The present invention is generally related to an apparatus for flatproofing tire and wheel assemblies, and, more particularly, to an apparatus for flatproofing tubeless tire and wheel assemblies using lightweight flexible polyurethane foam formed in the tubeless tire/wheel assemblies to replace air in the tubeless tire/wheel assemblies.
Traditionally, flatproof tires have been made by one of the following methods. In one method, a solid polyurethane material is injected into a solid mold for producing a flatproof tire. The mold with the solid polyurethane material is heated and rotated, and then allowed to cure. After curing the solid polyurethane tire is removed from the mold.
Another flatproofing method offered by several companies including, Arnco, CinAir and Carpenter, is generally known as “traditional fill” and involves filling a rubber tire mounted on a wheel with solid polyurethane. Polyurethane reactants (a polyol and an isocyanate) are mixed using a static mixer and pumped into the tire through the valve stem in the wheel under the same pressure as the normal air inflation pressure for the tire. The reactant mixture is then allowed to cure inside the tire forming a solid polyurethane fill within the tire. Typically, an extender, such as an oil, is included in the reactant mixture. Solid polyurethane, however, is very heavy. For example, a typical solid polyurethane fill with an oil extender has no cells and has a high density of about 62.4 lbs/ft3 making it practical for use only with heavy equipment. This method has additional drawbacks. Because the reactants are pumped into the tire under pressure, namely the normal inflation pressure of the tire, the tire must be filled while placed within a safety cage in case the tire fails during filling.
Other flatproofing methods use non-urethane flatproofing materials that do not replace the air in the tire and wheel assembly. They seal leaks and/or punctures in the tire to minimize the loss of air. In this regard, these non-urethane flatproofing materials are not considered flatproof.
From the above, it can be appreciated that it would be desirable to have a flexible, lightweight polyurethane foam that replaces the inflating air in the tire as a means to support the tubeless rubber tire allowing it to be used in low speed applications and applications other than for heavy equipment. Examples of such desired low speed, light weight applications include, off-road, construction and turf and garden applications. Such flexible foam would provide the pneumatic performance of an air inflated pneumatic tire due to its flexible cell walls, semi-open cell structure, and density, size and uniform distribution of the cells. It can also be appreciated that it would be desirable to have a process for flatproofing a tire and wheel assembly by injecting liquid reactant materials into the tire and wheel assembly to form a flexible polyurethane foam that replaces the inflating air in the tubeless tire and wheel assembly that is relatively maintenance free. Further, it can be appreciated that it would be desirable to have a portable apparatus that injects the liquid reactant materials into a tubeless tire and wheel assembly for flatproofing, and can be used in the field by the tire dealers, avoiding the need to return the tire to a factory. Further it can be appreciated that it would be desirable for safety considerations to have a fill process that does not require the tire cavity to be pressurized.
An apparatus is disclosed for flatproofing a tire and wheel assembly by forming a flexible foam, namely a lightweight, flexible polyurethane foam, in situ, in a tire and wheel assembly. The lightweight, flexible polyurethane foam replaces the inflating air as the means to inflate and support the tire used in low speed applications. The flexible polyurethane foam provides a pneumatic performance similar to inflating air due to its flexible cell walls, cellular structure, and low density, size and uniform distribution of the cells. Based on the combination of the light weight flexible polyurethane foam and the foam-filled dispensing apparatus of the present invention, tire factories and/or dealers in the field may obtain a portable apparatus for injecting liquid reactant materials into the tire and wheel assembly. In an exemplary embodiment, the flexible polyurethane foam reactants of the present invention can be stored and processed at ambient temperature (meaning about 70 degrees Fahrenheit+about 10 degrees).
Moreover, the reactants are not required to be injected into the tire at the normal air inflation pressure of the tire. They do not need to be pumped into the tire under pressure as the foaming action of the reactant material forces the air out of the tire cavity and fills the entire cavity. Thus, the reactants can be pumped into the tire at effectively ambient pressure.
The flexible polyurethane is a polymerization product of a polyol component, an isocyanate component, water (optional) and a catalyst system that promotes a polymerization reaction between the isocyanate component and the polyol component to form the polyurethane. Normal practice in the art is to form an isocyanate mixture, referred to as SIDE A; and to form a mixture of polyols, chain extenders, cross linking agents, fillers, blowing agents, surfactants, catalysts etc., commonly referred to as SIDE B. The SIDE A component and the SIDE B component are mixed together at a given ratio to form the desired polyurethane polymer.
