The present disclosure is directed to an apparatus for heating a metallic vessel, and more particularly an apparatus for heating a metallic vessel configured to convey a material, and the material contained therein, by direct electrical heating of the vessel. The material may be, for example, molten glass.
The manufacture of glass on a commercial scale is typically carried out within a refractory ceramic melting furnace wherein raw materials (batch) are added to the melting furnace and heated to a temperature at which the batch undergoes chemical reactions to produce the molten glass. Several methods of heating the batch can be used, including gas-fired burners, an electric current, or both. In a so-called hybrid process, a gas flame from one or more gas-fired combustion burners initially heats the batch. As the temperature of the batch increases and the molten glass is formed, the electrical resistance of the material decreases such that an electric current can be introduced into the molten glass through electrodes mounted in the side walls and/or floor of the melting furnace. The electric current heats the molten glass from within, and the gas burners heat the molten glass from above. In some embodiments submerged combustion can be employed.
Downstream processing of the molten glass, for example fining and homogenizing, can be carried out in certain portions of the furnace structure or in other vessels located downstream from the melting furnace and connected to the melting furnace by conduits. To maintain an appropriate temperature of the molten glass as the molten glass is being conveyed, the molten glass may be heated. In some processes, such as the fining process, the molten glass can be heated in a fining vessel to a temperature greater than the furnace temperature to facilitate a more complete removal of bubbles from the molten glass. In other portions of the manufacturing apparatus downstream of the melting furnace the molten glass may be cooled while flowing through one or more conduits to bring the molten glass to an appropriate viscosity for forming. However, the cooling may be limited by the controlled addition of heat energy to prevent too rapid a cooling rate.
For the manufacture of optical quality glass, for example glass suitable for use as display glass for the manufacture of display panels used in such devices as televisions, computer monitors, tablets, smart phones and the like, the downstream processing equipment is typically formed from a precious metal, such as a platinum group metal. Platinum, and/or alloys thereof, is particularly useful for the manufacture of molten glass processing equipment as it is workable, has a high melting temperature, and exhibits good resistance to corrosion.
Traditionally, metal vessels downstream from the melting furnace, including the conduits and other processing equipment, have been heated by external electrical heating elements, for example windings mounted in refractory insulating materials positioned around the vessels. These windings are often platinum windings, or alloys of platinum. While this can be satisfactory for small volume operations, it should be apparent that if the volume of molten glass must be increased, for example on a per hour or per day basis, significant capital expense associated with adding new manufacturing equipment can be avoided by simply increasing the flow rate of molten glass through the processing equipment. However, the increased flow volume may require a greater influx of heat energy. At some point this becomes difficult to achieve with external heating elements. Accordingly, modern large-scale glass manufacturing of glass articles, and in particular glass articles manufactured by flowing molten glass through precious metal vessels, employs so-called direct heating of the molten glass by establishing an electric current in the vessel itself that heats the vessel and therefore the molten glass within the vessel.
Other considerations include pre-heating the downstream metallic processing equipment during initial system preparation, before molten glass is introduced into the system. Under these conditions, a large current may be required to achieve the requisite temperature prior to the introduction of molten glass into the vessel. Connections to the vessel must be capable of carrying this current without detrimental effects to the vessel or the connection components.
In its most basic embodiment, the downstream process equipment can comprise a metal vessel including at least two flanges connected thereto. The flanges in turn are in electrical communication with an electric current source, and typically include electrode portions intermediate between the flange body and the electric cables (e.g. buses) that deliver the electric current to the flange from the power source. Conventional flange designs may not adequately distribute the current around a perimeter of the vessel, often simply because current flow within the flanges was not considered, which can create hot spots around the vessel. This can be particularly troublesome for non-circular vessels such as conduits with an oblong cross section. Accordingly, what is needed is a flange design that, when the flange is coupled to the vessel, distributes current more uniformly about the vessel, preventing hot spots in the vessel wall and uneven heating of the molten glass therein.
Described herein are flanges for attachment to vessels in a glass making apparatus. The flanges function to distribute an electric current to a wall of the vessel to which the flanges are attached, for example a metallic conduit, thereby heating the vessel and molten glass that may be present in the vessel. The flanges according to the present description include a first ring formed of a precious metal capable of withstanding high temperature, such as one of the platinum group metals or an alloy thereof. Suitable precious metals include the platinum group metals platinum, rhodium, iridium, ruthenium, palladium and osmium and alloys thereof. The first ring in accordance with the present disclosure comprises at least two individual portions that may differ in thickness. The individual portions may also differ in material such that the individual portions exhibit different material electrical resistances. And, whereas the first ring taken as a whole extends around the vessel in a closed loop, neither of the individual portions of the first ring extend completely around the entire vessel. Accordingly, the individual portions are discrete regions, wherein one portion may have a thickness different from (i.e., less than or greater than) another portion. For example embodiments described herein, a line infinitely extending from a center of the vessel outward along one angular position may intersect only one portion of the first ring. Yet for another line extending along a different angular position, the line may cross a width of both portions of the first ring. Thus, the portions of the first ring overlap in an edge-to-edge fashion along certain regions of the edges, but neither portion extends entirely around the vessel.
The plurality of portions contained within the first ring, particularly when the first ring is the innermost ring of the flange, function to direct current in a way that avoids a high concentration of electric current along the shortest conduction path between an electrode portion of the flange and the electrode portion of another flange attached to the vessel and spaced apart from the first flange, namely along a linear path between the electrode and the vessel, and along the vessel wall at a position closest to the electrode portion. For example, if the electrode portions of two spaced-apart flanges are both oriented at the top of the vessel, the shortest conduction path between the flanges is along the top of the vessel. Embodiments of the present disclosure direct current toward the sides and the bottom of the vessel, thereby reducing the electric current at the top of the flange and the top of the vessel.
It should be appreciated that the principals and example embodiments disclosed herein, while described in the context of a glass making apparatus, can be directed to other apparatus for processing other materials that are conveyed or contained in metallic vessels.
Accordingly, in one embodiment an apparatus for processing a material is disclosed comprising a vessel comprising a wall, the vessel arranged to convey the material. A flange is attached to the vessel and is configured to deliver an electric current to the vessel wall, the flange comprising a first ring extending completely around the vessel in a closed loop, the first ring comprising a first portion including a first thickness and a second portion including a second thickness different from the first thickness. A cross sectional shape of the vessel in a plane perpendicular to a longitudinal axis of the vessel can be circular or oblong. In some embodiments the vessel can be, for example, a fining vessel. In some embodiments the material is molten glass.
The first portion and the second portion of the first ring overlap in a plane of the flange such that the first portion is positioned between the second portion and the vessel wall, and neither the first portion nor the second portion extends completely around the vessel. In some embodiments, the thickness of the first portion of the first ring is different than a thickness of the second portion. For example, the thickness of the first portion of the first ring may be less than the thickness of the second portion of the first ring.
