Antistatic resin composition

BACKGROUND OF THE INVENTION
The present invention relates to a resin composition comprising a graft copolymer alone or a mixture of the graft copolymer and a thermoplastic resin compatible therewith, the graft copolymer having been obtained by graft-polymerizing a vinyl or vinylidene monomer onto a rubber trunk polymer with low electrical resistance comprising 1 to 50% (by weight, as in all percentages and parts set forth hereinafter) of a monomer comprising 4 to 500 alkylene oxide groups and a conjugated diene and/or an alkyl acrylate, which graft copolymer possesses an antistatic property that is not practically lowered by washing.
In general, plastics have high electrical resistance and tend to be easily charged with static electricity due to friction or peeling. For this reason, plastics are liable to attract dust and dirt, resulting in various troubles such as impairment of the appearances of shaped articles, sheets, films and fibers formed from these plastics.
Methods for imparting antistatic property to such plastics that are susceptible to static electricity have been investigated and can be roughly classified as follows.
1. Methods which involve kneading an antistatic agent into the plastics.
2. Methods which involve applying an antistatic agent (surfactant) over the surface of the plastics.
3. Methods which involve applying a silicone compound over the surface of plastics.
4. Methods which involve chemically reforming the molecular structure of plastics.
Of these methods, a method which involves kneading an antistatic agent into plastics cannot successfully impart a permanent antistatic effect, and, when the antistatic agent present over the surface of the plastics is removed by washing with water or rubbing, the antistatic effect is lost.
As an exception, an antistatic agent of kneading-in type possessing an antiwashing property suitable for use in polyethylene, polypropylene and polyvinyl chloride has been reduced to practice. However, this antistatic agent is accompanied by certain problems. One is that a considerable time is required until its antistatic effect is restored after washing. Another is that, if an antistatic agent bleeds excessively over the surface of plastics, dust and dirt adhere thereonto. Still another problem is that a satisfactory antistatic agent has not yet been obtained for transparent and hard plastics on a commerical basis. Furthermore, this method requires a step of kneading-in an antistatic agent.
If the method which involves applying an anti-static agent over the surface of plastics is employed, its antistatic effect is drastically impaired upon washing.
The method which involves applying a silicone compound over the surface of plastics provides an excellent and substantially permanent antistatic effect but is disadvantageous from the standpoint of process efficiency and economy.
The method which involves chemically reforming the molecular structure of plastics by introducing hydrophilic groups into plastics by polymerization and the like generally requires the introduction of a considerable quantity of hydrophilic groups in order to obtain a high antistatic effect, so that the mechanical and other properties of the plastics deteriorate because of the increased hygroscopicity thereof.
SUMMARY OF THE INVENTION
As a result of our intensive investigation on processes for producing resins possessing permanent antistatic property that is now lowered by washing, we have obtained a rubber trunk polymer having a low specific volume resistivity. Further, we have found that a graft copolymer alone obtained by graft-polymerizing a vinyl or vinylidene monomer onto this rubber trunk polymer, or a mixture of the graft copolymer thus obtained and a resin compatible therewith possesses a permanent antistatic effect, and that a copolymer comprising 1 to 50% of a monomer comprising 4 to 500 alkylene oxide groups and 50 to 99% of a conjugated diene and/or an alkyl acrylate is suitable as the rubber trunk polymer. On the basis of these findings, we have arrived at the present invention.
More specifically, the antistatic resin composition according to the present invention comprises (A) 10 to 100 parts of a graft copolymer obtained by graft-polymerizing 20 to 95% of at least one vinyl or vinylidene monomer onto 5 to 80% of a rubber trunk polymer which in turn is a copolymer of 50 to 99% of a member selected from the group consisting of conjugated dienes, alkyl acrylates and mixtures thereof, 1 to 50% of a polyalkylene oxide monomer which is a monomer comprising 4 to 500 alkylene oxide groups together with an ethylenic unsaturation, and 0 to 49% of a vinyl or vinylidene monomer copolymerizable with the conjugated diene or alkyl acrylate; and (B) 0 to 90 parts of a thermoplastic resin compatible with the graft copolymer (A), the rubber trunk polymer being 5 to 80% of the total of the graft copolymer (A) and the thermoplastic resin (B).
