Patent Application
20140072826
Transparent and conductive films (TCF) have been used extensively in recent years in applications such as touch panel displays, liquid crystal displays, electroluminescent lighting, organic light-emitting diode devices, and photovoltaic solar cells. Indium tin oxide (ITO) based transparent conductive film has been the transparent conductor-of-choice for most applications due to its high conductivity, transparency, and relatively good stability. However, indium tin oxide based transparent conductive films have limitations due to the high cost of indium, the need for complicated and expensive vacuum deposition equipment and processes, and indium tin oxide's inherent brittleness and tendency to crack, especially when it is deposited on flexible substrates.
Two of the most important parameters for measuring the properties of transparent conductive films are total light transmittance (% T) and film surface electric conductivity. Higher light transmittance allows clear picture quality for display applications, higher efficiency for lighting and solar energy conversion applications. Lower resistivity is most desirable for most transparent conductive films applications in which power consumption can be minimized. Therefore, the higher the T/R ratio of the transparent conductive films is, the better the transparent conductive films are.
U.S. Patent Application Publication 2006/0257638A1 describes a transparent conductive film comprising carbon nanotubes (CNT) and vinyl chloride resin polymer binder.
U.S. Pat. No. 8,049,333 and U.S. Patent Application Publication 2008/0286447A1 describe a transparent conductive film in which silver nanowires are deposited onto a substrate to form a bare nanowire network followed by overcoating the silver nanowire network with a polymer matrix material to form a transparent conductive film. The polymer materials such as polyacrylates and carboxyl alkyl cellulose ether polymers were suggested as useful materials for the matrix.
US Patent Application Publication 2008/0286447 suggests the use of aromatic triazoles and other nitrogen containing compounds as corrosion inhibitors for silver nanowire based transparent conductors. Long chain alkylthio compounds have also been suggested as useful corrosion inhibitors.
U.S. Patent Application Publication 2008/0292979 describes a transparent conductive film comprising silver nanowires, or a mixture of silver nanowires and carbon nanotubes. The transparent conductive network is formed either without polymer binder or in a photoimageable composition. The transparent and conductive films were coated on both glass and polyethylene terephthalate (PET) supports.
U.S. Patent Application Publication 2009/0130433A1 describes a transparent conductive film which is formed from coating of silver nanowires to form a network followed by overcoating with a layer of urethane acrylate polymer.
U.S. Patent Application Publication 2011/0024159 discloses use of corrosion inhibitors in an overcoat layer of a transparent conductive film.
PCT Patent Publication WO 2011/115603 discloses anticorrosion agents comprising 1,2-diazine compounds for use in transparent conductive films.
Certain 1,2-diazine compounds are particularly useful as anticorrosion agents for the stabilization of a network of silver nanowire-based transparent conductive films toward the undesirable reaction of such conductive films with corrosive agents such as hydrogen sulfide.
We have discovered that the effectiveness of such 1,2-diazine compounds may be enhanced by their introduction in at least one coating mix for at least one layer disposed adjacent to the at least one layer comprising silver nanowires. Such a layer might be an overcoat or topcoat layer, if disposed on the at least one layer comprising silver nanowires. Such an overcoat or topcoat layer may, for example, be thermally cured or UV cured. Alternatively, such a layer might be a primer or undercoat layer, if disposed between the at least one layer comprising silver nanowires and the transparent support. Or the 1,2-diazine compounds might be included in layers both above and below that at least one layer comprising silver nanowires. In any of these cases, the 1,2-diazine compounds may, optionally, also be added to at least one of the layers comprising silver nanowires.
At least a first embodiment provides a transparent conductive article comprising a transparent support; at least one first layer disposed on the transparent support, the at least one first layer comprising a network of silver nanowires dispersed within a polymer binder; and at least one second layer disposed on the at least one second layer, the at least one second layer comprising one or more 1,2-diazine compounds having the general structure (I) or (II):
wherein R1, R2, R3, and R4 are independently: hydrogen, a substituted or unsubstituted alkyl group comprising up to 20 carbon atoms, a substituted or unsubstituted aryl group comprising up to 10 carbon atoms, a substituted or unsubstituted heteroaryl group comprising up to 10 carbon, oxygen, nitrogen, or sulfur atoms, a halogen atom (F, Cl, Br, or I), a hydroxyl group (OH), a thiol group (SH), a substituted or unsubstituted alkoxy group comprising up to 20 carbon atoms, an amino group (NR5R6) where R5 and R6 are independently a hydrogen, an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a thioether group (SR7) where R7 is an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a sulfoxy group (SOR7), a sulfone group (SO2R7), a carboxylic acid group (COOH) or a salt of a carboxylic acid (CO2−M+) where M+ is a cation (such as a metal cation, a quaternary ammonium cation or a quaternary phosphonium cation), a carboxamide group (CONR5R6), an acylamino group (NR5COR7), an acyl group (COR7), an acyloxy group (OCOR7), or a sulfonamido group (SO2NR5R6), or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 1 to 5 carbon, nitrogen, sulfur, and/or oxygen atoms to form an alicylic or aromatic ring(s).
In at least some such embodiments, the at least one first layer may further comprise one or more 1,2-diazine compounds having the general structure (I) or (II), as described above.
At least a second embodiment provides a transparent conductive article comprising a transparent support; at least one first layer disposed on the transparent support, the at least one first layer comprising one or more 1,2-diazine compounds having the general structure (I) or (II):
wherein R1, R2, R3, and R4 are independently: hydrogen, a substituted or unsubstituted alkyl group comprising up to 20 carbon atoms, a substituted or unsubstituted aryl group comprising up to 10 carbon atoms, a substituted or unsubstituted heteroaryl group comprising up to 10 carbon, oxygen, nitrogen, or sulfur atoms, a halogen atom (F, Cl, Br, or I), a hydroxyl group (OH), a thiol group (SH), a substituted or unsubstituted alkoxy group comprising up to 20 carbon atoms, an amino group (NR5R6) where R5 and R6 are independently a hydrogen, an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a thioether group (SR7) where R7 is an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a sulfoxy group (SOR7), a sulfone group (SO2R7), a carboxylic acid group (COOH) or a salt of a carboxylic acid (CO2−M+) where M+ is a cation (such as a metal cation, a quaternary ammonium cation or a quaternary phosphonium cation), a carboxamide group (CONR5R6), an acylamino group (NR5COR7), an acyl group (COR7), an acyloxy group (OCOR7), or a sulfonamido group (SO2NR5R6), or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 1 to 5 carbon, nitrogen, sulfur, and/or oxygen atoms to form an alicylic or aromatic ring(s); and at least one second layer disposed on the at least one first layer, the at least one second layer comprising a network of silver nanowires dispersed within a polymer binder.
