Patent Application
20140199358
1. Field of the Invention
The present invention relates to antimicrobial polymer systems.
2. Related Art
Material surfaces of polymer products may become contaminated with disease-causing agents. For example, used in aqueous environments or environments where moisture is present, microbes may be transferred to the surface of the polymer products.
According to a first broad aspect, the present invention provides a product comprising: a polymer host matrix comprising polyurethane, and one or more antimicrobial organometallic additives dispersed throughout the polymer host matrix, wherein each of the one or more antimicrobial organometallic additives is water insoluble or sparingly soluble in water and comprises a long-chain fatty acid group, and wherein a majority of metallic species dispersed throughout the polymer host matrix are in the one or more antimicrobial organometallic additives.
According to a second broad aspect, the present invention provides a method comprising the following step: (a) mixing one or more antimicrobial organometallic additives with a liquid polyurethane at room temperature to form a polymer product comprising the one or more antimicrobial organometallic additives dispersed throughout the polymer host matrix, wherein each of the one or more antimicrobial organometallic additives is water insoluble or sparingly soluble in water and comprises a long-chain fatty acid group, wherein a majority of metallic species dispersed throughout the polymer host matrix are in the one or more antimicrobial organometallic additives.
According to a third broad aspect, the present invention provides a product comprising: a polymer host matrix comprising polyurethane, and one or more antimicrobial organometallic additives dispersed throughout the polymer host matrix, wherein the one or more antimicrobial organometallic additives comprise a mixture of two or more members of the group consisting of the following antimicrobial organometallic additives: silver stearate, cupric stearate and zinc stearate.
According to a fourth broad aspect, the present invention provides a product comprising: a substrate, and a thermoset powder coating on the substrate, wherein the thermoset powder coating comprises a polymer host matrix and one or more antimicrobial organometallic additives dispersed throughout the polymer host matrix, wherein each of the one or more antimicrobial organometallic additives is water insoluble or sparingly soluble in water and comprises a long-chain fatty acid group, and wherein a majority of the metallic species dispersed throughout the polymer host matrix are in the one or more antimicrobial organometallic additives.
According to a fifth broad aspect, the present invention provides a method comprising the following step: (a) heating a mixture on a substrate to melt the mixture to form a thermoset powder coating on the substrate, wherein the mixture comprises one or more antimicrobial organometallic powders mixed with a thermosetting powder, wherein the thermoset powder coating comprises a polymer host matrix and one or more antimicrobial organometallic additives dispersed throughout the polymer host matrix, wherein each of the one or more antimicrobial organometallic additives is water insoluble or sparingly soluble in water and comprises a long-chain fatty acid group, and wherein a majority of the metallic species dispersed throughout the polymer host matrix are in the one or more antimicrobial organometallic additives.
According to a sixth broad aspect, the present invention provides a product comprising: a substrate, and a thermoset powder coating on the substrate, wherein the thermoset powder coating comprises a polymer host matrix and one or more antimicrobial organometallic additives dispersed throughout the polymer host matrix, and wherein the one or more antimicrobial organometallic additives comprise a mixture of two or more members of the group consisting of the following antimicrobial organometallic additives: silver stearate, cupric stearate and zinc stearate.
According to a seventh broad aspect, the present invention provides a product comprising: a polymer host matrix comprising paraffin wax, and one or more antimicrobial organometallic additives dispersed throughout the polymer host matrix, wherein each of the one or more antimicrobial organometallic additives is water insoluble or sparingly soluble in water and comprises a long-chain fatty acid group, and wherein a majority of metallic species dispersed throughout the polymer host matrix are in the one or more antimicrobial organometallic additives.
According to an eighth broad aspect, the present invention provides a method comprising the following step: (a) mixing one or more antimicrobial organometallic additives with liquid paraffin wax to form a polymer product comprising the one or more antimicrobial organometallic additives dispersed throughout the polymer host matrix, wherein each of the one or more antimicrobial organometallic additives is water insoluble or sparingly soluble in water and comprises a long-chain fatty acid group, wherein a majority of metallic species dispersed throughout the polymer host matrix are in the one or more antimicrobial organometallic additives.
According to a ninth broad aspect, the present invention provides a product comprising: a polymer host matrix comprising paraffin wax, and one or more antimicrobial organometallic additives dispersed throughout the polymer host matrix, wherein each of the one or more antimicrobial organometallic additives is water insoluble or sparingly soluble in water and comprises a long-chain fatty acid group, and wherein the one or more antimicrobial organometallic additives comprise a mixture of two or more members of the group consisting of the following antimicrobial organometallic additives: silver stearate, cupric stearate and zinc stearate.
The accompanying drawings, which are incorporated herein and constitute part of this specification, illustrate exemplary embodiments of the invention, and, together with the general description given above and the detailed description given below, serve to explain the features of the invention. The sizes and the relative heights, widths, diameters, thicknesses, etc. of features in the drawings are not necessarily to scale unless specifically indicated otherwise. For example, in the drawings the thickness of a coating in the drawings may be shown thicker relative to the substrate on which the coating is coated to allow for details of the components of the coating to be better illustrated. Also in the drawings, organometallic additives are shown as being much larger than these components would be in the polymer host matrix in which these components are dispersed for ease of illustration. In the drawings, the organometallic additives are depicted as circles. This is only a schematic representation as the additive form factor of the present invention may be circular, spherical, linear, branched or other form factor.
Where the definition of terms departs from the commonly used meaning of the term, applicant intends to utilize the definitions provided below, unless specifically indicated.
For purposes of the present invention, it should be noted that the singular forms, “a,” “an,” and “the” include reference to the plural unless the context as herein presented clearly indicates otherwise.
For purposes of the present invention, directional terms such as “top,” “bottom,” “upper,” “lower,” “above,” “below,” “left,” “right,” “horizontal,” “vertical,” “up,” “down,” etc. are merely used for convenience in describing the various embodiments of the present invention. The embodiments of the present invention may be oriented in various ways. For example, the diagrams, apparatuses, etc. shown in the drawing figures may be flipped over, rotated by 90° in any direction, reversed, etc.
