This invention relates to a continuous process and related apparatus for producing structural panels using settable slurry, and more specifically, to a slurry mixer apparatus used in the manufacture of reinforced cementitious panels, referred to herein as structural cement panels (SCP), in which fibers are combined with quick-setting slurry for providing flexural strength.
Cementitious panels have been used in the construction industry to form the interior and exterior walls of residential and/or commercial structures. The advantages of such panels include resistance to moisture compared to standard gypsum-based wallboard. However, a drawback of such conventional panels is that they do not have sufficient structural strength to the extent that such panels may be comparable to, if not stronger than, structural plywood or oriented strand board (OSB).
Typically, the cementitious panel includes at least one hardened cement composite layer between layers of a reinforcing or stabilizing material. In some instances, the reinforcing or stabilizing material is fiberglass mesh or the equivalent. The mesh is usually applied from a roll in sheet fashion upon or between layers of settable slurry. Examples of production techniques used in conventional cementitious panels are provided in U.S. Pat. Nos. 4,420,295; 4,504,335 and 6,176,920, the contents of which are incorporated by reference herein. Further, other gypsum-cement compositions are disclosed generally in U.S. Pat. Nos. 5,685,903; 5,858,083 and 5,958,131.
U.S. Pat. No. 6,620,487 to Tonyan, which is incorporated herein by reference in its entirety, discloses a reinforced, lightweight, dimensionally stable panel capable of resisting shear loads when fastened to framing equal to or exceeding shear loads provided by plywood or oriented strand board panels. The panels employ a core of a continuous phase resulting from the curing of an aqueous mixture of calcium sulfate alpha hemihydrate, hydraulic cement, an active pozzolan and lime, the continuous phase being reinforced with alkali-resistant glass fibers and containing ceramic microspheres, or a blend of ceramic and polymer microspheres, or being formed from an aqueous mixture having a weight ratio of water-to-reactive powder of 0.6/1 to 0.7/1 or a combination thereof. At least one outer surface of the panels may include a cured continuous phase reinforced with glass fibers and containing sufficient polymer spheres to improve nailability or made with a water-to-reactive powders ratio to provide an effect similar to polymer spheres, or a combination thereof.
US Patent Application Publication No. 2005/0064055 to Porter, application Ser. No. 10/665,541, which is incorporated herein by reference in its entirety, discloses an embedment device for use in a structural panel production line wherein a slurry is transported on a moving carrier relative to a support frame, and chopped fibers are deposited upon the slurry, includes a first elongate shaft secured to the support frame and having a first plurality of axially spaced disks, a second elongate shaft secured to the support frame and having a second plurality of axially spaced disks, the first shaft being disposed relative to the second shaft so that the disks intermesh with each other. The intermeshing relationship enhances embedment of the fibers into the slurry and also prevents clogging of the device by prematurely set slurry particles.
US Patent Application Publication No. 2005/0064164 to Dubey et al., application Ser. No. 10/666,294, incorporated herein by reference in its entirety, discloses a multi-layer process for producing structural cementitious panel which includes: (a.) providing a moving web; (b.) one of (i) depositing a first layer of individual, loose fibers upon the web, followed by depositing a layer of settable slurry upon the web and (ii) depositing a layer of settable slurry upon the web; (c.) depositing a second layer of individual, loose fibers upon the slurry; (d.) actively embedding said second layer of individual, loose fibers into the slurry to distribute said fibers throughout the slurry; and (e.) repeating steps (ii) through (d.) until the desired number of layers of settable fiber-enhanced slurry is obtained and so that the fibers are distributed throughout the panel. Also provided are a structural panel produced by the process, an apparatus suitable for producing structural cementitious panels according to the process, and a structural cementitious panel having multiple layers, each layer created by depositing a layer of settable slurry upon a moving web, depositing fibers upon the slurry and embedding the fibers into the slurry such that each layer is integrally formed with the adjacent layers.
U.S. Pat. No. 6,986,812 of Dubey et al., incorporated herein by reference in its entirety, features a slurry feed apparatus for use in a SCP panel production line or the like application where settable slurries are used in the production of building panels or board. The apparatus includes a main metering roll and a companion roll placed in close, generally parallel relationship to each other to form a nip in which a supply of slurry is retained. Both rolls preferably rotate in the same direction so that slurry is drawn from the nip over the metering roll to be deposited upon a moving web of the SCP panel production line. A thickness control roll is provided in close operational proximity to the main metering roll for maintaining a desired thickness of the slurry.
U.S. Patent Application Publication No. 2006/0174572 to Tonyan et al., incorporated herein by reference in its entirety, discloses non-combustible SCP panel metal frame systems for shear walls.
In preparing the SCP panels, an important step is mixing cementitious powder to form slurry. The slurry is then withdrawn from the bottom of the chamber and pumped through a cavity pump to the slurry feeding apparatus. A typical conventional continuous cement mixer is the DUO MIX2000 continuous cement mixer from M-TEC GmbH, Neuenburg, Germany which is used in the construction industry to mix and pump concrete slurry.
However, conventional mixers tended to clog resulting in production interruptions. Thus, there is a need for an improved wet mixing apparatus that insure supply of sufficient mixed cementitious slurry to supply a continuous panel production line. The degree of mixing of the powder and water in the mixer is also an area of desired improvement to breakup small lumps in the wet mix and to more thoroughly mix the powder and water to allow for the smooth and consistent slurry to provide a continuous curtain of slurry for use in the continuous manufacturing line.
There is a desire for an improved process and/or a related apparatus for producing fiber-reinforced cementitious panels which results in a board with structural properties comparable to structural plywood and OSB which reduces production line downtime. There is also a desire for a process and/or a related apparatus for producing such structural cementitious panels which more efficiently uses component materials to reduce production costs over conventional production processes.
Furthermore, the above-described cementitious structural panels, also referred to as SCP's, are preferably configured to behave in the construction environment similar to plywood and OSB. Thus, the SCP panels are preferably nailable and can be cut or worked using conventional saws and other conventional carpentry tools. Further, the SCP panels should meet building code standards for shear resistance, load capacity, water-induced expansion and resistance to combustion, as measured by recognized tests, such as ASTM E72, ASTM 661, ASTM C 1185 and ASTM E136 or equivalent, as applied to structural plywood sheets.
The present invention features a wet mixer apparatus for preparing slurry to be fed to a slurry feed apparatus (typically known as a “headbox”) for use in depositing slurry on a moving web of a structural cementitious panel (SCP panel) production line or the like where settable slurries are used for producing fiber reinforced building panels or boards.
The mixer includes an auger which feeds dry cementitious material to a vertical chamber. The dry cementitious material then drops from the auger outlet into a pool of slurry in the vertical mixing chamber. Meanwhile, liquid is separately dropped into the pool of slurry in the vertical mixing chamber. Then, the mixture and liquid are mixed in the pool of slurry for a sufficient time to form a slurry having desirable properties. Then the slurry is discharged from a lower portion of the mixer.
The present wet cement mixer has a sufficient size and applies sufficient shear force in the vertical mixing chamber to produce a uniform slurry, increase the volume of slurry available in the chamber, and avoid slurry level fluctuations to support higher manufacturing line speeds.
If desired, a liquid level control sensor is used to measure the level of the slurry in the vertical chamber of the mixer. The liquid level sensor also serves to actuate control of the amount of water and cementitious powder fed into the vertical mixing chamber to ensure adequate mixing of the slurry while ensuring an adequate supply of slurry to the manufacturing line for preparing a fiber reinforced structural cement panel.
