The present invention relates to an apparatus and a method for producing a web of fibrous material.
From U.S. Pat. No. 2,624,245 a method is known for producing continuous webs of paper extensible in a mainly longitudinal direction, i.e. in the direction in which the web extends. This method uses a plant comprising a heated roll having a smooth, preferably chromium-plated surface, and a rubber belt of a certain thickness maintained adhering to the heated roll along a certain portion of its surface by a series of transmission rollers which are at least partly motor-driven. The diameter of the roller which causes the rubber belt to adhere to the commencement of the portion in contact with the heated roll (upstream transmission roller) is small compared with the diameter of said heated roll, such that at their contact generating line the rubber belt undergoes a sudden deviation and then a sudden variation in concavity. The combined effect of this sudden concavity variation, to which the rubber belt is subjected by the upstream transmission roller, which causes said belt to adhere to the heated roll, means that when a paper web under formation, still having a high water content, is introduced between the rubber belt and the heated roll, it is subjected in the portion immediately downstream of the contact generating line to a longitudinal compaction linked to the water quantity contained, to the thickness of the rubber belt, and to the ratio of the diameter of the upstream transmission roller to the diameter of the heated roll.
In its turn, this longitudinal compaction gives the paper web obtained a longitudinal extensibility of about 15% in practice.
However, paper obtained by this method has almost no transverse extensibility, in the sense that the value of this transverse extensibility is of the order of 4-5%, i.e. virtually the same as that found in any traditionally produced paper, for equal mix and refining. It should be also noted that higher values of transverse extensibility can be achieved only by costly refining methods at high density, using complex costly plants with high energy consumption.
From WO2005/100686 a machine is known for producing paper extensible longitudinally and transversely which at the same time is of better smoothness than that obtainable by traditional methods. This known machine comprises a compaction station with a pair of counter-rotating rollers, one of which is of steel, is driven at higher velocity and comprises in its surface a series of circumferentially extending incisions of spiral development, while the other is covered with a rubber layer and is driven at lesser velocity.
When the paper web under formation is made to pass between the two rollers, the combined effect of their different rotation velocity and the presence of the incisions on the steel roller causes longitudinal compaction of the material forming the web and its accumulation within the incisions of the steel roller, and essentially results in the obtaining of a paper web of smooth surface which at the same time possesses good longitudinal and transverse extensibility.
This known solution has proved valid from a theoretical viewpoint but has highlighted limits and drawbacks in its practical implementation, in particular in achieving the high production rate for which current papermaking machines are dimensioned (about 1000 m/min). Taking account of the fact that at the nip between the rubber roller and the steel roller the rubber layer is subjected to local temporary compression, it is clear that a usual rubber roller of diameter 500 mm is subjected to 637 compression cycles per minute, i.e. more than 10 compressions per second. However experimental tests carried out under actual operating conditions have shown that if the number of compressions exceeds 2 per second, the life of the roller suffers, even with the use of complex costly cooling systems.
Hence to reduce to this value the number of compressions of the rubber roller, rollers of a diameter of at least 2500 mm would have to be used, with considerable machine dimension problems and periodic replacement of the rubber layer, an operation which cannot be carried out in the paper works, but only by specialized industries, which are usually not equipped to operate on rollers of such dimensions.
Moreover, rubber-coated rollers of these dimensions present considerable difficulties in their replacement by others with their outer layer of a rubber of different properties such as required for obtaining paper webs of particular characteristics.
From GB 868391 it is also known to produce an extensible paper web by passing the paper web under formation between a rubber roller and a steel roller made to rotate in the opposite directions at the same peripheral velocity. The compression of the paper web on passage between the two rollers results in a temporary local reduction in cross-section, so increasing its passage velocity. When at the exit from the two rollers the paper web under formation regains its original cross-section, the consequent reduction in velocity, accompanied by its adherence to the rubber roller, results in its longitudinal compaction. This is a technical principle totally different from that known from WO2005/100686, which instead uses the different peripheral velocity of two counter-rotating rubber and steel rollers to produce longitudinal compaction of the forming paper web and simultaneous accumulation thereof in incisions provided in the steel roller; and this different principle makes it impossible to combine the teachings deriving from the two aforesaid documents.
