Patent Application
20060057857
The invention relates to fabrication of circuits and circuit elements, and more particularly to deposition techniques using aperture masks.
Circuits include combinations of resistors, diodes, capacitors and transistors linked together by electrical connections. Thin film integrated circuits include a number of layers such as metal layers, dielectric layers, and active layers typically formed by a semiconductor material such as silicon. Typically, thin film circuit elements and thin film integrated circuits are created by depositing various layers of material and then patterning the layers using photolithography in an additive or subtractive process, which includes a chemical etching step to define various circuit components. Additionally, aperture masks have been used to deposit a patterned layer without an etching step.
In general, the invention is directed to aperture mask deposition techniques for use in creating integrated circuits or integrated circuit elements. The techniques involve sequentially depositing material through a number of repositionable aperture masks formed with patterns of vias that define layers, or portions of layers of the circuit. In some embodiments, circuits can be created solely using aperture mask deposition techniques, without requiring any of the etching or photolithography steps typically used to form integrated circuit patterns. The techniques can be particularly useful in creating circuit elements for electronic displays such as liquid crystal displays and low-cost integrated circuits such as radio frequency identification (RFID) circuits or electronic memory. In addition, the techniques can be advantageous in the fabrication of integrated circuits incorporating organic semiconductors, which typically are not compatible with photolithography or other wet etching processes.
In one embodiment, the invention is directed to a mask set for use in a deposition process such as a vapor deposition process. The mask set may include a first aperture mask formed with a first pattern of deposition apertures that define at least part of a first layer of a circuit, and a second aperture mask formed with a second pattern of deposition apertures that define at least part of a second layer of the same circuit. Additionally, any number of aperture masks may be included in the mask set depending on the number of layers in the circuit. The various deposition apertures in the aperture masks may have widths less than approximately 20 microns, less than approximately 10 microns, or even less than approximately 5 microns. Apertures of these sizes are particularly useful in creating small circuit elements for integrated circuits. Moreover, one or more gaps between deposition apertures may be less than approximately 20 microns or less than approximately 10 microns, which is also useful in creating small circuit elements or relatively closely spaced circuit elements.
In another embodiment, the invention is directed to one or more mask fabrication methods. For example, a method according to the invention may include forming a first pattern of deposition apertures that define at least part of a first layer of a circuit in a first silicon wafer to create a first aperture mask, and forming a second pattern of deposition apertures that define at least part of a second layer of the circuit in a second silicon wafer to create a second aperture mask. The deposition apertures may have the widths mentioned above and gaps between one or more deposition apertures may have the dimensions mentioned above.
Once the first and second aperture masks have been created, they can be used in a deposition process to create circuit elements on a deposition substrate. Additional aperture masks can also be created and used in a similar manner to ultimately define any number of circuit layers on the deposition substrate.
In another embodiment, the invention is directed to an aperture mask for use in a deposition process. In particular, the aperture mask may include a mask substrate having alignment edges, and a pattern defined in the mask substrate in relation to the alignment edges such that spatial alignment of the alignment edges aligns the pattern for the deposition process. Again, deposition apertures may have widths as mentioned above and gaps between two deposition apertures may have the dimensions mentioned above to facilitate the creation of sufficiently small circuit elements.
In another embodiment, the invention is directed to a deposition system. The system may include an aperture mask having alignment edges and a deposition pattern defined in relation to the alignment edges. In addition, the system may include an alignment fixture having at least three contact points, wherein exactly three contact points contact the alignment edges of the aperture mask to align the pattern for a deposition process. The same or a different set of three contact points can be used for alignment of the aperture masks used in different depositions. The deposition pattern can be defined in relation to the alignment edges such that, upon contact of the alignment edges with the contact points, the pattern is aligned to within a tolerance of less than approximately 10 microns, less than approximately 5 microns, or even less than approximately 2 microns. The alignment fixture may include additional features such as a securing element to secure the aperture mask into alignment, and a spring member that exerts a spring bias to force the aperture mask and deposition substrate against the alignment fixture to ensure that alignment and intimate contact are maintained during the deposition process.