For purposes of the present invention, a value or property is “based” on a particular value, property, the satisfaction of a condition or other factor, if that value is derived by performing a mathematical calculation or logical decision using that value, property, the satisfaction of a condition or other factor.
For purposes of the present invention, the term “antimicrobial” refers to a material that kills or inhibits the growth of microorganisms such as bacteria, viruses, fungi, molds or protozoans.
For purposes of the present invention, the term “antimicrobial organometallic additive” refers to an organometallic additive that imparts antimicrobial properties to a product of which the antimicrobial organometallic additive is a part or increases the antimicrobial properties of a product of which the antimicrobial organometallic additive is a part.
For purposes of the present invention, the term “degree of antimicrobial activity” refers to the percentage reduction in Colony Forming Units (CFU) observed when a polymer product is subjected to JIS Z 2801 test protocol described below in the Examples section. For example, if a 99.99831% reduction in Colony Forming Units (CFU) is observed for a polymer product, the product has a 99.99831% degree of antimicrobial activity.
For purposes of the present invention, the term “dispersed throughout” refers to one or more antimicrobial organometallic additives being distributed relatively evenly throughout a polymer host matrix.
For purposes of the present invention, the term “long-chain fatty acid” refers to a fatty acid having an aliphatic tail of 13 or more carbon atoms.
For purposes of the present invention, the term “long-chain fatty acid group” refers to the ester group derived from a long-chain fatty acid. An example of a long-chain fatty acid group is a stearate group.
For purposes of the present invention, the term “majority” refers to a majority by molar amount. For example, if there were a mixture of antimicrobial organometallic additives comprising 1.0 mole of cupric stearate and 1.0 mole of silver stearate present in a polymer product, 0.1 total moles of metals in a UV absorber dispersed throughout the polymer product and 0.2 moles of metal ions in a color in the polymer product, the antimicrobial organometallic additives would constitute a majority of the metallic species in the polymer product: 2.0 total moles of antimicrobial organometallic additives to 0.3 total moles of metallic species from other sources dispersed throughout the polymer.
For purposes of the present invention, the term “metallic species” refers to the metals, metal ions and metal-containing compounds present in a polymer product, depending on the polymer product. In addition to the metals in the antimicrobial organometallic additive of the present invention, polymer products of the present invention may also include metallic species that are metals, metal ions and metal-containing compounds such as metal salts, metal oxides, organometallic oxides, etc.
For purposes of the present invention, the term “organometallic additive” refers to a compound including a metal bound to an organic radical, where the metal species has a valence state of +1, +2, +3, etc.
For purposes of the present invention, the term “polymer host matrix” refers to a polymer or mixtures of polymers in which one or more antimicrobial organometallic additives are dispersed. A polymer may be a copolymer. A polymer host matrix includes components in addition to the polymer that do not react with the organometallic additives dispersed in the polymer host matrix. For example, the polymer host matrix may be fiberglass which comprises a polymer having dispersed therein glass fibers. Other fibers, such as carbon or graphene, metals and ceramics may also be used, as well as polymer fibers such as Kevlar® (DuPont's registered trademark for a para-aramid synthetic fiber).
For purposes of the present invention, the term “room temperature” refers to a temperature of from about 20° C. to about 25° C.
For purposes of the present invention, the term “a solid solution in a polymer host matrix” refers to an organometallic additive mechanically dispersed throughout and suspended within the polymer host matrix.
For purposes of the present invention, the term “sparingly soluble in water” refers to a substance having a solubility of 0.1 g per 100 ml of water to 1 g per 100 ml of water. Unless specified otherwise, the term “sparingly soluble” and “sparingly soluble in water” are used interchangeably in the description of the invention below to refer to substances that are sparingly soluble in water.
For purposes of the present invention, the term “thermosetting powder” refers to a powder that when applied and subjected to heat will melt, flow and chemically crosslink to form a film coating on a substrate. Thermosetting powders are primarily composed of relatively high molecular weight solid resins and a crosslinker. The primary resins used in the formulation of a thermosetting powder are: epoxy, polyester and acrylic. These primary resins may be used with different crosslinkers to produce a variety of powder coatings.
For purposes of the present invention, the term “thermoset powder coating” refers to a film coating formed by melting, flowing and chemically crosslinking a thermosetting powder. Chemical reactions during the curing cycle of a thermoset powder coating create a polymer network which may provide resistance to coating breakdown. Once cured and crosslinked, this polymer network will not melt and flow again if heat is applied.
For purposes of the present invention, the term “water insoluble” refers to a substance that has a solubility of less than 0.1 g per 100 ml of water.
Because material surfaces may become contaminated with disease-causing agents, there is a need for materials with anti-bacterial, anti-virus, anti-fungal, anti-mold, etc. functionality; these are generally referred to as antimicrobials. Polymeric materials made from organic materials, inorganic materials or organic-inorganic material blends are ubiquitous in the environment, and if made to reduce antimicrobial disease-causing agents would play a valuable role in producing a healthier environment.
Three general classes of art for producing antimicrobial bulk polymers and polymer surfaces using additive systems currently exist: (1) nanoscale metal particles, (2) metal aluminosilicates, and (3) organic compounds. Although this art has demonstrated some utility it suffers from several limitations of which the following are the most often cited:
In addition to the above-mentioned limitations of the existing art, the current products employing metal and aluminosilicate antimicrobial additives: (a) are costly, (b) have final product process-related issues such as reduced time-to-fabrication tooling wear out, therefore requiring more frequent tool replacement, and (c) require novel chemical moieties as surface ligands to help disperse and keep the particles from settling or agglomerating. Furthermore, current products employ organic antimicrobial additives that cannot be readily incorporated with many organic materials since these antimicrobial additives are: (a) chemically aggressive and inhibit the reaction processes of many thermosets and (b) degrade the mechanical, thermal and optical properties of many thermoplastics and thermosets.