An object of the invention is to obtain a web of fibrous material which overcomes the limits and drawbacks of the state of the art and which presents both a high longitudinal extensibility, in particular up to 20%, and also a high transverse extensibility, in particular exceeding 6%, without the use of high density refining.
Another object of the invention is to obtain a web of fibrous material with an apparatus which does not require costly maintenance, and in particular does not require frequent costly replacement of components made of materials which undergo wear.
Another object of the invention is to obtain a web of fibrous material formed from cellulose fibres, from vegetable fibres in general and/or from synthetic fibres, and in any event with characteristics which can be modified within certain limits, according to requirements.
These and other objects which will be apparent from the ensuing description are attained according to the invention, by an apparatus for producing a fibrous material web of high longitudinal and transverse extensibility, as indicated in claim 1.
A method for producing a fibrous material web of high longitudinal and transverse extensibility is indicated in claim 14.
The present invention is further clarified hereinafter with reference to the accompanying drawings, in which:
The apparatus according to the invention for producing a web of fibrous material of high longitudinal and transverse extensibility, for example of paper material, can be inserted into an in-line plant for paper production, in which case it is fed with a sheet of cellulose fibre (virgin, recovered or mixed) to form the web, or can consist of a self-standing apparatus, in which case it is fed with an already formed paper web previously subjected to wetting to a water content between 82% and 30%.
A similar apparatus and plant can also be used to produced vegetable fibre webs, non-woven fabric webs or synthetic fibre webs; in this case it is not possible to talk of water content of the sheet of cellulose fibre mix or of the rewetted paper web, but of the pliability of the fibrous material web, and essentially of its softening temperature.
Independent thereof, the apparatus comprises a cylindrical roll 2, of metal material, possibly covered with a layer of material presenting different mechanical characteristics (for example ceramic material), and in any event comprising on its cylindrical surface a series of incisions 4 extending along parallel circumferential lines or along spiral lines, and in any event extending with a pattern having a circumferential component.
They can have a depth between 0.01 and 2 mm, preferably between 0.05 and 0.5 mm, width between 0.01 and 2 mm, preferably between 0.07 and 0.9 mm, and pitch between 0.01 and 10 mm, preferably between 0.125 and 1.25 mm. Moreover, in the case of spiral incisions, the angle of inclination can be from the minimum value allowed by the width of the incision to a maximum of 45°, preferably between 5° and 20°, with the spiral pattern being the same along the entire axial length of the roll 2 or be opposing on the two halves of the roll.
As an alternative to the cylindrical shape, the roll 2 can have a convex shape (not shown) which has proved particularly useful for compensating the flexure of its shaft resulting from the forces applied to the ends thereof to exert pressure on the opposing roller, as apparent hereinafter.
The roll 2 is made to rotate at a peripheral velocity v1 substantially equal to the operative velocity of the upstream station, i.e. at the velocity with which a sheet of fibrous material 6 to be processed is fed.
The apparatus according to the invention also comprises a belt 8 of rubber or of different elastic material stretched between motorized rollers 10 and having a thickness between 1 cm and 10 cm, preferably between 2.5 cm and 5 cm, and hardness between 24° Shore and 70° Shore, preferably between 29° Shore and 50° Shore.
The rollers 10 present a degree of friction against the rubber belt 8 sufficient to ensure its driving at a velocity v2 less than the peripheral velocity v1 of the roll 2. In particular, the ratio v1/v2 varies between 1.05 and 1.40.
The belt 8 is substantially inextensible longitudinally (during operation it presents a maximum elongation of 5%) at least on that side adhering to the rollers 10, which inextensibility can be achieved, for example, by incorporating longitudinal steel wires into the belt or applying an inextensible fabric to the belt.
Moreover the belt 8 must have a dimensional stability along its entire length, to prevent possible deformations, given that on one side it is in contact with the roll 2, having a peripheral velocity v1, while on the other side it is made to advance at a velocity v2<v1, and is hence braked longitudinally.
The belt 8 is maintained pressed against the roll 2 by a presser roller 12, made preferably of steel, possibly covered with a surface layer of suitable mechanical characteristics. It can be idle or motorized, but in any event it must have a peripheral velocity of v2. The pressure with which the roller 12 presses the belt 8 against the roll 2 is controlled by suitable mechanical, pneumatic or hydraulic known means. This pressure is between 1 kg and 200 kg per centimetre of width of the belt 8, and is preferably between 20 kg and 40 kg.
