The present invention relates to the separation and selective recombination of ions from differing electrolyte solutions to produce useful chemical compounds, and compounds which have limited occurrence in nature, such as soda ash.
There are many chemical compounds which must be manufactured through special chemical processes. Such compounds are typically useful for various industrial purposes worldwide, but have only a limited occurrence in nature. The synthesis of these compounds typically requires a large number of steps, a large amount of energy, and the formation of intermediate by-products that are often of to value or are useless or even harmful to the environment. Therefore, in order to reduce energy consumption and the number of intermediate steps needed prior to reaching a final product, it would be advantageous in the industrial chemical arts to provide simplified synthesis processes for various useful chemical compounds.
Presently three industrial processes are used for manufacturing sodium carbonate (i.e. Soda Ash). The Solvay process uses limestone (calcium carbonate, CaCO3) and salt brine (sodium chloride, NaCl) as raw materials, and ammonia (NH3) as an intermediary, and is the prevailing process used in Europe and many other regions. The overall chemical equation for the Solvay Process can be written as:
CaCO3+2NaCl→Na2CO3+CaCl2 (Equation 1)
However, in order to reach the end products, the Solvay process involves many intermediate steps. First, calcium carbonate (limestone) is heated to release carbon dioxide:
CaCO3→CaO+CO2 (Equation 2)
The remainder of the process is centered about a large hollow tower. At the top of the tower, a concentrated solution of sodium chloride and ammonia enter the tower. As the carbon dioxide bubbles up through this solution, sodium bicarbonate is produced and precipitates according to the following equation:
NaCl+NH3+CO2+H2O→NaHCO3+NH4Cl (Equation 3)
The sodium bicarbonate, separated by filtration, is then converted to sodium carbonate by heating it, which also releases water and carbon dioxide:
2NaHCO3→NaCO3+H2O+CO2 (Equation 4)
Calcium hydroxide is then produced by reacting the calcium oxide generated in Equation 2 with water:
CaO+H2O→Ca(OH)2 (Equation 5)
From here, the ammonium chloride produced in Equation 3 is treated with the calcium hydroxide produced in Equation 5 mainly to recover the ammonia which is recycled:
Ca(OH)2+2NH4Cl→CaCl2+2NH3+2H2O (Equation 6)
In addition to producing Soda Ash (i.e. sodium carbonate, see Equation 4), the Solvay process also generates calcium chloride as a by-product (see Equation 6). While calcium chloride has a number of uses, most notably as a road de-icing agent, typically the manufacturers of Soda Ash have a major issue disposing of this by-product. For example, in seaside locations such as Saurashtra, Gujarat, India, excess calcium chloride is deposited into the sea; or in Osborne, South Australia, after it was observed that calcium chloride was silting up the shipping channel, the practice of dumping it into a settling pond was adopted.
Another well-known process for manufacturing sodium carbonate is Hou's process. This process is advantageous where a supply of carbon dioxide is available but sources of limestone (i.e. calcium carbonate) are distant. In this process carbon dioxide (produced by such processes as steam reforming) is passed through a nearly saturated solution of sodium chloride and ammonia, much like the Solvay process (see Equation 3, above). However, after removal of the precipitated sodium bicarbonate (NaHCO3), the remaining solution is cooled to allow the precipitation of ammonium chloride (NH4Cl), which can be sold as a fertilizer after removal from the cooled solution. Because the ammonia and sodium chloride need to be replenished, Hou process plants need to be located near ammonia production facilities.
In the United States, the discovery in Wyoming and California of major sodium carbonate deposits in the form of the mineral Trona has led to the gradual replacement of synthetic Soda Ash production, partially in an effort to lessen the environmental impact of calcium chloride (from industrial Solvay process plants) polluting the ground water at plant site landfills. There are also Trona mines in Turkey and in Lake Magadi in Kenya. Purified Soda Ash produced by refining mined Trona ore can be shipped to paper and glass factories and for use in various chemical and petrochemical plants. For example, purified Soda Ash is typically shipped from mines in Wyoming and California to eastern and southern U.S. states, mostly by rail.
While the mining of Trona ore is one solution to synthetically manufacturing Soda Ash, the economic cost of transporting the purified Soda Ash across the country becomes a major consideration. And while synthesizing Soda Ash locally would be the preferred solution, current synthesis processes such as the Solvay process have their own economic and environmental problems, associated with the supply of reactants and the disposal of by-product calcium chloride and the economics of the scale requiring rather large plants to produce soda ash using the Solvay process.