In another embodiment, a method may include aligning a pattern of an aperture mask relative to a deposition substrate by aligning the alignment edges of the aperture mask with corresponding alignment edges of the deposition substrate, and depositing material onto the deposition substrate through the pattern of the aperture mask. Prior to aligning the aperture mask and the deposition substrate, the method may include forming a pattern in a mask substrate relative to alignment edges on the mask substrate to define the aperture mask.
In another embodiment, a method of creating a circuit including an organic semiconductor includes aligning an aperture mask with a deposition substrate, and depositing a first material onto the substrate through a pattern of deposition apertures defined by the aperture mask. The method may also include re-aligning the aperture mask with the substrate, and depositing a second material onto the deposition substrate through the pattern. For example, the first and second materials may comprise hole conducting semiconductor material and electron conducting semiconductor material, respectively, in which case, deposition of the first and second materials creates the active layers of complimentary transistor circuit elements such as a metal oxide semiconductor (CMOS) element. Alternatively, the materials may comprise red, green or blue light emitting materials or optical filters, in which case, deposition can be performed to define display pixels for a display circuit.
In another embodiment, the invention is directed to an integrated circuit. For example, the integrated circuit may include a deposition substrate, a first patterned electrode layer formed adjacent to the substrate, an organic semiconductor layer formed adjacent to the first electrode layer, and a second patterned electrode layer deposited adjacent to the organic semiconductor layer. The first patterned electrode layer may define a gate electrode, and the second patterned electrode layer may define source and drain electrodes, wherein at least one of the electrodes has a width less than approximately 20 microns, less than approximately 10 microns, or even less than approximately 5 microns. Alternatively, the first patterned electrode layer may define source and drain electrodes, and the second patterned electrode layer may define a gate electrode. The integrated circuit may further include a dielectric layer formed over the gate electrode and under the organic semiconductor layer. Each of the above-described layers of the integrated circuit can be patterned, wherein the patterns of each layer are defined by an aperture mask. Additionally, the gap between the electrodes may be less than 20 microns, or even less than 10 microns which can be particularly useful in creating small circuit elements or closely spaced circuit elements. The integrated circuit may also include one or more interconnect layers as well as interconnects formed as part of other metal layers, for example, by implementing stitching techniques of successive aperture mask depositions. The integrated circuit may form part of an electronic display, an RFID circuit or an electronic memory.
In another embodiment, the invention is directed to a transistor. For example, the transistor may form part of an integrated circuit such as an RFID circuit, or alternatively, the transistor may form a control element for a pixel of a display such as an LCD display. The transistor may include a first deposited conductive layer, a deposited dielectric layer formed over the deposited conductive layer, a deposited organic semiconductor layer formed over the deposited dielectric layer, and a second deposited conductive layer formed over the deposited organic semiconductor layer. At least one layer may define at least one feature having a width less than approximately 20 microns, 10 microns, or even 5 microns.
In another embodiment, an integrated circuit may include a number of deposited layers, wherein none of the layers are etched, and wherein at least one of the layers defines features having widths less approximately than 20 microns, less approximately than 10 microns, or even less approximately than 5 microns. Integrated circuits according to the invention can be particularly useful when organic semiconductors are implemented because no etching or photolithography is required in the circuit fabrication process.
The various embodiments of the invention can provide a number of advantages. For example, the aperture mask deposition techniques described herein can facilitate the creation of circuits without using etching or photolithographic techniques. Again, this is particularly useful for circuits that use organic semiconductors because chemical etching and/or photolithographic techniques generally are not compatible with patterning of organic semiconductors. The organic semiconductors used may be polycrystalline, such as pentacene. In addition, aperture masks having deposition apertures of widths on the order of those discussed herein can facilitate the creation of circuits having small circuit elements in a simple and relatively low cost vapor deposition process. Also, deposition apertures separated by gaps on the order of those discussed herein can also facilitate the creation of smaller circuit elements. Still, the aperture masks described herein are durable and thus can be reused a number of times. Furthermore, non-metallic aperture masks may be less prone to the formation of creases which can render thin metal masks unusable.
