Patent Application
20120103550
The present invention relates to an apparatus for transferring a wet paper web from a press nip defined between two press members in a press section to a drying section of a papermaking machine, and for structuring the web, comprising: an impermeable transfer belt arranged in a loop such that the transfer belt passes through the press nip and the wet paper web passes through the press nip enclosed between a press felt and the transfer belt, said transfer belt having a surface in contact with the wet paper, and a permeable final fabric in form of a structuring fabric for transfer of the web onto a drying cylinder of said drying section, the structuring fabric having a structured surface and being arranged in a loop within which a suction transfer device is disposed, said suction transfer device having a suction zone in which suction is exerted through the structuring fabric.
Many attempts to combine the bulk-generating benefit of throughdrying with the dewatering efficiency of wet-pressing have been disclosed over the past 20 years. An example of such a process is disclosed in U.S. Pat. No. 6,287,426 issued Sep. 11, 2001 to Edwards et al., which is herein incorporated by reference. This process utilizes a high pressure dewatering nip formed between a felt and an impermeable belt to increase the wet web consistency to about 35 to 50 percent. The web adheres to and follows the impermeable belt as it exits the press nip. The dewatered web is then transferred to a “web-structuring” fabric with the aid of a vacuum roll to impart texture to the web prior to drying.
Transfer belts having a regular or uniform grooved micro-structure on their surface running in the machine direction have been used for transferring a web from a press felt to a further downstream process. The grooved belt is compressed flat in the dewatering press nip, allowing the dewatered web to transfer to the belt, but then rebounds to its natural grooved state soon after leaving the press. While effective for relatively heavy basis weight webs, the use of such modified belts still is not effective for processing light-weight tissue webs at high speeds necessary for commercial applications because of the difficulty associated with transferring low basis weight wet webs, which have virtually no strength. A wet fiber web will not naturally make such a transfer because there is a thin water film between the fiber web and the belt surface that generates a high adhesion force between the two materials. Attempts to remove the fragile web from the belt surface often result in torn webs.
Therefore, there is a need for an efficient apparatus for and method of making wet-pressed paper webs at high speeds.
The apparatus according to the present invention is characterized in that the surface of the transfer belt that contacts the wet paper web has a non-uniform distribution of microscopic-scale depressions, and that the suction zone includes a transfer point spaced a distance D from the press nip in a machine direction along which the transfer belt runs, the transfer belt being arranged to bring the paper web into contact with the structuring fabric in the suction zone for a length L in the machine direction, such that suction is exerted on the paper web to transfer the paper web from the transfer belt onto the structuring fabric at the transfer point.
The present disclosure is directed to a papermaking machine and associated methods for forming a fibrous paper web from papermaking fibers, and in some embodiments for structuring the tissue web for increasing its effective bulk. In accordance with a first aspect of the disclosure, a papermaking machine for making a paper web comprises a forming section for forming a wet fiber web, a press section arranged to receive the wet fiber web from the forming section and operable to press the wet fiber web to partially dewater the web, and a drying section for drying the fiber web. The press section comprises at least one press having two cooperating press members forming a press nip therebetween, and a press felt arranged in a loop such that the press felt passes through the press nip. The papermaking machine further comprises an impermeable transfer belt arranged in a loop such that the transfer belt passes through the press nip and the wet fiber web passes through the press nip enclosed between the press felt and the transfer belt. The papermaking machine further includes a final fabric arranged in a loop within which a suction transfer device is disposed.
The suction transfer device has a suction zone in which suction is exerted through the final fabric, the suction zone including a transfer point spaced a distance D from the press nip in a machine direction along which the transfer belt runs, the transfer belt being arranged to bring the fiber web into contact with the final fabric in the suction zone for a length L in the machine direction, such that suction is exerted on the fiber web to transfer the fiber web from the transfer belt onto the final fabric at the transfer point.
The transfer belt has a surface in contact with the wet fiber web characterized by a non-uniform distribution of microscopic-scale pits or depressions. By “microscopic-scale” is meant that the average diameter of the depressions is less than about 200 μm. For examples, the depressions can range from 10 μm to about 200 μm, and more particularly from about 50 μm to about 200 μm in size. By “non-uniform” is meant that the depressions do not form a regular pattern but instead are essentially randomly distributed over the surface.
In one embodiment, the surface of the transfer belt (also referred to as a “particle belt”) that contacts the wet fiber web is formed by a coating of a polymeric resin having inorganic particles dispersed therein. The particles give the web-contacting surface a microscopically rough topography characterized by a non-uniform or random distribution of depressions. However, the desired belt surface can be provided in other ways. For example, a foamed polymeric surface can be formed and then sanded to expose the gas-filled pores of the foam, thus forming microscopic-scale depressions in the surface.
In one embodiment, the transfer belt runs at a speed of at least 1000 m/min, the distance D is at least about 2 m, and the length L is at least about 10 mm during machine operation.
In particular embodiments, the suction transfer device has a curved outer surface about which the final fabric is partially wrapped, and the transfer belt partially wraps the outer surface of the suction transfer device with the final fabric disposed between the suction transfer device and the transfer belt having the fiber web thereon. For example, the transfer belt can wrap the suction transfer device for the length L, measured as an arc length while vacuum is applied, of about 10 mm to about 200 mm, such as about 10 mm to about 50 mm, the transfer belt diverging from the final fabric at a point P located at an outgoing end of the arc length L.