In light of the above, it is apparent that there is a need in the art for a more economically and environmentally friendly process for the production of Soda Ash. U.S. Pat. Nos. 8,715,477, 9,309,133 and 9,315,398, which are all by the current inventor A. Yazdanbod and are incorporated herein by reference in their entireties, teach processes and devices for Ion Separation and Recomposition Technology (ISART). ISART involves synthesizing new chemical compounds that traditionally have been hard to construct, by exchanging oppositely charged ions from one chemical compound for those of another. The ISART inventions described in the patents listed above can also be used for desalination of water by selective removal and depletion of ions. With ISART, in its many variations, it is now possible to separately remove charged ions from a first electrolyte solution and selectively recombine these charged ions with oppositely charged ions from a second electrolyte solution to form new chemical compositions in one or two steps.
In light of the above discussion regarding the production of Soda Ash, it would be advantageous to employ certain applications of ISART technology to produce needed industrial chemical compounds such as Soda Ash. It would also be advantageous to provide a chemical production process for Soda Ash which uses less energy than current Solvay or Hou processes and does not include the production of calcium chloride. It would likewise be useful if an industrial plant producing Soda Ash has no by-products requiring disposal. It would further be advantageous if an industrial plant producing Soda Ash can be located near points of consumption, to significantly reduce transportation costs. It would also be useful if such a plant could have flexible production, capabilities to adjust to varying market demands. It would further be advantageous if the polluting and greenhouse gas carbon dioxide could be utilized by a novel process to produce Soda Ash.
Accordingly, the present invention relates to improvements in the apparatuses and methods used and patented by the present inventor for Ion Separation and Recomposition Technology (ISART). The invention also relates to a novel approach for the production of Soda Ash (i.e. sodium carbonate) using the ISART process. Industrial plants employing the ISART process can have the flexibility to produce needed industrial chemical compounds such as Soda Ash, Caustic Soda, hydrochloric acid and chlorine gas, based on market demand, and can be located near points of consumption to significantly reduce transportation costs.
A first aspect of the invention is a process for capacitive generation of ion streams, comprising: (a) providing a first electrolyte solution in a first hydraulically isolated section and a second electrolyte solution in a second hydraulically isolated section, wherein each electrolyte solution comprises positive ions and negative ions; (b) separating the positive ions from the negative ions in each of the first and second electrolyte solutions, wherein separating comprises the steps of: (i) placing a first. EDLC electrode inside the first electrolyte solution; (ii) placing a second EDLC electrode inside the second electrolyte solution; and (iii) applying an electric potential difference between the EDLC electrodes such that two capacitors in series are formed in each of the first and second electrolyte solutions; (c) electrically drawing the ions out of each of the first and second electrolyte solutions as oppositely charged ion streams, wherein the positive and negative ion streams are generated in a continuous fashion and are selectively drawn through an ion selective membrane selective to the ion stream; and (d) pooling the ion stream from the first electrolyte solution and the oppositely charged ion stream from the second electrolyte solution into a third hydraulically isolated section with sides made up of the ion selective membranes of the first and the second hydraulically isolated sections.
A second aspect of the invention provides an apparatus for separation and selective recomposition of ions, comprising (a) a cell comprising (i) a first insulated container; (ii) a first ion selective membrane; (iii) a second ion selective membrane, wherein the first and second ion selective membranes divide the volume of the first insulated container into a first hydraulically isolated volume, a second hydraulically isolated volume and a third hydraulically isolated volume, wherein the third hydraulically isolated volume is located between the first and the second hydraulically isolated volumes; (iv) a first EDLC electrode secured within the first hydraulically isolated volume; and (v) a second EDLC electrode secured within the second hydraulically isolated volume; and (b) an electric current supply source for connecting to and controlling the polarities of the first and second EDLC electrodes.
