This invention relates generally to apparatus and methods for assembling thermoplastic or elastomer materials, and to construction of resilient playgrounds or safety mats made of tiles. In particular the invention refers to means for assembling and co-adhering an array of laid-down tiles made of a poly vinyl chloride plastics composition.
This invention relates to resilient playground or floor (safety) mats, as embodied in the applicants' products most of which are made up of arrays of square tiles, 0.5 metre along an edge, made of a resilient material such as polyvinyl chloride (PVC) cast in moulds including perforations and surface detailing, so that the tiles have improved grip and resilience properties. Such PVC mats may include plasticisers, fillers, and colouring material and may include conductive material. Mats are intended to lie flat on a substrate and be attached by their edges to neighbouring tiles. Interlocking complementary lugs and pockets are of assistance. It has been found that more extreme environments such as outdoors in North America have been causing unexpected expansion/contraction of playground mats as a result of temperature changes. In addition a loss of dimension over a period of years is known to occur because of the gradual loss of the significant amount of plasticiser incorporated with the plasticiser. (Typically, about 20% by weight of flexible PVC is a plasticiser such as dioctyl phthalate. This substance can diffuse through the mass of the PVC). As a result, the glued joints become infiltrated with plasticiser. The inventors have realised that glued joints can be expected to fail when the plasticiser migrates into the glue itself, over time, and causes weakening of the joint. As a result, tiles lift off the substrate and/or separate from each other. Of course, the invention is in no way limited to use with the applicant's tiles; the above problem has merely stimulated the research that resulted in this invention. Many other articles constructed from plastics are amenable to a welding treatment according to the invention, as will shortly be described.
The problem to be solved could be stated as providing a permanent join between parts made of a plastics material where glued joins have been found to be weak and of short life. The inventor's particular desire is to halt any tendency of tiles to lift off the substrate and/or to separate from each other. One response would be to render the body of the tiles less prone to expansion or contraction, but as yet no economical solution having this effect has been found. Another solution is to provide better adhesive procedures including use of melted and then flowed-together plastics material; that is, welds. A further solution is to include tough fibrous material that traverses parts such as an array of tiles, having sufficient tensile strength to hold the tiles in place despite the forces of contraction or expansion.
U.S. Pat. No. 6,520,790 (Sumitomo Wiring Systems) teaches a method for waterproof lighting fixture assembly in which wiring is at first continuously routed through one or more sockets and then after a heat-welding process using resistive heating of the wire that melts a sealing material on to the wiring, the wires are cut at the sockets so that the same wire can supply power to lamps inserted in the sockets. This is a dual use of the same wire; first in an assembly phase then in a normal-use phase.
U.S. Pat. No. 6,676,861 Van Der Werf et al suggests that “the wire” as we later define it could be coated with various granules including coloured granules, for joining linoleum. The coated non-metallic cord of this invention does not include means for internal (resistive) heating.
There is a known technique in which a wire embedded in rubber windscreen mouldings of automobiles is heated in order to vulcanise the rubber. The wire is left in place.
It is an object of this invention to provide arrays of safety floor tiles or particularly play mats having a better capacity to stay united, or at least to provide the public with a useful choice.
In a first broad aspect this invention provides means for construction of an array of thermoplastic safety floor mats or play mats upon a substrate or surface; wherein heating means capable of causing the thermoplastic material to soften at least in a localised area is employed to cause the mats of the array to become linked or welded together along their edges, so that use of a glue is avoided.
In a first related aspect this invention provides means for the joining together by welding of an array of safety floor mats or play mats by their edges upon a substrate or surface; wherein heating means consisting of an electrically conductive elongated member having tensile strength is placed along at least one edge of a first tile between an upper surface and a lower surface of the tile and adjacent a second tile to which the first tile is to be joined, the adjacent edges comprising what is or will become a seam; the elongate member being capable of being heated by the passage of electric current in order to cause welding together of the first tile and the second tile along the seam.
In a second related aspect this invention provides an electrically conductive elongated member comprising a wire comprised of a metal or a metal alloy, having tensile strength and electrical conductivity.
Preferably the elongated member is composed of a stainless steel wire.
