergence from what has be previously accepted in medical, and specifically orthopedic, implants in that the anisotropic structure results in implants in which there are mechanical properties in one or more axis that are less than the optimal mechanical properties which may be achieved by the materials from which the implant is comprised. In contrast, traditional implants have relied upon the uniform mechanical properties of the materials from which they are comprised as this does not require compromising in any axis.


The anisotropic approach can only be applied following biomechanical analysis to determine that greater implant mechanical properties is required in certain axes as opposed to other axes. For example, an implant may be subjected to very high bending forces but only nominal tensile forces and therefore require a much greater emphasis on bending forces. Other relevant axes of force in a medical implant can include tensile, compression, bending, torsion, shear, pull-out (from bone) force, etc.


There are several factors that affect the mechanical properties of an implant. As described above, material composition alone results in a generally uniform or isotropic structure. Without wishing to be limited by a closed list or a single hypothesis, within fiber-reinforced biocomposite medical implants, an anisotropic structure may result from one or more of the following characteristics:

    • 1. The weight ratio of reinforcing fibers to biopolymer. Preferably this ratio is in the range of 1:1 to 3:1 and more preferably 1.5:1 to 2.5:1.
    • 2. The density of the medical implant (this characteristic is also determined to some extent the ratio of reinforcing fiber to polymer)
    • 3. The diameter of reinforcing fiber. The average fiber diameter is preferably between 5 and 50 μm. More preferably between 10-30 μm.
    • 4. Length of fiber (continuous fiber, long fiber, short fiber). Preferably, having continuous fiber reinforcement with fibers that run across the entire implant.
    • 5. The alignment of fibers or fiber layers. Preferably, in each segment of the implant, a majority of fibers or fiber layers are aligned or partially aligned with the axis that will be exposed to the highest bending forces. If partially aligned, then preferably within a 45° angle of the axis.
    • 6. The number of fibers or fiber layers aligned in any given direction. Preferably fiber layers are 0.1 to 1 mm in thickness and more preferably 0.15 to 0.25 mm.
    • 7. The order of fiber layers.


In one embodiment of the present invention, the medical implant is a pin, screw, or wire.


Preferably, a pin or wire of 2 mm external diameter will have a shear load carrying capacity of greater than 200 N. More preferably shear load carrying capacity of 2 mm pin will exceed 400 N and most preferably will exceed 600 N.


Bioabsorbable Polymers


In a preferred embodiment of the present invention, the biodegradable composite comprises a bioabsorbable polymer.


The medical implant described herein may be made from any biodegradable polymer. The biodegradable polymer may be a homopolymer or a copolymer, including random copolymer, block copolymer, or graft copolymer. The biodegradable polymer may be a linear polymer, a branched polymer, or a dendrimer. The biodegradable polymers may be of natural or synthetic origin. Examples of suitable biodegradable polymers include, but are not limited to polymers such as those made from lactide, glycolide, caprolactone, valerolactone, carbonates (e.g., trimethylene carbonate, tetramethylene carbonate, and the like), dioxanones (e.g., 1,4-dioxanone), 6-valerolactone, 1, dioxepanones) e.g., 1,4-dioxepan-2-one and 1,5-dioxepan-2-one), ethylene glycol, ethylene oxide, esteramides, γ-ydroxyvalerate, β-hydroxypropionate, alpha-hydroxy acid, hydroxybuterates, poly (ortho esters), hydroxy alkanoates, tyrosine carbonates, polyimide carbonates, polyimino carbonates such as poly (bisphenol A-iminocarbonate) and poly (hydroquinone-iminocarbonate, (polyurethanes, polyanhydrides, polymer drugs (e.g., polydiflunisol, polyaspirin, and protein therapeutics (and copolymers and combinations thereof. Suitable natural biodegradable polymers include those made from collagen, chitin, chitosan, cellulose, poly (amino acids), polysaccharides, hyaluronic acid, gut, copolymers and derivatives and combinations thereof.


According to the present invention, the biodegradable polymer may be a copolymer or terpolymer, for example: polylactides (PLA), poly-L-lactide (PLLA), poly-DL-lactide (PDLLA); polyglycolide (PGA); copolymers of glycolide, glycolide/trimethylene carbonate copolymers (PGA/TMC); other copolymers of PLA, such as lactide/tetramethylglycolide copolymers, lactide/trimethylene carbonate copolymers, lactide/d-valerolactone copolymers, lactide/ε-caprolactone copolymers, L-lactide/DL-lactide copolymers, glycolide/L-lactide copolymers (PGA/PLLA), polylactide-co-glycolide; terpolymers of PLA, such as lactide/glycolide/trimethylene carbonate terpolymers, lactide/glycolide/ε-caprolactone terpolymers, PLA/polyethylene oxide copolymers; polydepsipeptides; unsymmetrically-3,6-substituted poly-1,4-dioxane-2,5-diones; polyhydroxyalkanoates; such as polyhydroxybutyrates (PHB); PHB/b-hydroxyvalerate copolymers (PHB/PHV); poly-b-hydroxypropionate (PHPA); poly-p-dioxanone (PDS); poly-d-valerolactone-poly-ε-capralactone, poly(ε-caprolactone-DL-lactide) copolymers; methylmethacrylate-N-vinyl pyrrolidone copolymers; polyesteramides; polyesters of oxalic acid; polydihydropyrans; polyalkyl-2-cyanoacrylates; polyurethanes (PU); polyvinylalcohol (PVA); polypeptides; poly-b-malic acid (PMLA): poly-b-alkanbic acids; polycarbonates; polyorthoesters; polyphosphates; poly(ester anhydrides); and mixtures thereof; and natural polymers, such as sugars; starch, cellulose and cellulose derivatives, polysaccharides, collagen, chitosan, fibrin, hyalyronic acid, polypeptides and proteins. Mixtures of any of the above-mentioned polymers and their various forms may also be used.


The biodegradable composite is preferably embodied in a polymer matrix, which may optionally comprise any of the above polymers. Optionally and preferably, it may comprise a polymer selected from the group consisting of a bioabsorbable polyester, PLLA (poly-L-lactide), PDLLA (poly-DL-lactide), PLDLA, PGA (poly-glycolic acid), PLGA (poly-lactide-glycolic acid), PCL (Polycaprolactone), PLLA-PCL and a combination thereof. If PLLA is used, the matrix preferably comprises at least 30% PLLA, more preferably 50%, and most preferably at least 70% PLLA. If PDLA is used, the matrix preferably comprises at least 5% PDLA, more preferably at least 10%, most preferably at least 20% PDLA.


Optionally, the inherent viscosity (IV) of the polymer matrix (independent of the reinforcement fiber) is in the range of 0.2-6 dl/g, preferably 1.0 to 3.0 dl/g, more preferably in the range of 1.5 to 2.4 dl/g, and most preferably in the range of 1.6 to 2.0 dl/g.


Inherent Viscosity (IV) is a viscometric method for measuring molecular size. IV is based on the flow time of a polymer solution through a narrow capillary relative to the flow time of the pure solvent through the capillary.


Reinforced Biocomposite


According to at least some embodiments of the present invention, the medical implant comprises a reinforced biocomposite (i.e. a bioabsorbable composite that includes the previously described polymer and also incorporates a reinforcing filler, generally in fiber form, to increase the mechanical strength of the polymer). For the avoidance of doubt, the terms “filler” and “fiber” are used interchangeably to describe the reinforcing material structure.


In a more preferred embodiment of the present invention, the reinforced bioabsorbable polymer is a reinforced polymer composition comprised of any of the above-mentioned bioabsorbable polymers and a reinforcing filler, preferably in fiber form. The reinforcing filler may be comprised of organic or inorganic (that is, natural or synthetic) material. Reinforcing filler may be a biodegradable glass or glass-like materials, a ceramic, a mineral composition (optionally including one or more of hydroxyapatite, tricalcium phosphate, calcium sulfate, calcium phosphate), a cellulosic material, a nano-diamond, or any other filler known in the art to increase the mechanical properties of a bioabsorbable polymer. The filler may also optionally be a fiber of a bioabsorbable polymer itself. Preferably, reinforcing fiber is comprised of a bioabsorbable glass, ceramic, or mineral composition.


Preferably, reinforcement fiber is comprised of silica-based mineral compound such that reinforcement fiber comprises a bioresorbable glass fiber, which can also be termed a bioglass fiber composite.


According to at least some embodiments, bioresorbable glass fiber may optionally have oxide compositions in the following mol. % ranges (as a percent over the glass fiber composition):


Na2O: 11.0-19.0 mol. %


CaO: 9.0-14.0 mol. %


MgO: 1.5-8.0 mol. %


B2O3: 0.5-3.0 mol. %


Al2O3: 0-0.8 mol. %


P2O3: 0.1-0.8 mol. %


SiO2: 67-73 mol. %


but preferably preferably in the following mol. % ranges:


Na2O: 12.0-13.0 mol. %


CaO: 9.0-10.0 mol. %


MgO: 7.0-8.0 mol. %


B2O3: 1.4-2.0 mol. %


P2O3: 0.5-0.8 mol. %


SiO2: 68-70 mol. %


Additional optional bioresorbable glass compositions are described in the following patent applications, which are hereby incorporated by reference as if fully set forth herein: Biocompatible composite and its use (WO2010122098); and Resorbable and biocompatible fibre glass compositions and their uses (WO2010122019).