In at least some such embodiments, the at least one second layer may further comprise one or more 1,2-diazine compounds having the general structure (I) or (II), as described above.
At least a third embodiment provides a transparent conductive article comprising a transparent support; at least one first layer disposed on the transparent support, the at least one first layer comprising one or more 1,2-diazine compounds having the general structure (I) or (II);
wherein R1, R2, R3, and R4 are independently: hydrogen, a substituted or unsubstituted alkyl group comprising up to 20 carbon atoms, a substituted or unsubstituted aryl group comprising up to 10 carbon atoms, a substituted or unsubstituted heteroaryl group comprising up to 10 carbon, oxygen, nitrogen, or sulfur atoms, a halogen atom (F, Cl, Br, or I), a hydroxyl group (OH), a thiol group (SH), a substituted or unsubstituted alkoxy group comprising up to 20 carbon atoms, an amino group (NR5R6) where R5 and R6 are independently a hydrogen, an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a thioether group (SR7) where R7 is an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a sulfoxy group (SOR7), a sulfone group (SO2R7), a carboxylic acid group (COOH) or a salt of a carboxylic acid (CO2−M+) where M+ is a cation (such as a metal cation, a quaternary ammonium cation or a quaternary phosphonium cation), a carboxamide group (CONR5R6), an acylamino group (NR5COR7), an acyl group (COR7), an acyloxy group (OCOR7), or a sulfonamido group (SO2NR5R6), or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 1 to 5 carbon, nitrogen, sulfur, and/or oxygen atoms to form an alicylic or aromatic ring(s); at least one second layer disposed on the at least one first layer, the at least one second layer comprising a network of silver nanowires dispersed within a polymer binder; at least one third layer disposed on the at least one second layer, the at least one third layer comprising one or more 1,2-diazine compounds having the general structure (I) or (II), as described above.
In at least some such embodiments, the at least one second layer may further comprise one or more 1,2-diazine compounds having the general structure (I) or (II), as described above.
At least a fourth embodiment provides methods comprising applying at least one first coating mixture onto a transparent support to form at least one first coated layer, the at least one first coating mixture comprising silver nanowires and at least one polymer binder; and applying at least one second coating mixture onto the at least one first coated layer to form at least one second coated layer, the at least one second coating mixture comprising one or more 1,2-diazine compounds having the general structure (I) or (II):
wherein R1, R2, R3, and R4 are independently: hydrogen, a substituted or unsubstituted alkyl group comprising up to 20 carbon atoms, a substituted or unsubstituted aryl group comprising up to 10 carbon atoms, a substituted or unsubstituted heteroaryl group comprising up to 10 carbon, oxygen, nitrogen, or sulfur atoms, a halogen atom (F, Cl, Br, or I), a hydroxyl group (OH), a thiol group (SH), a substituted or unsubstituted alkoxy group comprising up to 20 carbon atoms, an amino group (NR5R6) where R5 and R6 are independently a hydrogen, an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a thioether group (SR7) where R7 is an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a sulfoxy group (SOR7), a sulfone group (SO2R7), a carboxylic acid group (COOH) or a salt of a carboxylic acid (CO2−M+) where M+ is a cation (such as a metal cation, a quaternary ammonium cation or a quaternary phosphonium cation), a carboxamide group (CONR5R6), an acylamino group (NR5COR7), an acyl group (COR7), an acyloxy group (OCOR7), or a sulfonamido group (SO2NR5R6), or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 1 to 5 carbon, nitrogen, sulfur, and/or oxygen atoms to form an alicylic or aromatic ring(s).
In at least some such embodiments, the at least one first coating mixture may further comprise one or more 1,2-diazine compounds having the general structure (I) or (II), as described above.
At least a fifth embodiment provides methods comprising applying at least one first coating mixture onto a transparent support to form at least one first coated layer, the at least one first coating mixture comprising one or more 1,2-diazine compounds having the general structure (I) or (II):
wherein R1, R2, R3, and R4 are independently: hydrogen, a substituted or unsubstituted alkyl group comprising up to 20 carbon atoms, a substituted or unsubstituted aryl group comprising up to 10 carbon atoms, a substituted or unsubstituted heteroaryl group comprising up to 10 carbon, oxygen, nitrogen, or sulfur atoms, a halogen atom (F, Cl, Br, or I), a hydroxyl group (OH), a thiol group (SH), a substituted or unsubstituted alkoxy group comprising up to 20 carbon atoms, an amino group (NR5R6) where R5 and R6 are independently a hydrogen, an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a thioether group (SR7) where R7 is an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a sulfoxy group (SOR7), a sulfone group (SO2R7), a carboxylic acid group (COOH) or a salt of a carboxylic acid (CO2−M+) where M+ is a cation (such as a metal cation, a quaternary ammonium cation or a quaternary phosphonium cation), a carboxamide group (CONR5R6), an acylamino group (NR5COR7), an acyl group (COR7), an acyloxy group (OCOR7), or a sulfonamido group (SO2NR5R6), or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 1 to 5 carbon, nitrogen, sulfur, and/or oxygen atoms to form an alicylic or aromatic ring(s); and applying at least one second coating mixture onto the at least one first coated layer, the at least one second coating mixture comprising silver nanowires and at least one polymer binder.
In at least some such embodiments, the at least one second coating mixture may further comprise one or more 1,2-diazine compounds having the general structure (I) or (II), as described above.
These embodiments and other variations and modifications may be better understood from the description, exemplary embodiments, examples, and claims that follow. Other desirable objectives and advantages inherently achieved may occur or become apparent to those skilled in the art. The invention is defined by the appended claims.
All publications, patents, and patent documents referred to in this document are incorporated by reference in their entirety, as though individually incorporated by reference.
U.S. Provisional Patent Application No. 61/700,366, filed Sep. 13, 2012, entitled “ANTICORROSION AGENTS FOR TRANSPARENT CONDUCTIVE FILM,” is hereby incorporated by reference in its entirety.
The terms “conductive layer” or “conductive film” refer to the network layer comprising silver nanowires dispersed within a polymer binder.
The term “conductive” refers to electrical conductivity.
The term “article” refers to the coating of a “conductive layer” or “conductive film” on a support.
The terms “coating weight,” “coat weight,” and “coverage” are synonymous, and are usually expressed in weight or moles per unit area such as g/m2 or mol/m2.
The term “transparent” means capable of transmitting visible light without appreciable scattering or absorption.