The flange may further comprise a second ring extending in a closed loop around the first ring. A thickness of the second ring can be greater than the thickness of either one or both of the first or second portions of the first ring. The second ring may be an outermost ring
The first ring can comprise a first metal while the second ring comprises a second metal different from the first metal. For example, the first ring may comprise a platinum group metal, or an alloy thereof, while second ring may comprise, as examples and not limitation nickel, copper or alloys thereof. In some embodiments the first ring may be a platinum-rhodium alloy.
In accordance with examples of the present disclosure, a first radial line extending from and perpendicular to a centerline of the vessel in a plane of the flange may cross the first portion of the first ring without intersecting the second portion of the first ring. The first radial line may be parallel to a minor axis of the vessel.
The first ring may further comprise a third portion, wherein the third portion does not extend completely around the vessel. In example embodiments, the third portion may be positioned between the first portion and the second portion.
In another embodiment, an apparatus for making glass is described comprising a vessel including a wall and a flange attached to the vessel. A cross sectional shape of the vessel in a plane perpendicular to a longitudinal axis of the vessel can be circular or oblong. In some embodiments the vessel can be, for example, a fining vessel. The flange is configured to deliver an electric current to the vessel wall. The flange can comprise a first ring extending completely around the vessel and attached to the vessel wall in a closed loop, the first ring comprising a first portion including a first thickness and a second portion including a second thickness different from the first thickness. Any one or both of the first portion or the second portion may, however, be of uniform thickness. Neither the first portion nor the second portion extends completely around the vessel and there can be at least one radial line extending from and perpendicular to a centerline of the vessel in a plane of the flange that crosses a width of both the first portion and the second portion. The flange may further comprise a second ring extending completely around the first ring in a closed loop
The first ring may comprise a first metal while the second ring may comprise a second metal different than the first metal.
In some embodiments, the second ring contacts the first ring around an entire perimeter of the first ring, and both the first portion and the second portion contact the second ring.
In still another embodiment, a method is described for making an electrically heated vessel comprising an electrical flange configured to supply an electric current to the vessel attached thereto, the electrical flange encircling the vessel in a plane substantially perpendicular to a centerline of the vessel, the method comprising (a) parameterizing the electrical flange, the electrical flange comprising a first ring comprising a first metal and a second ring comprising a second metal different from the first metal, the first ring comprising in a plane of the flange a plurality of radially overlapping portions of different thickness, wherein the first ring comprises first and second overlapping portions and none of the overlapping portions extend completely around the vessel. The parameterizing can include determining a thickness, a shape and a position of the overlapping portions, (b) calculating, for a total predetermined electric current supplied to the vessel through the flange, a current density in the first ring at a predetermined position, and (c) if a difference between the current density at the predetermined position is greater than a predetermined current density value, then modifying at least one of the size, shape and position of the overlapping portions, then (e) repeating steps (b) and (c) until the electric current density in the first ring is less than the predetermined current density value. The predetermined current density value can be an absolute current density value or a percentage current density value.
Embodiments of the present disclosure can produce, for a vessel comprising adjacent flanges supplied with an electric current, an electric current density at the vessel-flange junction at a position nearest the electrode portion of the flange that can be less than an electric current density at a midpoint between adjacent flanges. This location may, in some examples, be the top of the vessel, wherein the electrode portion extends vertically upward from the flange body in a 12 O'clock position. In other examples, the electrode portion may extend vertically downward relative to the flange body in a 6 O'clock position. In still other examples, the electrode portion may extend horizontally relative to the flange body in a 3 O'clock or 9 O'clock position. It should be apparent that positions intermediate the foregoing positions are also possible. In an example where the electrode portions of adjacent flanges extend vertically upward from the flange bodies in a 12 O'clock position (i.e. near the top of the vessel), on a line extending between the adjacent flanges on a line between the adjacent flanges, for example at the 12 O'clock position, a difference in current density between the maximum current density on the line and a current density at the vessel-flange junction on the line can be equal to or less than 10%, for example equal to or less than 6%, or equal to or less than 5%, for example in a range from about 4% to about 10%, including all ranges and sub-ranges therebetween.
In example embodiments, the maximum current density along a line on the vessel in a circumferential (angular) position nearest the electrode portion of the flanges, e.g. in the 12 O'clock position, occurs within about 20% of the total distance between adjacent flanges, for example equal to or less than about 18%, equal to or less than about 15% or equal to or less than about 13%.
It is to be understood that both the foregoing general description and the following detailed description present embodiments of the present disclosure, and are intended to provide an overview or framework for understanding the nature and character of the embodiments as they are described and claimed. The accompanying drawings are included to provide a further understanding of the embodiments, and are incorporated into and constitute a part of this specification. The drawings illustrate various embodiments of the disclosure, and together with the description serve to explain the principles and operations thereof.
Apparatus and methods will now be described more fully hereinafter with reference to the accompanying drawings in which example embodiments of the disclosure are shown. Whenever possible, the same reference numerals are used throughout the drawings to refer to the same or like parts. However, this disclosure may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein.
Ranges can be expressed herein as from “about” one particular value, and/or to “about” another particular value. When such a range is expressed, another embodiment includes from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another embodiment. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint.
Directional terms as used herein—for example up, down, right, left, front, back, top, bottom—are made only with reference to the figures as drawn and are not intended to imply absolute orientation.
Unless otherwise expressly stated, it is in no way intended that any method set forth herein be construed as requiring that its steps be performed in a specific order. Accordingly, where a method claim does not actually recite an order to be followed by its steps or it is not otherwise specifically stated in the claims or description that the steps are to be limited to a specific order, it is in no way intended that an order be inferred, in any respect. This holds for any possible non-express basis for interpretation, including: matters of logic with respect to arrangement of steps or operational flow; plain meaning derived from grammatical organization or punctuation; the number or type of embodiments described in the specification.
As used herein, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a” component includes aspects having two or more such components, unless the context clearly indicates otherwise.
Aspects of the disclosure include apparatus for processing batch into a molten glass, and more particularly to apparatus for processing the molten glass. Furnaces of the disclosure may be provided for a wide range of applications to heat gases, liquids and/or solids. In one example, apparatus of the present disclosure are described with reference to a glass melting system configured to melt batch into molten glass and convey the molten glass to downstream processing equipment.
Methods of the disclosure may process the molten glass in a wide variety of ways. For instance, the molten glass may be processed by heating the molten glass to a temperature greater than an initial temperature. In further examples, the molten glass may be processed by maintaining a temperature of the molten glass or by reducing the rate of heat loss that might otherwise occur by inputting heat energy into the molten glass and thereby controlling the cooling rate of the molten glass.
Methods of the disclosure may process the molten glass with a fining vessel or with a mixing vessel, for example a stirring vessel. Optionally, the apparatus may include one or more further components such as thermal management devices, electronic devices, electromechanical devices, support structures or other components to facilitate operation of the glass manufacturing apparatus including conveying vessels (conduits) that transport the molten glass from one location to another location.
Shown in
Glass melting vessel 14 is typically comprised of refractory material, such as a refractory ceramic material. In some examples, glass melting vessel 14 may be constructed from refractory ceramic bricks, for example refractory ceramic bricks comprising alumina or zirconia.