Tensile strength of the reinforcement fiber is preferably in the range of 1200-2800 MPa, more preferably in the range of 1600-2400 MPa, and most preferably in the range of 1800-2200 MPa.


Elastic modulus of the reinforcement fiber is preferably in the range of 30-100 GPa, more preferably in the range of 50-80 GPa, and most preferably in the range of 60-70 GPa.


Reinforcing filler is preferably incorporated in the bioabsorbable polymer matrix of the biocomposite in fiber form. Preferably, such fibers are continuous fibers.


Preferably continuous fibers are aligned within the implant such that the ends of fibers don't open at the surface of the implant.


Preferably, fibers are distributed evenly within the implant.


Specifically within bioabsorbable fiber-reinforced composites, achieving the high strengths and stiffness required for many medical implant applications can require the use of continuous-fiber reinforcement rather than short or long fiber reinforcement. This creates a significant difference from the implant structures, architectures, designs, and production techniques that have been previously used with medical implants produced from polymers or composites comprising short or long fiber reinforced polymers. Those implants are most commonly produced using injection molding, or occasionally 3-D printing, production techniques. The production of these implants generally involves homogeneity of the material throughout the implant and the finished implant is then comprised of predominantly isotropic material. However, with continuous fiber-reinforcement, the fibers must be carefully aligned such that each fiber or bundle of fibers runs along a path within the composite material such that they will provide reinforcement along specific axes within the implant to provide stress resistance where it is most needed.


The present invention provides, in at least some embodiments, implant compositions from continuous-fiber reinforced bioabsorbable composite materials that are a significant step forward from previous bioabsorbable implants in that they can achieve sustainably high, load bearing strengths and stiffness. Additionally, many embodiments of the present invention additionally facilitate these high strength levels with efficient implants of low volume since the anisotropic nature of the implants can allow the implants to achieve high mechanical properties in axes where those properties are needed (for example in bending resistance) without necessitating the additional volume that would be needed to uniformly provide high mechanical properties in all other axes.


According to at least some embodiments, there is provided a medical implant comprising a plurality of composite layers, said layers comprising a biodegradable polymer and a plurality of uni-directionally aligned continuous reinforcement fibers. Optionally and preferably, the biodegradable polymer is embodied in a biodegradable composite. Also optionally and preferably, the fibers are embedded in a polymer matrix comprising one or more bioabsorbable polymers.


According to at least some embodiments, the composite layers are each comprised of one or more composite tapes, said tape comprising a biodegradable polymer and a plurality of uni-directionally aligned continuous reinforcement fibers. Optionally and preferably, the biodegradable polymer is embodied in a biodegradable composite. Also optionally and preferably, the fibers are embedded in a polymer matrix comprising one or more bioabsorbable polymers.


Preferably, the composite tape layer comprises reinforcement fibers that are pre-impregnated with polymer.


Preferably, each composite layer is of thickness 0.05 mm-0.5 mm, more preferably 0.15-0.35 mm, and most preferably 0.1-0.25 mm.


Preferably, each composite tape is of width 2-30 mm, more preferably tape is of width 4-16 mm, and most preferably of width 6-12 mm.


Preferably, reinforcement fiber content within the composite tape is in the range of 20-70%, more preferably in the range of 30-60%, more preferably in the range of 40-50%, and most preferably 45-50% over the entire composite tape materials.


Optionally and preferably, the fiber-reinforced biodegradable composite within the implant has a flexural modulus exceeding 10 GPa and flexural strength exceeding 100 MPa.


Optionally, the fiber-reinforced biodegradable composite within the implant has flexural strength in range of 200-1000 MPa, preferably 300-800 MPa, more preferably in the range of 400-800 MPa, and most preferably in the range of 500-800 MPa


Optionally, the fiber-reinforced biodegradable composite within the implant has elastic modulus in range of 10-30 GPa, preferably 12-28 GPa, more preferably in the range of 16-28 GPa, and most preferably in the range of 20-26 GPa.


Optionally, fibers may be aligned at an angle to the longitudinal axis (i.e. on a diagonal) such that the length of the fiber may be greater than 100% of the length of the implant. Optionally and preferably, a majority of reinforcement fibers are aligned at an angle that is less than 90°, alternatively less than 60°, or optionally less than 45° from the longitudinal axis.


Preferably, the implant preferably comprises between 2-20 composite tape layers, more preferably between 2-10 layers, and most preferably between 2-6 layers; wherein each layer may be aligned in a different direction or some of the layers may be aligned in the same direction as the other layers.


Preferably, the maximum angle between fibers in at least some of the layers is greater than the angle between the fibers in each layer and the longitudinal axis. For example, one layer of reinforcing fibers may be aligned and a right diagonal to the longitudinal axis while another layer may be aligned at a left diagonal to the longitudinal axis.


Optionally and preferably, the composite composition additionally includes a compatibilizer, which for example be such an agent as described in WO2010122098, hereby incorporated by reference as if fully set forth herein.


Reinforcing fiber diameter preferably in range of 2-40 um, preferably 8-20 um, most preferably 12-18 um (microns).


Preferably, the implant includes only one composition of reinforcing fiber.


Preferably fibers don't open at the surface of the implant.


Numerous examples of reinforced polymer compositions have previously been documented. For example: A biocompatible and resorbable melt derived glass composition where glass fibers can be embedded in a continuous polymer matrix (EP 2 243 749 A1), Biodegradable composite comprising a biodegradable polymer and 20-70 vol % glass fibers (WO2010128039 A1), Resorbable and biocompatible fiber glass that can be embedded in polymer matrix (US 2012/0040002 A1), Biocompatible composite and its use (US 2012/0040015 A1), Absorbable polymer containing poly[succinimide] as a filler (EPO 671 177 B1).


In a more preferred embodiment of the present invention, the reinforcing filler is covalently bound to the bioabsorbable polymer such that the reinforcing effect is maintained for an extended period. Such an approach has been described in US 2012/0040002 A1 and EP 2243500B1, hereby incorporated by reference as if fully forth herein, which discusses a composite material comprising biocompatible glass, a biocompatible matrix polymer and a coupling agent capable of forming covalent bonds.


Fabrication of the Implant


Any of the above-described bioabsorbable polymers or reinforced bioabsorbable polymers may be fabricated into any desired physical form for use with the present invention. The polymeric substrate may be fabricated for example, by compression molding, casting, injection molding, pultrusion, extrusion, filament winding, composite flow molding (CFM), machining, or any other fabrication technique known to those skilled in the art. The polymer may be made into any shape, such as, for example, a plate, screw, nail, fiber, sheet, rod, staple, clip, needle, tube, foam, or any other configuration suitable for a medical device.


Load-Bearing Mechanical Strength


The present invention particularly relates to bioabsorbable composite materials that can be used in medical applications that require high strength and a stiffness compared to the stiffness of bone. These medical applications require the medical implant to bear all or part of the load applied by or to the body and can therefore be referred to generally as “load-bearing” applications. These include bone fixation, fracture fixation, tendon reattachment, joint replacement, spinal fixation, and spinal cages.


The flexural strength preferred from a bioabsorbable composite (such as a reinforced bioabsorbable polymer) for use in the load-bearing medical implant is at least 200 MPa, preferably above 400 MPa, more preferably above 600 MPa, and even more preferably above 800 MPa. The Elastic Modulus (or Young's Modulus) of the bioabsorbable composite for use with present invention is preferably at least 10 GPa, more preferably above 15 GPa, and even more preferably above 20 GPa but not exceeding 100 GPa and preferably not exceeding 60 GPa.


Sustained Mechanical Strength


There is a need for the bioabsorbable load-bearing medical implants of the present invention to maintain their mechanical properties (high strength and stiffness) for an extended period to allow for sufficient bone healing. The strength and stiffness preferably remains above the strength and stiffness of cortical bone, approximately 150-250 MPa and 15-25 GPa respectively, for a period of at least 3 months, preferably at least 6 months, and even more preferably for at least 9 months in vivo (i.e. in a physiological environment).


More preferably, the flexural strength remains above 400 MPa and even more preferably remains above 600 MPa.


The present invention overcomes the limitations of previous approaches and provides medical implants comprised of biodegradable compositions that retain their high mechanical strength and stiffness for an extended period sufficient to fully support bone regeneration and rehabilitation.


“Biodegradable” as used herein is a generalized term that includes materials, for example polymers, which break down due to degradation with dispersion in vivo. The decrease in mass of the biodegradable material within the body may be the result of a passive process, which is catalyzed by the physicochemical conditions (e.g. humidity, pH value) within the host tissue. In a preferred embodiment of biodegradable, the decrease in mass of the biodegradable material within the body may also be eliminated through natural pathways either because of simple filtration of degradation by-products or after the material's metabolism (“Bioresorption” or “Bioabsorption”). In either case, the decrease in mass may result in a partial or total elimination of the initial foreign material. In a preferred embodiment, said biodegradable composite comprises a biodegradable polymer that undergoes a chain cleavage due to macromolecular degradation in an aqueous environment.


