Antireflection coated refractory metal matched emitters for use in thermophotovoltaic generators

Abstract

Thermophotovoltaic (TPV) electric power generators have emitters with infrared (IR) outputs matched with usable wavelengths for converter cells. The emitters have durable substrates, optional refractory isolating layers, conductive refractory metal or inter-metallic emitter layers, and refractory metal oxide antireflection layers. SiC substrates have tungsten or TaSi2 emitter layers and 0.14 micron HfO2, ZrO2, Al2O3, Ta2O5 and TiO2 antireflection layers used as IR emitters for GaSb converter cells in TPV generators.

Description

BACKGROUND OF THE INVENTION

Recently, low bandgap photovoltaic cells such as the GaSb cell have made it possible to produce practical thermophotovoltaic (TPV) electric power generators. The low bandgap cells in these TPV generators convert infrared (IR) radiation from heated (IR) emitters into electric power. The IR emitters in these units operate at moderate temperatures between 900° C. and 1400° C. Baseline commercial TPV generators use gray-body SiC emitters with GaSb cells. The SiC emitter emits infrared energy at all wavelengths. However, the GaSb cells convert only infrared photons with wavelengths less than 1.8 microns to electric power. Infrared filters are used to reflect some of the non-useful longer wavelength photons back to the emitter. Unfortunately, the available filters are far from perfect. Some non-convertible infrared radiation still passes through the filters, and some of the reflected photons do not hit the emitter after reflection by the filter.

It is preferable to replace the gray-body emitter with a “matched” infrared emitter that emits only convertible infrared radiation. Mathematically, this perfect “matched” emitter has an emittance of 1.0 for wavelengths less than 1.8 microns and 0 for longer wavelengths. Several prior art infrared emitters have been proposed for use in TPV generators.

The oldest type of IR emitter proposed is the rare earth oxide selective emitter. Erbia is an example of this type of emitter. While the emittance at 1.5 microns can be as high as 0.5, the emittance for erbia falls to 0.1 at 1.4 and 1.6 microns and rises again beyond 3 microns. The result is that the emitted useful power is small because of the narrow emittance bandwidth. Furthermore, the spectral efficiency, defined as the in-band convertible power divided by the total emitted power, is low because a lot of power is emitted at wavelengths beyond 3 microns.

Refractory metal IR emitters, such as tungsten, have also been described. Those materials are somewhat selective in that the emittance at 1.5 microns (typically 0.3) is higher than the emittance at longer wavelengths (0.15 at 3 microns). Unlike the oxide emitters, the emittance stays low at long wavelengths (0.1 at 6 microns). Unfortunately, these metal emitters need to run very hot because of the low in-band emittance. They also produce volatile oxides when operated in air.

Recently, JX Crystals has described a cobalt doped spinel “matched” emitter. This “matched” emitter has an emittance of 0.7 at 1.5 microns with a large bandwidth. This emitter is selective, because the emittance falls off to 0.25 at 3 microns. Unfortunately, however, like all oxide emitters, the emittance rises again beyond 6 microns.

There are other disadvantages of the oxide emitters. Specifically, they are subject to cracking upon extensive thermal cycling, and they have poor thermal conductivity.

It is desirable to find an improved “matched” emitter with a high emittance at wavelengths below 1.8 microns and low emittance for all longer wavelengths. It is very desirable to find a “matched” emitter coating that may be applied to the current SiC emitter structures, since SiC is a proven material with good thermal conductivity and thermal cycle durability.

SUMMARY OF THE INVENTION

The invention provides a matched emitter which emits infrared radiation at 1.8 microns and less than 1.8 microns to match the wavelengths of photons that GaSb cells absorb and convert to electricity.

In one form, a refractory metal coating such as tungsten (W) having a thickness of about 4 microns or from about 1-6 microns is deposited on a durable high temperature substrate such as SiC. The W coating may be isolated chemically from the substrate by a refractory oxide coating, such as HfO 2 , Ta 2 O 5 , ZrO 2 or Al 2 O 3 , so that it does not react with the substrate. The W coating is coated with a high index refractory oxide coating of a thickness such that a minimum reflectivity occurs in the center of the cell convertible wavelength band. This refractory oxide coating serves as an anti-reflection (AR) coating. The thickness of the oxide coating is specifically set to produce an absorption (emission) peak in the TPV cell conversion wavelength band.