An example of existing art appears in United States Patent Application No. 2011/0002872 to Ohashi et al., but this patent application does not describe the final form of the product that integrates the antimicrobial invention, but instead describes a conversion process (e.g., thermal decomposition) of a fatty acid metal salt for forming ultrafine metal particles that can be dispersed in a resin for further processing.
In one embodiment, the present invention provides a polymer product comprising a polymer host matrix having dispersed therein at least one antimicrobial organometallic additive or a blend of antimicrobial organometallic additives that impart antimicrobial properties to the bulk and surface of the polymer host matrix.
In one embodiment, the present invention provides uniformly dispersed antimicrobial functionality in a variety of host matrix polymer materials and a broad range of form factors. For example, the dispersed antimicrobial organometallic additives may be used to impart antimicrobial properties to the bulk and surface of a polymer host matrix in the form of bulk polymer products, film polymer products, sheet polymer products, polymer coating products, coated polymer products, composite polymer products, fibrous polymer products, a rod polymer products, core-containing polymer products and other types of polymer products.
In one embodiment, the present invention provides a polymer product comprising a polymer host matrix having dispersed therein at least one distributed metal type of antimicrobial organometallic additive or a blend of antimicrobial organometallic additives of more than one type of metal, said antimicrobial organometallic additives imparting antimicrobial properties to the bulk polymer products, film polymer products, sheet polymer products, polymer coating products, coated polymer products, composite polymer products, fibrous polymer products, a rod polymer products, core-containing polymer products and other types of polymer products.
In one embodiment of the present invention, the antimicrobial organometallic additive is about 0.008% to about 3% by volume of the total volume of the mixture of the antimicrobial organometallic additive in the polymer host matrix. In one embodiment of the present invention, the antimicrobial organometallic additive is about 0.008% to about 2.5% by volume of the total volume of the mixture of the antimicrobial organometallic additive in the polymer host matrix. In one embodiment of the present invention, the antimicrobial organometallic additive is about 0.008% to about 2% by volume of the total volume of the mixture of the antimicrobial organometallic additive in the polymer host matrix.
In one embodiment of the present invention, the blend of the antimicrobial organometallic additive is about 0.008% to about 3% by volume of the total volume of the mixture of the antimicrobial organometallic additive in the polymer host matrix. In one embodiment of the present invention, the blend of the antimicrobial organometallic additive is about 0.008% to about 2.5% by volume of the total volume of the mixture of the antimicrobial organometallic additive in the polymer host matrix. In one embodiment of the present invention, the blend of the antimicrobial organometallic additive is about 0.008% to about 2% by volume of the total volume of the mixture of the antimicrobial organometallic additive in the polymer host matrix.
In one embodiment, the present invention provides the ability to integrate one or more antimicrobial organometallic additives comprised of metals that are compatible with a variety of host matrix polymer materials that can be processed using conventional manufacturing equipment to fabricate various types of polymer products. In one embodiment of the present invention, the antimicrobial organometallic additives form a solid solution with the polymer host matrix and are distributed homogeneously throughout the polymer. Furthermore, the polymer host matrix may be an organic material, an inorganic material (e.g., silicone, etc.) or an organic-inorganic material blend. Also, the polymer host matrix may demonstrate the physical properties of a solid material, a liquid material, or a material having both solid-like and liquid-like physical properties.
In one embodiment of the present invention, an antimicrobial organometallic additive is an organic chemical moiety chemically bonded to a metal, either covalently or ionically. The chemical structure provides for enhanced miscibility throughout the polymer host matrix to produce various types of polymer products. Organic chemical moieties that may be bound to a metal in an antimicrobial organometallic additive of the present invention include but are not limited to the following chemical moieties: hydrocarbons, acetates, stearates, laureates, palmitates, oleates, abietates, fatty acids, etc.
Metals that may be used in the antimicrobial organometallic additives of the present invention include, but are not limited to, copper (Cu), silver (Ag), gold (Au), iridium (Ir), palladium (Pd), platinum (Pt), iron (Fe), nickel (Ni), cobalt (Co), zinc (Zn), niobium (Nb), ruthenium (Ru), rhodium (Rh), tellurium (Te), antimony (Sb), bismuth (Bi), tin (Sn), gallium (Ga), indium (In), titanium (Ti), vanadium (V), chromium, (Cr), manganese (Mn), molybdenum (Mo), tungsten (W), tantalum (Ta), hafnium (Hf), zirconium (Zr), scandium (Sc), and yttrium (Y), aluminum (Al), cadmium (Cd), mercury (Hg), thalium (Tl), lead (Pb), selenium (Se).
Metals that may be used in the antimicrobial organometallic additives of the present invention include alkali metals and alkali earth metals including, but are not limited to lithium (Li), sodium (Na), potassium (K), rubidium (Rb) cesium (Cs), beryllium (Be), magnesium (Mg), calcium (Ca), strontium (Sr), and barium (Ba).
Metals for the antimicrobial organometallic additives may be selected based on required functionality (e.g., anti-bacterial, anti-virus, anti-fungal, anti-mold, etc.) and may be chosen from the categories of transition metals, post-transition metals, metalloids, lanthanides, actinides, rare earth metals, alkaline earth metals, and alkali metals.
Suitable polymers that may be used in the polymer host matrix of the polymer products of the present invention include thermoplastics and thermosets and mixtures thereof.
In one embodiment of the present invention, the polymer host matrix may comprise a thermoplastic such as polyethylene (PE), polypropylene (PP), polycarbonate (PC), polystyrene (PS), polyamide (PA), polybutylene terephthalate (PBT), polyethylene terephthalate (PET), wax (e.g., paraffin, etc.), etc. In one embodiment, the polymer host matrix polymer may be a blend comprising more than one thermoplastic.
