The present disclosure relates to an anode layer for a fluoride ion battery in which decomposition of a binder is restrained.
Li ion batteries have been known as a battery with a high voltage and high energy density for example. The Li ion battery is a cation based battery utilizing the reaction of Li ions with cathode active materials, and the reaction of Li ions with anode active materials. On the other hand, fluoride ion batteries have been known as an anion based battery that utilizes the reaction of fluoride ions.
For example, Patent Literature 1 discloses an electrode utilizing fluoride ions, the electrode containing carbon nanomaterials, a metal-based material, and a polymeric binder. Further, in Examples of Patent Literature 1, polyvinylidene fluoride (PVDF) is used as the polymeric binder.
In a fluoride ion battery, fluoride ions directly contribute to a reaction with anode active materials. If a fluorine-based binder such as PVDF is used therein, the anode active material affects the fluorine contained in the fluorine-based binder and easily brings decomposition of the binder (reductive decomposition).
The present disclosure has been made in view of the above circumstances, and an object thereof is to provide an anode layer (an anode layer for a fluoride ion battery) in which decomposition of a binder is restrained.
To achieve the above object, the present disclosure provides an anode layer to be used for a fluoride ion battery, the anode layer comprising an anode active material and a non-fluorine-based binder having aromaticity.
According to the present disclosure, using the non-fluorine-based binder having aromaticity allows the anode layer in which decomposition of the binder is restrained.
In the disclosure, the non-fluorine-based binder is preferably a polyimide resin.
Also, the present disclosure provides a fluoride ion battery comprising a cathode layer, an anode layer, and an electrolyte layer formed between the cathode layer and the anode layer, wherein the anode layer is the above described anode layer.
According to the present disclosure, using the above described anode layer allows a fluoride ion battery to have favorable durability.
The anode layer for a fluoride ion battery of the present disclosure exhibits effects such that decomposition of a binder is restrained.
The anode layer for a fluoride ion battery and the fluoride ion battery of the present disclosure are hereinafter described in details.
A. Anode Layer for Fluoride Ion Battery
The anode layer for a fluoride ion battery of the present disclosure comprises an anode active material and a non-fluorine-based binder having aromaticity.
According to the present disclosure, using the non-fluorine-based binder having aromaticity allows the anode layer in which decomposition of the binder is restrained. If a fluorine-based binder such as PVDF is used herein, a reductive decomposition of the binder may proceed along with the usage of the fluoride ion battery, to possibly cause a capacity decrease and a deterioration of the cycle property due to the adhesion decrease of the anode active material to the anode current collector. For example, lithium ion batteries utilizing a carbon material as the anode active material have been generally known; in that case, usage of the fluorine-based binder for the anode layer does not cause a big problem. The reason therefor is that Li ions (cations) react with the anode active material prior to the reductive decomposition of the binder.
In contrast, in fluoride ion batteries, the fluoride ions directly contribute to the reaction with the anode active material, so that not only the fluoride ions in the electrolyte material but also the fluorine included in the fluorine-based binder are used for the reaction to promote the reductive decomposition of the binder. In the present disclosure, the reductive decomposition of the binder may be restrained since the binder not containing fluorine is used. Further, the non-fluorine-based binder having aromaticity allows high stability to fluoride ions. In these manners, the capacity decrease and the deterioration of the cycle property due to the adhesion decrease may be restrained.
The anode layer for a fluoride ion battery of the present disclosure is hereinafter described in each constitution.
1. Anode Active Material
Examples of the anode active material in the present disclosure may include a simple substance of metal, an alloy, a metal oxide, and fluorides thereof. Examples of the metal element to be contained in the anode active material may include La, Ca, Al, Eu, Li, Si, Ge, Sn, In, V, Cd, Cr, Fe, Zn, Ga, Ti, Nb, Mn, Yb, Zr, Sm, Ce, Mg, and Pb. Above all, the anode active material is preferably Mg, MgFx, Al, AlFx, Ce, CeFx, Ca, CaFx, Pb, and PbFx. Incidentally, the “x” is a real number larger than 0. Also, other examples of the anode active material may include carbon materials and fluorides thereof. Examples of the carbon material may include graphite, coke, and carbon nanotube. Also, additional examples of the anode active material may include polymeric materials. Examples of the polymeric material may include polyaniline, polypyrrole, polyacetylene, and polythiophene.