A polymer is “absorbable” as described herein if it is capable of breaking down into small, non-toxic segments which can be metabolized or eliminated from the body without harm. Generally, absorbable polymers swell, hydrolyze, and degrade upon exposure to bodily tissue, resulting in a significant weight loss. The hydrolysis reaction may be enzymatically catalyzed in some cases. Complete bioabsorption, i.e. complete weight loss, may take some time, although preferably complete bioabsorption occurs within 24 months, most preferably within 12 months.


The term “polymer degradation” means a decrease in the molecular weight of the respective polymer. With respect to the polymers, which are preferably used within the scope of the present invention said degradation is induced by free water due to the cleavage of ester bonds. The degradation of the polymers as for example used in the biomaterial as described in the examples follows the principle of bulk erosion. Thereby a continuous decrease in molecular weight precedes a highly pronounced mass loss. Such loss of mass is attributed to the solubility of the degradation products. Methods for determination of water induced polymer degradation are well known in the art such as titration of the degradation products, viscometry, differential scanning calorimetry (DSC).


Bulk degradation refers to a process of degradation in which there is at least some perfusion of fluid through the material that is being degraded, such as the body of the implant, thereby potentially degrading the bulk of the material of the implant (as opposed to the external surface alone). This process has many effects. Without wishing to be limited to a closed list, such bulk degradation means that simply making an implant larger or thicker may not result in improved retained strength.


Surface degradation refers to a process of degradation in which the external surface undergoes degradation. However, if there is little or no perfusion of fluid through the material that is being degraded, then the portion of the implant that is not on the surface is expected to have improved retained strength over implants in which such perfusion occurs or occurs more extensively.


Clinical Applications


The medical implants discussed herein are generally used for bone fracture reduction and fixation to restore anatomical relationships. Such fixation optionally and preferably includes one or more, and more preferably all, of stable fixation, preservation of blood supply to the bone and surrounding soft tissue, and early, active mobilization of the part and patient.


There are several exemplary, illustrative, non-limiting types of bone fixation implants for which the materials and concepts described according to at least some embodiments of the present invention may be relevant, as follows:


Screws


Screws are used for internal bone fixation and there are different designs based on the type of fracture and how the screw will be used. Screws come in different sizes for use with bones of different sizes. Screws can be used alone to hold a fracture, as well as with plates, rods, or nails. After the bone heals, screws may be either left in place or removed.


Screws are threaded, though threading can be either complete or partial. Screws can include compression screws, locking screws, and/or cannulated screws. External screw diameter can be as small as 0.5 or 1.0 mm but is generally less than 3.0 mm for smaller bone fixation. Larger bone cortical screws can be up to 5.0 mm and cancellous screws can even reach 7-8 mm. Some screws are self-tapping and others require drilling prior to insertion of the screw. For cannulated screws, a hollow section in the middle is generally larger than 1 mm diameter in order to accommodate guide wires.


Wires/Pins


Wires are often used to pin bones back together. They are often used to hold together pieces of bone that are too small to be fixed with screws. They can be used in conjunction with other forms of internal fixation, but they can be used alone to treat fractures of small bones, such as those found in the hand or foot. Wires or pins may have sharp points on either one side or both sides for insertion or drilling into the bone.


“K-wire” is a particular type of wire generally made from stainless steel, titanium, or nitinol and of dimensions in the range of 0.5-2.0 mm diameter and 2-25 cm length. “Steinman pins” are general in the range of 2.0-5.0 mm diameter and 2-25 cm length. Nonetheless, the terms pin and wire for bone fixation are used herein interchangeably.


Anchors


Anchors and particularly suture anchors are fixation devices for fixing tendons and ligaments to bone. They are comprised of an anchor mechanism, which is inserted into the bone, and one or more eyelets, holes or loops in the anchor through which the suture passes. This links the anchor to the suture. The anchor which is inserted into the bone may be a screw mechanism or an interference mechanism. Anchors are generally in the range of 1.0-6.5 mm diameter


Cable, Ties, Wire Ties


Cables, ties, or wire ties (one example of wire tie is Synthes ZipFix™) can be used to perform fixation by cerclage, or binding, bones together. Such implants may optionally hold together bone that cannot be fixated using penetration screws or wires/pin, either due to bone damage or presence of implant shaft within bone. Generally, diameter of such cable or tie implants is optionally in the range of 1.0 mm-2.0 mm and preferably in the range of 1.25-1.75 mm. Wire tie width may optionally be in the range of 1-10 mm.


Nails or Rods


In some fractures of the long bones, medical best practice to hold the bone pieces together is through insertion of a rod or nail through the hollow center of the bone that normally contains some marrow. Screws at each end of the rod are used to keep the fracture from shortening or rotating, and also hold the rod in place until the fracture has healed. Rods and screws may be left in the bone after healing is complete. Nails or rods for bone fixation are generally 20-50 cm in length and 5-20 mm in diameter (preferably 9-16 mm). A hollow section in the middle of nail or rod is generally larger than 1 mm diameter in order to accommodate guide wires.


Other non-limiting, illustrative examples of bone fixation implants may optionally include plates, plate and screw systems, and external fixators.


Any of the above-described bone fixation implants may optionally be used to fixate various fracture types including but not limited to comminuted fractures, segmental fractures, non-union fractures, fractures with bone loss, proximal and distal fractures, diaphyseal fractures, osteotomy sites, etc.


Bending Resistance


The primary mechanical challenge to wires or pins used for bone fixation is providing mechanical support (i.e. bending resistance) under bending/flexural stress to prevent the stress from creating a gap between the bone surfaces in the fracture which can prevent good bone healing. For absorbable bone fixation implants, it is desirable for the implant to provide bending resistance such that the implant deflects a similar amount or less than the bones which it is fixating when exposed to bending stress. It is further desirable for the implant to provide this bending resistance with the minimal profile (i.e. minimal amount of material) in order to minimize the amount of degradation products over time and also to reduce implant cost.


For a wire or pin, the amount of deflection it undergoes when subjected to a flexural stress is directly related to (i) the flexural modulus of the material of which the implant is made; and (ii) the second moment of inertia of the cross-section of the wire or pin across the axis across which the flexural stress is being applied.


Second moment of inertia refers to the property of a shape that directly correlates to its ability to resist bending and deflection. Second moment of inertia can alternatively be referred to as second moment of area, moment of inertia of plane area, area moment of inertia, polar moment of area or second area moment.


In a preferred embodiment of the present invention, the elastic modulus of the implant or a segment of the implant as measured with flexural/bending testing is greater than the elastic modulus of the implant or a segment of the implant as measured with tensile testing. Preferably, the difference is greater than 5%, more preferred the difference is greater than 10%, even more preferred greater than 20%, 30%, 40%, 50%.


In a preferred embodiment of the present invention, the flexural/bending strength of the implant is greater than its tensile or compressive strength. In a more preferred embodiment, this difference is greater than 5%. Even more preferred, the higher flexural/bending strength as compared with tensile or compressive strength is greater by at least 10%, 30%, 50%, 70%, and most preferably 100%.


In an optional embodiment, the anisotropic nature of the medical implants described according to at least some embodiments of the present invention result in the mechanical properties in the bending axis that are superior to the mechanical properties in the tensile or compressive axis. This difference can be at least partially determined by the alignment, orientation, or structure of reinforcing fibers with the bioabsorbable polymer matrix, as described in more detail above.


In a hollow tube geometry, its flexural/bending stiffness is relatively greater than its tensile stiffness. The flexural stiffness is relative to the second moment of inertia around the axis of bending, for example the second moment of inertia around the midline axis of a square pin/beam is Ix=bh3/12 and for a hollow circular pin/beam, Ix=π(do4−di4)/64. Conversely, the tensile stiffness is relative to the cross-sectional area, A=bh for a square pin/beam and A=π(do2−di2)/4 for a hollow circular pin/beam.


In a preferred embodiment of the present invention, one or more voids are present within the implant, such that the second moment of inertia of the cross-section of the wire or pin across the mid-line axis of the implant is less than the second moment of inertia for such a part with the same or similar external dimensions but a void-less (i.e. whole or solid) cross-sectional area. Preferably, the reduction in the second moment of inertia is smaller than 30%, more preferably 20% and most preferably 10% than for a solid part.


Alternatively, a wire or pin may comprise open space between different struts, ribs, arms, etc of the wire or pin such that wire or pin forms an asterisk type cross-section thereby similarly providing increased relative flexural stiffness in relation to its tensile stiffness.


Preferably, the average cross-sectional area of the wire or pin is reduced by a greater percentage than the average second moment of inertia of its cross-section as compared to a solid part with similar dimensions as previously described. More preferably, the cross-sectional area is more than 20% smaller while the second moment of inertia is reduced by less than 20%. Even more preferably, the cross-sectional area is more than 20% smaller while the second moment of inertia is reduced by less than 10%.


