Anticorrosion primer coating composition

BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to an anticorrosion primer coating composition for metals of the type generally called a "wash primer", "shop primer", "etch primer" or "prefabrication primer". More particularly, the invention relates to an anticorrosion primer coating composition for metals which comprises as indispensable components (i) a polyvinyl butyral resin, (ii) a mixture of a borate compound and a molybdate compound or a polyphosphate compound and (iii) phosphoric acid and which may further comprise a phenolic resin and/or a metal powder according to need.
2. Description of the Prior Art
Steel frames and metal sheets or plates for steel structures such as ships and bridges have heretofore been ordinarily coated with anticorrosion primer coating paints, that is, shop primers, after complete removal of rust and mill scales by sand blasting so as to prevent rusting during processing or fabrication.
For example, D. A. Bayliss et al. proposed and examined various prefabrication primers (shop primers) in the Journal of the Oil and Colour Chemists' Association, 51, pages 792-915 (1968) published by the Oil and Colour Chemists' Association.
Shop primers include wash primers for which the conversion treatment is conducted simultaneously with the coating operation, namely shop primers called "shop primers of the conversion treatment type".
A typical composition for such wash primer comprises a polyvinyl butyral resin as a vehicle, phosphoric acid, chromic anhydride, zinc chromate and an alcohol.
The above-mentioned wash primer is produced in two types: a wash primer of the etching type and a wash primer of the high exposure resistance type.
The wash primer of the etching type is suitable for the preliminary treatment of metals to be coated and is prepared by dissolving a polyvinyl butyral resin in an alcohol, kneading and grinding a zinc chromate pigment with the resulting solution and adding an additive containing phosphoric acid to the so prepared main composition. In general, wash primers of this type are used when top coating is effected within a short time from the primer coating and are applied so as to improve adherence between a metal substrate and a top coating layer. In other words, it is not such a strict requirement for single layers of wash primers of the etching type to have high corrosion resistance as it for wash primers of the high exposure resistance type.
As the wash primer of the etching type, there has long been known a composition comprising a polyvinyl butyral resin, phosphoric acid and zinc tetraoxychromate (see the specification of U.S. Pat. No. 2,525,107). There is also known a composition comprising a modified vinyl resin obtained by reacting chromium trioxide and phosphoric acid with a vinyl resin and basic zinc chromate (see the specification of U.S. Pat. No. 2,488,651).
The wash primer of the latter type, namely the wash primer of the high exposure resistance type, comprises a main composition comprising a polyvinyl butyral resin and a phenolic resin as a vehicle and a zinc chromate pigment kneaded and ground with the vehicle and an additive including an alcohol solution of phosphoric acid. In general, the main composition is mixed with the additive at the time of application and the resulting coating composition is applied to form a coating layer excellent in adhesion to a metal substrate and to a top coat paint. Since the wash primer of this type is used when top coating is applied after the lapse of a long time from formation of the primer coating, the wash primer of this type is required to have such a corrosion resistance that the primer coating is resistant to exposure for at least about 6 months.
A typical composition for such wash primer of the high exposure resistance type is disclosed in the specification of U.S. Pat. No. 3,791,850.
In the art, wash primers of the high exposure resistance type have heretofore been mainly used as shop primers.
As will be apparent from the foregoing, conventional wash primers include a zinc chromate pigment or chromic anhydride. Therefore, they entail a problem of chromium pollution. Namely, workers breath in spray dust formed in the coating step and their health is impaired by chromium ions contained in such spray dust.
This chromium pollution is now a serious social problem, and development of an anti-pollution wash primer has been eagerly desired in the art.
For example, attempts have heretofore been made to replace zinc chromate pigments by other anti-pollution pigments. However, coatings formed from wash primers containing such pigments are defective in the corrosion resistance and adhesion. Thus, no practical anti-pollution wash primer has yet been developed in the art.
For example, although an anticorrosion primer paint comprising a polyvinyl butyral resin, zinc chromate and barium metaborate is disclosed in Japanese Patent Public Disclosure No. 44322/73, in this primer paint only a part of the zinc chromate is replaced by barium metaborate and the hygienic problem of prevention of harmful pollution is not completely solved. Further, as is taught in this publicly disclosed specification, a coating from a primer comprising a polyvinyl butyral resin and barium metaborate alone is extremely poor in corrosion resistance and though this wash primer is free of chromium and does not cause a pollution problem, it cannot be used practically.
Further, a paint composition comprising an oil varnish, oil-modified alkyd resin or drying oil as a vehicle and barium borate is known in the art (see the specification of U.S. Pat. No. 2,818,344), but this composition only provides a film having improved mold resistance or chalk resistance and has few properties required of a wash primer.
Still further, the specifications of U.S. Pat. Nos. 3,272,663 and 3,527,860 teach that a molybdate compound is used as an anticorrosion pigment for the wash primer. However, paints of this type are still insufficient in corrosion resistance.
Moreover, an attempt has been made to replace a zinc chromate pigment by a phosphate, for example, zinc phosphate (see the above-mentioned D. A. Bayliss et al. reference). Furthermore, a flame or corrosion resistant paint comprising a white pigment such as silicon phosphate, zirconium phosphate, zinc phosphate or titanium phosphate and an alkyd resin, epoxy resin, air-drying oil, phenolic resin, polyvinyl acetate resin, vinyl chloride resin or polyvinyl acetal resin is known in the art (see the specification of U.S. Pat. No. 3,892,577). These paints, however, have few of the properties required of a wash primer.
As one kind of shop primer, there is known a so-called zinc rich primer formed by incorporating zinc dust at a high concentration in a vehicle. Although this primer has a very high corrosion resistance, it has a fatal defect of poor weldability. Namely, when a steel material coated with this primer is subjected to the welding operation, blow holes are formed by a gas generated from the primer coating and the weld strength is drastically reduced. Furthermore, fumes of zinc generated at the step of welding of the primer-coated material has serious influences on the health of workers and the problems of maintenance of good health conditions is left unsolved.
From a different viewpoint, a so-called electroprint marking process in which an impage is directly formed and developed on a coated steel plate according to the electroprint process has recently been adopted in the ship-building industry so as to save labor.
In this case, a paint excellent in both electric conductivity and corrosion resistance is ordinarily applied to a steel plate, and a wash primer to which electric conductivity has been imparted is especially used for formation of such electrically conductive corrosion-resistant coating. Development of a wash primer free of chromium and capable of eliminating safety and health problems has also been desired in this field where a wash primer is utilized in the electroprint marking process.