Examples of the shape of the anode active material may include a granular shape. The average particle diameter (D50) of the anode active material is, for example, in a range of 0.1 μm to 50 μm, and may be in a range of 1 μm to 20 μm. Also, the content of the anode active material in the anode layer is preferably larger from the viewpoint of the capacity. The content of the anode active material is, for example, 50 volume % or more and preferably 70 volume % or more.
2. Non-Fluorine-Based Binder
The non-fluorine-based binder in the present disclosure has aromaticity. Here, “non-fluorine-based” refers to the binder that does not contain fluorine as the constituent of the binder. Incidentally, if the binder not containing fluorine is exposed to fluoride ions in the battery, the fluoride ions may possibly be adsorbed to apart of the binder (fluorinated). The fluoride ions adsorbed this way do not fall under the constituent of the binder. Also, the binder may be a non-halogen-based binder that does not contain halogen as the constituent of the binder. Also, “having aromaticity” refers to having a conjugated unsaturated ring structure (an aromatic structure). Examples of the aromatic structure may include an aromatic hydrocarbon structure comprising only hydrocarbon, and a heteroaromatic structure in which an element other than carbon is included in the cyclic structure. Examples of the element other than carbon may include nitrogen.
Examples of the non-fluorine-based binder may include a polyimide resin, a polyphenylene sulfide resin, and a polyphenylene ether resin.
Examples of the polyimide resin may include a resin represented by the following general formula (1). In the formula, R and R′ are each independently an arbitrary atomic group; however, at least one of R and R′ has aromaticity, and preferably both R and R′ have aromaticity. Such a polyimide resin has high stability to fluoride ions. Incidentally, “n” is an arbitrary positive number.
The polyimide resin may be obtained by heat treating a precursor (a polyamic acid) for example. Examples of the precursor of the polyimide resin may include a polyamic acid synthesized from a composition containing a tetracarboxylic dianhydride and a diamine. A typical example of the method for synthesizing the polyimide resin may be conducting a heat treatment to imidize a polyamic acid, in which a pyromellitic dianhydride and 4,4′-diaminodiphenylether are polymerized, as shown in the following reaction formula.
Examples of the tetracarboxylic dianhydride may include: an alicyclic tetracarboxylic anhydride (such as a cyclohexanetetracarboxylic dianhydride), and an aromatic tetracarboxylic dianhydride (such as: arenetetracarboxylic anhydrides such as pyromellitic dianhydride and naphthalene-tetracarboxylic dianhydride; bisphenoltetracarboxylic dianhydrides such as biphenyltetracarboxylic dianhydrides, biphenylethertetracarboxylic dianhydrides such as 4,4′-oxydiphthalic anhydride (ODPA, 3,4,3′,4′-diphenylethertetracarboxylic dianhydride), benzophenonetetracarboxylic dianhydrides, biphenylalkanetetracarboxylic dianhydrides, and biphenylsulfonetetracarboxylic dianhydrides; and biphenilethertetracarboxylic dianhydrides having a biphenylalkane skeleton such as 4,4′-(4,4′-isopropylidenediphenoxy)bis(phthalic anhydride) (BPADA, the anhydride of 2,2-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane)).
Examples of the diamine may include an aliphatic diamine (such as: straight chain or branched chain alkylene diamines such as ethylenediamine, propylenediamine, 1,4-butylenediamine, hexamethylenediamine, and trimethylhexamethylenediamine; and polyetherdiamines), an alicyclic diamine (such as: bis(aminocyclohexyl)alkanes such as menthenediamine, isophoronediamine, hydrogen-added-xylylenediamine, diaminodicyclohexylmethane, and bis(4-amino-3-methylcyclohexyl)methane), and an aromatic diamine [such as: phenylenediamines, xylenediamines, bis(aminophenyl)ethers such as 4,4′-diaminodiphenylether, bis(aminophenyl)ketones such as 4,4′-diaminodiphenylketone, bis(aminophenyl)sulfones such as 4,4′-diaminodiphenylsulfone, such as bis(aminophenyl)alkanes such as 1,1-bis(4-aminophenyl)methane, and bis(aminophenyl)benzenes such as 1,3-bis(2-aminophenyl)benzene. These acid anhydrides and diamines may respectively be used alone or in combination of the two kinds or more.
The weight average molecular weight of the polyimide resin is preferably in a range of 3,000 to 1,000,000 for example. The weight average molecular weight refers to a value calculated as polystyrene according to the gel permeation chromatography (GPC).
The content of the non-fluorine-based binder in the anode layer is preferably smaller from the viewpoint of the capacity. The content of the non-fluorine-based binder is 30 volume % or less for example, and preferably 15 volume % or less.
