Patent Application
20230174731
The present invention relates to an aqueous binder composition for mineral fibres, a method for producing a bonded mineral fibre product using said binder, and a mineral fibre product comprising mineral fibres in contact with a cured binder.
Mineral fibre products generally comprise man-made vitreous fibres (MMVF) such as, e.g., glass fibres, ceramic fibres, basalt fibres, slag wool, mineral wool and stone wool, which are bonded together by a cured thermoset polymeric binder material. For use as thermal or acoustical insulation products, bonded mineral fibre mats are generally produced by converting a melt made of suitable raw materials to fibres in conventional manner, for instance by a spinning cup process or by a cascade rotor process. The fibres are blown into a forming chamber and, while airborne and while still hot, are sprayed with a binder solution and randomly deposited as a mat or web onto a travelling conveyor. The fibre mat is then transferred to a curing oven where heated air is blown through the mat to cure the binder and rigidly bond the mineral fibres together.
In the past, the binder resins of choice have been phenol-formaldehyde resins which can be economically produced and can be extended with urea prior to use as a binder. However, the existing and proposed legislation directed to the lowering or elimination of formaldehyde emissions have led to the development of formaldehyde-free binders such as, for instance, the binder compositions based on polycarboxy polymers and polyols or polyamines, such as disclosed in EP-A-583086, EP-A-990727, EP-A-1741726, U.S. Pat. No. 5,318,990 and US-A-2007/0173588.
Another group of non-phenol-formaldehyde binders are the addition/elimination reaction products of aliphatic and/or aromatic anhydrides with alkanolamines, e.g., as disclosed in WO 99/36368, WO 01/05725, WO 01/96460, WO 02/06178, WO 2004/007615 and WO 2006/061249. These binder compositions are water soluble and exhibit excellent binding properties in terms of curing speed and curing density. WO 2008/023032 discloses urea-modified binders of that type which provide mineral wool products having reduced moisture take-up.
Since some of the starting materials used in the production of these binders are rather expensive chemicals, there is an ongoing need to provide formaldehyde-free binders which are economically produced.
A further effect in connection with previously known aqueous binder compositions from mineral fibres is that at least the majority of the starting materials used for the productions of these binders stem from fossil fuels. There is an ongoing trend of consumers to prefer products that are fully or at least partly produced from renewable materials and there is therefore a need to provide binders for mineral wool which are, at least partly, produced from renewable materials.
A further effect in connection with previously known aqueous binder compositions for mineral fibres is that they involve a high amount of components which are corrosive and/or harmful. This requires protective measures for the machinery involved in the production of mineral wool products to prevent corrosion and also requires safety measures for the persons handling this machinery. This leads to increased costs and health issues and there is therefore a need to provide binder compositions for mineral fibres with a reduced content of corrosive and/or harmful materials.
In the meantime, a number of binders for mineral fibres have been provided, which are to a large extend based on renewable starting materials. In many cases these binders based to a large extent on renewable resources are also formaldehyde-free.
However, many of these binders are still comparatively expensive because they are based on comparatively expensive basic materials.
Accordingly, it was an object of the present invention to provide a binder composition which is particularly suitable for bonding mineral fibres, uses renewable materials as starting materials, reduces corrosive and/or harmful materials, and is comparatively inexpensive to produce.
A further object of the present invention was to provide a mineral wool product bonded with such a binder composition.
A further object of the present invention was to provide a method of making such a mineral wool product.
In accordance with a first aspect of the present invention, there is provided a, preferably formaldehyde-free binder composition, comprising:
In accordance with a second aspect of the present invention, there is provided a method of producing a bonded mineral fibre product which comprises the step of contacting the mineral fibres with the aqueous binder composition described above.
In accordance with a third aspect of the present invention, there is provided a mineral wool product, comprising mineral fibres in contact with the cured binder composition according to the present invention.
The present inventors have surprisingly found that it is possible to obtain a mineral wool product comprising mineral fibres bound by a binder resulting from the curing of a binder composition, whereby the binder composition can be produced from inexpensive renewable materials to a large degree and does contain only to a minor degree any corrosive and/or harmful agents.
The aqueous binder composition for mineral fibres according to the present invention comprises
In a preferred embodiment, the binders according to the present invention are formaldehyde free.
For the purpose of the present application, the term “formaldehyde free” is defined to characterize a mineral wool product where the emission is below 5 μg/m2/h of formaldehyde from the mineral wool product, preferably below 3 μg/m2/h. Preferably, the test is carried out in accordance with ISO 16000 for testing aldehyde emissions.
Component (i)
Component (i) is in form of one or more oxidized lignins.
Lignin, cellulose and hemicellulose are the three main organic compounds in a plant cell wall. Lignin can be thought of as the glue, that holds the cellulose fibres together. Lignin contains both hydrophilic and hydrophobic groups. It is the second most abundant natural polymer in the world, second only to cellulose, and is estimated to represent as much as 20-30% of the total carbon contained in the biomass, which is more than 1 billion tons globally.
There are at least four groups of technical lignins available in the market. These four groups are shown in
A summary of the properties of these technical lignins is shown in
Lignosulfonate from the sulfite pulping process remains the largest commercial available source of lignin, with capacity of 1.4 million tonnes. But taking these aside, the kraft process is currently the most used pulping process and is gradually replacing the sulfite process. An estimated 78 million tonnes per year of lignin are globally generated by kraft pulp production but most of it is burned for steam and energy. Current capacity for kraft recovery is estimated at 160,000 tonnes, but sources indicate that current recovery is only about 75,000 tonnes. Kraft lignin is developed from black liquour, the spent liquor from the sulfate or kraft process. At the moment, 3 well-known processes are used to produce the kraft lignin: LignoBoost, LignoForce and SLRP. These 3 processes are similar in that they involve the addition of CO2 to reduce the pH to 9-10, followed by acidification to reduce pH further to approximately 2. The final step involves some combination of washing, leaching and filtration to remove ash and other contaminants. The three processes are in various stages of commercialization globally.
The kraft process introduces thiol groups, stilbene while some carbohydrates remain. Sodium sulphate is also present as an impurity due to precipitation of lignin from liquor with sulphuric acid but can potentially be avoided by altering the way lignin is isolated. The kraft process leads to high amount of phenolic hydroxyl groups and this lignin is soluble in water when these groups are ionized (above pH˜10).
Commercial kraft lignin is generally higher in purity than lignosulfonates. The molecular weight are 1000-3000 g/mol·s
Soda lignin originates from sodium hydroxide pulping processes, which are mainly used for wheat straw, bagasse and flax. Soda lignin properties are similar to kraft lignins one in terms of solubility and Tg. This process does not utilize sulphur and there is no covalently bound sulphur. The ash level is very low. Soda lignin has a low solubility in neutral and acid media but is completely soluble at pH 12 and higher.
The lignosulfonate process introduces large amount of sulphonate groups making the lignin soluble in water but also in acidic water solutions. Lignosulfonates has up to 8% sulfur as sulphonate, whereas kraft lignin has 1-2% sulfur, mostly bonded to the lignin. The molecular weight of lignosulfonate is 15.000-50.000 g/mol. This lignin contains more leftover carbohydrates compared to other types and has a higher average molecular weight. The typical hydrophobic core of lignin together with large number of ionized sulphonate groups make this lignin attractive as a surfactant and it often finds application in dispersing cement etc.
A further group of lignins becoming available is lignins resulting from biorefining processes in which the carbohydrates are separated from the lignin by chemical or biochemical processes to produce a carbohydrate rich fraction. This remaining lignin is referred to as biorefinery lignin. Biorefineries focus on producing energy, and producing substitutes for products obtained from fossil fuels and petrochemicals as well as lignin. The lignin from this process is in general considered a low value product or even a waste product mainly used for thermal combustion or used as low grade fodder or otherwise disposed of.
Organosolv lignin availability is still considered on the pilot scale. The process involves extraction of lignin by using water together with various organic solvents (most often ethanol) and some organic acids. An advantage of this process is the higher purity of the obtained lignin but at a much higher cost compared to other technical lignins and with the solubility in organic solvents and not in water.