In one embodiment, the suction zone Z is longer than the arc length L and extends downstream of the point P. The point P can be located intermediate between upstream and downstream ends of the suction zone Z in the machine direction.
In some embodiments, the papermaking machine is configured for making a tissue fiber web having a basis weight less than about 20 grams/m2 (“gsm”). Further, some embodiments are configured for making a structured tissue web, wherein the final fabric is a web-structuring fabric (also referred to as a “texturizing fabric”) for imparting a structure to the tissue web for enhancing its effective bulk. The suction transfer device suctions the damp fiber web onto the web-structuring fabric to cause the fiber web to conform to its structured surface.
In accordance with another aspect of the disclosure, a method of configuring and operating a papermaking machine for making a paper web is provided. The method comprises steps of using a forming section to form a wet fiber web, using a press section as previously described to press and dewater the wet fiber web, and using a drying section to dry the fiber web. The method further comprises the step of selecting the distance D between the press nip and the transfer point taking into account at least a linear speed of the transfer belt, a basis weight of the paper web, and a roughness characteristic of the surface of the transfer belt in contact with the wet fiber web, such that within the distance D a thin water film between the fiber web and the surface of the transfer belt at least partially dissipates to allow the fiber web to be separated from the transfer belt without breaking.
In another aspect, the present disclosure describes a method for making a wet-pressed tissue comprising: (a) forming a wet tissue web having a basis weight of about 20 grams or less per square meter by depositing an aqueous suspension of papermaking fibers onto a forming fabric; (b) carrying the wet tissue web to a dewatering pressure nip while supported on a papermaking felt; (c) compressing the wet tissue web between the papermaking felt and a particle belt, whereby the wet tissue web is dewatered to a consistency of about 30 percent or greater and transferred to the surface of the particle belt; (d) transferring the dewatered web from the particle belt to a texturizing fabric, with the aid of vacuum, to mold the dewatered web to the surface contour of the fabric; (e) pressing the web against the surface of a Yankee dryer while supported by a texturizing fabric and transferring the web to the surface of the Yankee dryer; and (f) drying and creping the web to produce a creped tissue sheet.
The wet tissue web can be dewatered to a consistency of about 30 percent or greater, more specifically about 40 percent or greater, more specifically from about 40 to about 50 percent, and still more specifically from about 45 to about 50 percent. As used herein and well understood in the art, “consistency” refers to the bone dry weight percent of the web based on fiber.
The level of compression applied to the wet web to accomplish dewatering can advantageously be higher when producing light-weight tissue webs. Suitable press loads have a peak pressure of about 4 MPa or greater, more specifically from about 4 to about 8 MPa, and still more specifically from about 4 to about 6 MPa.
The machine speed for the method described above can be about 1000 meters per minute or greater, more specifically from about 1000 to about 2000 meters per minute, more specifically from about 1200 to about 2000 meters per minute, and still more specifically from about 1200 to about 1700 meters per minute. As used herein, the machine speed is measured as the linear speed of the particle belt.
The dwell time, which is the time the dewatered tissue sheet remains supported by the particle belt, is a function of the machine speed and the length of the particle belt run between the point at which the web transfers from the felt to the particle belt and the point at which the web transfers from the particle belt to the texturizing fabric. Because a light-weight wet tissue web is very weak, the water film between the web and the transfer belt needs to be well disrupted, more than for heavier paper grades, before subsequent transfer to the texturizing fabric is attempted. The water film break-up is a time-dependent process and, although various things (e.g., heat energy, electrostatic energy, surface energy, vibration) can accelerate it, the time available for the film to break up is reduced as the machine speed increases. Thus, all things being equal, the distance between the nip press and the point of transfer to the texturizing fabric (at the vacuum roll) needs to be increased beyond conventional distances in order to run faster. Similarly, the distance also needs to be increased in order to run lower basis-weight webs in order to achieve a more complete film break-up. It is estimated that the distance scales linearly with machine speed. Suitable distances between the nip press and the point of transfer to the texturizing fabric can be about 2.0 meters/1000 meters/minute of machine speed or greater, more specifically from about 2.5 to about 10 meters/1000 meters/minute of machine speed.
As used herein, a “texturizing fabric” (also referred to as a “web-structuring fabric”) is a papermaking fabric, particularly a woven papermaking fabric, having a topographical or three-dimensional surface that can impart’ bulk to the final tissue sheet. Examples of such fabrics suitable for purposes of this invention include, without limitation, those disclosed in U.S. Pat. No. 5,672,248 to Wendt et al., U.S. Pat. No. 5,429,686 to Chiu et al., U.S. Pat. No. 5,832,962 to Kaufman et al., U.S. Pat. No. 6,998,024 B2 to Burazin et al., and U.S. Patent Application Publication 2005/0236122 A1 by Mullally et al., all of which are incorporated herein by reference.
The level of vacuum used to effect the transfer of the tissue web from the particle belt to the texturizing fabric will depend upon the nature of the texturizing fabric. In general, the vacuum can be about 5 kPa or greater, more specifically from about 20 to about 60 kPa, still more specifically from about 30 to about 50 kPa. The vacuum at the pick-up (vacuum transfer roll) plays a much more important role for transferring light-weight tissue webs from the transfer belt to the texturizing fabric than it does for heavier paper grades. Because the wet web tensile strength is so low, the transfer must be 100 percent complete before the belt and fabric separate, or else the web will be damaged. On the other hand, for heavier-weight paper webs there is sufficient wet strength to accomplish the transfer, even over a short micro-draw, with modest vacuum (20 kPa). For light-weight tissue webs, the applied vacuum needs to be much stronger in order to cause the vapor beneath the tissue to expand rapidly and push the web away from the belt and transfer the web to the fabric prior to fabric separation. On the other hand, the vacuum cannot be so strong as to cause pinholes in the sheet after transfer.
