Aqueous and radiation-curable printing varnishes and printing inks with improved properties

Abstract

Aqueous and radiation-curable printing varnishes and printing inks, are disclosed which contain special polyoxyalkylene polysiloxane copolymers. These printing varnishes and printing inks have improved scratch resistance, a higher gliding ability and an extremely low tendency to foam, so that the production of printing inks proceeds without problems and, at the same time, an optically attractive typography can be obtained.

Description

FIELD OF INVENTION

The invention relates to aqueous and radiation-curable printing varnishes and printing inks, which contain special polyoxyalkylene polysiloxane copolymers. These printing varnishes and printing inks have improved scratch resistance, increased sliding ability, as well as an extremely low tendency to foam, so that the production of printing inks proceeds with less problems and, at the same time, an optically attractive typography can be obtained.

BACKGROUND INFORMATION AND PRIOR ART

A constantly increasing number of printing inks and printing varnishes are being changed over to ecologically safer, water-based and radiation-curable systems. These systems are known and described, for example, in "The Printing Ink Manual" (R. H. Leach, R. J. Pearce, London 1993) or "UV and EB Curing Formulation for Printing Inks, Coatings and Paints" (R. Holeman, P. Oldring, London 1988).

Their production and especially their processing properties are causally linked to the additives used. Because of the binders and wetting agents used, aqueous printing inks and printing varnishes have a great tendency to foam. This becomes noticeable, not only during the production of these inks, but also especially during the application, when high amounts of air are introduced into the printing inks and printing varnishes.

Defoaming is frequently also a very critical problem for radiation-curable systems. In order to achieve a defoaming effect, a certain incompatibility is necessary. Radiation-curable systems frequently also have a very low dissolving power, so that the addition of known defoaming substances (such as silicone oils) easily leads to cloudiness, flow disorders or gloss reduction particularly in the case of printing varnishes.

The use of silicone oils, particularly of dimethylpolysiloxanes of low to moderate viscosity, for defoaming aqueous and radiation-curable printing inks is known and described, for example, in the book by W. Noll, "Chemie und Technologie der Silicone" (Chemistry and Technology of the Silicones) or in the aforementioned literature. The use of polyoxyalkylene polysiloxane copolymers as defoaming agents is also known. The U.S. Pat. No. 3,763,021 discloses a preparation for defoaming aqueous latexes, which is composed of (1) 1 to 20% by weight of a siloxane glycol copolymer of the general formula ##STR1## wherein x has an average value of 6 to 420 and y an average value of 3 to 30 and G represents a group having the structure --D(OR) .sub.z A, in which D is an alkylene group, R represents ethylene groups and propylene groups or butylene groups in such a ratio of ethylene groups to other alkylene groups, that the ratio of carbon atoms to oxygen atoms in all OR blocks ranges from 2.3:1 to 2.8:1, z has an average value of 25 to 100 and A is a terminal group, (2) 65 to 98% by weight of polypropylene glycol with an average molecular weight ranging from 1000 to 2000 and (3) 1 to 15% by weight of a hydrophobic silicon oxide.

Typical methods for producing these aforementioned polyoxyalkylene polysiloxane copolymers are described in U.S. Pat. No. 3,402,192, U.S. Pat. No. 3,746,653, U.S. Pat. No. 3,784,479 and U.S. Pat. No. 3,865,544.

These preparations, containing silicone oils or polyoxyalkylene polysiloxane copolymers, as known in the art, are suitable to a greater or lesser extent to prevent the formation of foam or destroy already existing foam in aqueous or radiation-curable printing inks or printing varnishes. However, it has turned out that printing varnishes and printing inks, to which polysiloxanes or polyoxyalkylene polysiloxane copolymers were added for defoaming, frequently have wetting defects or reduced gloss when applied on surfaces. This becomes evident particularly in highly sensitive systems and for printing on critical substrates (such as polyolefin film).

An important field of use are printing inks for paper and film. The handling of these objects for the industrial production of these printed products creates difficulties, because it is not always possible to avoid damaging the surface of the elements, which are often stacked or transported after the printing process.