In another embodiment, a refractory inter-metallic coating such as TaSi 2 is deposited on a durable high temperature substrate such as SiC. The metal silicide coating may be isolated chemically from the substrate by a refractory oxide coating, such as Ta 2 O 5 , so that it does not react with the substrate. In the case that the durable substrate is SiC, the inter-metallic coating can be a refractory compound containing a metal such as Ta along with Si and C. Alternative inter-metallic compounds may include Pd m (Si 1-x C x )or Pt m (Si 1-x C x ) n . The metal silicide is coated with a high index refractory oxide coating of a thickness such that a minimum reflectivity occurs in the center of the cell convertible wavelength band. This refractory oxide coating serves as an anti-reflection (AR) coating. The thickness of the oxide coating is specifically set to produce an absorption (emission) peak in the TPV cell conversion wavelength band.

Key elements in this concept are the reflecting metallic or inter-metallic coating, the AR coating, and the durable substrate. In the case of a TPV generator using GaSb cells, this AR wavelength is about 1.4 microns. A spacer layer may be provided between the substrate and metallic layers to prevent interaction of the two.

A typical thickness for the metal silicide is approximately 4.0 microns, while a typical thickness for the refractory oxide AR coatings is approximately 0.14 microns. Various substrates are possible including but not limited to SiC, Ta, NICHROME (alloys of nickel, chromium and iron), KANTHAL (heat resistant metal alloys) and stainless steel. Various metal silicides are possible including but not limited to TaSi 2 , NbSi 2 , TiSi 2 , and VSi 2 . Various refractory oxides are possible including, but not limited to, HfO 2 , Ta 2 O 5 , Al 2 O 3 , TiO 2 and ZrO 2 .

Adding Si to the Ta has two beneficial effects. First, the emittance at 1.5 microns increases from 0.3 to 0.55. Second, the silicides are more resistant to oxidation. Adding an AR coating then amplifies on these same two beneficial effects. The AR coating increases the emittance again from 0.55 to 0.98 at 1.5 microns, and the refractory oxide AR coating protects the structure from oxidation.

In another preferred embodiment, another AR coating includes, but is not limited to, hafnia (HfO 2 ) as the refractory oxide. Hafnia survives higher temperatures. Emissivity measurements show excellent spectral selectivity and no change in emissivity at temperatures up to 1300° C. This is consistent with the Ultramet data showing that hafnia has 10-100 times lower vapor pressures and evaporation rates at 1650° C. than either alumina or zirconia. Hafnia also has a lower thermal expansion coefficient (closer to tungsten) than alumina or zirconia and a high refractive index of 1.9, almost as good as zirconia (2.0) and higher than alumina (1.63). A higher index gives a higher emittance at the resonant peak.

The AR coated refractory metal “matched” emitters of the present invention are useable with cells other than the GaSb cell. They are adaptable to cells that respond out to 2.3 microns by simply shifting the thickness of the AR coating. They may be used in various environments including air, vacuum, or various inert atmospheres. They may be used with various heat sources, including not just hydrocarbon flames but also nuclear heat sources.

These and further and other objects and features of the invention are apparent in the disclosure, which includes the above and ongoing written specification, with the claims and the drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a side view of an AR coated refractory metal matched emitter.

FIG. 2 is a graph of the reflection curves for Ta, TaSi 2 and AR coated TaSi 2 .

FIG. 3 is the emittance curve for the refractory metal silicide matched emitter.

FIG. 4 is a graph of the emissive power for the refractory metal silicide matched emitter and a SiC (blackbody) emitter.

FIG. 5 is a graph of 2nk/λ vs wavelength for TaSi 2 .

FIG. 6 is a graph of 2nk/λ vs wavelength for several pure metals.

FIG. 7 shows a vertical section through a thermophotovoltaic generator.