As will be apparent from the foregoing, shop primers excellent in corrosion resistance, adhesion to a top coating or over-coating (over-coatability), weldability, adaptability to the electroprint marking process and operation safety (freedom from environmental and hygienic problems at various operation steps) have not yet been developed in the art.
The present invention has now been achieved as a result of our research work made with a view to developing primer coating compositions which overcome the foregoing defects involved in conventional coating compositions.
SUMMARY OF THE INVENTION
The present invention relates to a novel anticorrosion primer coating composition.
It is a primary object of the present invention to provide an anticorrosion primer coating composition which does not cause environmental pollution, especially chromium pollution.
Another important object of the present invention is to provide an anticorrosion primer coating composition capable of providing a coating excellent in physical and chemical properties such as corrosion resistance, weldability, workability of flame cutting, adherence and the like.
Still another object of the present invention is to provide an anticorrosion primer coating composition excellent in adaptability to the electroprint marking process.
More specifically, in accordance with the present invention, there is provided an anticorrosion primer coating composition of the etching type comprising (i) a polyvinyl butyral resin, (ii) a mixture of borate compound and polyphosphate compound or molybdate compound and (iii) phosphoric acid. In accordance with the present invention, there also is provided an anticorrosion primer coating composition of the high exposure resistance type formed by incorporating a phenolic resin into the above primer coating composition of the etching type. Further, in accordance with the present invention, there is provided an anticorrosion primer coating composition having good adaptability to the electroprint marking process, which is formed by adding a metal powder to the above-mentioned anticorrosion primer coating composition of the etching type or high exposure resistance type.
DETAILED DESCRIPTION OF THE INVENTION
Commercially available polyvinyl butyral resins having an average degree of polymerization of about 500 to about 1000 and a degree of butyration of about 57 to about 70 mole % can be directly used as the polyvinyl butyral resin (i) in the present invention.
As the borate compound that can be used as one of the component (ii) in the present invention, there can be mentioned, for example, zinc borate (2ZnO.3B.sub.2 O.sub.3.3.5H.sub.2 O), barium borate (BaB.sub.2 O.sub.4.H.sub.2 O), calcium borate (CaO.B.sub.2 O.sub.3.5H.sub.2 O), potassium tetraborate (K.sub.2 B.sub.4 O.sub.7.5H.sub.2 O), calcium tetraborate (CaB.sub.4 O.sub.7.6H.sub.2 O), sodium tetraborate (Na.sub.2 B.sub.4 O.sub.7), barium tetraborate (BaB.sub.4 O.sub.7), manganese tetraborate (MnB.sub.4 O.sub.7.8H.sub.2 O), zinc tetraborate (ZnB.sub.4 O.sub.7), lithium tetraborate (Li.sub.2 B.sub.4 O.sub.7), magnesium metaborate (Mg.sub.2 B.sub.2 O.sub.4.8H.sub.2 O) and aluminum orthoborate (Al.sub.2 O.sub.3.B.sub.2 O.sub.3). These borates may be used singly or in the form of a mixture of two or more of them. Use of zinc borate and/or barium borate is especially preferred.
As the polyphosphate compound that can be used as the other type of the component (ii) in the present invention, there can be mentioned compounds obtained by reacting phosphoric acid with a di- to hexa-valent metal or its oxide or hydroxide (presented as "X") at a P.sub.2 O.sub.5 /X molar ratio in the range of from 1 to 6 under heating to effect condensation.
As the reactant X, there can be mentioned, for example, metals such as Mg, Al, Ca, Zn, Mn, Fe and Ba, oxides such as MgO, Al.sub.2 O.sub.3, CaO, ZnO, MnO.sub.2, FeO, MoO.sub.3, BaO and WO.sub.3, and hydroxides such as Mg(OH).sub.2, Al(OH).sub.3, Ca(OH).sub.2, Zn(OH).sub.2, Ba(OH).sub.2 and Fe(OH).sub.3.
These polyphosphate compounds can be used singly or in the form of a mixture of two or more of them. Use of zinc polyphosphate, aluminum polyphosphate, calcium polyphosphate and mixtures of two or more of them is especially preferred. Commercially available aluminum polyphosphate K-50, K-80 and K-82 (trademarks for products manufactured by Teikoku Kako Co., Ltd.) and HB Hardener (trademark for the product Hoechst AG) are conveniently used in the present invention.
As the molybdate compound that can be used as the still another type of the component (ii) in the present invention, there can be mentioned, for example, zinc molybdate, calcium molybdate. These molybdate compound may be used singly or in the form of a mixture.
Phosphoric acid that is used as the component (iii) in the present invention is an acid formed by hydration of diphosphorus pentoxide.
More specifically, there can be mentioned metaphosphoric acid, pyrophosphoric acid, orthophosphoric acid, triphosphoric acid, tetraphosphoric acid and the like. These phosphoric acids may be used singly or in the form of a mixture of two or more of them.
Any of metal powders capable of imparting an electric conductivity to the resulting coatings can be used as the metal powder in the present invention. Ordinary metal powders having a size of about 500 to about 180 mesh can be used in the present invention. More specifically, in the present invention there can be used aluminum powder and powders of alloys of aluminum with at least one metal selected from the group consisting of zinc, magnesium, tin, silicon, copper and manganese. Use of aluminum powder is especially preferred.
In the present invention, these metal powders can be used singly or in the form of a mixture of two or more of them.
The anticorrosion primer coating composition according to another embodiment of the present invention further comprises a phenolic resin. Commercially available phenolic resins for paints can be directly used for this embodiment of the present invention. These phenolic resins are ordinarily formed by condensing a phenol with an aldehyde according to a customary method and they have an average molecular weight of about 100 to about 1000.
In the present invention, good results are obtained when 100 parts by weight of a polyvinyl butyral resin is mixed with 20 to 350 parts by weight, preferably 50 to 250 parts by weight, of a mixture of a borate compound and a molybdate or polyphosphate compound, and 5 to 50 parts by weight, preferably 15 to 40 parts by weight, of phosphoric acid. The mixing weight ratio of borate compound and molybdate or polyphosphate compound is from 9/1 to 1/9, preferably from 8/2 to 4/6.
When the amount of the mixture of the borate compound and polyphosphate compound of molybdate compound is outside the above-mentioned range, reduction of the corrosion resistance is observed.