While the antistatic property of the resin composition according to the present invention can, of course, be improved by adding an antistatic agent, no antistatic agent, practically, needs to be added. Since the polyalkylene oxide groups are chemically bonded to the rubber trunk polymer, the antistatic property of the resin composition will not be lowered even under severe washing conditions.
Further, since the matrix resin need not be modified to be hydrophilic, the overall properties of the composition will not appreciably be affected even if the rubber phase absorbs moisture. By suitably controlling the particle size, quantity and refractive index of the rubber trunk polymer, a transparent resin composition possessing improved impact strength can be obtained.
Processes for preparing resin compositions possessing an antistatic property by copolymerizing monomers comprising polyalkylene oxide groups are disclosed, for example, in Japanese Patent Laid-Open Publications No. 18521/1973, No. 29526/1976 and No. 78642/1975. However, all of the resins obtained by these processes are random copolymers of monomers comprising polyalkylene oxide groups or mixtures thereof with other polymers. If the monomers comprising polyalkylene oxide groups are used in small quantity, an excellent antistatic property cannot be obtained, while these monomers in large quantity increase the hygroscopicity of the resin composition.
In contrast, it is essential in the present invention that the monomer comprising polyalkylene oxide groups be present as a constituent of the rubber trunk polymer. The resin composition of this invention exhibits an excellent antistatic effect presumably because the rubber trunk polymer is dispersed in branch polymers or in the matrix resin composed of a thermoplastic resin compatible with the graft copolymer and branch polymers in mutually bridged state in a shaped resin article, and the electric charge is diffused mainly through the rubber trunk polymer phase and thus is reduced. In the resin composition of this invention, the hygroscopicity of the branch polymer phase undergoes substantially no change even if the hygroscopicity of the rubber trunk polymer phase increases, and hence the mechanical strength or heat resistance of the composition is not appreciably reduced.
As has been set forth hereinabove, the monomer comprising alkylene oxide groups must be present in the rubber trunk polymer. In the case where this monomer is present, not as a constituent of the rubber trunk polymer, but as a constituent of a random copolymer, a polymer possessing excellent antistatic property cannot be obtained as in the present invention with the same quantity of the monomer.
DETAILED DESCRIPTION OF THE INVENTION
The rubber trunk polymer of the present invention is a rubbery copolymer of 50 to 99% of a conjugated diene and/or an alkyl acrylate, 1 to 50% of a monomer comprising 4 to 500 alkylene oxide groups together with an ethylenic unsaturation (hereinafter referred to as a polyalkylene oxide monomer), and optionally 0 to 49% of one or more vinyl or vinylidene monomers copolymerizable with the conjugated diene or alkyl acrylate.
This rubber trunk polymer predominantly comprises a conjugated diene and/or an alkyl acrylate.
For the conjugated dienes, 1,3-butadiene, isoprene, chloroprene, and 1,3-pentadiene are used.
For the alkyl acrylates, ethyl acrylate, propyl acrylate, butyl acrylate, hexyl acrylate, octyl acrylate, and nonyl acrylate are used.
The sum of the quantities of the conjugated diene and alkyl acrylate amounts to 50 to 99% of the rubber trunk polymer. If this sum is less than 50%, the rubber trunk polymer cannot have a sufficiently low glass transition temperature, resulting in a poorer antistatic effect.
Conversely, in the case where this sum is greater than 99%, the quantity of the polyalkylene oxide monomer to be added will necessarily be reduced, and thus the desired antistatic effect cannot be obtained.
The polyalkylene oxide monomer comprises, in addition to an ethylenic unsaturation, a polyalkylene oxide chain or block represented by the formula: ##STR1## wherein each of R.sub.2 and R.sub.3, which may be the same or different, is hydrogen or an alkyl group having 1 to 4 carbon atoms, and m and n are integers that meet the requirement 4.ltoreq.m+n.ltoreq.500. Preferably, a polyalkylene oxide monomer in which at least one of R.sub.2 and R.sub.3 is hydrogen and which comprises a polyethylene oxide block consisting of 4 or more ethylene oxide groups is used.