In some examples, the glass melting furnace may be incorporated as a component of a glass manufacturing apparatus configured to fabricate a glass ribbon. In some examples, the glass melting furnace of the disclosure may be incorporated as a component of a glass manufacturing apparatus comprising a slot draw apparatus, float bath apparatus, down-draw apparatus including fusion down-draw apparatus, up-draw apparatus, press-rolling apparatus, tube drawing apparatus or other glass ribbon manufacturing apparatus. By way of example,
The glass manufacturing apparatus (e.g., the fusion down-draw apparatus 10) can optionally include an upstream glass manufacturing apparatus 16 positioned upstream of glass melting vessel 14 relative to the molten glass direction of flow. In some examples, a portion of, or the entire upstream glass manufacturing apparatus 16, may be incorporated as part of the glass melting furnace 12.
As shown in the illustrated example, the upstream glass manufacturing apparatus 16 can include a batch storage bin 18, a batch delivery device 20 and a motor 22 connected to the batch delivery device. Storage bin 18 may be configured to store a quantity of batch 24 that can be fed into melting vessel 14 of glass melting furnace 12, as indicated by arrow 26. In some examples, batch delivery device 20 can be powered by motor 22 configured to deliver a predetermined amount of batch 24 from the storage bin 18 to melting vessel 14. In further examples, motor 22 can power batch delivery device 20 to introduce batch material 24 at a controlled rate based on a sensed level of molten glass downstream from melting vessel 14. Batch 24 within melting vessel 14 can thereafter be heated to form molten glass 28.
Glass manufacturing apparatus 10 can also optionally include a downstream glass manufacturing apparatus 30 positioned downstream from the glass melting furnace 12 relative to the flow direction of molten glass. In some examples, a portion of the downstream glass manufacturing apparatus 30 may be incorporated as part of glass melting furnace 12. For instance, first connecting conduit 32 discussed below, or other portions of the downstream glass manufacturing apparatus 30, may be incorporated as part of the glass melting furnace 12. Elements of the downstream glass manufacturing apparatus, including first connecting conduit 32, may be formed from a precious metal. Suitable precious metals include platinum group metals selected from the group of metals consisting of platinum, iridium, rhodium, osmium, ruthenium and palladium, and alloys thereof. For example, downstream components of the glass manufacturing apparatus may be formed from a platinum-rhodium alloy including 70 to 90% by weight platinum and 10 to 30% by weight rhodium.
The downstream glass manufacturing apparatus 30 can include a first conditioning vessel such as fining vessel 34, located downstream from melting vessel 14 and coupled to melting vessel 14 by way of the above-referenced first connecting conduit 32. In some examples, molten glass 28 may be gravity fed from melting vessel 14 to fining vessel 34 by way of first connecting conduit 32. For instance, gravity may cause molten glass 28 to pass through an interior pathway of first connecting conduit 32 from melting vessel 14 to fining vessel 34.
Within fining vessel 34, bubbles may be removed from molten glass 28 by various techniques. For example, batch 24 may include multivalent compounds (i.e. fining agents) such as tin oxide that, when heated, undergo a chemical reduction reaction and release oxygen. Other suitable fining agents include without limitation arsenic, antimony, iron and cerium. Fining vessel 34 is heated to a temperature greater than the melting vessel temperature, thereby heating the fining agent. Oxygen bubbles produced by the temperature-induced chemical reduction of the fining agent(s) rise through the molten glass within the fining vessel, wherein gases in the melt produced in the melting furnace can coalesce into the oxygen bubbles produced by the fining agent. The enlarged gas bubbles can then rise to a free surface of the molten glass in the fining vessel and thereafter be vented out.
The downstream glass manufacturing apparatus 30 can further include a second conditioning vessel such as a mixing vessel 36 for mixing the molten glass that may be located downstream from the fining vessel 34. The glass melt mixing vessel 36 can be used to provide a homogenous glass melt composition, thereby reducing or eliminating cords of inhomogeneity that may otherwise exist within the fined molten glass exiting the fining vessel. As shown, fining vessel 34 may be coupled to molten glass mixing vessel 36 by way of a second connecting conduit 38. In some examples, molten glass 28 may be gravity fed from the fining vessel 34 to mixing vessel 36 by way of second connecting conduit 38. For instance, gravity may cause molten glass 28 to pass through an interior pathway of second connecting conduit 38 from fining vessel 34 to mixing vessel 36.
Downstream glass manufacturing apparatus 30 can further include another conditioning vessel, such as delivery vessel 40, located downstream from mixing vessel 36. Delivery vessel 40 may condition molten glass 28 to be fed into a downstream forming device. For instance, delivery vessel 40 can act as an accumulator and/or flow controller to adjust and provide a consistent flow of molten glass 28 to forming body 42 by way of exit conduit 44. As shown, mixing vessel 36 may be coupled to delivery vessel 40 by way of third connecting conduit 46. In some examples, molten glass 28 may be gravity fed from mixing vessel 36 to delivery vessel 40 by way of third connecting conduit 46. For instance, gravity may act to drive molten glass 28 to pass through an interior pathway of third connecting conduit 46 from mixing vessel 36 to delivery vessel 40.
Downstream glass manufacturing apparatus 30 can further include forming apparatus 48 comprising the above-referenced forming body 42 including inlet conduit 50. Exit conduit 44 can be positioned to deliver molten glass 28 from delivery vessel 40 to inlet conduit 50 of forming apparatus 48. In a fusion forming process, forming body 42 can comprise a trough 52 positioned in an upper surface of the forming body and converging forming surfaces 54 that converge along a bottom edge (root) 56 of the forming body. Molten glass delivered to forming body trough 52 via delivery vessel 40, exit conduit 44 and inlet conduit 50 overflows the walls of the trough and descends along converging forming surfaces 54 as separate flows of molten glass. The separate flows of molten glass join below and along root 56 to produce a single ribbon of glass 58 that is drawn from root 56 by applying tension to the glass ribbon, such as by gravity and pulling rolls (not shown), to control the dimensions of the glass ribbon as the glass cools and the viscosity of the molten glass increases such that the glass ribbon 58 goes through a visco-elastic transition and has mechanical properties that give glass ribbon 58 stable dimensional characteristics. The glass ribbon may subsequently be separated into individual glass sheets by a glass separation apparatus (not shown).
Unlike other components of the downstream glass manufacturing apparatus, forming body 42 is typically formed from a refractory ceramic material such as alumina (aluminum oxide) or zirconia (zirconium oxide), although other refractory materials may be used. In some examples, forming body 42 is a monolithic block of ceramic material that has been isostatically pressed and sintered, then machined into the appropriate shape. In other examples, the forming body may be formed by joining two or more blocks of refractory material, e.g. ceramic refractory material. Forming body 42 may include one or more precious metal components configured to direct the flow of molten glass over and from the forming body.
