Anodic bonding process and method of producing an ink-jet print head using the same process

Abstract
A method of producing an ink-jet print head comprises the step of joining a head base to a vibrating plate without use of any adhesive and has a sufficient joining strength even if the joining layers are formed to be as thin as possible. The joining process comprises the steps of providing a head base of glass including an array of individual ink passages formed therein, forming an electrically conductive film on the joint surface of the head base through sputtering, superposing a vibrating plate of glass on the joint surface of the head base through the electrically conductive film, and applying a voltage between the head base and vibrating plate with the electrically conductive film and vibrating plate being respectively anode and cathode while being subjected to pressure and heat, thereby carry out anodic bonding the head base and vibrating plate to each other.
Description

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a process of anodic bonding between substrates and particularly to a method of producing an ink-jet print head which can be mounted in an electronic instrument such as a printer, a word processor, a facsimile machine, a plotter or the like.
2. Description of the Related Art
Various electric instruments include an ink-jet print head which functions as part of the printing mechanism thereof. There is known Kyser type of ink-jet print head. As shown in FIGS. 1 to 3, such a type of ink-jet print head generally comprises a head base 50 in which an array of individual ink passages 51 are formed. As best seen from FIG. 3, each of the individual ink passages 51 comprises an ink supply passage 51a, a pressure chamber 51b and a nozzle 51c. A vibrating plate 60 is joined over the top of the head base 50 and includes a plurality of piezoelectric elements 70 mounted thereon, each of which is positioned corresponding to the respective one of the pressure chambers 51b in the individual ink passages 51. When an electric field is applied to one of the piezoelectric elements 70 according to printing information, that piezoelectric element 70 is displaced. The displacement of the piezoelectric element 70 moves the corresponding part of the vibrating plate 60 to apply an instantaneous pressure to the ink which in turn is extruded from the individual ink passage 51 through its nozzle 51c. The extruded ink is thus sprayed toward a printing sheet. In producing the Kyser type print head, the head base and vibrating plate 50, 60 are frequently formed of glass. It is customary that after the individual ink passages 51 have been formed on the glass head base 50, the glass vibrating plate 60 is adhered to the head base 50 using any suitable adhesive.
It is, however, difficult to apply the adhesive onto the substrate (the head base and vibrating plate 50, 60) with a thickness equal to or less than a certain level. In addition, the adhesive has a fluidity. For such reasons, the adhesive tends to flow into the individual ink passages 51 during the joining step, resulting in reduction of the width in the individual ink passages 51. This frequently causes the flow of ink to be disturbed or partially blocked in the individual ink passages on use of the ink-jet print head. Particularly, narrower ink supply passages and nozzles 51a, 51c connected to the individual ink passages 51 may be very easily blocked by the adhesive used, resulting in complete blockage of ink in the individual ink passages.
SUMMARY OF THE INVENTION
It is therefore an object of the present invention to provide a method of producing an ink-jet print head which can overcome the aforementioned problem with respect to the flowing of the ink into the individual ink passages and which can provide a sufficient joining strength even if the thickness of the adhesive layer applied is reduced so as to be thin as possible.
The present invention provides an anodic bonding process characterized by the steps of providing two substrates to be joined, that is, a head base and a vibrating plate in an ink-jet print head; forming a film of electrically conductive material on the joint surface of one of the substrates while forming a film of glass on the joint surface of the other substrate, depending on the materials of the head base and vibrating plate themselves; mating the joint surfaces of the head base and vibrating plate; and applying a voltage between the head base and vibrating plate with the conductive and glass joint surfaces being respectively used as anode and cathode while heating the head base and vibrating plate under pressure. The present invention is based on the anodic bonding technique which is generally known as a process of joining a member of glass with another metal member without the need of any adhesive, that is, such a technique that at least two members of glass and metal to be joined to each other are superposed one above another and then subjected to application of a joining voltage while maintaining them at a temperature equal to or less than the softening point of the glass. In accordance with the principle of the anodic bonding, the joint surface of one of the head base and vibrating plate has a film which is made of electrically conductive material while the joint surface of the other of the head base and vibrating plate has a film which is formed of Glass material. Thereafter, the head base and vibrating plate are joined to each other by applying a voltage therebetween while being subjected to pressure and heat. Therefore, the materials of the head base and vibrating plate may be freely selected. Since no adhesive is used in the anodic bonding process, there will not be raised such a problem that the adhesive flows into the individual ink passages to disturb and/or block them. In addition, the anodic bonding process provides a sufficient joining strength between the base head and vibrating plate even though the films of conductive and glass materials formed on the point surfaces of the head base and vibrating plate depending on their materials are much thinner than that of the adhesive layer used and particularly have a thickness equal to or less than one .mu.m.





BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a perspective view of the outline of a conventional Kyser type print head.
FIG. 2 is a cross-sectional view of FIG. 1 taken along a line A--A therein.
FIG. 3 is a plan view showing the surface of a head base shown in FIG. 2.
FIG. 4 illustrates a first step in one embodiment of a print head producing process constructed in accordance with the present invention.
FIG. 5 is a plan view showing the surface of a head base shown in FIG. 4.
FIG. 6 illustrates a second step in the print head producing process of the present invention.
FIG. 7 illustrates a third step in the print head producing process of the present invention.
FIG. 8 is a plan view of a print head shown in FIG. 7.
FIG. 9 is a schematic view of an apparatus provided with an ink-jet print head which is produced according to the anodic bonding process of the present invention.





DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
A method of producing an ink-jet print head which is embodied in accordance with the present invention will be described by way of example with respect to the drawings. It is, however, to be understood that the illustrated embodiment of the present invention is applied to case that both the head base and vibrating plate are made of glass material.
FIGS. 4 through 8 sequentially illustrate various steps in the process of the present invention. Although a single print head is shown in these figures for convenience sake, it is to be understood that a plurality of print heads are actually produced at a time.
Referring first to FIG. 4, an array of individual ink passages 11 are formed in a head base 10 which is made of glass. Each of the individual ink passages 11 is of such a configuration as shown in FIG. 5 which comprises an ink supply passage 11a formed in the rearward end of the head base 10, a pressure chamber 11b connected to the ink supply passage 11a and a nozzle 11c formed in the forward end of the head base 10 and connected to the pressure chamber 11b.
An electrically conductive film 40 having a uniform thickness equal to or less than one .mu.m is then formed on the surface of the head base 10 through sputtering. As best seen from FIG. 5, the conductive film 40 covers the entire head base surface except the individual ink passages 11. A vibrating plate 20 made of glass material is superposed or mated on the surface of the head base 10 through the conductive film 40.
As shown in FIG. 6, thereafter, an assembly of the head base and vibrating plate 10, 20 is placed and heated in air atmosphere at a temperature ranged between room temperature and 600.degree. C. At the same time, a DC voltage ranged between 200 volts and 2000 volts is applied between the head base and vibrating plate with the conductive film 40 and vibrating plate 20 being respective anode and cathode while a load F ranged between about 200 g/cm.sup.2 and about 400 g/cm.sup.2 is being applied to the assembly. Under such conditions, the head base 10 is firmly joined to the vibrating plate 20 for a time period ranged between 10 seconds and 600 seconds depending on the materials of the head base and vibrating plate.
After being joined, a piezoelectric element 30 is adhered to the vibrating plate 20 at a location corresponding to each of the pressure chambers 11b in the individual ink passages 11 through any suitable conductive adhesive (see FIGS. 7 and 8). In such a manner, an equivalent print head as shown in FIG. 1 may be produced.
Although the embodiment of the present invention has been described as to the conductive film 40 formed on the point surface of the head base 10, the equivalent joining advantage can be provided even if a conductive film is formed on the point surface of the vibrating plate 20. Even if both the head base and vibrating plate 10, 20 are made of electrically conductive material, the process of the present invention may be similarly carried out. In the latter case, the illustrated conductive film 40 is replaced by a glass film which is formed on either of the head base 10 or vibrating plate 20.
If one of the head base and vibrating plate is made of glass while the other is formed of metal, the point surfaces of these components may be bonded directly to each other by the anodic bonding process. However, if both the head base and vibrating plate are formed of electrically conductive or glass material or plastic material or if one of the head base and vibrating plate is made of conductive or glass material while the other is formed of plastic material, the respective components must be coated with the conductive or glass material depending on the materials of the head base and vibrating plate themselves. More particularly, if both the head base and vibrating plate are formed of conductive material, the point surface of one of these components is coated with a glass film formed therein. If both the head base and vibrating plate are made of glass, an electrically conductive film is formed on the joint surface of one of the head base and vibrating plate. If one of the head base and vibrating plate is made of conductive or glass material while the other component is formed of plastic material, the joint surface of the other component is coated with a glass or conductive film. If both the head base and vibrating plate are formed of plastic material, a conductive film is formed on one of the joint surfaces while a glass film is formed on the other point surface. In such a manner, it is necessarily accomplished that one of the joint surface is formed of glass material while the other joint surface is made of conductive material. Therefore, the anodic bonding may be carried out against the head base and vibrating plate, irrespectively of their materials.