A preferred polyalkylene oxide monomer is one or more monomers represented either by the following formula (2): ##STR2## wherein: R.sub.1 is hydrogen or an alkyl group having 1 to 4 carbon atoms; X is hydrogen, an alkyl group having 1 to 9 carbon atoms, a phenyl group, SO.sub.3 Me, SO.sub.2 Me, PO.sub.3 Me.sub.2, ##STR3## each of R.sub.4, R.sub.5 and R.sub.6 being hydrogen or an alkyl group having 1 to 9 carbon atoms, and Me being hydrogen, Na, Li or K; and R.sub.2, R.sub.3, m, and n have the same meaning as in the formula (1), or by the formula (3): ##STR4## wherein Z is hydrogen, an alkyl group having 1 to 40 carbon atoms, a cycloalkyl group having 3 to 6 carbon atoms, a phenyl group, or ##STR5## k and l being integers that meet the requirement 4.ltoreq.k+l.ltoreq.500; and R.sub.1 to R.sub.6, X, Me, m, and n are as defined above.
Among the monomers represented by the formula (2) or (3), those in which at least one of R.sub.2 and R.sub.3 is hydrogen and which comprises a polyethylene oxide block consisting of 4 or more ethylene oxide groups are particularly preferable as mentioned earlier.
It is of course possible, however, to use analogous monomers other than the monomers represented by the formula (2) or (3), which comprise an ethylenic unsaturation and further can lower the volume resistivity of the rubber trunk polymer.
The polyalkylene oxide monomer comprises 4 to 500, preferably 6 to 50, and more preferably 9 to 50, alkylene oxide groups. In the case where the quantity of the alkylene oxide groups is less than 4, it is difficult to obtain an antistatic property. A polyalkylene oxide monomer comprising more than 500 alkylene oxide groups, when subjected to polymerization, is not easily soluble in water or other monomers, resulting in poor polymerizability.
Further, if the quantity of the monomer comprising polyalkylene oxide groups is less than 1% of the rubber trunk polymer, sufficient antistatic property cannot be obtained. Conversely, more than 50% of this monomer results in some difficulty in the polymerization required for the formation of the rubber trunk polymer or the graft copolymer as well as in post-treatments of the polymer obtained such as precipitation with an acid or salting out.
For vinyl or vinylidene monomers copolymerizable with the conjugated diene or alkyl acrylate which are optionally used in the preparation of the rubber trunk polymer, known monomers can be utilized.
For example, one or more monomers selected from alkyl methacrylates, acrylic acid, methacrylic acid, acrylamide, methacrylamide, vinyl acetate, unsaturated nitriles, aromatic vinyl monomers, alkyl vinyl ethers, alkyl vinyl ketones, 2-hydroxyethyl (meth)acrylate, diacetone acrylamide, vinyl chloride, vinylidene chloride, itaconic acid, alkyl itaconates, isobutene, 2-acid phosphoxyethyl methacrylate, 3-chloro-2-acid phosphoxypropyl methacrylate, and sodium styrene-sulfonate can be used.
An improved antistatic property can be obtained by selecting as the above enumerated vinyl or vinylidene monomers copolymerizable with the conjugated diene or alkyl acrylate highly polar monomers such as acrylonitrile or monomers having an anionic substituent such as a sulfonate group, phosphate group or carboxylate group.
These vinyl or vinylidene monomers are used in a quantity of 49% or less of the monomer mixture which provides the rubber trunk polymer. If this quantity is larger than 49%, the glass transition temperature becomes higher and the rubbery property of the trunk polymer is lost.
The rubber trunk polymer can optionally comprise as a crosslinking agent a polyfunctional monomer having two or more of at least one species of ethylenically unsaturated groups, such as vinyl group, 1,3-butadienyl group, acryloxy group, methacryloxy group, and allyl group, in a quantity of 0 to 10% of the rubber trunk polymer. A polyfunctional monomer further comprising 4 to 500, preferably 9 to 50, polyalkylene glycol groups is particularly preferred because such a monomer acts as a crosslinking agent and simultaneously serves as an antistatic property modifier.
By graft-polymerizing a vinyl or vinylidene monomer onto the rubber trunk polymer thus obtained, the graft copolymer of the present invention possessing excellent antistatic property can be obtained.