Dimensions


For orthopedic implants, it is desirable for the implant to have a minimal profile so as to allow for implantation with minimal soft tissue damage. Furthermore, it is preferable to produce the implant with sufficient robustness to provide necessary mechanical strength but otherwise not contain extraneous material.


In a preferred embodiment of the present invention, the external diameter of the wire or pin is less than 15 mm, more preferably less than 10 mm, even more preferably less than 5 mm and most preferably less than 3 mm.


In a preferred embodiment of the present invention, the wall thickness of the wire or pin is less than 5 mm, more preferably less than 3 mm, even more preferably less than 1 mm and most preferably less than 0.7 mm.


Voids in Implant


As described above, it may be desirable to have a wire or pin that is hollow in order to provide bending resistance with the most efficient amount of material. Nonetheless, there are potential complications involved in implanting a hollow implant in bone, as non-bone tissue cells, such as fibroblasts, can penetrate into the hollow void and thereby impede or slow regeneration of bone in that area.


In a preferred embodiment of the present invention, the wire or pin contains a hollow section or void internally but such void is covered such that cells cannot invade void prior to degradation of implant material.


In another embodiment of the present invention, the hollow section can be filled with active ingredients such as antibiotics, growth factors or bone filler to prevent such invasion.


In another embodiment hollow section can be used to introduce active ingredients into fracture area via holes in the wall of the hollow wire or pin.


Example #1

The below example describes the extent to which the anisotropic nature of the herein described reinforced biocomposite implants impacts the mechanical properties of the implants. Depending on the mechanical property parameter, the differences in the degree of anisotropicity in a medical implant or medical implant part can reach even 5× or greater. Without wishing to be limited by a single hypothesis, these differences may be due to differences between alignments of reinforcing fibers within the implant.


Materials and Methods


Rectangular testing samples (dimensions 50.8 mm×12.7 mm×1 mm), simulating plates used for small bone fixation, were produced using reinforced composite material. Material composite was comprised of PLDLA 70/30 polymer reinforced with 40%-50% w/w continuous mineral fibers. Mineral fibers were as described for composition “NX-8” in Lehtonen T J et al. Acta Biomaterialia 9 (2013) 4868-4877. Mineral composition was specifically approximately Na2O 14%, MgO 5.4%, CaO 9%, B2O3 2.3%, P2O5 1.5%, and SiO2 67.8% w/w. All testing samples were from one plate, manufactured by compression molding of five layers of composite material, each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers. Each layer was 0.18 mm thick.


In four samples, orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 45°, 0°, −45°, 0°. In four other samples, orientation of layers relative to longitudinal axis were 90° (perpendicular to implant longitudinal axis), −45°, 90°, 45°, 90°.


Implant samples were tested for Flexural strength, Elastic modulus and Maximum load according to ASTM D790-10 with a 500N load cell and a 3 point bending fixture (220Q1125-95, TestResources, MN, USA). Load span was 25.4 mm and cross head speed was set at 1.092 mm/min. Dimensions, weight and density of samples were measured. Statistical comparison between two treatments was performed using a t-test. A confidence level of p=0.05 was used.


Results



FIG. 2 shows the anisotropic properties of a bio-composite plate as demonstrated by the large difference in mechanical properties of samples with identical compositions, but with a majority of layers aligned at either 0° (Parallel) or 90° (Perpendicular) to the longitudinal axis of the implant sample (n=4). The numerical results are summarized in Table 1.









TABLE 1







Mean values and standard deviations of statistically significant mechanical


properties of the anisotropic implants. (n = 4). Density and Volume of the different


samples were similar.














Flexural
Max
Density
Volume



E [MPa]
Strength [MPa]
Load [N]
[gr/ml]
[mm3]
















Perpendicular
1524.4 ± 281
45.9 ± 1.6
12.4 ± 1.4
1.48 ± 0.01
662.1 ± 32.3


Parallel
9795.4 ± 610
235.4 ± 25.4
81.4 ± 7.7
1.49 ± 0.03
694.0 ± 19.3


Anisotropicity [%]
642.6
512.8
656.3


[Par/perp * 100]










FIG. 3 shows representative examples of samples. FIG. 3A shows a sample with majority of layers with fiber orientation perpendicular to implant longitudinal axis. FIG. 3B shows a sample with majority of layers with fiber orientation parallel to implant longitudinal axis. The mechanical properties of sample B were superior to those of sample A. Anisotropicity of mechanical properties in this example was more than 500%. The anisotropocity was calculated as a percentage by dividing each of the mechanical parameter values as measured for the samples with perpendicular (tranverse) fiber alignment by the corresponding value as measured for the samples with parallel fiber alignment.


Example #2

The below example describes the extent to which the anisotropic nature of the herein described reinforced biocomposite implants impacts the mechanical properties of the implants. This example additionally shows that an implant comprised of a randomly distributed, or amorphous, composition of reinforced biocomposite materials will have far inferior mechanical properties in the desired axis to the herein described anisotropic medical implant with alignment of reinforcing fibers that maximizes the mechanical properties in the desired axis (in this case, bending force).


The example also demonstrates anisotropicity in that the modulus, when measured by flexural testing, can be either higher or lower than the tensile modulus of the same part depending on the directionality of the flexural test.


Materials and Methods


Rectangular testing samples (dimensions 50.8 mm×12.7 mm×0.7 mm), simulating plates used for small bone fixation, were produced using reinforced composite material. Material composite was as described in Example 1.


16 testing samples were produced, manufactured by compression molding of four layers of composite material. Each layer was 0.18 mm thick. In four samples, samples were each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 0°, 0°, 0°. In four other samples, orientation of layers relative to longitudinal axis were 90°(perpendicular to implant longitudinal axis), 90°, 90°, 90°. In four other samples, the continuous fiber embedded layers were not uni-directionally aligned but rather the layers were chopped into segments of approximately 3 mm and then molded together into the rectangular plates in bulk. In other words, the composition of these last four samples was identical to that of the continuous fiber groups but the material was used with random alignment, hereafter referred to as an “amorphous” form.


12 implant samples were tested for Flexural strength, Elastic modulus and Maximum load according to ASTM D790-10 with a 500N load cell and a 3 point bending fixture (220Q1125-95, TestResources, MN, USA). Load span was 25.4 mm and cross head speed was set at 1.47 mm/min (1.71 mm/min for amorphous plates due to thinner dimension). Dimensions, weight and density of samples were measured. 4 implant samples (n=4) were tested for tensile strength, tensile modulus and maximum load according to modified ASTM D3039M with a 5 KN load cell and an appropriate fixture (220Q1125-95, TestResources, MN, USA). Sample span was 30 mm at the beginning of the test and cross head speed was set at 2 mm/min. Dimensions, weight and density of samples were recorded.


Results



FIG. 4 shows that the anisotropic properties of a bio-composite plate are directly affected by fiber orientation, as demonstrated by the large difference in mechanical properties of samples with identical compositions, but with non-aligned layers (Amorphous) or with layers aligned at either 0° (Parallel) or 90° (Perpendicular) to the longitudinal axis of the implant sample (n=4). Table 2 summarizes the numerical results for mechanical properties;









TABLE 2







Mean values and standard deviations of statistically significant mechanical


properties of the anisotropic implants. (n = 4).














Flexural
Max Load
Density




E [Mpa]
Strength [Mpa]
[N]
[gr/ml]
Volume [mm3]
















Amorphous
3183.15 ± 396.7
56.56 ± 6.2 
6.10 ± 0.73
1.46 ± 0.05 
405.50 ± 49


Parallel
10572.5 ± 878.2
333.1 ± 32.8
41.74 ± 6.17 
1.34 ± 0.066
447.67 ± 21


Perpendicular
483.47 ± 84.4
14.22 ± 0.76
2.13 ± 0.13
1.33 ± 0.021
  487.26 ± 18.3


Parallel to
332%
589%
684%


Amorphous


Anisotropocity (%)


Parallel to
2189% 
2342% 
1960% 


Perpendicular


Anisotropocity (%)


Amorphous to
659%
398%
286%


Perpendicular


Anisotropocity (%)
















TABLE 3







Mean values and standard deviations of tensile mechanical properties of the implants (n = 4).















Tensile
Ultimate







Strength
tensile strain
Tensile Max
Density
Volume



E [MPa]
[MPa]
[mm/mm]
Load [N]
[gr/ml]
[mm3]

















Tensile Plate (Parallel)
7700.35 ± 594.7
89.65 ± 6.71
0.075 ± 0.01
752.5 ± 94.8
1.47 ± 0.03
428.66 ± 48.9


Improvement in mechanical
137%
372%


properties as tested in


flexural axis as compared with


mechanical properties as tested


in tensile axis (% of flexural


value divided by tensile value)










FIG. 5 shows representative sample examples. FIG. 5A shows an amorphous fiber orientation sample; FIG. 5B shows a sample with majority of layers with fiber orientation perpendicular to implant longitudinal axis. FIG. 5C shows a sample with majority of layers with fiber orientation parallel to implant longitudinal axis. Mechanical properties of sample C were superior to those of samples A and B; however sample A had properties that were superior to sample B, presumably due to the presence of at least some parallel fibers.