Alternatively the wire can be comprised of other conductors having tensile strength, including “Nichrome” alloys.
More preferably the wire includes at least two stainless steel wire strands twisted together, so that the combination produces a given amount of heat at a higher current but lower voltage yet retains more flexibility than a single thicker wire.
Optionally the wire is coated with compounds capable of enhancing the welding process.
Optionally the wire is coated with materials capable of increasing the effective diameter of the wire so that there is less tendency for the wire to pull or be pulled from its location.
Alternatively the wire is configured so that its surface includes projections.
Optionally the wire may be laid in a pattern which traverses more than one length of tile-tile weld, or intended weld, by returning to the source along the same or a different folds back onto itself.
Optionally, the wire is provided with a number of short sleeves of an insulating material so that perpendicular cross-over of wires does not carry current. One material suitable for a sleeve is shrink-wrap insulation.
In an alternative aspect the initial or a remedial welding process is provided by an alternative heat source: the local application of heat along the seam from a source of energy in contact with a surface overlying the seam.
Preferably the source of energy comprises a source of heat within a metal block.
In a second broad aspect the wire, which remains in place, is used also as a tensile reinforcing member within the array of safety floor mats or play mats by connecting each end of a length of wire to an anchoring means attached to the ground, each anchoring means being capable of holding the wire under a controlled amount of tension.
Optionally at least some of the tiles are provided with longitudinal edge grooves for holding the wire along their edges, although ungrooved tiles are satisfactory.
Preferably enough wires are included in an installed array of tiles to surround all edges of each tile of the array with a weld-capable retaining wire.
In a third broad aspect the invention provides apparatus for supplying the elongated conductive members with a welding current; the apparatus comprising means for generating the delivered current and controlling the delivered current.
Preferably the apparatus includes means for indicating the delivered current and for controlling the time of delivery and displaying the subsequent recommended cooling time, and connecting means for joining more than one wire to the current supply apparatus.
In a fourth broad aspect the invention provides a method for providing a more secure array of resilient tiles for play and/or safety purposes, the method including the steps of:—
In a fourth broad aspect the invention provides a group of means for the local application of heat along two adjoining edges, so that the edges are raised to a welding temperature of between 130 and 190 degrees Celsius, and then brought firmly together so that the edges fuse and remain fused after cooling down.
Preferably the group of means for local application of heat includes hot air blowers, heated contact elements, ultrasonic energy, radio-frequency heating (including microwave heating), and infra-red heating; all adapted for the application of heat to a localised strip along the edges of adjoining items made of a poly vinyl chloride plastics material; and used either alone or in combination with other means.
Preferably the group of means for local application of heat are used in conjunction with head localising devices including air controlling barriers, ultrasonic transducers of controlled shapes, radio frequency electrodes, microwave applicators, and infra-red reflectors and directors, so that the heat is restricted to a localised area to be welded.
A preferred microwave frequency is in the range of either about 915 MHz or about 2.4 Ghz).
In a fifth broad aspect the invention provides for the use of a plastisol glue as defined else wherein this specification, either separately or together with methods previously described in this section; the plastisol glue being first placed in the area to become welded, and then heated to a temperature sufficient to cause the sol to melt and become converted into a mass of poly vinyl chloride material.
Preferred heating means include the heating of embedded wires, hot air blowers, heated contact elements, ultrasonic energy, radio-frequency heating (including microwave heating), and infra-red heating;
The description of the invention to be provided herein is given purely by way of example and is not to be taken in any way as limiting the scope or extent of the invention.
The welding and holding wire central to this Example is laid along the seams between an array of flexible PVC-based tiles as sold by the inventors under the trade mark “PLAY MATTA” when laid down for use upon a substrate. The wire has two main purposes: (1) for welding use during installation, when it provides the localised intense heat for a mat welding procedure, and (2) for use after installation when the tensile properties of the wire are used to hold the array of tiles together, and also down on to the underlying substrate despite forces tending to pull the tiles away; including thermal expansion and contraction, contraction on volatilisation of plasticiser, and applied forces.
The applicant usually provides tiles either in single units (0.5 metres square), or as one-metre pre-welded squares each holding four tiles (size information by way of example only).