To result in adequately mixed slurry, the vertical chamber provides a suitable mixing volume for an average slurry residence time of typically about 10 to about 360 seconds while the spinning paddle applies shear force to the slurry in the mixing chamber. Typically, the vertical chamber provides an average slurry residence time of about 15 to about 240 seconds. The RPM range of the mixer paddle is typically 70 RPM to 270 RPM. Other typical ranges for average slurry residence time are from about 15 seconds to about 30 seconds or about 20 seconds to about 60 seconds.
Typically the mixer is employed in a multi-layer process for producing structural cementitious panels (SCP's or SCP panels), and SCP's produced by such a process. After one of an initial deposition of loosely distributed, chopped fibers or a layer of slurry upon a moving web, fibers are deposited upon the slurry layer. An embedment device thoroughly mixes the recently deposited fibers into the slurry so that the fibers are distributed throughout the slurry, after which additional layers of slurry, then chopped fibers are added, followed by more embedment. The process is repeated for each layer of the panel, as desired. Upon completion, the board has a more evenly distributed fiber component, which results in relatively strong panels without the need for thick mats of reinforcing fibers, as are taught in prior art production techniques for cementitious panels.
In addition, the resulting panel is optionally provided with increased amount of fibers per slurry layer than in prior panels.
In a preferred embodiment, multiple layers of chopped individual loose fibers are deposited relative to each layer of deposited slurry. The preferred sequence is that a layer of loose fibers are deposited, upon either the moving web or existing slurry, followed by a layer of slurry, then another layer of fibers. Next, the fiber/slurry/fiber combination is subjected to embedding to thoroughly mix the fibers in the slurry. This procedure has been found to permit the incorporation and distribution of a relatively larger amount of slurry fibers throughout the slurry using fewer slurry layers. Thus, panel production equipment and processing time can be reduced, while providing an SCP panel with enhanced strength characteristics.
More specifically, a process is provided for producing structural cementitious panels made of at least one layer of fiber reinforced cementitious slurry, the process for each such layer of slurry including providing a moving web; depositing a first layer of individual, loose fibers upon the web; depositing a layer of settable slurry upon the deposited first layer of individual, loose fibers; depositing a second layer of individual, loose fibers upon the deposited layer of settable slurry; and actively embedding both layers of individual, loose fibers into the layer of slurry to distribute the fibers throughout the slurry.
In another embodiment, an apparatus for producing a multi-layered structural cementitious panel includes a conveyor-type frame supporting a moving web; a first loose fiber distribution station in operational relationship to the frame and is configured for depositing loose fibers upon the moving web; a first slurry feed station in operational relationship to the frame and configured for depositing a thin layer of settable slurry upon the moving web so that the fibers are covered. A second loose fiber distribution station is provided in operational relationship to the frame and is configured for depositing loose fibers upon the slurry. An embedment device is in operational relationship to the frame and is configured for generating a kneading action in the slurry to embed the fibers into the slurry.
In yet another embodiment, a process is provided for making fiber-embedded cementitious panels, comprising:
using a first formula:
for determining a projected fiber surface area fraction of a first fiber layer to be deposited in each settable slurry layer of the resulting panel;
using a second formula:
for determining a projected fiber surface area fraction of a second fiber layer to be deposited in each settable slurry layer of the resulting panel;
providing a desired slurry volume fraction Vf of a percentage of the fibers in the fiber-reinforced slurry layer;
adjusting at least one of the fiber diameter df, and a fiber-reinforced slurry layer thickness tl to in the range of 0.05-0.35 inches, and further apportioning the volume fraction Vf of fibers into a proportion Xf of the supply of fibers comparing the fibers in the second layer to the fibers in the first fiber layer so that the fiber surface area fraction Sf1,lP and the fiber surface area fraction Sf2,lP for each fiber layer is less than 0.65;
providing a supply of loose, individual fibers according to the above-calculated fiber surface area fraction Sf1,lP;
providing a moving web;
depositing the first layer of loose, individual fibers upon the web;
depositing a layer of settable slurry upon the first layer of individual, loose fibers;
depositing the second layer of loose, individual fibers upon the layer of settable slurry; and
embedding the loose, individual fibers in the slurry so that the multiple layers of fibers are distributed throughout each slurry layer in the panel.
Referring now to
In this embodiment, a web 26 of Kraft paper, release paper, or a plastic carrier, for supporting a slurry prior to setting, may be provided and laid upon the carrier 14 to protect it and/or keep it clean.
However, it is also contemplated that, rather than the continuous web 26, individual sheets (not shown) of a relatively rigid material, e.g., sheets of polymer plastic, may be placed on the carrier 14.
It is also contemplated that the SCP panels produced by the present line 10 are formed directly upon the carrier 14. In the latter situation, at least one belt washing unit 28 is provided. The carrier 14 is moved along the support frame 12 by a combination of motors, pulleys, belts or chains which drive the main drive roll 16 as is known in the art. It is contemplated that the speed of the carrier 14 may vary to suit the product being made.
In the present invention, structural cement panel (SCP panel) production is initiated by depositing a layer of loose, chopped fibers 30 of about one inch in size upon a plastic carrier on the web 26. A variety of fiber depositing and chopping devices are contemplated by the present line 10. For example, a typical system employs a rack 31 holding several spools 32 of fiberglass cord, from each of which a length or string 34 of fiber is fed to a chopping station or apparatus, also referred to as a chopper 36. Typically a number of strands of fiberglass are fed at each of the chopper stations.
The chopper 36 includes a rotating bladed roll 38 from which project radially extending blades 40 extending transversely across the width of the carrier 14, and which is disposed in close, contacting, rotating relationship with an anvil roll 42. In the preferred embodiment, the bladed roll 38 and the anvil roll 42 are disposed in relatively close relationship such that the rotation of the bladed roll 38 also rotates the anvil roll 42, however the reverse is also contemplated. Also, the anvil roll 42 is preferably covered with a resilient support material against which the blades 40 chop the cords 34 into segments. The spacing of the blades 40 on the roll 38 determines the length of the chopped fibers. As is seen in
The present production line 10 includes a slurry preparation and feeding section 2 (
While a variety of settable slurries are contemplated, the present process is particularly designed for producing structural cement panels (SCP panels). As such, the slurry 46 is preferably comprised of varying amounts of Portland cement, gypsum, aggregate, water, accelerators, plasticizers, foaming agents, fillers and/or other ingredients well known in the art, and described in the patents listed below which have been incorporated by reference. The relative amounts of these ingredients, including the elimination of some of the above or the addition of others, may vary to suit the intended use of the final product.
U.S. Pat. No. 6,620,487 to Tonyan et al., incorporated herein by reference in its entirety, discloses a reinforced, lightweight, dimensionally stable structural cement panel (SCP) which employs a core of a continuous phase resulting from the curing of an aqueous mixture of calcium sulfate alpha hemihydrate, hydraulic cement, an active pozzolan and lime. The continuous phase is reinforced with alkali-resistant glass fibers and containing ceramic microspheres, or a blend of ceramic and polymer microspheres, or being formed from an aqueous mixture having a weight ratio of water-to-reactive powder of 0.6/1 to 0.7/1 or a combination thereof. At least one outer surface of the SCP panels may include a cured continuous phase reinforced with glass fibers and containing sufficient polymer spheres to improve nailability or made with a water-to-reactive powders ratio to provide an effect similar to polymer spheres, or a combination thereof.
If desired the composition may have a weight ratio of water-to-reactive powder of 0.4/1 to 0.7/1.