Example #3

Example 3 differs from Examples 1 and 2 in that identical material composites were used to produce rectangular plate implants but a different production method was used that resulted in a lower density. This examples shows that such samples with lower density have much inferior mechanical properties as compared with the otherwise similar higher density samples described in examples 1 and 2. Density changes are due to the production method. Without wishing to be limited by a single hypothesis, density depends on how much air or water is incorporated in the implant over the course of production.


Materials and Methods


Rectangular testing samples (dimensions 50.8 mm×12.7 mm×1.1 mm), simulating plates used for small bone fixation, were produced using reinforced composite material. Material composite was as described in Example 1.


Four testing samples were produced, manufactured by a two step process of 1) wrapping two complete layers of composite material around a 40 mm diameter tube using a hot air blower to adhere layers to each other and form a two layer biocomposite tube; 2) cutting biocomposite tube into two sheets and pressing sheets against each other using heated steel blocks. Each layer was 0.18 mm thick. The resulting samples were each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers where orientation of layers relative to longitudinal axis of implant were 8°, −8°, 8°, −8°. This specific alignment was designed to approximate 0° and would be expected to approximate the mechanical properties of the 0° (Parallel) samples described in example 2 if all other parameters were equal.


Implant samples were tested for Flexural strength, Elastic modulus and Maximum load according to ASTM D790-10 with a 500N load cell and a 3 point bending fixture (220Q1125-95, TestResources, MN, USA). Load span was 25.4 mm and cross head speed was set at 0.942 mm/min (Dimensions, weight and density of samples were measured. Statistical comparison between two treatments was performed using a t-test. A confidence level of p=0.05 was used.


Results


Table 4 shows the significance of structural differences between reinforced composites. The alignment with 8 degree fiber offset described herein would be expected to be nearly identical to the parallel fiber alignment described in Example 1, and yet the strength and modulus are drastically lower. Without wishing to be limited by a single hypothesis, it is believed that the much lower density seen in this example (Example 3) was the cause or at least a significantly contributing factor.









TABLE 4







Mean values and standard deviations of the mechanical properties of the


anisotropic implant. (n = 4).














Flexural







Strength
Max Load
Density
Volume



E [MPa]
[MPa]
[N]
[gr/ml]
[mm3]
















4 layers, 8 deg
2052.47 ± 96.55
49.24 ± 2
18.52 ± 0.43
0.935 ± 0.01
775.49 ± 17.11









Example #4

The below example describes how anisotropic biocomposite implants retain significant mechanical properties (modulus and strength) after exposure to rigorous accelerated degradation conditions.


Materials and Methods


Rectangular testing samples (dimensions 50.8 mm×12.7 mm×1.1 mm), simulating plates used for small bone fixation, were produced using reinforced composite material. Material composite was as described in Example 1.


Eight testing samples were produced, manufactured by compression molding of four or five layers of composite material. Each layer was 0.18 mm thick. In four samples, five layer samples were each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 45°, 0°, −45°, 0°. In four other samples, four layer samples were each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers where orientation of layers relative to longitudinal axis were 0° (parallel to implant longitudinal axis), 45°, −45°, 0°.


Implant samples were tested for Flexural strength, Elastic modulus and Maximum load according to ASTM D790-10 with a 500N load cell and a 3 point bending fixture (220Q1125-95, TestResources, MN, USA). Load span was 25.4 mm and cross head speed was set at 1.536 mm/min. Implants were tested either at time=0 or after incubation in simulated body fluid (SBF). SBF was comprised of: 142 Na+, 5 K+, 1.5 Mg 2+, 2.5 Ca2+, 147.8 Cl−, 4.2 HCO3−, 1 HPO43−, 0.5 SO4 2− mol/m3. Samples were incubated at either 60 or 50 degrees C. in a shaking incubator (Wis-30 shaking incubator, Witeg, Germany) at 30 rpm for 3-4 days.


Results



FIGS. 6 and 7: After exposure to accelerated degradation conditions of 50° C. for three days, both groups of samples retained >80% of their elastic modulus and >30% of their flexural strength. 50° C. is the highest indicative temperature for incubation conditions for accelerated degradation since the Tg of the biocomposite material is ˜56 C.) FIG. 6 shows elastic modulus after exposure to forced degradation, while FIG. 7 shows flexural strength after exposure to forced degradation.


Example #5

Below example describes production of hollow pin implants with reinforced biocomposite materials. As with plates, hollow pins with alignment with anisotropic characteristics, result in higher mechanical properties in the desired bending force parameters.


Materials and Methods


Hollow pin implants of dimensions appropriate for small bone fixation (2 mm OD, 1 mm ID, 5 cm) were made of composite material of composition as described in Example 1. Pin implants were manufactured in two steps and two types of pin implants were produced: Parallel alignment and amorphous alignment.


For parallel alignment samples (n=7), plates of 0.5-0.6 mm were produced by compression molding three 0.18 mm thick layers of biocomposite material. Plates were each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 0°, 0°. Two 5 cm length segments of plate were put into a tube mold such that parallel fiber orientation was also parallel to the longitudinal of the pin. The plate segments were thus molded into tube form to form tubes where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 0°, 0°.


For amorphous alignment samples (n=3), plates of 0.5-0.6 mm were produced by compression molding three 0.18 mm thick layers of biocomposite material. Plates were each comprised of the PLDLA polymer with embedded continuous fibers that were not uni-directionally aligned but rather the layers were chopped into segments of approximately 3 mm and then molded together into the rectangular plates in bulk. Two 5 cm length segments of plate were put into a tube mold. The plate segments were thus molded into tube form to form tubes with amorphous alignment.


Implant pins samples were tested for Flexural strength, Elastic modulus and Maximum load according to modified ASTM D790-10 with a 500N load cell and a 3 point bending fixture (220Q1125-95, TestResources, MN, USA). Load span was 25.4 mm and cross head speed was set at 2 mm/min.


Flexural modulus was calculated according to:










σ
max

=


8






F
max



Ld
0



π


(


d
0
4

-

d
i
4


)







(
1
)







Where d0 is the outer diameter of the tube, di is the inner diameter of the tube and L is the support span.


Flexural Elastic modulus was calculated according to:









E
=


4






mL
3



3


π


(


d
0
4

-

d
i
4


)








(
2
)








Results


Table 5 shows the numerical summary of the various mechanical parameters for the pins for material aligned in parallel, tested and then calculated as described above. Table 6 shows the corresponding results for amorphous (non-aligned) pins. With the exception of volume and density, pins made from the parallel aligned material had nearly four times as great mechanical properties as pins made from the amorphous material.









TABLE 5







Mean values and standard deviations of mechanical properties for parallel


aligned pins as compared with amorphous (non-aligned) pins














Flexural







Strength
Density


Sample
E [MPa]
[MPa]
[gr/ml]
Max Load [N]
Volume [mm3]





Parallel Tubes
8890.74 ± 1209.5
158.62 ± 19.3
1.47 ± 0.02
19.82 ± 3.2 
121.88 ± 7.06


(n = 7)


Amorphous Tubes
2907.13 ± 730.9 
40.15 ± 7.8
1.35 ± 0.04
4.82 ± 0.68
138.52 ± 2.96


(n = 3)


Parallel to
306%
395%


Amorphous


Anisotropocity (%)










FIG. 8 is a photograph of a representative hollow pin implant, 5 cm length, 2 mm OD, 1 mm ID. FIG. 8A is a photo of the pin along its length; FIG. 8B is a photo of the cross-section of the pin.


Example #6

Below example describes production of reinforced biocomposite pin implants that are not hollow.


Materials and Methods


Pin implants of dimensions appropriate for small bone fixation (2 mm OD, 5 cm) were made of composite material of composition as described in Example 1. Pin implants were manufactured in two steps. Plates of 0.5-0.6 mm were produced by compression molding three 0.18 mm thick layers of biocomposite material. Plates were each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 0°, 0°. Four 5 cm length segments of plate were put into a cylinder mold such that parallel fiber orientation was also parallel to the longitudinal of the pin. The plate segments were thus molded into cylinder form to form cylinders where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 0°, 0°.


Implant pins were tested for Flexural strength, Elastic modulus and Maximum load according to modified ASTM D790-10 with a 500N load cell and a 3 point bending fixture (220Q1125-95, TestResources, MN, USA). Load span was 25.4 mm and cross head speed was set at 2 mm/min.


Flexural modulus was calculated according to:










σ
max

=


8






F
max


L


πd
0
3






(
1
)







Where d0 is the outer diameter of the cylinder and L is the support span.


Flexural Elastic modulus was calculated according to:









E
=


4






mL
3



3


πd
0
4







(
2
)








Results









TABLE 7







Mean values and standard deviations of mechanical properties (n = 3).