To further effect transfer and molding of the web into the texturizing fabric, the vacuum transfer roll may contain a second vacuum holding zone.
The transfer of the web to the texturizing fabric can include a “rush” transfer or a “draw” transfer. Rush transfers are transfers where the receiving fabric (downstream fabric) is traveling at a machine speed that is lower than the machine speed of the upstream fabric. Draw transfers are the opposite, i.e., the receiving fabric is traveling at a machine speed that is higher than the upstream fabric. Depending upon the nature of the texturizing fabric, rush transfer can aid in creating higher sheet caliper. When used, the level of rush transfer can be about 5 percent or less.
Fabric cleaning can be particularly advantageous, particularly using a method that leaves a minimal amount of water on the fabric (about 3 gsm or less). Suitable fabric cleaning methods include air jets, thermal cleaning, and high pressure water jets. Coated fabrics, which clean more-easily than non-coated fabrics, can be employed.
The bulk of the tissue sheets produced by the method of this invention can be about 10 cubic centimeters or greater per gram of fiber, more specifically from about 10 to about 20 cubic centimeters per gram of fiber (cc/g).
Having thus described the invention in general terms, reference will now be made to the accompanying drawings, which are not necessarily drawn to scale, and wherein:
The present inventions now will be described more fully hereinafter with reference to the accompanying drawings, in which some but not all embodiments of the inventions are shown. Indeed, these inventions may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein; rather, these embodiments are provided so that this disclosure will satisfy applicable legal requirements. Like numbers refer to like elements throughout.
A papermaking machine 10 is illustrated in
The drying section 50 comprises a heated drying cylinder 52, which is covered by a hood 54. The drying cylinder and hood collectively can comprise a Yankee dryer. At the outlet side of the drying section, a creping doctor 56 is arranged to crepe the fibrous web off the drying cylinder 52. An application device 58 is provided for applying a suitable adhesive or other composition on the envelope surface of the drying cylinder 52. The resulting creped web is thereafter rolled into a parent roll (not shown) for subsequent conversion into the final product form as desired.
The press section 30 comprises at least one press, which has two cooperating first and second press members 31 and 32, which press members together define a press nip. Further, the press section comprises an endless press felt 33 that runs in a loop around the first press member 31 and guide rolls 34, and an endless impermeable transfer belt 35. The transfer belt 35 runs in a loop around the second press member 32 and a plurality of guide rolls 36. A suction roll (not numbered) is also shown in
In the embodiment shown in
The papermaking machine further comprises a permeable final fabric 37 arranged to run in a loop around a suction transfer device 38 located adjacent to the transfer belt 35 to define a transfer point 40 for transfer of the paper web from the transfer belt 35 to the final fabric 37. The transfer point 40 is located at a distance D from the press nip, as measured along the path traversed by the transfer belt 35. The suction transfer device 38 forms a suction zone 41 operable to exert suction through the final fabric 37 to transfer the paper web from the transfer belt 35 onto the final fabric 37. In the case of manufacturing a structured tissue web, the final fabric comprises a web-structuring fabric (or “texturizing fabric”) having a structured surface, and the suction exerted by the suction transfer device 38 further serves to mold the damp tissue web to the structured surface of the fabric. The “web-structuring fabric” can have about 25 or fewer machine direction-oriented knuckles or other raised surface features per square centimeter. The fabric 37 runs around a transfer roll 39, which defines a non-compressing nip with the drying cylinder 52 for transfer of the tissue web from the fabric 37 onto the drying cylinder 52.
In the embodiment shown in
The characteristics of the transfer belt 35 and the arrangement of the transfer belt 35 in relation to the web-structuring fabric 37 and suction transfer device 38 are of particular importance in the case of the manufacture of low-basis-weight tissue webs, such as tissue webs having a basis weight of about 20 grams per square meter (gsm) or less, more specifically from about 10 to about 20 gsm, still more specifically from about 10 to about 15 gsm. As used herein, “basis weight” refers to the amount of bone dry fiber in the web while positioned on the drying cylinder 52 during the tissue making process. This is to be distinguished from “finished” basis weight, which can be influenced by the presence of crepe folds that foreshorten the web in the machine direction. However, the basis weight of a fiber web on the dryer can be closely estimated from a finished basis weight by measuring the basis weight of the tissue web after all of the machine-direction foreshortening has been pulled out. Fiber webs having such low basis weight are particularly difficult to handle in a papermaking machine because a wet fiber web has virtually no tensile strength. As a consequence, the process of separating the wet fiber web from the transfer belt 35 and transferring it onto the web-structuring fabric 37 is complicated by the extremely low strength of the web.
