Antioxidants of bisphenolic polymers

BACKGROUND OF THE INVENTION
Olefin polymers are particularly subject to severe deterioration from the oxidative action of air at elevated temperatures. They are also vulnerable to degradation by the action of ionizing radiation when large amounts of such radiation are deposited into the polymer, e.g., amounts of 5 .times. 10.sup.10 ergs per gram and higher. Oxidative deterioration at elevated temperatures is manifested by surface crazing, then cracking and ultimately a complete embrittlement.
It is known that small amounts of some antioxidants, e.g., 4,4'-thiobis(6-5-butyl-m-cresol), can be added to polyolefins and more particularly to polyethylenes to prevent or impede these degradative effects without the contribution of color to the polymer. However, such conventional antioxidants are not effective under conditions of high vacuum and/or high temperatures since with time the antioxidant volatilizes away from the substance into which it was incorporated.
Until recently, the volatility of such antioxidants in a crosslinked polyolefin composition was undesirable primarily because of the reduction in oxidative stability which occurred as the antioxidant volatilized away.
The use of crosslinked polyolefin materials in space vehicles has brought to light a still more important disadvantage of these antioxidant materials. When used in a space vehicle, a crosslinked polyolefin material, employed for example in the form of electrical wire installation on solar panel wiring or in front of tubing, may be exposed to solar radiation in the hard vacuum of space such that the polyolefin may be heated to temperatures as high as 125.degree. to 150.degree. C. Under such conditions, most of the prior art antioxidants, such as those previously mentioned, will be volatilized away. Since optical systems in the space vehicle, shielded to solar radiation, may be at a relatively low temperature, perhaps 10.degree. C., the gas formed from the antioxidant will condense on the optical system thereby adversely effecting its transmitive and reflective optical characteristics. Furthermore, the heated polyolefin with its antioxidant-radiation protectant volatilized away is now vulnerable to radiolytic degradation such as that which may be caused by energetic solar protons.
It is also known that certain polymeric involatile materials may be used as antioxidants. Thus, certain phenolformaldehyde polymers may be used as antioxidants. Also, bisphenols and triphenols such as those described in U.S. Pat. No. 3,247,262 may be used to protect against oxidative degradation. The bis and triphenols are still volatile, however. The phenol-formaldehyde resins, which have lower volatility, have disadvantages including thermosetting characteristics of the phenol-formaldehyde antioxidant, choice of precursors on the basis of synthetic convenience rather than antioxidant capability and a pronounced tendency to impart coloration to polymers to which they are added.
U.S. Pat. No. 3,133,899 to Kwiatek proposes the copper chloride-catalyzed oxidative polymerization of a thiobisphenol to form polymeric ethers of formula ##SPC1##
the thiobisphenols employed having the formula ##SPC2##
wherein at least one R on each phenolic group is alkyl, the other being alkyl or hydrogen, alkyl in every case preferably having 1 to 3 carbon atoms. Should those R groups be of more than 3 carbon atoms, the work of Hay et al. in J.A.C.S. 81,6335 (1959) with oxidative coupling of 2,6-disubstituted phenols would suggest that the Kwiatek procedure would yield diphenoquinones as the sole product. Such materials form undesirable color bodies when blended in olefinic polymers and the like.
Braus et al., in U.S. Pat. No. 3,462,375 disclose antioxidant compositions of formula ##SPC3##
but the values assigned Z.sub.1-2, Y.sub.1-3 and M.sub.1-3 make clear that it is a phenol-substituted benzene compound rather than a bisphenolic polymer which is proposed. Again, in U.S. Pat. Nos. 3,377,333 and 3,044,960, respectively, to Ciesielski et al. and Norway et al. alkyl-substituted thiophenolic polymers are disclosed whose repeating units are, e.g., ##SPC4##
Such polymers are distinguished from the bisphenolic polymers of the present invention by, inter alia, the characteristic lack in the former of direct carbon-carbon bonding between the phenolic rings of adjoining thiobisphenolic repeating units.