The polyol component can contain either a single polyol or a mixture of two or more polyols. The specific polyols useful in the manufacture of polyurethane foams are well known in the art and include aliphatic, alicyclic and aromatic polyols. The isocyanate component can contain either a single isocyanate or a mixture of two or more isocyanates. The specific isocyanates useful in the manufacture of polyurethane polymers are well-known in the art and include aliphatic, alicyclic and aromatic isocyanates. Suitable isocyanates have an average functionality within the range of 2-8, preferably within the range of 2-5. Examples of suitable isocyanates are 2,4-toluene diisocyanate; 2,6-toluene diisocyanate; 1,6-hexamethylene diisocyanate; naphthalene-1,4-diisocyanate; diphenyl methane 4,4′-diisocyanate; 4,4′-diphenylene diisocyanate; 3,3′-dimethoxy biphenylene diisocyanate; polymeric forms of the above diisocyanates, diisocyanato carbodiimide modified MDI, isocyanate terminated prepolymers, and mixtures of the above listed isocyanates. The preferred reactant materials are obtained from Textile Rubber Company and are identified as EX303-41A and EZ303-41B.
A tire, such as a pneumatic tire, is mounted on a wheel. The tire is then inflated with air or other gas to its maximum rated inflation pressure to stretch the tire out. After the tire has had sufficient time to stretch, vent holes are formed in the tire and the valve stem removed. Reactant materials to produce a foam are mixed in liquid form, and a nucleating gas, such as air, is introduced into the liquid reactant mixture to entrain the gas within the reactant mixture. This reactant mixture can be formed under ambient conditions. The liquid reactant mixture with entrained gas is then introduced into the tire through the valve stem opening of the wheel. Once the tire is filled with the specified amount of liquid reactant mixture, a plug is inserted into the valve stem opening. The reactant mixture is then allowed to react or foam within the tire. The foaming action produces a cellular foam structure of flow density, meaning a density of approximately 20 lbs./ft3 or less. The vent holes in the tire allow air or other gas to escape from the tire as the reactant mixture is pumped into the tire, foams and pushes out the air that was previously in the tire. The foam is then allowed to cure. The curing time can be as much as 12 to 24 hours.
In an exemplary embodiment, an apparatus is provided to carry out the above-described process for flatproofing a tire with a cellular foam structure. The apparatus includes a reactant mixing head and at least two supply lines for supplying individual reactant components to the mixing head. A mixer is attached to the mix head. A supply line is also provided to the mixer for supplying nucleating gas to the mixer. The mixer has an outlet nozzle for delivering the liquid reactant mixture with entrained gas into the tire through the valve stem opening of the wheel. In an exemplary form, the mixing head is what is referred to as a static mixer, and the reactant materials are mixed and pumped into the tire under ambient conditions. The mixer and supply lines can be associated with a portable cart having a work surface on which a tire and wheel assembly may be placed for filling with the liquid reactant mixture. The cart can optionally include motive means, such as pumps or compressed gas sources for delivering the reactant materials and/or the nucleating gas to the mixing head. If desired, a weight scale may be included in the work surface for monitoring the weight of the tire and wheel assembly during filling with the liquid reactant mixture.
Other systems, devices, features and advantages of the disclosed apparatus will be or become apparent to one with skill in the art upon examination of the following drawings and detailed description. It is intended that all additional systems, devices, features, and advantages be included within this description, be within the scope of the present invention, and be protected by the accompanying claims.
Many aspects of the disclosed apparatus can be better understood with reference to the attached drawings,
Referring now to the drawing figures, wherein like reference numerals represent like parts throughout the several views, an exemplary embodiment of an apparatus for producing foam-filled flatproofed tire and wheel assembly of the present invention is illustrated in
A nucleating gas compressor (not shown) is coupled to a nucleating gas supply line 118, which is coupled to the static mixer 116. The nucleating gas compressor supplies nucleating gas through the nucleating material supply line 118 to the mixed reactant materials in the static mixer 116. The preferred source for nucleating gas is one that provides a dry, clean gas. One way to keep the gas dry and clean is to use an oil free compressor for the gas. Such a compressor can be mounted on the cart assembly 110 or located off the cart assembly. The source of the gas can be either an air tank or a commercial source.
In an exemplary embodiment, the tire and wheel assembly is filled with a low-density flexible polyurethane foam. The reactant materials for creating the foam are a polyisocyanate and a polyol. The nucleating gas can be air. However, any other gas which would be inert with the reactant materials and the resultant foam can be used.
Also referring to
Also referring to
FIGS. 4A-B illustrate the process for flatproofing a tire and wheel assembly carried out by the above-described apparatus. Referring to
In block 406, the size of the tire and wheel assembly 208 is obtained so that the amount of the mixture to be injected into the tire and wheel assembly 208 can be determined. The worktable 114 may include a built-in weight scale 120 to weigh the tire and wheel assembly 208. The tire and wheel assembly 208 may be placed on its side on the weight scale 120 to obtain the size and/or weight of the tire and wheel assembly 208. Inclusion and use of such a weight scale is optional.