The alignment techniques described herein can be highly advantageous to quickly and effectively align deposition masks for the deposition process. In particular, the formation of alignment edges on the mask avoids the need for registration holes and posts, which may introduce slight clearances that permit movement and can result in misalignment. Moreover, for non-metallic masks, the use of registration holes and posts can cause damage to the mask, particularly as efforts are made to provide a tight fit that reduces clearances in the holes. Accordingly, the use of alignment edges can be more effective in aligning the aperture mask than registration holes. In some cases, the use of alignment edges may facilitate mechanical alignment of an aperture mask with a deposition substrate to within a tolerance less than approximately 10 microns, less than approximately 5 microns, or even less than approximately 2 microns. The invention can avoid mask damage and facilitate precise alignment for the formation of circuits created in the deposition process.
Details of these and other embodiments of the invention are set forth in the accompanying drawings and the description below. Other features, objects, and advantages of the invention will become apparent from the description and drawings, and from the claims.
a is a top view of an aperture mask according to an embodiment of the invention.
b is an enlarged view of a portion of the aperture mask in FIG 1a.
a is a top view of an aperture mask according to an embodiment of the invention. Aperture mask 10 can comprise any of a variety of metallic or non-metallic materials. Non-metallic materials may be particularly useful for some embodiments. For example, aperture mask 10 may comprise single crystal silicon, rigid polymer or filled polymer substrates, glass, or the like. In the case of silicon, aperture mask 10 may have a thickness of less than approximately 100 microns, or even less than 50 microns. Such thicknesses of silicon can be effective for use in deposition techniques for circuit fabrication. Moreover, aperture mask 10 formed from non-metallic material can yield advantages over conventional metallic masks such as lower cost formation and better resolution of a deposition pattern. Aperture mask 10 is free-standing in that it forms a separate and distinct structure that does not form part of a deposition substrate. Aperture mask 10 may be reusable in a number of deposition processes.
As shown in
Aperture mask 10 can be used in a deposition process, such as a vapor deposition process in which material is deposited onto a deposition substrate through deposition apertures 14 to define at least a portion of a circuit. Advantageously, aperture mask 10 enables deposition of a desired material and, simultaneously, formation of the material in a desired pattern. Accordingly, there is no need for a separate patterning step preceding or following deposition. Aperture mask 10 can be particularly useful in creating circuits in electronic displays, low-cost integrated circuits such as RFID circuits, or any circuit that implements thin film transistors. Moreover, circuits that make use of organic semiconductors can benefit from various aspects of the invention as described in greater detail below.
One or more deposition apertures 14 can be formed to have widths less than approximately 20 microns, less than approximately 10 microns, or even less than approximately 5 microns. By forming deposition apertures 14 to have widths in these ranges, the size of circuit elements may be reduced. Moreover, a distance (gap) between two deposition apertures (such as for example the distance between deposition aperture 14C and 14D) may be less than approximately 20 microns or less than approximately 10 microns, to reduce the size of various circuit elements and possibly improve performance.
If aperture mask 10 is formed from a silicon wafer, the pattern 12 of deposition apertures 14 can be created using reactive ion etching or laser ablation techniques to achieve acceptable widths of deposition apertures 14 as well as acceptable gaps between deposition apertures 14. Alternatively, if aperture mask 10 is formed from another non-metallic material, such as a polymer, laser ablation techniques or micro-replication techniques such as micro-molding may be used to define pattern 12 of deposition apertures 14. Accordingly, formation of aperture mask 10 from non-metallic materials may allow the use of fabrication processes that can be less expensive, less complicated, and/or more precise than those generally required for metallic masks. When an aperture mask is fabricated, for example, by creating deposition pattern 12 in a crystalline wafer, the straight edges of the deposition apertures may be purposely misaligned with respect to cleavage planes or crystallographic axes of the wafer. If the straight edges of the apertures are aligned with the crystallographic axes, the mask may be prone to breakage. Such misalignment would also be useful in aperture masks made from crystalline wafers, including for example, wafers comprising single crystal silicon, Ge or GaAs. The angle of misalignment may be five degrees or greater.