More particularly, as the transfer belt 35 with the fiber web thereon exits the press nip formed by the press members 31, 32, a thin water film exists between the fiber web and the surface of the transfer belt 35. It is theorized that as long as this water film is intact, the fiber web cannot be separated from the transfer belt without significant risk of the web breaking. It has been found through multiple trials of transfer belts having different properties that the surface characteristics of the transfer belt play an important role in determining whether or not the fiber web can be separated from the transfer belt. Specifically, it has been found that some types of transfer belts make it difficult or essentially impossible to separate the fiber web, while other types of transfer belts allow the fiber web to be separated (as long as other criteria are also met, as further described below). Based on these trials, it is theorized that the transfer belts that permit the web to be separated somehow allow the thin water film to dissipate or break up after a certain period of time has elapsed after the web exits the press nip, while the transfer belts that do not permit the web to be separated without breaking do not allow the water film to dissipate.
In view of the trial results, it has been found that a papermaking machine such as the one depicted in
Regarding the surface characteristics of the transfer belt 35, it has been found that a transfer belt whose web-contacting surface is formed by a substantially nonporous polymeric coating, and which may have a surface that is ground or sanded to increase its surface roughness to an arithmetic average roughness of about Ra=2 to 5 μm generally does not allow the fiber web to be separated from the transfer belt even when the distance D is made long enough to provide a dwell time td of at least 0.5 s. It should be noted that for reasons of machine compactness it is usually desired to keep the distance D as small as possible while still allowing the fiber web transfer to be carried out reliably without breaking the web. Thus, based on the trials that have been done, it was determined that transfer belts with a substantially nonporous polymeric coating cannot be used, even if sanded to increase their surface roughness.
Such sanded or ground belts are generally ground using a drum sander and thus have a web-contacting surface that is characterized by a plurality of grooves or striations extending along the machine direction (MD), as can be seen in
On the other hand, it has been found that a transfer belt having a web-contacting surface characterized by a nonuniform distribution of microscopic-scale depressions (also referred to as “pits” or “holes”), even though its surface roughness is in generally the same range as the ground belts discussed above (e.g., Ra of about 2 to about 10 μm), allows the fiber web to separate from the belt in a reasonably short distance D. As an example, a suitable transfer belt 35 can comprise a G3 TRANSBELT®, or an LA TRANSBELT®, which are available from Albany International Corp., and are substantially as described in U.S. Pat. No. 5,298,124, incorporated herein by reference. Alternatively, the transfer belt can be a T2-style transfer belt from Ichikawa Co., Ltd., substantially as described in U.S. Pat. No. 6,319,365 and U.S. Pat. No. 6,531,033, the disclosures of which are incorporated herein by reference. The surface of the belt is formed by a coating of a resin such as acrylic or aliphatic polyurethane, into which is blended a quantity of inorganic particulate filler such as kaolin clay. The embedded particles of the filler give the surface of the belt a surface topography characterized by a non-uniform or random distribution of depressions on the microscopic scale as that term has been previously defined. The particles have a particle size generally less than about 50 μm, and a substantial proportion of the particles are less than about 10 μm.
Even using the above-described type of “micro-depression” transfer belt, it is still necessary to meet a number of other criteria in order to assure that particularly low-basis-weight fiber webs can be successfully transferred to the web-structuring fabric 37 at the transfer point 40. These criteria include the dwell time td as previously noted, the dryness of the web exiting the press nip, the amount of suction exerted by the suction transfer device 38, and the specific manner in which the transfer belt 35 engages the suction transfer device.
Regarding the dwell time td, for machine speeds (i.e., the linear speed of the transfer belt 35) of at least 1000 m/min up to a maximum of about 2000 m/min (more particularly, 1000 m/min to about 1700 m/min, and still more particularly about 1200 m/min to about 1700 m/min), the dwell time td should be at least about 0.1 s, more particularly at least about 0.15 s, and still more particularly at least about 0.2 s. Based on the machine speed, the distance D can be estimated in order to provide the requisite dwell time. For example, if the machine speed has been set at 1500 m/min, then it can be estimated that the distance D likely should be at least about 2.5 m (to give a dwell time td of at least 0.1 s), more likely should be at least about 3.75 m (to give a dwell time of about 0.15 s), and still more likely should be at least about 5 m (to give a dwell time of about 0.2 s). This initial estimate of the distance D may need to be adjusted somewhat based on other factors, but can provide at least a rough estimate of the minimum distance that is likely to be workable. Of course, the distance D can always be made longer than the estimated minimum.
With respect to the dryness of the fiber paper web leaving the press nip, in general, the dryer the web is, the easier it is to separate the web from the transfer belt 35 because the wet strength of the web generally increases with increasing dryness. Accordingly, as the web dryness increases, generally the distance D can be reduced; conversely, the less dry the web is, the greater the distance D must be, all other things being equal. The press section 30 of the papermaking machine 10 of
The level of vacuum in the suction transfer device 38 used to effect the transfer of the fiber web from the transfer belt 35 to the web-structuring fabric 37 will depend upon the nature of the web-structuring fabric. In general, the vacuum can be about 5 kPa or greater, more specifically from about 20 to about 70 kPa, still more specifically from about 30 to about 50 kPa. The vacuum at the vacuum transfer device plays a much more important role for transferring light-weight tissue webs from the transfer belt to the web-structuring fabric than it does for heavier paper grades. Because the wet web tensile strength is so low, the transfer must be 100 percent complete before the belt and fabric separate, or else the web will be damaged. On the other hand, for heavier-weight paper webs there is sufficient wet strength to accomplish the transfer, even over a short micro-draw, with modest vacuum (20 kPa). For light-weight tissue webs, the applied vacuum needs to be much stronger in order to cause the vapor beneath the web to expand rapidly and push the web away from the belt and transfer the web to the web-structuring fabric prior to fabric separation. On the other hand, the vacuum cannot be so strong as to cause pinholes in the fiber web.