In block 408, at least one vent hole is drilled to provide an outlet for the air within the tire carcass to escape as the tire 210 is filled with the reactant material. The vent hole(s) can be located on the side wall of the tire 210 where the tire side wall contacts the drill fixture 212 at one or more radial slots in the drill fixture 212. In block 410, the valve stem is removed from the tire and wheel assembly 208 to form a valve stem opening 206 such that the static mixer 116 is disposed therein. The static mixer 116 is placed into the valve stem opening 206 to inject foam through the valve stem opening 206 into the tire. In block 412, the pumps 108A-B are activated to supply the polyurethane reactant materials to the static mixer 116.
Referring to
In block 418, the mixture of the liquid reactants with entrained nucleating gas is injected into the tire and wheel assembly 208 via the valve stem opening 206. In an exemplary embodiment, the reactant materials are mixed and injected into the tire under ambient temperature and pressure conditions. By ambient temperature, is meant, in the range of about 70° F. to about 80° F. At the lower end of this temperature range, it is preferred that the temperature be high enough to avoid freezing of the polyisocyanate which can cause the polyisocyanate to become unstable.
Once the tire and wheel assembly 208 is filled with the mixture, the apparatus shuts down and the static mixer 116 is removed from the valve stem opening 206. The dispensing apparatus 100 can automatically input the amount of mixture necessary to fill the tire and wheel assembly 208 based on the size and/or weight of the tire and wheel assembly 208 obtained as described in block 406. In an exemplary embodiment, the tire can be filled in about 30 seconds or less. The apparatus 100 can also have a safety feature for automatically filling the tire and shutting down the apparatus 100 when the desired amount of mixture is injected into the tire and wheel assembly to prevent from over filling the tire with the mixture. For example, the apparatus 100 may include a trigger that activates injecting the mixture into the tire and wheel assembly 208. If the trigger is accidentally released prior to the apparatus 100 completing the injection of the mixture, the apparatus will automatically shut down as a safety precaution.
The automatic filling feature can be carried out by a control panel (not shown) mounted on the cart assembly 110 including a key pad allowing the operator to enter the number of pounds of fill desired for a given tire size. The key pad can also be used to input the specific gravity for the fill mixture to be injected into the tire. The control panel can include a processor programmed to convert the weight number input to a volume to determine the desired flow rate (pump rate) required to inject the selected weight of fill into the tire. Pump speed for the reactant materials can be monitored and controlled by, for example, placing a counter on the drive shaft of each pump to monitor the number of rotations of the shaft and thereby monitor the volume of the reactant materials. The weight scale 120 on work surface 114 can be used to weigh the empty tire and wheel assembly to obtain a tare weight for the tire and wheel assembly and to monitor weight increase for the tire and wheel assembly as the mixture of reactant materials with entrained gas is injected into the tire. Once the weight selected by the operator is reached, the control panel can be programmed to shut off the pumps for the reactant materials and also the source of nucleating gas to the mixer.
In block 420, after filling, the valve stem opening 206 can be plugged with a rubber plug to keep the mixture inside the tire and wheel assembly 208. The inserted plug can also serve to prevent a user from accidentally adding air to the foam-filled tire and wheel assembly 208. The plug may be an indication that the tire and wheel assembly 208 has been filled with foam. The filled tire and wheel assembly 208 is placed on its side for about 3-10 minutes to allow the mixture to react to create the foam and to allow the foam to rise and to allow trapped air to escape from the vent holes(s) formed in the tire, as shown in block 422. This also allows the foam to take an initial cure. If the filled tire is handled before the initial foam cure takes, the tire bead may be dislodged from the wheel. The foam-filled tire and wheel assembly 208 can then be placed on a holding fixture, such as a storage rack, and set aside for about 12-24 hours (cure time), as shown in block 424. After 12-24 hours, the foam-filled tire 208 can be returned to service. The tire is now filled with a flexible, light weight foam having a cellular structure with a density of about 30 lbs/ft3 or less. In one, but not the only, exemplary embodiment the resulting foam has a density of 14.5 lbs/ft3 or less.
It should be emphasized that the above-described embodiments of the present apparatus for flatproofing a tire, particularly, any “preferred” embodiments, are merely possible examples of implementations, merely set forth for a clear understanding of the principles of the invention. Many variations and modifications may be made to the above-described embodiment(s) without departing substantially from the spirit and principles of the invention. All such modifications and variations are intended to be included herein within the scope of this disclosure and protected by the following claims.