Previous attempts to use lignin as a basic compound for binder compositions for mineral fibres failed because it proved difficult to find suitable cross-linkers which would achieve desirable mechanical properties of the cured mineral wool product and at the same time avoid harmful and/or corrosive components. Presently lignin is used to replace oil derived chemicals, such as phenol in phenolic resins in binder applications or in bitumen. It is also used as cement and concrete additives and in some aspects as dispersants.
The cross-linking of a polymer in general should provide improved properties like mechanical, chemical and thermal resistance etc. Lignin is especially abundant in phenolic and aliphatic hydroxyl groups that can be reacted leading to cross-linked structure of lignin. Different lignins will also have other functional groups available that can potentially be used. The existence of these other groups is largely dependent on the way lignin was separated from cellulose and hemicellulose (thiols in kraft lignin, sulfonates in lignosulfonate etc.) depending on the source.
It has been found that by using oxidized lignins, binder compositions for mineral fibres can be prepared which allow excellent properties of the mineral fibre product produced.
In one embodiment, the component (i) is in form of one or more oxidized kraft lignins.
In one embodiment, the component (i) is in form of one or more oxidized soda lignins.
In one embodiment, the component (i) is in form of one or more ammonia-oxidized lignins. For the purpose of the present invention, the term “ammonia-oxidized lignins” is to be understood as a lignin that has been oxidized by an oxidation agent in the presence of ammonia. The term “ammonia-oxidized lignin” is abbreviated as AOL.
In an alternative embodiment, the ammonia is partially or fully replaced by an alkali metal hydroxide, in particular sodium hydroxide and/or potassium hydroxide.
A typical oxidation agent used for preparing the oxidized lignins is hydrogen peroxide.
In one embodiment, the ammonia-oxidized lignin comprises one or more of the compounds selected from the group of ammonia, amines, hydroxides or any salts thereof.
In one embodiment, the component (i) is having a carboxylic acid group content of 0.05 to 10 mmol/g, such as 0.1 to 5 mmol/g, such as 0.20 to 1.5 mmol/g, such as 0.40 to 1.2 mmol/g, such as 0.45 to 1.0 mmol/g, based on the dry weight of component (i).
In one embodiment, the component (i) is having an average carboxylic acid group content of more than 1.5 groups per macromolecule of component (i), such as more than 2 groups, such as more than 2.5 groups.
In the binder composition according to the present invention, component (i), i.e. the one or more oxidized lignins, may be present in an amount of 25 to 95 wt.-%, such as 30 to 90 wt.-%, such as 35 to 85 wt.-%, based on the dry weight of binder composition.
It is believed that the carboxylic acid group content of the oxidized lignins plays an important role in the surprising advantages of the aqueous binder compositions for mineral fibres according to the present invention. In particular, it is believed that the carboxylic acid group of the oxidized lignins improve the cross-linking properties and therefore allow better mechanical properties of the cured mineral fibre products.
Component (ii)
Component (ii) is in form of one or more cross-linkers.
In one embodiment, the component (ii) is one or more cross-linkers selected from the group consisting of multifunctional organic amines such as an alkanolamine, diamines, such as hexamethyldiamine, triamines.
In one embodiment, the component (ii) is one or more cross-linkers selected from the group consisting of monoethanolamine, diethanolamine, triethanolamine, polyethylene imine, polyvinyl amine, fatty amines.
In one embodiment, the component (ii) is a fatty amide.
In one embodiment, the component (ii) is one or more cross-linkers selected from the group consisting of aldehydes, such as formaldehyde, glyoxal, glutaraldehyde, dimethoxyethanal, furfural, glycolaldehyde, glyoxalic acid, hydroxymethyl furfural.
In one embodiment, the component (ii) is one or more cross-linkers selected from the group consisting of isocyanates, polyacrylates.
In one embodiment, the component (ii) is one or more cross-linkers selected from molecules with a molecular weight less than 1500 g/mol having less than 3 epoxy groups; wherein preferably, it is not one or more flexible oligomer or polymer, such as a low Tg acrylic based polymer, such as a low Tg vinyl based polymer, such as low Tg polyether, which contains reactive functional groups such as carbodiimide groups, such as anhydride groups, such as oxazoline groups, such as amino groups, such as epoxy groups.
In one embodiment, the component (ii) is one or more cross-linkers selected from polyester polyols, such as polycaprolactone.
In one embodiment, the component (ii) is one or more cross-linkers in form of aziridines, such as CX100, NeoAdd-Pax 521/523.
In one embodiment, the component (ii) is one or more cross-linkers selected from the group consisting of starch, modified starch, CMC.
In one embodiment, the component (ii) is one or more cross-linkers in form of aliphatic multifunctional carbodiimides.
In one embodiment, the component (ii) is one or more cross-linkers selected from melamine based cross-linkers, such as a hexakis(methylmethoxy)melamine (HMMM) based cross-linkers.
Examples of such compounds are Picassian XL 701, 702, 725 (Stahl Polymers), such as ZOLDINE® XL-29SE (Angus Chemical Company), such as CX300 (DSM), such as Carbodilite V-02-L2 (Nisshinbo Chemical Inc.).
In one embodiment, the component (ii) is a melamine based crosslinker, such as a hexakis(methylmethoxy)melamine (HMMM) based cross-linker.
In one embodiment, the component (ii) is one or more cross-linkers selected from the group consisting of multifunctional organic amines such as an alkanolamine, diamines, such as hexamethyldiamine, triamines.
In one embodiment, the component (ii) is one or more cross-linkers selected from the group consisting of polyethylene imine, polyvinyl amine, fatty amines.
In one embodiment, the component (ii) is a fatty amide.
In one embodiment, the component (ii) is one or more cross-linkers selected from the group consisting of dimethoxyethanal, glycolaldehyde, glyoxalic acid.
In one embodiment, the component (ii) is one or more cross-linkers selected from polyester polyols, such as polycaprolactone.
In one embodiment, the component (ii) is one or more cross-linkers selected from the group consisting of starch, modified starch, CMC.
In one embodiment, the component (ii) is one or more cross-linkers in form of aliphatic multifunctional carbodiimides.
In one embodiment, the component (ii) is one or more cross-linkers selected from melamine based cross-linkers, such as a hexakis(methylmethoxy)melamine (HMMM) based cross-linkers.
Examples of such compounds are Picassian XL 701, 702, 725 (Stahl Polymers), such as ZOLDINE® XL-29SE (Angus Chemical Company), such as CX300 (DSM), such as Carbodilite V-02-L2 (Nisshinbo Chemical Inc.).
In one embodiment, the component (ii) comprises one or more cross-linkers selected from β-hydroxyalkylamide-cross-linkers and/or oxazoline-cross-linkers.
β-hydroxyalkylamide-cross-linkers is a curing agent for the acid-functional macromolecules. It provides a hard, durable, corrosion resistant and solvent resistant cross-linked polymer network. It is believed the β-hydroxyalkylamide cross-linkers cure through esterification reaction to form multiple ester linkages. The hydroxy functionality of the β-hydroxyalkylamide-cross-linkers should be an average of at least 2, preferably greater than 2 and more preferably 2-4 in order to obtain optimum curing response.
Oxazoline group containing cross-linkers are polymers containing one of more oxazoline groups in each molecule and generally, oxazoline containing crosslinkers can easily be obtained by polymerizing an oxazoline derivative. The U.S. Pat. No. 6,818,699 B2 provides a disclosure for such a process.
In one embodiment, the component (ii) is an epoxidised oil based on fatty acid triglyceride.
It is noted that epoxidised oils based on fatty acid triglycerides are not considered hazardous and therefore the use of these compounds in the binder compositions according to the present invention do not render these compositions unsafe to handle.
In one embodiment, the component (ii) is a molecule having 3 or more epoxy groups.
In one embodiment, the component (ii) is one or more flexible oligomer or polymer, such as a low Tg acrylic based polymer, such as a low Tg vinyl based polymer, such as low Tg polyether, which contains reactive functional groups such as carbodiimide groups, such as anhydride groups, such as oxazoline groups, such as amino groups, such as epoxy groups.