Flexural Strength
Density
Max Load
Volume



E [MPa]
[MPa]
[gr/ml]
[N]
[mm3]
















Full
9536.53 ± 1348.7
202.82 ± 90.7
1.403 ± 0.003
24.79 ± 10.12
169.58 ± 6.6


Cylinders










FIG. 9 is a photograph of a representative pin, 5 cm length, 2 mm OD. FIG. 9A is a photo of the pin along its length; FIG. 9B is a photo of the cross-section of the pin.


Example #7

The below example describes how anisotropic biocomposite implants retain a high amount of mechanical properties (modulus and strength) after exposure to degradation conditions.


Materials and Methods


Rectangular testing samples (dimensions 50.8 mm×12.7 mm×0.75 mm), simulating plates used for small bone fixation, were produced using reinforced composite material. Material composite was as described in Example 1.


Samples were produced by compression molding of five layers of composite material. Each layer was 0.18 mm thick. Five layer samples were each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 45°, 0°, −45°, 0°.


Implant samples were tested for Flexural strength, Elastic modulus and Maximum load according to ASTM D790-10 with a 500N load cell and a 3 point bending fixture (220Q1125-95, TestResources, MN, USA). Load span was 25.4 mm and cross head speed was set at 1.536 mm/min. Implants were tested either at time=0 or after incubation in simulated body fluid (SBF). SBF was comprised of: 142 Na+, 5 K+, 1.5 Mg 2+, 2.5 Ca2+, 147.8 Cl−, 4.2 HCO3−, 1 HPO43−, 0.5 SO4 2− mol/m3. Samples were incubated in SBF at 37 degrees C. in a shaking incubator (Wis-30 shaking incubator, Witeg, Germany) at 30 rpm for five days.


Results




















Flexural







Strength
Max Load
Density
Volume



E [MPa]
[MPa]
[N]
[gr/ml]
[mm3]





















T0
10859.44 ± 163.6 
281.59 ± 2.97 
43.37 ± 0.91
1.47 ± 0.002
479.33 ± 12.29


5 days, 37 C.
9694.59 ± 1322.5
188.24 ± 39.85
37.84 ± 1.69
1.47 ± 0.03 
550.05 ± 85.07









Table 8 shows the mean values and standard deviations of mechanical properties of the implants at t0 (n=2) and after 5 days at 37 C (n=3), demonstrating degradation after this elapsed time.



FIG. 10 shows the decrease in mechanical properties due to incubation under conditions that force degradation. These results show that after 5 days of simulated strength degradation, implants retained >60% of flexural strength, >85% of Modulus and Max load.


Additionally, implant swelling was measured following the incubation at 37 C for 5 days, with thickness of implants increasing by 1.9% and overall volume by 2.8%.


Example #8

The below example describes how anisotropic biocomposite implants retain a high amount of mechanical properties (modulus and strength) after exposure to degradation conditions.


Materials and Methods


Rectangular testing samples (dimensions 50.8 mm×12.7 mm×0.75 mm), simulating plates used for small bone fixation, were produced using reinforced composite material. Material composite was as described in Example 1.


Samples were produced by compression molding of five layers of composite material. Each layer was 0.18 mm thick. Five layer samples were each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 45°, 0°, −45°, 0°.


Implant samples were tested for Flexural strength, Elastic modulus and Maximum load according to ASTM D790-10 with a 500N load cell and a 3 point bending fixture (220Q1125-95, TestResources, MN, USA). Load span was 25.4 mm and cross head speed was set at 1.536 mm/min. Implants were tested either at time=0 or after incubation in simulated body fluid (SBF). SBF was comprised of: 142 Na+, 5 K+, 1.5 Mg 2+, 2.5 Ca2+, 147.8 Cl−, 4.2 HCO3−, 1 HPO43−, 0.5 SO4 2− mol/m3. Samples were incubated in SBF at 37 degrees C. in a shaking incubator (Wis-30 shaking incubator, Witeg, Germany) at 30 rpm for one day.


Results




















Flexural Strength

Density
Volume



E [MPa]
[MPa]
Max Load [N]
[gr/ml]
[mm3]





















T0
11416.92 ± 403.7
289.67 ± 20.9
88.45 ± 7.5 
1.45 ± 0.05
668.49 ± 23.5


24 hrs, 37 C.
 11698.2 ± 502.5
260.05 ± 14.2
74.04 ± 5.25
1.50 ± 0.03
638.58 ± 55.2









Table 9 shows the mean values and standard deviations of mechanical properties of The implants before and after incubation at 37 C in SBF for 24 hrs (n=4).


After 24 hour incubation, there was no change in elastic modulus, >85% of flexural strength was retained, and >20% of max load.


Example #9

Below example describes production of hollow pin implants with reinforced biocomposite materials. As with plates, hollow pins with alignment with anisotropic characteristics, result in higher mechanical properties in the desired bending force parameters.


Materials and Methods


Hollow pin implants of dimensions appropriate for small bone fixation (2 mm OD, 1 mm ID, 5 cm length) were made of composite material of composition as described in Example 1. Pin implants were manufactured in two steps and two types of pin implants were produced: hollow cylindrical pins and full cylindrical pins.


For hollow pins (n=3), plates of 0.5-0.6 mm were produced by compression molding three 0.18 mm thick layers of biocomposite material. Plates were each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 0°, 0°. One 5 cm length segment of plate was put into each side of a tube mold (total of two segments) such that parallel fiber orientation was also parallel to the longitudinal of the pin. The plate segments were thus molded into tube form to form tubes where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 0°, 0°.


For full cylindrical pins (n=3), plates of 0.5-0.6 mm were produced by compression molding three 0.18 mm thick layers of biocomposite material. Plates were each comprised of the PLDLA polymer with embedded uni-directionally aligned continuous fibers where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 0°, 0°. Four 5 cm length segments of plate were put into a cylindrical mold such that parallel fiber orientation was also parallel to the longitudinal of the pin. The plate segments were thus molded into cylinder form to form cylinders where orientation of layers relative to longitudinal axis of implant were 0° (parallel to implant longitudinal axis), 0°, 0°.


Implant samples were tested for tensile strength, tensile modulus and maximum load according to modified ASTM D3039M with a 5 KN load cell and an appropriate fixture (220Q1125-95, TestResources, MN, USA). Sample span was 30 mm at the beginning of the test and cross head speed was set at 2 mm/min. Dimensions, weight and density of samples were recorded.


Results


Perhaps unsurprisingly, measures of mechanical strength (including elastic module, tensile strength and max load) were all significantly higher for full (non-hollow) pins as compared to hollow pins, as shown in Tables 10 and 11.









TABLE 10







Mean values and standard deviations of mechanical properties of hollow


pin implants (n = 3) and full pin implants (n = 3).
















Ultimate







Tensile
tensile




strength
strain

Density
Volume



E [MPa]
[MPa]
[mm/mm]
Max Load [N]
[gr/ml]
[mm3]

















Hollow Pin
8244.3 ± 1379.8
78.01 ± 32.6 
0.026 ± 0.008
261.85 ± 113.3
1.41 ± 0.06
2.548 ± 0.17


Tensile


Full Pin
10724.7 ± 969.7 
132.9 ± 23.09
0.029 ± 0.002
431.77 ± 75.9 
1.43 ± 0.03
 3.25 ± 0.18


Tensile









Notably, the ratio of modulus as tested in tensile testing between hollow pins and full pins was 0.77 and the ratio of tensile strength was 0.59. For similar pins, as described in examples 5 and 6, the ratio of modulus as tested in flexural testing between hollow pins and full pins was 0.93 and the ratio of flexural strength was 0.78. These results suggest that the same 25% loss in volume between a full and hollow cylindrical geometry results in a different effect on modulus and strength depending on the axis of mechanical testing (tensile or flexural). More strength and modulus are retained for bending resistance (flexural axis) than are retained for elongation resistance (tensile axis) in the hollow geometry.


Example #10

Composite material technology can result in performance unattainable by individual constituents, achieving diverse performance demands that could not be met by one material. A unique combination of strength, stiffness, density and degradation rate is achieved based on the structural composition and orientation of fibers inside the implants.


A mechanical simulations of fiber orientations and structural compositions using the above-described aligned reinforced biocomposite material was performed. The simulation suggested fiber orientations and structural compositions that best fit the bending force load conditions involved in many applications of orthopedic bone fixation. Biomechanical design of implant per clinical application allows for maximizing clinical benefit by reducing implant size and the amount of foreign material being implanted, achieving both required strengths and desired rate of implant absorption.



FIG. 11 shows a graphical finite elements simulation. FIG. 11A shows force distribution on a hollow cylinder pin implant with a wall thickness made of 5 layers as demonstrated in FIG. 11B.


Finite element modeling on a hollow bone fixation pin was performed to evaluate possible layer set ups that can support the expected biomechanical load (FIG. 1). Exact fiber orientation per layer greatly affects the performance of an implant. Table 12 shows how an increase in 10 [N] for the buckling load of an implant in a single direction can be theoretically achieved using different layer structures.