SUMMARY OF THE INVENTION
According to this invention, there are provided antioxidants and antioxidant-containing polymer compositions, the antioxidants having the formula ##STR1## wherein n is from about 2 to 12 and wherein for each repeat unit, Z and X are independently selected from the group consisting of ##SPC5##
R.sub.2 and R.sub.3 being independently hydrogen or alkyl, cycloalkyl, aryl or alkaryl groups having from 1 to 8 carbon atoms, R.sub.4 being alkyl of 4 to 8 carbon atoms, preferably tertiary alkyl and Y is selected from the group consisting of sulfur methylene and butylidene. It has been found that the controlled oxidative coupling reaction of certain bisphenolic compounds will produce a non-volatile compound which is surprisingly effective as an antioxidant. The polymeric antioxidants of the present invention are generally colorless or only very slightly colored and thus may be used at relatively high levels, i.e., 1% in polymers such as polyolefins without causing undue coloration in the finished fabricated article. The antioxidants of the invention are resistant to the effects of high temperature and high vacuum and are capable of imparting radiation resistance to polymeric compounds.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
The low molecular weight phenolic compounds suitable as precursors in this invention have the following formulae: ##SPC6##
wherein R.sub.1 is hydrogen; R.sub.2 and R.sub.3 are independently selected from the group consisting of hydrogen or alkyl, cycloalkyl, aryl or alkaryl groups having from 1 to 8 carbon atoms, R.sub.4 is an alkyl group having from 4 to 8 carbon atoms and Y is selected from the group consisting of sulfur, methylene or butylidene. R.sub.4 is preferably tertiary alkyl, i.e., at least one carbon atom is substituted only by carbon. Phenolic moieties whose valence bonds to sulfur are para to hydroxyl, such as compound (2) above are preferred from the standpoint of avoiding coloration of polymers in which the antioxidants of the invention are employed.
The low molecular weight bisphenolic compounds suitable for use as precursors in this invention may be selected from a wide variety of available phenolic compounds which have antioxidant properties, e.g., 4,4' methylene bis(6-t-butyl-m-cresol); 4,4' thiobis (6-t-butyl-m-cresol); 4,4' butylidene bis(6-t-butyl-m-cresol); 2,2'-methylene bis (6-t-butyl-m-cresol); 2,2' thiobis (6-t-butyl-m-cresol); 2,2'-butylidene-bis(6-t-butyl-m-cresol). These and other bisphenolic precursors suitable in this invention may be conventionally prepared by, e.g., reaction of one or more phenolic compounds with sulfur mono- or dichloride; by the reaction of olefin and a suitable thiobisphenol in the presence of an alkylation catalyst, etc.
The precursor used to produce the antioxidants of the present invention must have available at least one unsubstituted ortho or para position relative to the phenolic hydroxyl groups. For example, in 4,4'-thiobis(6-t-butyl-m-cresol) there are two ortho positions unsubstituted.
Normally, oxidative coupling yields a mixture of molecular species of varying length (e.g., n ranges from 2 to about 12), n average for the mixture being from about 2 to about 10, preferably from about 2 to about 7, and most preferably from about 2 to about 4.
The antioxidants of the present invention are useful in polymers generally and particularly olefin polymers and copolymers such as polyethylene, polypropylene, polyisoprene, ethylene-propylene copolymers, acrylic polymers such as polyethyl acrylate and other polymers such as polyamides, Teflon, etc., which are known to be stabilized by hindered phenols. The antioxidant can be incorporated in effective amounts into the polymer by conventional methods such as hot milling, mixing in a Banbury mixer, extrusion, etc. Normally, from about 1 to about 10 percent by weight of antioxidant is employed, based upon the weight of the normally oxidizable polymer.
The final polymeric systems containing these polymeric stabilizers are particularly suitable where it is desired to crosslink by the use of ionizing radiation because these stabilizers do not appreciably inhibit crosslinking as compared with the low molecular weight precursors and are more resistant to radiation damage.
The coupling reactions suitable for use in this invention include oxidative coupling of the bisphenols by oxidizing agents such as K.sub.3 Fe(CN).sub.6, chromic acid, organic peroxides, manganese dioxide, potassium permanganate, potassium dichromate and electrolytic oxidation. Coupling agents which do not form molecular oxygen upon decomposition are employed to avoid formation of undesirable by-products. Coupling may take place in situ although it is preferred to perform the coupling reaction under conditions such that the structure and nature of the resulting antioxidant can be controlled to prevent undesirable side reactions.