In this embodiment of the present invention using a phenolic resin, it is preferred that up to 200 parts by weight, especially 70 to 170 parts by weight, of the phenolic resin be incorporated in 100 parts by weight of the polyvinyl butyral resin. When the amount of the phenolic resin exceeds 200 parts by weight per 100 parts by weight of the polyvinyl butyral resin, the adhesion to the top coating or over-coating (over-coatability) is reduced.
When a metal powder is incorporated in the anticorrosion primer coating composition of the present invention, the metal powder is used in an amount of 10 to 130 parts by weight, preferably 15 to 90 parts by weight, per 100 parts by weight of the polyvinyl butyral resin. When the amount of the metal powder is smaller than 10 parts by weight per 100 parts by weight of the polyvinyl butyral resin, the adaptability to the electroprint marking process is degraded, and when the amount of the metal powder is larger than 130 parts by weight per 100 parts by weight of the polyvinyl butyral resin, the corrosion resistance or adhesion tends to decrease.
The coating composition of the present invention comprises as indispensable components (i) a polyvinyl butyral resin, (ii) a mixture of borate compound and polyphosphate compound or molybdate compound and (iii) phosphoric acid.
For example, in case of a composition comprising a polyginyl butyral resin, phosphoric acid and a borate (namely, the composition free of a molybdate or polyphosphate compound) or a composition comprising a polyvinyl butyral resin, phosphoric acid and a molybdate or polyphosphate compound (namely, the composition free of a borate compound), it is substantially impossible to obtain a coating satisfying the primary object of the present invention, namely a coating having a high corrosion resistance.
According to the present invention, a high anticorrosion effect can be obtained by an anticorrosion primer coating composition comprising a polyvinyl butyral resin, a mixture of borate compound and polyphosphate compound or molybdate compound, and phosphoric acid, which may further comprise a phenolic resin and/or a metal powder according to need.
In the coating composition of the present invention, a polyvinyl butyral resin, a mixture of borate compound and polyphosphate compound or molybdate compound are mixed and ground with a solvent customarily used for a wash primer, for example, an alcohol optionally with another pigment, such as an extender pigment or color pigment and other compatible resin or additive and further optionally with a phenolic resin and/or a metal powder to form a main composition, and the so formed main composition is mixed with a separately prepared solution of phosphoric acid when the coating composition is actually applied.
The so formed coating composition of the present invention is applied to a substrate to be coated, such as iron, aluminum or zinc plate or the like, according to a customary coating method.
The resulting coating formed by application of the above coating composition is tightly and closely bonded to the metal substrate by the synergistic effect of the borate compound and molybdate or polyphosphate compound and therefore, a coating excellent in corrosion resistance can be obtained.
When the anticorrosion primer coating composition of the present invention comprising a polyvinyl butyral resin, a mixture of borate compound and a molybdate or a polyphosphate compound and phosphoric acid optionally with a metal powder is used as a wash primer of the etching type, or when the anticorrosion primer coating composition of the present invention comprising a polyvinyl butyral resin, phosphoric acid, a mixture of borate compound and molybdate or polyphosphate compound and a phenolic resin optional with a metal powder is used as a wash primer of the high exposure resistance type, a coating excellent in corrosion resistance, weldability, workability of flame cutting, adaptability to electroprint marking process and over-coatability can be obtained. Further, the anticorrosion primer coating composition of the present invention is a chromium-free coating composition causing no environmental pollution and having no harmful influence on the health of workers. Accordingly, the anticorrosion primer coating composition of the present invention is industrially valuable as a shop primer.
The present invention will now be described in detail by reference to the following Examples, in which all of "parts" and "%" are by weight.

EXAMPLE 1
______________________________________Main CompositionIngredients Parts______________________________________Phenolic resin (Hitanol 4020 manu- 11.0factured by Hitachi Chemical Co.Ltd.)Polyvinyl butyral resin (S-LEC 9.0BM-2 manufactured by SekisuiChemical Co., Ltd.)Yellow iron oxide (Mapico Yellow) 3.0Phthalocyanine Blue 0.3Carbon black 0.3Zinc molybdate.sup.1) 2.5Talc 5.9Barium borate.sup.2) 2.5Suspending agent (organic bentonite) 1.0Butyl alcohol 11.0Isopropyl alcohol 25.0Toluol 30.5Total 100.0______________________________________AdditiveIngredients Parts______________________________________85% Aqueous solution of phosphoric 9.0acidWater 5.0Isopropyl alcohol 86.0Total 100.0______________________________________ Notes .sup.1) Product manufactured and sold under the tradename "Moly-White 212 by Sherwin Williams Chemicals Co., Ltd. .sup.2) Barium metaborate manufactured and sold under the tradename "Busa 11-Ml" by Buckman Laboratories Co.
The ingredients of the main composition were kneaded and ground overnight, and 80 parts of the main composition was mixed with 20 parts of the additive to form a coating composition of the present invention.
The so formed coating composition was applied to a steel plate by means of an air spray so that the thickness of the coating was 20.mu., and the coating was dried in a room maintained at a temperature of 20.degree. C. and a relative humidity of 75% of 3 days and was then subjected to comparison tests to obtain the results shown in Table 4.
EXAMPLES 2 TO 10
A main composition comprising the ingredients shown in Table 1 was kneaded and ground in the same manner as described in Example 1, and 85 parts of the main composition was mixed with 15 parts of the same additive as used in Example 1. The resulting composition was applied, dried and subjected to comparison tests in the same manner as described in Example 1.
Each of the so obtained coatings was as excellent as the coating obtained in Example 1 with respect to results of the salt spray test and the out-door exposure test.