A desired welding process has a cycle length of 5 to 8 minutes at a power input in the range of about 100-150 watts per metre. The actual temperature reached has not been measured, but is less than the decomposition temperature for PVC and is probably 140-180 deg C. The power supply of Example 1E may be adjusted in order to provide this amount and duration of heating power.
An option of providing a thick coating of relatively meltable granules applied to the wire or to the tile edge before the welding process has been considered, but subsequent migration of plasticiser may weaken this material a while after it has formed an adhesive, and it comprises an extra step in manufacture over simply welding with the bulk material of the tiles. Perhaps tile pressure could be realised within a confining outer frame by weighting the slightly oversize tiles down. Clips are not essential.
Temporary clips or other devices to pull the seam shut during the welding process and hold it shut in compression until the weld has cooled are desirable. One device is a pair of rows of lever-actuated pushing rods that engage with existing holes through the tiles, as shown in
The seam compressor shown in plan view (top view) in
If an iron is not likely to be used, a simpler version of clamps for holding the tiles close together along the seam may be made. See the perspective drawing of
Apparatus for supplying the welding current is described here, Environmental conditions and working voltages and currents must be considered in relation to operator safety since potentially lethal amounts of current are used. A motor-driven generator may be preferred, being portable, inherently isolated from ground, and being a variable power supply. Isolating transformers and return-current detection circuit breakers are of assistance if the utility power is used. About 12 volts RMS per metre of seam, at a current within a range of about 5 to 20 amperes (depending on the resistance per unit length of the wire used) is required to be supplied for a duration of 5 to 8 minutes. A constant-voltage power supply is preferred over a constant-current type, using the negative temperature dependence of resistance of a metal for some auto-regulation. A mains-driven arc welder can be used if suitably calibrated. DC power is acceptable except that it is more difficult to control cheaply: because of factors such as switch derating and non-availability of transformer or phase-controlled rectifier (Triac) controls for instance. The power supply may be required to produce from 6 volts to, for a 20-285 metre span, over 240 volts (measured as RMS voltage across the length buried between tiles) depending on the length of seam between tiles to be welded at any one time. A selectable transformer tapping may be the most reliable way to achieve the variable voltage although solid-state devices are preferred options and are amenable to automatic control. The operator would be required to select the closest tapping or power setting for the wire length and type in use. The current should be delivered in a controlled manner over a period so that the result is melting and welding, rather than overheating and charring of the materials surrounding the wire (the welding wire) if too much current is used. The operator would be instructed never to overheat a seam—which would char it and require replacement of adjoining tiles. Underheating would fail to weld the tile material.
Ideally there would be a display device to show (a) the progress (time elapsed) of the welding cycle, (b) that current is flowing properly, and (c) the status of delivered power. A temperature probe may be used. Signalling the end of a suitable cool-down period at the end of a weld is also important, in case under-skilled workers try to rush the process and pull the retaining clips out too soon.
This presently preferred circuit relies on an alternating-current source, such as a motor generator as would be used in the field (or alternatively use of a large isolating transformer) to ensure isolation of the power from the general ground, and hence safety. 230-250 volts is generally required to match power transfer to a desirable welding wire thickness, and length, rather than the perhaps more obvious 110 volts, for which wire thickness has to be increased significantly (hence raising cost and using a stiffer wire which is hard to handle). Continuously variable heating control is provided with little heat dissipation by phase control (using the circuit board (CB) and the phase shifting componenents mounted on it) of a “Triac” solid-state device. A snubberless type is preferred since it commutates better when driving an inductive load. A purely resistive load (R6) is also provided since this power supply includes a step-down transformer for better control over short lengths of wire. That second range of heating currents is made using the 6.6:1 step-down toroidal power transformer (TT), for use on short lengths of welding wire. The controller is provided in a box having a lid. Some parts are mounted under the lid; others on the base. Meter measurements of delivered voltage and current are provided, and timer action is indicated by the two lamps. The circuit of
The “Omron HC3A” timer ensures accurately repeatable yet variable-length applications of heating current by time, and the control R1 is used to apply an amount of heat according to the amount of resistive wire in use at any time, so that the workman's job is simplified. In effect, the circuit on the left represents means to energise the selected portions of the circuit on the right for a controlled period by the mechanism of relay coil power (coils SRC, and either LRC or HRC are energised). Conventional “TRIAC” triggering circuitry is provided along with a 50 or 60 Hz frequency selection switch.