As molten glass 28 travels from the melting vessel 14 to forming body 42, the molten glass is thermally conditioned within the various precious metal vessels through which the molten glass flows. For example, as molten glass 28 travels through the first connecting conduit 32 into fining vessel 34, the molten glass can be heated to a temperature greater than the temperature of the molten glass in the melting vessel to facilitate the fining process. Molten glass 28 can be further heated within the fining vessel as the molten glass flows along the length of the fining vessel. As previously described, the relatively high temperature in the fining vessel relative to the melting vessel both enhances the chemical reduction of the fining agent, thereby increasing the release of oxygen by the fining agent, and reduces the viscosity of the molten glass, thereby facilitating the rise of bubbles entrained within the molten glass to the free surface of the molten glass. Accordingly, first conduit 32 and fining vessel 34 may be configured to include flanges for directing an electric current through the walls of the first conduit and the fining vessel.
As the molten glass is being conveyed from fining vessel 34 to mixing vessel 36 through second conduit 38, a temperature of the molten glass must be prevented from reducing below a temperature at which the molten glass can be easily mixed (homogenized), for example by a stirrer rotatably positioned within the mixing vessel. If the temperature of the molten glass in the mixing vessel becomes too viscous, mixing efficiency can be negatively impacted, thereby reducing the effectiveness of the mixing process in homogenizing the molten glass. Accordingly, second connecting conduit 38 positioned between fining vessel 34 and mixing vessel 36, and the mixing vessel itself, may be configured with flanges for directing an electric current through the walls of the second conduit and the mixing vessel.
Molten glass 28 delivered to forming body 42 by delivery vessel 40 must be of a suitable viscosity to enable forming of the glass ribbon. If a viscosity of the molten glass is too low, applying the appropriate tension to the glass ribbon may become difficult or impossible. If the viscosity is too high, thickness control may become a problem. Moreover, the temperature of molten glass 28 as it flows over forming surfaces 54 of forming body 42 must be controlled to prevent crystallization (devitrification) of both the molten glass itself and to prevent crystallization and precipitation of forming body material that may dissolve into the molten glass as the molten glass flows over the forming surfaces of the forming body. To achieve the proper temperature and viscosity of molten glass 28 as the molten glass is delivered to forming body 42, net heat loss from the molten glass as it travels through third connecting conduit 46 must be sufficiently controlled. Accordingly, third connecting conduit 46 may be configured with flanges to direct an electric current through the wall of the third conduit.
Any or all of the foregoing components of glass manufacturing apparatus 10 can be configured with one or more flanges. The flanges can be configured such that the electric current supplied to the flanges is separately controllable to produce zones of various temperatures. For example, fining vessel 34 may comprise a plurality of flanges, wherein groups of two or more flanges can be controlled to provide zones of different temperatures along the fining vessel. It should be apparent that such zones of different temperatures could be established in any one or more locations along the metallic components of the downstream glass manufacturing apparatus. The following description provides a more detailed discussion of flanges suitable for use within the glass manufacturing apparatus, such as within the downstream glass manufacturing apparatus, including their construction and their operation.
Shown in
Flange 100 comprises body portion 110 including first ring 112, second ring 114 and an electrode portion 116 attached to an outermost ring of body portion 110. Second ring 114 may, in some examples, be the outermost ring. Electrode portion 116 is directly coupled to the outermost ring, for example second ring 114 as shown in
In the embodiment shown in
Second ring 114 is spaced apart from wall 104 of vessel 102 and is positioned in a closed loop about first ring 112, and, being more distant from vessel wall 104 than first ring 112 and therefore exposed to a lower temperature than first ring 112, can, if desired, comprise a metal different from the metal or metals used in the manufacture of first ring 112. For example, while first ring 112 can be formed from a precious metal, including platinum group metals or alloys thereof, second ring 114 may also be formed from a less expensive and/or less temperature resistant yet electrically conducting metal, such as, for example and not limitation nickel, copper or alloys thereof. However, as described supra, in some examples second ring 114 may be a platinum-containing ring. Second ring 114 further includes a width W2, where width W2 is taken along a line perpendicular to longitudinal axis 108. Width W2 may vary as a function of angular position relative to vessel 102 (e.g. longitudinal axis 108), or width W2 may be substantially constant. In some embodiments, second ring 114 can be joined directly to first ring 112 such as by welding. In other embodiments, second ring 114 may be spaced apart from first ring 112 and not in direct contact with first ring 112. For example, flange 100 may comprise one or more intermediate rings between first ring 112 and second ring 114.
In some embodiments a thickness of the outermost ring, e.g., in a direction perpendicular to a major surface of flange 100, may vary as a function of angular position about the vessel to which the flange is attached. For example, the outermost ring may be formed from nickel, copper or other metal less expensive and less temperature resistant than platinum or alloys thereof, wherein regions of the outermost ring adjacent electrode portion 116 are thicker than other regions of the outermost ring. Such thicker portions may be adjacent electrode portion 116, but not directly between electrode portion 116 and first portion 118 of first ring 112 (see
As previously described, first ring 112 extends in a closed loop around vessel 102 and, in the instance where first ring 112 is the innermost ring, first ring 112 may be attached to vessel 102 around an outer perimeter of vessel wall 104 along an inner edge of first ring 112. For example, the inner edge of first ring 112 may be welded to an exterior surface of vessel wall 104. Similarly, in examples such as that illustrated in
As further illustrated by
The preceding description can be viewed another way by imagining two radial lines extending perpendicular to and infinitely outward from longitudinal axis (centerline) 108 in a plane of flange 100, first radial line 130 and second radial line 132, wherein first radial line 130 intersects only a single point on first portion 118 on one side of vertical line 120 (point A) and second radial line 132 intersects a different single point on first portion 118 on the opposite side of vertical line 120 (point B). An arc between and bounded by first radial line 130 and second radial line 132 over a region where first portion 118 extends around vessel 102 subtends an angle of 360°−α. In this example the angle α may be less than 180°. Additionally, in the example of
It should also be noted that first portion 118 is adjacent electrode portion 116 and on the same side of horizontal line 124 as electrode portion 116. The significance of this point will be explained in more detail further below.
First ring 112 further comprises a second portion 128 comprising a second thickness T2. Second thickness T2 may be different from first thickness T1. For example, second thickness T2 may be greater than first thickness T1. In some embodiments T2 may be in a range from about 80 mil (about 0.2 cm) to about 100 mil (about 0.25 cm). Second portion 128 extends around that portion of the vessel wall 104 that first portion 118 does not, e.g. at least over an angular extent of α. In the embodiment illustrated in
Summarizing the foregoing description, first ring 112 extends in a closed loop about vessel 102. First ring 112 comprises at least two portions, first portion 118 and second portion 128, neither of which first or second portion extends individually in a closed loop about vessel 102. First portion 118 and second portion 128 are at least partially nested in that there is a region of edge-to-edge overlap wherein at least a portion, but not all, of an outside edge of first portion 118 is in contact with a portion, but not all, of an inside edge of second portion 128. Relative to a centerline of the vessel, first portion 118 extends around at least a portion of vessel 102, and may extend over an angle greater than 180 degrees relative to longitudinal axis 108. Similarly, second portion 128 extends around at least a portion of vessel 102, and may extend over an angle greater than 180 degrees relative to longitudinal axis 108. In example embodiments, first thickness T1 of first portion 118 may be less than second thickness T2 of second portion 128. In other embodiments, the materials of first portion 118 and second portion 128 may be selected to provide different intrinsic electrical resistances.