It has been found that the antioxidant polymer of this invention is particularly effective if it is formed using a ferricyanide coupling agent, e.g., K.sub.3 Fe(CN).sub.6. The increased effectiveness obtained by this method may be due to the fact that undesirable by-products are substantially reduced. Thus, other coupling systems may produce by-products which detract from the effectiveness of the antioxidant. In any event, the antioxidants prepared with K.sub.3 Fe(CH).sub.6 do exhibit increased effectiveness when compared with antioxidants of this invention prepared from the same precursors with other oxidizing agents.
Any suitable ferricyanide may be used in the coupling reaction, e.g., K.sub.3 Fe(CN).sub.6, Na.sub.3 (CN).sub.6, etc. The molar ratios of ferricyanide to bisphenol may vary from about 0.5 to 2 with the preferred ratio being about 1.33 to 1.
Increasing the ratio of ferricyanide to bisphenol will increase the molecular weight of the antioxidant. At a ratio of 1.33 to 1, the resulting polymeric antioxidant will contain an average of about 3 bisphenol units. The molecular weight can also be controlled by controlling the reaction period, a shorter reaction time resulting in lower molecular weights.
The ferricyanide may be added to the bisphenol as a water solution. Addition may be dropwise or the entire water solution may be added at once to the bisphenol dissolved in an organic solvent.
It is important to maintain the pH of the reaction solution near 7. Thus, the pH may vary from about 5 to 9 without any substantial adverse effect. In order to maintain the pH at the desired level, an acid acceptor or buffer such as sodium carbonate or bicarbonate can be used. In general, any acid acceptor which will maintain the pH near 7 may be used.
The reaction temperature should be maintained at as low a level as possible. Thus the temperature should be maintained below about 80.degree. C. and preferably below about 50.degree. C. If the temperature is allowed to exceed 80.degree. C., discoloration of the polymer and decreased antioxidant effectiveness may result.
The oxidative coupling using an organic peroxide can be accomplished either in solution or in situ by adding the peroxide to a polymer containing an antioxidant precursor. Suitable peroxides include t-butyl perbenzoate, dicumyl peroxide, benzoyl peroxide, 2,5-dimethyl-2,5-bis(t-butyl-peroxy)hexane, 2,5-dimethyl-2,5-di(t-butyl-peroxy)hexyne-3, t-butyl-peroxy-isopropyl carbonate, etc.
Suitable solvents in which the coupling with organic peroxide can be carried out include cyclohexane, benzene, toluene, xylene, chlorobenzene, etc. In general, the preferred solvent with peroxides is xyxlene, because of its lower vapor pressure at the convenient decomposition temperature of the peroxide. Benzene is preferred when a ferricyanide coupling agent is used.
The molar ratio of peroxide to the antioxidant precursor should be maintained between a lower limit of about 0.5 and an upper limit of about 2 to 1 with a ratio of about 0.9 to 1 being preferred.
The present invention is further illustrated by the following examples in which parts are by weight unless otherwise indicated.
The effectiveness of the antioxidant was measured by temperature programmed differential thermal analysis in oxygen. In this technique, which has been described by V. E. Althouse (Am. Chem. Soc., Div. Polymer Chem. Preprints 4, (1), 256 (1963)), the temperature of a polymer sample containing a certain percentage of the antioxidant is increased at a uniform rate (in this case, 61/4.degree. per minute) with a constant flow of oxygen, until an autocatalytic oxidation (accompanied by an exotherm) occurs. The temperature at which the oxidation exotherm appears has been shown to be proportional to the logarithm of the concentration of an antioxidant and to indicate to a degree its effectiveness as an antioxidant.