In the process of the present invention, the conductive and glass films may be formed through any suitable known technique such as sputtering, deposition, CVD (chemical vapor deposition), dipping or the like. The thickness of the respective conductive and glass films is substantially thinner than that of the adhesive layer and preferably equal to or less than about one .mu.m. The electrically conductive material usable in the present invention includes silicon, aluminum or the like.
The process of the present invention can be performed under the conventional anodic bonding conditions, for example, under a pressure from a load ranged between 200 g/cm.sup.2 and 400 g/cm.sup.2 at a temperature from a heated air atmosphere ranged between room temperature and 600.degree. C. However, when a glass film is to be formed on the joint surface of plastic material, the glass film is preferably of low-melting point glass, in view of the melting points of plastics in general. In this case, thus, the heating temperature will be ranged between room temperature and about 150.degree. C. When a low-melting point glass film is formed on the joint surface of a glass substrate, the latter can be subjected to the anodic bonding process at a temperature lower than the normal level. DC voltage ranged between 200 volts and 2000 volts is used in the anodic bonding process of the present invention when the conductive and glass joint surfaces are set to be anode and cathode, respectively. Depending on the materials of the head base vibrating plate themselves, the process may be performed for a time period ranged between 10 seconds and 600 seconds.
Although the process of the present invention is characterized by the joining step, the other steps such as steps of forming a plurality of individual ink passages on the head base, mounting the piezoelectric elements on the vibrating plate at locations corresponding to the individual ink passages after formation of the individual ink passages, forming a pattern wiring relating to the piezoelectric elements and others may be carried out in accordance with the related art.
Referring next to FIG. 9, there is schematically shown an ink-jet printer 70 provided with an ink-jet print head which is constructed in accordance with the present invention.
The ink-jet printer 70 comprises a paper tray 78 on which sheets of paper 76 are stacked; a conveying path 90 for conveying a sheet of paper at a time from the stacked sheet; three pairs of rollers (92a, 92b; 92c, 92d; 92e, 92f) for moving the sheets 76 along the conveying path 90; an ink-jet print head 72 constructed according to the present invention which is movably arranged on a line transverse to the conveying path 90 and adapted to spray the ink against the sheet of paper 76 moved thereto by the rollers (92a, 92b and 92c, 92d); a capping mechanism 74 for protecting the ink-jet print head and for drawing and exhausting an excess of the ink sprayed from the ink-jet print heads 72 onto the sheet of paper 76 when there is any failure such as clogging in the nozzle portion; and a sheet receiver 94 onto which the sheets of paper 76 are moved and stacked by the rollers 92e, 92f after the ink has been fixed on the sheets of paper 76.
On operation, the sheets 76 are fed out of the paper tray 78 one at a time. The sheet 76 is moved to the ink-jet print head 72 along the conveying path 90 by the rollers (92a, 92b and 92c, 92d). The ink is then sprayed onto the moved sheet 76 through the ink-jet print head 72 to form a desired image thereon. In use, the nozzle of the ink-jet print head is directed toward the sheet 76 as shown. When it is not used, however, the nozzle is oriented in a direction out of the sheet 76. Thus, the sheet will not be contaminated with ink even in the event of any wrong function.
The sheet 76 is then moved to and stacked in the sheet receiver 94 by the rollers 92e and 92f.
Thus, the materials of the head base and vibrating plate of the ink jet print head may be freely selected so that cost for the materials, or processing will be decreased. No adhesive is used in the anodic bonding process so that there will not be raised such a problem that the adhesive flows into the individual ink passages to disturb and/or block them. As the results, the apparatus provides high quality printing.
The present invention is not limited to such an ink-jet printer as described above, but may be similarly applied to any other apparatus having an ink-jet print head, such as a word processor, a facsimile, a plotter and the like.
Claims
  • 1. A method of producing an ink-jet print head, the method comprising the steps of:
  • providing a first substrate having a surface including plastic;
  • providing a second substrate having a surface with a conductive material;
  • forming a glass film on the surface of the first substrate, the glass having a low melting point;
  • positioning the first and second substrates one above another after the glass film has been formed on the surface of the first substrate so that the surfaces face each other;
  • applying pressure and heat to the substrates; and
  • applying a voltage between the first and second substrates while subjecting the substrates to pressure and heat.
  • 2. A method of producing an ink-jet print head as defined in claim 1 wherein the glass film is formed by sputtering.
  • 3. A method of producing an ink-jet print head as defined in claim 1 wherein the glass film is formed by deposition.