Table 1______________________________________Amounts (parts) of Ingredients in Main CompositionIngredients Example 2 Example 3______________________________________Phenolic resin 8.0 9.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.0 3.0Carbon black 0.3 0.3Phthalocyanine Blue 0.3 0.3Borate compound 5.0.sup.1) 15.0.sup.2)Molybdate compound 5.0.sup.6) 5.0.sup.7)Polyphosphate compound -- --Suspending agent 1.0 1.0Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 32.4 21.4Talc -- --Total 100.0 100.0Ingredients Example 4 Example 5______________________________________Phenolic resin 7.0 8.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.0 3.0Carbon black 0.3 0.3Phthalocyanine Blue 0.3 0.3Borate compound 10.0.sup.3) 6.0.sup.4)Molybdate compound 10.0.sup.8) 7.0.sup.6)Polyphosphate compound -- --Suspending agent 1.0 1.0Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 23.4 29.4Talc -- --Total 100.0 100.0Ingredients Example 6 Example 7______________________________________Phenolic resin 8.0 11.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.0 3.0Carbon black 0.3 0.3Phthalocyanine Blue 0.3 0.3Borate compound 8.0.sup.5) 2.5.sup.2)Molybdate compound 5.0.sup.7) --Polyphosphate compound -- 2.5.sup.9)Suspending agent 1.0 1.0Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 29.4 30.5Talc -- 3.9Total 100.0 100.0 Example Example ExampleIngredients 8 9 10______________________________________Phenolic resin 8.0 9.0 7.0Polyvinyl butyral 9.0 9.0 9.0resinYellow iron oxide 3.0 3.0 3.0Carbon black 0.3 0.3 0.3Phthalocyanine Blue 0.3 0.3 0.3Borate compound 5.0.sup.1) 15.0.sup.2) 10.0.sup.3)Molybdate compound -- -- --Polyphosphate compound 5.0.sup.9) 5.0.sup.10) 10.0.sup.11)Suspending agent 1.0 1.0 1.0Butyl alcohol 11.0 11.0 11.0Isopropyl alcohol 25.0 25.0 25.0Toluol 32.4 21.4 23.4Talc -- -- --Total 100.0 100.0 100.0______________________________________ Notes: .sup.1) Zinc borate (2ZnO.multidot.3B.sub.2 O.sub.3 .multidot.3.multidot.5H.sub.2 O) .sup.2) Barium metaborate (BaB.sub.2 O.sub.4 .multidot.H.sub.2 O) .sup.3) Mixture of equal amounts of zinc borate and barium metaborate .sup.4) Sodium tetraborate (Na.sub.2 B.sub.4 O.sub.7) .sup.5) Magnesium metaborate (Mg.sub.2 B.sub.2 O.sub.4 .multidot.8H.sub.2 O) .sup.6) Zinc molybdate .sup.7) Calcium molybdate .sup.8) Mixture of zinc molybdate and calcium molybdate (mixing weight ratio = 5 : 1) .sup.9) Aluminum polyphosphate (Product manufactured and sold under tradename "K-82" by Teikoku Kako Co., Ltd.) .sup.10) Zinc polyphosphate formed by mixing zinc oxide (ZnO) with 85% phosphoric acid so that the P.sub.2 O.sub.5 /ZnO mole ratio was 3.5, gradually heating the resulting starting mixture in a porcelain crucible under agitation so that the temperature was elevated to 250.degree. C ove a period of 2 hours, heating the mixture for 4 hours in an electric furnace maintained at 400.degree. C, cooling the heated product and then pulverizing it .sup.11) Mixture of aluminum polyphosphate and zinc polyphosphate (mixing weight ratio = 5 : 1)
EXAMPLE 11
______________________________________Main CompositionIngredients Parts______________________________________Polyvinyl butyral resin 9.0Barium metaborate 2.5Zinc molybdate 2.5(same as used in Example 1)Talc 5.0Isopropyl alcohol 61.0Butyl alcohol 20.0Total 100.0AdditiveIngredients Parts______________________________________85% Aqueous solution of 18.0phosphoric acidWater 16.0Isopropyl alcohol 66.0Total 100.0______________________________________
The ingredients of the main composition were kneaded and ground in a pot mill overnight, and 80 parts of the main composition was mixed with 20 parts of the additive to obtain a coating composition of the present invention. In the same manner as described in Example 1, the resulting coating composition was applied, dried and subjected to comparison tests to obtain the results shown in Table 4.
EXAMPLES 12 TO 19
A main composition comprising the ingredients shown in Table 2 was kneaded and ground, and 85 parts of the main composition was mixed with 15 parts of the same additive as used in Example 11 to obtain a coating composition. The coating composition was coated, dried and subjected to comparison tests. It was found that each of the resulting coatings showed as excellent results as were shown by the coating obtained in Example 11.
Table 2__________________________________________________________________________Amounts (parts) of Ingredients in Main Component Polyvinyl Poly- Iso-Example Butyral Borate Molybdate phosphate propyl ButylNo. Resin Compound Compound Compound Alcohol Alcohol Talc Total__________________________________________________________________________12 9.0 2.5.sup.1) 2.5.sup.5) -- 60.5 20.5 5.0 100.013 9.0 5.0.sup.2) 5.0.sup.6) -- 60.5 20.5 -- 100.014 9.0 5.0.sup.3) 5.0.sup.7) -- 60.5 20.5 -- 100.015 9.0 5.0.sup.4) 6.0.sup.5) -- 60.0 20.0 -- 100.016 9.0 2.5.sup.2) -- 2.5.sup.8) 61.0 20.0 5.0 100.017 9.0 2.5.sup.1) -- 2.5.sup.8) 60.5 20.5 5.0 100.018 9.0 5.0.sup.2) -- 5.0.sup.9) 60.5 20.5 -- 100.019 9.0 5.0.sup.3) -- 5.0.sup.10) 60.5 20.5 -- 100.0__________________________________________________________________________ Notes .sup.1) Zinc borate mentioned above .sup.2) Barium metaborate mentioned above .sup.3) Mixture of zinc borate and barium metaborate mentioned above (mixing weight ratio = 1:1) .sup.4) Potassium tetraborate .sup.5) Zinc molybdate mentioned above .sup.6) Calcium molybdate .sup.7) Mixture of calcium molybdate and zinc molybdate mentioned above (mixing weight ratio = 1:3) .sup.8) Aluminum polyphosphate mentioned above .sup.9) Zinc polyphosphate mentioned above .sup.10) Calcium polyphosphate prepared from a mixture of calcium oxide and 85% phosphoric acid (P.sub.2 O.sub.5 /CaO mole ratio = 4) according t the same method as adopted in Example 9 for preparation of zinc polyphosphate
COMPARATIVE EXAMPLES 1 TO 8
Ingredients of a main composition indicated in Table 3 were kneaded and ground, and 80 parts of the resulting main composition was mixed with 20 parts of an additive indicated in Table 3. In the same manner as described in Example 1, the resulting composition was applied, dried and tested to obtain the results shown in Table 4.