It should further be apparent with the aid of
It was previously noted in reference to
The foregoing phenomenon can result in non-uniform heating of the molten glass flowing through the vessel because certain portions of the vessel carry a different electric current density than other portions of the vessel. More importantly, a significant portion of the electric current is concentrated on a line along the electrode portions and the top of the vessel. This high concentration of electric current along a line along the vessel wall nearest the electrode portions can result in excessive heating of the flange in a region along this line, and in particular near the junction between the flange and that part of the vessel nearest the electrode portions. Excessive heating of selected portions of the flange and/or the vessel can result, in a worst case scenario, in thermal damage (e.g., melting) to the flange or vessel. In addition, non-uniform heating of the molten glass can subsequently result in a non-uniform viscosity such that some regions of the molten glass flowing through the vessel exhibit a different viscosity that other regions of the molten glass. For example, in the case where the vessel 144 is filled with molten glass flowing therethrough, and in a cross section thereof, the bottom portion of the flow of molten glass may be cooler (receive less heating) than the top portion of the flow of molten glass, and therefore exhibit a greater viscosity than the top portion of the flow of molten glass. This can not only perturb the flow of molten glass through the vessel, it may disrupt downstream processes. For example, where the non-uniform heating occurs upstream of and near the stirring vessel, the non-uniform viscosity may interfere with mixing and homogenization. Where the non-uniform viscosity occurs upstream of and near the forming body, non-uniform viscosity can interfere with the forming process and prevent the production of quality glass sheet with uniform thickness.
For certain vessel types, for example vessels not completely filled with molten glass, the foregoing situation can be especially problematic. For example, a fining vessel during operation may be incompletely filled with molten glass and the molten glass therefor comprises a free surface. The volume of the fining vessel not including molten glass comprises a gaseous atmosphere between the free surface of the molten glass and the upper inner surface of the fining vessel. The molten glass flowing through the fining vessel can be a better thermal conductor than the gaseous atmosphere, and when the electrode of the flange is oriented vertically upward, the greatest amount of resistive heating can occur in that portion of the vessel exhibiting the least amount of thermal conduction for at least the foregoing reasons. To wit, the top of the vessel can be damaged by undesirably high temperatures produced by the high electric current density and the concurrent inability of the vessel along the electric current path to radiate or conduct away sufficient heat to avoid damage, owing at least to the relatively poor thermal conduction of the gaseous atmosphere.
It should also be noted that foregoing similar difficulty regarding electric current path can be experienced by the flange itself, since a significant portion of the electric current follows the shortest conduction path between electrode portion 116 and the vessel. Therefore, flange 100 can also suffer from thermal damage resulting from high electrical current density. Accordingly, in some embodiments flange 100 may include a cooling conduit 145, typically placed around a perimeter (e.g., outer edge) of the outermost ring, the cooling conduit configured to carry a cooling fluid, such as a suitable fluid, for example air or water.
Even more problematic is an initial pre-heat of the downstream manufacturing apparatus in preparation for the introduction of molten glass into the apparatus. During this operation very high current values may be necessary to achieve the proper heating of the apparatus components prior to the introduction of a flow of molten glass. Since under these conditions the entire vessel may be filled with a gaseous atmosphere, certain portions of the vessel wall may be subjected to very high current density and high temperature.
The flanges described herein in various embodiments mitigate or avoid problems such as those described above by effectively steering the electric current so that the electric current is distributed safely—away from the shortest conduction path described above. For example, when first portion 118 of first ring 112 that lies on the shortest conduction path as described above is made thinner than other portions of the first ring (e.g., second portion 128), the higher electrical resistance exhibited by the thinner first portion results in a more even distribution of the electric current by effectively steering electric current away from first portion 118. This can result in a lower overall temperature in flange 100 and thus avoiding significant hot spots. This is distinctly different than conventional flange designs that utilize thicker regions about the entire perimeter of the vessel, either in the vessel itself or in that portion of the flange directly attached to the vessel, as a means to accommodate greater current. Accordingly, as described in respect of FIG. 2, first ring 112 includes at least a first portion near electrode portion 116, and therefore on the shortest conduction path between electrode portion 116 and vessel 102, that is thinner than the rest of the first ring. Moreover, modeling has shown that the overlapping configuration of the first and second portions 118, 128 may not only steer the electric current to reduce the electric current density at the near-electrode portion of the flange and/or vessel, but may contribute to the uniformity of the electric current about vessel 102 where first ring 112 may be attached. It should be noted that the description of first ring 112, even when attached to vessel 102, discounts the presence of the weld material that may be positioned between first ring 112 and vessel wall 104, and that the weld material per se has minimal effect on electric current distribution to the vessel. It should also be noted that throughout the present description, the term “ring” is intended to represent a closed shape, and not necessarily a circular shape. Thus, the term ring may refer to any closed form and the foregoing description is applicable to non-circular vessel and flange designs as will be discussed more fully hereinbelow.
Shown in
Flange 200, similar to flange 100, comprises a body portion 214 including a first ring 216, a second ring 218 and an electrode portion 220 attached to an outermost ring. Second ring 218 may, in some examples, be the outermost ring wherein electrode portion 220 is directly coupled to second ring 218 as shown. For example, electrode portion 220 may be integral with second ring 218 and formed therewith. In some examples electrode portion 220 may be separately formed and attached to the outermost ring, e.g. second ring 218, such as by welding. First ring 216 is positioned between second ring 218 and vessel 202 and may be the innermost ring and in intimate contact with vessel wall 204. For example, first ring 216 may be welded to vessel wall 204 around an inner edge of first ring 216
In the embodiment shown in
Second ring 218 is spaced apart from wall 204 of vessel 202 and can comprise a metal different from the metal or metals used in the manufacture of first ring 216. For example, while first ring 216 can be formed from a precious metal, including the platinum group metals or alloys thereof, second ring 218 can be formed from a less expensive electrical conductor, such as for example and not limitation nickel, copper or alloys thereof. Second ring 218 further includes a width W2. Width W2 may be constant, or width W2 may vary as a function of angular position around vessel 202.