In one embodiment of the present invention, the polymer host matrix may comprise a thermoset plastic such as an epoxy, a phenolic, a cyanate ester, a bismaleimide, a polyimide, an acrylic, a silicone, a urethane, a latex, etc. In one embodiment, the polymer host matrix polymer may be a blend comprising more than one thermoset.
In one embodiment of the present invention, the polymer host matrix may comprise a polyurethane. The polymer host matrix may be a one-part polyurethane liquid polymer or a two-part polyurethane liquid polymer. The polyurethane polymer host matrix may be air cured, thermally cured, or UV-radiation cured.
In one embodiment of the present invention, the polymer host matrix may comprise a stable dispersion (emulsion) of polymer microparticles in an aqueous medium such as, but not limited to natural and synthetic latexes. The polymer host matrix may be a single polymer, a polymer blend, a co-polymer, or a co-polymer blend.
In one embodiment of the present invention, the polymer host matrix may comprise a mixture of a polymer and other materials such as glass. For example, the host matrix may be fiberglass which is a plastic matrix reinforced with fine glass fibers.
In various embodiments of the present invention, the polymer host matrix of the present invention may be formulated to achieve specific materials properties e.g., optical (clarity, refractive index, color, transparency), mechanical (elongation, glass transition temperature, coefficient of thermal expansion, elastic and shear modulus, toughness, adhesion, surface roughness), rheological (viscosity, melt flow index, surface energy, etc.), electrical (dielectric strength) and antimicrobial efficacy as required for optimal end product performance.
During thermal processing of the polymer host matrix and the antimicrobial organometallic additive, the antimicrobial organometallic additive may be converted to an organometallic-oxide.
In one embodiment, the present invention may be used as a bulk polymer product. In one embodiment, the present invention may be used as a polymer film. In one embodiment, the present invention may be used as a polymer sheet.
Bulk polymer products such as but not limited to master blends, toys, electronic housings, automotive interior panels, airplane passenger compartment structures, dental appliances such as mouth protectors, mouth guards, dentures and retainers, corrective vision devices (contact lenses, contact lens storage containers, eye glass frames), windows, aquarium walls, soap dispensers, paper towel dispensers, toilet paper dispensers, portable toilets, and portable washing stations. In these products, the host matrix bulk polymer provides substantial structural integrity for the device or application.
Film polymer products include but are not limited to flexible wrapping agents, film coats, and laminates. These products may have surface treatments to provide static or chemical adhesion as commonly used for promotional advertising, and marketing posters and labels. Film materials may be used in combination with touch screens and displays. Another example of a film polymer product is currency (banknotes). Furthermore, the film may be transparent, contain graphic art, text, or a combination of these. In these products, the film polymer provides little structural integrity to the device, but acts as a barrier or as a carrier of graphic information. In one embodiment, the film material is less than 0.1 mm thick.
Although one antimicrobial organometallic additive is shown in
The polymer product of
A polymer product of the present invention that is a block of material may be made in various shapes such as spherical, rectangular box-shaped, cube-shaped, ellipsoid-shaped, cone-shaped, pyramidal, rod-shaped, ring-shaped, disks, rectangular plate-shaped, irregularly shaped, etc. A spherical or nearly spherical polymer product may be used in balls for purifying liquids such as but not limited to water and water-based fruit juices and forming master batches for draw-down during manufacture of the final polymer product. A spherical or nearly spherical polymer product may be fabricated with different densities so that polymer product may float at different levels in a liquid environment.
In one embodiment, the polymer product of
In one embodiment, the polymer product of
In one embodiment, the polymer product of
In one embodiment the present invention provides polymer coatings comprising one or more antimicrobial organometallic additives uniformly dispersed in a polymer material. Such coatings may have a variety of uses such as for powder coats, paints, shrink wraps, films, etc. In polymer coatings, the polymer coating may act as a surface protector and barrier. The polymer coatings of the present invention may be used on a variety of substrates such as carts, hospital gurneys, desks, chairs, metal gratings, shelving (e.g., refrigerator, produce, dairy, candy, and health care products), filters, and corrugated metal such as used for architectural wall finishing, etc. Polymer coatings of the present invention may also be coated on substrates such as gratings, animal cages, livestock fencing, animal feeding containers (bowls, troughs, plates, dispensers), filters, architectural wall finishing, privacy walls in bathrooms, hand dryers, hand rails and escalator guard rails). A polymer coating of the present invention may be transparent, translucent or opaque and may be colored with dyes (e.g., organic polymers, inorganic suspensions). A polymer coating host matrix that is transparent has a refractive index of at least 1.1 at 633 nm with optical transmission of >90% from 375 to 600 nm. In one embodiment of the present invention, a coating may be less than 1 mm thick.
A polymer coating of the present invention may be formed by mixing one or more antimicrobial organometallic additive in powder form with a polymer host matrix material in powder form, such as a thermosetting powder, to form a mixture in which the one or more antimicrobial organometallic additives are dispersed throughout the mixture. The mixture may then be heated to melt the mixture and form a polymer coating product in which the one or more antimicrobial organometallic additives are suspended in the polymer host. The coating product may be heated in place on the substrate to form a coating or the coating product may be heated and then applied to the substrate as a coating.
A polymer coating of the present invention may be formed by mixing one or more antimicrobial organometallic additive in powder form with a polymer host matrix material in liquid form to form a mixture in which the one or more antimicrobial organometallic additives are dispersed throughout the liquid. The liquid mixture may then be applied to a substrate to form a polymer coating product in which the one or more antimicrobial organometallic additives are suspended in the polymer host. The coating product may be heated in place on the substrate to form a coating, polymerized on the substrate using ultraviolet radiation (UV) to form a coating, dried via evaporation of solvent to form a coating, polymerized on the substrate via chemical reactions (i.e., curing) to form a coating. Examples of polymer host materials are latex paints, oil-based paints, 1-part polyurethane, 2-part polyurethane, 1-part epoxy, 2-part epoxy, etc.