Table 3______________________________________Amounts (parts) of Ingredients ofMain Composition and Additive Comparative ComparativeIngredients Example 1 Example 2______________________________________Main CompositionPhenolic resin 11.0 11.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.0 3.0Carbon black 0.3 0.3Phthalocyanine Blue 0.3 0.3Zinc chromate 5.0 --Suspending agent 1.0 1.0Barium metaborate -- 10.0Aluminum polyphosphate -- --Zinc molybdate.sup.1) -- --Talc -- --Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 34.4 29.4Additive85% Aqueous solution of 9.4 9.0phosphoric acidChromic anhydride 0.2 --Water 4.5 5.0Isopropyl alcohol 85.9 86.0______________________________________ Comparative ComparativeIngredients Example 3 Example 4______________________________________Main CompositionPhenolic resin 11.0 11.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.0 3.0Carbon black 0.3 0.3Phthalocyanine Blue 0.3 0.3Zinc chromate -- --Suspending agent 1.0 1.0Barium metaborate -- --Aluminum polyphosphate 10.0 --Zinc molybdate.sup.1) -- 10.0Talc -- --Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 29.4 29.4Additive85% Aqueous solution 9.0 9.0of phosphoric acidChromic anhydride -- --Water 5.0 5.0Isopropyl alcohol 86.0 86.0______________________________________ Comparative ComparativeIngredient Example 5 Example 6______________________________________Main CompositionPhenolic resin -- --Polyvinyl butyral resin 9.0 9.0Yellow iron oxide -- --Carbon black -- --Phthalocyanine Blue -- --Zinc chromate 8.6 --Suspending agent -- --Barium metaborate -- 10.0Aluminum polyphosphate -- --Zinc molybdate.sup.1) -- --Talc 1.4 --Butyl alcohol 20.0 20.0Isopropyl alcohol 61.0 61.0Toluol -- --Additive85% Aqueous solution 18.0 18.0of phosphoric acidChromic anhydride -- --Water 16.0 16.0Isopropyl alcohol 66.0 66.0______________________________________ Comparative ComparativeIngredient Example 7 Example 8______________________________________Main CompositionPhenolic resin -- --Polyvinyl butyral resin 9.0 9.0Yellow iron oxide -- --Carbon black -- --Phthalocyanine Blue -- --Zinc chromate -- --Suspending agent -- --Barium metaborate -- --Aluminum polyphosphate 10.0 --Zinc molybdate.sup.1) -- 10.0Talc -- --Butyl alcohol 20.0 20.0Isopropyl alcohol 61.0 61.0Toluol -- --Additive85% Aqueous solution 18.0 18.0of phosphoric acidChromic anhydride -- --Water 16.0 16.0Isopropyl alcohol 66.0 66.0______________________________________ Note: .sup.1) Product manufactured and sold under the tradename "Moly-White 212" by Sherwin Williams Chemicals Co., Ltd.
Table 4______________________________________Results of Comparison Tests OutdoorSample Salt Spray Test.sup.1) Exposure Test.sup.2)Coating 50 hours 150 hours 3 months 6 months______________________________________Example 1Example 3Example 7Example 9Example 11 -- -- --Example 13 -- -- --Example 16 -- -- --Example 18 -- -- --ComparativeExample 1 0 0ComparativeExample 2 .DELTA. X .DELTA. XComparativeExample 3 .DELTA. X .DELTA. XComparativeExample 4 .DELTA. X .DELTA. XComparativeExample 5 0 - -- -- --ComparativeExample 6 X -- -- --ComparativeExample 7 X -- -- --ComparativeExample 8 X -- -- --______________________________________ Notes .sup.1) The salt spray test was conducted by using a 5% aqueous solution of NaCl. The test results were evaluated according to the scale indicated below. .sup.2) The outdoor exposure test results were evaluated according to the scale indicated below.
In each of the salt spray test and outdoor exposure tests, the corrosion resistance was evaluated according to the following scale:
: not changed
O: slight rusting and blistering
.DELTA.: rusting and blistering on 10 to 50% of the total area
X: rusting and blistering on substantially entire area
From the foregoing test results, it will readily be understood that coating compositions of the high exposure resistance type according to the present invention (Examples 1, 3, 7 and 9) comprising a polyvinyl butyral resin, a phenolic resin, phosphoric acid and a mixture of a borate compound and a polyphosphate compound or a molybdate compound are far superior to the conventional wash primer of the high exposure resistance type (Comparative Example 1) with respect to the long lasting corrosion resistance. Further, since these coating compositions of the present invention are free of chromium and cause no environmental pollution, they are far superior to the conventional wash primer with respect to operation safety, health maintenance and pollution-preventing effect. Moreover, in view of the ingredients constituting the coating compositions of the present invention, it will be apparent that they are much improved over the conventional zinc-rich paint with respect to weldability and workability of flame cutting.
Chromium-free paints formed by replacing a zinc chromate pigment by other corrosion-resistant pigment in the conventional wash primer of the high exposure resistance type (Comparative Examples 2 to 4) have no practical utility because they are much inferior to the conventional wash primer with respect to corrosion resistance.
It will also be apparent that coating compositions of the etching type according to the present invention (Examples 11, 13, 16 and 18) comprising a polyvinyl butyral resin, phosphoric acid and a mixture of a borate compound and a polyphosphate compound or a molybdate compound are superior to the conventional wash primer of the etching type (Comparative Example 5), the composition including a borate compound alone (Comparative Example 6), the composition including a polyphosphate alone (Comparative Example 7), and the composition including a molybdate compound alone (Comparative Example 8) with respect to corrosion resistance, operation safety and pollution-preventing effect.
EXAMPLE 20
______________________________________Main CompositionIngredients Parts______________________________________Phenolic resin (Hitanol 4020 11.0mentioned above)Polyvinyl butyral resin (S-LEC 9.0BM-2 mentioned above)Yellow iron oxide (Mapico Yellow) 3.5Carbon black 0.9Phthalocyanine Blue 1.0Barium borate (Busan 11-M1) 2.5Aluminum polyphosphate (K-82) 2.5Talc 3.9Aluminum powder paste (solid 5.0content = 64%; mineral terpenesolution: product manufacturedand sold under tradename"Alpaste 1100N" by Toyo AluminumCo., Ltd.)Suspending agent (organic bentonite) 1.0Butyl alcohol 11.0Isopropyl alcohol 25.0Toluol 23.7Total 100.0AdditiveIngredients Parts______________________________________85% Aqueous solution of 9.0phosphoric acidWater 5.0Isopropyl alcohol 86.0Total 100.0______________________________________
Ingredients of the main composition except the aluminum powder paste were kneaded and ground overnight, and the prescribed amount of the aluminum power paste was added to the kneaded mixture and uniformly dispersed therein to form the main composition. Then, 80 parts of the so formed main composition was mixed with 20 parts of the additive to form a coating composition of the present invention.