In some cases, the first and second aperture masks 10A and 10B may define different layers of a circuit, and in other cases, first and second aperture masks 10A and 10B may define different portions of the same circuit layer or may define parts of other layers. For example, stitching techniques can be used to form interconnects in which first and second aperture masks 10A and 10B define different portions of the same circuit layer. In other words, two or more masks may be used in separate depositions to define a single circuit layer, which may include one or more interconnects. Stitching techniques can be used, for example, to avoid relatively long deposition apertures, closed curves, or patterns that could cause portions of the aperture masks to be poorly supported. The solution is to form long lines and closed curves by “stitching” together the deposition patterns associated with two or more aperture masks to define a single circuit feature. In a first deposition, one mask forms part of a feature, and in a second deposition, another mask forms the remainder of the feature.
Each aperture mask 10 in mask set 20 can be formed with one or more deposition apertures having widths less than approximately 20 microns, less than approximately 10 microns, or even less than approximately 5 microns. In addition, at least two deposition apertures in each aperture mask may be separated by a gap less than approximately 20 microns, or less than approximately 10 microns. Again, apertures and aperture gaps of these dimensions can reduce circuit size, and in some cases improve circuit performance.
Deposition station 30 is typically a vacuum chamber. After aperture mask 10 is placed into intimate contact with deposition substrate 32, material 36 is vaporized by deposition unit 34. For example, deposition unit 34 may include a boat of material that is heated to vaporize the material. The vaporized material 36 deposits on deposition substrate 32 through the deposition apertures of aperture mask 10 to define at least a portion of a circuit layer on deposition substrate 32. Upon deposition, material 36 forms the pattern defined by aperture mask 10. As mentioned above, aperture mask 10 may include deposition apertures and gaps that are sufficiently small to facilitate the creation of small circuit elements using the deposition process. Additionally, various alignment techniques may be used as described in greater detail below, to ensure that the aperture mask is properly aligned during the deposition process. Specifically, each aperture mask in the mask set may need to be similarly aligned for the sequential deposition process through each mask in the set. Other suitable deposition techniques include e-beam evaporation, various forms of sputtering, and pulsed laser deposition.
Thin film transistors are commonly implemented in a variety of different circuits, including for example, RFID circuits and other low cost circuits. In addition, thin film transistors can be used as control elements for liquid crystal display pixels, or other flat panel display pixels. Many other applications for thin film transistors also exist.
As shown in
In particular, thin film transistor 40 includes a first deposited conductive layer 42 formed over deposition substrate 41. A deposited dielectric layer 43 is formed over first conductive layer 42. A second deposited conductive layer 44 defining source electrode 45 and drain electrode 46 is formed over deposited dielectric layer 43. A deposited active layer 47, such as a deposited semiconductor layer, or a deposited organic semiconductor layer is formed over second deposited conductive layer 44.
Deposition techniques using mask set 20, for example, represent one exemplary method of creating thin film transistor 40. In that case, each layer of thin film transistor 40 may be defined by one or more deposition apertures in non-metallic deposition masks 10 that form mask set 20. Alternatively, one or more of the features of the thin film transistor may be created using a number of aperture masks and stitching techniques, as described above.
By forming deposition apertures 14 in masks 10 to be sufficiently small, one or more features of thin film transistor 40 can be made less than 20 microns, less than 10 microns, or even less than 5 microns. Moreover, by forming a gap in an aperture mask to be sufficiently small, other features such as the distance between source electrode 45 and drain electrode 46 can be made less than 20 microns or even less than 10 microns. In that case, a single mask may be used to deposit second conductive layer 44, with each of the two electrodes 45, 46 being defined by deposition apertures separated by a sufficiently small gap, such as a gap less than 20 microns or a gap less than 10 microns. In this manner, the size of thin film transistor 40 can be reduced, enabling fabrication of smaller, higher density circuitry while maintaining the performance of thin film transistor 40.
Again, by forming deposition apertures 14 in masks 10 to be sufficiently small, one or more features of thin film transistor 50 can have widths on the order of those discussed herein. Also, by forming a gap in an aperture mask to be sufficiently small, the distance between source electrode 56 and drain electrode 57 can be on the order of the gaps discussed herein. In that case, a single mask may be used to deposit second conductive layer 55, with each of the two electrodes 56, 57 being defined by deposition apertures separated by a sufficiently small gap. In this manner, the size of thin film transistor 50 can be reduced, and in some cases the performance of thin film transistor 50 may even be improved.