“Haze” is wide-angle scattering that diffuses light uniformly in all directions. It is the percentage of transmitted light that deviates from the incident beam by more than 2.5 degrees on the average. Haze reduces contrast and results in a milky or cloudy appearance. Materials having lower haze percentages appear less hazy than those having higher haze percentages.
The term “organic solvent” means “a material, liquid at use temperature, whose chemical formula comprises one or more carbon atoms.”
The term “aqueous solvent” means a material, liquid at use temperature, whose composition in a homogeneous solution comprises water in the greatest proportion (i.e., at least 50 percent water by weight).
The term “water soluble” means the solute forms a homogenous solution with water, or a solvent mixture in which water is the major component.
The terms “a” or “an” refer to “at least one” of that component (for example, the anticorrosion agents, nanowires, and polymers described herein).
Furthermore, all publications, patents, and patent documents referred to in this document are incorporated by reference herein in their entirety, as though individually incorporated by reference.
In order for silver based transparent conductors to have practical use it is important that these silver based transparent conductors be stable for a long period when subjected to environmental conditions.
Any atmospheric corrosion due to the reaction of low levels of chemicals in the air will induce undesirable chemical reactions at the metal nanowire surface, impacting the conductivity and performance of the metal nanowire based transparent conductors. It is well known that corrosion, or “tarnishing,” may readily occur on silver metal surfaces when exposed to the atmosphere. Without wishing to be bound by theory, one example of such a tarnishing mechanism is sulfidation of silver surface by reaction of hydrogen sulfide with silver:
2Ag+H2S→Ag2S+H2
Because the electric conductivity of silver compounds such as silver sulfide is much lower than that of silver metal, silver nanowire based conductors can gradually lose conductivity when exposed to the atmosphere.
In contrast to bare metal wires exposed to the air, silver nanowires in a polymer matrix are more stable since the presence of the polymer slows down the diffusion of hydrogen sulfide (or other corrosive agents) to the silver nanowire surface. Nevertheless, it is important to stabilize the silver nanowire surface to prevent the sulfidation process, even when the nanowires are embedded in a polymer matrix.
It would be useful to find anticorrosion agents for transparent electrically conductive films comprising a network of silver nanowires in polymer binder(s) that can be coated from aqueous or from organic solvents, using common coating techniques
The silver nanowires are an essential component for imparting electrical conductivity to the conductive films, and to the articles prepared using the conductive films. The electrical conductivity of the transparent conductive film is mainly controlled by a) the conductivity of a single nanowire, b) the number of nanowires between the terminals, and c) the connectivity between the nanowires. Below a certain nanowire concentration (also referred as the percolation threshold), the conductivity between the terminals is zero, as there is no continuous current path provided because the nanowires are spaced too far apart. Above this concentration, there is at least one current path available. As more current paths are provided, the overall resistance of the layer will decrease. However, as more current paths are provided, the clarity (i.e., percent light transmission) of the conductive film decreases due to light absorption and back scattering by the nanowires. Also, as the amount of silver nanowires in the conductive film increases, the haze of the transparent film increases due to light scattering by the silver nanowires. Similar effects will occur in transparent articles prepared using the conductive films.
In one embodiment, the silver nanowires have aspect ratio (length/width) of from about 20 to about 3300. In another embodiment, the silver nanowires have an aspect ratio (length/width) of from about 500 to 1000. Silver nanowires having a length of from about 5 μm to about 100 μm (micrometer) and a width of from about 10 nm to about 200 nm are useful. Silver nanowires having a width of from about 20 nm to about 100 nm and a length of from about 10 μm to about 50 μm are also particularly useful for construction of a transparent conductive network film.
Silver nanowires can be prepared by known methods in the art. In particular, silver nanowires can be synthesized through solution-phase reduction of a silver salt (e.g., silver nitrate) in the presence of a polyol (e.g., ethylene glycol or propylene glycol) and poly(vinyl pyrrolidone). Large-scale production of silver nanowires of uniform size can be prepared according to the methods described in, e.g., Ducamp-Sanguesa, C. et al, J. of Solid State Chemistry, (1992), 100, 272-280; Sun, Y. et al., Chem. Mater (2002), 14, 4736-4745, Sun, Y. et al., Nano Letters, (2003), 3(7), 955-960; US patent application publication 2012/0063948, published Mar. 15, 2012; US patent application publication 2012/0126181, published May 24, 2012; US patent application publication 2012/0148436, published Jun. 14, 2012; US patent application publication 2012/0207644, published Aug. 16, 2012; and U.S. patent application Ser. No. 13/439,983, filed Apr. 5, 2012, entitled “NANOWIRE PREPARATION METHODS, COMPOSITIONS, AND ARTICLES,” each of which is incorporated by reference in its entirety.
For a practical manufacturing process for transparent conductive films, it is important to have both the conductive components, such as silver nanowires, and a polymer binder in a coating solution. The polymer binder solution serves a dual role, as dispersant to facilitate the dispersion of silver nanowires and as a viscosifier to stabilize the silver nanowire coating dispersion so that the sedimentation of silver nanowires does not occur at any point during the coating process. It is also desirable to have the silver nanowires and the polymer binder in a single coating dispersion. This simplifies the coating process and allows for a one-pass coating, and avoids the method of first coating bare silver nanowires to form a weak and fragile film that is subsequently over-coated with a polymer to form the transparent conductive film.
In order for a transparent conductive film to be useful in various device applications, it is also important for the polymer binder of the transparent conductive film to be optically transparent and flexible, yet have high mechanical strength, good hardness, high thermal stability and light stability. This requires polymer binders to be used for transparent conductive film to have Tg (glass transition temperature) greater than the use temperature of the transparent conductive film.
Transparent, optically clear polymer binders are known in the art. Examples of suitable polymeric binders include, but are not limited to: polyacrylics such as polymethacrylates (e.g., poly(methyl methacrylate)), polyacrylates and polyacrylonitriles, polyvinyl alcohols, polyesters (e.g., polyethylene terephthalate (PET), polybutylene terephthalate, and polyethylene naphthalate), polymers with a high degree of aromaticity such as phenolics or cresol-formaldehyde (Novolacs®), polystyrenes, polyvinyltoluene, polyvinylxylene, polyimides, polyamides, polyamideimides, polyetheramides, polysulfides, polysulfones, polyphenylenes, and polyphenyl ethers, polyurethane (PU), polycarbonates, epoxy, polyolefins (e.g. polypropylene, polymethylpentene, and cyclic olefins), acrylonitrile-butadiene-styrene copolymer (ABS), cellulosics, silicones and other silicon-containing polymers (e.g. polysilsesquioxanes and polysilanes), polyvinylchloride (PVC), polyvinylacetates, polynorbornenes, synthetic rubbers (e.g. EPR, SBR, EPDM), and fluoropolymers (e.g., polyvinylidene fluoride, polytetrafluoroethylene (TFE) or polyhexafluoropropylene), copolymers of fluoro-olefin and hydrocarbon olefin (e.g., Lumiflon®), and amorphous fluorocarbon polymers or copolymers (e.g., CYTOP® by Asahi Glass Co., or Teflon® AF by Du Pont), polyvinylbutryals, polyvinylacetals, gelatins, polysaccharides, and starches.