A third aspect of the invention provides an apparatus for separation and selective recomposition of ions, comprising in combination: (a) a first cell comprising (i) a first insulated container; (ii) a first ion selective membrane; (iii) a second ion selective membrane, wherein the first and second ion selective membranes divide the volume of the first insulated container into a first hydraulically isolated volume, a second hydraulically isolated volume and a third hydraulically isolated volume, wherein the third hydraulically isolated volume is located between the first and the second hydraulically isolated volumes; (iv) a first EDLC electrode secured within the first hydraulically isolated volume; and (v) a second EDLC electrode secured within the second hydraulically isolated volume; (b) a second cell comprising (i) a second insulated container; (ii) a third ion selective membrane; (iii) a fourth ion selective membrane, wherein the third and fourth ion selective membranes divide the volume of the second insulated container into a fourth hydraulically isolated volume, a fifth hydraulically isolated volume and a sixth hydraulically isolated volume wherein the sixth hydraulically isolated volume is located between the fourth and the fifth ones; (iv) a third EDLC electrode secured within the fourth hydraulically isolated volume; and (v) a fourth EDLC electrode secured within the fifth hydraulically isolated volume; (c) a first electric current supply source for connecting to and controlling the polarities of the first and second electrodes; and (d) a second electric current supply source for connecting to and controlling the polarities of the third and fourth electrodes.
A fourth aspect of the invention provides an apparatus for separation and selective recomposition of ions, comprising in combination; (a) a first cell comprising (i) a first insulated container; (ii) a first ion selective membrane; (iii) a second ion selective membrane, wherein the first and second ion selective membranes divide the volume of the first insulated container into a first hydraulically isolated volume, a second hydraulically isolated volume and a third hydraulically isolated volume, wherein the third hydraulically isolated volume is located between the first and the second hydraulically isolated volumes; (iv) a first electrode secured within the first hydraulically isolated volume, wherein the first electrode is a low electrical capacitance electrode which allows the occurrence of electrode reactions; and (v) a second electrode secured within the second hydraulically isolated volume, wherein the second electrode is an EDLC electrode; (b) a second cell comprising (i) a second insulated container; (ii) a third ion selective membrane, (iii) a fourth ion selective membrane, wherein the third and fourth ion selective membranes divide the volume of the second insulated container into a fourth hydraulically isolated volume, a fifth hydraulically isolated volume and a sixth hydraulically isolated volume wherein the sixth hydraulically isolated volume is located between the fourth and the fifth hydraulically isolated volumes; (iv) a half fuel cell device placed within the fourth isolated volume; and (v) a third electrode secured within the fifth hydraulically isolated volume, wherein the third electrode is an EDLC electrode; (c) a first electric current supply source for connecting to and controlling the polarities of the first and second electrodes; and (d) a second electric current supply source for connecting to and controlling the polarities of the third electrode and the porous electrode of the half fuel cell structure in the fourth volume, wherein the first hydraulically isolated volume includes a cap, the cap including a tube connecting the empty space above the first electrolyte solution to the half fuel cell device, and wherein the second current supply source includes a resistive or capacitive load that can consume the electric energy generated between its two ends so that the energy is used.
A fifth aspect of the invention provides an apparatus for separation and selective recomposition of ions, comprising in combination; (a) a first cell comprising (i) a first insulated container; (ii) a first ion selective membrane; (iii) a second ion selective membrane, wherein the first and second ion selective membranes divide the volume of the first insulated container into a first hydraulically isolated volume, a second hydraulically isolated volume and a third hydraulically isolated volume wherein the third hydraulically isolated volume is located between the first and the second hydraulically isolated volumes; (iv) a first electrode secured within the first hydraulically isolated volume, wherein the first electrode is a low electrical capacitance electrode which allows the occurrence of electrode reactions; and (v) a second electrode secured within the second hydraulically isolated volume, wherein the second electrode is an EDLC electrode; (b) a second cell comprising (i) a second insulated container; (ii) a third ion selective membrane; (iii) a fourth ion selective membrane, wherein the third and fourth ion selective membranes divide the volume of the second insulated container into a fourth hydraulically isolated volume, a fifth hydraulically isolated volume and a sixth hydraulically isolated volume wherein the sixth hydraulically isolated volume is located between the fourth and the fifth hydraulically isolated volumes; (iv) a third electrode secured within the fourth hydraulically isolated volume, wherein the third electrode is a low electrical capacitance electrode which allows the occurrence of electrode reactions; and (v) a fourth electrode secured within the fifth hydraulically isolated volume, wherein the fourth electrode is an EDLC electrode; (c) a first electric current supply source for connecting to and controlling the polarities of the first and second electrodes; and (d) a second electric current supply source for connecting to and controlling the polarities of the third and fourth electrodes.
The nature and advantages of the present invention will be more fully appreciated from the following drawings, detailed description and claims.