A: A hand-held hot-air blower might be used for local additional heating, such as for patching use after the main process has been completed. Since the air heats only the upper surface it would be usefully complemented by sub-surface wire heating.
B: The most straightforward of many alternative processes is thermal conduction from an internally heated metal block device (herein called “an iron”) which is a simple and effective method such as for patching a playground surface by welding if a tile needs to be replaced. It also heats only the upper surface of adjoining tiles. The compressing clip system would be used at the same time. In some cases, access to the welding wire may be inaccessible, or may not have been used. One must remember that the workmen need simple, reliable and easy-to-understand equipment. This description of a prototype iron is given by way of example. A rectangular bar of copper or aluminium, 25 mm×25 mm×0.5 metres (1 inch×1 inch×20 inches) is used. Copper is heavier and a better thermal conductor than aluminium. The bar is drilled out axially lengthwise in order to accommodate two resistive heater units each rated at about 500 watts at the local mains voltage (117 or 240 volts), or as generated by a motor generator. In this case electrical isolation between the heating element and the metal block is reasonably likely and can be checked by means of a residual current sensing device. Example heaters are 5 to 6 mm diameter. The bar is also milled lengthwise along what will become the top surface in order to accommodate the metal bulb of a thermostat, placed so that it samples an average of the temperature of the bar. (A thermocouple, read by a circuit within the power supply unit, is preferred for production units. Fail-safe means include testing for open circuited thermocouple wires and use of a backup thermocouple to sense over-temperature conditions. The bar is covered with insulating material on all but the base. A sheet mica material (Hislop & Barley, Onehunga, New Zealand) is used and a glass-reinforced “Teflon”® sheet covers the base through which sheet heat will be transferred to the underlying plastic in order to cause a weld. The Teflon allows release afterwards. An electrical circuit for use with an “iron” includes these features:
Total wire length will be limited by the amount of power that can be inserted. Relatively long straight lines may be welded at one time, using one or more low-resistance insulated connecting leads to close the current path. Insulating sleeves such as heat-shrink sleeves may be slipped over the welding wires where they cross over other wires between the tiles in order to avoid bypassed current effects and to avoid local heating arising from poor contacts.
The preferred method for providing a more secure array of resilient tiles for play and/or safety purposes includes the steps of:—
The additional step of tying down the free ends of the wire to ground anchors (retainers) is not a necessary step, but if done is according to the following extra steps:
If the wire is not to be used with anchors or retainers it may be clipped off flush with the edges of the tiles or inserted into crimped-on covers in order to cover the sharp ends.
Although this description relates to working with resilient PVC playground tiles that include plasticiser, a similar approach may be applied to other structures made of similar plastics especially those that are unsuitable for gluing or RF heating. This may include flooring or roofing, for example.
The process may be used to vulcanise glued joints between rubber or predominantly rubber (such as rubber with urethane mixtures) tiles, and can also be used to weld synthetic rubber.
Some other plastics, blends and mixtures that may be used for tiles (apart from the PVC that forms the majority of examples considered herein) include (as a non-limiting list): high-density polyethylene (HDPE), ethylene copolymers with vinyl acetate (EVA), polyurethane (PUR), rubber, and other elastomers, or blends thereof. There are many further possible elastomers, for instance.
As mentioned previously in this specification, there have been problems with resilient floor tiles and play tiles coming apart or coming off their substrate especially as a result of temperature excursions (20 deg F. in winter to over 120 deg F. in the summer sun). The use of a welding process provides superior tile—tile edge adherence because glue is susceptible to later becoming softened by diffusing plasticiser. The inclusion of tension-bearing elements which can be secured to lateral supports such as pegs in the ground assists in keeping the array of tiles flat and in place despite expansion and contraction.
Finally, it will be understood that the scope of this invention as described and/or illustrated herein is not limited to the specified embodiments. Those of skill will appreciate that various modifications, additions, known equivalents, and substitutions are possible without departing from the scope and spirit of the invention as set forth in the following claims.