Additionally, as previously noted, the reliability of the web transfer onto the web-structuring fabric 37 is aided by properly configuring the suction transfer device 38 and its engagement with the transfer belt 35. In particular, the contact between the fiber web W on the transfer belt 35 and the web-structuring fabric 37 is not a tangential contact, but rather the contact area occupies a finite predetermined length L (
In one embodiment, the point at which the transfer belt 35 first becomes tangent to the suction transfer device 38 defines an angle α measured between the transfer belt 35 and web-carrying fabric 37 and a horizontal plane, the upstream end of the suction zone defines an angle β between the web-carrying fabric 37 and the horizontal plane, the point P at which the transfer belt 35 is tangent to the suction transfer device 38 at the outgoing side defines an angle γ between the transfer belt 35 and the horizontal plane, and the downstream end of the suction zone defines an angle δ between the web-carrying fabric 37 and the horizontal plane. In one embodiment, the angle α can be about 31.7°, the angle β can be about 30.7°, the angle γ can be about 29.6°, and the angle δ can be about 11.9°. Thus, the total wrap of the transfer belt 35 about the suction transfer device is 2.1° (α minus γ), and the amount of that wrap subject to vacuum is 1.1° (β minus γ). Given a suction transfer device diameter of about 800 mm, the wrap distance L corresponding to the 2.1° wrap is about 15 mm.
As also illustrated in
As the fiber web is subjected to a high vacuum and the web is still damp during the suction phase, the structure of the fiber web W will remain after the suction device (s). To achieve the desired structuring it is also advantageous that the speed of the fabric 37 is not greater than, and preferably is less than, the speed of the transfer belt 35. In particular, this difference in speed can be from about 0% up to about 10%, more particularly about 0% to about 5%. However, in other embodiments, the speed of the fabric 37 can be slightly greater (e.g., up to about 3% greater) than that of the transfer belt 35 so as to effect a “draw” transfer of the fiber web W, although this is not preferred.
The length L of the contact area in particular embodiments can be at least about 10 mm and can be up to about 200 mm. More particularly, the length L can be from about 10 mm to about 50 mm. It will be understood that the distance L is measured during machine operation when the suction transfer device is applying suction and the transfer belt is suctioned against the device.
A papermaking machine 110 in accordance with another embodiment is shown in
The drying section 150 comprises a heated drying cylinder 152, which is covered by a hood 154. The drying cylinder and hood collectively can comprise a Yankee dryer. At the outlet side of the drying section, a creping doctor 156 is arranged to crepe the fibrous web off the drying cylinder 152. An application device 158 is provided for applying a suitable glue on the envelope surface of the drying cylinder 152.
The press section 130 comprises at least one press, which has two cooperating first and second press members 131 and 132, which press members together define a press nip. Preferably, the press is a shoe press in which the first press member comprises a shoe press roll 131 and the second press member comprises a counter roll 132. Further, the press section comprises an endless impermeable transfer belt 135. The transfer belt 135 runs in a loop around the second press member 132 and a plurality of guide rolls 136. Unlike the machine of
A papermaking machine 210 in accordance with a third embodiment is depicted in
The drying section 250 comprises a heated drying cylinder 252, which is covered by a hood 254. The drying cylinder and hood collectively can comprise a Yankee dryer. At the outlet side of the drying section, a creping doctor 256 is arranged to crepe the fibrous web off the drying cylinder 252. An application device 258 is provided for applying a suitable coating on the envelope surface of the drying cylinder 252.
The press section 230 comprises at least one press, which has two cooperating first and second press members 231 and 232, which press members together define a press nip. Further, the press section comprises an endless impermeable transfer belt 235. The transfer belt 235 runs in a loop around the second press member 232 and a plurality of guide rolls 236. Unlike the machine of
A papermaking machine 310 in accordance with a fourth embodiment is shown in
The drying section 350 comprises a heated drying cylinder 352, which is covered by a hood 354. The drying cylinder and hood collectively can comprise a Yankee dryer. At the outlet side of the drying section, a creping doctor 356 is arranged to crepe the fibrous web off the drying cylinder 352. An application device 358 is provided for applying a suitable coating on the envelope surface of the drying cylinder 352.
The press section 330 comprises at least one press, which has two cooperating first and second press members 331 and 332, which press members together define a press nip. Further, the press section comprises an endless impermeable transfer belt 335. The transfer belt 335 runs in a loop around the second press member 332 and a plurality of guide rolls 336. As in the machines of
Unlike the machines of
The bulk of the tissue sheets produced by the papermaking machine in accordance with the present disclosure can be about 10 cubic centimeters or greater per gram (cc/g) of fiber, more specifically from about 10 to about 20 cc/g.
As used herein, “bulk” is calculated as the quotient of the “calliper” (hereinafter defined) of a tissue sheet, expressed in microns, divided by the dry basis weight, expressed in grams per square meter. The resulting sheet bulk is expressed in cubic centimeters per gram. More specifically, the tissue sheet caliper is the representative thickness of a single tissue sheet measured in accordance with TAPPI test methods T402 “Standard Conditioning and Testing Atmosphere For Paper, Board, Pulp Handsheets and Related Products” and T411 om-89 “Thickness (caliper) of Paper, Paperboard, and Combined Board” with Note 3 for stacked sheets. The micrometer used for carrying out T411 om-89 is an Emveco 200-A Tissue Caliper Tester available from Emveco, Inc., Newberg, Oregon. The micrometer has a load of 2 kilo-Pascals, a pressure foot area of 2500 square millimeters, a pressure foot diameter of 56.42 millimeters, a dwell time of 3 seconds and a lowering rate of 0.8 millimeters per second.