3. Anode Layer
The anode layer of the present disclosure may further contain a conductive material. The conductive material is not particularly limited if it has the desired electron conductivity, and examples thereof may include carbon materials. Examples of the carbon material may include carbon blacks such as acetylene black, Ketjen black, furnace black and thermal black. Also, the thickness of the anode layer is in a range of 0.1 μm to 1000 μm for example.
An example of the method for producing the anode layer is a method wherein slurry containing an anode active material and a binder precursor (such as polyamic acid) is used for a coating, and thereafter the coating is heat treated to obtain a binder (such as polyimide) from the binder precursor. Another example of the method for producing the anode layer is a method wherein slurry containing an anode active material and a binder is used for coating, and then dried.
B. Fluoride Ion Battery
According to the present disclosure, usage of the above described anode layer allows a fluoride ion battery to have favorable durability.
The fluoride ion battery of the present disclosure is hereinafter described in each constitution.
1. Anode Layer
The anode layer in the present disclosure is in the same contents as the description in “A. Anode layer for fluoride ion battery” above; thus, the description herein is omitted.
2. Cathode Layer
The cathode layer in the present disclosure is a layer containing at least a cathode active material. Also, the cathode layer may further contain at least one of a conductive material and a binder other than the cathode active material.
Examples of the cathode active material in the present disclosure may include a simple substance of metal, an alloy, a metal oxide, and fluorides thereof. Examples of the metal element to be contained in the cathode active material may include Cu, Ag, Ni, Co, Pb, Ce, Mn, Au, Pt, Rh, V, Os, Ru, Fe, Cr, Bi, Nb, Sb, Ti, Sn, and Zn. Above all, the cathode active material is preferably Cu, CuFx, Fe, FeFx, Ag, and AgFx. Incidentally, the “x” is a real number larger than 0. Also, the above described carbon materials and polymeric materials may be used as the cathode active material.
The same conductive materials described in “A. Anode layer for fluoride ion battery” above can be used as the conductive material. Examples of the binder may include fluorine-based binders such as polyvinylidene fluoride (PVDF) and polytetra fluoroethylene (PTFE). Also, the content of the cathode active material in the cathode layer is preferably larger from the viewpoint of the capacity. Also, the thickness of the cathode layer may greatly vary with the constitution of the battery, and thus is not particularly limited.
3. Electrolyte Layer
The electrolyte layer in the present disclosure is a layer to be formed between the cathode layer and the anode layer. The electrolyte material included in the electrolyte layer may be an electrolyte solution (liquid electrolyte) and may be a solid electrolyte material.
The liquid electrolyte contains a fluoride salt and an organic solvent for example. Examples of the fluoride salt may include inorganic fluoride salts and organic fluoride salts. An example of the inorganic fluoride salt is XF (X is Li, Na, K, Rb, or Cs). An example of the cation of the organic fluoride salt is alkylammonium cations such as tetramethylammonium cation. The concentration of the fluoride salt in the liquid electrolyte is in a range of 0.1 mol % to 40 mol % for example, and preferably in a range of 1 mol % to 10 mol %. Also, the liquid electrolyte may contain a fluoride complex salt such as LiPF6.
Examples of the organic solvent for the liquid electrolyte may include glyme such as triethylene glycol dimethyl ether (G3) and tetraethylene glycol dimethyl ether (G4), cyclic carbonates such as ethylene carbonate (EC), fluoroethylene carbonate (FEC), difluoroethylene carbonate (DFEC), propylene carbonate (PC) and butylene carbonate (BC), and chain carbonates such as dimethyl carbonate (DMC), diethyl carbonate (DEC), and ethyl methyl carbonate (EMC). Also, an ionic solution may be used as the organic solvent.
Meanwhile, examples of the solid electrolyte material may include fluorides of lanthanoid elements such as La and Ce, fluorides of alkali elements such as Li, Na, K, Rb, and Cs, and fluorides of alkali earth elements such as Ca, Sr, and Ba. Specific examples thereof may include a fluoride of La and Ba (such as La0.9Ba0.1F2.9), and a fluoride of Pb and Sn.
4. Other Constitutions
The fluoride ion battery of the present disclosure comprises at least the above described anode layer, cathode layer, and electrolyte layer, and usually further comprises a cathode current collector for collecting currents of the cathode layer, and an anode current collector for collecting currents of the anode layer. Examples of the shape of the current collectors may include a foil shape, a mesh shape, and a porous shape. Also, the fluoride ion battery of the present disclosure may comprise a separator between the cathode layer and the anode layer. The reason therefor is to obtain a battery with higher safety.