The temperature at which an oxidative exotherm occurred (hereafter known as the DTA temperature) was measured by the above procedure on the polymer samples as prepared, and also after the samples has been maintained at 200.degree. C. for 66 hours in a slow stream of argon. It is found that lower molecular weight antioxidants, such as 4,4'-thiobis (6-t-butyl-m-cresol), are substantially volatilized out of the polymer sample after such an aging procedure. Consequently, the DTA temperature of such samples is drastically reduced by this treatment. On the other hand, the involatile antioxidants prepared according to the practice of this invention show very little change in DTA temperature after such a treatment.
Hence, the difference in DTA temperature before and after aging in argon affords a sensitive means of measuring volatility of an antioxidant. Furthermore, because the temperature is logarithmically related to antioxidant concentration, a small difference in temperature can reflect a large difference in antioxidant concentration as shown in the table below.
______________________________________Relationship Between DTA Tem-perature and Concentration of4,4'-thiobis(6-t-butyl-m-cresol) Approximate DTAConcentration % Temperature .degree. C.______________________________________.01 2420.1 2590.3 2680.5 2731.0 2782.0 282______________________________________

EXAMPLES 1-2
These examples illustrate formation of my polymeric antioxidants in situ. The antioxidant was formed by milling the bisphenol and peroxide into polyethylene and curing at 172.degree. C. Both mixes contained 1 part per hundred of t-butyl perbenzoate which was equivalent to 1.04 mol per mol of bisphenol used. Comparative runs were made using the same formula except that the peroxide was omitted. The resulting compositions were compared by a differential thermal analysis comprising heating a reference and the antioxidant-containing sample at the same rate. Volatility of the antioxidant was indicated by comparing the DTA values before and after heat aging. The results are set forth in Table I.
TABLE I__________________________________________________________________________Antioxidant Color DTA Performance .degree. C.__________________________________________________________________________ With Peroxide Without Peroxide__________________________________________________________________________ Before AfterExample Type p.h.r. Cure Cure Unaged Argon Aged Unaged Argon Aged__________________________________________________________________________1 4,4'-butylidene- 2.1 White White 261.2 252.9 263.5 232.7 bis(6-t-butyl-m- cresol)2 4,4'-thiobis(6-t- 2.0 White Light 285.7 284.1 281.6 266.1 butyl-m-cresol) Yellow__________________________________________________________________________
EXAMPLES 3-22
The method of Example 1 was repeated using various peroxides and 4,4' -thiobis(6-t-butyl-m-cresol). The results are set forth in Table II. It is seen that maximum retention of performance after aging in argon results when the weight ratio of peroxide to antioxidant precursor is between 1 and 2 to 1, the actual optimum value varying with the peroxide used.
TABLE II__________________________________________________________________________Peroxide DTA Temperatures Cure Time atExample Type p.h.r. 340.degree. F. (min.) Unaged Argon Aged__________________________________________________________________________3 No peroxide -- 10 281.6 260.34 Lupersol 101.sup.1 0.7 10 285.2 277.15 Lupersol 101 .8 10 285.4 281.36 Lupersol 101 .9 10 285.8 281.37 Lupersol 101 1.0 10 286.1 281.68 Lupersol 101 1.2 10 285.9 281.59 Lupersol 101 1.4 10 285.4 282.210 Lupersol 101 1.6 10 286.8 283.811 Lupersol 101 0.4 10 283.5 274.712 Lupersol 101 0.8 10 286.3 276.013 Lupersol 101 1.6 10 285.7 281.214 Lupersol 101 2.4 10 283.4 280.815 Lupersol 130.sup.2 0.4 20 283.6 263.416 Lupersol 130 0.8 20 284.3 278.417 Lupersol 130 1.2 20 284.8 281.018 Lupersol 130 1.6 20 285.3 284.119 Dicumylperoxide 1.3 10 285.6 283.620 Dicumylperoxide 1.5 10 285.3 283.021 Dicumylperoxide 1.75 10 285.0 283.522 Dicumylperoxide 2.0 10 284.0 284.3__________________________________________________________________________ .sup.1 2,5-Dimethyl-2,5-bis(t-butyl peroxy)hexane .sup.2 2,5-Dimethyl-2,5-di(t-butyl peroxy)hexyne-3
EXAMPLES 23-26
These examples illustrate preparation of the polymeric antioxidant in a solvent. A mixture of 4,4'-thiobis(6-t-butyl-m-cresol) and di-t-butyl peroxide in xylene under nitrogen was heated in an autoclave and the product evaporated to dryness. The conditions are described in Table III. The molecular weight of the antioxidant polymer was determined by the freezing technique known as Beckman's method and set forth in Glasstone, Textbook of Physical Chemistry, 2 Ed (1947), 646-47. Molecular weight measurements in this experiment were made on 5% solutions in benzene.