As used herein, the “machine direction (MD) tensile strength” is the peak load per 3 inches of sample width when a sample is pulled to rupture in the machine direction. Similarly, the “cross-machine direction (CD) tensile strength” is the peak load per 3 inches of sample width when a sample is pulled to rupture in the cross-machine direction. The percent elongation of the sample prior to breaking is the “stretch”.
The procedure for measuring tensile strength and stretch is as follows. Samples for tensile strength testing are prepared by cutting a 3 inches (76.2 mm) wide by 5 inches (127 mm) long strip in either the machine direction (MD) or cross-machine direction (CD) orientation using a JDC Precision Sample Cutter (Thwing-Albert Instrument Company, Philadelphia, Pa., Model No. JDC 3-10, Serial No. 37333). The instrument used for measuring tensile strengths is an MTS Systems Sintech IIS, Serial No. 6233. The data acquisition software is MTS TestWorks® for Windows Ver. 3.10 (MTS Systems Corp., Research Triangle Park, N.C.). The load cell is selected from either a 50 Newton or 100 Newton maximum, depending on the strength of the sample being tested, such that the majority of peak load values fall between 10% and 90% of the load cell's full scale value. The gauge length between jaws is 4+/−0.04 inches (101.6+/−1 mm). The jaws are operated using pneumatic-action and are rubber coated. The minimum grip face width is 3 inches (76.2 mm), and the approximate height of a jaw is 0.5 inches (12.7 mm). The crosshead speed is 10+/−0.4 inches/min (254+/−1 mm/min), and the break sensitivity is set at 65%. The sample is placed in the jaws of the instrument, centered both vertically and horizontally. The test is then started and ends when the specimen breaks. The peak load is recorded as either the “MD tensile strength” or the “CD tensile strength” of the specimen depending on direction of the sample being tested. At least six (6) representative specimens are tested for each product or sheet, taken “as is”, and the arithmetic average of all individual specimen tests is either the MD or CD tensile strength for the product or sheet.
“Surface roughness” of the transfer belts can be measured by several methods, including optical microscopy of cross-sections of the belt, or by stylus profilometry of the surface. Since the roughness of the belt surface may differ in the MD and CD directions with the CD value typically greater, the stated roughness is the CD roughness. A suitable portable device that enables in-field measurement is made by Taylor-Hobson Corporation, Model Surtronic 25 Ra.
A twin-wire former was used to make a lightweight paper sheet of less than 20 gsm. The papermaking machine speed was 600 m/min. The wet fiber web was transferred to a felt and partially dewatered with vacuum to a dryness of about 25% dry solids content. The web was then compressively dewatered with an extended nip press at a load of 400 kN/m, with a peak pressure of 4 MPa, to a dryness of about 40%. The felt and fiber web were pressed against a belt similar to an Albany T2 transfer belt with a roughness Ra of about 6 micrometers as measure by stylus profilometry. Upon exiting the press the sheet was attached to the transfer belt. The transfer belt and web traveled around the press roll and were then contacted with a texturizing fabric (style 44GST) manufactured by Albany. The distance from the press to the vacuum roll was about 2.4 meters. The texturizing fabric was in contact with the fiber web for a distance of about 25 mm after it came into contact with the vacuum roll. Just prior to separation of the fabric and the transfer belt, a high vacuum level exceeding 20 kPa was supplied from inside the vacuum roll, causing the fiber web to transfer from the transfer belt to the fabric. The fiber web and fabric traveled together to a pressure roll at the Yankee dryer, where the fiber web was pressed to the Yankee. The fiber web adhered to the Yankee with the aid of adhesives sprayed onto the Yankee surface prior to the pressure roll. The sheet was dried and creped and wound up at a speed 20% slower than the Yankee speed. The resulting physical properties were measured:
The conditions of Example 1 were repeated with a higher machine speed of 1000 m/min. The transfer of the fiber web to the fabric failed. From these trials, it was determined that the Albany T2 type of belt is not suitable for high-speed manufacture of low basis-weight paper in the type of process described herein.
The conditions of Example 1 were repeated with a transfer belt similar to an Albany LA particle belt with a roughness of 3 micrometers. The fiber web transferred to the fabric at speeds up to 1200 m/min.
Product samples were taken at 600 meters/minute because of limitations with the reel, but the properties of sheets produced at higher speeds are believed to be very similar. The properties of the tissue were as follows:
This Example illustrates that the use of a particle belt as the transfer belt enables transfer of the web at higher speeds than conventional transfer belts.
The process of Example 3 was repeated, except the distance from the press to the vacuum roll was increased from 2.4 meters to 4 meters. The fiber web transferred to the fabric at speeds up to 1400 m/min. The consistency of the web transferred to the dryer was 48% dry solids content, resulting in 22% less water evaporation compared to a normal wet-press process, and 50-60% less water evaporation than a typical through-air-drying process. This Example illustrates that the maximum speed at which the fiber web will transfer is increased with increased residence time on the transfer belt prior to transfer to the texturizing fabric.