Attempts have already been made to improve the ability to manipulate freshly printed objects by adding friction reducing additives, such as oils or waxes (for example, polyethylene or polytetrafluoroethylene waxes) to the printing ink or applying these subsequently on the printed surface. This frequently also leads to a disturbing loss of gloss. Also subsequent application of wax on the printed product may not always be satisfactory, particularly since the manufacturing costs are increased by this additional processing step. Furthermore, high use concentrations are required in order to achieve an improvement in the scratch resistance.

In much the same way as in air drying or forced (temperature) drying system, silicone oils, organically modified siloxanes, such as polyoxyalkylene polysiloxane copolymers (for example, German patent 36 37 155) or also spherical silicone elastomer particles are also added for these purposes at the present time to aqueous and radiation-curable printing varnishes and printing inks.

However, the aforementioned polyoxyalkylene polysiloxane copolymers, which effectively improve scratch resistance only at very high concentrations, lead to appreciable foam stabilization. Such foam stabilization is undesirable for the production of printing inks as well as for the actual printing process, since the printing result or the typography is negatively affected. On the other hand, those skilled in the art are also aware that the use of spherical, elastomeric silicone particles can lead to a reduction in gloss and can also lead to various wetting defects.

There is therefore a practical need for modified silicone additives, which in small concentrations improve the ability to manipulate objects, particularly objects printed serially. These additives are needed to, in particular, improve the scratch resistance of fresh surfaces, increase the sliding ability of these surfaces and, at the same time, prevent the formation of foam or destroy foam already formed, without having a negative effect on the typography.

Moreover, such additives shall be universally usable that is, largely independent of the nature and composition of the printing inks and printing varnishes to which they are added in order to improve the aforementioned properties. These additive should be effective in the least possible quantities and should not adversely affect the application properties of the printing inks and the printing varnishes. In particular, they should not have a harmful effect on the development of the surface film and the curing of the printing inks. Furthermore, they may not have a disadvantageous effect on the stability of the printing inks and the printing varnishes and should not make the running properties worse.

OBJECT OF THE INVENTION

It is therefore an object of the invention to provide compounds which fulfill the aforementioned requirements and are effective when added in small amounts.

SUMMARY OF THE INVENTION

Pursuant to the invention, this objective is accomplished by aqueous and radiation-curable printing varnishes and printing inks, which contain polyoxyalkylene polysiloxane copolymers of the general formula ##STR2## wherein R.sup.1 =an alkyl group with 1 to 8 carbon atoms,

R.sup.2 =(CH.sub.2).sub.p O--, wherein p=2, 3 or 4, R.sup.3 =hydrogen, an alkyl group with 1 to 4 carbon atoms or a (meth) acryloxy group, n=40 to 60 and m=0 to 3, x and y being selected so that the average molecular weight (Mw) of the polyoxyalkylene blocks is 300 to 800 g/mole and the molar ratio of x:y is 0.2 to 0.7, in amounts of 0.001 to 1.5% by weight based on the varnish formulation, for improving scratch resistance and for defoaming.

The numerical values of the subscripts n and m are of vital importance for the properties of the compounds; n indicating the number of methylalkylsiloxy units and determining the chain length. For the compounds, which are to be used pursuant to the invention, n has a numerical value of 40 to 60. It is well known to those skilled in the art that the compounds are present in the form of a mixture with a distribution determined essentially by the laws of statistics. The value of n therefore represents the average value of the number of methylalkylsiloxy units.

The value of m is 0 to 3 and preferably 0 to 1. If m=0, the compounds are linear siloxanes, which have terminal polyoxyalkylene units. The polyoxyalkylene blocks consist of oxyethylene and oxypropylene units, the molecular weight of the polyoxyalkylene blocks being 300 to 800 g/mole. The molar ratio of oxyethylene units to oxypropylene units, expressed by the ratio of x:Y, is 0.2 to 0.7. It has turned out that these structures of the block copolymers are of decisive importance for the advantages achieved pursuant to the invention.

For formulating radiation-curable systems in the printing ink industry, it is constantly becoming more important to increase the proportion of cross-linkable components in the formulation. The use of acrylated or methacrylated and thus cross-linkable additives minimizes their tendency to migrate and the proportion of substances extractable from the film. Their use in radiation-curable printing varnishes and printing inks is therefore particularly preferred.