In one embodiment, component (ii) is selected from the group consisting of cross-linkers taking part in a curing reaction, such as hydroxyalkylamide, alkanolamine, a reaction product of an alkanolamine and a polycarboxylic acid. The reaction product of an alkanolamine and a polycarboxylic acid can be found in U.S. Pat. No. 6,706,853B1.
In one embodiment, the component (ii) is one or more cross-linkers selected from the group consisting of multifunctional organic amines such as an alkanolamine, diamines, such as hexamethyldiamine, triamines.
Without wanting to be bound by any particular theory, the present inventors believe it is believed that the very advantageous properties of the aqueous binder compositions according to the present invention are due to the interaction of the oxidized lignins used as component (i) and the cross-linkers mentioned above. It is believed that the presence of carboxylic acid groups in the oxidized lignins enable the very effective cross-linking of the oxidized lignins.
In one embodiment, the binder composition according to the present invention comprises component (ii) in an amount of 1 to 40 wt.-%, such as 4 to 20 wt.-%, such as 6 to 12 wt.-%, based on the dry weight of component (i).
It is noted that epoxidised oils based on fatty acid triglycerides are not considered hazardous and therefore the use of these compounds in the binder compositions according to the present invention do not render these compositions unsafe to handle.
In one embodiment, the component (ii) is a molecule having 3 or more epoxy groups.
In one embodiment, the component (ii) is one or more flexible oligomer or polymer, such as a low Tg acrylic based polymer, such as a low Tg vinyl based polymer, such as low Tg polyether, which contains reactive functional groups such as carbodiimide groups, such as anhydride groups, such as oxazoline groups, such as amino groups, such as epoxy groups.
In one embodiment, component (ii) is selected from the group consisting of cross-linkers taking part in a curing reaction, such as hydroxyalkylamide, alkanolamine, a reaction product of an alkanolamine and a polycarboxylic acid. The reaction product of an alkanolamine and a polycarboxylic acid can be found in U.S. Pat. No. 6,706,853B1.
In one embodiment, component (ii) is Primid XL552, which has the following structure:
Component (ii) can also be any mixture of the above-mentioned compounds.
Without wanting to be bound by any particular theory, the present inventors believe it is believed that the very advantageous properties of the aqueous binder compositions according to the present invention are due to the interaction of the oxidized lignins used as component (i) and the cross-linkers mentioned above. It is believed that the presence of carboxylic acid groups in the oxidized lignins enable the very effective cross-linking of the oxidized lignins.
In one embodiment, the binder composition according to the present invention comprises component (ii) in an amount of 1 to 40 wt.-%, such as 4 to 20 wt.-%, such as 6 to 12 wt.-%, based on the dry weight of component (i).
Component (iii)
Component (iii) is in form of one or more plasticizers.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of fatty alcohols, monohydroxy alcohols such as pentanol, stearyl alcohol.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of alkoxylates such as ethoxylates such as butanol ethoxylates, such as butoxytriglycol.
In one embodiment, component (iii) is in form of propylene glycols.
In one embodiment, component (iii) is in form of glycol esters.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of adipates, acetates, benzoates, cyclobenzoates, citrates, stearates, sorbates, sebacates, azelates, butyrates, valerates.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of phenol derivatives such as alkyl or aryl substituted phenols.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of silanols, siloxanes.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of sulfates such as alkyl sulfates, sulfonates such as alkyl aryl sulfonates such as alkyl sulfonates, phosphates such as tripolyphosphates; such as tributylphosphates.
In one embodiment, component (iii) is in form of hydroxy acids.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of monomeric amides such as acetamides, benzamide, fatty acid amides such as tall oil amides.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of quaternary ammonium compounds such as trimethylglycine, distearyldimethylammoniumchloride.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of vegetable oils such as castor oil, palm oil, linseed oil, tall oil, soybean oil.
In one embodiment, component (iii) is in form of tall oil.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of hydrogenated oils, acetylated oils.
In one embodiment, component (iii) is in form of fatty acid methyl esters.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of alkyl polyglucosides, gluconamides, aminoglucoseamides, sucrose esters, sorbitan esters.
In one embodiment, component (iii) comprises one or more plasticizers selected from the group consisting of polyethylene glycols, polyethylene glycol ethers.
In one embodiment, component (iii) comprises one or more plasticisers selected from the group consisting of propylene glycols, phenol derivatives, silanols, siloxanes, hydroxy acids, vegetable oils, polyethylene glycols, polyethylene glycol ethers.
It has surprisingly been found that the inclusion of plasticizers in the aqueous binder compositions according to the present invention strongly improves the mechanical properties of the mineral fibre products according to the present invention.
The term plasticizer refers to a substance that is added to a material in order to make the material softer, more flexible (by decreasing the glass-transition temperature Tg) and easier to process.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of polyethylene glycols, polyethylene glycol ethers, polyethers, hydrogenated sugars, phthalates and/or acids, such as adipic acid, vanillic acid, lactic acid and/or ferullic acid, acrylic polymers, polyvinyl alcohol, polyurethane dispersions, ethylene carbonate, propylene carbonate, lactones, lactams, lactides, acrylic based polymers with free carboxy groups and/or polyurethane dispersions with free carboxy groups.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of polyols, such as carbohydrates, hydrogenated sugars, such as sorbitol, erythriol, glycerol, monoethylene glycol, polyethylene glycols, polyethylene glycol ethers, polyethers, phthalates and/or acids, such as adipic acid, vanillic acid, lactic acid
and/or ferullic acid, acrylic polymers, polyvinyl alcohol, polyurethane dispersions,
ethylene carbonate, propylene carbonate, lactones, lactams, lactides, acrylic based polymers with free carboxy groups and/or polyurethane dispersions with free carboxy groups, polyamides, amides such as carbamide/urea, or any mixtures thereof.
In one embodiment, component (iii) is in form of one or more plasticizers selected from the group consisting of carbonates, such as ethylene carbonate, propylene carbonate, lactones, lactams, lactides, compounds with a structure similar to lignin like vanillin, acetosyringone, solvents used as coalescing agents like alcohol ethers, polyvinyl alcohol.
In one embodiment, component (iii) is in form of one or more non-reactive plasticizer selected from the group consisting of polyethylene glycols, polyethylene glycol ethers, polyethers, hydrogenated sugars, phthalates and/or other esters, solvents used as coalescing agents like alcohol ethers, acrylic polymers, polyvinyl alcohol.
In one embodiment, component (iii) is one or more reactive plasticizers selected from the group consisting of carbonates, such as ethylene carbonate, propylene carbonate, lactones, lactams, lactides, di- or tricarboxylic acids, such as adipic acid, or lactic acid, and/or vanillic acid and/or ferullic acid, polyurethane dispersions, acrylic based polymers with free carboxy groups, compounds with a structure similar to lignin like vanillin, acetosyringone.
Another particular surprising aspect of the present invention is that the use of plasticizers having a boiling point of more than 100° C., in particular 140 to 250° C., strongly improves the mechanical properties of the mineral fibre products according to the present invention although, in view of their boiling point, it is likely that these plasticizers will at least in part evaporate during the curing of the aqueous binders in contact with the mineral fibres.
In one embodiment, component (iii) comprises one or more plasticizers having a boiling point of more than 100° C., such as 110 to 280° C., more preferred 120 to 260° C., more preferred 140 to 250° C.
Without wanting to be bound by any particular theory, the present inventors believe It is believed that the effectiveness of these plasticizers in the aqueous binder composition according to the present invention is associated with the effect of increasing the mobility of the oxidized lignins during the curing process. It is believed that the increased mobility of the lignins or oxidized lignins during the curing process facilitates the effective cross-linking.
In one embodiment, component (iii) comprises one or more polyethylene glycols having an average molecular weight of 150 to 50000 g/mol, in particular 150 to 4000 g/mol, more particular 150 to 1000 g/mol, preferably 150 to 500 g/mol, more preferably 200 to 400 g/mol.