Example 4 conditions were repeated with an Albany G3 style belt. The fiber web transferred to the fabric at speeds up to 1600 meters/minute. From these trials, it was determined that the Albany LA and G3 type belts are suitable for high-speed manufacture of low basis-weight paper in the type of process described herein. This Example illustrates that altering the surface structure of the particle belt can improve transfer to the texturizing fabric.
Example 5 conditions were repeated, but the contact between the texturizing fabric and the transfer belt was increased to over 100 mm and the vacuum zone of the vacuum roll was adjusted to cover at least half of that region. The fiber web was transferred to the texturizing fabric with ease at vacuum levels of 5 kPa. This Example illustrates that the residence time under vacuum at the transfer roll can improve transfer to the texturizing fabric.
A crescent former was used to make a lightweight paper sheet of 13.8 gsm using the process illustrated in
The tissue sheet was converted into 2-ply bath tissue with calendering and exhibited good softness.
A tissue sheet was made generally as described in Example 7, except that the paper machine speed at the Yankee dryer was 1000 m/min and the texturizing fabric was of a different style. The dryer basis weight was 13.7 gsm. There was a 3% rush transfer of the web to the fabric. The physical properties of the resulting tissue sheet were as follows:
A tissue sheet was made generally as described in Example 7 but with slightly less tensile strength in order to develop more softness in the final product. The physical properties of the resulting tissue sheet were as follows:
The basesheet was then converted into a 2-ply roll of bath tissue by plying the basesheet with another roll of similar properties, with the fabric-facing side of the basesheets facing each other in the final product. The 2-ply product was calendered with steel rollers spaced apart by 635 micron (0.025 inch) and 35.5 meters of tissue were wound onto a 43 mm diameter core. This product was preferred over existing commercial bath tissue product in consumer testing. The resulting physical properties of the finished product were as follows:
The foregoing examples illustrate the ability of the process to make a wide range of products of high bulk at high rate of production on the paper machine and at a reduced energy usage for drying the paper.
Many modifications and other embodiments of the inventions set forth herein will come to mind to one skilled in the art to which these inventions pertain having the benefit of the teachings presented in the foregoing descriptions and the associated drawings. Therefore, it is to be understood that the inventions are not to be limited to the specific embodiments disclosed and that modifications and other embodiments are intended to be included within the scope of the appended claims. Although specific terms are employed herein, they are used in a generic and descriptive sense only and not for purposes of limitation.
According to one aspect the present disclosure refers to an apparatus for transferring a wet paper web from a press nip defined between two press members in a press section to a drying section of a papermaking machine, comprising: an impermeable transfer belt arranged in a loop such that the transfer belt passes through the press nip and a wet paper web passes through the press nip enclosed between a press felt and the transfer belt; and a permeable web-carrying fabric having a structured surface and being arranged in a loop within which a suction transfer device is disposed, the suction transfer device having a suction zone in which suction is exerted through the web-carrying fabric, the suction zone including a transfer point spaced a distance D from the press nip in a machine direction along which the transfer belt runs, the transfer belt being arranged to bring the paper web into contact with the web-carrying fabric in the suction zone for a length L in the machine direction, such that suction is exerted on the paper web to transfer the paper web from the transfer belt onto the web-carrying fabric at the transfer point, the transfer belt having a surface in contact with the wet paper web characterized by a non-uniform distribution of microscopic-scale depressions.
According to another aspect the present disclosure refers to a papermaking machine for making a paper web from an aqueous suspension of papermaking fibers, comprising: a forming section structured and arranged to form a wet paper web; a press section arranged to receive the wet paper web from the forming section, the press section comprising a press having two cooperating press members forming a press nip therebetween, a press felt arranged in a loop such that the press felt passes through the press nip, and an impermeable transfer belt arranged in a loop such that the transfer belt passes through the press nip and the wet paper web passes through the press nip enclosed between the press felt and the transfer belt; a permeable web-carrying fabric arranged in a loop within which a suction transfer device is disposed, the suction transfer device having a suction zone in which suction is exerted through the web-carrying fabric, the suction zone including a transfer point spaced a distance D from the press nip in a machine direction along which the transfer belt runs, the transfer belt being arranged to bring the paper web into contact with the web-carrying fabric in the suction zone for a length L in the machine direction, such that suction is exerted on the paper web to transfer the paper web from the transfer belt onto the web-carrying fabric at the transfer point; the transfer belt having a surface in contact with the wet paper web characterized by a non-uniform distribution of microscopic-scale depressions; and a drying cylinder onto which the web-carrying fabric transfers the paper web for final drying thereof.
According to a further aspect the present disclosure refers to a method of configuring and operating a papermaking machine for making a paper web, comprising the steps of: using a forming section to form a wet paper web; employing a press section to receive the wet paper web from the forming section and dewater the wet paper web, the press section comprising a press having two cooperating press members forming a press nip therebetween, a press felt arranged in a loop such that the press felt passes through the press nip, an impermeable transfer belt arranged in a loop such that the transfer belt passes through the press nip and the wet paper web passes through the press nip enclosed between the press felt and the transfer belt, and a permeable web-carrying fabric being arranged in a loop within which a suction transfer device is disposed, the suction transfer device having a suction zone in which suction is exerted through the web-carrying fabric, the suction zone including a transfer point spaced a distance D from the press nip in a machine direction along which the transfer belt runs, the transfer belt bringing the paper web into contact with the web-carrying fabric in the suction zone for a length L in the machine direction, such that suction is exerted on the paper web to transfer the paper web from the transfer belt onto the web-carrying fabric at the transfer point, the transfer belt having a surface in contact with the wet paper web characterized by a non-uniform distribution of microscopic-scale depressions; using a drying cylinder onto which the web-carrying fabric transfers the paper web to dry the paper web; and selecting the distance D taking into account at least a linear speed of the transfer belt, a basis weight of the paper web, and a roughness characteristic of the surface of the transfer belt in contact with the wet paper web, such that within the distance D a thin water film between the paper web and the surface of the transfer belt at least partially dissipates to allow the paper web to be separated from the transfer belt and to be suctioned onto the web-carrying fabric.