Examples of polyoxyalkylene polysiloxane copolymers, which can be used pursuant to the invention and are particularly suitable are ##STR3##

These polyoxyalkylene polysiloxane copolymers are synthesized by the addition reaction between polyoxyalkylene glycols or polyoxyalkylene ethers of olefinically unsaturated alcohols, such as allyl polyoxyalkylene ethers, and appropriate hydrogensiloxanes. This reaction is catalyzed by platinum compounds and described, for example, in the German patent 11 65 028.

Any free polyoxyalkylene glycols or their monoethers or monoesters which, due to the synthesis procedure, are contained in the copolymers to be used pursuant to the invention, can be tolerated and do not have to be removed from the product.

By reacting hydroxy-functional polyoxyalkylene-polysiloxane copolymers with acrylic acid or methacrylic acid or their esters, the corresponding acryloxy-functional or methacryloxy-functional polyoxyalkylene polysiloxane copolymers can be obtained by esterification and transesterification reactions known in the art.

The polyoxyalkylene polysiloxane copolymers can be used as such or in the form of aqueous emulsions.

The compounds, which are to be used pursuant to the invention, are added to aqueous, radiation-curable printing varnishes and printing inks in amounts of 0.001 to 1.5% by weight, based on the formulation of the paint or varnish.

The polyoxyalkylene polysiloxane copolymers which are to be tested, correspond to the general formula I, in which the R.sup.1, R.sup.2 and R.sup.3 groups as well as the subscripts n, m, x and y have the meanings or values given in the table below.

TABLE______________________________________Compound n m x y x/y R1 R2 R3______________________________________1 50 0 3 7 0.43 methyl propoxy H2 47 3 3 7 0.43 methyl propoxy methyl3 40 0 3 11 0.28 methyl propoxy H4 40 0 4 6 0.66 methyl propoxy acryl5 20 0 3 7 0.43 methyl propoxy H6 20 0 3 7 0.43 methyl propoxy H7 50 0 9 21 0.43 methyl propoxy H8 47 3 7 7 1 methyl propoxy H9 47 3 7 7 1 methyl propoxy acryl10 40 0 0 10 0 methyl propoxy methyl______________________________________

The application properties of various compounds 1 to 4, which are to be used pursuant to the invention, as well as of the compounds of the comparison examples 5 to 10 are shown in the following.

For checking the application properties, the following formulations of aqueous and radiation-curable printing varnishes and printing inks were selected. The numerical data is given in % by weight.

______________________________________1. Aqueous Test SystemsPrinting Varnish 1Neocryl BT 21 Solution. *) 39.0Neocryl BT 44 48.5 styrene modified acrylate emulsion/ZenecaIsopropanol 3.8Propylene glycol 1.9Aquacare 531 1.9 wax emulsion/W. Priem GmbH & Co. KGWaer, demineralized 4.7Additive 0.2 100.0*) Neocryl BT 21 62.5 anionic acrylate emulsion/ ZenecaAmmonia, 25% 3.3Isopropanol 4.0Water, demineralized 30.2 100.0Printing Varnish 2Joncryl 74 50.5 Acrylate dispersion/Johnson PolymerJoncryl 680 solution *) 23.9Jonwax 35 7.2 polyethylene wax emulsion/ Johnson PolymerWater, demineralized 12.4Isopropanol 2.9Zinc solution 2.9Additive 0.2 100.0*) Joncryl 680 45.0 acrylate resin/Johnson PolymerAmmonia, 25% 11.2Isopropanol 10.0Water, demineralized 33.8 100.0Printing Varnish 3Joncryl 90 51.4 Styrol acrylate dispersion/ Johnson PolymerJoncryl 682 solution *) 25.7Dowanol DPM 1.8Jonwax 35 4.6 polyethylene wax emulsion/ Johnson PolymerIsopropanol 3.7Water, demineralized 8.9Dioctyl sulfosuccinate 3.7solution 50%Additive 0.2 100.0*) Joncryl 682 47.3 Acrylate resin/Johnson PolymerAmmonia, 25% 15.8Isopropanol 5.3Water, demineralized 31.6 100.0Printing Ink 1Material to be milled:Joncryl 61 18.7 Acrylate resin solution/ Johnson PolymerFoamex 810 0.1 Defoamer/Tego Chemie ServiceWater, demineralized 7.5Heliogenblau D7080 11.2 Phthalocyanine blue/BASFDispersed for one hour (equipment: Scandex)Lacquer deposit:Joncryl 8051 46.2 Acrylate dispersion/Johnson PolymerJonwax 35 4.7 Polyethylene wax emulsion/ Johnson PolymerAdditive 0.1Water, demineralized 6.8Isopropanol 4.7Dispersed for 5 minutes (equipment: Scandex) 100.02. Radiation-Curable SystemsEbecryl 608 40.0 Epoxy acrylate oligomer/UCBTPGDA 19.0 Difunctional acrylate monomer/ UCBEbecryl P 115 5.0 Tertiary amine/UCBOTA 480 20.0 Trifunctional acrylate oligomer/ UCBBenzophenone 3.0 Photoinitiator/UCBIrgacure 651 2.0 Photoinitiator/UCBAdditive 1.0 100.0Printing Varnish BEbecryl 204 41.5 PU acrylate/UCBTPGDA 41.0 Difunctional acrylate monomer/ UCBDarocure 1173 4.0 Photoinitiator/Ciba-GeigyEbecryl P 115 8.0 Tertiary amine/UCBAdditive 1.0 100.0______________________________________