For the vinyl or vinylidene monomers to be used in the graft polymerization, known monomers can be employed. For example, one or more monomers selected from alkyl acrylates, alkyl methacrylates, acrylic acid, methacrylic acid, acrylamide, methacrylamide, vinyl acetate, unsaturated nitriles, aromatic vinyl monomers, conjugated dienes, alkyl vinyl ethers, alkyl vinyl ketones, 2-hydroxyethyl (meth)acrylate, (alkoxy)polyethylene glycol (meth)acrylate, diacetone acrylamide, vinyl chloride, vinylidene chloride, itaconic acid, alkyl itaconates, and isobutene can be used.
The proportion of the rubber trunk polymer in the graft copolymer ranges from 5 to 80%, preferably from 8 to 70%, the proportion of the branch polymer ranging from 20 to 95%, preferably from 30 to 92%. If the proportion of the rubber trunk polymer is lower than 5%, it will be difficult to obtain antistatic property. On the other hand, the rubber trunk polymer in higher proportions results in loss of the rigidity of the graft copolymer as well as in poor processability.
The composition of the graft copolymer as herein referred to and that of the rubber trunk polymer mentioned earlier are determined on the basis of the starting monomers. However, since the degree of polymerization in the respective stages is 90% or higher, the resin composition of the present invention has substantially the same composition as that of the monomers.
While the graft copolymer of this invention endowed with improved antistatic property can be prepared by an ordinary graft polymerization process using emulsion polymerization in the presence of a radical initiator, suspension polymerization or bulk polymerization, emulsion polymerization is most suitable for effectively controlling the particle size or dispersion of the rubber trunk polymer.
The monomer for the branch polymer may be polymerized either at one time or, in the case where the polymerization entails intense heat or monomers having different reactivities are used together, may be added and polymerized intermittently or continuously in accordance with a conventional process to prepare the desired graft copolymer.
The antistatic resin composition of the present invention can be a graft copolymer alone which comprises a rubber trunk polymer comprising polyalkylene oxide groups obtained as described above. A resin composition possessing excellent antistatic property can also be obtained by blending with 10 to 100 parts of the graft copolymer 0 to 90 parts of a thermoplastic resin compatible therewith. In this case, however, it is essential that the ratio of the rubber trunk polymer to the total of the graft copolymer and the thermoplastic resin be 5 to 80%, preferably 8 to 60%. A percentage of less than 5% of the rubber trunk polymer cannot readily produce antistatic property, while that in excess of 80% results in low heat resistance and poor processability.
Examples of thermoplastic resins to be used in combination with the graft copolymer are polyethylene, polypropylene, polyvinyl chloride, polyvinylidene chloride, aromatic vinyl polymers, nitrile resins, polymethyl methacrylate and the copolymers thereof, acrylonitrile-styrene-butadiene resins, acrylonitrile-styrene resins, polycarbonates, polyamide resins, polyester resins, and fluoro-resins. Needless to say, any other thermoplastic resins that are compatible with the graft copolymer can be used.
In accordance with the present invention, transparent resin products can easily be obtained by controlling the refractive indices of the rubber trunk polymer and branch polymer, although the products of the present invention are not limited to transparent products.
The resin composition of the present invention possessing excellent antistatic property can be formed or molded by an ordinary process, for example, injection molding, extrusion molding, compression molding, or vacuum forming. Accordingly, this resin composition can be formed into plastic moldings, sheets, films, tubes, and fibers.
The resin composition of the present invention is suitable for use, for instance, in electrical appliances or accessaries thereof (e.g., cassette tape recorder cases, front covers of picture tubes, record player covers, dust collectors and hoses of vacuum cleaners, covers of instruments, IC element casings, and various cases); packaging materials (e.g., doll cases, cans, bottles, and packaging films); acoustic materials (e.g., audio discs, video discs, and tapes for tape recorders); building materials (e.g., wall materials, flooring materials, panels, and window materials); lighting equipment (e.g., lamp shades, and displays); and plastics in general wherein an antistatic property is required.
In order to indicate more fully the nature and utility of this invention, the following specific examples of practice constituting preferred embodiments of the invention and comparison examples are set forth, it being understood that these examples are presented as illustrative only and not intended to limit the scope of the invention.
Test specimens were measured 7 days after forming upon adjusting their moisture content and 7 days after washing with water as described in Example 1. The data obtained show that the resin products according to the present invention have satisfactory antistatic property immediately after forming or washing with water. Thus, the antistatic property achieved by the present invention is not due to bleeding of the antistatic agent over the surface of the resin product with the elapse of time nor due to the moisture absorbed after forming or washing with water.
