Patent Application
20130298628
The present invention relates, in general, to an apparatus and method for manufacturing a large-caliber product using a hydroforming process and, more particularly, to an apparatus and method for manufacturing a large-caliber product which can minimize a sealing force that acts in an axial direction of the large-caliber product when the product is manufactured.
Generally, large-caliber products such as wheel rims for vehicles are produced mainly by roll forming processes. In such a roll forming process, a tube is shaped by several stepwise roll forming operations such that a flange is expanded to reach an area at which a wheel rim makes contact with a tire. Thereafter, the expanded tube is shaped by an additional two or three roll forming operations using rolls which are disposed inside and outside the tube. Subsequently, a size compensation operation using an expender is carried out, thus completely forming a wheel rim for vehicles.
However, in the case where the roll forming process is used to manufacture a wheel rim for vehicles, because a tubular steel substance is processed by several stepwise roll forming operations, the productivity is comparatively low. In addition, a heat treatment process such as an annealing process must accompany the roll forming process, since severe local work hardening is induced during the roll forming process which is carried out at room temperature.
In an effort to overcome the above-mentioned problems of the apparatus using the roll forming process, methods for manufacturing large-caliber products such as wheel rims for vehicles using hydroforming processes are being studied.
A typical hydroforming process which is used to manufacture a torsion beam for vehicles includes: an operation of bending a tubular steel substance in response to the shape of a final product; an operation of forming the bending-processed steel substance through press work into a shape in which it can be seated into a hydroforming mold; and a hydroforming operation of supplying fluid onto an inner surface of the steel substance and pressurizing the inner surface thereof to expand the diameter of the steel substance, thus completing a final product.
In the case of a large-caliber product that is comparatively short and has a simple shape, such as a wheel rim, it can be formed only by the simple hydroforming process. Therefore, compared to the manufacturing process using the roll forming process which requires several steps to be carried out, the apparatus using the hydroforming process can markedly enhance the productivity. Furthermore, fluid applies hydrostatic pressure to the entirety of the inner surface of the steel substance, thus making it possible to uniformly shape the steel substance without causing local work hardening. Therefore, a separate heat treatment process is not required.
As such, the method for manufacturing a large-caliber product using the hydroforming process can provide several advantages, compared to the method using the roll forming process. However, there is a problem that must be solved in order to manufacture a large-caliber product using the hydroforming manufacturing apparatus. The problem is that because sealing force that acts in the axial direction of a steel substance when the large-caliber product is formed is very large, it is not easy to manufacture an axial pressurization cylinder or mold which can withstand the large sealing force.
Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and an object of the present invention is to provide an apparatus and method for manufacturing a large-caliber product using a hydroforming process which is configured such that axial punches which are disposed at opposite sides of the apparatus so as to be movable towards each other can be coupled to each other, whereby sealing force that acts in the axial direction when the large-caliber product is manufactured can be minimized.
In order to accomplish the above object, in an aspect, the present invention provides an apparatus for manufacturing a large-caliber product using a hydroforming process, including: upper and lower molds into which a tubular steel substance having a large caliber is seated; a first axial punch and a second axial punch disposed on opposite sides of the steel substance so as to be movable towards each other, the first and second axial punches having front surfaces configured so as to be insertable into each other; a first pressurization cylinder and a second pressurization cylinder respectively moving the first axial punch and the second axial punch towards each other and inserting the first and second axial punches into each other, thus forming a sealing space defined by the first and second axial punches and a pressurization space defined by an inner surface of the steel substance and the first and second axial punches; and a hydroforming control unit supplying fluid into the pressurization space through an oil-pressure passage formed in at least one of the first and second axial punches so as to pressurize the inner surface of the steel substance, thus forming the large caliber product.
In another aspect, the present invention provides a method for manufacturing a large-caliber product using a hydroforming process, including: a hydroforming preparation operation of seating a steel substance having a large caliber onto a lower mold and moving an upper mold downwards, thus closing an entirety of the upper and lower molds; an axial punch setting operation of moving a first axial punch and a second axial punch towards each other from opposite sides of the steel substance and inserting the first and second axial punches into each other, thus forming a sealing space defined by the first and second axial punches, and a pressurization space defined by an inner surface of the steel substance and the first and second axial punches; and a hydroforming operation of supplying fluid into the pressurization space through at least one of the first and second axial punches and pressurizing the inner surface of the steel substance, thus forming the large-caliber product.
In an apparatus and method for manufacturing a large-caliber product using a hydroforming process according to the present invention, it is possible to produce a final product using only a single process. Thanks to a reduced number of processes, the production cost can be reduced, and the productivity of the apparatus can be markedly enhanced.