In one embodiment, component (iii) comprises one or more polyethylene glycols having an average molecular weight of 4000 to 25000 g/mol, in particular 4000 to 15000 g/mol, more particular 8000 to 12000 g/mol.
In one embodiment component (iii) is capable of forming covalent bonds with component (i) and/or component (ii) during the curing process. Such a component would not evaporate and remain as part of the composition but will be effectively altered to not introduce unwanted side effects e.g. water absorption in the cured product. Non-limiting examples of such a component are caprolactone and acrylic based polymers with free carboxyl groups.
Component (iii) can also be any mixture of the above-mentioned compounds.
In one embodiment, component (iii) is present in an amount of 0.5 to 50, preferably 2.5 to 25, more preferably 3 to 15 wt.-%, based on the dry weight of component (i).
Aqueous binder composition for mineral fibers comprising components (i) and (iia)
In one embodiment the present invention is directed to an aqueous binder composition for mineral fibers comprising:
The present inventors have found that the excellent binder properties can also be achieved by a two-component system which comprises component (i) in form of one or more oxidized lignins and a component (iia) in form of one or more modifiers, and optionally any of the other components mentioned above and below.
In a preferred embodiment, component (iia) is a modifier in form of one or more compounds selected from the group consisting of epoxidised oils based on fatty acid triglycerides.
In one embodiment, component (iia) is a modifier in form of one or more compounds selected from molecules having 3 or more epoxy groups.
In one embodiment, component (iia) is a modifier in form of one or more flexible oligomer or polymer, such as a low Tg acrylic based polymer, such as a low Tg vinyl based polymer, such as low Tg polyether, which contains reactive functional groups such as carbodiimide groups, such as anhydride groups, such as oxazoline groups, such as amino groups, such as epoxy groups.
In one embodiment, the component (iia) is one or more cross-linkers selected from the group consisting of amines such as monoethanolamine, diethanolamine, triethanolamine, polyethylene imine, polyvinyl amine, fatty amines.
In one embodiment, the component (iia) is a polymeric carbodiimides and/or multifunctional carbodiimide.
Without wanting to be bound by any particular theory, the present inventors believe that the excellent binder properties achieved by the binder composition for mineral fibers comprising components (i) and (iia), and optional further components, are at least partly due to the effect that the modifiers used as components (iia) at least partly serve the function of a plasticizer and a crosslinker.
In one embodiment, the aqueous binder composition comprises component (iia) in an amount of 1 to 40 wt.-%, such as 4 to 20 wt.-%, such as 6 to 12 wt.-%, based on the dry weight of the component (i).
Further Components
In some embodiments, the aqueous binder composition according to the present invention comprises further components.
In one embodiment, the aqueous binder composition according to the present invention comprises a catalyst selected from inorganic acids, such as sulfuric acid, sulfamic acid, nitric acid, boric acid, hypophosphorous acid, and/or phosphoric acid, and/or any salts thereof such as sodium hypophosphite, and/or ammonium salts, such as ammonium salts of sulfuric acid, sulfamic acid, nitric acid, boric acid, hypophosphorous acid, and/or phosphoric acid, and/or sodium polyphosphate (STTP), and/or sodium metaphosphate (STMP), and/or phosphorous oxychloride. The presence of such a catalyst can improve the curing properties of the aqueous binder compositions according to the present invention.
In one embodiment, the aqueous binder composition according to the present invention comprises a catalyst selected from Lewis acids, which can accept an electron pair from a donor compound forming a Lewis adduct, such as ZnCl2, Mg(ClO4)2, Sn[N(SO2-n-C8F17)2]4.
In one embodiment, the aqueous binder composition according to the present invention comprises a catalyst selected from metal chlorides, such as KCl, MgCl2, ZnCl2, FeCl3 and SnCl2.
In one embodiment, the aqueous binder composition according to the present invention comprises a catalyst selected from organometallic compounds, such as titanate-based catalysts and stannum based catalysts.
In one embodiment, the aqueous binder composition according to the present invention comprises a catalyst selected from chelating agents, such as transition metals, such as iron ions, chromium ions, manganese ions, copper ions.
In one embodiment, the aqueous binder composition according to the present invention further comprises a further component (iv) in form of one or more silanes.
In one embodiment, the aqueous binder composition according to the present invention comprises a further component (iv) in form of one or more coupling agents, such as organofunctional silanes.
In one embodiment, component (iv) is selected from group consisting of organofunctional silanes, such as primary or secondary amino functionalized silanes, epoxy functionalized silanes, such as polymeric or oligomeric epoxy functionalized silanes, methacrylate functionalized silanes, alkyl and aryl functionalized silanes, urea functionalised silanes or vinyl functionalized silanes.
In one embodiment, the aqueous binder composition according to the present invention further comprises a component (v) in form of one or more components selected from the group of ammonia, amines or any salts thereof.
The present inventors have It has been found that the inclusion of ammonia, amines or any salts thereof as a further component can in particular be useful when oxidized lignins are used in component (i), which oxidised lignin have not been oxidized in the presence of ammonia.
In one embodiment, the aqueous binder composition according to the present invention further comprises a further component in form of urea, in particular in an amount of 5 to 40 wt.-%, such as 10 to 30 wt.-%, 15 to 25 wt.-%, based on the dry weight of component (i).
In one embodiment, the aqueous binder composition according to the present invention further comprises a further component in form of one or more carbohydrates selected from the group consisting of sucrose, reducing sugars, in particular dextrose, polycarbohydrates, and mixtures thereof, preferably dextrins and maltodextrins, more preferably glucose syrups, and more preferably glucose syrups with a dextrose equivalent value of DE=30 to less than 100, such as
DE=60 to less than 100, such as DE=60-99, such as DE=85-99, such as DE=95-99.
In one embodiment, the aqueous binder composition according to the present invention further comprises a further component in form of one or more carbohydrates selected from the group consisting of sucrose and reducing sugars in an amount of 5 to 50 wt.-%, such as 5 to less than 50 wt.-%, such as 10 to 40 wt.-%, such as 15 to 30 wt.-% based on the dry weight of component (i).
In the context of the present invention, a binder composition having a sugar content of 50 wt.-% or more, based on the total dry weight of the binder components, is considered to be a sugar based binder. In the context of the present invention, a binder composition having a sugar content of less than 50 wt.-%, based on the total dry weight of the binder components, is considered a non-sugar based binder.
In one embodiment, the aqueous adhesive composition according to the present invention further comprises a further component in form of one or more surface active agents that are in the form of non-ionic and/or ionic emulsifiers such as polyoxyethylenes (4) lauryl ether, such as soy lecithin, such as sodium dodecyl sulfate.
In one embodiment, the aqueous binder composition according to the present invention comprises
In one embodiment, the aqueous binder composition according to the present invention comprises
In one embodiment, the aqueous binder composition according to the present invention comprises
In one embodiment, the aqueous binder composition according to the present invention comprises
In one embodiment, the aqueous binder composition according to the present invention consists essentially of
In one embodiment, the aqueous binder composition according to the present invention consists essentially of
A Method for Producing a Mineral Fibre Product
The present invention also provides a method for producing a mineral fibre product by binding mineral fibres with the binder composition.
Accordingly, the present invention is also directed to a method for producing a mineral fibre product which comprises the steps of contacting mineral fibres with a binder composition comprising
Curing
The web is cured by a chemical and/or physical reaction of the binder components.
In one embodiment, the curing takes place in a curing device.
In one embodiment, the curing is carried out at temperatures from 100 to 300° C., such as 170 to 270° C., such as 180 to 250° C., such as 190 to 230° C.
In one embodiment, the curing takes place in a conventional curing oven for mineral wool production operating at a temperature of from 150 to 300° C., such as 170 to 270° C., such as 180 to 250° C., such as 190 to 230° C.
In one embodiment, the curing takes place for a time of 30 seconds to 20 minutes, such as 1 to 15 minutes, such as 2 to 10 minutes.