The so formed coating composition was applied to a steel plate by means of an air spray so that the thickness of the resulting coating was 20.mu. and was dried in a room maintained at a temperature of 20.degree. C. and a relative humidity of 75% for 3 days. The resulting coating was subjected to comparison tests to obtain the results shown in Table 8.
Electroprint marking was carried out in the following manner.
A mixture comprising 10 parts of a silicone resin (50% solution in a mixed solvent of xylol and toluol), 10 parts of a vinyl acetate resin (50% solution in a mixed solvent of xylol and toluol), 50 parts of zinc oxide, 20 parts of xylol and 10 parts of ethyl acetate was blended and dispersed in a ball mill, and the resulting dispersion was heated, dried and pulverized to obtain a photoconductive powder having an average particle size of 20.mu..
The so prepared photoconductive powder was uniformly scattered on a steel plate coated with the above-mentioned coating composition by an electrostatic powder coating machine, and the coated steel plate was exposed to rays projected from a xenon lamp through a positive original to form an electrostatic latent image. The photoconductive powder on exposed areas was selectively removed and recovered by application of pneumatic pressure to obtain a marked visible image. Then, the image was fixed by heating at 130.degree. C. for 30 minutes.
EXAMPLES 21 TO 32
Ingredients of a main composition indicated in Table 5 were kneaded and ground in the same manner as described in Example 20 and 85 parts of the resulting main composition was mixed with 15 parts of the same additive as used in Example 20. The resulting composition was applied, dried and tested in the same manner as described in Example 20.
It was found that each of the so prepared compositions was as excellent in corrosion resistance of the coating and adaptability to the electroprint marking process as the coating composition obtained in Example 20.
Table 5______________________________________Amounts (parts) of Ingredients in Main CompositionIngredients Example 21 Example 22______________________________________Phenolic resin 8.0 8.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.5 3.5Carbon black 0.9 0.9Phthalocyanine Blue 1.0 1.0Borate compound 5.0.sup.1) 5.0.sup.1)Polyphosphate compound 5.0.sup.6) 5.0.sup.6)Molybdate compound -- --Talc -- --Aluminum powder paste 3.0.sup.12) 5.0.sup.12)Suspending agent 1.0 1.0Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 27.6 25.6Total 100.0 100.0Ingredients Example 23 Example 24______________________________________Phenolic resin 8.0 8.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.5 3.5Carbon black 0.9 0.9Phthalocyanine Blue 1.0 1.0Borate compound 5.0.sup.1) 5.0.sup.1)Polyphosphate compound 5.0.sup.6) 5.0.sup.6)Molybdate compound -- --Talc -- --Aluminum powder paste 5.0.sup.13) 10.0.sup.12)Suspending agent 1.0 1.0Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 25.6 20.6Total 100.0 100.0Ingredients Example 25 Example 26______________________________________Phenolic resin 9.0 7.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.5 3.5Carbon black 0.9 0.9Phthalocyanine Blue 1.0 1.0Borate compound 15.0.sup.2) 10.0.sup.3)Polyphosphate compound 5.0.sup.7) 10.0.sup.8)Molybdate compound -- --Talc -- --Aluminum powder paste 5.0.sup.12) 5.0.sup.12)Suspending agent 1.0 1.0Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 14.6 16.6Total 100.0 100.0Ingredients Example 27 Example 28______________________________________Phenolic resin 11.0 8.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.0 3.0Carbon black 0.3 0.3Phthalocyanine Blue 0.3 0.3Borate compound 2.5.sup.2) 5.0.sup.1)Polyphosphate compound -- --Molybdate compound 2.5.sup.9) 5.0.sup.9)Talc 3.9 --Aluminum powder paste 5.0.sup.12) 3.0.sup.12)Suspending agent 1.0 1.0Butyl alcohol 11.0 11.0Isopropyl alcohol 20.0 25.0Toluol 30.5 29.4Total 100.0 100.0______________________________________Ingredients Example 29 Example 30______________________________________Phenolic resin 9.0 7.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.0 3.0Carbon black 0.3 0.3Phthalocyanine Blue 0.3 0.3Borate compound 15.0.sup.2) 10.0.sup.3)Polyphosphate compound -- --Molybdate compound 5.0.sup.10) 10.0.sup.11)Talc -- --Aluminum powder paste 7.0.sup.12) 6.0.sup.12)Suspending agent 1.0 1.0Butyl alcohol 11.0 11.0Isopropyl alcohol 22.0 25.0Toluol 17.4 17.4Total 100.0 100.0______________________________________Ingredients Example 31 Example 32______________________________________Phenolic resin 8.0 8.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.0 3.0Carbon black 0.3 0.3Phthalocyanine Blue 0.3 0.3Borate compound 6.0.sup.4) 8.0.sup.5)Polyphosphate compound -- --Molybdate compound 7.0.sup.9) 5.0.sup.10)Talc -- --Aluminum powder paste 5.0.sup.13) 4.0.sup.12)Suspending agent 1.0 1.0Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 24.4 25.4Total 100.0 100.0______________________________________ Notes .sup.1) Zinc borate (2ZnO.multidot.3B.sub.2 O.sub.3 .multidot.3.multidot.5H.sub.2 O) .sup.2) Barium metaborate mentioned above .sup.3) Mixture of equal amounts of zinc borate and barium metaborate .sup.4) Sodium tetraborate (Na.sub.2 B.sub.4 O.sub.7) .sup.5) Magnesium metaborate (Mg.sub.2 B.sub.2 O.sub.4 .multidot..8H.sub. O) .sup.6) Aluminun polyphosphoate (same as used in Example 20) .sup. 7) Zinc polyphosphate (same as used in Example 9) .sup.8) Mixture of aluminum polyphosphate and zinc polyphosphate (mixing weight ratio = 5:1) .sup.9) Zinc molybdate .sup.10) Calcium molybdate .sup.11) Mixture of zinc molybdate and calcium molybdate (mixing weight ratio = 5:1) .sup.12) Alpaste 1100N (same as used in Exampl 20) .sup.13) Aluminum alloy powder paste (Aluminum/zinc weight ratio 95/5; solid content 64%, mineral terpene solution)
EXAMPLE 33
______________________________________Main CompositionIngredients Parts______________________________________Polyvinyl butyral resin 9.0Yellow iron oxide 3.5Carbon black 0.9Phthalocyanine Blue 1.0Barium metaborate 2.5Aluminum polyphosphate (Product 2.5manufactured and sold undertradename "HB Hardener" byHoechst AG)Talc 6.3Aluminum powder paste (Product 3.0manufactured and sold undertradename "Alpaste 1700NL" byToyo Aluminum Co., Ltd. (solidcontent - 64%; mineral terpenesolution))Isopropyl alcohol 60.5Butyl alcohol 10.8Total 100.0AdditiveIngredients Parts______________________________________85% Aqueous solution of phosphoric 18.0acidWater 16.0Isopropyl alcohol 66.0Total 100.0______________________________________
The ingredients of the main composition were kneaded and ground in the same manner as in Example 20, and 80 parts of the resulting main composition was mixed with 20 parts of the additive to obtain a coating composition of the present invention. The coating composition was applied, dried and tested in the same manner as in Example 20 to obtain results shown in Table 8.