Various formulations for the composite slurry used in the current process are also shown in published US applications US2006/185267, US2006/0174572; US2006/0168905 and US 2006/0144005, all of which are incorporated herein by reference in their entirety. A typical formulation would comprise as the reactive powder, on a dry basis, 35 to 75 wt. % calcium sulfate alpha hemihydrate, 20 to 55 wt. % hydraulic cement such as Portland cement, 0.2 to 3.5 wt. % lime, and 5 to 25 wt. % of an active pozzolan. The continuous phase of the panel would be uniformly reinforced with alkali-resistant glass fibers and would contain 20-50% by weight of a uniformly distributed lightweight filler particles selected from the group consisting of ceramic microspheres, glass microspheres, fly ash cenospheres and perlite. Although the above compositions for the SCP panels are preferred, the relative amounts of these ingredients, including the elimination of some of the above or the addition of others, may vary to suit the intended use of the final product.
An embodiment of the wet powder mixer 47 of this invention is shown in
Volumetric feeding systems would use the auger screw conveyor 163 running at a constant speed to discharge powder from the storage hopper bin 160 at a constant rate (volume per unit time, e.g., cubic feet per minute. Gravimetric feeding systems generally use a volumetric feeder associated with a weighing system to control the discharge of powder from the storage hopper bin 160 at a constant weight per unit of time, e.g., pounds per minute. The weight signal is used via a feedback control system to constantly monitor the actual feed rate and compensate for variations in bulk density, porosity, etc. by adjusting the speed (RPM) of the auger screw 163.
The auger screw 163 feeds the powder directly into the vertical mixing chamber 165 through powder inlet 166 located in an upper section 165A of the vertical mixing chamber 165. Then the powder drops by gravity into the agitator equipped lower section 165B of the vertical mixing chamber 165.
Liquid comprising water is simultaneously supplied to the vertical chamber 165 by water inlets 167, e.g. nozzles, disposed around the perimeter of the upper portion 165A of the chamber 165 at a point below the dry powder inlet 166 so that it also drops to the level of the agitator section (lower portion 165B) of the vertical chamber 165. The direction of the individual water inlets 167 can be manually adjusted to be directed on the paddle blades, etc. to maintain the surfaces free from powder build-up. The individual water inlets 167 may be provided with valves 167A. Dropping the powder and liquid separately into the vertical chamber 165 advantageously avoids clogging at the inlet of the powder to the chamber 165, that might occur if the liquid and powder were mixed before entering the chamber 165, and permits feeding the powder directly into the vertical chamber using a smaller outlet for the auger 163 than would be used if the liquid and powder were mixed before entering the chamber 165.
The water and powder are thoroughly mixed by the mixer paddle 174 which has multiple paddle blades 175 that are rotated on the paddle central shaft 173 (
The level of the slurry 46 in the vertical mixing chamber 165 is controlled by electrical level control sensor 169 disposed within the vertical mixing chamber 165. The control sensor 169 controls the flow of water through electronically controlled valves 167A and controls the powder feed into the vertical chamber 165 by turning the auger motor 164 on or off via a controller 162A. The control of the volume of added water and slurry is thus used to control both the volume of the slurry in the vertical mixing chamber 165 and the mixing residence time in the vertical mixing chamber 165. Once the slurry 46 is adequately mixed, it is pumped from the bottom of the vertical mixing chamber 165 by the slurry pump 170 to the slurry feeding apparatus 44 by means of pump outlet 172. The pump 170 is run by the paddle central shaft 173 that is driven by the top mounted electric motor 168. However, a separate pump motor (not shown) could be used to drive the pump 170 if desired.
The mixing residence time of the powder and water in the vertical mixing chamber 165 is important to the design of the vertical chamber 165. The slurry mixture 46 must be thoroughly mixed and be of a consistency that can be easily pumped and deposited uniformly over the much thicker fiberglass layer on the web.
To result in adequately mixed slurry 46, the vertical chamber 165 provides a suitable mixing volume for an average slurry residence time of typically about 10 to about 360 seconds while the spinning paddle 174 applies shear force to the slurry in the mixing chamber. Typically, the vertical chamber 165 provides an average slurry residence time of about 15 to about 240 seconds. The RPM range of the mixer paddle 174 is typically 70 RPM to 270 RPM. Other typical ranges for average slurry residence time are from about 15 seconds to about 30 seconds or about 20 seconds to about 60 seconds.
A typical embodiment of a vertical chamber 165 of the mixer 47 has a nominal inside diameter of about 8 to 14 inches (20.3 to 35.6 cm) or 10 to 14 inches (25.4 to 35.6 cm), e.g., 12 inches (30.5 cm.), a total vertical height of about 20 to 30 inches (50.8 to 76.2 e.g., about 25 inches (63.5 cm) and a vertical height below sensor 169 of about 6 to 10 inches (15.2 to 25.4 cm), e.g. about 8 inches (20.3 cm.). As the diameter increases, the paddles should be designed to accommodate these larger diameters to minimize the vortex effect caused by increases paddle tip speed at a given RPM as discussed above. The outer tips of the paddles are generally designed to be close, e.g., within about a quarter inch (0.64 cm) or about an eighth inch (0.32 cm), of the inner walls of the chamber 165. Too great a distance between the paddle tips and the inner walls of the chamber 165 would result in slurry build-up.
The vertically mounted paddle 174 has an extended central shaft 173 as shown in
Referring now to
The preferred slurry feeder 44 includes a main metering roll 48 disposed transversely to the direction of travel “T” of the carrier 14. A companion or back up roll 50 is disposed in close, parallel, rotational relationship to the metering roll 48. Slurry 46 is deposited in a nip 52 between the two rolls 48, 50.
The slurry feeder 44 also has a gate 132 mounted to sidewalls 54 of the slurry feed apparatus 44 to be mounted adjacent to the surface of the metering roll 48 to form a nip 55 therebetween. As seen in
While other sizes are contemplated, typically the metering roll 48 has a larger diameter than the companion roll 50.
Also, typically one of the rolls 48, 50 has a smooth, stainless steel exterior, and the other, preferably the companion roll 50, has a resilient, non-stick material covering its exterior.
In particular, the gate 132 comprises a blade 132A mounted to a vibrating gate support shaft/bar (not shown) and, optionally a stiffening member (not shown) mounted to the vibrating gate support shaft/bar. The gate blade 132a is typically made of 16-12 gauge stainless sheet metal.
The stiffening member is attached to the backside of the vibrating gate support shaft and vibrating gate 132. The gate 132 is vibrated by means of a rotary vibrator 155. The rotary vibrator 155 is mounted on the stiffening channel/member on the—backside—of the gate. Piece 156 is actually just a piece of flat stock that “clamps” the sheet metal gate to the gate support shaft (aluminum square stock).
If the stiffening member is not provided then the rotary vibrator may be attached to the gate support shaft or other suitable portion of the gate 132. The vibrating means is typically a pneumatic rotary ball vibrator. The level of vibration can be controlled with a conventional air regulator (not shown).
The stiffening member functions not only to stiffen the slurry gate, but, by mounting the vibratory unit on this stiffening member, this distributes the vibration across the length of the device more evenly. For example, if we mount the vibratory unit directly to the slurry gate, without the stiffening member, the vibration from the vibratory unit would be highly localized at the mounting point, with relatively little vibration out on the edges of the sheet. This is not to say that the vibratory unit cannot be mounted anywhere besides the stiffening member, but it is a preferred location since a stiffening member is typically employed and it does a good job of equally distributing the vibration.