TABLE 12







Finite element simulation results on a 2 mm pin implant


for different layer configurations. Orientation presented


as: inner (left) to outer (right). Simulation confirms


that higher buckling loads can be reached when optimizing


layer orientation. In this example optimizing can result


in an increase in buckling load from 23 [N] to 32 [N]









Configuration
Bending stiffness [N/mm]
Buckling load [N]





0/0/0/45/−45
0.554
22.7


45/0/0/0/−45
0.589
24.0


0/45/0/−45/0
0.591
24.2


45/−45/0/0/0
0.626
25.7


20/−20/20/−20/20
0.610
24.8


15/−15/15/−15/15
0.629
29.1


10/−10/10/−10/10
0.788
32.5









It will be appreciated that various features of the invention which are, for clarity, described in the contexts of separate embodiments may also be provided in combination in a single embodiment. Conversely, various features of the invention which are, for brevity, described in the context of a single embodiment may also be provided separately or in any suitable sub-combination. It will also be appreciated by persons skilled in the art that the present invention is not limited by what has been particularly shown and described hereinabove.


All references cited or described herein are hereby incorporated by reference as if set forth herein to the extent necessary to support the description of the present invention and/or of the appended claims.


Although the invention has been described in conjunction with specific embodiments thereof, it is evident that many alternatives, modifications and variations will be apparent to those skilled in the art. Accordingly, it is intended to additionally embrace all such alternatives, modifications and variations that fall within the spirit and broad scope of the appended claims.