The test specimens used in Examples were prepared by pressing the resultant resin powder under heat. However, substantially the same results can be obtained with specimens prepared by pressing after kneading the powder with heated rolls or by extrusion molding through an extruder.

EXAMPLE 1
An aqueous dispersion composed of the following ingredients was adjusted to a pH of 7 with an aqueous solution of sodium hydroxide and charged into a 10-l stainless steel autoclave provided with agitating blades.
______________________________________ Part______________________________________(a) 1,3-butadiene 6 methyl acrylate 3 methoxypolyethylene glycol methacrylate 1 (having an average of ca.23 ethylene oxide groups) tertiary dodecylmercaptan 0.05 diisopropylbenzene hydroperoxide 0.02 formaldehyde sodium sulfoxylate 0.01 ferrous sulfate heptahydrate 0.0004 disodium ethylenediaminetetraacetate 0.0006 sodium pyrophosphate 0.05 sodium dodecylbenzenesulfonate 0.1 deionized water 30______________________________________
The atmosphere within the autoclave was thoroughly purged with nitrogen, and the reaction mixture was agitated at 40.degree. C. for 20 hours, whereupon a rubber latex of an average particle size of 0.08.mu. was obtained in a yield of 99%.
To 40 parts (10 parts as a rubber trunk polymer) of this rubber latex were added the following ingredients.
______________________________________ Part______________________________________(b) acrylonitrile 54 methyl acrylate 36 normal dodecylmercaptan 3.6 potassium persulfate 0.072 sodium hydrogensulfite 0.018 sodium dodecylbenzenesulfonate 0.9 deionized water 270______________________________________
The atmosphere within the autoclave was purged with nitrogen, and the reaction mixture was subjected to graft copolymerization at 50.degree. C. for 20 hours under agitation. The resulting latex was withdrawn from the autoclave, and then subjected to deposition with an aqueous aluminum sulfate solution, adjusted to a pH of 7 with an aqueous sodium pyrophosphate solution, dehydrated, washed, and dried at 55.degree. C. for 24 hours. As a result, a white powder was obtained in a yield of 97%.
This powder as pressed at 200.degree. C. and 200 kg/cm.sup.2 for 5 min. to prepare test specimens of 0.6 to 0.8 mm thickness. These test specimens were stored under normal conditions of 23.degree. C. and 50% RH for a week, and thereafter the half-life of the charged voltage was measured by means of a Static Honest Meter (mfd. by Shishido Shokai, Japan) to evaluate the antistatic property thereof. The results obtained are shown in Table 1.
The measurement conditions were as follows.
______________________________________Applied voltage 8,000 VRotational speed 1,300 rpm.Humidity 50-55% RHTemperature 23.degree. C.Time period 1 min.______________________________________
In order to evaluate the antiwashing property, the surface of each test specimen was thoroughly washed with an aqueous solution of a commercially available detergent (mfd. by Lion Yushi K.K., Japan, under the trade name "Mama Lemon") and then thoroughly washed with distilled water. The specimens were stored under the conditions of 50% RH and 23.degree. C. for a week to adjust their moisture content, whereafter the half-life of the charged voltage was measured by means of the Static Honest Meter. The results are set forth in Table 1.
EXAMPLE 2
Test specimens were prepared substantially in the manner set forth in Example 1 except that 81 parts of methyl methacrylate and 9 parts of methyl acrylate were used in place of the acrylonitrile and methyl acrylate, and the half-life of the charged voltage was measured by means of the Static Honest Meter. The results obtained are shown in Table 1.
EXAMPLES 3, 4 AND 5
Graft copolymers having the compositions shown in Table 2 were prepared by the procedure of Example 1 from rubber trunk polymers and branch polymers each having the same composition as that of Example 2.
The results obtained in the same manner as in Example 1 are summarized in Table 2.
TABLE 1______________________________________ Half-life of charged voltage (sec.) Untreated Washed with water______________________________________Example 1 10 6Example 2 27 21______________________________________
TABLE 2______________________________________Rubber trunk Branch Half-life of chargedpolymer polymer voltage (sec.)(part (part Washed withby wt.) by wt.) Untreated water______________________________________Example2 10 90 27 21Example3 20 80 10 9Example4 50 50 2 2Example5 70 30 >1 >1______________________________________
EXAMPLES 6 THROUGH 18
Test specimens were prepared substantially in the manner described in Example 1 except that the monomer composition was modified as shown in Table 3.