Although three antimicrobial organometallic additives are shown in the polymer coating of
The substrate on which a polymer coating of the present invention is coated may be a metal such as aluminum, titanium, copper, brass, bronze, nickel, pewter, silver, gold, stainless steel, carbon steel, steel, molybdenum, Inconel, alloys of these metals, etc., a ceramic such as aluminum oxide (sapphire), ceramic tile, glass (borosilicate, soda-lime-silicate, quartz), granite, marble, etc., a plastic such as a vinyl polymer, polycarbonate, polyethylene, polypropylene, PEN, PET, wax (paraffin) etc, or any other type of suitable substrate material.
In one embodiment, the present invention provides a composite product including one or more antimicrobial organometallic additives in a polymer host matrix. Such composite products include fabrics, bandages, tents, mats (e.g., wrestling, gymnastics, bathroom), tarps, clothing used by first responders, clothing used by campers, clothing used for recreational purposes, work clothing, sports clothing, uniforms, space suits, military operations personnel, healthcare professionals, and hospital staff (e.g., surgical garments), etc. In a composite product of the present invention, a discrete layer or film comprising the one or more antimicrobial organometallic additives in a polymer host matrix is integrated into the composite product. A polymer layer comprising one or more antimicrobial organometallic additives in a polymer host matrix acts as a surface protector and barrier. The barrier functionality of such a polymer layer may include transmission of liquid such as water, and gases such as water vapor and air. In one embodiment, such a polymer layer is less than 1 mm thick.
Although the edge coating in
Although in
Although three antimicrobial organometallic additives are shown in the polymer layer and the edge coating of
The polymer host matrix and the antimicrobial organometallic additives of the polymer layer and the edge coating may be the same or different.
In one embodiment of the present invention, the polymer layer of a composite product may have a thickness of 10 mm or less.
In one embodiment of the present invention the outer layer and inner layer of the composite product may be porous to allow transmission of liquids such as water, and gases such as water vapor and air to the polymer layer.
The inner and outer layers may be made from a variety of materials including woven or non-woven textiles such as silk, cotton, polymer textiles or blends thereof, high strength plastics such as but not limited to poly-paraphenylene terephthalamide (e.g., Kevlar®), and metals such as but not limited to aluminum, titanium, copper, brass, bronze, nickel, pewter, silver, gold, stainless steel, carbon steel, steel, molybdenum, Inconel, alloys of these metals, etc., a ceramic such as aluminum oxide (sapphire), ceramic tile, glass (borosilicate, soda-lime-silicate, quartz), granite, marble, etc., a plastic such as a vinyl polymer, polycarbonate, polyethylene, polypropylene, PEN, PET, wax (paraffin) etc., or any other type of suitable substrate material.
Although the edge coating in
Although in
Although three antimicrobial organometallic additives are shown in the lower polymer layer, upper polymer layer and the edge coating of
The polymer host matrix and the antimicrobial organometallic additives of the lower polymer layer, upper polymer layer and the edge coating may be the same or different for each of the lower polymer layer upper polymer layer and the edge coating.
In one embodiment of the present invention, the lower polymer layer and/or upper polymer layer of a composite product may have a thickness of 1 mm or less.
In one embodiment of the present invention the inner layer of the composite product may be porous to allow transmission of liquids such as water, and gases such as water vapor and air to the polymer layer.
The inner layer may be made from a variety of materials including woven or non-woven textiles such as silk, cotton or blends thereof, high strength plastics such as but not limited to poly-paraphenylene terephthalamide (e.g., Kevlar®), and metals such as but not limited to aluminum, titanium, copper, brass, bronze, nickel, pewter, silver, gold, stainless steel, carbon steel, steel, molybdenum, Inconel, alloys of these metals, etc., a ceramic such as aluminum oxide (sapphire), ceramic tile, glass (borosilicate, soda-lime-silicate, quartz), granite, marble, etc., a plastic such as a vinyl polymer, polycarbonate, polyethylene, polypropylene, PEN, PET, wax (paraffin) etc., or any other type of suitable substrate material.
Although the edge coating in
Although in
Although three antimicrobial organometallic additives are shown in the lower polymer layer, upper polymer and the edge coating of
The polymer host matrix and the antimicrobial organometallic additives of the lower polymer layer upper polymer layer and the edge coating may be the same or different for each of the lower polymer layer upper polymer layer and the edge coating.
In one embodiment of the present invention, the lower polymer layer and/or upper polymer layer of a composite product may have a thickness of 1 mm or less.
In one embodiment of the present invention, the lower inner layer, middle inner layer and/or upper middle layer of the composite product may be porous to allow transmission of liquids such as water, and gases such as water vapor and air to the polymer layer.
The lower inner layer, middle inner layer and/or upper middle layer may each be made from a variety of materials including woven or non-woven textiles such as silk, cotton, polymer textiles or blends thereof, high strength plastics such as but not limited to poly-paraphenylene terephthalamide (e.g., Kevlar®), and metals such as but not limited to aluminum, titanium, copper, brass, bronze, nickel, pewter, silver, gold, stainless steel, carbon steel, steel, molybdenum, Inconel, alloys of these metals, etc., a ceramic such as aluminum oxide (sapphire), ceramic tile, glass (borosilicate, soda-lime-silicate, quartz), granite, marble, etc., a plastic such as a vinyl polymer, polycarbonate, polyethylene, polypropylene, PEN, PET, wax (paraffin) etc., or any other type of suitable substrate material.
In one embodiment, the present invention may be a fiber polymer product. Fiber polymer products of the present invention may be used in various types of products such as floor coverings (e.g., carpets, rugs), artificial turf (e.g., residential, athletic, landscaping), window shades and draperies, privacy curtains, wall coverings (e.g., wall paper), seating upholstery, air filters, water filters, thread, fabric, cloth, clothing, textiles, etc.