The resulting polymeric antioxidant was incorporated into polyethylene and the DTA exotherm temperature was determined.
TABLE III__________________________________________________________________________ DTA Exotherm Temperature .degree. C__________________________________________________________________________ Thiobisphenol Concentration Temperature Time Yield MolecularExample kg. gms/100 mls .degree. C Hrs. % Weight Unaged Argon Aged__________________________________________________________________________23 0.108 14.5 155-160 2 105 876 287.5 283.224 4.0 16.2 160 6 101 880 287.9 286.825 15.0 35.8 160-167 3 101 1,287 283.5 285.126 0.324 43.9 160-163 31/2 102 640 284.5 284.1__________________________________________________________________________
EXAMPLES 27-31
These examples illustrate the effect of pH on the polymer properties obtained using a ferricyanide to prepare the antioxidants. In Examples 27-31, the ferricyanide was dissolved in 80% of the water used and added dropwise over 3 hours to a mixture of 4,4'-thiobis(6-t-butyl-m-cresol), benzene, an acid acceptor, and the remaining water. Molecular weights of the product were determined according to the method of Example 23.
TABLE IV__________________________________________________________________________ Thiobisphenol K.sub.3 Fe(CN).sub.6 Water Benzene MolecularExample g. g. Type pH g. mls. mls. Weight Appearance__________________________________________________________________________27 100 90 NaOH 7-11 20 300 200 663 Light green28 120 146 NaOH 7-11 30 400 200 860 Green brown29 120 146 Na.sub.2 CO.sub.3 8-10 60 500 200 890 Deep yellow30 120 146 NaHCO.sub.3 6-8 42 500 200 900 Light yellow31 120* 146 NaHCO.sub.3 6-8 42 500 200 944 Very light yellow__________________________________________________________________________ *The thiobisphenol used in this example had been recrystallized from benzene-cyclohexane.
EXAMPLES 32-39
The following examples illustrate the effect of varying reaction conditions on the molecular weight, color and DTA performance of the antioxidant. The reaction conditions set forth in Example 27 were followed except that in Examples 37, 38 and 39, the ferricyanide solution was added in one hatch at the beginning of the reaction. All experiments used analytical reagent grade benzene except 39 which used a technical grade. Experiments 38 and 39 used technical grade ferricyanide while the others used analytical reagent grade ferricyanide. The molar ratio of ferricyanide to thiobisphenol in the above experiments is uniformly about 1.33 to 1. The results are set forth below in Table V.
TABLE V__________________________________________________________________________ D.T.A. Thiobisphenol Ferricyanide NaHCO.sub.3 Benzene Water Temp. Molecular PerformanceExample g. g. g. ml. ml. .degree. C Color Weight Unaged__________________________________________________________________________ .degree. C.32 300 365 105 650 1250 15-30 Lt. Yellow 922 289.033 300 365 105 650 1250 50 Yellow 977 289.434 500 608 175 1080 2218 35 Lt. Yellow 937 288.635 1250 1520 437 2100 5000 35 Lt. Yellow 1000 288.536 300 365 105 650 1000 25 Lt. Yellow 955 289.837 1500 1824 520 2500 4500 35-50 Lt. Yellow 289.338 300 365 105 650 1000 35 Lt. Yellow 92439 300 365 105 650 1000 35 Lt. Yellow__________________________________________________________________________
EXAMPLES 40-45
Polymeric antioxidants made according to the present invention were incorporated into polyethylene at various levels irradiated to 10 megarads, except the 2 p.h.r. level which was given a dose of 20 megarads. The irradiated products were evaluated for heat aging characteristics and modulus of elasticity at a variety of temperatures. The results are shown in Table VI and Table VII. The compositions in Table VI and Table VII were prepared in slab form, except for the 2 p.h.r. values which were prepared in the form of 0.125 in i.d., 0.020 in thick tubing.