In certain embodiments, in order to disperse and stabilize silver nanowires in polymeric coating solution, the use of polymer binders having high oxygen content is advantageous. Oxygen-containing groups, such as hydroxyl group and carboxylate groups have a strong affinity for binding to the silver nanowire surface and facilitate the dispersion and stabilization. Many oxygen-rich polymers also have good solubility in the polar organic solvents commonly used to prepare organic solvent-coated materials, while other oxygen-rich polymers have good solubility in water or the aqueous solvent mixtures commonly used to prepare aqueous solvent-coated materials.
In certain embodiments, cellulose ester polymers, such as cellulose acetate butyrate (CAB), cellulose acetate (CA), or cellulose acetate propionate (CAP) are superior to other oxygen-rich polymer binders when used to prepare silver nanowire based transparent conductive films that are coated from organic solvents such as 2-butanone (methyl ethyl ketone, MEK), methyl iso-butyl ketone, acetone, methanol, ethanol, 2-propanol, ethyl acetate, propyl acetate, butyl acetate, or mixtures thereof. Their use results in transparent conductive films in which both the optical light transmittance and electrical conductivity of the coated films are greatly improved. In addition, these cellulose ester polymers have glass transition temperatures of at least 100° C. and provide transparent, flexible films having high mechanical strength, good hardness, high thermal stability, and light stability.
The cellulose ester polymers can be present in from about 40 to about 90 wt % of the dried transparent conductive films. Preferably, they are present in from about 60 to about 85 wt % of the dried films. In some constructions, a mixture of a cellulosic ester polymer and one or more additional polymers may be used. These polymers should be compatible with the cellulosic polymer. By compatible is meant that a mixture comprising at least one cellulosic ester polymer and one or more additional polymers forms a transparent, single phase composition when dried. The additional polymer or polymers can provide further benefits such as promoting adhesion to the support and improving hardness and scratch resistance. As above, total wt % of all polymers is from about 40 to about 95 wt % of the dried transparent conductive films. Preferably, the total weight of all polymers is from about 60 to about 85 wt % of the dried films. Polyester polymers, urethanes, and polyacrylics are examples of additional polymers useful for blending with cellulosic ester polymers.
In other embodiments, water soluble polymer binders can also be used, such as polyvinyl alcohol, gelatin, polyacrylic acid, polyimides. Other water dispersible latex polymers can also be used such as polyacrylates and polymethacrylates containing methyl acrylic acid units. Coating from aqueous solutions benefits the environment and reduces the emission of volatile organic compounds during manufacturing.
The use of water soluble polymers, such as polyvinyl alcohol or gelatin as binders for silver nanowire based transparent conductors results in superior transparent conductive films in which both film transmittance and conductivity are greatly improved. Transparent conductive films prepared using either polyvinyl alcohol or gelatin polymer binders also show excellent clarity, scratch resistance, and hardness when polymer cross linkers are added to the polymer solution. Transparent conductive films prepared according to this invention provide transmittance of at least 80% across entire spectrum range of about 350 nm to about 1100 nm, and surface resistivity of 500 ohm/sq or less.
The transparent conductive articles comprising silver nanowires and water soluble polymer binders also show excellent clarity, high scratch resistance and hardness. In addition, transparent conductive films prepared using these polymer binders have good adhesion to supports comprising polyethylene terephthalate (PET), poly(methylmethacrylate), polycarbonate, and the like, when an appropriate subbing layer is applied between the support and the conductive layer.
The water soluble polymer binders are present in from about 40 to about 95 wt % of the dried transparent conductive films. Preferably, they are present in from about 60 to about 85 wt % of the dried films.
In some constructions, up to 50 wt % of the gelatin or polyvinyl alcohol polymer binder can be replaced by one or more additional polymers. These polymers should be compatible with the gelatin or polyvinyl alcohol polymer binder. By compatible is meant that the all polymers form a transparent, single phase mixture when dried. The additional polymer or polymers can provide further benefits such as promoting adhesion to the support and improving hardness and scratch resistance. Water soluble acrylic polymers are particularly preferred as additional polymers. Examples of such polymers are polyacrylic acid and polyacrylamides, and copolymers thereof. As above, total wt % of all polymers is from about 50 to about 95 wt % of the dried transparent conductive films. Preferably, the total weight of all polymers is from about 70 to about 85 wt % of the dried films.
If desired, scratch resistance and hardness of the transparent conductive films with these polymer binders to the support can be improved by use of crosslinking agents to crosslink the polymer binders. Isocyanate silanes are examples of typical crosslinking agents for cellulose ester polymers containing free hydroxyl groups. Vinyl sulfones and aldehydes are examples of typical crosslinking agents for gelatin binders.
Anticorrosion agents are chemical compounds that, when added to the transparent conductive film, improve the stability of the construction with respect to atmospheric corrosion caused by the reaction of oxygen or one or more other chemicals in the atmosphere with one or more components in the film. This reaction results in deterioration of the electric conductivity, optical properties, and/or physical integrity of the film. Anticorrosion agents should be colorless and odorless when used in the transparent conductive film, and should be stable to the conditions of heat, light, and humidity in the environment where transparent conductive film is used.
For a silver nanowire based conductive film, chemical compounds with functional group containing N, O, or S are potentially useful anticorrosion agents due to coordinating ability of these functional groups to the silver nanowire surfaces. Coordination is thought to complex with these compounds and passivate the silver surface to prevent the reaction of atmosphere gases with the silver surface. However, in practice, many such compounds, when bound to a silver nanowire surface, will drastically reduce the electric conductivity of the resultant conductive film. Apparently, the insulating effect of these compounds prevents electron “flow” at nanowire contact points. Therefore, it is important to identify a class of compounds that will provide anticorrosion protection to transparent conductive film without causing significant reduction in conductivity and other negative effects. Advantageously, delaying introduction of the anticorrosion agents into the conductive nanowire network until after its formation can minimize the destruction of conductive paths in the network.