The results of the measurement by means of the Static Honest Meter are set forth in Table 3.
TABLE 3__________________________________________________________________________ Half-life of charged voltage (sec.)Monomer composition (wt. %) Un- WashedRubber trunk treat- withpolymer Branch polymer ed water__________________________________________________________________________Example 6 But MA M1 TDM MMA NDM 12 6 2 0.1 80 2.4 25 18 7 But MA M1 TDM St NDM 12 6 2 0.1 80 1.0 23 21 8 But MA M1 TDM St AN NDM 6 3 1 0.05 67.5 22.5 2.7 12 3 9 But MA M1 TDM MMA MA M1 NDM 6 3 1 0.05 81 8 1 2.7 18 1510 But St M1 MMA St NDM 13 5 2 48 32 1.5 21 1911 But AN M1 AN St NDM 6 2 2 67 23 2.4 8 712 But M1 MMA MA NDM 6 4 72 18 1.8 6 513 But MA M2 DVB AN MA NDM 12 6 2 0.2 48 32 3.2 30 2514 But MA M3 Cl AN MA NDM 12 5 2 1 48 32 3.2 4 315 But MA M4 MMA MA NDM 12 5 3 64 16 1.6 7 616 But MA M5 MMA MA NDM 12 6 2 64 16 1.6 13 1117 But MA AN M1 DVB MMA NDM 12 4 2 2 0.3 80 0.8 3 318 BA AN M1 DVB MMA NDM 16 2 2 0.3 80 0.8 4 4__________________________________________________________________________
The symbols used in Table 3 and all succeeding tables denote the following.
But . . . 1,3-butadiene
MA . . . methyl acrylate
MMA . . . methyl methacrylate
St . . . styrene
AN . . . acrylonitrile
BA . . . butyl acrylate
M1 . . . methoxypolyethylene glycol methacrylate (having an average of 23 ethylene oxide groups)
M2 . . . methoxypolyethylene glycol methacrylate (having an average of 9 ethylene oxide groups)
M3 . . . methoxypolyethylene glycol methacrylate (having an average of 40 ethylene oxide groups)
M4 . . . methoxypolyethylene glycol acrylate (having an average of 23 ethylene oxide groups)
M5 . . . polyethylene glycol acrylamide (having an average of 23 ethylene oxide groups)
TDM . . . tertiary dodecylmercaptan
NDM . . . normal dodecylmercaptan
DVB . . . divinylbenzene
C1 . . . polyethylene glycol dimethacrylate (having an average of 23 ethylene oxide groups)
COMPARISON EXAMPLES 1 THROUGH 7
Test specimens were prepared substantially in the manner described in Example 1 except that the monomer composition was modified as shown in Table 4.
The results of the measurement by means of the Static Honest Meter are set forth in Table 4.
TABLE 4__________________________________________________________________________ Half-life of charged voltage (sec.)Monomer composition (wt. %) Un- WashedRubber trunk treat- withpolymer Branch polymer ed water__________________________________________________________________________Compa-risonExample1 But MA TDM MMA MA NDM 6 4 0.05 72 18 1.8 >3600 >36002 But MA TDM AN MA NDM 6 4 0.05 54 36 3.6 510 5503 MMA MA M1 NDM 78.5 19.5 2 0.1 >3600 >36004 St M1 NDM 98 2 0.1 >3600 >36005 MMA NDM 100 0.1 >3600 >36006 St NDM 100 0.1 >3600 >36007 But MMA MA NDM 6 72 22 0.1 >3600 >3600__________________________________________________________________________
EXAMPLE 19
Graft polymerization was carried out by continuously adding over a period of about 5 hours 80 parts of methyl methacrylate containing 0.8 part of normal dodecylmercaptan as a molecular weight regulator to 80 parts (20 parts as a rubber trunk polymer) of the same rubber latex as was used in Example 17.
The graft copolymer obtained was subjected to the procedure of Example 1 to prepare test specimens.
The results of the measurement by means of the Static Honest Meter were as follows.