Thin film transistors implementing organic semiconductors generally take the form of
By forming at least the top two layers of the thin film transistor using aperture mask deposition techniques, the invention can facilitate the configuration of
As shown in
The formation of alignment edges on mask 60 avoids the need for registration holes and posts, which can introduce slight clearances that permit movement and can result in misalignment. Moreover, for non-metallic masks, the use of registration holes and posts can even cause damage to the mask, particularly as efforts are made to provide a tight fit that reduces clearances in the holes. Accordingly, the use of alignment edges 62 can be more effective in aligning aperture mask 60 than registration holes. In some cases, the use of alignment edges 62 can facilitate mechanical alignment of aperture mask 60 and deposition substrate 70 to within a tolerance less than approximately 10 microns, less than approximately 5 microns, or even less than approximately 2 microns. The invention can avoid mask damage and facilitate precise alignment for the formation of circuits created in the deposition process.
A number of aperture masks including alignment edges may form a mask set, in which case each aperture mask may include similar alignment edges but different patterns defined in relation to the alignment edges. In this manner, each aperture mask in the mask set can be properly aligned with deposition substrate 70 by aligning the edges of each mask with the edges of deposition substrate 70.
Alignment fixture 80 includes at least three contact points 82A, 82B and 82C. The contact points 82A, 82B and 82C are illustrated as forming pins, but other configurations of contact points 82, such as posts, bumps and the like are also envisioned. The aperture mask having alignment edges and the deposition substrate having alignment edges can be placed into alignment fixture 80 such that the alignment edges of both the aperture mask and the deposition substrate contact alignment fixture 80 at exactly the three contact points 82A, 82B and 82C. In this manner, quick and precise alignment can be achieved, in some cases, to a tolerance less than approximately 10 microns, less than approximately 5 microns, or even less than approximately 2 microns. In other cases, additional contact points can be added to define exactly three different contact points for a different deposition.
Alignment fixture 80 is capable of providing precise alignment without the need for alignment posts that extend through registration holes in the aperture mask and the deposition substrate. Moreover, alignment fixture 80 is capable of avoiding the slight movement that may occur with the use of alignment posts that extend through registration holes. In particular, alignment fixture 80 does not rely on alignment holes in the mask, which can be slightly larger than the alignment posts. Additionally, temperature differentials can compound problems associated with alignment posts that extend through registration holes in a mask.
The alignment edges used with alignment fixture 80 help to achieve precise alignment without the problems associated with registration holes and posts that extend through the holes. Also, the simplicity of the alignment fixture 80 can also allow aperture masks and deposition substrates to be aligned more quickly, decreasing production costs and increasing throughput of a large-scale manufacturing process for some applications.
Deposition station 100 is typically a vacuum chamber. After aperture mask 101 is placed in proximity or into intimate contact with a deposition substrate 103 within alignment fixture 80, material 106 is vaporized by deposition unit 108. For example, deposition unit 108 may include a boat of material that is heated to vaporize the material. The vaporized material 106 passes through hole 81 (not shown in
After proper alignment is achieved, material can be deposited on the deposition substrate through the aperture mask (123). In this manner, aperture mask deposition techniques can be used to achieve circuit elements having relatively small widths. In particular, relatively small deposition aperture widths and relatively small gaps between deposition apertures, together with the use of the precision alignment techniques described herein can achieve deposition circuits having very small feature widths.
In one example, patterns are formed in masks for sequential depositions in which the pattern of the first aperture mask forms a gate electrode and wherein the material deposited onto the deposition substrate through the pattern of the second aperture mask is a semiconductor, the semiconductor being deposited after the gate electrode is deposited. In that case, source and drain electrodes can be deposited onto the semiconductor through the pattern of a third aperture mask.
In another example, patterns are formed in masks for sequential depositions in which the pattern of the first aperture mask forms a gate electrode, wherein the material deposited onto the deposition substrate through the pattern of the second aperture mask forms a dielectric layer. In that case, a semiconductor can be deposited onto the dielectric layer through the pattern of a third aperture mask, and source and drain electrodes can be deposited onto the semiconductor through the pattern of a fourth aperture mask. For each deposition, the pattern of the respective aperture mask can be positioned relative to the deposition substrate by positioning the alignment edges of the respective aperture mask and the alignment edges of the deposition substrate in contact with the exactly three contact points of alignment fixture 80.