The aqueous and radiation-curable printing inks are formulated in the usual manner in accordance with the formulations above. In each case, the additives are added as the last component and are incorporated by means of a Perlmill disk for 3 minutes at 1500 rpm. The printing ink is produced with the formulation above, using a Scandex for the dispersing, and the additives are the last components to be added to the lacquer deposit.

The radiation-curable printing varnishes are applied with a spiral doctor blade (12 .mu.m) on wet Lenetta film, which has been pretreated with a corona discharge, and the printing inks are applied with a doctor blade on transparent PVC film. Curing is accomplished by two passages through 120 watt/cm ultraviolet light at a speed of 20 m/min.

Scratch resistance is the ability of a surface to resist visible, linear damage by hard objects moving in contact with the surface. Specially converted film-drawing equipment, which is driven by an electric motor, is used for the measurement of so-called scratch values. Instead of the film-drawing doctor blade, a plate is mounted on the moving doctor blade holder; at the other end of the equipment the plate lies on rollers. The plate, on which the substrate (with the film coated with the printing ink) is fastened, can be moved with the help of the doctor blade holder. In order to simulate scratch stresses, a block with three points is placed on the printing ink film and loaded down with 500 g. The test film on the plate is pulled at a speed of 12 mm/sec under the weight. The vertical force required for this is measured and referred to as the scratch value. Scratch values are determined 24 hours after the film is cured.

If the points are replaced by hemispheres and the procedure above is followed, the so-called sliding value is measured as a frictional force.

Foaming Test

The aqueous printing varnish or printing ink (50 g) is weighed into a 150 mL beaker and sheared for 1 minute at 250 rpm with a Dissolver disk (3 cm diameter). Subsequently, 45 g are weighed into a measuring cylinder and the foam height is given in mm.

Deaeration Test

The radiation-curable printing varnish (30 g) is weighed into a 50 mL screw-top jar and sheared for 5 minutes at 3000 rpm with a Dissolver disk (2 cm diameter). The foam height is measured in mm and the decay height of the foam is measured in hours.

Wetting Behavior

The films, produced as described previously, are examined visually for wetting disorders and evaluated on a scale from 1 to 4, 1 being a defect-free film and 4 being a film with many wetting defects.