______________________________________ Half-life of charged voltage (sec.)______________________________________Untreated 12Washed with water 11______________________________________
EXAMPLES 20, 21 AND 22
40 parts each of graft copolymers obtained substantially as in Example 1 except that the monomer composition was modified as shown in Table 5 and 60 parts each of the thermoplastic resins shown in the same table were kneaded with rolls heated to 170.degree. C. for 3 min. The resulting mixture was molded in the same manner as in Example 1 to prepare test specimens.
The results of the measurement by means of the Static Honest Meter are set forth in Table 5.
TABLE 5__________________________________________________________________________ Half-life of chargedMonomer composition (wt. %) voltage (sec.)Rubber trunk Thermopla- Wash withpolymer Branch polymer stic resin Untreated water__________________________________________________________________________Example 20 But MA AN M1 MMA NDM DELPET 60N*.sup.1 30 10 5 5 50 1.0 (Asahi Dow) 8 7Example 21 But St AN M1 St AN NDM TOYOLAC 900*.sup.2 30 10 5 5 37.5 12.5 1.0 (Toray, K.K.) 15 13Example 22 But St AN M1 St AN NDM TYRIL 780*.sup.3 30 10 5 5 37.5 12.5 1.0 (Asahi Dow) 12 10__________________________________________________________________________ *.sup.1 polymethyl methacrylate resin *.sup.2 acrylonitrilebutadiene-styrene resin *.sup.3 acrylonitrilestyrene resin
EXAMPLES 23, 24 and 25
Graft copolymers obtained substantially as in Example 1 except that the monomer composition was modified as shown in Table 6 and a polyvinyl chloride compound (average degree of polymerization 700; dioctyltin maleate 2 PHR, stearyl alcohol 0.8 PHR and a butyleneglycol montanate 0.2 PHR added; abbreviated to PVC), respectively in the quantities shown in Table 6 were kneaded with rolls heated to 160.degree. C. for 3 min. The resulting mixture was molded in the same manner as in Example 1 to prepare test specimens.
The results of the measurement by means of the Static Honest Meter are summarized in Table 6.
TABLE 6__________________________________________________________________________ Quantity of graft Quantity Half-life of charged copolymer of PVC voltage (sec.)Monomer composition (wt. %) blended Blended WashedRubber trunk (part (part withpolymer Branch polymer by wt.) by wt.) Untreated water__________________________________________________________________________Example 23 But BA AN M1 MMA NOM* 36 15 3 6 40 0.36 17 83 15 13Example 24 But BA AN M1 MMA NOM 36 15 3 6 40 0.36 34 66 <1 <1Example 25 But BA AN M1 MMA St NOM 48 20 4 8 14 6 0.18 25 75 1 1__________________________________________________________________________ *Normal octylmercaptan as in all succeeding tables.
EXAMPLES 26 THROUGH 31
Test specimens were prepared as in Example 1 except that the monomer composition was modified as shown in Table 7.
The results of the measurement by means of the Static Honest Meter are set forth below.
TABLE 7__________________________________________________________________________ Half-life of charged voltage (sec.)Monomer composition (wt. %) Un- WashedRubber trunk treat- withpolymer Branch polymer ed water__________________________________________________________________________Example But BA M1 MAA MMA NOM26 12 5 2 1 80 0.72 1 1.527 But BA M1 IA MMA NOM 12 5 2 1 80 0.72 2 228 But BA M1 SS MMA NOM 12 5 2 1 80 0.72 1 129 But M1 AN MMA NOM 12 4 4 80 0.72 1 230 But M1 MMA NOM 12 8 80 0.72 2 231 But BA MAA M2 MMA BA St NDM 12 10.5 1.5 6 59.5 7 3.5 0.42 <1 <1__________________________________________________________________________ MAA methacrylic acid IA itaconic acid SS sodium styrenesulfonate
EXAMPLES 32 THROUGH 35
20 parts each of the graft copolymers shown in Table 8 and 80 parts each of the thermoplastic resins shown in the same table were kneaded with a kneader heated to 220.degree. to 270.degree. C. for 3 min., and the resulting mixture was pressed at 220.degree. to 280.degree. C. under 200 kg/cm.sup.2 for 3 min. to prepare test specimens.
The results of the measurement by means of the Static Honest Meter are set forth in Table 8.