We have found that 1,2-diazine compounds provide anticorrosion properties when incorporated into silver nanowire containing films. The 1,2-diazine compounds have the general structure (I) or (II).
wherein R1, R2, R3, and R4 are independently: hydrogen, a substituted or unsubstituted alkyl group comprising up to 20 carbon atoms, a substituted or unsubstituted aryl group comprising up to 10 carbon atoms, a substituted or unsubstituted heteroaryl group comprising up to 10 carbon, oxygen, nitrogen, or sulfur atoms, a halogen atom (F, Cl, Br, or I), a hydroxyl group (OH), a thiol group (SH), a substituted or unsubstituted alkoxy group comprising up to 20 carbon atoms, an amino group (NR5R6) where R5 and R6 are independently a hydrogen, an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a thioether group (SR7) where R7 is an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a sulfoxy group (SOR7), a sulfone group (SO2R7), a carboxylic acid group (COOH) or a salt of a carboxylic acid (CO2−M+) where M+ is a cation (metal ion or quaternary ammonium or quaternary phosphonium ion), a carboxamide group (CONR5R6), an acylamino group (NR5COR7), an acyl group (COR7), an acyloxy group (OCOR7), or a sulfonamido group (SO2NR5R6), or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 1 to 5 carbon, nitrogen, sulfur, and/or oxygen atoms to form an alicylic or aromatic ring(s).
In another embodiment, R1, R2, R3, and R4 are hydrogen, halogen, hydroxyl, alkyl groups comprising 1 to 6 carbon atoms, aryl groups comprising 6 carbon atoms, alkoxy groups comprising 1 to 6 carbon atoms, or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 4 carbon atoms to form a fused benzo ring.
In another embodiment, R1, R2, R3, and R4 are hydrogen, chloro, bromo, hydroxyl, alkyl groups comprising 1 to 4 carbon atoms, aryl groups comprising 6 carbon atoms, alkoxy groups comprising 1 to 4 carbon atoms, or (R2 and R3) are joined together with 4 carbon atoms to form a fused benzo ring.
Nonlimiting examples of 1,2-diazine compounds having structures (I) and (II) include:
An organic solvent-based coating formulation for the transparent silver nanowire films can be prepared by mixing the various components with one or more polymer binders in a suitable organic solvent system that usually includes one or more solvents such as toluene, 2-butanone (methyl ethyl ketone, MEK), methyl iso-butyl ketone, acetone, methanol, ethanol, 2-propanol, ethyl acetate, propyl acetate, butyl acetate, ethyl lactate, tetrahydrofuran, or mixtures thereof. An aqueous-based coating formulation for the transparent silver nanowire films can be prepared by mixing the various components with one or more polymer binders in water or in a mixture of water with a water miscible solvent such as acetone, acetonitrile, methanol, ethanol, 2-propanol, or tetrahydrofuran, or mixtures thereof. Transparent films containing silver nanowires can be prepared by coating the formulations using various coating procedures such as wire wound rod coating, dip coating, knife or blade coating, curtain coating, slide coating, slot-die coating, roll coating, or gravure coating. Surfactants and other coating aids can be incorporated into the coating formulation.
In one embodiment the coating weight of the silver nanowires is from about 10 mg/m2 to about 500 mg/m2. In another embodiment the coating weight of silver nanowires is from about 20 mg/m2 to about 200 mg/m2. In a further embodiment, the coating weight of silver nanowires is from about 30 mg/m2 to about 120 mg/m2. A useful coating dry thickness of the transparent conductive coating is from about 0.05 μm to about 2.0 μm, and preferably from about 0.1 μm to about 0.5 μm.
Upon coating and drying, the transparent conductive film should have a surface resistivity of less than 1,000 ohms/sq and preferably less than 500 ohm/sq.
Upon coating, and drying, the transparent conductive film should have as high a % transmittance as possible. A transmittance of at least 70% is useful. A transmittance of at least 80% and even at least 90% are even more useful.
Particularly useful are films with a transmittance of at least 70% and a surface resistivity of less than 500 ohm/sq.
Such transparent conductive films provide transmittance of at least 80% across entire spectrum range of from about 350 nm to about 1100 nm, and surface resistivity of less than 500 ohm/sq.
In one embodiment, the conductive materials are coated onto a support. The support may be rigid or flexible.
Suitable rigid substrates include, for example, glass, polycarbonates, acrylics, and the like.
When the conductive materials are coated onto a flexible support, the support is preferably a flexible, transparent polymeric film that has any desired thickness and is composed of one or more polymeric materials. The support is required to exhibit dimensional stability during coating and drying of the conductive layer and to have suitable adhesive properties with overlying layers. Useful polymeric materials for making such supports include polyesters [such as poly(ethylene terephthalate) (PET) and poly(ethylene naphthalate) (PEN)], cellulose acetates and other cellulose esters, polyvinyl acetal, polyolefins, polycarbonates, and polystyrenes. Preferred supports are composed of polymers having good heat stability, such as polyesters and polycarbonates. Support materials may also be treated or annealed to reduce shrinkage and promote dimensional stability. Transparent multilayer supports can also be used.
Coating of the Conductive Films onto a Support
Transparent conductive articles can be prepared by coating the formulations described above onto a transparent support using various coating procedures such as wire wound rod coating, dip coating, knife coating, curtain coating, slide coating, slot-die coating, roll coating, gravure coating, or extrusion coating.
Alternatively, transparent conductive articles can be prepared by laminating the transparent conductive films prepared as described above onto a transparent support.
In some embodiments, a “carrier” layer formulation comprising a single-phase mixture of two or more polymers may be applied directly onto the support and thereby located between the support and the silver nanowire layer. The carrier layer serves to promote adhesion of the support to the transparent polymer layer containing the silver nanowires. The carrier layer formulation can be sequentially or simultaneously applied with application of the transparent conductive silver nanowire layer formulation. It is preferred that all coating be applied simultaneously onto the support. Carrier layers are often referred to as “adhesion promoting layers,” “interlayers,” or “intermediate layers.”
As noted above, in one embodiment the coating weight of the silver nanowires is from about 20 mg/m2 to about 500 mg/m2. In other embodiments, coating weight of silver nanowires is from about 10 mg/m2 to about 200 mg/m2. Embodiments wherein the silver nanowires are coated at from about 10 mg/m2 to about 120 mg/m2 are also contemplated.
Upon coating and drying, the transparent conductive article should have a surface resistivity of less than 1,000 ohms/sq and preferably less than 500 ohm/sq.
Similarly, upon coating and drying on a transparent support, the transparent conductive article should have as high an optical transmittance as possible. A transmittance of at least 70% is useful. A transmittance of at least 80% and even at least 90% are even more useful.