The accompanying drawings illustrate embodiments of the invention and, together with a general description of the invention given above, and the detailed description given below, serve to explain the principles of the invention.
As noted above, the scientific foundations of the present invention have been detailed in U.S. Pat. Nos. 8,715,477, 9,309,133 and 9,315,398 to current inventor A. Yazdanbod, which teach a number of embodiments of Ion Separation and Recomposition Technology (ISART). Generally, these patents teach that oppositely charged ions can be separately extracted from two differing input solutions, resulting in depletion of ions from the input solution and generation of two ionic streams, i.e. a positive ionic stream and a negative ionic stream, each having an excess of one polarity of ions. The oppositely charged ionic streams from each of the two differing solution can then be drawn into an ion sink and combined to form different, new solutions or chemical compounds as compared with the original input solutions.
Briefly, when two single Electric Double Layer Capacitor (EDLC) electrodes (i.e. a capacitive electrode which functions in a capacitive mode without the occurrence of electrode reactions) are each placed inside a separate electrolyte filled insulated container, herein called ion Repulsion Cells (IRCs), and a DC voltage is applied between these two electrodes, there will be an excess of ions (having the same polarity as the charge applied to the electrode) that will concentrate at the outer edge of each of the individual containers. EDLC electrodes are made of electrically conductive material, such as carbon aerogels, carbon aerogel composites or any electrically conductive material exhibiting such electric capacitances of more than 1 Farads per gram, preferably more than 10 Farads per gram, and ideally more than 50 Farads per gram. When placed in contact with an electrolyte solution and DC voltage is applied, EDLC electrodes absorb ions and create an electric double layer of ions on the electrode. If the IRCs are hydraulically connected by a tube to a third container, herein called an Ion Sink, and there is an Ion Selective Membrane (ISM) associated with each of these tubes which create an ion selective barrier within the interior cross-section of these tubes, and if the polarity of each ISM is such that it would prevent the flow of ions of opposite polarity and allow ions of the same polarity of the ions accumulated on the inner surface of the related IRC, then there will be an ionic current of single polarity generated from each IRC, each having opposite polarity ions with respect to the other, entering the Ion Sink and neutralizing the other in the Ion Sink.
A direct current electric current supply source 60 capable of polarity reversal and having electric ports 61 and 62 is included. Each of the first and second EDLC electrodes 5 and 25 are connected to a metallic wire, 70 and 71 leading out of the IRC and connected to one pole of the power supply 60 through wires 74 and 75 respectively. Electric ports 61 and 62 could each be either positive or negative polarity. Power supply 60 also has another port 66 that outputs a given electric signal that changes depending on the polarity between poles 61 and 62. Cable 79 connects this port 66 to port 81 of a control device 80. The four output ports, shown together as outlet 82 of the control device 80, are each connected through appropriate cables (not shown) to one of the flow cut-off valves 31, 32, 33, 34. The control device 80 senses the polarity dependent signal through port 66 and switches the first and second flow cut-off valves 31 and 32 to a first orientation, e.g. to an open position, while simultaneously switching the third and fourth flow cut-off valves 33 and 34 to the opposite orientation, e.g. to a closed position.