COMPARISON EXAMPLES 8 THROUGH 11
Test specimens were prepared substantially as in Examples 32 through 35 except that no graft copolymers were added, and the results shown in Table 8 were obtained.
TABLE 8__________________________________________________________________________ Half-life of char- ged voltage (sec.)Monomer composition (wt. %) WashedRubber trunk Thermoplastic withpolymer Branch polymer resin Untreated water__________________________________________________________________________Example But BA M2 MAA MMA MA NOM PET-G6763*.sup.132 26 23 13 3 21 14 0.07 (Eastman Kodak Co.) 1 1 But BA M2 MAA MMA MA NOM Idemitsu polycarbonate33 26 23 13 3 21 14 0.07 A-2700*.sup.2 (Idemitsu 1 1 Sekiyu Kagaku K.K.) But BA M2 MAA MMA NOM DAIAMID L2101*.sup.334 26 23 13 3 35 0.28 (Daciell K.K.) 0.8 1 But BA M2 MAA MMA NOM KF polymer #1000*.sup.435 26 23 13 3 35 0.28 (Kureha Kagaku Kogyo 3 3 K.K.)Compari- -- -- PET-G6763son (Eastman Kodak Co.) 660 680EXAMPLE 8 9 -- -- Idemitsu polycarbonate A-2700 (Idemitsu Sekiyu >3600 >3600 Kagaku K.K.)10 -- -- DAIAMID L2101 53 550 (Daicell K.K.)11 -- -- KF polymer #1000 (Kure- 720 750 ha Kagaku Kogyo, K.K.)__________________________________________________________________________ *.sup.1 polyester copolymer, *.sup.2 polycarbonate, *.sup.3 nylon 12, *.sup.4 polyvinylidene fluoride.
EXAMPLE 36
The same resin as was used in Example 26 was molded into T-die extruded sheets of about 100.mu. thickness through an extruder provided with a T-die, the resin temperature being 205.degree. C. at the outlet of the T-die.
The half-life of the charged voltage of each of these sheets as measured by means of the Static Honest Meter was 1 sec. irrespective of whether the sheet was washed with water.
EXAMPLE 37
The same resin as was used in Example 31 was molded into a product of a size of 100.times.50.times.3 mm through an injection molding machine, the resin and mold temperatures being 210.degree. C. and 60.degree. C., respectively.
Test specimens were prepared by cutting the injection-molded product thus obtained to a size of 40.times.50.times.3 mm at its central portion.
The half-life of the charged voltage of each of these test specimens as measured by means of the Static Honest Meter was as follows.
______________________________________Untreated 1 sec.Washed with water 1 sec.______________________________________
COMPARISON EXAMPLES 12, 13 AND 14
MMA copolymers (A) and MMA copolymers (B) each having the composition set forth below were blended in latex form at the resin weight ratios shown in Table 9, and thoroughly mixed by agitation. The resulting mixtures were subjected to salting out, heat treatment, washing with water and drying in the same manner as in Example 1, whereupon a white powder was obtained in a yield of 99%.
Test specimens were prepared by the procedure of Example 1, and the antistatic property of each of the specimens was similarly evaluated.
The results obtained are shown in Table 9.
______________________________________MMA copolymer (A)MMA 70MA 10M4 20NOM 0.8MMA copolymer (B)MMA 80MA 20NOM 0.8______________________________________
TABLE 9______________________________________ Half-life of charged MMA co- MMA co- voltage (sec.) polymer polymer Un- Washed with (A) (B) treated water______________________________________ComparisonExample 12 10 90 2400 2400ComparisonExample 13 20 80 780 1300ComparisonExample 14 50 50 300 720______________________________________

Number	Name	Date
3074905	Douglas	Jan 1963
3962187	Kline	Jun 1976
4302558	Ohya et al.	Nov 1981
4315081	Kobayashi et al.	Feb 1982

Number	Date	Country
2309590	Sep 1975	DEX
45-334426	Oct 1970	JPX
47-9742	Mar 1972	JPX
48-18521	Mar 1973	JPX
50-78642	Jun 1975	JPX
51-29526	Mar 1976	JPX

Antistatic resin composition

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

REFERENCE TO PRIOR APPLICATION

US Referenced Citations (4)

Foreign Referenced Citations (6)

Continuations (1)