The gate 132 may be mounted to the sidewalls 54 of the headbox 44 by a support system (not shown) to permit the position of the blade to be adjusted the horizontally, vertically as well. The support system includes a pivot pin attached, respectively, to each end of the gate support shaft and seated in an adjustable mount attached to a sidewall 54 of the slurry feed apparatus. An embodiment of the adjustable mount has a pivot yoke seated in a U-shaped member. Screws pass through the upwardly extending legs of the U-shaped mount to permit forward and backwards adjustment of the position of the pivot yoke, and in turn the gate 132. Also, bolts are provided through holes of the U-shaped member for permitting up and down adjustment of the position of the pivot yoke, and in turn the gate 132.
Preferably, the vibrating gate 132 may be pivotally adjusted to vary the gap “D” (
The vibrating gate 132 helps to prevent significant build-up of slurry 46 on the gate 132 and controls the thickness of the slurry 46 deposited on the metering roll 48. The vibrating gate 132 can easily be removed from the wall mounts for cleaning and maintenance.
Additional details of the slurry feeder (headbox) 44 are disclosed in U.S. patent application Ser. No. ______ (Attorney Docket No. APV31960/3991) filed concurrently with the present application and incorporated herein by reference in its entirety.
Typically the slurry feeder 44 has a pair of relatively rigid sidewalls 54 (one shown), preferably made of, or coated with non-stick material such as TEFLON® material or the like. The sidewalls 54 prevent slurry 46 poured into the nip 52 from escaping out the sides of the slurry feeder 44. The sidewalls 54, which are preferably secured to the support frame 12 (
The slurry feeder 44 deposits an even layer of the slurry 46 of relatively controlled thickness upon the moving carrier web 26. Suitable layer thicknesses range from about 0.08 inch to 0.16 inch or 0.25 inch. However, with four layers preferred in the structural panel produced by the production line 10, and a suitable building panel being approximately 0.5 inch, an especially preferred slurry layer thickness is in the range of 0.125 inch. However, for a target panel forming thickness is about 0.84″, the standard layer thickness is typically closer to about 0.21 inches at each of the 4 forming stations. A range of 0.1 inch to 0.3 inch per headbox may also be suitable.
Thus, the relative distance “D” (
To ensure a uniform disposition of the slurry 46 across the entire web 26, the slurry 46 is delivered to the slurry feeder 44 through a hose 56 or similar conduit having a first end 60 (
The reciprocating dispensing mechanism 64 is explained in greater detail in U.S. patent application Ser. No. ______ (Attorney Docket No. APV31960/3991), entitled PROCESS AND APPARATUS FOR FEEDING CEMENTITIOUS SLURRY FOR FIBER-REINFORCED STRUCTURAL CEMENT PANELS, filed concurrently with the present application and incorporated herein by reference in its entirety as well as U.S. Pat. No. 6,986,812 to Dubey et al. incorporated herein by reference in its entirety.
Another feature of the present feeder apparatus 44 is that the main metering roll 48 and the companion roll 50 are both driven in the same direction which minimizes the opportunities for premature setting of slurry on the respective moving outer surfaces. A drive system (not shown), including a fluid-powered, electric or other suitable motor is connected to the main metering roll 48 or the companion roll 50 for driving the roll(s) in the same direction, which is clockwise when viewed in
As the slurry 46 on the outer surface 70A moves toward the moving carrier web 26, it is important that all of the slurry be deposited on the web, and not travel back upward toward the nip 52. Such upward travel would facilitate premature setting of the slurry 46 on the rolls 48, 50 and would interfere with the smooth movement of slurry from the reservoir 57 to the carrier web 26.
To assist in this, the slurry feeder 44 has a doctor blade 134 (
The doctor blade 134 is an improvement over prior art stripping wires used in early slurry feeding systems and which allowed thinner slurries to deposit as drops of slurry on the web.
The doctor blade 134 is mounted on a doctor blade support shaft (not shown) mounted on a doctor blade tension arm pivotably mounted to adjustable pivot mount attached to the support frame or sidewall 54 of the slurry feeder 44. A shaft or bar is attached to the sidewalls 54 of the slurry feeder 44 above the metering roller 48. The doctor blade 134 is biased towards the roll 48 by a tensioning spring having a first end attached to the shaft or bar and a second end attached to the free end of the doctor blade tension arm. Thus, the doctor blade 134 is held in a position adjacent to the outer surface of the metering roll 48 by the tensioning arm and tensioning spring. The position of the doctor blade 134 can be adjusted by adjusting the adjustable pivot mount attached to the support frame or sidewall 54 of the slurry feeder 44.
The doctor blade 134 removes the slurry from the surface of the metering roll 48 like the wire used in the process of U.S. Pat. No. 6,986,812 to Dubey et al. The doctor blade 134 also serves to collect the slurry 46 in a uniform layer or curtain and downwardly directs the slurry 46 in the direction of the movement of the web to a point about 1.0 to 1.5 inches (92.54 to 3.81 cm.) over the fiberglass layer on the web to uniformly cover the fiberglass layer with the slurry 46. This is particularly important where thinner slurries are used to cover the fiberglass layer, since thinner slurries have a tendency to drip over wires.
The doctor blade 134 is explained in greater detail in U.S. patent application Ser. No. ______ (Attorney Docket No. APV31960/3991), entitled PROCESS AND APPARATUS FOR FEEDING CEMENTITIOUS SLURRY FOR FIBER-REINFORCED STRUCTURAL CEMENT PANELS, filed concurrently with the present application and incorporated herein by reference in its entirety.
Referring again to
U.S. Pat. No. 6,986,812 to Dubey et al., entitled SLURRY FEED APPARATUS FOR FIBER-REINFORCED STRUCTURAL CEMENTITIOUS PANEL PRODUCTION, herein incorporated by reference in its entirety; and
the following co-pending, commonly assigned, U.S. patent applications all herein incorporated by reference in their entirety:
United States Patent Application Publication No. 2005/0064164 A1 to Dubey et al., application Ser. No. 10/666,294, entitled, MULTI-LAYER PROCESS AND APPARATUS FOR PRODUCING HIGH STRENGTH FIBER-REINFORCED STRUCTURAL CEMENTITIOUS PANELS;
United States Patent Application Publication No. 2005/0064055 A1 to Porter, application Ser. No. 10/665,541, entitled EMBEDMENT DEVICE FOR FIBER-ENHANCED SLURRY;
U.S. patent application Ser. No. ______ (Attorney Docket No. APV 31960/3991), filed concurrently with the present application, and entitled PROCESS AND APPARATUS FOR FEEDING CEMENTITIOUS SLURRY FOR FIBER-REINFORCED STRUCTURAL CEMENT PANELS,;
U.S. patent application Ser. No. ______ (Attorney Docket No. APV 31962/3993), filed concurrently with the present application, and entitled METHOD FOR WET MIXING CEMENTITIOUS SLURRY FOR FIBER-REINFORCED STRUCTURAL CEMENT PANELS;
U.S. patent application Ser. No. ______ (Attorney Docket No. APV 31964/3995), entitled PANEL SMOOTHING PROCESS AND APPARATUS FOR FORMING A SMOOTH CONTINUOUS SURFACE ON FIBER-REINFORCED STRUCTURAL CEMENT PANELS, filed concurrently with the present application;
U.S. patent application Ser. No. ______ (Attorney Docket No. APV 31965/3845), filed concurrently with the present application, entitled WET SLURRY THICKNESS GAUGE AND METHOD FOR USE OF SAME;
U.S. patent application Ser. No. ______ (Attorney Docket No. 2033.75722/3615A), filed concurrently with the present application, and entitled MULTI-LAYER PROCESS AND APPARATUS FOR PRODUCING HIGH STRENGTH FIBER-REINFORCED STRUCTURAL CEMENTITIOUS PANELS WITH ENHANCED FIBER CONTENT, filed concurrently with the present application; and
U.S. patent application Ser. No. ______ (Attorney Docket 2033.76667/3589A), entitled EMBEDMENT ROLL DEVICE, filed concurrently with the present application;
all herein incorporated by reference in their entirety.