Particularly preferred are articles with a transmittance of at least 80% and a surface resistivity of less than 500 ohm/sq.
The following examples are provided to illustrate the practice of the present invention and the invention is not meant to be limited thereby.
The following are 42 non-limiting exemplary embodiments:
A. A transparent conductive article comprising:
a transparent support;
at least one first layer disposed on the transparent support, the at least one first layer comprising a network of silver nanowires dispersed within at least one polymer binder; and
at least one second layer disposed on the at least one first layer, the at least one second layer comprising one or more 1,2-diazine compounds having the general structure (I) or (II);
wherein R1, R2, R3, and R4 are independently: hydrogen, a substituted or unsubstituted alkyl group comprising up to 20 carbon atoms, a substituted or unsubstituted aryl group comprising up to 10 carbon atoms, a substituted or unsubstituted heteroaryl group comprising up to 10 carbon, oxygen, nitrogen, or sulfur atoms, a halogen atom (F, Cl, Br, or I), a hydroxyl group (OH), a thiol group (SH), a substituted or unsubstituted alkoxy group comprising up to 20 carbon atoms, an amino group (NR5R6) where R5 and R6 are independently a hydrogen, an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a thioether group (SR7) where R7 is an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a sulfoxy group (SOR7), a sulfone group (SO2R7), a carboxylic acid group (COOH) or a salt of a carboxylic acid (CO2−M+) where M+ is a cation (such as a metal cation, a quaternary ammonium cation or a quaternary phosphonium cation), a carboxamide group (CONR5R6), an acylamino group (NR5COR7), an acyl group (COR7), an acyloxy group (OCOR7), or a sulfonamido group (SO2NR5R6),
or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 1 to 5 carbon, nitrogen, sulfur, and/or oxygen atoms to form an alicylic or aromatic ring(s).
B. The transparent conductive article of embodiment A, wherein the transparent support is a flexible transparent polymer film.
C. The transparent conductive article of embodiment A, wherein the silver nanowires are present in an amount sufficient to provide a surface resistivity of less than 1000 ohm/sq.
D. The transparent conductive article of embodiment A, wherein the silver nanowires have an aspect ratio of from about 20 to about 3300.
E. The transparent conductive article of embodiment A, wherein the silver nanowires are present in an amount of from about 10 mg/m2 to about 500 mg/m2.
F. The transparent conductive article of embodiment A, having a transmittance of at least 80% across entire spectrum range of from about 350 nm to about 1100 nm and a surface resistivity of 500 ohm/sq or less.
G. The transparent conductive article of embodiment A, wherein the at least one polymer binder comprises at least one water soluble polymer.
H. The transparent conductive article of embodiment G, wherein the at least one water soluble polymer comprises gelatin, polyvinyl alcohol, or mixtures thereof.
J. The transparent conductive article of embodiment H, wherein the at least one polymer binder further comprises up to 50 wt % of one or more additional water soluble polymers.
K. The transparent conductive article of embodiment J, wherein one or more of the additional water soluble polymers is a polyacrylic polymer.
L. The transparent conductive article of embodiment A, wherein the at least one polymer binder comprises an organic solvent soluble polymer.
M. The transparent conductive article of embodiment L, wherein the organic solvent soluble polymer binder comprises at least one cellulose ester polymer.
N. The transparent conductive article of embodiment L, wherein the organic solvent soluble polymer binder comprises cellulose acetate, cellulose acetate butyrate, or cellulose acetate propionate, or mixtures thereof.
P. The transparent conductive article of embodiment M, wherein the at least one cellulose ester polymer has a glass transition temperature of at least 100° C.
Q. The transparent conductive article of embodiment L, wherein the at least one polymer binder further comprises up to 50 wt % of one or more additional organic solvent soluble polymers.
R. The transparent conductive article of embodiment Q, wherein the one or more of the additional organic solvent soluble polymers is a polyester polymer.
S. The transparent conductive article of embodiment A, wherein
R1, R2, R3, and R4 are hydrogen, halogen, hydroxyl, alkyl groups comprising 1 to 6 carbon atoms, aryl groups comprising 6 carbon atoms, alkoxy groups comprising 1 to 6 carbon atoms,
or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 4 carbon atoms to form a fused benzo ring.
T. The transparent conductive article of embodiment A, wherein the 1,2-diazine compounds are represented by one or more of the structures:
U. A transparent conductive article comprising:
a transparent support;
at least one first layer disposed on the transparent support, the at least one first layer comprising one or more 1,2-diazine compounds having the general structure (I) or (II);
wherein R1, R2, R3, and R4 are independently: hydrogen, a substituted or unsubstituted alkyl group comprising up to 20 carbon atoms, a substituted or unsubstituted aryl group comprising up to 10 carbon atoms, a substituted or unsubstituted heteroaryl group comprising up to 10 carbon, oxygen, nitrogen, or sulfur atoms, a halogen atom (F, Cl, Br, or I), a hydroxyl group (OH), a thiol group (SH), a substituted or unsubstituted alkoxy group comprising up to 20 carbon atoms, an amino group (NR5R6) where R5 and R6 are independently a hydrogen, an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a thioether group (SR7) where R7 is an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a sulfoxy group (SOR7), a sulfone group (SO2R7), a carboxylic acid group (COOH) or a salt of a carboxylic acid (CO2−M+) where M+ is a cation (such as a metal cation, a quaternary ammonium cation or a quaternary phosphonium cation), a carboxamide group (CONR5R6), an acylamino group (NR5COR7), an acyl group (COR7), an acyloxy group (OCOR7), or a sulfonamido group (SO2NR5R6),
or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 1 to 5 carbon, nitrogen, sulfur, and/or oxygen atoms to form an alicylic or aromatic ring(s); and
at least one second layer disposed on the at least one first layer, the at least one second layer comprising a network of silver nanowires dispersed within at least one polymer binder.
V. The transparent conductive article of embodiment U, wherein the transparent support is a flexible transparent polymer film.
W. The transparent conductive article of embodiment U, wherein the silver nanowires are present in an amount sufficient to provide a surface resistivity of less than 1000 ohm/sq.
X. The transparent conductive article of embodiment U, wherein the silver nanowires have an aspect ratio of from about 20 to about 3300.
Y. The transparent conductive article of embodiment U, wherein the silver nanowires are present in an amount of from about 20 mg/m2 to about 500 mg/m2.
Z. The transparent conductive article of embodiment U, having a transmittance of at least 70% across entire spectrum range of from about 350 nm to about 1100 nm and a surface resistivity of 500 ohm/sq or less.