In one embodiment of the present invention, a fiber polymer product may have a diameter of 10 mm or less.
In one embodiment, the present invention may be a rod polymer product. Rod polymer products of the present invention may be used in such products as a guard rails, hand rails (e.g., for a banister, escalator), door handles, grab bars, shower rods, shopping cart handles, extruded products, facemasks for helmets, electrical wiring, etc. The rod form may be modified to form belts, or have multiple surfaces, detents, notches, flats, indents, etc.
In one embodiment of the present invention, a rod polymer product may have a diameter of 10 mm or greater.
Although three antimicrobial organometallic additives are shown in the polymer product of
Although the cross-sectional shape of the polymer product shown in
In one embodiment, the present invention may be a reinforced fiber polymer product. Reinforced fiber polymer products of the present invention may be used in various types of products such as floor coverings (e.g., carpets, rugs), artificial turf (e.g., residential, athletic, landscaping), window shades and draperies, privacy curtains, wall coverings (e.g., wall paper), seating upholstery, air filters, water filters, electrical wiring, thread, fabric, cloth, clothing, textiles, etc.
In one embodiment of the present invention, a reinforced fiber polymer product may have a diameter of 10 mm or less.
In one embodiment, the present invention may be a rod polymer product. Rod polymer products of the present invention may be used in such product as a guard rails, hand rails (e.g., for a banister, escalator), door handles, grab bars, shower rods, shopping cart handles, extruded products, facemasks for helmets, electrical wiring, etc. The rod form may be modified to form belts, or have multiple surfaces, detents, notches, flats, indents, etc.
In one embodiment, a reinforced rod polymer product may have a diameter of 10 mm or greater.
Although three antimicrobial organometallic additives are shown in the reinforced polymer product of
Although the cross-sectional shape of the reinforced polymer product and support structure shown in
The length of a support structure relative to a reinforced polymer product may be the same as the reinforced polymer product, shorter than the reinforced polymer product or longer than the reinforced polymer product. A reinforced polymer product may also include more than one support structure that may be arranged along the same axis in the reinforced polymer product and/or along different axes in the reinforced polymer product and/or scattered throughout the reinforced polymer product.
The support structure of a reinforced polymer product may form the bulk of a reinforced polymer product. The support structure of a reinforced polymer product may be made of various materials such as a metal, ceramic, a plastic material, etc. or combinations thereof, depending on the desired property of the reinforced polymer product.
Spherical or nearly spherical products may be used in purifying liquids such as water, water-based fruit juices, etc. Pelletized polymer products used as the feedstock in the manufacture of final polymer products by thermal injection molding, extrusion, etc., can also have spherical or near spherical form. The spherical or nearly spherical products may be fabricated with different densities so that they may float at different levels in a liquid environment. Non-spherical shapes, such as but not limited to rods, rings, disks, rectangular plates, pyramidal and other geometries may also be used.
A polymer product of the present invention that is a core-containing polymer product may be made in various shapes such as spherical, rectangular box-shaped, cube-shaped, ellipsoid-shaped, cone-shaped, pyramidal, rod-shaped, ring-shaped, disks, rectangular plate-shaped, irregularly shaped, etc. A spherical or nearly spherical polymer product may be used in balls for purifying liquids such as but not limited to water, water-based liquids, water-based fruit juices, milk, etc. Pelletized polymer products used as the feedstock in the manufacture of final polymer products, for example, thermal injection molding, extrusion, etc., can also have spherical or near spherical form. A spherical or nearly spherical polymer product may be fabricated with different densities so that the polymer product may float at different levels in a liquid environment.
A core-containing polymer product of the present invention may have various shapes such as spherical (as shown in
A core-containing polymer product of the present invention may have various shapes such as spherical (as shown in
The antimicrobial organometallic additive in any of the polymer products and/or any portion and/or layer of a polymer product of the present invention may be at various ratios with respect to each other. For example, when a blend of three antimicrobial organometallic additives are dispersed in a polymer host matrix of the present invention, the ratio of the antimicrobial organometallic additives may be 1:1:1, 1:2:1, 2:3:4, or any other suitable ratio.
In one embodiment, the antimicrobial organometallic additives are a majority of the metallic species present in a polymer host matrix of a polymer product of the present invention. In some embodiments of the present invention there may be low levels of metals or metal ions present from other additives dispersed throughout the polymer host matrix (e.g., UV protectors, colorants, etc.). In some embodiments of the present invention, the antimicrobial organometallic additives may be the only metallic species present in a polymer host matrix of a polymer product of the present invention.
In one embodiment, the antimicrobial polymer products of the present invention include antimicrobial organometallic additives that are water insoluble or sparingly soluble in water. A single water insoluble or sparingly insoluble antimicrobial organometallic additive may be employed or mixtures of water insoluble and/or sparingly soluble antimicrobial organometallic additives may be employed. In one embodiment of the present invention, the water insoluble antimicrobial organometallic additives may comprise a long-chain fatty acid group as their organic component. Such compounds include, metal stearates and mixtures thereof. Suitable metal stearates that provide antimicrobial activity to a polymer product include, silver stearate, cupric stearate, zinc stearate, etc., and mixtures thereof. One advantage of using water insoluble antimicrobial organometallic additives having a long-chain fatty acid group as their organic component is that that they should provide long-lasting antimicrobial activity to polymer products, even when the polymer products are exposed to moisture or immersed in water. The water insolubility of such additives and the presence of the long-chain fatty acid group should cause such additives to stay bound and/or complexed in the polymer of the polymer product and not leach into the moisture or water. This is different than that for water soluble antimicrobial organometallic additives, for example, acetate based systems.
In one embodiment, the present invention provides a polyurethane product having antimicrobial activity that may be made by mixing one or more antimicrobial organometallic additives of the present invention with a liquid polyurethane at room temperature.