Furthermore, the hydroforming manufacturing apparatus is advantageous in that a steel substance can be uniformly shaped by hydrostatic pressure of fluid without local work hardening being caused. Therefore, a separate heat treatment process is not required.
Moreover, the hydroforming manufacturing apparatus makes it possible to precisely shape the steel substance. Thus, the products produced by the present invention are superior in terms of shape uniformity and roundness (the center of gravity).
As described above, if a large-caliber product such as a wheel rim for vehicles is manufactured by the conventional hydroforming manufacturing apparatus, sealing force acting in the axial direction markedly increases, thus making it difficult to operate the apparatus normally. The reason for this will be explained with reference to
A hydroforming manufacturing apparatus includes upper and lower molds 1 and 2 into which a steel substance 3 is seated, first and second axial punches 10 and 20 which are moved from opposite sides of the upper and lower molds 1 and 2 into the upper and lower molds 1 and 2 to seal the steel substance 3, and first and second pressurization cylinders 15 and 25 which respectively move the first and second axial punches 10 and 20 in the horizontal direction. The operation method of the hydroforming manufacturing apparatus will be described below.
First, the steel substance 3 is placed onto the lower mold 2. The upper mold 1 is moved downwards to close the entirety of the molds. Thereafter, the first and second pressurization cylinders 15 and 25 respectively move the first and second axial punches 10 and 20 towards each other from the opposite sides of the upper and lower molds 1 and 2, thus sealing opposite sides of the steel substance 3. As shown in sectional view 1-1′ of
After the steel substance 3 has been sealed, fluid is supplied into the steel substance 3 through an oil-pressure passage 22 which is formed in at least one of the first and second axial punches 10 and 20, thus pressurizing an inner surface of the steel substance 3. Hydrostatic pressure of the fluid that is applied to the steel substance 3 expands the diameter of the steel substance 3. As a result, the steel substance 3 is brought into close contact with the upper and lower molds 1 and 2 and thus shaped into a shape of a wheel rim for vehicles. Here, when the steel substance 3 is being shaped by hydrostatic pressure of fluid, high pressure is also applied to the first and second axial punches 10 and 20. Sufficient sealing force to withstand the high pressure must be applied to the first and second axial punches 10 and 20 so that hydrostatic pressure of the fluid can be continuously applied to the inner surface of the steel substance 3.
The sealing force applied to the first and second axial punches 10 and 20 is increased in proportion to a cross-sectional area of a portion to which fluid is applied. In more detail, the sealing force is increased in proportion to the square of the diameter of the steel substance 3. The reason for this is due to the fact that if the diameter of the steel substance 3 is d0, fluid is applied to the entirety of the cross-sectional area (πd02) of the first or second axial punch which has the same diameter as that of the steel substance 3. Therefore, when a large-caliber product such as a wheel rim for vehicles is manufactured, sealing force applied to the first and second axial punches 10 and 20 is exponentially increased as the diameter of the product is increased.
However, because the maximum pressure of the first and second pressurization cylinders 15 and 25 of the hydroforming manufacturing apparatus that has been commercialized is comparatively low, the apparatus must be remodeled to have high-pressure cylinders which are required to manufacture a large-caliber product. For this, a massive remodeling process is required, and this process is expensive. In the worst case, a layout of the apparatus would be changed in such a way that the molds are not installed, making it impossible to produce a large-caliber product.
To solve the above-mentioned problems, the inventor of the present invention introduces a method in which the sealing force can be effectively reduced by changing the shaft of the axial punches rather than remodeling the cylinders. Hereinafter, an apparatus and method for manufacturing a large-caliber product using a hydroforming process according to the present invention will be described in detail with reference to the attached drawings.
As shown in
Comparing
However, unlike in the conventional technique, the hydroforming manufacturing apparatus according to the present invention is configured such that the first axial punch 30 and the second axial punch 40 can be moved towards each other and inserted into the steel substance 3. In other words, as shown in sectional view 2-2′ of
Furthermore, the hydroforming manufacturing apparatus according to the present invention is configured such that the first axial punch 30 and the second axial punch 40 are inserted into each other in the steel substance 3. For this, a protrusion and a depression are formed in the front surface of each axial punch such that the axial punches can correspond to each other. When the first axial punch 30 and the second axial punch 40 are moved towards each other by the first pressurization cylinder 50 and the second pressurization cylinder 60 and are coupled to each other, the sealing space A is defined by both axial punches, and the pressurization space B is defined by the inner surface of the steel substance and both axial punches are formed. As such, the protrusion and the depression of each axial punch can be formed in any shapes, so long as the sealing space A and the pressurization space B can be formed when the axial punches are coupled to each other.