While a variety of embedment devices are contemplated, including, but not limited to vibrators, sheep's foot rollers and the like, in the present embodiment of the embedment device 70 includes at least a pair of generally parallel shafts 76 mounted transversely to the direction of travel of the carrier web 14 on the frame 12. Each shaft 76 is provided with a plurality of relatively large diameter disks 76 which are axially separated from each other on the shaft by small diameter disks (not shown).
During SCP panel production, the shafts 76 and the disks 74 rotate together about the longitudinal axis of the shaft 76. As is well known in the art, either one or both of the shafts 76 may be powered, and if only one is powered, the other may be driven by belts, chains, gear drives or other known power transmission technologies to maintain a corresponding direction and speed to the driven shaft. The respective disks 74 of the adjacent, preferably parallel shafts 76 overlap and are intermeshed with each other for creating a “kneading” or “massaging” action in the slurry, which embeds the previously deposited fibers 68. In addition, the close, intermeshed and rotating relationship of the disks 74 prevents the buildup of slurry 46 on the disks, and in effect creates a “self-cleaning” action which significantly reduces production line downtime due to premature setting of clumps of slurry.
The intermeshed relationship of the disks 74 on the shafts 76 includes a closely adjacent disposition of opposing peripheries of the small diameter spacer disks (not shown) and the relatively large diameter main disks 74, which also facilitates the self-cleaning action. As the disks 74 rotate relative to each other in close proximity (but preferably in the same direction), it is difficult for particles of slurry to become caught in the apparatus and prematurely set. By providing two sets of disks 74 which are laterally offset relative to each other, the slurry 46 is subjected to multiple acts of disruption, creating a “kneading” action which further embeds the fibers 68 in the slurry 46.
An embodiment of embedment device 70 suitable for use in production line 10 is disclosed in greater detail in co-pending U.S. patent application Ser. No. 10/665,541, filed Sep. 18, 2003, published as US 2005/0064055, and entitled EMBEDMENT DEVICE FOR FIBER-ENHANCED SLURRY, and incorporated herein by reference in its entirety.
Another embodiment of an embedment device suitable for use in production line 10 is disclosed by U.S. patent application Ser. No. ______ (Attorney Docket No. 2033.75722/3615A), entitled MULTI-LAYER PROCESS AND APPARATUS FOR PRODUCING HIGH STRENGTH FIBER-REINFORCED STRUCTURAL CEMENTITIOUS PANELS WITH ENHANCED FIBER CONTENT, filed concurrently with the present application, and U.S. patent application Ser. No. ______ (Attorney Docket 2033.76667/3589A), entitled EMBEDMENT ROLL DEVICE, filed concurrently with the present application, both incorporated herein by reference in its entirety.
Once the fiber 68 has been embedded, a first layer 77 of the panel 92 is complete. In a preferred embodiment, the height or thickness of the first layer 77 is in the approximate range of 0.05 to 0.15 inches. This range has been found to provide the desired strength and rigidity when combined with like layers in a SCP panel. However other thicknesses are contemplated depending on the final intended use of the SCP panel.
To build a structural cementitious panel of desired thickness, additional layers are typically added. To that end, a second slurry feeder 78, which is substantially identical to the feeder 44, is provided in operational relationship to the moving carrier 14, and is disposed for deposition of an additional layer 80 of the slurry 46 upon the existing layer 77.
Next, an additional chopper 82, substantially identical to the choppers 36 and 66, is provided in operational relationship to the frame 12 to deposit a third layer of fibers 68 provided from a rack (not shown) constructed and disposed relative to the frame 12 in similar fashion to the rack 31. The fibers 68 are deposited upon the slurry layer 80 and are embedded using a second embedment device 86. Similar in construction and arrangement to the embedment device 70, the second embedment device 86 is mounted slightly higher relative to the moving carrier web 14 so that the first layer 77 is not disturbed. In this manner, the second layer 80 of slurry and embedded fibers is created.
Referring now to
An important feature of the present invention is that the panel 92 has multiple layers 77, 80, 88, 90 which upon setting, form an integral, fiber-reinforced mass. Provided that the presence and placement of fibers in each layer are controlled by and maintained within certain desired parameters as is disclosed and described herein, it will be virtually impossible to delaminate the panel 92 produced by the present process.
Upon the disposition of the four layers of fiber-embedded settable slurry as described above, a forming device may provided to the frame 12 to shape an upper surface 96 of the panel 92.
However, forming devices which scrape away excess thickness of SCP panel material are not desired. For example, forming devices such as spring-loaded or vibrating plates or vibrating leveling screeds designed to conform the panel to suit desired dimensional characteristics are not used with SCP material since they scrape away excess thickness of SCP panel material are not employed. Such devices would not effectively scrape away or flatten the panel surface. They would cause the fiberglass to begin to roll up and mar the surface of the panel instead of flattening and smoothing it.
In particular, rather than spring-loaded devices and vibrating leveling screeds, the production line 10 may include a smoothing device, also termed a vibrating shroud, 144 provided to the frame 12 to gently smooth an upper surface 96 of the panel 92. The smoothing device 144 includes a mounting stand 146 (
The stiffening member 150B functions not only to stiffen the smoothing sheet, but, by mounting the vibratory unit on this stiffening member, this distributes the vibration across the length of the device more evenly. For example, if we mount the vibratory unit directly to the smoothing sheet (say, in the center), without the stiffening member, the vibration from the vibratory unit would be highly localized at the mounting point, with relatively little vibration out on the edges of the sheet. This is not to say that the vibratory unit cannot be mounted anywhere besides the stiffening member 150B, but it is a preferred location since a stiffening member is typically anyway and it does a good job of equally distributing the vibration.
By applying vibration to the slurry 46, the smoothing device 144 facilitates the distribution of the fibers 30, 68 throughout the panel 92, and provides a more uniform upper surface 96.
Additional details regarding the vibrating shroud 144 are disclosed by U.S. patent application Ser. No. ______ (Attorney Docket No. APV31964/3995), entitled PANEL SMOOTHING PROCESS AND APPARATUS FOR FORMING A SMOOTH CONTINUOUS SURFACE ON FIBER-REINFORCED STRUCTURAL CEMENT PANELS, filed concurrently with the present application and incorporated herein by reference in its entirety.
Other forming devices are contemplated as otherwise known in the art. However, the smoothing device 144 advantageously avoids disrupting or tearing portions of the SCP panel from carrier web 26. Forming devices that scrape away excess SCP material are not employed because they disrupt or tear the SCP material due to the fibrous nature of the panel product as it is being formed.
At this point, the layers of slurry have begun to set, and the respective panels 92 are separated from each other by a cutting device 98, which in a typical embodiment is a water jet cutter. Other cutting devices, including moving blades, are considered suitable for this operation, provided they can create suitably sharp edges in the present panel composition. The cutting device 98 is disposed relative to the line 10 and the frame 12 so that panels are produced having a desired length, which may be different from the representation shown in
The production line 10 includes sufficient fiber chopping stations 36, 66, 82, slurry feeder stations 44, 78 and embedment devices 70, 86 to produce at least four layers 77, 80, 88 and 90 (
Upon creation of the SCP panels 92, an underside 102 or bottom face of the panel may be smoother than the upper side or top face 96, even after being engaged by the forming device 94. In some cases, depending on the application of the panel 92, it may be preferable to have a smooth face and a relatively rough face. However, in other applications, it may be desirable to have a board in which both faces 96, 102 are smooth. The smooth texture is generated by the contact of the slurry with the smooth carrier 14 or the carrier web 26.