FIG. 8 is a graph of the emissivity of hafnia AR coated tungsten.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

FIG. 1 shows the structure of the AR coated refractory metal “matched” emitter 1 of the present invention. A refractory metal or metal silicide emitter layer 2 , such as W or TaSi 2 , is deposited on a durable high temperature substrate 4 , such as SiC. The metal or metal silicide emitter layer 2 is isolated chemically from the substrate 4 by a refractory oxide 6 , such as HfO 2 , so that the emitter layer does not react with the substrate. Finally, the metal or metal silicide 2 is coated with a high index refractory oxide coating 8 of a thickness such that a minimum reflectivity occurs in the center of the cell convertible wavelength band. This refractory oxide coating 8 serves as an anti-reflection (AR) coating. In the case of a TPV generator using GaSb cells, this AR wavelength is about 1.4 microns. A typical thickness for the metal or metal silicide is approximately 4.0 microns for W or for the TaSi 2 . A typical thickness for the refractory oxide coatings is approximately 0.14 microns. Various substrates 4 are possible including, but not limited to, SiC, Ta, NICHROME, KANTHAL, and stainless steel. Various refractory metal emitters 2 are possible, including, but not limited to, W, Ta, Nb and Mo. Various metal silicides 2 are possible including, but not limited to, TaSi 2 , NbSi 2 , TiSi 2 , and VSi 2 . Various refractory oxides 6 and 8 are possible including, but not limited to, HfO 2 , Ta 2 O 5 , Al 2 O 3 , TiO 2 , and ZrO 2 .

The emitter structure 1 of FIG. 1 is effective as a “matched” emitter for TPV generators (shown in FIG. 7 ). This may be seen by reference to Tables 1, 2, and 3, and to FIGS. 2 , 3 , and 4 . Referring to table 1, the emittances for SiC, tungsten (W), and cobalt doped spinel at 1.5, 3, and 6 microns are given for reference. Refer now to the emittances of Ta, TaSi 2 , and AR coated TaSi 2 . The emittance of Ta by itself is similar to that of W. Adding Si to the Ta has two beneficial effects. First, the emittance at 1.5 microns increases from 0.3 to 0.55. Second, the silicides are more resistant to oxidation. Adding an AR coating then amplifies on these same two beneficial effects. Th AR coating increases the emittance again from 0.55 to 0.98 at 1.4 microns, and the refractory oxide AR coating protects the structure from oxidation.

FIG. 2 shows the reflection curves for Ta, TaSi 2 , and AR coated TaSi 2 as a function of wavelength. Note that while the reflectivity decreases at 1.5 microns, the reflectivity at long wavelengths remains high for our refractory metal silicide “matched” emitter.

Since the absorptance and emittance for metals are simply minus the reflectivity, FIG. 3 shows the emittance curve for our refractory metal silicide “matched” emitter.

Referring again to Table 1, note that the refractory meta silicide “matched” emitter of the present invention has the highest in-band emittance relative to all of the available emitters. This means that more electric power is producible for a given emitter temperature. Also note that the ratio of in-band emittance to out-of-band emittance for our AR coated refractor metal “matched” emitter is higher than for any other emitter. This leads to higher conversion efficiency.

FIG. 4 and Table 2 allow a comparison of a emitter with our refractory metal silicide “matched” emitter. FIG. 4 shows the emissive power as a function of wavelength for an AR-coated TaSi 2 emitter and a blackbody emitter with both operating at 1400° C. Table 2 gives the calculated values for the in-band emitted power, the out-of-band emitted power, and the spectral efficiency for these two emitters. Note that the in-band power is nearly the same for each, while the out-of-band power is reduced by a factor of 3 for the AR-coated TaSi 2 emitter. The spectral efficiency is increased by nearly a factor of 2.

The AR coated refractory silicide “matched” emitters of the present invention are useable with cells other than the GaSb cell. They are adaptable to cells that respond out to 2.3 micron wavelengths by simply shifting the thickness of the AR coating. They may be used in various environments including air, vacuum, or various inert atmospheres. They may be used with various heat sources, including not just hydrocarbon flames but also nuclear heat sources.