In the instance where first ring 216 is an innermost ring and connected to vessel wall 104, an inner edge of first ring 216 can be attached to vessel wall 204 and extend in a closed loop around vessel 202. For example, the inner edge of first ring 216 may be welded to vessel wall 204. Similarly, in the example illustrated in
In some embodiments, a thickness of the outermost ring, whether the outermost ring is second ring 218 or not, may vary as a function of angular position about the vessel to which the flange is attached. For example, the outermost ring may be formed from nickel, copper or other metal less expensive and less temperature resistant than platinum or alloys thereof, wherein regions of the outermost ring adjacent electrode portion 220 are thicker than other regions of the outermost ring. Such thicker portions may be adjacent electrode portion 220, but not directly between electrode portion 220 and first portion 222 of first ring 216 (see
As further illustrated by
First ring 216 further comprises a second portion 228 comprising a second thickness T2. Second thickness T2 may be different than first thickness T1. In the illustrated embodiment of
From the foregoing description it can be observed that first ring 216 extends in a closed loop about vessel 202 and that first ring 216 comprises at least two portions 222, 228. Neither portion 222 or 228 extends completely around the vessel. These portions 222, 228 are nested in that there is a region of edge-to-edge overlap wherein an outside edge of first portion 216 is in contact with an inside edge of second portion 228. Looked at yet another way, consider in a plane of flange 200 a radial line 232 extending perpendicular to and infinitely outward from longitudinal axis 208 and intersecting only a single point of first portion 222 (point E). Consider also radial line 234 extending perpendicular to and infinitely outward from longitudinal axis 208 and intersecting another single point F of first portion 222 on an opposite side of vertical line 224. An arc between first and second radial lines 232, 234 may subtend an angle α less than 180 degrees, and first portion 222 extends around vessel 202 at least by an angle of 360°−α. Similarly, consider radial line 236 extending perpendicular to and infinitely outward from longitudinal axis 208 and intersecting only a single point G of second portion 228. Consider also radial line 238 extending perpendicular to and infinitely outward from longitudinal axis 208 and also intersecting only a single point H of second portion 228 different from point G. An arc between third and fourth radial lines 236 and 238 may subtend an angle β less than 180 degrees, and second portion 228 extends around vessel 202 at least by an angle of 360°−β. In example embodiments the thickness T1 of first portion 222 can be less than a thickness T2 of second portion 228. In some embodiments the materials of first portion 118 and second portion 128 may be selected to provide different intrinsic electrical resistances.
It should be apparent with the aid of
In still another embodiment illustrated in
Flange 300, similar to flanges 100 and 200, comprises a body portion 314 including a first ring 316, a second ring 318 and an electrode portion 320 attached to an outermost ring. Second ring 318 may, in some examples, be the outermost ring wherein electrode portion 320 may be directly coupled to second ring 318 as shown. For example, electrode portion 320 may be integral with second ring 318 and formed therewith. In some examples electrode portion 320 may be separately formed and attached to the outermost ring, e.g. second ring 318, such as by welding. First ring 316 may, in some embodiments, be the innermost ring and in intimate contact with vessel wall 304.
In some embodiments, a thickness of the outermost ring may vary as a function of angular position about the vessel to which the flange is attached. For example, the outermost ring may be formed from nickel, copper or other metal less expensive and less temperature resistant than platinum or alloys thereof, wherein regions of the outermost ring adjacent electrode portion 320 are thicker than other regions of the outermost ring. Such thicker portions may be adjacent electrode portion 320, but not directly between electrode portion 320 and first portion 322 of first ring 316 (see
In the embodiment shown in
Second ring 318 is spaced apart from wall 304 of vessel 302 and accordingly second ring 318 can comprise a metal different from the metal or metals used in the manufacture of first ring 316. For example, while first ring 316 can be formed from a precious metal, including the platinum group metals or alloys thereof, second ring 318 can be formed from a less expensive electrical conductor, such as for example and not limitation nickel, copper or alloys thereof. Second ring 318 further includes a width W2. Width W2 may be constant, or width W2 may vary as a function of angular position around vessel 302.
In the instance where first ring 316 is an innermost ring, an inner edge of first ring 316 can be attached to vessel wall 304 in a closed loop around vessel 302. For example, the inner edge of first ring 316 may be welded to vessel wall 304. Similarly, in the example illustrated in
As further illustrated by
First ring 316 further comprises a second portion 328 comprising a second thickness T2. Second thickness T2 may be the same or different than first thickness T1. In the illustrated embodiment of
First ring 316 may further comprise a third portion divided into two discrete sub-portions, portion 332a and 332b, wherein each of sub-portions 332a and 332b extend around at least a portion of vessel wall 304 and each have a thickness T3. The two sub-portions 332a and 332b may be oppositely and symmetrically positioned about vertical line 324. In some embodiments sub-portions 332a and 332b may be positioned between first portion 322 and second portion 328. Third thickness T3 may be less than second thickness T2 but greater than thickness T1, e.g. T1<T3<T2.
In some embodiments the inner edge of first ring 316 may be attached to vessel wall 304 and extend in a closed loop around vessel 302. For example, the inner edge of first ring 316 may be welded to vessel wall 304. Similarly, in the example illustrated in
As also shown in
Looked at yet another way, consider in a plane of flange 300 a radial line 336 extending perpendicular to and infinitely outward from longitudinal axis 308 and intersecting only a single point of first portion 322 (point J) relative to vessel 302. Consider also radial line 338 extending infinitely outward from longitudinal axis 208 and intersecting another single point (point K) of first portion 322 on an opposite side of vertical line 324. An arc between radial lines 336, 338 subtends an angle α less than 180 degrees, and first portion 322 extends around vessel 302 at least by an angle of 360°−α. Similarly, consider radial line 340 extending perpendicular to and infinitely outward from longitudinal axis 308 and intersecting only a single point (point L) of sub-portion 332a. Consider also radial line 342 extending perpendicular to and infinitely outward from longitudinal axis 308 and also intersecting only a single point (point M) of sub-portion 332b. An arc between radial lines 340 and 342 subtends an angle ϕ less than 180 degrees, and at least a portion of sub-portion 332a or 332b may be positioned between second portion 328 and vessel wall 304. Indeed, at least a portion of sub-portion 332a may be positioned between second portion 328 and first portion 322.
Finally, consider an additional radial line 348. An arc between radial lines 342 and 348 subtends an angle Ψ less than 180 degrees, and may define the angular extent by which first portion 322 is in contact with second ring 318. Similarly, an arc between radial lines 340 and 344 can subtend an angle θ less than 180 degrees, and may define the angular extent by which second portion 328 is in contact with vessel wall 304.
It should further be apparent with the aid of
In yet another embodiment illustrated in
Flange 400, similar to flanges 100, 200 and 300, comprises a body portion 414 including a first ring 416, a second ring 418 and an electrode portion 420 attached to an outermost ring. Second ring 418 may, in some examples, be the outermost ring wherein electrode portion 420 may be directly coupled to second ring 418 as shown. For example, electrode portion 420 may be integral with second ring 418 and formed therewith. In some examples electrode portion 420 may be separately formed and attached to the outermost ring, e.g. second ring 418, such as by welding. First ring 416 may be the innermost ring and in intimate contact with vessel wall 404. For example, innermost ring 416 may be welded to vessel wall 404 around an inner edge of first ring 416.