To obtain a SCP panel with both faces or sides smooth, both upper and lower faces 96, 102 may be formed against the carrier 14 or the release web 26 as disclosed by U.S. patent application Ser. No. ______ (Attorney Docket No. 2033.75722/3615A), entitled MULTI-LAYER PROCESS AND APPARATUS FOR PRODUCING HIGH STRENGTH FIBER-REINFORCED STRUCTURAL CEMENTITIOUS PANELS WITH ENHANCED FIBER CONTENT, filed concurrently with the present application.
Another alternative (not shown) is to sand one or both faces or sides 96, 102.
Another feature of the present invention is that the resulting SCP panel 92 is constructed so that the fibers 30, 68 are uniformly distributed throughout the panel. This has been found to enable the production of relatively stronger panels with relatively less, more efficient use of fibers. The volume fraction of fibers relative to the volume of slurry in each layer preferably constitutes approximately in the range of 1% to 5% by volume, preferably 1.5% to 3% by volume, of the slurry layers 77, 80, 88, 90. If desired, the outer layers 77, 90 may have a higher volume fraction that either or both of inner layers 80, 88.
The incorporation of a volume fraction of loose fibers distributed throughout the slurry 46 is an important factor in obtaining desired panel strength. Thus, improved efficiency in incorporating such fibers is desirable. It is believed the system depicted in
Accordingly, an alternate SCP panel production line or system is illustrated in
More specifically, in
It is also contemplated that the system 130 of
In the alternate system 130, SCP panel production is initiated by depositing a first layer of loose, chopped fibers 30 upon the web 26. Next, the slurry feed station, or the slurry feeder 44 receives a supply of slurry 46 from the remote mixer 47.
It is contemplated that the mixer 47 and slurry 46 in this embodiment are the same as that used in the production line 10 of
Also, the slurry feeder 44 is basically the same, including the main metering roll, 48 and the back up roll 50 to form the nip 52 and having the sidewalls 54. Suitable layer thicknesses range from about 0.05 inch to 0.35 inch (0.13 to 0.9 cm). For instance, for manufacturing a nominal ¾ inch (1.9 cm) thick structural panel, four layers are preferred with an especially preferred slurry layer thickness less than approximately 0.25 inch (0.64 cm) in the preferred structural panel produced by the present process.
Referring to
The system 130 is preferably provided with the above-described vibrating gate 132 which meters slurry onto the deposition or metering roll 48. By vibrating, the gate 132 prevents significant buildup in the corners of the headbox 44 and provides a more uniform and thicker layer of slurry than was provided without vibration.
Even with the addition of the vibrating gate 132, the main metering roll 48 and the backup roll 50 are rotatably driven in the same direction of travel “T” as the direction of movement of the carrier 14 and the carrier web 26 which minimizes the opportunities for premature setting of slurry 46 on the respective moving outer surfaces.
As the slurry 46 on the outer surface 62 of the main metering roll 48 moves toward the carrier web 26, the above-described spring biased doctor blade 134 is provided which separates the slurry 46 from the main metering roll 48 and deposits the slurry 46 onto the moving web 26. The doctor blade 134 provides the slurry 46 with a direct path down to within about 1.5 inches of the carrier web 26, allowing an unbroken curtain of slurry to be continuously deposited onto the web or forming line, which is important to producing homogeneous panels.
Additional details of the gate 132 and the doctor blade 134 are provided in commonly assigned copending U.S. patent application Ser. No. ______, filed concurrently with the present application, and entitled PROCESS AND APPARATUS FOR FEEDING CEMENTITIOUS SLURRY FOR FIBER-REINFORCED STRUCTURAL CEMENT PANELS, (Docket APV31960/3991) which is incorporated by reference.
A second chopper station or apparatus 66, preferably identical to the chopper 36, is disposed downstream of the feeder 44 to deposit a second layer of fibers 68 upon the slurry 46. The chopper apparatus 66 may be fed cords 34 from the same rack 31 that feeds the chopper 36. However, it is contemplated that separate racks 31 could be supplied to each individual chopper.
Referring again to
Further details of the embedment device 136 are found in copending, commonly assigned U.S. patent application Ser. No. ______, entitled EMBEDMENT ROLL DEVICE (Docket 2033.76667/3589A), filed concurrently with the present application, which is incorporated by reference. Otherwise, the embedment device 136 provides the same sort of kneading action as the device 70, with the objective of embedding or thoroughly mixing the fibers 30, 68 within the slurry 46.
If desired to further enhance the embedment of the fibers 30, 68 into the slurry 46, at each embedment device 136 the frame 12 is provided with at least one vibrator 141 in operational proximity to the carrier web 14 or the paper web 26 to vibrate the slurry 46. Such vibration has been found to more uniformly distribute the chopped fibers 30, 68 throughout the slurry 46. Conventional vibrator devices are deemed suitable for this use.
As seen in
Upon the disposition of the four layers of fiber-embedded settable slurry as described above, a forming device such as the smoothing device, or vibrating shroud, 144 is preferably provided to the frame 12 to shape or smooth an upper surface 96 of the panel 92. By applying vibration to the slurry 46, the smoothing device 144 facilitates the distribution of the fibers 30, 68 throughout the panel 92, and provides a more uniform upper surface 96. The smoothing device 144 includes a mounting stand 146, a flexible sheet 148 secured to the mounting stand, a stiffening member 149 extending the width of the sheet 148 and a vibration generator 150 preferably located on the stiffening member to cause the sheet to vibrate.
As mentioned above, an important feature of the present invention is that the panel 92 has multiple layers 77, 80, 88, 90 which upon setting, form an integral, fiber-reinforced mass. Provided that the presence and placement of fibers in each layer are controlled by and maintained within certain desired parameters as is disclosed and described below, it will be virtually impossible to delaminate the panel 92 produced by the present process.
Utilizing two discrete layers of reinforcing fibers with each individual discrete slurry layer provides the following benefits. First, splitting the total amount of fibers to be incorporated in the slurry layer into two or more discrete fiber layers reduces the respective amount of fibers in each discrete fiber layer. Reduction in the amount of fibers in the individual discrete fiber layer enhances efficiency of embedment of fibers into the slurry layer. Improved fiber embedment efficiency in turn results in superior interfacial bond and mechanical interaction between the fibers and the cementitious matrix.
Next, a greater amount of reinforcing fibers can be incorporated into each slurry layer by utilizing multiple discrete layers of reinforcing fibers. This is due to the finding that the ease of embedment of the fibers into the slurry layer has been found to depend upon the total surface area of the fibers in the discrete fiber layer. Embedment of the fibers in the slurry layer becomes increasingly difficult as the amount of fibers in the discrete fiber layer increases, causing an increase in the surface area of the fibers to be embedded in the slurry layer. It has been found that when the total surface area of the fibers in the discrete fiber layer reaches a critical value, embedment of the fibers into the slurry layers becomes almost impossible. This imposes an upper limit on the amount of fibers that can successfully be incorporated in the discrete layer of slurry. For a given total amount of fibers to be incorporated in the discrete slurry layer, use of multiple discrete fiber layers reduces the total surface area of the fibers in each discrete fiber layer. This reduction in the fiber surface area (brought about by the use of multiple discrete fiber layers) in turn provides an opportunity to increase the total amount of fibers that can successfully be embedded into the discrete layer of slurry.