For example, when the system is operated, the first EDLC electrode 5 could be negatively charged while the second EDLC electrode 25 could be positively charged. If, under this condition, flow cut-off valves 31 and 32 are open, and valves 33 and 34 are closed through the action of the control device 80, the ion selective membranes in inline filter holders 8 and 29 will be anion exchange membranes while the membranes in the filter holders 9 and 28 will be cation exchange membranes. With reference now to
Under this condition, if the first electrolyte solution 3 in IRC 1 is a solution of silver nitrate (AgNO3) and the second electrolyte solution 23 in IRC 21 is a solution of sodium chloride (NaCl), silver ions (Ag+) will begin to be capacitively absorbed to electrode 5 and chlorine ions (Cl−) will begin, to be capacitively absorbed to electrode 25. At the same time, an ionic current of nitrate ions (NO3−) will pass through tube 6 and inline filter 8 (containing an ion selective membrane ISM), entering Ion Sink 41 while an ionic current of sodium (Na+) will flow out of IRC 21 through line 26 and ISM 28 and will also enter Ion Sink 41, neutralizing the nitrate ion stream and together forming a sodium nitrate solution (NaNO3) in Ion Sink 41. Once the potential between one or both electrodes 5 and 25 and the ions capacitively absorbed to each electrode reach a level that would allow electrode reactions to occur between the ions and the electrode they are capacitively absorbed to, that is, once one or both these capacitors fill up, the polarity of the electric current supplied by power supply 60 could be reversed, signalling the control device 80 to close valves 31 and 32, and open valves 33 and 34. This reversal of applied potential to electrodes 5 and 25 will initially release the ions previously absorbed to these electrodes and in continuation of the process, will result in absorption of charges of opposite polarity with respect to the previously absorbed ions on the electrodes. This reversal of polarity combined with closure of valves 31 and 32 and the opening of valves 33 and 34 will now generate two oppositely charged ionic currents into Ion Sink 51. Thus, IRC 1 will now generate a sliver ion (Ag+) current while IRC 21 will now generate a chlorine ion (Cl−) current. These ionic currents pass through pipes 7 and 27, as well as ISM 9 and ISM 29, and neutralize each other in Ion Sink 51, forming silver chloride (AgCl) which precipitates therein. This was experimentally verified as reported in U.S. Pat. Nos. 8,715,477, 9,309,133 and 9,315,398. Once the capacitances of the electrodes fill up with ions or at any other earlier convenient time, the polarity of the voltage applied by power supply 60 is reversed again and the process switches to the formation of sodium nitrate (NaNO3) in Ion sink 41 and then again to formation of silver chloride (AgCl) in Ion Sink 51 and so on.
There are other embodiments of Ion Separation and Recomposition Technology, as illustrated in U.S. Pat. Nos. 8,715,477, 9,309,133 and 9,315,398 (e.g.
For example, in each half cycle operation of a given ion repulsion cell, one of the two valves each placed on the passage leading to an ion exchange membrane and its related ion sink is closed and the other is opened. This means that half of the time, one ion exchange membrane set and their related ion sink are used while the other ion exchange membrane set and its related ion sink sit idle. Thus, production capacity is technically reduced by 50% compared to full utilization of each ion exchange membrane and each cell. Further, in each half cycle of operation, a given valve needs to initially close and then re-open in the next half cycle. This places a lot of stress on the system and requires a good deal of maintenance work to insure that these large surface area valves remain electrically and hydraulically sealed when closed.
It would therefore be advantageous for certain industrial applications of the ISART technology if one were to eliminate the need for valves to operate the ion repulsion cells and to be able to continuously operate each ion sink. Indeed, if these valves could be eliminated, the connection passages between the ion sinks and ion repulsion cells can be made shorter, the surface areas of the ion exchange membranes can be increased, and each ion exchange membrane set and its related ion sink can be utilized almost continuously. The present invention results from the discovery that, by eliminating the flow cut-off valves 31, 33, 34 (see
As shown
When the power supply 260 is turned on for cell 201 while cell 101 is being operated, the same series of phenomena occurring in cell 101 will occur in cell 201, but with opposite charges. Specifically, with pole 261 being positively charged and pole 262 being negatively charged, negative ions in the solution in section 203 will be absorbed to electrode 205 and positive ions will be repulsed towards the outer perimeter of section 203 (i.e. towards the inner surface of section 203, including ISM 208). Further, in section 223 there will be absorption of positive ions onto electrode 225 and repulsion of negative ions to the outer perimeter of section 223. With ISM 208 being a cation exchange membrane and ISM 228 being an anion exchange membrane, the repulsed ions from sections 203 and 223 pass through their respective ISM and enter middle section 241, where they can form a new compound combining the positive ions passing from section 203 and the negative ions passing from section 223. Meanwhile, with absorption of ions onto EDLC electrodes 105 and 125, the capacitor formed between these ions and charges on the conductive body of each electrode begins to fill up, creating a potential difference between the two plates of the each EDLC electrode.