The matched emitter concept described here can be restated in more general terms as follows. Three elements are required: a durable refractory substrate 4 ( FIG. 1 ) with a refractory metallic (RM) coating 2 ( FIG. 1 ) with a resonant antireflection (AR) coating 8 (FIG. 1 ). In this three element system, the metallic coating 2 must be carefully chosen such that the 2nk/λ product for the material drops to 15 or lower at the desired resonant point and then rapidly rises for longer wavelengths. A spacer layer may be provided between the SiC and tungsten layers to prevent interaction of the two.

FIG. 5 shows a plot of 2nk/λ vs λ for TaSi 2 , while FIG. 6 shows plots of 2nk/λ vs λ for various pure metals. Referring to FIG. 6 suggests that pure Ta, W, Nb, or Mo could be used with an AR coating to create a matched emitter falling under the present invention. Pure Pd would not work because the AR coated resonance would be weak.

One of the best specific AR/RM is HfO 2 on W. Another consists of 4 microns of W on SiC followed by an AR coating of ZrO 2 . Yet another is Al 2 O 3 AR on W on SiC.

Referring to FIG. 7 , a thermophotovoltaic (TPV) generator 15 apparatus includes, in the order of energy flow, a heat source 3 , a matched coated infrared emitter 1 , an optional silica heat shield 7 , an infrared filter 9 and a low bandgap photovoltaic cell receiver 11 . The power band of the emitter 1 is matched with the energy conversion band of the TPV cells of the receiver 11 . The heat source 3 heats the infrared emitter 1 , which in turn emits infrared radiation. Low bandgap cells of the receiver 11 collect infrared radiation of a particular wavelength and convert the collected infrared radiation to electric power.

The refractory oxides include, but is not limited to, hafnia. Hafnia survives higher temperatures. FIG. 8 shows the emissivity of hafnia (HfO 2 ) AR on tungsten. Emissivity measurements show excellent spectral selectivity and no change in emissivity at temperatures up to 1300° C. This is consistent with the Ultramet data (Table 3) showing hafnia having 10-100 times lower vapor pressures and evaporation rates at 1650° C. than either alumina or zirconia. Hafnia also has a lower thermal expansion coefficient (closer to tungsten) than alumina or zirconia and a high refractive index of 1.9, almost as good as zirconia (2.0) and higher than alumina (1.63). A higher index gives a higher emittance at the resonant peak. A preferred combination includes a refractory metal coating of tungsten with a hafnia AR coating.

While the invention has been described with reference to specific embodiments, modifications and variations of the invention may be constructed without departing from the scope of the invention, which is defined in the following claims.

TABLE 1
Emittance Values for Various TPV Emitter Materials
	Material	ε at 1.5 μm	ε at 3 μm	ε at 6 μm
	SiC	0.8	0.85	0.9
	W	0.3	0.15	0.1
	Co/Spinel	0.7	0.25	0.7
	Ta	0.3	0.15	0.1
	TaSi 2	0.55	0.25	0.15
	AR/TaSi 2	0.98	0.28	0.15

TABLE 1
Emittance Values for Various TPV Emitter Materials
	Material	ε at 1.5 μm	ε at 3 μm	ε at 6 μm
	SiC	0.8	0.85	0.9
	W	0.3	0.15	0.1
	Co/Spinel	0.7	0.25	0.7
	Ta	0.3	0.15	0.1
	TaSi 2	0.55	0.25	0.15
	AR/TaSi 2	0.98	0.28	0.15