In addition, the use of multiple discrete fiber layers allows tremendous flexibility with respect to the distribution of fibers through the panel thickness. The amount of fibers in the individual discrete fiber layers may be varied to achieve desired objectives. The resulting creation of a “sandwich” construction is greatly facilitated with the presence of a larger number of discrete fiber layers. Panel configurations with fiber layers having higher amount of fibers near the panel skins and lower amount of fibers in the fiber layers near the panel core are particularly preferred from both product strength and cost optimization perspectives.
In quantitative terms, the influence of the number of fiber and slurry layers, the volume fraction of fibers in the panel, and the thickness of each slurry layer, and fiber strand diameter on fiber embedment efficiency has been investigated and established as part of the present system 130. A mathematical treatment for the concept of projected fiber surface area fraction for the case involving two discrete fiber layers and one discrete slurry layer is introduced and derived below. It has been found that it is virtually impossible to embed fibers in the slurry layer if the projected fiber surface area fraction of the discrete fiber layer exceeds a value of 1.0. Although the fibers may be embedded when the projected fiber surface area fraction falls below 1.0, the best results are obtained when the projected fiber surface area fraction is less than 0.65. When the projected fiber surface area fraction ranges between 0.65 and 1.00, the efficiency and ease of fiber embedment varies with best fiber embedment at 0.65 and worst at 1.00. Another way of considering this fraction is that approximately 65% of a surface of the slurry is covered by fibers.
Let,
To determine the projected fiber surface area fraction for a fiber layer in an arrangement of a fiber layer/slurry layer/fiber layer sandwich composed of one discrete slurry layer and two discrete fiber layers, the following relationship is derived.
Let,
v
f,l
=v
f1
+v
f2 (1)
and,
Let,
The total volume of the fundamental fiber-slurry layer, vt=Total volume of slurry layer+Total volume of the two fiber layers=vs,l+vf,l=vs,l+vf1=vf2 (3)
Combining (1) and (2):
The total fiber volume of the fundamental fiber-slurry layer in terms of the total fiber volume fraction can be written as:
v
f,l
=v
t
*V
f,l (5)
Thus, the volume of fibers in the layer 1 can be written as:
Similarly, the volume of fibers in the layer 2 can be written as:
Assuming fibers to have cylindrical shape, the total number of fibers in the layer 1, nf1,l can be derived from Equation 6 as follows:
where, df is the fiber strand diameter and lf is the fiber strand length
Similarly, the total number of fibers in the layer 2, nf2,l can be derived from Equation 7 as follows:
The projected surface area of a cylindrical fiber is equal to the product of its length and diameter. Therefore, the total projected surface area of all fibers in layer 1, sf1,lP can be derived as:
Similarly, the total projected surface area of fibers in layer 2, sf2,lP can be derived as:
The projected surface area of slurry layer, ss,lP can be written as:
Projected fiber surface area fraction of fiber layer 1, Sf1,lP is defined as follows:
Combining Equations 10 and 12, the projected fiber surface area fraction of fiber layer 1, Sf1,lP can be derived as:
Similarly, combining Equations 11 and 12, the projected fiber surface area fraction of fiber layer 2, Sf2,lP can be derived as:
Equations 14 and 15 depict dependence of the parameter projected fiber surface area fraction, Sf1,lP and Sf2,lP on several other variables in addition to the variable total fiber volume fraction, Vf,l. These variables are diameter of fiber strand, thickness of discrete slurry layer, and the amount (proportion) of fibers in the individual discrete fiber layers.
Experimental observations confirm that the embedment efficiency of a layer of fiber network laid over a cementitious slurry layer is a function of the parameter “projected fiber surface area fraction”. It has been found that the smaller the projected fiber surface area fraction, the easier it is to embed the fiber layer into the slurry layer. The reason for good fiber embedment efficiency can be explained by the fact that the extent of open area or porosity in a layer of fiber network increases with decreases in the projected fiber surface area fraction. With more open area available, the slurry penetration through the layer of fiber network is augmented, which translates into enhanced fiber embedment efficiency.
Accordingly, to achieve good fiber embedment efficiency, the objective function becomes keeping the fiber surface area fraction below a certain critical value. It is noteworthy that by varying one or more variables appearing in the Equation 15, the projected fiber surface area fraction can be tailored to achieve good fiber embedment efficiency.
Different variables that affect the magnitude of projected fiber surface area fraction are identified and approaches have been suggested to tailor the magnitude of “projected fiber surface area fraction” to achieve good fiber embedment efficiency. These approaches involve varying one or more of the following variables to keep projected fiber surface area fraction below a critical threshold value: number of distinct fiber and slurry layers, thickness of distinct slurry layers and diameter of fiber strand.
Based on this fundamental work, the preferred magnitudes of the projected fiber surface area fraction Sf1,lP have been discovered to be as follows:
For a design panel fiber volume fraction, Vf,for example a percentage fiber volume content in each slurry layer of 1-5%, achievement of the aforementioned preferred magnitudes of projected fiber surface area fraction can be made possible by tailoring one or more of the following variables—total number of distinct fiber layers, thickness of distinct slurry layers and fiber strand diameter. In particular, the desirable ranges for these variables that lead to the preferred magnitudes of projected fiber surface area fraction are as follows:
Referring now to
The slurry was produced according to the present process, using the present system, and is shown to have four slurry layers, 77, 80, 88 and 90. This panel should be considered exemplary only in that a panel 92 produced under the present system may have one or more layers. By using the above mathematical relationships, the slurry layers 77, 80, 88 and 90 can have different fiber volume fractions. For example, skin or face layers 77, 90 have a designated fiber volume fraction Vf of 5%, while inner layers 80, 88 have a designated Vf of 2%. This provides a panel with enhanced outer strength, and an inner core with comparatively less strength, which may be desirable in certain applications, or to conserve fibers for cost reasons. It is contemplated that the fiber volume fraction Vf may vary among the layers 77, 80, 88, 90 to suit the application, as can the number of layers.
Also, modifications of the fiber content can be accomplished within each slurry layer. For example, with a fiber volume fraction Vf of 5%, for example, fiber layer 1 optionally has a designated slurry volume fraction of 3% and fiber layer 2 optionally has a designated fiber volume fraction of 2%. Thus, Xf will be 3/2.
Referring now to Table 1, panels were manufactured using the system of
In the present system 130, by increasing the number of fiber layers, each with its own fiber surface area fraction, more fibers can be added to each slurry layer without requiring as many layers of slurry. Using the above process, the panel 92 can have the same thickness as prior panels, with the same number of fibers of the same diameter, with fewer number of slurry layers. Thus, the resulting panel 92 has layers of enhanced strength but is less expensive to produce, due to a shorter production line using less energy and capital equipment.
The residence time of the wet slurry in various embodiments of a vertical mixing chamber have been empirically determined by determining the residence time of a red dye tracer added to the slurry to completely exit the vertical chamber. Tests were conducted to determine residence time in the vertical mixing chambers using a red dye tracer added to the water and powder slurry as it enters the vertical chamber. The cementitious slurry had substantially the same composition as described above for Example 1.
The equipment used was a digital scale to weigh the slurry, a bucket to catch the slurry and a stop watch to measure the elapsed time of the various points. A mixer was used with three different mixing chamber designs as listed in Tables 2-4 as a 12 inch Mixer, an 8 inch Extended Mixer, and an 8 inch Stock Mixer.