In one embodiment, the present invention provides a powder coat product, such as a thermoset powder coating. A thermoset powder coating may be formed by mixing one or more antimicrobial organometallic additives in powder form with a thermosetting powder to form a powder mixture. The powder mixture is then applied to a substrate and heated to melt, flow and chemically crosslink the components of the thermosetting powder in the powder mixture to form a thermoset film coating on the substrate. The thermoset coating has the one or more antimicrobial organometallic additives dispersed therein. The temperature that is used to form the thermoset film coating depends on the particular components of the thermosetting powder. In one embodiment, the temperature used to form the thermoset film coating is from 170° C. to 215° C.
In one embodiment of the present invention, the polymer host matrix may be paraffin wax. A paraffin wax product of the present may be formed by mixing one or more antimicrobial organometallic additives with liquid paraffin wax at temperature of 37° C. to 100° C. to form a paraffin wax product having the one or more antimicrobial organometallic additives dispersed throughout the polymer host matrix.
The present invention will now be described by way of example.
The testing of antimicrobial activity for the polymer samples in Examples 1, 2, 3, 4, 5, 6, 7, 8 and 9 below is performed using the Antimicrobial Test Laboratories' JIS Z 2801 Test for Antimicrobial Activity of Plastics. A summary of the JIS Z 2801 Test procedure is provided below:
Composition 1. Silver stearate powder is added to a clear coat powder coat material supplied by The Finishing Company, Addison, Ill. Thermosetting powders are composed of relatively high molecular weight resins, typically blends of epoxy, polyester and acrylic, with crosslinking agents and color additives as required. Suppliers include DuPont, BASF, etc. The silver stearate powder and clear coat powder are then mixed vigorously to disperse the silver stearate powder in the clear coat powder and to form a powder blend. The powder blend is 2.5% silver stearate and 97.5% clear coat powder by volume. An approximately 5 ml sample of this powder blend is placed in an aluminum foil dish. The sample is heated at 380° F. for 10 minutes and then removed from the oven to cool. The sample is tested for antimicrobial activity using the JIS Z 2801 test procedure. A 99.99996% reduction in Colony Forming Units (CFU) is observed for this sample. The silver stearate powder used in this example has a particle size of less than 25 μm. The clear coat powder used in this example has a particle size of less than 25 μm.
Composition 2. Cupric stearate powder is added to a clear coat powder coat material supplied by The Finishing Company, Addison, Ill. The cupric stearate powder and clear coat powder are then mixed vigorously to disperse the cupric stearate powder in the clear coat powder and to form a powder blend. The powder blend is 2.5% cupric stearate and 97.5% clear coat powder by volume. An approximately 5 ml sample of this powder blend is placed in an aluminum foil dish. The sample is heated at 380° F. for 10 minutes and then removed from the oven to cool. The sample is tested for antimicrobial activity using the JIS Z 2801 test protocol. A 99.99996% reduction in CFU is observed for this sample. The cupric stearate powder used in this example has a particle size of less than 25 μm. The clear coat powder used in this example has a particle size of less than 25 μm.
Composition 3. Cupric stearate powder and silver stearate powder are added to a clear coat powder coat material of supplied by The Finishing Company, Addison, Ill. The cupric stearate powder and clear coat powder are then mixed vigorously to disperse the cupric stearate powder and silver stearate powder in the clear coat powder and to form a powder blend. The powder blend is 1% cupric stearate, 1% silver stearate and 98% clear coat powder by volume. The powder blend is deposited via an electrostatic powder coat process onto stainless steel test coupons to form a sample. The sample is tested for antimicrobial activity using the JIS Z 2801 test protocol. A 99.99994% reduction in CFU is observed for this sample. The cupric stearate powder used in this example has a particle size of less than 25 μm. The silver stearate powder used in this example has a particle size of less than 25 μm. The clear coat powder used in this example has a particle size of less than 25 μm.
Composition 4. Cupric acetate powder supplied by Sigma-Aldrich, St. Louis. Mo. is added to a clear coat powder coat material supplied by The Finishing Company, Addison, Ill. The cupric acetate powder and clear coat powder are then mixed vigorously to disperse the cupric acetate powder in the clear coat powder and to form a powder blend. The powder blend is 2.8% cupric acetate and 97.2% clear coat powder by volume. An approximately 5 ml sample of this powder blend is placed in an aluminum foil dish. The sample is heated at 380° F. for 10 minutes and then removed from the oven to cool. The sample is tested for antimicrobial activity using the JIS Z 2801 test protocol. A 99.99831% reduction in CFU is observed for this sample. The cupric acetate powder used in this example has a particle size of less than 25 μm. The clear coat powder used in this example has a particle size of less than 25 μm.
Composition 5. Silver acetate powder supplied by Sigma-Aldrich, St Louis, Mo. is added to a clear coat powder coat material supplied by The Finishing Company, Addison, Ill. The silver acetate powder and clear coat powder are then mixed vigorously to disperse the silver acetate powder in the clear coat powder and to form a powder blend. The powder blend is 2.8% silver acetate and 97.2% clear coat powder by volume. An approximately 5 ml sample of this powder blend is placed in an aluminum foil dish. The sample is heated at 380° F. for 10 minutes and then removed from the oven to cool. The sample is tested for antimicrobial activity using the JIS Z 2801 test protocol. A 99.99831% reduction in Colony Forming Units (CFU) is observed for this sample. The silver acetate powder used in this example has a particle size of less than 25 μm. The clear coat powder used in this example has a particle size of less than 25 μm.
The thermoset powder coatings of Examples 1, 2, 3, 4 and 5, i.e., Compositions 1, 2, 3, 4 and 5, demonstrate that cupric stearate, silver stearate and mixtures of cupric stearate and silver stearate are compatible with thermoset powder coatings and provide antimicrobial properties to the thermoset powder coating.