The time to crack on flexing was determined by heating the samples to the indicated temperature for the indicated time and bending them through 180.degree. with cracking observed visually. The values in Table VI represent the average of the times to slight cracking and the times to serious cracking.
The elastic modulus was determined above the melting point of the polymer by statically loading strips of polymer and measuring the strain. The initial slope of the resulting stress-strain curve was taken as the elastic modulus.
These examples illustrate the marked advantage of polymeric antioxidants at high concentrations and elevated temperatures. At lower concentration, oxidation occurs so rapidly that the effect of volatilization is masked. At lower temperatures, volatilization is not a problem.
TABLE VI__________________________________________________________________________Time to Crack on Flexing at 155.degree. C and 175.degree. CAntioxidant Concentration (p.h.r.) 0.063 0.125 0.25 0.5 1.0 2.0__________________________________________________________________________Example Type 155.degree. 175.degree. 155.degree. 175.degree. 155.degree. 175.degree. 155.degree. 175.degree. 155.degree. 175.degree. 200.degree.__________________________________________________________________________40 4,4'-thiobis(6-t- 71 29 144 41 271 79 623 172 >600* 320 78 butyl-m-cresol)41 A 71 30 154 48 293 94 752 220 >600* 490 13042 B 69 29 160 50 374 86 793 217 >600* 580 162__________________________________________________________________________ NOTE: A was prepared from 4,4'-thiobis(6-t-butyl-m-cresol) using di-t-butyl peroxide as shown in Example 23 while B was prepared using potassium ferricyanide as in Example 35. *These tests were abandoned after all samples at the 1% level had withstood 600 hours at 155.degree. C without cracking.
TABLE VII______________________________________Modulus (p.s.i.) at 160.degree. C.______________________________________Antioxidant Concentration (p.h.r.)Ex-ample Type 0.0 0.063 0.125 0.25 0.5 1.0 2.0______________________________________43 4,4'-thiobis(6-t- 30 -- 10 10 7 7 21 butyl-m-cresol)44 A -- -- 33 19 19 9 5645 B -- -- 21 15 17 9 69______________________________________
EXAMPLES 46-51
A further series of thiobisphenolic antioxidants were prepared as shown in Table VIII, following the procedure of Examples 27-31, supra. Molecular weight values reported are number average molecular weights determined by vapor phase osmometry.
TABLE VIII__________________________________________________________________________Antioxidants Based on 4,4'-thiobis-(6-t-butyl-3-methylphenol)__________________________________________________________________________ Potassium 4,4'-thiobis- Sodium MolecularExample Ferricyanide (6-t-butyl-3-methylphenol) Bicarbonate Wt. (g.) (g.) (g.)__________________________________________________________________________46 906 660 246 169747 970 660 263 239348 810 660 220 107649a 2040 1500 553 136049b 2040 1500 553 149050 1930 1500 524 118951a 2170 1500 590 145051b 2170 1500 590 1869__________________________________________________________________________
The duplicate preparations 49a and 49b were combined together for testing (average molecular weight 1430) and labelled 49. Similarly 51a and 51b were combined, (M.W. 1660) and labelled 51.
The antioxidants shown in Table VIII were blended into a low density polyethylene (DFD 6040, Union Carbide Corp.) irradiated to various dose levels and the elastic modulus (Young's modulus) at 160.degree. C measured. The samples irradiated to 20 mrads dose were hung in a circulating air oven at 185.degree. C, and their room temperature elongation measured after various exposure times. One sample containing tetrakis [methylene 3-(3',5'-di-t-butyl-4'-hydroxyphenyl) propionate] methane (Irganox 1010) was included in these tests for comparison purposes. All antioxidants were incorporated into DFD 6040 (0.2 M.I.; 0.92 density) at the 2% w/w level.