The 8 inch Stock Mixer is a DUO MIX 2000 mixer which is similar to that of
The 8 inch Extended Mixer is disclosed in U.S. patent application Ser. No. ______ (Attorney Docket No. APV31962/3993), entitled APPARATUS AND METHOD FOR WET MIXING CEMENTITIOUS SLURRY FOR FIBER-REINFORCED STRUCTURAL CEMENT PANELS, filed concurrently with the present application. It differs from the 8 inch Stock Mixer at least because its vertical chamber was extended to provide a relatively larger working volume.
The 12 inch Mixer is of the type shown in present
After achieving and maintaining a consistent slurry fluidity of 6-8 inches (15 to 20 cm) slump a liquid solution of common brick dye (tracer) was added to the vertical chamber at a set mixer output speed (say 60%, initially). Mixer output speed is directly related to paddle speed and pump speed. These mixers had a 1-10 speed controller. Basically setting of 1=about 45 RPM and a setting of 10=about 260 RPM.
The watch was started when the dye was added. The time that red-dyed slurry first exited the hose was noted (T1). The time at which the red dye no longer visibly stained the slurry was noted as well (T2). This process was repeated at the various pump output speeds and again with all the various mixer chamber designs. All time values were lowered by the amount of time required to pump the slurry through the specific length of hose at a given pump speed. This effectively eliminates the time the slurry takes to travel through the hose and allowed a more accurate comparison between the various chamber designs.
Slump was measured by pouring slurry into a 2 inch diameter cylinder that is 4″ tall (open on each end and placed on end on a flat smooth surface) and screeding the top of the slurry off. This provides a set volume of slurry for every test. Then the cylinder was immediately lifted and the slurry rushed out the open bottom end of the cylinder. This act formed a circular “patty” of slurry. The diameter of this patty is measured in inches and recorded. A more fluid slurry will typically result in a larger diameter patty.
Table 2 displays the time elapsed from the addition of the dye (T0) to the time the dye is first seen (T1) until the time the dye is no longer visible (T2). The time to first dye visible (T1) is subtracted from the time until dye no longer visible (T2) to obtain total residence time and these values are shown in Table 3. Table 4 lists average residence times (Time to Empty Vertical Chamber) of the runs of this example as calculated as slurry flow rate divided by Working Volume.
In Tables 2 and 3 the inches represent the nominal OD of the mixing chambers. The 8 inch Stock Mixer is a comparative example. The overall length of the mixing chambers are as follows: 8 inch stock mixer: 17 inches tall, about 5 inch working height (depth of slurry); 8 inch Extended mixer: 25 inches tall about 14 inch working height (depth of slurry); 12 inch mixer: 25 inches tall, about 13 inches working height (depth of slurry).
The mixer output speed represents the speed of the mixer impeller and the rate material is flowing through the mixer because the same motor powers the impeller paddle and the discharge pump.
Comparing Total Residence Time of the 8 inch Extended Mixer or the 12 inch Mixer to the 8 inch Stock Mixer shows the significant increase in residence time found by increasing mixer volume (at any pump speed (60%, 80% or 100%)). Also, the Time to Dye First Visible shows a significant increase in the time elapsed from the time the dye (or slurry) enters the chamber until the dye (or slurry) first begins to exit the mixer. This helps ensure material does not enter the mixing chamber and then quickly exit without being adequately mixed.
Thus, increasing the volume of the chamber significantly increases the time cement slurry must remain in the chamber (undergoing mixing) before it can first exit the chamber. In addition, the amount of time elapsed before all the slurry that entered the chamber at a discrete point in time is emptied from the chamber is significantly increased with the larger volume mixers. These findings are supported by the increase in compressive strength noted when mixing time was increased.
This example used the DUO MIX mixer, a hand stirrer (similar to a paint stick, a hand drill with a joint compound mixing paddle, a 5 gallon bucket and a stop watch. Cementitious slurry was collected from the discharge hose and compressive cubes were cast using method ASTM C109. The cementitious slurry had substantially the same composition as described above for Example 1.
In particular, slurry was taken directly from the output hose of the DUOMIX mixer. Compressive strength cubes were then made from the slurry using the above-mentioned method ASTM C109.
Immediately afterwards, cementitious slurry was again collected in a bucket and stirred by hand with a metal spatula for 1 minute. The slurry was then used to cast the compressive strength cubes using the above-mentioned method ASTM C109 and tested to determine compressive strength. In particular, cement slurry from the mixer hose was pumped into a 5 gallon bucket and this slurry was gently stirred with by hand with a paddle. Compressive strength cubes were then made from the slurry using the above-mentioned method ASTM C109.
Immediately after this, cement slurry was collected again and this time mixed for 1 minute in a bucket using a hand drill and a mixing paddle similar to that used to mix joint compound. In particular, cement slurry from the mixer hose was pumped into another 5 gallon bucket and this slurry was mixed with a drill equipped with a stirring device (the mixing paddle), similar to that used to mix joint compound. Compressive strength cubes were then made from the slurry using the above-mentioned method ASTM C109.
The cubes made from the slurry taken directly from the output hose of the DUOMIX mixer were tested for compressive strength at 7, 14 and 28 days after they were produced. The compressive strength results of each time period were averaged and reported in the table of
The cubes made from the slurry that had been hand mixed were tested for compressive strength at 7, 14 and 28 days after they were produced. The compressive strength results of each time period were averaged and reported in the table of
The cubes made from the slurry that had been mixed with the drill mixer were tested for compressive strength at 7, 14 and 28 days after they were produced. The compressive strength results of each time period were averaged and reported in the table of
The general conclusion from this investigation was that increasing the mixing energy and or the mixing time significantly improves development of material compressive strength, a key component of the panel's overall performance characteristics.
While a particular embodiment of the present slurry feed apparatus for fiber-reinforced structural cementitious panel production has been shown and described, it will be appreciated by those skilled in the art that changes and modifications may be made thereto without departing from the invention in its broader aspects and as set forth in the following claims.
This application is related to co-pending: U.S. patent application Ser. No. ______ (Attorney Docket No. APV31960/3991), entitled PROCESS AND APPARATUS FOR FEEDING CEMENTITIOUS SLURRY FOR FIBER-REINFORCED STRUCTURAL CEMENT PANELS, filed concurrently with the present application; U.S. patent application Ser. No. ______ (Attorney Docket No. APV31962/3993), entitled METHOD FOR WET MIXING CEMENTITIOUS SLURRY FOR FIBER-REINFORCED STRUCTURAL CEMENT PANELS, filed concurrently with the present application; U.S. patent application Ser. No. ______ (Attorney Docket No. APV31964/3995), entitled PANEL SMOOTHING PROCESS AND APPARATUS FOR FORMING A SMOOTH CONTINUOUS SURFACE ON FIBER-REINFORCED STRUCTURAL CEMENT PANELS, filed concurrently with the present application; U.S. patent application Ser. No. ______ (Attorney Docket No. APV31965/3845), entitled WET SLURRY THICKNESS GAUGE AND METHOD FOR USE OF SAME, filed concurrently with the present application; U.S. patent application Ser. No. ______ (Attorney Docket No. 2033.75722/3615A), entitled MULTI-LAYER PROCESS AND APPARATUS FOR PRODUCING HIGH STRENGTH FIBER-REINFORCED STRUCTURAL CEMENTITIOUS PANELS WITH ENHANCED FIBER CONTENT, filed concurrently with the present application; and U.S. patent application Ser. No. ______ (Attorney Docket 2033.76667/3589A), entitled EMBEDMENT ROLL DEVICE, filed concurrently with the present application; all herein incorporated by reference in their entirety.