Composition 6. Silver stearate powder and cupric stearate powder were added to commercial polypropylene pellets (supplied by a commercial manufacturer). A 2% by volume powder blend was produced (1% silver stearate and 1% cupric stearate) with about 1 pound of polypropylene pellets. The samples were thermal injection molded into disks by a commercial manufacturer following standard industry processes for polypropylene. The sample is tested for antimicrobial activity using the JIS Z 2801 test protocol and 99.99989% reduction in Colony Forming Units (CFU) is observed for this sample. The silver stearate powder used in this example had a particle size of less than about 25 μm. The cupric stearate powder used in this example had a particle size of less than about 25 μm. The polypropylene pellet size was about 4 mm.
Composition 7. Silver stearate powder and cupric stearate powder were added to commercial polypropylene pellets (supplied a commercial manufacturer). A 0.2% by volume powder blend was produced (0.1% silver stearate and 0.1% cupric stearate) with about 1 pound of polypropylene pellets. The samples were thermal injection molded into disks by a commercial manufacturer following standard industry processes for polypropylene. The sample is tested for antimicrobial activity using the JIS Z 2801 test protocol and 99.76966% reduction in Colony Forming Units (CFU) is observed for this sample. The silver stearate powder used in this example had a particle size of less than about 25 μm. The cupric stearate powder used in this example had a particle size of less than about 25 μm. The polypropylene pellet size was about 4 mm. This demonstrates that the volume fraction of additive can produce different efficacy levels in the final product. This enables optimization for a variety of product attributes e.g. cost, efficacy, processing, and performance via permutations of the metal and organic components.
The injection molded products of Examples 6 and 7, i.e., Compositions 6 and 7, demonstrate that cupric stearate and silver stearate mixtures are compatible with injection molded polymer products and provide antimicrobial properties to the injection molded polymer product.
Composition 8. Cupric stearate powder and silver stearate powder was added to 2-part commercial polyurethane (Envirotex Lite Pour-on High Gloss Finish Polyurethane, Environmental Technology, Inc, Fields Landing Calif. 95537) at room temperature. A 1.1% by volume powder blend was produced (1% cupric stearate and 0.1% silver stearate) with the liquid polyurethane. The polyurethane was cast over a test coupon per the manufacturer's directions. The sample is tested for antimicrobial activity using the JIS Z 2801 test protocol and 99.99997% reduction in Colony Forming Units (CFU) is observed for this sample.
Composition 9. Cupric stearate powder and silver stearate powder was added to 1-part commercial water-based polyurethane (Hanson Group, Atlanta Ga.). A 1.1% by volume powder blend was produced (1% cupric stearate and 0.1% silver stearate) with the liquid water-based polyurethane at room temperature. The polyurethane was spray deposited over a test coupon per the manufacturer's standard operating procedures. The sample is tested for antimicrobial activity using the JIS Z 2801 test protocol and 99.99982% reduction in Colony Forming Units (CFU) is observed for this sample.
The polyurethane coatings of Examples 8 and 9, i.e., Compositions 8 and 9, demonstrate that cupric stearate and silver stearate mixtures are compatible with polyurethane and provide antimicrobial properties to a polyurethane coating. Composition 9 also demonstrates that a polyurethane including the antimicrobial organometallic additives cupric stearate and silver stearate may be deposited as a coating on a substrate via spray deposition techniques, the spray deposition techniques used in Example 9 being different that the electrostatic-based powder coat process technique described above in Example 3.
This enables optimization of the antimicrobial organometallic additives used for a variety of product attributes e.g. cost, efficacy, processing, and performance via permutations of the metal and organic components. The results for various embodiments of the present invention employing organometallic stearate additives in host polymers are summarized in
Y=b+(a−b))/(1+10(X−c)) (Equation 1)
where Y is the Log Reduction result derived from the JIS Z 2081 test protocol, X is the concentration of the antimicrobial organometallic additive and parameters a=−2.306×106, b=6.769 and c=−5.530. Equation 1 is a type of dose reduction model, and the fitted data has a chi-square value of 1.163 and an R-square value of 0.975, indicating a reasonable fit to the data. Other equations or systems of equations can also be used, for example the sum of a linear function to approximate the slowly varying concentration “plateau region” plus a polynomial function to approximate the smoothly increasing section of the data set prior to the “plateau region.”
Similar to
The data in
Composition 10. Cupric stearate powder and silver stearate powder was added to commercial food grade paraffin wax (Gulf Wax Household Paraffin Wax, distributed by Royal Oak Enterprises, LLC, Roswell, Ga. 30076). A 1.1% by volume powder blend was produced (1% cupric stearate and 0.1% silver stearate) by adding the powders to molten wax at a temperature of about 90° C. The molten wax mixture was deposited over a paper substrate (butcher paper). The sample coated the substrate in a uniform manner Immersion in water for 48 hours did not cause the paper substrate of wax-coated paper to wet. It is expected that this sample will have antimicrobial activity similar to the antimicrobial activity of the samples described above in Examples 1, 2, 3, 4, 5, 6, 7, 8 and 9.
All documents, patents, journal articles and other materials cited in the present application are incorporated herein by reference.
Having described a particular embodiment of the present invention, it will be apparent that modifications and variations are possible without departing from the scope of the invention as defined in the appended claims. Furthermore, it should be appreciated that all examples provided in the present disclosure, while illustrating a particular embodiment of the invention, are provided as non-limiting examples and are, therefore, not to be taken as limiting the various aspects so illustrated.
While the present invention has been disclosed with references to certain embodiments, numerous modifications, alterations and changes to the described embodiments are possible without departing from the sphere and scope of the present invention, as defined in the appended claims. Accordingly, it is intended that the present invention not be limited to the described embodiments, but that it has the full scope defined by the language of the following claims and equivalents thereof.
This application claims benefit of priority to U.S. Provisional Patent Application No. 61/751,940 to Chason et al., entitled “ANTI-MICROBIAL POLYMER SYSTEMS USING MULTIFUNCTIONAL ORGANOMETALLIC ADDITIVES,” filed Jan. 14, 2013 which is incorporated herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61751940 | Jan 2013 | US |