TABLE IX__________________________________________________________________________ Elastic Modulus Elongation at room temperature at 160.degree. C after after days at 185.degree. CAntioxidant Mol. Wt. 10 20 40 60 mrads 0 8 14 17 21__________________________________________________________________________50 1190 5 13 40 63 560 290 230 105 6049 1430 6 16 44 77 550 340 190 125 6551 1660 5 16 47 81 540 360 180 110 3047 2390 6 18 51 86 550 290 170 105 25Irganox 1010 -- 7 18 48 73 520 <20 <20 -- --__________________________________________________________________________
EXAMPLES 52- 57
Other oligomeric antioxidants were prepared from 4,4'-butylidene-bis(6-t-butyl-3-methylphenol) as in the previous example. Table III shows the recipes used in the preparation and the molecular weights of the products, determined as in Examples 46- 51. Preparations were based on 1500 g. of the antioxidant starting material. 4700 ml. of dearated water was used in each reaction to dissolve the salts.
TABLE X______________________________________ Potassium SodiumSample Ferricyanide Bicarbonate MolecularNo. (g.) (g.) Benzene Wt.______________________________________52 1840 500 5400 123053 2040 553 5400 179054 1940 500 5400 146055 1840 500 5400 124056 1650 500 6500 134057 1750 500 6500 1610______________________________________
Certain of the foregoing antioxidants were milled into polypropylene (Profax 6823; flow rate (g./10 min.), 0.4 (ASTM-D1238L); 0.903 density) and aged at 150.degree. C in a air circulation oven. The results are given in Table XI. Some of these materials were also blended with distearyl pentaerylthritol disphosphite and blended into polyethylene containing a polyfunctional monomer (triallyl isocyanurate). The irradiated samples were aged at 175.degree. C and the results are shown in Table XII.
TABLE XI__________________________________________________________________________ 1 2 3 4 5 6 7 8__________________________________________________________________________Profax 6823 99.7 99.7 99.7 99.7 99.7 99.7 99.7 99.7Irganox 1010 0.3 0.075 -- -- -- -- -- --Dilauryl Thio-dipropionate -- 0.225 -- -- -- 0.225 0.225 0.225Sample 52 -- -- 0.3 -- -- 0.075 -- --Sample 53 -- -- -- 0.3 -- -- 0.075 --Sample 55 -- -- -- -- 0.3 -- -- 0.075 Average ultimate elongation (at 2"/min.) following heat aging at 150.degree. C, %Original 500-530%4 weeks 267 355 450 320 210 -- 210 --5 weeks 225 333 367 330 -- 450 170 --6 weeks 180 320 350 -- -- 390 -- 2907 weeks -- 250 -- -- -- 243 100 300__________________________________________________________________________
TABLE XII______________________________________Samples irradiated to 25 mrads 1 2 3 4 5______________________________________DFD 6040 95 95 95 95 95Triallyl Isocyanurate 3 3 3 3 3Irganox 1010 2 -- -- -- --Distearyl pentaerythritoldiphosphite -- 1 1 1 1Sample 52 -- -- 1 -- --Sample 53 -- -- -- 1 --Sample 55 -- -- -- -- 1M100 at 160.degree. C, psi 91 36.5 83 85 86Average elongation (at 2"/min.) after heat aging (at 175.degree. C, %Original >500%1 day 310 447 333 253 3102 days 277 420 320 177 2824 days 140-280 367 283 <20 2707 days <20 <20 30-300 <20 293______________________________________
The above examples are not to be construed as limiting but merely illustrative of the scope of the present invention. Thus, it can be seen that the antioxidants of the present invention can be formed from a wide variety of bisphenol materials. The antioxidants are generally effective in all polymers, particularly those which are known to be stabilized by hindered phenols, and they can be incorporated in such polymers by conventional methods such as hot milling, mixing in a Banbury mixer, extrusion, etc.

Number	Name	Date	Kind
3637809	Kleiner	Jan 1972
3743623	Kleiner	Jul 1973

	Number	Date	Country
Parent	150831	Jun 1971
Parent	660198	Aug 1967

Antioxidants of bisphenolic polymers

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

CROSS-REFERENCE TO RELATED APPLICATIONS

US Referenced Citations (2)

Continuation in Parts (2)