In a typical embodiment, curing takes place at a temperature of 150 to 250° C. for a time of 30 seconds to 20 minutes.
The curing process may commence immediately after application of the binder to the fibres. The curing is defined as a process whereby the binder composition undergoes a physical and/or chemical reaction which in case of a chemical reaction usually increases the molecular weight of the compounds in the binder composition and thereby increases the viscosity of the binder composition, usually until the binder composition reaches a solid state.
In a one embodiment, the curing of the binder in contact with the mineral fibres takes place in a heat press.
The curing of a binder in contact with the mineral fibres in a heat press has the particular advantage that it enables the production of high-density products.
In one embodiment the curing process comprises drying by pressure. The pressure may be applied by blowing air or gas through/over the mixture of mineral fibres and binder.
Mineral Fibre Product According to the Present Invention
The present invention is also directed to a mineral fibre product comprising mineral fibres in contact with a cured binder composition as described above, i.e. in contact with a cured binder resulting from the curing of the aqueous binder composition described above.
The mineral fibres employed may be any of man-made vitreous fibres (MMVF), glass fibres, ceramic fibres, basalt fibres, slag fibres, rock fibres, stone fibres and others. These fibres may be present as a wool product, e.g. like a stone wool product.
Fibre/Melt Composition
The man-made vitreous fibres (MMVF) can have any suitable oxide composition. The fibres can be glass fibres, ceramic fibres, basalt fibres, slag fibres or rock or stone fibres. The fibres are preferably of the types generally known as rock, stone or slag fibres, most preferably stone fibres.
Stone fibres commonly comprise the following oxides, in percent by weight:
SiO2: 30 to 51
CaO: 8 to 30
MgO: 2 to 25
FeO (including Fe2O3): 2 to 15
Na2O+K2O: not more than 10
CaO+MgO: 10 to 30
In preferred embodiments the MMVF have the following levels of elements, calculated as oxides in wt %:
SiO2: at least 30, 32, 35 or 37; not more than 51, 48, 45 or 43
Al2O3: at least 12, 16 or 17; not more than 30, 27 or 25
CaO: at least 8 or 10; not more than 30, 25 or 20
MgO: at least 2 or 5; not more than 25, 20 or 15
FeO (including Fe2O3): at least 4 or 5; not more than 15, 12 or 10
FeO+MgO: at least 10, 12 or 15; not more than 30, 25 or 20
Na2O+K2O: zero or at least 1; not more than 10
CaO+MgO: at least 10 or 15; not more than 30 or 25
TiO2: zero or at least 1; not more than 6, 4 or 2
TiO2+FeO: at least 4 or 6; not more than 18 or 12
B2O3: zero or at least 1; not more than 5 or 3
P2O5: zero or at least 1; not more than 8 or 5
Others: zero or at least 1; not more than 8 or 5
The MMVF made by the method of the invention preferably have the composition in wt %:
Another preferred composition for the MMVF is as follows in wt %:
SiO2 39-55% preferably 39-52%
Al2O3 16-27% preferably 16-26%
CaO 6-20% preferably 8-18%
MgO 1-5% preferably 1-4.9%
Na2O 0-15% preferably 2-12%
K2O 0-15% preferably 2-12%
R2O (Na2O+K2O) 10-14.7% preferably 10-13.5%
P2O5 0-3% preferably 0-2%
Fe2O3 (iron total) 3-15% preferably 3.2-8%
B2O3 0-2% preferably 0-1%
TiO2 0-2% preferably 0.4-1%
Others 0-2.0%
Glass fibres commonly comprise the following oxides, in percent by weight:
SiO2: 50 to 70
Al2O3: 10 to 30
CaO: not more than 27
MgO: not more than 12
Glass fibres can also contain the following oxides, in percent by weight: Na2O+K2O: 8 to 18, in particular Na2O+K2O greater than CaO+MgO B2O3: 3 to 12
Some glass fibre compositions can contain Al2O3: less than 2%.
Suitable fibre formation methods and subsequent production steps for manufacturing the mineral fibre product are those conventional in the art. Generally, the binder is sprayed immediately after fibrillation of the mineral melt on to the air-borne mineral fibres. The aqueous binder composition is normally applied in an amount of 0.1 to 18%, preferably 0.2 to 8% by weight, of the bonded mineral fibre product on a dry basis.
The spray-coated mineral fibre web is generally cured in a curing oven by means of a hot air stream. The hot air stream may be introduced into the mineral fibre web from below, or above or from alternating directions in distinctive zones in the length direction of the curing oven.
Typically, the curing oven is operated at a temperature of from about 150° C. to about 300° C., such as 170 to 270° C., such as 180 to 250° C., such as 190 to 230° C. Generally, the curing oven residence time is from 30 seconds to 20 minutes, such as 1 to 15 minutes, such as 2 to 10 minutes, depending on, for instance, the product density.
In a typical embodiment, the mineral fibre product according to the present invention is cured at a temperature of 150° C. to 250° C. for a time of 30 seconds to 20 minutes.
If desired, the mineral wool web may be subjected to a shaping process before curing. The bonded mineral fibre product emerging from the curing oven may be cut to a desired format e.g., in the form of a batt. Thus, the mineral fibre products produced, for instance, have the form of woven and nonwoven fabrics, mats, batts, slabs, sheets, plates, strips, rolls, granulates and other shaped articles which find use, for example, as thermal or acoustical insulation materials, vibration damping, construction materials, facade insulation, reinforcing materials for roofing or flooring applications, as filter stock and in other applications.
In accordance with the present invention, it is also possible to produce composite materials by combining the bonded mineral fibre product with suitable composite layers or laminate layers such as, e.g., metal, glass surfacing mats and other woven or non-woven materials.
The mineral fibre products according to the present invention generally have a density within the range of from 6 to 250 kg/m3, preferably 20 to 200 kg/m3. The mineral fibre products generally have a loss on ignition (LOI) within the range of 0.3 to 18.0%, preferably 0.5 to 8.0%.
Although the aqueous binder composition according to the present invention is particularly useful for bonding mineral fibres, it may equally be employed in other applications typical for binders and sizing agents, e.g. as a binder for foundry sand, glass fibre tissue, composites, moulded articles, coatings, such as metal adhesives.
Oxidized lignins which can be used as component (i) in the aqueous binder composition for mineral fibres according to the present invention and method for preparing such oxidised lignins
In the following, we describe oxidised lignins which can be used as component of the binder composition and their preparation.
Method I to Prepare Oxidised Lignins
Oxidised lignins, which can be used as component for the binders used in the present invention can be prepared by a method comprising bringing into contact
Component (a)
Component (a) comprises one or more lignins.
In one embodiment of the method according to the present invention, component (a) comprises one or more kraft lignins, one or more soda lignins, one or more lignosulfonate lignins, one or more organosolv lignins, one or more lignins from biorefining processes of lignocellulosic feedstocks, or any mixture thereof.
In one embodiment, component (a) comprises one or more kraft lignins.
Component (b)
In one embodiment according to the present invention, component (b) comprises ammonia, one or more amino components, and/or any salts thereof. Without wanting to be bound by any particular theory, the present inventors believe that replacement of the alkali hydroxides used in previously known oxidation processes of lignin by ammonia, one or more amino components, and/or any salts thereof, plays an important role in the improved properties of the oxidised lignins prepared according to the method of the present invention.
The present inventors have surprisingly found that the lignins oxidised by an oxidation agent in the presence of ammonia or amines contain significant amounts of nitrogen as a part of the structure of the oxidised lignins. Without wanting to be bound to any particular theory, the present inventors believe that the improved fire resistance properties of the oxidised lignins when used in products where they are comprised in a binder composition, said oxidised lignins prepared by the method according to the present invention, are at least partly due to the nitrogen content of the structure of the oxidised lignins.
In one embodiment, component (b) comprises ammonia and/or any salt thereof.
Without wanting to be bound by any particular theory, the present inventors believe that the improved stability properties of the derivatized lignins prepared according to the present invention are at least partly due to the fact that ammonia is a volatile compound and therefore evaporates from the final product or can be easily removed and reused. In contrast to that, it has proven difficult to remove residual amounts of the alkali hydroxides used in the previously known oxidation process.