Claims
  • 1. An orthopedic fixation implant comprising absorbable structural material, wherein strength and stiffness properties are anisotropic; the absorbable structural material comprising a reinforcement filler, wherein said absorbable structural material further comprises a biodegradable polymer; wherein an average density of the absorbable structural material is in a range of 1.3-3.0 g/cm3; wherein said reinforcing filler comprises a plurality of reinforcing fibers and wherein a weight ratio of reinforcing fibers to said biodegradable polymer is in the range of 1:1 to 1:3; and wherein a percentage of reinforcing fibers is in the range of 40% to 50% weight per weight; wherein a plurality of said reinforcement fibers are arranged in parallel to a longitudinal axis of the implant.
  • 2. The implant of claim 1, wherein the biodegradable composite has a maximum flexural modulus in the range of 6 GPa to 30 GPa and flexural strength in the range of 100 MPa to 1000 MPa.
  • 3. The implant of claim 1, having improved mechanical properties in at least one mechanical axis or parameter as compared with at least one other mechanical axis or parameter within the same implant, such that the implant is anisotropic; wherein said mechanical parameter comprises one or more of bending strength and stiffness (resistance to bending force), tensile strength and stiffness (resistance to tensile force), compression strength and stiffness (resistance to compression force), shearing strength and stiffness (resistance to shearing force), or torsional strength and stiffness (resistance to torsional force); where in properties are anisotropic of at least 10%, at least 20%, at least 30%, 40%, 50%, 60%, 70%, 80%, 90% or 100%, or any number in between.
  • 4. The implant of claim 1, wherein said biodegradable polymer comprises a homopolymer or a copolymer; wherein said copolymer comprises a random copolymer, block copolymer, or graft copolymer; and wherein said biodegradable polymer comprises a linear polymer, a branched polymer, or a dendrimer, of natural or synthetic origin; wherein said biodegradable polymer comprises lactide, glycolide, caprolactone, valerolactone, carbonates (e.g., trimethylene carbonate, tetramethylene carbonate), dioxanones (e.g., 1,4-dioxanone), δ-valerolactone, 1, dioxepanones (e.g., 1,4-dioxepan-2-one and 1,5-dioxepan-2-one), ethylene glycol, ethylene oxide, esteramides, y-hydroxyvalerate, β-hydroxypropionate, alpha-hydroxy acid, hydroxybutyrates, poly (ortho esters), hydroxy alkanoates, tyrosine carbonates, polyimide carbonates, polyimino carbonates, such as poly (bisphenol A-iminocarbonate) and poly (hydroquinone-iminocarbonate), polyurethanes, polyanhydrides, polymer drugs (e.g., polydiflunisol, poly aspirin, and protein therapeutics), sugars; starch, cellulose and cellulose derivatives, polysaccharides, collagen, chitosan, fibrin, hyaluronic acid, polypeptides, proteins, poly (amino acids), polylactides (PLA), poly-L-lactide (PLLA), poly-DL-lactide (PDLLA); polyglycolide (PGA); copolymers of glycolide, glycolide/trimethylene carbonate copolymers (PGA/TMC); other copolymers of PLA, such as lactide/tetramethylglycolide copolymers, lactide/trimethylene carbonate copolymers, lactide/d-valerolactone copolymers, lactide/ε-caprolactone copolymers, L-lactide/DL-lactide copolymers, glycolide/L-lactide copolymers (PGA/PLLA), polylactide-co-glycolide; terpolymers of PLA, such as lactide/glycolide/trimethylene carbonate terpolymers, lactide/glycolide/ε-caprolactone terpolymers, PLA/polyethylene oxide copolymers; polydepsipeptides; unsymmetrically- 3,6-substituted poly-1,4-dioxane-2,5-diones; polyhydroxyalkanoates, such as polyhydroxybutyrates) PHB); PHB/b-hydroxyvalerate copolymers (PHB/PHV); poly-b-hydroxypropionate (PHPA);poly-p-dioxanone (PDS); poly-d-valerolactone-poly-ε-capralactone, poly(ε-caprolactone-DL-lactide) copolymers; methylmethacrylate-N-vinyl pyrrolidone copolymers; polyesteramides;polyesters of oxalic acid; polydihydropyrans; polyalkyl-2-cyanoacrylates; polyurethanes (PU);polyvinylalcohol (PVA); polypeptides; poly-b-malic acid (PMLA): poly-b-alkanoic acids;polycarbonates; polyorthoesters; polyphosphates; poly(ester anhydrides); and derivatives, copolymers and mixtures thereof.
  • 5. The implant of claim 1, wherein the polymer is in a form of a polymer matrix; wherein said polymer matrix comprises a polymer selected from the group consisting of PLLA (poly-L-lactide), PDLLA (poly-DL-lactide), PLDLA, PGA (poly-glycolic acid), PLGA (poly-lactide-glycolic acid), PCL (polycaprolactone), PLLA-PCL and a combination thereof.
  • 6. The implant of claim 5, wherein an inherent viscosity (IV) of the polymer matrix alone is in the range of 0.2-6 dl/g, 1.0 to 3.0 dl/g, 1.5 to 2.4 dl/g, or 1.6 to 2.0 dl/g, wherein IV is measured according to a flow time of a polymer solution through a narrow capillary relative to the flow time of a pure solvent through the capillary.
  • 7. The implant of claim 1, wherein if PLLA is used, the matrix comprises at least 30% 50%, or at least 70% PLLA; or wherein if PDLA is used, the matrix comprises at least 5%, at least 10%, or at least 20% PDLA.
  • 8. The implant of claim 1, wherein said weight ratio is in a range of 0.75:1 to 1.25:1.
  • 9. The implant of claim 8, wherein said fibers comprise one or more of a biodegradable glass or glass-like materials, a ceramic, a mineral composition (optionally including one or more of hydroxyapatite, tricalcium phosphate, calcium sulfate, calcium phosphate), a cellulosic material, a nano-diamond, or any other filler known in the art to increase the mechanical properties of a bioabsorbable polymer, or wherein said fiber comprises a bioabsorbable glass, ceramic, or mineral composition.
  • 10. The implant of claim 9, wherein said biodegradable glass has oxide compositions in the following mol. % ranges (as a percent over the glass fiber composition): Na2O: 11.0-19.0 mol. %,CaO: 9.0-14.0 mol. %,MgO: 1.5-8.0 mol. %,B2O3: 0.5-3.0 mol. %,Al2O3: 0-0.8 mol. %,P2O3: 0.1-0.8 mol. %,SiO2: 67-73 mol. %.
  • 11. The implant of claim 10 where said ranges are the following mol. % ranges: Na2O: 12.0-13.0 mol. %,CaO: 9.0-10.0 mol. %,MgO: 7.0-8.0 mol. %,B2O3: 1.4-2.0 mol. %,P2O3: 0.5-0.8 mol. %,SiO2: 68-70 mol. %.
  • 12. The implant of claim 1, wherein an average fiber diameter is between 5 and 50 um.
  • 13. The implant of claim 12, wherein a tensile strength of the reinforcement fiber is in the range of 1200-2800 MPa, or wherein an elastic modulus of the reinforcement fiber is in the range of 30-100 GPa, or a combination thereof.
  • 14. The implant of claim 1 wherein at least 50% of elastic modulus is retained following exposure to simulated body fluid (SBF) at 50 C for 3 days, or at least 70% is retained, and even at least 80% is retained.
  • 15. The implant of claim 1 wherein implant is an orthopedic implant and is selected from the groups including bone fixation plates, intramedullary nails, joint (hip, knee, elbow) implants, spine implants, screws, pins, wires, soft tissue anchors and other devices for such applications such as for fracture fixation, tendon reattachment, spinal fixation, and spinal cages.
  • 16. The implant of claim 1 wherein a reinforcing fiber diameter is in a range of 2-40 um, 8-20 um, or 12-18 um (microns).
  • 17. The implant of claim 1, wherein the orthopedic fixation implant is a pin, plate, screw, nail, fiber, sheet, rod, staple, clip, needle, tube, anchor, cable, tie, or wire tie.
  • 18. The implant of claim 17, wherein the implant is a pin, screw, plate, nail, rod, staple, or wire.
PCT Information
Filing Document Filing Date Country Kind
PCT/IL2015/050903 9/7/2015 WO 00
Publishing Document Publishing Date Country Kind
WO2016/035088 3/10/2016 WO A
US Referenced Citations (44)
Number Name Date Kind
4911718 Lee et al. Mar 1990 A
5064439 Chang Nov 1991 A
5312669 Bedard May 1994 A
5522817 Sander Jun 1996 A
5522904 Moran Jun 1996 A
5674294 Bainville et al. Oct 1997 A
6004650 Schweizer Dec 1999 A
6299649 Chang Oct 2001 B1
6471707 Miller Oct 2002 B1
6511511 Slivka Jan 2003 B1
6916321 Tenhuisen Jul 2005 B2
7541049 Toermaelae Jun 2009 B1
7918879 Yeung Apr 2011 B2
7947069 Sanders May 2011 B2
8702716 Stein Apr 2014 B1
8992622 Ullrich, Jr. Mar 2015 B2
20050118326 Anfinsen Jun 2005 A1
20050177245 Leatherbury Aug 2005 A1
20050216016 Contiliano Sep 2005 A1
20050226904 Choi Oct 2005 A1
20050228500 Kim Oct 2005 A1
20060020266 Cooper Jan 2006 A1
20060095134 Trieu et al. May 2006 A1
20060154206 Petersson Jul 2006 A1
20060178748 Dinger, III Aug 2006 A1
20070150059 Ruberte Jun 2007 A1
20070185568 Schwartz Aug 2007 A1
20070270969 Schmid Nov 2007 A1
20070282455 Luginbuehl Dec 2007 A1
20090112317 Li Apr 2009 A1
20090240337 Myung Sep 2009 A1
20090304761 Rabiei Dec 2009 A1
20100119564 Kasuga May 2010 A1
20100168798 Clineff Jul 2010 A1
20110098826 Mauck Apr 2011 A1
20110166659 Luginbühl et al. Jul 2011 A1
20120040015 Lehtonen Feb 2012 A1
20120040137 Palasis Feb 2012 A1
20120191214 Nies Jul 2012 A1
20120265206 Jang Oct 2012 A1
20130144400 Day Jun 2013 A1
20130218291 Giorno Aug 2013 A1
20130317555 Schaller Nov 2013 A1
20150289979 Gabele Oct 2015 A1
Foreign Referenced Citations (34)
Number Date Country
1168105 Dec 1997 CN
1214939 Apr 1999 CN
1371664 Oct 2002 CN
1565396 Jan 2005 CN
1593356 Mar 2005 CN
1953719 Apr 2007 CN
101437467 May 2009 CN
101790559 Jul 2010 CN
102395329 Mar 2012 CN
102421463 Apr 2012 CN
1716874 Nov 2006 EP
2292166 Mar 2011 EP
3236866 Nov 2017 EP
6415040 Jan 1989 JP
2002501418 Jan 2002 JP
2004160157 Jun 2004 JP
2008200510 Sep 2008 JP
2009541568 Nov 2009 JP
9819616 May 1998 WO
9819617 May 1998 WO
9853768 Dec 1998 WO
9853768 Dec 1998 WO
0132072 May 2001 WO
2005077039 Aug 2005 WO
2005077039 Aug 2005 WO
2005077039 Aug 2005 WO
2010122019 Oct 2010 WO
2010122098 Oct 2010 WO
2013116624 Aug 2013 WO
2016035088 Mar 2016 WO
2016035088 Mar 2016 WO
2016103049 Jun 2016 WO
2016103049 Jun 2016 WO
2017155956 Sep 2017 WO
Non-Patent Literature Citations (39)
Entry
Search report for parent PCT application No. PCT/IL2015/050903, dated Jan. 7, 2016.
European Search Report for EP15838477.6 dated Mar. 5, 2018, 5 pages.
Scholz et al., “Composites Science and Technology”, www.elsevier.com/locate/compscitech 71(2011) 1791-1803.
Supplementary European Search Report for EP15837823 dated Mar. 28, 2018, 6 pgs.
European Search Report and Written Opinion dated Jun. 12, 2018 for EP Application No. 158720441, 5 pages.
Chinese Office Action dated Jul. 13, 2018 for corresponding CN Patent Application No. 201580037255.8, 9 pages.
Arthrex Inc., “BioComposite Interference Screws—A Stronger turn in ACL/PCL Reconstruction”, Scientific Research and Development, (20100000), URL: http://www.arthrex.com/knee/biocomposite-interference-screws.
Brazilian Search Report (with English language translation) for App No. BR112017001049-6, dated Apr. 8, 2020, 8 pages.
Brazilian Technical Report (with English language translation) for App No. BR112017012508-0, dated Apr. 8, 2020, 7 pages.
Chinese Office Action (with English language translation) for App No. CN201580070362.0, dated May 20, 2020, 9 pages.
Hyon et al., “Effects of Residual Monomer on the Degradation of DL-Lactide Polymer” Polymer International 46 (1998) 196-202.
Australian Examination Report No. 1 for Application No. AU2015370600, dated Oct. 2, 2019, 3 pages.
Chinese Office Action (with English language translation) for Application No. CN201580036606.3, dated Oct. 25, 2019, 9 pages.
European Search Report dated Oct. 16, 2019 for EP Application No. 17763876.4, 11 pages.
International Search Report issued in PCT/IL2019/050843, dated Nov. 6, 2019, 3 pages.
Japanese Office Action (with English language translation) for Application No. JP2017-527796, dated Nov. 5, 2019, 6 pages.
Kulkova J. et al. “Hydroxyapatite and bioactive glass surfaces for fiber reinforced composite implants via surface ablation by Excimer laser” (2017) Journal of the Mechanical Behavior of Biomedical Materials, vol. 75, pp. 89-96, DOI: 10.1016/j.jmbbm.2017.07.005 (published on-line Jul. 4, 2017).
Office Action dated Nov. 18, 2019 for U.S. Appl. No. 16/081,605 (pp. 1-19).
Office Action dated Nov. 7, 2019 for U.S. Appl. No. 15/523,389 (pp. 1-11).
Australian Examination Report No. 2 for Application No. AU2015310510, dated Dec. 1, 2019, 3 pages.
Australian Examination Report No. 2 for Application No. AU2015370600, dated Jan. 29, 2020, 2 pages.
Extended European Search Report for Application No. EP17819487.4, dated Feb. 4, 2020, 7 pages.
Extended European Search Report for Application No. EP19200585.8, dated Feb. 28, 2020, 8 pages.
Japanese Office Action (with English language translation) for Application No. JP2017-504425, dated Jan. 7, 2020, 6 pages.
Office Action dated Dec. 26, 2019 for U.S. Appl. No. 15/509,274, 18 pages.
Office Action dated Feb. 10, 2020, for U.S. Appl. No. 16/081,605 (pp. 1-17).
Office Action dated Jan. 13, 2020 for U.S. Appl. No. 15/523,389 (pp. 1-11).
Australian Examination Report No. 1 for Application No. 2015310510, dated Aug. 10, 2019, 6 pages.
Chinese Office Action (with English language translation) for Application No. 201580036606.3, dated Mar. 12, 2019, 13 pages.
Chinese Office Action (with English language translation) for Application No. CN201580037255.8, dated Aug. 26, 2019, 16 pages.
Chinese Office Action (with English language translation) for Application No. CN201580070362.0, dated Aug. 29, 2019, 10 pages.
Chinese Office Action for Appl. No. 201580037255.8, dated Mar. 26, 2019, 7 pages.
IP Office of Singapore Written Opinion for Application No. SG11201610671P, dated Aug. 14, 2019, 5 pages.
Japanese Office Action (with English language translation) for Application No. 2017-504425, dated May 28, 2019, 7 pages.
Office Action dated Aug. 5, 2019 for U.S. Appl. No. 15/509,274 (pp. 1-19).
Wang et al., “Promising Poly(E-caprolactone) composite reinforced with weft-knitted polyester for small-diameter vascular graft application”, Advances in Materials Science and Engineering, 2014, vol. 2014, p. 273891.
Wegener et al., “Microstructure, cytotoxicity and corrosion of powder-metallurgical iron alloys for biodegradable bone replacement materials”, Materials Science & Engineering. B. Advanced Functional Solid-State Materials, 2011, vol. 176, No. 20, p. 1789-1796.
European Patent Office Communication pursuant to Article 94(3) EPC for App. No. EP17763876.4, dated Aug. 19, 2020, 9 pages.
Office Action dated Jul. 13, 2020 for U.S. Appl. No. 15/523,389 (pp. 1-12).
Related Publications (1)
Number Date Country
20170246355 A1 Aug 2017 US
Provisional Applications (1)
Number Date Country
62047023 Sep 2014 US