In some embodiments, a thickness of the outermost ring may vary as a function of angular position about the vessel to which the flange is attached. For example, the outermost ring may be formed from nickel, copper or other metal less expensive and less temperature resistant than platinum or alloys thereof, wherein regions of the outermost ring adjacent electrode portion 420 are thicker than other regions of the outermost ring. For example, portions 419 of the outermost ring of the embodiment of
In the embodiment shown in
Second ring 418 is spaced apart from wall 404 of vessel 402 and can comprise a metal different from the metal or metals used in the manufacture of first ring 416. For example, while first ring 416 can be formed from a precious metal, including the platinum group metals or alloys thereof, second ring 418 can be formed from a less expensive electrical conductor, such as for example and not limitation nickel, copper or alloys thereof. Second ring 418 further includes a width W2. Width W2 may be constant, or width W2 may vary as a function of angular position around vessel 402. In the embodiment shown in
Flange 400 illustrated in
In another embodiment illustrated in
Flange 500 is similar to flanges 100, 200, 300 and 400, and comprises a body portion 514 including a first ring 516, a second ring 518 and an electrode portion 520 attached to an outermost ring. Accordingly, the foregoing description of flanges 200, 300 and 400 in respect of their major components can be applied to flange 500. Second ring 518 may, in some examples, be the outermost ring wherein electrode portion 520 may be directly coupled to second ring 518 as shown. For example, electrode portion 520 may be integral with second ring 518 and formed therewith. In some examples electrode portion 520 may be separately formed and attached to the outermost ring, e.g. second ring 518, such as by welding. First ring 516 may, in some embodiments, be the innermost ring and in intimate contact with vessel wall 504.
In the embodiment shown in
Second ring 518 is spaced apart from wall 504 of vessel 502 and can comprise a metal different from the metal or metals used in the manufacture of first ring 516. For example, while first ring 516 can be formed from a precious metal, including the platinum group metals or alloys thereof, second ring 518 can be formed from a less expensive electrical conductor, such as for example and not limitation nickel, copper and alloys thereof. Second ring 518 further includes a width W2. Width W2 may be constant, or width W2 may vary as a function of angular position around vessel 502.
In some embodiments, a thickness of the outermost ring may vary as a function of angular position about the vessel to which the flange is attached. For example, the outermost ring may be formed from nickel, copper or other metal less expensive and less temperature resistant than platinum or alloys thereof, wherein regions of the outermost ring adjacent electrode portion 520 are thicker than other regions of the outermost ring. For example, portions 519 of the outermost ring of the embodiment of
In the instance where first ring 516 is an innermost ring, an inner edge of first ring 516 can be attached to vessel wall 504 and extend in a closed loop around vessel 502. For example, the inner edge of first ring 516 may be welded to vessel wall 504. Similarly, in the example illustrated in
Similar to the embodiments of
It should further be apparent with the aid of
Flange 600, shown in
In the embodiment shown in
Additionally, first ring 616 comprises a first portion 622 and a second portion 628 corresponding, for example, to portions 222 and 228 of flange 200, respectively.
Second ring 618 is spaced apart from wall 604 of vessel 602 and accordingly second ring 618 can comprise a metal different from the metal or metals used in the manufacture of first ring 616. For example, while first ring 616 can be formed from a precious metal, including the platinum group metals or alloys thereof, second ring 618 can be formed from a less expensive electrical conductor, such as nickel or copper. Second ring 618 further includes a width W2. Width W2 may be constant, or width W2 may vary as a function of angular position around vessel 602.
In some embodiments, a thickness of the outermost ring may vary as a function of angular position about the vessel to which the flange is attached. For example, the outermost ring may be formed from nickel, copper or other metal less expensive and less temperature resistant than platinum or alloys thereof, wherein regions of the outermost ring adjacent electrode portion 620 are thicker than other regions of the outermost ring. For example, portions 650 of the outermost ring of the embodiment of
In the instance where first ring 616 is an innermost ring, an inner edge of first ring 616 can be attached to vessel wall 604 and extend in a closed loop around vessel 602. For example, the inner edge of first ring 616 may be welded to vessel wall 604. Similarly, in the example illustrated in
In the embodiment of
Shown in
Flange 700 comprises body portion 710 including first ring 712 and second ring 714. In the embodiment of
In the embodiment shown in
Second ring 714 is spaced apart from wall 704 of vessel 702 and is positioned in a closed loop about first ring 712, and, being more distant from vessel wall 704 than first ring 712 and therefore exposed to a lower temperature than first ring 712, can comprise a metal different from the metal or metals used in the manufacture of first ring 712. For example, while first ring 712 can be formed from a precious metal, including platinum group metals or alloys thereof, second ring 714 can be formed from a less expensive electrically conducting metal, such as nickel or copper. Second ring 714 further includes a width W2. Width W2 may vary as a function of angular position relative to vessel 702, or W2 may be substantially constant. In some embodiments, an inner edge of second ring 714 can be joined directly to an outer edge of first ring 712 such as by welding.
First ring 712 extends in a closed loop around vessel 702 and, in the instance where first ring 712 is the innermost ring, first ring 712 may be attached to vessel 702 around an outer perimeter of vessel wall 704. For example, an inner edge of first ring 712 may be welded to an exterior surface of vessel wall 704. Similarly, in the example illustrated in
In some embodiments, a thickness of the outermost ring may vary as a function of angular position about the vessel to which the flange is attached. For example, the outermost ring may be formed from nickel, copper or other metal less expensive and less temperature resistant than platinum or alloys thereof, wherein regions of the outermost ring adjacent electrode portion 716a, 716b are thicker than other regions of the outermost ring. For example, portions 716a, 716b may be up to or greater than 50% thicker than other regions of the outermost ring, for example in a range from about 25% thicker to about 75% thicker, such as in a range from about 30% thicker to about 70% thicker, in a range from about 35% thicker to about 60% thicker or in a range from about 40% thicker to about 55% thicker. The thicker portions of the outermost ring aid in steering the electric current around a circumference of the vessel and minimize, such as eliminate, the formation of hot spots on the outermost ring near the electrode portions. Such overheating can occur because electric current density is high in and around electrode portions 716a, 716b. The thicker portions of the outermost ring adjacent the electrode portions present an increased cross sectional area and therefore a reduced current density. Thus, portions of the outermost ring adjacent the electrode portions can be thicker than other portions of the outermost ring, for example portions of the outermost ring between the electrode portions and the thick portions adjacent thereto. As described supra, the outermost ring may be second ring 714. However, in other embodiments, second ring 714 may be a ring intermediate between the outermost ring and first ring 712, or intermediate between the outermost ring and vessel wall 704.
As further illustrated by
First ring 712 further comprises sub-portions 722a and sub-portion 722b. Sub-portions 722a and 722b may have the same thickness T2, or sub-portions 722a and 722b may have different thicknesses T2a and T2b, where T2b is different from T2a. Similar to sub-portions 718a and 718b, sub-portions 722a and 722b are separate and oppositely positioned around vessel 702. Also like sub-portions 718a and 718b, sub-portions 722a and 722b each extend less than 180 degrees around vessel 702. In some embodiments T1 is less than T2. In some embodiments T1a and T lb are equal, and T2a and T2b are equal and T1a, T lb are less than T2a, T2b. In some embodiments the material of each sub-portion may be selected to have different intrinsic electrical resistances.