AA. The transparent conductive article of embodiment U, wherein the at least one polymer binder comprises at least one water soluble polymer.
AB. The transparent conductive article of embodiment AA, wherein the at least one water soluble polymer comprises gelatin, polyvinyl alcohol, or mixtures thereof.
AC. The transparent conductive article of embodiment AB, wherein the at least one polymer binder further comprises up to 50 wt % of one or more additional water soluble polymers.
AD. The transparent conductive article of embodiment AC, wherein one or more of the additional water soluble polymers is a polyacrylic polymer.
AE. The transparent conductive article of embodiment U, wherein the at least one polymer binder comprises an organic solvent soluble polymer.
AF. The transparent conductive article of embodiment 29, wherein the organic solvent soluble polymer binder comprises at least one cellulose ester polymer.
Ag. The transparent conductive article of embodiment AE, wherein the organic solvent soluble polymer binder comprises cellulose acetate, cellulose acetate butyrate, or cellulose acetate propionate, or mixtures thereof.
AH. The transparent conductive article of embodiment AF, wherein the at least one cellulose ester polymer has a glass transition temperature of at least 100° C.
AJ. The transparent conductive article of embodiment AE, wherein the at least one polymer binder further comprises up to 50 wt % of one or more additional organic solvent soluble polymers.
AK. The transparent conductive article of embodiment AJ, wherein the one or more of the additional organic solvent soluble polymers is a polyester polymer.
AL. The transparent conductive article of embodiment U, wherein
R1, R2, R3, and R4 are hydrogen, halogen, hydroxyl, alkyl groups comprising 1 to 6 carbon atoms, aryl groups comprising 6 carbon atoms, alkoxy groups comprising 1 to 6 carbon atoms,
or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 4 carbon atoms to form a fused benzo ring.
AM. The transparent conductive article of embodiment U, wherein the 1,2-diazine compounds are represented by one or more of the structures:
AN. A method comprising:
applying at least one first coating mixture onto a transparent support to form at least one first coated layer, the at least one first coating mixture comprising silver nanowires and at least one polymer binder; and
applying at least one second coating mixture onto the at least one first coated layer to form at least one second coated layer, the at least one second coating mixture comprising one or more 1,2-diazine compounds having the general structure (I) or (II):
wherein R1, R2, R3, and R4 are independently: hydrogen, a substituted or unsubstituted alkyl group comprising up to 20 carbon atoms, a substituted or unsubstituted aryl group comprising up to 10 carbon atoms, a substituted or unsubstituted heteroaryl group comprising up to 10 carbon, oxygen, nitrogen, or sulfur atoms, a halogen atom (F, Cl, Br, or I), a hydroxyl group (OH), a thiol group (SH), a substituted or unsubstituted alkoxy group comprising up to 20 carbon atoms, an amino group (NR5R6) where R5 and R6 are independently a hydrogen, an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a thioether group (SR7) where R7 is an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a sulfoxy group (SOR7), a sulfone group (SO2R7), a carboxylic acid group (COOH) or a salt of a carboxylic acid (CO2−M+) where M+ is a cation (such as a metal cation, a quaternary ammonium cation or a quaternary phosphonium cation), a carboxamide group (CONR5R6), an acylamino group (NR5COR7), an acyl group (COR7), an acyloxy group (OCOR7), or a sulfonamido group (SO2NR5R6),
or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 1 to 5 carbon, nitrogen, sulfur, and/or oxygen atoms to form an alicylic or aromatic ring(s).
AP. The method according to embodiment AN, wherein the applying the at least one first coating mixture and the applying the at least one second coating mixture occur simultaneously.
AQ. The method according to embodiment AN, further comprising drying the at least one first layer or the at least one second layer or both.
AR. A method comprising:
applying at least one first coating mixture onto a transparent support to form at least one first coated layer, the at least one first coating mixture comprising one or more 1,2-diazine compounds having the general structure (I) or (II):
wherein R1, R2, R3, and R4 are independently: hydrogen, a substituted or unsubstituted alkyl group comprising up to 20 carbon atoms, a substituted or unsubstituted aryl group comprising up to 10 carbon atoms, a substituted or unsubstituted heteroaryl group comprising up to 10 carbon, oxygen, nitrogen, or sulfur atoms, a halogen atom (F, Cl, Br, or I), a hydroxyl group (OH), a thiol group (SH), a substituted or unsubstituted alkoxy group comprising up to 20 carbon atoms, an amino group (NR5R6) where R5 and R6 are independently a hydrogen, an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a thioether group (SR7) where R7 is an alkyl group comprising up to 20 carbon atoms, or an aryl group comprising up to 10 carbon atoms, a sulfoxy group (SOR7), a sulfone group (SO2R7), a carboxylic acid group (COOH) or a salt of a carboxylic acid (CO2−M+) where M+ is a cation (such as a metal cation, a quaternary ammonium cation or a quaternary phosphonium cation), a carboxamide group (CONR5R6), an acylamino group (NR5COR7), an acyl group (COR7), an acyloxy group (OCOR7), or a sulfonamido group (SO2NR5R6),
or (R1 and R2) or (R2 and R3) or (R3 and R4) are joined together with 1 to 5 carbon, nitrogen, sulfur, and/or oxygen atoms to form an alicylic or aromatic ring(s); and
applying at least one second coating mixture onto the at least one first coated layer, the at least one second coating mixture comprising silver nanowires and at least one polymer binder.
AS. The method according to embodiment AR, wherein the applying the at least one first coating mixture and the applying the at least one second coating mixture occur simultaneously.
AT. The method according to embodiment AR, further comprising drying the at least one first layer or the at least one second layer or both.
All materials used in the following examples are readily available from standard commercial sources, such as Aldrich Chemical Co. (Milwaukee, Wis.) unless otherwise specified. All percentages are by weight unless otherwise indicated. The following additional methods and materials were used.
BHTT is 4-Benzyl-1,2,4-triazole-3-thiol. Its structure is shown below.
Bismuth neodecanoate is the bismuth salt of neodecanoic acid.
BuPHZ is 6-iso-Butylphthalazine (Structure I-4).
BZT is benzotriazole. Its structure is shown below.
CAB 171-15 is a cellulose acetate butyrate resin available from Eastman Chemical Co. (Kingsport, Tenn.). It has a glass transition temperature of 161° C.
CAB 381-20 is a cellulose acetate butyrate resin available from Eastman Chemical Co. (Kingsport, Tenn.). It has a glass transition temperature of 141° C.