EXAMPLES 34 TO 43
Ingredients of a main composition indicated in Table 6 were kneaded and ground, and 85 parts of the resulting main composition was mixed with 15 parts of the same additive as used in Example 33. The resulting compositions were subjected to comparison tests in the same manner as described in Example 33. It was found that each coating composition was as excellent as the coating composition obtained in Example 33 with respect to corrosion resistance of the resulting coating and adaptability to the electroprint marking process.
Table 6__________________________________________________________________________Amounts (parts) of Ingredients in Main CompositionIngredients Example 34 Example 35 Example 36 Example 37 Example 38__________________________________________________________________________Polyvinyl butyral resin 9.0 9.0 9.0 9.0 9.0Yellow iron oxide 3.5 3.5 3.5 3.5 3.5Carbon black 0.9 0.9 0.9 0.9 0.9Phthalocyanine Blue 1.0 1.0 1.0 1.0 1.0Borate compound 2.5.sup.1) 2.5.sup.1) 2.5.sup.1) 5.0.sup.2) 5.0.sup.3)Polyphosphate compound 2.5.sup.5) 2.5.sup.5) 2.5.sup.5) 5.0.sup.6) 5.0.sup.7)Molybdate compound -- -- -- -- --Talc 5.0 5.0 1.8 -- --Aluminum powder paste 5.0.sup.10) 5.0.sup.11) 10.0.sup.10) 5.0.sup.10) 5.0.sup.10)Isoproyl alcohol 60.5 60.5 60.5 60.5 60.5Butyl alcohol 10.1 10.1 8.3 10.1 10.1Total 100.0 100.0 100.0 100.0 100.0__________________________________________________________________________Ingredients Example 39 Example 40 Example 41 Example 42 Example 43__________________________________________________________________________Polyvinyl butyral resin 9.0 9.0 9.0 9.0 9.0Yellow iron oxide -- -- -- -- --Carbon black -- -- -- -- --Phthalocyanine Blue -- -- -- -- --Borate compound 2.5.sup.2) 2.5.sup.1) 5.0.sup.2) 5.0.sup.3) 5.0.sup.4)Polyphosphate compound -- -- -- -- --Molybdate compound 2.5.sup.8) 2.5.sup.9) 5.0.sup.8) 5.0.sup.9) 6.0.sup.8)Talc 5.0 5.0 -- -- --Aluminum powder paste 5.0.sup.12) 7.0.sup.12) 3.0.sup.12) 4.0.sup.12) 5.0.sup.11)Isopropyl alcohol 56.0 53.5 57.5 56.5 55.0Butyl alcohol 20.0 20.5 20.5 20.5 20.0Total 100.0 100.0 100.0 100.0 100.0__________________________________________________________________________ Notes .sup.1) Zinc borate .sup.2) Barium metaborate .sup.3) Mixture of equal amounts of zinc borate and barium metaborate .sup.4) Potassium tetraborate .sup.5) Aluminum polyphosphate (same as used in Example 33) .sup.6) Zinc polyphosphate (same as used in Example 25) .sup.7) Calcium polyphospate (same as used in Example 19) .sup.8) Zinc molybdate .sup.9) Calcium molybdate .sup.10) Alpaste 1100N mentioned above .sup.11) Aluminum alloy powder paste (same as used in Example 23) .sup.12) Alpaste 1700NL mentioned above
COMPARATIVE EXAMPLES 9 TO 16
Ingredients of a main composition indicated in Table 7 were kneaded and ground in the same manner as described in Example 20, and 80 parts of the so formed main composition was mixed with 20 parts of an additive indicated in Table 7 to form a coating composition. The resulting coating composition was tested in the same manner as described in Example 20 to obtain the results shown in Table 8.