The apparatus according to the invention operates in the following manner.
In the initial stage, i.e. before the apparatus is fed with the fibrous material sheet 6, the roll 2 and the rollers 10, 12 rotate at the same peripheral velocity v1 with the roller 12 simply resting on the roll 2.
Under these conditions, the fibrous material sheet 6, having a water content between 82% and 30% in the case of cellulose or vegetable fibre in general, or at a temperature not less than the initial softening temperature in the case of synthetic fibres, and advancing at the velocity v1, is introduced between the rubber roller 8 and the roll 2; the rollers 10 and 12 are progressively raised to the velocity v2<v1, and the roller 12 is pressed with increasing pressure against the roll 2, to squeeze the belt 8 and the sheet 6 of fibrous material adhering to it.
The combined effect of the longitudinal braking and the squeezing in the thickness direction is to cause the sheet 6 to locally fill the incisions 4 of the roll 2, and become accumulated longitudinally in bands corresponding to the incisions and with curved compaction lines 14, of the type illustrated in
In its turn, this longitudinal accumulation and the particular arrangement of the fibres, determine the longitudinal and transverse extensibility of the formed fibrous material web, when this reaches the final moisture content of the paper in the case of vegetable fibres, or its dimensional stability in the case of synthetic fibres.
The degree of both longitudinal and transverse extensibility depends on the ratio between the velocities v1 and v2, on the force with which the belt 8 is pressed against the roll 2, on the characteristics of the incisions 4 on the roll 2, on the pliability of the sheet 6 at the commencement and termination of treatment, and on the physical and geometrical characteristics of the rubber belt 8.
Experimental tests carried out to test the effectiveness of the method have enabled paper to be obtained with a degree of longitudinal extensibility of about 20% and transverse extensibility of about 15%.
If the apparatus according to the invention is inserted into a paper web production line, the plant also comprises, in traditional manner, stations for tensioning the rubber belt 8, for its centring, for its cooling, and for its grinding to maintain its thickness uniform.
Before the fibrous material sheet 6 is engaged between the rubber belt 8 and the roll 2, it is impregnated with specific additives able to provide particular characteristics and properties to the final web obtained.
Finally the roll 2 and/or rollers 10 and/or 12 are subjected to cooling or heating during operation, according to specific technological requirements and/or to the properties which the web of fibrous material is required to present.
From the aforegoing it is apparent that the apparatus and method for obtaining webs of fibrous material according to the invention are particularly advantageous, in that they enable webs to be obtained with characteristics of high extensibility both longitudinally and transversal by simple apparatuses of low installation, running and maintenance costs, and with the facility for modifying the extensibility characteristics of the web obtained, on the basis of specific requirements.
In order to obtain fibrous material webs of different characteristics and performance, the fibrous material sheet 6 can be subjected to more than one compaction treatment of the described type, in the sense that the web leaving one apparatus can be inserted, after being possibly subjected to other intermediate treatments, into another apparatus in which the rubber belt 8 and/or the incisions on the surface of the roll 2 and/or the velocities in play and/or the pressures in play can be different.
In the variant illustrated in
The fibrous material sheet 6, which enters along a first contact generating line between the first rubber belt 8 and the roll 2 at the velocity v1 leaves these at the velocity v2<v1, compacted in both the longitudinal and traverse directions. The said sheet 6, which is withdrawn at its exit along this first contact generating line at the velocity v2, is made to enter along a second contact generating line between the second rubber belt 8′, which advances at a velocity v3<v2, and the said roll 2, and is subjected to a second compaction treatment.
As there is only one roll 2 there is only a single set of incisions 4 to determine the two compaction treatments on the fibrous material sheet 6.
However, as the two rubber belts 8, 8′ can be different, the pressures with which they are pressed against the roll 2 can be different and the velocities in play are different, the second treatment will give the sheet 6 characteristics and performance which are different from those obtained by the first treatment.
From the aforegoing it is apparent that the apparatus and method for producing extensible paper according to the present invention are much more advantageous than those of the state of the art, and in particular of U.S. Pat. No. 2624245, WO2005/100686 and GB 868391, in that:
| Number | Date | Country | Kind |
|---|---|---|---|
| VE2013A000038 | Jul 2013 | IT | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2014/001379 | 7/22/2014 | WO | 00 |