The method of
In other examples, a first light emitting material can be deposited, the aperture mask realigned, and then a second light emitting material can be deposited. For example, the mask may be aligned for three separate depositions, corresponding the red, green and blue sub-pixels. In that case, the three depositions may define a pixel for a display. The deposited materials may be organic or inorganic. In some cases, one material may be organic and another may be inorganic. A similar process may be used to make colored sub-pixels using color filter material for use in a display or a sensor.
In one example, alignment edges of the aperture mask and deposition substrate can be used to facilitate realignment. For example, the deposition substrate may define alignment edges that are slightly different on the various sides of the deposition substrate. In that case, realignment may comprise removing the aperture mask from the alignment fixture, rotating the aperture mask (such as by a quarter turn) and then reinserting the rotated aperture mask into the alignment fixture. In other words, a first material can be deposited though the aperture mask formed with alignment edges, and the aperture mask can be rotated relative to the deposition substrate. A second material can then be deposited through the aperture mask. The different alignment edges, such as alignment edges 62A and 62B (
Organic integrated circuits were fabricated using four vacuum deposition steps and four thin (50 micrometer thick) single crystal silicon masks. Four silicon masks were fabricated simultaneously by processing a single photolithographically patterned silicon wafer in a deep trench etcher (PlasmaTherm SLR Series using inductively coupled plasma). Four separate patterns were defined, one on each quadrant of the single wafer, and each pattern had with it associated alignment edges located in the same position relative to each pattern to allow rapid mechanical alignment using 3 point contact on 2 flat edges to within a tolerance of 10 micrometers or less. Each pattern (and corresponding alignment edges) was etched through the wafer to form vias. Each of the resulting aperture masks was patterned to form a separate deposited device layer as follows: (1) gate metal, (2) insulator, (3) semiconductor, and (4) source/drain metal.
After the aperture masks were formed, integrated circuits were fabricated by vapor deposition using no photolithography or wet processing. A first aperture mask was placed on an alignment fixture like that illustrated in
The first mask was removed and replaced by the second mask. The second mask was then aligned to the pattern on the substrate and the edges of the substrate by mechanically tapping the mask against the contact points of the alignment fixture and affixing the securing element to hold the assembly securely in place. The second material was then deposited through the mask. The second mask was then replaced by the third mask, the mechanical alignment was repeated, and the third material was deposited through the mask. Finally the third mask was replaced by the fourth, alignment was repeated, and the fourth material was deposited through the mask. The fourth mask was then removed, at which stage the circuit component was complete. Interconnections between circuit components were made by “stitching” traces in the gate and source/drain layers.
Using the above four masks, seven-stage pentacene ring oscillators were fabricated on glass substrates and tested. Palladium (50 nm thick) was vapor deposited as the gate metal, aluminum oxide (150 nm thick) as the insulator layer, pentacene (50 nm thick) as the semiconductor, and palladium (50 nm thick) as the source/drain layer. In this example, the integrated circuit was designed with minimum line widths of 15 micrometers. Performance of the resulting ring oscillator was evaluated at a test voltage of −30V, and the oscillator was found to be functional.
A number of embodiments of the invention have been described. For example, a number of different structural components and different aperture mask deposition techniques have been described. The aperture mask deposition techniques can be used to create various different circuits solely using deposition, avoiding any chemical etching processes or photolithography, which is particularly useful when organic semiconductors are involved. Nevertheless, it is understood that various modifications can be made without departing from the spirit and scope of the invention. For example, although the aperture mask deposition techniques have been specifically described using a thermal deposition example, the techniques and aperture masks are readily applicable for use in other deposition processes including sputtering, electron beam evaporation processes, other thermal evaporation processes, and the like. Thus, these other embodiments are within the scope of the following claims.
This application is a divisional of U.S. Ser. No. 10/076003, filed Feb. 14, 2002, now pending, the disclosure of which is herein incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10076003 | Feb 2002 | US |
| Child | 11258330 | Oct 2005 | US |