Nevertheless, it can be advantageous in the method according to the present invention that component (b), besides ammonia, one or more amino components, and/or any salts thereof, also comprises a comparably small amount of an alkali and/or earth alkali metal hydroxide, such as sodium hydroxide and/or potassium hydroxide.
In the embodiments, in which component (b) comprises alkali and/or earth alkali metal hydroxides, such as sodium hydroxide and/or potassium hydroxide, as a component in addition to the ammonia, one or more amino components, and/or any salts thereof, the amount of the alkali and/or earth alkali metal hydroxides is usually small, such as 5 to 70 weight parts, such as 10 to 20 weight parts alkali and/or earth alkali metal hydroxide, based on ammonia.
Component (c)
In the method according to the present invention, component (c) comprises one or more oxidation agents.
In one embodiment, component (c) comprises one or more oxidation agents in form of hydrogen peroxide, organic or inorganic peroxides, molecular oxygen, ozone, air, halogen containing oxidation agents, or any mixture thereof.
In the initial steps of the oxidation, active radicals from the oxidant will typically abstract the proton from the phenolic group as that bond has the lowest dissociation energy in lignin. Due to lignin's potential to stabilize radicals through mesomerism multiple pathways open up to continue (but also terminate) the reaction and various intermediate and final products are obtained. The average molecular weight can both increase and decrease due to this complexity (and chosen conditions) and in their experiments, the inventors have typically seen moderate increase of average molecular weight of around 30%.
In one embodiment, component (c) comprises hydrogen peroxide.
Hydrogen peroxide is perhaps the most commonly employed oxidant due to combination of low price, good efficiency and relatively low environmental impact. When hydrogen peroxide is used without the presence of catalysts, alkaline conditions and temperature are important due to the following reactions leading to radical formation:
H2O2+OH−⇄HOO−+H2O
H2O2+OOH−⇄·OH+H2O+·O2−
The present inventors have found that the derivatized lignins prepared with the method according to the present invention contain increased amounts of carboxylic acid groups as a result of the oxidation process. Without wanting to be bound by any particular theory, the present inventors believe that the carboxylic acid group content of the oxidised lignins prepared in the process according to the present invention plays an important role in the desirable reactivity properties of the derivatized lignins prepared by the method according to the present invention.
Another advantage of the oxidation process is that the oxidised lignin is more hydrophilic. Higher hydrophilicity can enhance solubility in water and facilitate the adhesion to polar substrates such as mineral fibers.
Further Components
In one embodiment, the method according to the present invention comprises further components, in particular a component (d) in form of an oxidation catalyst, such as one or more transition metal catalyst, such as iron sulfate, such as manganese, palladium, selenium, tungsten containing catalysts.
Such oxidation catalysts can increase the rate of the reaction, thereby improving the properties of the oxidised lignins prepared by the method according to the present invention.
Mass Ratios of the Components
The person skilled in the art will use the components (a), (b) and (c) in relative amounts that the desired degree of oxidation of the lignins is achieved.
In one embodiment,
wherein the mass ratios of lignin, ammonia and hydrogen peroxide are such that the amount of ammonia is 0.01 to 0.5 weight parts, such as 0.1 to 0.3, such as 0.15 to 0.25 weight parts ammonia, based on the dry weight of lignin, and wherein the amount of hydrogen peroxide is 0.025 to 1.0 weight parts, such as 0.05 to 0.2 weight parts, such as 0.075 to 0.125 weight parts hydrogen peroxide, based on the dry weight of lignin.
Process
There is more than one possibility to bring the components (a), (b) and (c) in contact to achieve the desired oxidation reaction.
In one embodiment, the method comprises the steps of:
In one embodiment, the pH adjusting step is carried so that the resulting aqueous solution and/or dispersion is having a pH≥9, such as ≥10, such as ≥10.5.
In one embodiment, the pH adjusting step is carried out so that the resulting aqueous solution and/or dispersion is having a pH in the range of 10.5 to 12.
In one embodiment, the pH adjusting step is carried out so that the temperature is allowed to raise to ≥25° C. and then controlled in the range of 25-50° C., such as 30-45° C., such as 35-40° C.
In one embodiment, during the oxidation step, the temperature is allowed to raise ≥35° C. and is then controlled in the range of 35-150° C., such as 40-90° C., such as 45-80° C.
In one embodiment, the oxidation step is carried out for a time of 1 second to 48 hours, such as 10 seconds to 36 hours, such as 1 minute to 24 hours such as 2-5 hours.
Method II to Prepare Oxidised Lignins
Oxidised lignins, which can be used as component for the binders used in the present invention can be prepared by a method comprising bringing into contact
Component (a)
Component (a) comprises one or more lignins.
In one embodiment of the method according to the present invention, component (a) comprises one or more kraft lignins, one or more soda lignins, one or more lignosulfonate lignins, one or more organosolv lignins, one or more lignins from biorefining processes of lignocellulosic feedstocks, or any mixture thereof.
In one embodiment, component (a) comprises one or more kraft lignins.
Component (b)
In one embodiment according to the present invention, component (b) comprises ammonia, one or more amino components, and/or any salts thereof and/or an alkali and/or earth alkali metal hydroxide, such as sodium hydroxide and/or potassium hydroxide.
“Ammonia-oxidized lignins” is to be understood as a lignin that has been oxidized by an oxidation agent in the presence of ammonia. The term “ammonia-oxidized lignin” is abbreviated as AOL.
In one embodiment, component (b) comprises ammonia and/or any salt thereof.
Without wanting to be bound by any particular theory, the present inventors believe that the improved stability properties of the derivatized lignins prepared according to the present invention with component (b) being ammonia and/or any salt thereof are at least partly due to the fact that ammonia is a volatile compound and therefore evaporates from the final product or can be easily removed and reused.
Nevertheless, it can be advantageous in this embodiment of the method according to the present invention that component (b), besides ammonia, one or more amino components, and/or any salts thereof, also comprises a comparably small amount of an alkali and/or earth alkali metal hydroxide, such as sodium hydroxide and/or potassium hydroxide.
In the embodiments, in which component (b) comprises alkali and/or earth alkali metal hydroxides, such as sodium hydroxide and/or potassium hydroxide, as a component in addition to the ammonia, one or more amino components, and/or any salts thereof, the amount of the alkali and/or earth alkali metal hydroxides is usually small, such as 5 to 70 weight parts, such as 10 to 20 weight parts alkali and/or earth alkali metal hydroxide, based on ammonia.
Component (c)
In the method according to the present invention, component (c) comprises one or more oxidation agents.
In one embodiment, component (c) comprises one or more oxidation agents in form of hydrogen peroxide, organic or inorganic peroxides, molecular oxygen, ozone, air, halogen containing oxidation agents, or any mixture thereof.
In the initial steps of the oxidation, active radicals from the oxidant will typically abstract the proton from the phenolic group as that bond has the lowest dissociation energy in lignin. Due to lignin's potential to stabilize radicals through mesomerism, multiple pathways open up to continue (but also terminate) the reaction and various intermediate and final products are obtained. The average molecular weight can both increase and decrease due to this complexity (and chosen conditions) and in their experiments, the inventors have typically seen moderate increase of average molecular weight of around 30%.
In one embodiment, component (c) comprises hydrogen peroxide.
Hydrogen peroxide is perhaps the most commonly employed oxidant due to combination of low price, good efficiency and relatively low environmental impact. When hydrogen peroxide is used without the presence of catalysts, alkaline conditions and temperature are important due to the following reactions leading to radical formation:
H2O2+OH−⇄HOO−+H2O
H2O2+OOH−⇄·OH+H2O+·O2−
The present inventors have found that the derivatized lignins prepared with the method according to the present invention contain increased amounts of carboxylic acid groups as a result of the oxidation process. Without wanting to be bound by any particular theory, the present inventors believe that the carboxylic acid group content of the oxidized lignins prepared in the process according to the present invention plays an important role in the desirable reactivity properties of the derivatized lignins prepared by the method according to the present invention.