According to a further aspect the present disclosure refers to a method for carrying a tissue web having a basis weight between 10 and 20 g/m2 from a press nip to a dryer section in a papermaking machine, the method comprising the steps of: arranging a press fabric to pass through the press nip; arranging an impermeable transfer belt to pass through the press nip with a wet tissue web enclosed between the press fabric and the transfer belt, the tissue web adhering to and following the transfer belt after the press fabric and transfer belt diverge downstream of the press nip, the transfer belt having a surface in contact with the tissue web characterized by a non-uniform distribution of microscopic-scale depressions, the transfer belt traveling in a machine direction at a speed of about 1000 m/min or greater; carrying the tissue web on the transfer belt to a suction transfer device having a permeable web-carrying fabric partially wrapped thereabout, the suction transfer device defining a suction zone, the transfer belt being arranged to partially wrap about the suction transfer device, the transfer belt bringing the tissue web into contact with the web-carrying fabric in the suction zone for a length L in the machine direction, such that suction is exerted on the tissue web to transfer the tissue web from the transfer belt onto the web-carrying fabric at a transfer point; and arranging the transfer belt and suction transfer device such that the transfer belt and tissue web travel a distance D from the press nip to the transfer point, the distance D being selected taking into account at least the speed of the transfer belt, the basis weight of the tissue web, and a roughness characteristic of the surface of the transfer belt in contact with the tissue web, such that within the distance D a thin water film between the tissue web and the surface of the transfer belt at least partially dissipates to allow the tissue web to be separated from the transfer belt and to be suctioned onto the web-carrying fabric.
According to a further aspect the present disclosure refers to a method for using an impermeable transfer belt in a papermaking machine, the transfer belt having a web-contacting surface characterized by a non-uniform distribution of microscopic-scale depressions, the papermaking machine having two cooperating press members forming a press nip therebetween and a press felt arranged in a loop such that the press felt and a wet paper web pass through the press nip, having a permeable web-carrying fabric arranged in a loop within which a suction transfer device defining a suction zone is disposed, and having a drying cylinder onto which the web-carrying fabric transfers the paper web to dry the paper web, the method comprising the steps of: arranging the impermeable transfer belt to pass through the press nip with the wet paper web enclosed between the press fabric and the transfer belt with the paper web against the web-contacting surface of the transfer belt, the transfer belt traveling in a machine direction at a speed of about 1000 m/min. or greater, the paper web adhering to and following the transfer belt after the press fabric and transfer belt diverge downstream of the press nip; carrying the tissue web on the transfer belt to the suction transfer device having the permeable web-carrying fabric partially wrapped thereabout, and causing the transfer belt to bring the paper web into contact with the web-carrying fabric in the suction zone for a length L in the machine direction, such that suction is exerted on the paper web to transfer the paper web from the transfer belt onto the web-carrying fabric at a transfer point; and arranging the transfer belt and suction transfer device such that the transfer belt and paper web travel a distance D from the press nip to the transfer point, the distance D being selected taking into account at least the speed of the transfer belt, the basis weight of the paper web, and a roughness characteristic of the web-contacting surface of the transfer belt, such that within the distance D a thin water film between the paper web and the surface of the transfer belt at least partially dissipates to allow the paper web to be separated from the transfer belt and to be suctioned onto the web-carrying fabric.
According to a further aspect the present disclosure refers to a method for making a wet-pressed tissue comprising: (a) forming a wet tissue web having a basis weight of about 20 grams or less per square meter by depositing an aqueous suspension of papermaking fibers onto a forming fabric; (b) carrying the wet tissue web to a dewatering pressure nip while supported on a papermaking felt; (c) compressing the wet tissue web between the papermaking felt and a particle belt, whereby the wet tissue web is dewatered to a consistency of about 30 percent or greater and transferred to the surface of the particle belt; (d) transferring the dewatered web from the particle belt to a texturizing fabric, with the aid of vacuum, to mold the dewatered web to the surface contour of the fabric; (f) pressing the web against the surface of a Yankee dryer while supported by a texturizing fabric and transferring the web to the surface of the Yankee dryer; and (g) drying and creping the web to produce a creped tissue sheet.
This application is a divisional application of currently pending application Ser. No. 12/443,697, filed Mar. 31, 2009, which is a national stage application filed under 35 U.S.C. 371 of International Application No. PCT/SE2007/000939, filed Oct. 26, 2007, which claims priority from U.S. Provisional Application Nos. 60/854,964 and 60/863,200 both filed Oct. 27, 2006.
| Number | Date | Country | |
|---|---|---|---|
| 60854964 | Oct 2006 | US | |
| 60863200 | Oct 2006 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12443697 | Mar 2009 | US |
| Child | 13289626 | US |