TABLE 3
Refractory Oxides
Ultramet has developed processes for fabricating coatings of the oxides of hafnium (HfO 2 ),
zirconium (ZrO 2 ), tantalum (Ta 2 O 5 ), titanium (TiO 2 ), alumninum (Al 2 O 3 ), silicon (SiO 2 ) and yttrium
(Y 2 O 3 ). These oxides can be applied by CVD as a 100% dense, pinhole-free coating to a variety of
materials, including refractory metals, ceramics, and composites. Used for high temperature oxidation
and corrosion resistance (e.g. sulfur, vanadium), these coatings are capable of extending either the
service life or operating temperature capability of many components, including rocket nozzles, piston
heads and liners, turbine blades, and fuel-fired heat exchanger components.
	ThO 2	HfO 2	ZrO 2	Y 2 O 3	Al 2 O 3	SiO 2
MELTING TEMPERATURE (° C.)	3050	2810	2700	2460	2015	1728
DENSITY (g/cc)	9.86	9.68	5.60	5.03	3.98	2.32
THERMAL EXPANSION (ppm/° C.)	9.5	6.8	7.5	6.8	8.1	0.5
OXIDATION LIMIT (° C.)	2700	2500	2500	2200?	2015	1680
LIMIT of STABILITY w/CARBON (° C.)	2000	1700	1600	—	1900	—
VAPOR PRESSURE (Pa)
(×10 −6 ) @ 1650° C.	9.41	0.13	10.6	—	133	—
(×10 −5 ) @ 1927° C.	138	3.93	127	—	50	—
(×10 −3 ) @ 2200° C.	77.0	3.26	78.7	—	22	—
EVAPORATION RATE (μm/hr)
(×10 −6 ) @ 1650° C.	540	6.7	670	—	—	—
@ 1927° C.	0.74	.019	0.75	—	—	—
@ 2200° C.	39	1.4	44	—	—	—
CRYSTAL STRUCTURE	FCC*	FCC*	FCC*	BCC	HCP	CT
OXYGEN PERMEABILITY (g/cm-sec)	—	460	120	9.5	—	—
(×10 −13 ) @ 1000° C.

Claims

1. Antireflection coated matched emitters for thermophotovoltaic cells, comprising a durable high temperature substrate, a tungsten film emitter coating on the substrate, and an antireflection metal oxide coating on the tungsten film wherein the metal oxide coating is HfO2.

2. The matched emitters of claim 1, wherein the tungsten coating is about 4 microns in thickness.

3. The matched emitters of claim 2, wherein the substrate is sic.

4. The matched emitters of claim 1, further comprising a refractory oxide coating on the substrate for chemically isolating the emitter coating from the substrate.

5. The matched emitters of claim 1, wherein the antireflection metal oxide coating is about 0.14 microns thick.

6. An antireflection coated matched emitter for thermophotovoltaic cells, comprising:a durable high temperature substrate; a metal or metal silicide emitter layer coating on the substrate; and an antireflective HfO2 coating on the emitter layer.

7. The matched emitter of claim 6, wherein the substrate comprises SiC.

8. The matched emitter of claim 6, wherein the metal emitter layer comprises pure W.

9. The matched emitter of claim 6, wherein the metal silicide emitter comprises TaSi2.

10. The matched emitter of claim 6, wherein the antireflective HfO2 coating has a thickness of about 0.14 microns.

11. The matched emitter of claim 6 wherein the substrate is selected from the group consisting of SiC, Ta, metal alloys and stainless steel.

12. The matched emitter of claim 6, wherein the emitter layer is a metal selected from the group consisting of W, Ta, Nb and Mo.

13. The matched emitter of claim 6, wherein the metal silicide emitter is selected from the group of metal silicides consisting of TaSi2, NbSi2, TiSi2 and VSi2.

14. A thermophotovoltaic generator, comprising a heat source, an emitter for receiving heat from the source and emitting infrared light waves having wavelengths of about 1.8 microns and less, an infrared filter for passing infrared energy and reflecting wavelengths greater than 1.8 microns toward the emitter, and a photovoltaic receiver for receiving the infrared wavelengths, wherein the receiver comprises low bandgap photovoltaic cells, and wherein the emitter comprises a durable high temperature substrate, a refractory metal or metal silicide emitter layer on the substrate and a metal oxide antireflective layer of HfO2, wherein the photovoltaic receiver comprises GaSb cells which convert to electricity infrared energy in wavelengths below 1.8 microns.

15. The generator of claim 14, further comprising a chemically isolating layer between the substrate and the emitter layer.

16. The generator of claim 14, wherein the emitter comprises a refractory metal emitter selected from the group of pure metals consisting of W, Ta, Nb and Mo, having a thickness of from about 1 to about 6 microns.

17. The generator of claim 14, wherein the emitter comprises a metal silicide emitter selected from the group of metal silicides consisting of TaSi2, NbSi2, TiSi2 and VSi2.

18. The generator of claim 14, wherein the antireflective layer has a thickness of about 0.14 microns and an antireflective wavelength of about 1.4 microns.