Another advantage of the oxidation process is that the oxidized lignin is more hydrophilic. Higher hydrophilicity can enhance solubility in water and facilitate the adhesion to polar substrates such as mineral fibres.
Component (d)
Component (d) comprises one or more plasticizers.
In one embodiment according to the present invention, component (d) comprises one or more plasticizers in form of polyols, such as carbohydrates, hydrogenated sugars, such as sorbitol, erythriol, glycerol, monoethylene glycol, polyethylene glycols, polyethylene glycol ethers, polyethers, phthalates and/or acids, such as adipic acid, vanillic acid, lactic acid and/or ferullic acid, acrylic polymers, polyvinyl alcohol, polyurethane dispersions, ethylene carbonate, propylene carbonate, lactones, lactams, lactides, acrylic based polymers with free carboxy groups and/or polyurethane dispersions with free carboxy groups, polyamides, amides such as carbamide/urea, or any mixtures thereof.
The present inventors have found that the inclusion of component (d) in form of one or more plasticizers provides a decrease of the viscosity of the reaction mixture which allows a very efficient method to produce oxidised lignins.
In one embodiment according to the present invention, component (d) comprises one or more plasticizers in form of polyols, such as carbohydrates, hydrogenated sugars, such as sorbitol, erythriol, glycerol, monoethylene glycol, polyethylene glycols, polyvinyl alcohol, acrylic based polymers with free carboxy groups and/or polyurethane dispersions with free carboxy groups, polyamides, amides such as carbamide/urea, or any mixtures thereof.
In one embodiment according to the present invention, component (d) comprises one or more plasticizers selected from the group of polyethylene glycols, polyvinyl alcohol, urea or any mixtures thereof.
Further Components
In one embodiment, the method according to the present invention comprises further components, in particular a component (v) in form of an oxidation catalyst, such as one or more transition metal catalyst, such as iron sulfate, such as manganese, palladium, selenium, tungsten containing catalysts.
Such oxidation catalysts can increase the rate of the reaction, thereby improving the properties of the oxidized lignins prepared by the method.
Mass Ratios of the Components
The person skilled in the art will use the components (a), (b), (c), and (d) in relative amounts that the desired degree of oxidation of the lignins is achieved.
In one embodiment, the method according to the present invention is carried out such that the method comprises
For the purpose of the present invention, the “dry weight of lignin” is preferably defined as the weight of the lignin in the supplied form.
Process
There is more than one possibility to bring the components (a), (b), (c), and (d) in contact to achieve the desired oxidation reaction.
In one embodiment, the method comprises the steps of:
In one embodiment, the pH adjusting step is carried so that the resulting aqueous solution and/or dispersion is having a pH≥9, such as ≥10, such as ≥10.5.
In one embodiment, the pH adjusting step is carried out so that the resulting aqueous solution and/or dispersion is having a pH in the range of 9.5 to 12.
In one embodiment, the pH adjusting step is carried out so that the temperature is allowed to raise to ≥25° C. and then controlled in the range of 25-50° C., such as 30-45° C., such as 35-40° C.
In one embodiment, during the oxidation step, the temperature is allowed to raise to ≥35° C. and is then controlled in the range of 35-150° C., such as 40-90° C., such as 45-80° C.
In one embodiment, the oxidation step is carried out for a time of 1 seconds to 24 hours, such as 1 minutes to 12 hours, such as 10 minutes to 8 hours, such as 5 minutes to 1 hour.
The present inventors have found that the process according to the present invention allows to produce a high dry matter content of the reaction mixture and therefore a high throughput is possible in the process according to the present invention which allows the reaction product in form of the oxidised lignins to be used as a component in industrial mass production products such as mineral fibre products.
In one embodiment, the method according to the present invention is carried out such that the dry matter content of the reaction mixture is 20 to 80 wt. %, such as 40 to 70 wt. %.
In one embodiment, the method according to the present invention is carried out such that the viscosity of the oxidised lignin has a value of 100 cP to 100.000 cP, such as a value of 500 cP to 50.000 cP, such as a value of 1.000 cP to 25.000 cP.
For the purpose of the present invention, viscosity is dynamic viscosity and is defined as the resistance of the liquid/paste to a change in shape, or movement of neighbouring portions relative to one another. The viscosity is measured in centipoise (cP), which is the equivalent of 1 mPa s (milipascal second). Viscosity is measured at 20° C. using a viscometer. For the purpose of the present invention, the dynamic viscosity can be measured at 20° C. by a Cone Plate Wells Brookfield Viscometer.
In one embodiment, the method according to the present invention is carried out such that the method comprises a rotator-stator device.
In one embodiment, the method according to the present invention is carried out such that the method is performed as a continuous or semi-continuous process.
Apparatus for Performing the Method
The present invention is also directed to an apparatus for performing the method described above.
In one embodiment, the apparatus for performing the method comprises:
In one embodiment, the apparatus is constructed in such a way that the inlets for the premix of the components (a), (b) and (d) are to the rotor-stator device and the apparatus furthermore comprises a chamber, said chamber having an inlet for component (c) and said chamber having an outlet for an oxidised lignin.
A rotator-stator device is a device for processing materials comprising a stator configured as an inner cone provided with gear rings. The stator cooperates with a rotor having arms projecting from a hub. Each of these arms bears teeth meshing with the teeth of the gear rings of the stator. With each turn of the rotor, the material to be processed is transported farther outward by one stage, while being subjected to an intensive shear effect, mixing and redistribution. The rotor arm and the subjacent container chamber of the upright device allow for a permanent rearrangement of the material from the inside to the outside and provide for a multiple processing of dry and/or highly viscous matter so that the device is of excellent utility for the intensive mixing, kneading, fibrillating, disintegrating and similar processes important in industrial production. The upright arrangement of the housing facilitates the material's falling back from the periphery toward the center of the device.
In one embodiment, the rotator-stator device used in the method according to the present invention comprises a stator with gear rings and a rotor with teeth meshing with the teeth of the stator. In this embodiment, the rotator-stator device has the following features: Between arms of the rotor protrudes a guiding funnel that concentrates the material flow coming in from above to the central area of the container. The outer surface of the guiding funnel defines an annular gap throttling the material flow. At the rotor, a feed screw is provided that feeds towards the working region of the device. The guiding funnel retains the product in the active region of the device and the feed screw generates an increased material pressure in the center.
For more details of the rotator-stator device to be used in one embodiment of the method, reference is made to US 2003/0042344 A1, which is incorporated by reference.
In one embodiment, the method is carried out such that the method uses one rotator-stator device. In this embodiment, the mixing of the components and the reaction of the components is carried out in the same rotator-stator device.
In one embodiment, the method is carried out such that the method uses two or more rotator-stator devices, wherein at least one rotator-stator device is used for the mixing of the components and at least one rotator-stator device is used for reacting the components.
This process can be divided into two steps:
Typically, two different types of rotor-/stator machines are used:
In the open rotor-/stator system the highly concentrated (45 to 50 wt-%) mass of Lignin/water is prepared. The lignin powder is added slowly to the warm water (30 to 60 deg. C.) in which the correct amount of watery ammonia and/or alkali base have been added. This can be done in batch mode, or the materials are added intermittently/continuously creating a continuous flow of mass to the next step.
The created mass should be kept at a temperature of about 60 deg. to keep the viscosity as low as possible and hence the material pumpable. The hot mass of lignin/water at a pH of 9 to 12 is then transferred using a suitable pump, e.g. progressive cavity pump or another volumetric pump, to the oxidation step.
In on embodiment the oxidation is done in a closed rotor-/stator system in a continuous inline reaction. A watery solution of ammonia and/or alkali base is dosed with a dosing pump into the rotor-/stator chamber at the point of highest turbulence/shear. This ensures a rapid oxidation reaction. The oxidized material (AOL) leaves the inline-reactor and is collected in suitable tanks.