5. Fluoride Ion Battery
The fluoride ion battery of the present disclosure may be a primary battery and may be a secondary battery, but preferably is a secondary battery among them, so as to be repeatedly charged and discharged and useful as a car mounted battery for example. Also, examples of the shape of the fluoride ion battery may include a coin shape, a laminate shape, a cylindrical shape, and a square shape.
Incidentally, the present disclosure is not limited to the embodiments. The embodiments are exemplification, and other variations are intended to be included in the technical scope of the present disclosure if they have substantially the same constitution as the technical idea described in the claim of the present disclosure and offer similar operation and effect thereto.
The present disclosure is hereinafter described in more details with reference to Examples.
Prepared were Fe (manufactured by JAPAN PURE CHEMICAL CO., LTD.) as an active material and a polyimide resin (PI, DREAMBOND, manufactured by Industrial Summit Technology) as a binder, which were mixed at the solid weight ratio of Fe:PI=9:2 and used for coating a Fe foil (manufactured by The Nilaco Corporation), then heated at 200° C. in vacuum for 10 hours. Thereby, an evaluation electrode was obtained.
Prepared were Fe (manufactured by JAPAN PURE CHEMICAL CO., LTD.) as an active material and a polyvinylidene fluoride (PVdF, manufactured by Kureha Battery Materials Japan) as a binder, which were mixed at the solid weight ratio of Fe:PVdF=9:0.75 and used for coating a Fe foil (manufactured by The Nilaco Corporation), then heated at 120° C. in vacuum for 10 hours. Thereby, an evaluation electrode was obtained.
Prepared were Al (manufactured by JAPAN PURE CHEMICAL CO., LTD.) as an active material and a polytetra fluoroethylene (PTFE, manufactured by Du Pont-Mitsui Fluorochemicals Co., Ltd.) as a binder, which were kneaded and formed at the solid weight ratio of Al:PTFE=19:1 and used for coating an Al foil (manufactured by The Nilaco Corporation), then heated at 120° C. in vacuum for 10 hours. Thereby, an evaluation electrode was obtained.
An Fe foil (manufactured by The Nilaco Corporation) was used as an evaluation electrode.
An Al foil (manufactured by The Nilaco Corporation) was used as an evaluation electrode.
A foamed Al (manufactured by Mitsubishi Materials Corporation) was used as an evaluation electrode.
[Evaluations]
(Cyclic Voltammetry Measurement)
A CV measurement was conducted for the evaluation electrodes obtained in Example 1, Comparative Examples 1 and 2, and Reference Examples 1 to 3. First, a liquid electrolyte was produced. In specific, triglyme (G3, manufactured by KANTO CHEMICAL CO., INC.), lithium hexafluorophosphate (LiPF6, manufactured by Kishida Chemical Co., Ltd.), and lithium fluoride (LiF, manufactured by Wako Pure Chemical Industries, Ltd.) were weighed and mixed so as to be G3:LiPF6:LiF=20:5:1 in the molar ratio, and then stirred at 30° C. in a sealed container made of fluororesin to obtain the liquid electrolyte.
Next, a dip-type 3-electrodes cell was produced in a glove box under an Ar atmosphere. The evaluation electrode was used as the working electrode, and a mixture electrode of PTFE, acetylene black (AB), and carbon fluoride was used as the counter electrode. Incidentally, the mixture electrode was an electrode that contains the materials in the weight ratio of PTFE:AB:carbon fluoride=1:2:7. Also, a reference electrode was separated from the liquid electrolyte by a Vycor glass. Incidentally, the reference electrode used was a Ag line soaked in an acetonitrile solution in which silver nitrate and tetrabutylammonium perchlorate were dissolved in the concentration of 0.1 M respectively. The measurement was conducted in the conditions of at a room temperature and sweeping speed of 1 mV/s. Incidentally, regarding the potentials described in later described
The result of the reduction potential is shown in
On the other hand, as shown in
Number | Date | Country | Kind |
---|---|---|---|
2016-111053 | Jun 2016 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
7972725 | Krause | Jul 2011 | B2 |
20100021800 | Yazami et al. | Jan 2010 | A1 |
20160087308 | Nakamoto | Mar 2016 | A1 |
Number | Date | Country | |
---|---|---|---|
20170352887 A1 | Dec 2017 | US |