Now, if the electrolyte solutions in sections 103 and 203 are the same, such as a solution of silver nitrate (AgNO3), and if the electrolytes in sections 123 and 223 are also the same, such as a solution of sodium chloride (NaCl), positive silver ions (Ag+) will be absorbed to electrode 105 and negative chlorine ions (Cl−) will be absorbed to electrode 125. Thus, negative nitrate ions (NO3−) will be repulsed from section 103 and pass through ISM 108 (which is an anion exchange membrane) to enter the middle section 141 (i.e. the third hydraulically isolated volume 141 of cell 101), where they can encounter and neutralize positive sodium (Na+) ions being repulsed from volume 123 and passing through ISM 128 (which is an cation exchange membrane), forming sodium nitrate (NaNO3). Similarly, but with the charges on the electrodes being the reverse of those of electrodes 105 and 125, the ions absorbed to electrode 205 in cell 201 will be nitrate ions (NO3−) and the ions absorbed to electrode 225 will be sodium ions (Na+). Thus, positive silver ions (Ag+) will be repulsed from section 203 and pass through ISM 208 (which is an cation exchange membrane) to enter middle section 241 (i.e. the sixth hydraulically isolated volume 241 of cell 201), where they can encounter and neutralize negative chlorine ions (Cl−) being repulsed from section 223 and passing through ISM 228 (which is an anion exchange membrane), forming silver chloride (AgCl) as a precipitate.
Comparing
As noted above, ions of opposite polarity are capacitively absorbed to each EDLC electrode, creating a potential difference between the electrode and the surrounding electrolyte solution (due to the flow of ions out of each IRC). Once this potential difference reaches the level wherein electrode reactions (i.e. redox reactions) begin to occur between the absorbed ions and the electrodes, then the electrodes are saturated with ions and can no longer store additional ions. More specifically, with continuous operation of this system and the consequent further increase of the number of ions capacitively absorbed to each electrode, redox reactions occur such that absorbed positive ions on electrodes gain electrons from the negatively charged electrodes (such as Ag+ ions gaining an electron and becoming elemental silver) and the absorbed negative ions on positively charged electrodes give electrons to the electrodes (such as Cl− ions giving an electron to the electrode and becoming chlorine gas).
For example, looking at
Another embodiment of the present invention is shown in
Regarding the low capacitance electrode 305 in
Thus, when an electrolyte solution such as sodium hydroxide (NaOH, caustic soda) is placed in section 103, and with low capacitance electrode 305 being connected to a cathode pole, OH− ions will pass through ion exchange membrane (ISM) 10 and stream out of section 103 into ion sink 141, while redox reactions at the low capacitance electrode 305 cause hydrogen gas (H2) to emit from IRC 103 to the empty space above it. Inversely, when the goal is for IRC 103 to generate H+ ions, the electrolyte solution in section 103 should contain anions that have higher electrode potential than OH−, such as sulfuric acid (H2SO4). Under these conditions, the low capacitance electrode 305 will be an anode, redox reactions at electrode 305 will cause oxygen gas (O2) to be emitted from IRC 103 to the empty space above it, and a stream of H+ ions will pass through ISM 108 and into ion sink 141.
More specifically, looking at
Should be noted that if the requirements of a particular design do not require the separation of the electrolyte solutions in section 103 and ion sink 141, then the corresponding ISM 108 can also be eliminated. Thus, in the example above, since NaOH is present in both section 103 and ion sink 141, ISM 108 could be eliminated. The reverse is true as well, that is, if by necessities of a design such as differences in concentration or compositions the electrolytes in volumes 103 and 141 need to be kept separate, ISM 108 will have to be used. Furthermore, given the very high pH of the caustic soda electrolyte used in volume 103 in the example above, and the subsequent formation of high pH caustic soda in volume 141, both ISM 108 (if needed) and ISM 128 would have to be of material that are stable in high pH environments.
With DC power source 260 including electric load 306 connecting poles 261 and 262, moving EDLC electrode 125 (now containing a certain amount of chlorine ions) to volume 223 of cell 201 can cause electrode 125 to receive electrons generated by half fuel cell device 191. This can cause EDLC electrode 125 to release its chlorine ion (Cl−) content and allow interactions with hydrogen ions (H+) produced by device 191. Looking at
Hydrogen gas (H2) entering from tube or conduit 190 can be ionized by device 191, splitting into an electron and a proton, wherein a stream of positively charged hydrogen ions (H+, protons) can pass through the ISM 208 and combine with the negatively charged chlorine ions released from electrode 125 to form hydrochloric acid (HCl) in ion sink 241. At the same time, the negative electrons produced by ionization of the hydrogen gas will go through the electric load 306 of the DC power source 260 and back to electrode 125, making electrode 125 a cathode and facilitating the removal of chlorine ions therefrom. The potential difference across the electric load 306 is caused by the potential difference between the porous electrode 308 and electrode 125. This potential difference and the charges energized by it could then do work across the electric load 306. Alternatively, and with attention to
An alternative embodiment of the present invention is illustrated in
Simultaneously, low capacitance electrode 405 (acting as an anode) can be can be placed in volume 203 containing an electrolyte solution of sulfuric acid (H2SO4), and EDLC electrode 225 (acting as a cathode) can be placed in volume 223 containing an electrolyte solution of ammonium chloride (NH4Cl). With an applied potential provided by power source 260, section 203 acts as an IRC to generate a stream of hydrogen ions (H+) that pass through cation exchange membrane ISM 208 to enter ion sink 241, while redox reactions take place at electrode 405, emitting oxygen (O2) gas out above level 204. Section 223 will act as an Ion Repulsion Cell (IRC) to generate a stream of chlorine ions (Cl−) passing through ISM 228 to enter ion sink 241, such that the hydrogen and chloride ion streams can combine in ion sink 241 to form hydrochloric acid (HCl). This has been experimentally verified by the present inventor.