  • 4. A method of producing an ink-jet print head as defined in claim 1 wherein the glass film is formed by dipping,
  • 5. A method of producing an ink-jet print head as defined in claim 1 wherein the glass film is formed of low-melting glass.
  • 6. A method of producing an ink-jet print head as defined in claim 1 wherein the glass film is formed by chemical vapor deposition.
  • 7. The method of claim 1 wherein the step of applying heat comprises applying heat of about 150.degree. C. maximum.
  • 8. A method of producing an ink-jet print head, the method comprising the steps of:
  • providing a first substrate having a surface including a plastic material;
  • providing a second substrate having a surface made from glass, the glass having a low melting point;
  • forming a conductive film on the surface of the first substrate;
  • positioning the first and second substrates one above another after the conductive film has been formed on the surface of the first substrate so that the surfaces face each other;
  • applying pressure and heat to the substrates; and
  • applying a voltage between the first and second substrates while subjecting the substrates to pressure and heat.
  • 9. A method of producing an ink-jet print head as defined in claim 8 wherein the electrically conductive film is formed of aluminum.
  • 10. A method of producing an ink-jet print head as defined in claim 8 wherein the electrically conductive film is formed by sputtering.
  • 11. A method of producing an ink-jet print head as defined in claim 8 wherein the electrically conductive film is formed by deposition.
  • 12. A method of producing an ink-jet print head as defined in claim 8 wherein the electrically conductive film is formed by chemical vapor deposition.
  • 13. The method of claim 8 wherein the step of applying heat comprises applying heat of about 150.degree. C. maximum.
  • 14. A method of producing an ink-jet print head as defined in claim 8 wherein the electrically conductive film is formed by dipping.
  • 15. A method of producing an ink-jet print head as defined in claim 8 wherein the electrically conductive film is formed of silicon.
  • 16. A method for making an apparatus having an ink-jet print head, the method including the steps of:
  • providing a head base including a plurality of individual ink passages formed therein,
  • providing a vibrating plate to be joined to said head base, wherein one of the head base and vibrating plate includes plastic, wherein one of the vibrating plate and the head base has a surface including glass, and the other of the vibrating plate and the head base has a surface including an electrically conductive material, wherein one of the vibrating plate and head base includes plastic,
  • superposing said head base and vibrating plate one above another,
  • thereafter applying a voltage between said head base and vibrating plate to carry out anodic bonding while being subjected to pressure and heat.
  • 17. An apparatus as defined in claim 16 wherein said apparatus is an ink-jet printer.
  • 18. A method of producing an ink-jet print head by anodic bonding first and second substrates to each other, said method comprising the steps of:
  • providing a first substrate having a conductive material on a first surface so that the first substrate can function as an anode;
  • providing a second substrate having a glass material on a second surface so that the second substrate can function as a cathode, wherein the one of the first and second substrates includes plastic;
  • superposing the first and second substrates one above another so that the first surface faces the second surface; and
  • applying a voltage between said first and second substrates while subjecting the first and second substrates to pressure and heat.
  • 19. The method of claim 18 wherein the step of applying includes subjecting to heat of about 150.degree. C. maximum.
Priority Claims (1)
Number Date Country Kind
3-341681 Dec 1991 JPX
US Referenced Citations (15)
Number Name Date Kind
3397278 Pomerantz Aug 1968
4083710 Hewitt et al. Apr 1978
4158847 Heinzl et al. Jun 1979
4189734 Kyser et al. Jan 1980
4216483 Kyser et al. Aug 1980
4285714 Kirkpatrick Aug 1981
4364070 Matsuda et al. Dec 1982
4420764 Okada Dec 1983
4452624 Wohltjen et al. Jun 1984
4471363 Hanaoka Sep 1984
4520374 Koto May 1985
4525728 Koto Jun 1985
4528575 Matsuda et al. Jul 1985
4546362 Koto Oct 1985
5141148 Ichiyawa Aug 1992
Foreign Referenced Citations (6)
Number Date Country
54-146633 Nov 1979 JPX
62-130857 Jun 1987 JPX
62-265728 Nov 1987 JPX
63-265647 Nov 1988 JPX
2-80252 Mar 1990 JPX
2130528 Jun 1984 GBX
Non-Patent Literature Citations (2)
Entry
Oyo Buturi (Applied Physics) vol. 60 No. 3, 1991.
Room Temperature Anodic Bonding with Low Melting Point Glass Film H. Hebiguchi, et al.: Technical Digest of the 9th Sensor Symposium, 1990. pp. 31-34.