______________________________________Results in Printing Varnish 1 Foam Scratch Sliding Concen- Value Value Value Wetting BehaviorCompound tration mL/45 g mN/m mN/m (Scale of 1-4)______________________________________Blank 0 110 234 230 11 0.2 48 108 78 12 0.2 50 92 74 13 0.2 47 125 92 14 0.2 52 83 67 15 0.2 53 170 134 16 0.2 57 155 128 17 0.2 72 136 100 28 0.2 75 98 79 19 0.2 73 104 79 110 0.2 52 180 134 3______________________________________ ______________________________________Results in Printing Varnish 2 Foam Scratch Sliding Concen- Value Value Value Wetting BehaviorCompound tration mL/45 g mN/m mN/m (Scale of 1-4)______________________________________Blank 0 69 185 107 11 0.2 46 100 62 12 0.2 48 90 58 13 0.2 46 102 66 14 0.2 47 85 63 15 0.2 51 152 95 16 0.2 53 155 92 17 0.2 65 118 70 28 0.2 63 98 64 19 0.2 60 104 61 110 0.2 48 123 70 4______________________________________ ______________________________________Results in Printing Varnish 3 Foam Scratch Sliding Concen- Value Value Value Wetting BehaviorCompound tration mL/45 g mN/m mN/m (Scale of 1-4)______________________________________Blank 0 103 182 142 11 0.2 47 108 90 12 0.2 48 90 82 13 0.2 46 100 88 14 0.2 48 89 79 15 0.2 51 140 123 16 0.2 52 138 127 17 0.2 72 106 76 28 0.2 70 110 76 19 0.2 68 104 90 110 0.2 47 140 118 3______________________________________ ______________________________________Results in Printing Ink 1 Foam Scratch Sliding Concen- Value Value Value Wetting BehaviorCompound tration mL/45 g mN/m mN/m (Scale of 1-4)______________________________________Blank 0 62 159 120 11 0.2 45 106 70 12 0.2 47 90 68 13 0.2 46 99 72 14 0.2 47 89 66 15 0.2 49 128 99 26 0.2 52 138 106 17 0.2 58 103 73 28 0.2 57 108 75 29 0.2 57 104 74 210 0.2 46 140 108 4______________________________________ ______________________________________Results in Printing Varnish A Foam Foam Decay Scratch Sliding WettingCom- Concen- Height Time Value Value Behaviorpound tration mm min mN/m mN/m (Scale of 1-4)______________________________________Blank 0 10 180 230 198 31 1 1 15 102 84 12 1 1 15 94 80 13 1 1 10 99 86 14 1 1 15 89 79 15 1 1 20 168 150 26 1 1 15 150 135 27 1 7 150 107 89 38 1 8 220 99 80 29 1 8 250 97 74 210 1 1 15 140 123 4______________________________________ ______________________________________Results in Printing Varnish B Foam Foam Decay Scratch Sliding WettingCom- Concen- Height Time Value Value Behaviorpound tration mm min mN/m mN/m (Scale of 1-4)______________________________________Blank 0 150 210 168 21 1 1 10 80 72 22 1 1 15 78 70 23 1 1 10 85 75 24 1 1 15 80 69 25 1 1 20 159 109 26 1 1 15 150 115 27 1 7 100 97 85 38 1 8 170 80 78 39 1 8 150 84 80 310 1 1 10 136 99 4______________________________________

As can be seen from the preceding Tables, the compounds, which are to be used pursuant to the invention, are distinguished by their universal applicability.

As is evident from the Comparison Examples, the subscripts n and m and, the values of x and y as well as their ratio to one another are responsible for the fact that the polyoxyalkylene polysiloxane copolymers, which are to be used pursuant to the invention, are excellent defoamers and, at the same time, increase the scratch resistance of the printing inks as well as their sliding ability, without causing wetting defects during the printing process.

Claims

1. Aqueous and radiation-curable printing varnishes and printing inks, which contain polyoxyalkylene polysiloxane copolymers of the general formula ##STR4## wherein R.sup.1 =an alkyl group with 1 to 8 carbon atoms,

R.sup.2 =(CH.sub.2).sub.p O--, wherein p=2, 3 or 4,

R.sup.3 =hydrogen, an alkyl group with 1 to 4 carbon atoms or a (meth) acryloxy group with the proviso that at least one R.sup.3 is a (meth)acryloxy group,

n=40 to 60 and

m=0 to 3,

x and y being selected so that the average molecular weight (Mw) of the polyoxyalkylene blocks is 300 to 800 g/mole and the molar ratio of x:y is 0.2 to 0.7,

in amounts of 0.001 to 1.5% by weight based on the varnish and ink formulation.

2. Aqueous and radiation-curable (UV) printing varnishes and printing inks of claim 1, wherein m=0 or 1.

3. Radiation-curable (UV) printing varnishes and printing inks of claim 1, wherein the R.sup.3 group is methacryloxy or acryloxy.

4. The aqueous printing varnishes and printing inks of claim 1, wherein the R.sup.3 group is hydrogen or a methyl group.