In verification experiments carried out on this process using cell closely adhering to cell 101 in
The various embodiments of the present improvement of the ISART process described herein can be applied to the industrial production of Soda Ash. As noted above, the Solvay Process is one of the main industrial processes currently used for manufacturing sodium carbonate (i.e. Soda Ash), but the process involves many intermediate steps and produces non-useful by-products. To solve these problems, the present inventor surmised that the ISART process could be a likely candidate to improve the production process of Soda Ash. However, due to low solubility of some of the input compounds, ISART production of soda ash was found to proceed at a slow rate. For example, using the presently used raw materials used in the Solvay Process, namely limestone (calcium carbonate), salt brine (sodium chloride) and ammonia, it was believed that ISART could be used to easily and efficiently form sodium carbonate by replacing the calcium ions in calcium carbonate with sodium ions from sodium chloride; and the process would also be useful to combine the remaining oppositely charged ions, namely chlorine and calcium ions, to from calcium chloride. While in theory all looked good, it was found that the low solubility of limestone/calcium carbonate slows down the ISART process to a point of impracticality. Although the solubility of calcium carbonate in water can be increased by pressurizing the solvent (i.e. water) with carbon dioxide and dissolving it in the water, the improved solubility was determined to be insufficient for large industrial applications. The low solubility of calcium carbonate thus places a limitation on the capability of ISART for the industrial production of sodium carbonate using the raw materials of the Solvay Process.
To overcome such limitations, the present inventor has improved the ISART process so that it is practical to produce industrial amounts of soda ash. Thus it is possible to change the Solvay process to one similar to Hou's process, by using carbon dioxide (CO2) as an input while at the same time producing hydrochloric acid and recovering ammonia for reuse, without any need for lime. Here, referring to
2NaOH+CO2→Na2CO3+H2O (Equation 7)
Therefore, the ISART process can produce Soda Ash more easily if CO2 gas is introduced as one of the input materials eliminating the need for ammonia. Yet another variation would be to use carbon dioxide in a similar column as in Solvay process were instead of producing carbon dioxide by calcining lime stone, another source of carbon dioxide is used for injecting into the solution comprising a mixture of ammonia and sodium chloride as in Equation 3 and processing the remaining solution of ammonium chloride using ISART to recover the ammonia as described with respect to
While the present invention has been illustrated by the description of embodiments and examples thereof, it is not intended to restrict or in any way limit the scope of the appended claims to such detail. Additional advantages and modifications will be readily apparent to those skilled in the art. Accordingly, departures may be made from such details without departing from the scope of the invention.
Number | Name | Date | Kind |
---|---|---|---|
2704239 | Pike | Mar 1955 | A |
4022868 | Poncha | May 1977 | A |
4033842 | Loest | Jul 1977 | A |
4635289 | Mani et al. | Jan 1987 | A |
5989505 | Zolotoochin et al. | Nov 1999 | A |
6479025 | Denham, Jr. et al. | Nov 2002 | B2 |
8715477 | Yazdanbod | May 2014 | B2 |
9309133 | Yazdanbod | Apr 2016 | B2 |
9315398 | Yazdanbod | Apr 2016 | B2 |
20120097541 | Yazdanbod | Apr 2012 | A1 |
20160229718 | Yazdanbod | Aug 2016 | A1 |
20170088445 | Yazdanbod | Mar 2017 | A1 |
Number | Date | Country | |
---|---|---|---|
20190077673 A1 | Mar 2019 | US |