Table 7______________________________________Amounts (parts) of Ingredients ofMain Composition and Additive Comparative ComparativeIngredients Example 9 Example 10______________________________________Main CompositionPhenolic resin 11.0 11.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.5 3.5Carbon black 0.9 0.9Phthalocyanine Blue 1.0 1.0Zinc chromate 5.0 --Suspending agent 1.0 1.0Barium metaborate -- 10.0Aluminum polyphosphate -- --Zinc molybdate.sup.1) -- --Aluminum powder paste.sup.2) -- --Talc 8.2 3.2Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 24.4 24.4Additive85% Aqueous solution 9.4 9.4of phosphoric acidChromic anhydride 0.2 --Water 4.5 4.5Isopropyl alcohol 85.9 86.1______________________________________ Comparative ComparativeIngredients Example 11 Example 12______________________________________Main CompositionPhenolic resin 11.0 11.0Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.5 3.5Carbon black 0.9 0.9Phthalocyanine Blue 1.0 1.0Zinc chromate -- --Suspending agent 1.0 1.0Barium metaborate -- --Aluminum polyphosphate 10.0 --Zinc molybdate.sup.1) -- 10.0Aluminum powder paste.sup.2) 5.0 5.0Talc -- --Butyl alcohol 11.0 11.0Isopropyl alcohol 25.0 25.0Toluol 22.6 22.6Additive85% Aqueous solution 9.0 9.0of phosphoric acidChromic anhydride -- --Water 5.0 5.0Isopropyl alcohol 86.0 86.0______________________________________ Comparative ComparativeIngredients Example 13 Example 14______________________________________Main CompositionPhenolic resin -- --Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.5 3.5Carbon black 0.9 0.9Phthalocyanine Blue 1.0 1.0Zinc chromate 8.2 --Suspending agent -- --Barium metaborate -- 5.0Aluminum polyphosphate -- --Zinc molybdate.sup.1) -- --Aluminum powder paste.sup.2) -- --Talc -- 3.2Butyl alcohol 20.0 20.0Iospropyl alcohol 57.4 57.4Toluol -- --Additive85% Aqueous solution 18.0 18.0of phosphoric acidChromic anhydride -- --Water 16.0 16.0Isopropyl alcohol 66.0 66.0 Comparative ComparativeIngredients Example 15 Example 16______________________________________Main CompositionPhenolic resin -- --Polyvinyl butyral resin 9.0 9.0Yellow iron oxide 3.5 3.5Carbon black 0.9 0.9Phthalocyanine Blue 1.0 1.0Zinc chromate -- --Suspending agent -- --Barium metaborate -- --Aluminum polyphosphate 5.0 --Zinc molybdate.sup.1) -- 5.0Aluminum powder paste.sup.2) 5.0 5.0Talc -- --Butyl alcohol 20.0 20.0Isopropyl alcohol 55.6 55.6Toluol -- --Additive85% Aqueos solution 18.0 18.0of phosphoric acidChromic anhydride -- --Water 16.0 16.0Isopropyl alcohol 66.0 66.0______________________________________
Table 8______________________________________Test Results Salt Spray Test.sup.1)Sample Coating 50 hours 100 hours______________________________________Example 20Example 21Example 23Example 25Example 27Example 29Example 31Example 33 --Example 35 --Example 37 --Example 39 --Example 41 --Example 43 --Comparative Example 9 0Comparative Example 10 .DELTA. XComparative Example 11 .DELTA. XComparative Example 12 .DELTA. XComparative Example 13 0 - XComparative Example 14 X --Comparative Example 15 X --Comparative Example 16 X --______________________________________ Outdoor Exposure Test.sup.2)Sample Coating 3 months 6 months______________________________________Example 20Example 21Example 23Example 25Example 27Example 29Example 31Example 33 --Example 35 --Example 37 --Example 39 --Example 41 --Example 43 --Comparative Example 9 0Comparative Example 10 .DELTA. XComparative Example 11 .DELTA. XComparative Example 12 .DELTA. XComparative Example 13 -- --Comparative Example 14 -- --Comparative Example 15 -- --Comparative Example 16 -- --______________________________________Adaptability to ElectroprintMarking Process Recovery LossSample Resolution of Photoconduc- Sensitivity.sup.5)Coating of Image.sup.3) tive Powder.sup.4) (seconds)______________________________________Example 20 good below 1% 10Example 21 good 2% 10Example 23 good below 1% 10Example 25 good below 1% 10Example 27 good below 1% 10Example 29 good below 1% 10Example 31 good below 1% 10Example 33 good 2% 10Example 35 good below 1% 10Example 37 good below 1% 10Example 39 good below 1% 10Example 41 good below 1% 10Example 43 good below 1% 10Comparative bad 10% 60Example 9Comparative bad 10% 60Example 10Comparative good below 1% 10Example 11Comparative good below 1% 10Example 12Comparative bad 10% 60Example 13Comparative bad 10% 60Example 14Comparative good below 1% 10Example 15Comparative good below 1% 10Example 16______________________________________ Notes .sup.1) The salt spray test was conducted by using 5% aqueous solution of NaCl. The test results were evaluated according to the scale indicated below .sup.2) The outdoor exposure test results were evaluated according to the scale indicated below .sup.3) The resolution of the image was evaluated by naked eye observatio .sup.4) The recovery loss of the photoconductive powder was calculated according to the following formula: ##STR1## .sup.5) The sensitivity is expressed in terms of the time (seconds) durin which the sensitivity was attenuated under 60 luxes
In each of the salt spray test and outdoor exposure test, the corrosion resistance was evaluated according to the following scale:
: not changed
O: slight rusting and blistering
.DELTA.: rusting and blistering on 10 to 50% of the total area
X: rusting and blistering on substantially entire area
From the test results shown in Table 8, it will readily be understood that coating compositions of the high exposure resistance type according to the present invention (Examples 20, 21, 23, 25, 27, 29 and 31) comprising a polyvinyl butyral resin, a phenolic resin, a mixture of a borate compound and a molybdate or a polyphosphate compound, a metal powder and phosphoric acid are superior to the conventional wash primer of the high exposure resistance type (Comparative Example 9) with respect to long lasting corrosion resistance. Further, it is apparent that since these coating compositions are chromium-free paints causing no pollution, they are far superior to the conventional wash primer of the high exposure resistance type with respect to operation safety, health maintenance and the effect of preventing environmental pollution. Moreover, it is seen that these coating compositions are superior or comparable to the conventional wash primer with respect to adaptability to the electroprint marking process. Still further, in view of the constituents of these coating compositions according to the present invention, it is apparent that they are much improved over the conventional zinc-rich paint with respect to weldability.
Chromium-free paints formed by replacing a zinc chromate pigment by other anticorrosion pigment in the conventional wash primer of the high exposure resistance type (Comparative Examples 10 to 12) are much inferior to the conventional wash primer with respect to corrosion resistance and they have no practical utility at all.
It will also be apparent that coating compositions of the etching type according to the present invention (Examples 33, 35, 37, 39, 41 and 43) comprising a polyvinyl butyral resin, a mixture of a borate compound and a molybdate or a polyphosphate compound, a metal powder and phosphoric acid are superior to the conventional wash primer to the etching type (Comparative Example 13), the composition including a borate alone (Comparative Example 14), The composition including a polyphosphate alone (Comparative Example 15) and the composition including zinc molybdate (Comparative Example 16) with respect to corrosion resistance, operation safety, health maintenance, the effect of preventing environmental pollution and adaptability to the electroprint marking process.

Number	Date	Country
51-45909	Apr 1976	JPX
51-134634	Nov 1976	JPX
52-15233	Feb 1977	JPX
52-15729	Feb 1977	JPX

Number	Name	Date
2818344	Buckman	Dec 1957
3272663	Kronstein	Sep 1966
3791850	Deshay et al.	Feb 1974
3892577	Sugahara et al.	Jan 1975

Anticorrosion primer coating composition

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (4)

US Referenced Citations (4)

Non-Patent Literature Citations (2)