It is apparent from
It should be clear to one skilled in the art, having the benefit of the foregoing disclosure, that many flange designs can be generated. In particular, a consistent design methodology can be envisioned wherein the electric current carrying capacity of the flange, as a function of angular position on the flange, can be tailored such that electric current is uniformly delivered to the vessel wall where the flange intersects (is attached to) that wall. Accordingly, in one such method, a first step comprises parameterizing an initial flange and vessel design. The initial flange and/or vessel design can be an existing physical flange and/or vessel, or the initial flange and/or vessel design can be a virtual design. By parameterize what is meant is to reduce the flange and/or vessel to the necessary parameter values that define the structure and its operating characteristics. For example, a simple, circularly symmetric flange having only a single ring attached to a vessel at an innermost edge of the ring, the vessel having a predetermined wall thickness, can be parameterized by such parameter values as, but not limited to, an outer radius defining the outer perimeter of the ring, an inner radius defining the inside edge of the flange, a thickness, and a material (itself defined at least by, for example, an electrical resistance), a wall thickness of the vessel and even a flow rate of molten material (e.g. molten glass) through the vessel. Such parameter values can be used to calculate for a predetermined electric current in the flange an electric current density at any point on or in the flange. The requisite calculations can be made, for example, with software designed or adapted for the task, such as electrical circuit analysis software. Additionally, the electric current density can be used to determine, for a predetermined flow rate of material through the vessel, a temperature of the flange or the vessel wall at a predetermined position. These calculated results can be compared to a desired electric current density and/or temperature. Flow and temperature fields can be calculated, for example, using ANSYS Fluent software.
Accordingly, the method may further comprise using the parameterized values, as well as, for example, a predetermined electric current supplied to the flange and in some examples the flow rate of material (e.g. molten glass) through the vessel, to calculate an electric current density in the flange and/or vessel, and/or a temperature in the flange and/or vessel. The calculated electric current density and/or temperature can be used as a basis for modifying the flange and/or vessel. For example, the initial design of the flange can be modified by changing at least one of, without limitation, a number of individual portions of a first ring of material comprising the flange, the thicknesses of the individual portions of the first ring, a shape of the individual portions of the first ring, a variation in width of the first ring, and intrinsic electrical resistance of one or more materials comprising rings or portions thereof, and so forth. When the changes have been made, the electric current density and/or the temperature at predetermined points on the flange and/or vessel can be recalculated and again compared to the desired difference in electric current density and/or temperature between regions of interest on the flange or vessel, for example a difference in electric current density and/or temperature between a top portion of the vessel and a side or bottom portion of the vessel. The electric current density and/or temperature at the predetermined points can also be compared to predetermined values, such as predetermined limits. The process of modifying and calculating can be iteratively applied until the desired difference in electric current density and/or temperature is achieved. Upon completion, the parameter values of the final design can be used to manufacture a flange and/or vessel exhibiting the final parameter values.
Modeling was performed using FLUENT software and software developed for electrical circuit analysis to evaluate an empty conventional flange 800 shown in
In the modeling, both flanges were paired with a second flange of identical construction spaced 60 inches (152.4 cm) away and supplied with 10,000 amps. That is, flange 800 was paired with a second flange 800 and flange 200 was paired with a second flange 200. The modeling indicated a maximum temperature in the conventional flange 800 of 2030° C., well above the melting temperature of platinum (1768.3° C.). The maximum temperature occurred in the intermediate ring on a straight line between electrode portion 810 and the top of vessel 802. The maximum electric current density was 16 amps/mm2 and occurred in the innermost ring 812 adjacent to the arcuate portions of vessel wall 804. The maximum temperature occurring in the nickel ring 810 was 1096° C.
In contrast to flange 800, flange 200 under the same conditions exhibited a maximum temperature of 1523° C. occurring in first portion 222 on a straight line between electrode portion 220 and the top of vessel 802. The maximum temperature was below the melting temperature of platinum. The maximum electric current density was 11 amps/mm2, and occurred in the same location as for flange 800. The maximum temperature in the nickel outermost ring was 650° C.
In comparison, the electric current density at the flange-vessel junction (e.g. −30 inches) at the top of the vessel for flanges 200 (curve 906), is only about 6.5 amps/mm2, and about 5.8 amps/mm2 at the flange-vessel junction (e.g. −30 inches) at the bottom of the vessel (curve 910). At the edge (side) of the vessel (curve 910) the electric current density is about 7.3 amps/mm2. Thus, the maximum variation in electric current about a circumference of the vessel at the vessel-flange junction is about 1.5 amps/mm2, indicating electric current being steered in a direction away from the top of the vessel.
More importantly, over the distance between the flanges the electric current density along the top of the vessel (curve 906) varies only approximately 0.26 amps/mm2 (between about 6.76 amps/mm2 and 6.5 amps/mm2) for the same supplied electric current as for the conventional flange. This difference amounts to about 4% of the maximum electric current density at the top of the vessel. Moreover, as clearly seen in the figure, electric current density along the top of the vessel is lowest at the vessel-flange junctions (i.e. −30 inches and +30 inches) in contrast to the conventional flange, and increases to the maximum current density rapidly as one moves from one flange to the adjacent flange. In the illustrated example, the electric current density peaks very near the vessel-flange junction. In the present example the electric current density reaches a maximum within about 8 inches (20.32 cm) of a flange, or within about 13% of the total distance between adjacent flanges. Additionally, the electric current density is substantially constant between the peaks, locations at about −22 inches and +22 inches (a distance of 44 inches, 111.76 cm) in the example of
Summarizing, for the same input electric current, a flange according to embodiments described herein is capable of significantly reducing the electric current density at the junction between the flange and the vessel wall at a point nearest the position of the electrode portion (where electric current is introduced into the flange body), e.g. the top of the vessel in the present example, when compared to a conventional flange, and is shown to produce a more consistent (uniform) electric current density along the top of the vessel over the distance between adjacent flanges.
In comparison, the temperature at the top (12 O'clock position) of the vessel at the vessel flange junction for flange 200 (curve 918), the temperature is approximately 1300° C. and about 1075° C. at the bottom of the vessel (curve 922). At the 3 O'clock position of the vessel (curve 920) at the vessel-flange junction the temperature is about 1220° C.
The data for
At a position of about −25 inches (line 926 in
It will be apparent to those skilled in the art that various modifications and variations can be made to embodiments of the present disclosure without departing from the spirit and scope of the invention. Thus, it is intended that the present disclosure cover the modifications and variations of such embodiments provided they come within the scope of the appended claims and their equivalents.
This application claims the benefit of priority under 35 U.S.C. § 119 of U.S. Provisional Application Ser. No. 62/244,462, filed on Oct. 21, 2015, the content of which is relied upon and incorporated herein by reference in its entirety.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US16/58084 | 10/21/2016 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62244462 | Oct 2015 | US |