After the sealing space A and the pressurization space B have been formed by coupling the first and second axial punches 30 and 40 to each other, fluid is supplied, under the control of the hydroforming control unit, into the pressurization space B through the oil-pressure passage 42 which is formed in at least one of the first and second axial punches 30 and 40, thereby pressurizing the inner surface of the steel substance 3. At this time, the fluid does not enter the sealing space A. Therefore, hydrostatic pressure applied by the fluid is limited to the pressurization space B. As a result, a cross-sectional area of a portion to which the hydrostatic pressure is applied is markedly reduced. The sealing force applied to the first axial punch 30 and the second axial punch 40 can also be markedly reduced.
As such, the axial punches are coupled to each other, whereby space into which fluid is drawn is limited. Thereby, the cross-sectional area of a portion of each axial punch that makes with fluid can be reduced. As a result, the sealing force corresponding to the hydrostatic pressure of fluid can be reduced. The present invention is based on this technical idea. The inventor of the present invention introduces the following additional elements to embody the above-stated technical idea.
Separate sealing members 70 are provided on portions of the first and second axial punches 30 and 40 which form the sealing space A. As stated above, the technical idea of the present invention is that the sealing space A into which no fluid flows is formed by coupling the first and second axial punches 30 and 40 to each other. Therefore, if fluid enters the sealing space A during the hydroforming process, the effect of reducing the sealing force cannot be obtained. To prevent this, the sealing members 70 are preferably provided on the portions that form the sealing space A.
Given the fact that each axial punch has a cylindrical shape, each sealing member 70 is preferably an O-ring.
Furthermore, any member can be used as the sealing member 70, so long as it can provide a sealing effect that can prevent fluid from entering the sealing space A.
Preferably, an air hole 32 is formed in at least one of the first and second axial punches 30 and 40 so that air can be discharged to the outside from the sealing space A through the air hole 32. Because the first axial punch 30 and the second axial punch 40 are continuously moved towards each other during the hydroforming process, if the air hole 32 is not formed, air that has been in the sealing space A is compressed, thus acting as reaction force which impedes movement of the first and second axial punches 30 and 40. Since fluid does not enter the sealing space A, the air hole may be configured such that it communicates with the outside of the axial punch.
As shown in the lower portion of
As shown in
Hereinafter, the method for manufacturing the large-caliber product using the hydroforming process according to the present invention will be described in detail with reference to
First, the steel substance 3 having a large-caliber is seated onto the lower mold 2, and the upper mold 1 is moved downwards to close the entirety of the molds. Thereafter, the first and second axial punches 30 and 40 which have the front surfaces that can be coupled to each other are respectively disposed on the opposite sides of the steel substance 3 [(a) of
Subsequently, the first axial punch 30 and the second axial punch 40 are moved towards the steel substance 3 from the opposite sides of the steel substance 3 and then inserted into each other. Thereby, the sealing space A which is defined only by the first and second axial punches 30 and 40, and the pressurization space B which is defined by the inner surface of the steel substance 3 and the first and second axial punches 30 and 40 are formed [(b) of
Because the air hole 32 is formed in at least one of the first and second axial punches 30 and 40, when the first and second axial punches 30 and 40 move forwards, air can be discharged out of the sealing space A through the air hole 32. The reason for this is due to the fact that, if air is compressed in the sealing space A, the compressed air may impede the operation of the first and second axial punches 30 and 40.
Thereafter, fluid is supplied into the pressurization space B through at least one of the first and second axial punches 30 and 40, thus pressurizing the inner surface of the steel substance 3 [(c) of
In this case, because some of the fluid may flow backwards and leak out of the second axial punch 40, the stepped portions 48 are respectively provided on the first and second axial punches 30 and 40 so that the opposite side ends of the steel substance 3 can be reliably sealed.
Meanwhile, the fact that the oil-pressure passage 42 may be configured such that it directly communicates with the pressurization space B has been illustrated with reference to
After the diameter of the steel substance 3 has started to be expanded by hydrostatic pressure of fluid, the first axial punch 30 and the second axial punch 40 gradually move forwards to enable the fluid to compensate for expanded space and continuously pressurize the inner surface of the steel substance 3 [(d) of
Although the preferred embodiment of the present invention has been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/KR11/00486 | 1/24/2011 | WO | 00 | 6/13/2013 |