CAB 553-0.4 is a cellulose acetate butyrate resin available from Eastman Chemical Co. (Kingsport, Tenn.). It has a glass transition temperature of 136° C.
ClPHZ is 1,4-Dichlorophthalazine (Structure I-3).
Mayer Bars are ½ inch diameter Type 303 stainless steel coating rods and are available from R.D. Specialties, Inc. (Webster, N.Y.).
MEK is methyl ethyl ketone (or 2-butanone).
MMBI is 2-mercapto-4(5)-methylbenzimidazole. Its structure is shown below.
4-MPA is 4-Methylphthalic acid. Its structure is shown below.
PAZ is Phthalazone (Structure II-3).
PHZ is Phthalazine (Structure I-1).
PMT is 1-Phenyl-1H-tetrazole-5-thiol (phenyl-mercapto-tetrazole). Its structure is shown below.
PYZ is Pyridazine (Structure I-2).
Silver nanowires were prepared according to two procedures. For Example 1, a procedure similar to Example 13 of U.S. patent application Ser. No. 13/439,983, filed Apr. 5, 2012, entitled “NANOWIRE PREPARATION METHODS, COMPOSITIONS, AND ARTICLES” was followed, using a reaction temperature of 160° C. for 45 min. Silver nanowires so prepared exhibited an average diameter of 54±29 nm, and an average length of 18±14 μm. For Example 2, silver nanowires were prepared according to the procedure of Wiley, B.; Sun, Y.; Xia, Y. Langmuir, 21 (18), 8077, 2005. Silver nanowires so prepared exhibited diameters ranging from 80 to 140 nm, and length ranging from 10 to 50 μm.
TCPA is Tetrachlorophthalic acid. Its structure is shown below.
THDI is Desmodur N-3300 (2,2,4-trimethylhexamethylene diisocyanate). It is the trimer of hexamethylene diisocyanate and is available from Bayer Material Science (Pittsburgh, Pa.).
A CAB polymer premix solution was prepared by mixing 10 parts by weight of CAB 381-20 (cellulose acetate butyrate polymer, Eastman Chemical) with 90 parts by weight of isopropyl acetate (>98.6% purity, Aldrich). The resulting CAB polymer premix solution was filtered prior to use.
25.43 parts by weight of the CAB polymer premix solution was combined with 16.96 parts by weight ethyl lactate (>99.8% purity), 45.82 parts by weight of a 1.85% solids dispersion of silver nanowires in isopropanol, and 11.79 parts by weight of isopropyl acetate (>98.6% purity, Aldrich) to form a silver nanowire coating dispersion.
A CAB polymer premix solution was prepared by mixing 15 parts by weight of CAB 553-0.4 (cellulose acetate butyrate polymer, Eastman Chemical) into 42.50 parts by weight of denatured ethanol and 42.50 parts by weight methanol (>99% purity). The resulting CAB polymer premix solution was filtered prior to use.
A topcoat masterbatch solution was prepared by adding to 5000 parts by weight of the CAB polymer premix solution 4040 parts by weight denatured ethanol, 4017.75 parts by weight isopropanol, 2250 parts by weight of 33 wt % CYMEL 303 (hexamethoxymethylmelamine, Cytec) in denatured ethanol, 150 parts by weight of 10 wt % SLIP-AYD FS-444 (polysiloxane in dipropylene glycol ether, Elementis), and 375 parts by weight of 20 wt % p-toluene sulfonic acid (Fisher/Univar) in denatured ethanol. The topcoat masterbatch solution had 10 wt % solids.
Topcoat solutions were prepared by adding various loadings of phthalazone (PAZ) to aliquots of the topcoat masterbatch solution, as shown in Table I.
The silver nanowire coating dispersion was applied to polyethylene terephthalate supports using a gravure desktop proofer equipped with a 320 line per inch plate. Each of the topcoat solutions was then applied to a silver nanowire coated polyethylene terephthalate support using a gravure desktop proofer equipped with a 450 line per inch plate. The coated films were dried at 280° F. for 3 min.
Surface resistivity of the coated films was measured using an R-CHEK model RC2175 Surface Resistivity meter available from Electronic Design To Market, Inc. (Toledo, Ohio). The surface resistivity of the coated films was measured immediately after coating to provide the initial values shown in Table II
The coated sides of the films were exposed to 1500-2000 lux fluorescent lighting and indoor atmosphere for four months. Surface resistivities were measured periodically and percent changes from initial resistivities were calculated, as shown in Table II.
A cellulose acetate butyrate polymer premix solution was prepared by mixing the following materials:
To a solution of 1.46 g of polymer premix solution, prepared as shown above, was added 0.12 g of a silver nanowire dispersion in 2-propanol (˜5.0% silver nanowires), and 0.015 g solution containing anticorrosion compound as shown in TABLE III.
The resulting dispersions were mixed on a roller mixer for 10 minutes to obtain uniform dispersions. The dispersions were coated onto 4-mil (102 μm) clear polyethylene terephthalate supports using a #10 Mayer rod. The resulting coatings were dried in oven at 220° F. (104° C.) for 6 minutes to obtain transparent films to be tested.
Surface resistivities of the conductive sample coatings were measured using an R-CHEK model RC2175 Surface Resistivity meter available from Electronic Design To Market, Inc. (Toledo, Ohio).
Surface resistivities of the conductive sample coatings were measured immediately after coating, as shown in Table IV. The initial surface resistivities of the samples containing anticorrosion agents were all higher than that of control Sample 2-1, which contained no anticorrosion agent.
Sample 2-9 was made using PAZ in the same coating mixture as the silver nanowires. Its initial surface resistivity was 149 ohms/sq, which was over 1.4 times the initial surface resistivity of 104 ohms/sq for the control Sample 2-1.
By contrast, Samples 1-2 through 1-4 of Example 1 were made using PAZ in topcoat coating mixtures, rather than in the same coating mixtures as the silver nanowires. Initial surface resistivities of those samples ranged from 75 to 80 ohms/sq, as compared to 71 ohms/sq for control Sample 1-1, which contained no anticorrosion agent.
The invention has been described in detail with particular reference to a presently preferred embodiment, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention. The presently disclosed embodiments are therefore considered in all respects to be illustrative and not restrictive. The scope of the invention is indicated by the appended claims, and all changes that come within the meaning and range of equivalents thereof are intended to be embraced therein.
This application claims the benefit of U.S. Provisional Patent Application No. 61/700,366, filed Sep. 13, 2012, entitled “ANTICORROSION AGENTS FOR TRANSPARENT CONDUCTIVE FILM,” which is hereby incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61700366 | Sep 2012 | US |