Reaction Product
The present inventors have surprisingly found, that the oxidized lignins prepared have very desirable reactivity properties and at the same time display improved fire resistance properties when used in products where they are comprised in a binder composition, and improved long term stability over previously known oxidized lignins.
The oxidised lignin also displays improved hydrophilicity.
An important parameter for the reactivity of the oxidized lignins prepared is the carboxylic acid group content of the oxidized lignins.
In one embodiment, the oxidized lignin prepared has a carboxylic acid group content of 0.05 to 10 mmol/g, such as 0.1 to 5 mmol/g, such as 0.20 to 2.0 mmol/g, such as 0.40 to 1.5 mmol/g, such as 0.45 to 1.0 mmol/g, based on the dry weight of component (a).
Another way to describe the carboxylic acid group content is by using average carboxylic acid group content per lignin macromolecule according to the following formula:
In one embodiment, the oxidized lignin prepared has an average carboxylic acid group content of more than 1.5 groups per macromolecule of component (a), such as more than 2 groups, such as more than 2.5 groups.
Method III to Prepare Oxidised Lignins
Oxidised lignins, which can be used as a component for the binder used in the present invention can be prepared by a method comprising bringing into contact
and allowing a mixing/oxidation step, wherein an oxidised mixture is produced, followed by an oxidation step, wherein the oxidised mixture is allowed to continue to react for a dwell time of dwell time of 1 second to 10 hours, such as 10 seconds to 6 hours, such as 30 seconds to 2 hours.
Components (a), (b), (c) and (d) are as defined above under Method II to prepare oxidised lignins.
In one embodiment of the invention, the process comprises a premixing step in which components are brought into contact with each other.
In the premixing step the following components can be brought into contact with each other:
In an embodiment of the invention, it is possible that the premixing step is carried out as a separate step and the mixing/oxidation step is carried out subsequently to the premixing step. In such an embodiment of the invention it is particularly advantageous to bring component (a) and component (b) and optionally component (d) into contact with each other in a premixing step. In a subsequent mixing/oxidation step, component (c) is then added to the premixture produced in the premixing step.
In another example of the invention, it is possible that the premixing step corresponds to the mixing/oxidation step. In this embodiment of the invention, the components, for example component (a), component (b) and component (c) are mixed and an oxidation process is started at the same time. It is possible that the subsequent dwell time is performed in the same device as that used to perform the mixing/oxidation step. Such an implementation of the invention is particularly advantageous if component (c) is air.
The present inventors have found out that by allowing a mixing/oxidation step followed by an oxidation step, in which the reaction mixture is preferably not continued to be mixed, the oxidation rate can be controlled in a very efficient manner. At the same time, the costs for performing the method are reduced because the oxidation step subsequent to the mixing/oxidation step requires less complex equipment.
Another advantage is that oxidized lignin, which is produced is particularly stable. Another surprising advantage is that the oxidized lignin produced is very well adjustable in terms of viscosity. Another surprising advantage is that the concentration of the oxidized lignin can be very high.
In one embodiment, the dwell time is so chosen that the oxidation reaction is brought to the desired degree of completion, preferably to full completion.
System I for Performing the Method III
In one embodiment, the system for performing the method comprises:
In one embodiment, the system comprises one or more inlets for component (c) and/or component (d).
In one embodiment, the system comprises a premixing device.
The premixing device can comprise one or more inlets for water and/or component (a) and/or component (b) and/or component (c) and/or component (d).
In one embodiment of the invention, the premixing device comprises inlets for water and component (a) and component (b).
It is possible that, in a premixing step, component (c) is also mixed with the three mentioned ingredients (water, component (a) and component (b)). It is then possible that the premixing device has a further inlet for component (c). If component (c) is air, it is possible that the premixing device is formed by an open mixing vessel, so that in this case component (c) is already brought into contact with the other components (water, component (a) and component (b)) through the opening of the vessel. Also in this embodiment of the invention, it is possible that the premixing device optionally comprises an inlet for component (d).
In one embodiment, the system is constructed in such a way that the inlets for components (a), (b) and (d) are inlets of a premixing device, in particular of an open rotor-stator device, whereby the system furthermore comprises an additional rotor-stator device, said additional rotor-stator device having an inlet for component (c) and said additional rotor-stator device having an outlet for an oxidized lignin.
It is possible that the premixing step and the mixing/oxidizing step are carried out simultaneously. In this case, the premixing device and the mixing/oxidizing device are a single device, i. e. a rotor-stator device.
In one embodiment, one rotator-stator device used in the method according to the present invention comprises a stator with gear rings and a rotor with teeth meshing with the teeth of the stator. In this embodiment, the rotator-stator device has the following features: Between arms of the rotor protrudes a guiding funnel that concentrates the material flow coming in from above to the central area of the container. The outer surface of the guiding funnel defines an annular gap throttling the material flow. At the rotor, a feed screw is provided that feeds towards the working region of the device. The guiding funnel retains the product in the active region of the device and the feed screw generates an increased material pressure in the center.
System II for Performing the Method III
In one embodiment, the system for performing the method comprises:
In one embodiment, the system comprises additional one or more inlets for component (c) and/or component (d).
In one embodiment, the system comprises a premixing device.
The premixing device can comprise one or more inlets for water and/or component (a) and/or component (b) and/or component (c) and/or component (d).
In one embodiment, the premixing device comprises inlets for water and component (a) and component (b).
It is possible that, in a premixing step, component (c) is also mixed with the three mentioned ingredients (water, component (a) and component (b)). It is then possible that the premixing device has a further inlet for component (c). If component (c) is air, it is possible that the premixing device is formed by an open mixing vessel, so that in this case component (c) is already brought into contact with the other components (water, component (a) and component (b)) through the opening of the vessel. Also in this embodiment of the invention, it is possible that the premixing device optionally comprises an inlet for component (d).
In one embodiment, the system is constructed in such a way that the inlets for components (a), (b) and (d) are inlets of an open rotor-stator device, whereby the system furthermore comprises a mixer/heat-exchanger, having an inlet for component (c) and an outlet for an oxidized lignin.
It is possible that the premixing step and the mixing/oxidizing step are carried out simultaneously. In this case, the premixing device and the mixing/oxidizing device are a single device.
In one embodiment, one rotator-stator device used in the method according to the present invention comprises a stator with gear rings and a rotor with teeth meshing with the teeth of the stator. In this embodiment, the rotator-stator device has the following features: Between arms of the rotor protrudes a guiding funnel that concentrates the material flow coming in from above to the central area of the container. The outer surface of the guiding funnel defines an annular gap throttling the material flow. At the rotor, a feed screw is provided that feeds towards the working region of the device. The guiding funnel retains the product in the active region of the device and the feed screw generates an increased material pressure in the center.
Of course other devices can also be used as premixing devices. Furthermore, it is possible that the premixing step is carried out in the mixing and oxidizing apparatus.
In one embodiment, the mixing and oxidizing apparatus is a static mixer. A static mixer is a device for the continuous mixing of fluid materials, without moving components. One design of static mixer is the plate-type mixer and another common device type consists of mixer elements contained in a cylindrical (tube) or squared housing.
In one embodiment, the mixer/heat-exchanger is constructed as multitube heat exchanger with mixing elements. The mixing element are preferably fixed installations through which the mixture has to flow, whereby mixing is carried out as a result of the flowing through. The mixer/heat-exchanger can be constructed as a plug flow reactor.
The amounts of ingredients used according to the example IA are provided in table IA 1.1 and IA 1.2.
Although kraft lignin is soluble in water at relatively high pH, it is known that at certain weight percentage the viscosity of the solution will strongly increase. It is typically believed that the reason for the viscosity increase lies in a combination of strong hydrogen bonding and interactions of n-electrons of numerous aromatic rings present in lignin. For kraft lignin an abrupt increase in viscosity around 21-22 wt.-% in water was observed and 19 wt.-% of kraft lignin were used in the example presented.
Ammonia aqueous solution was used as base in the pH adjusting step. The amount was fixed at 4 wt.-% based on the total reaction weight. The pH after the pH adjusting step and at the beginning of oxidation was 10.7.
Table IA2 shows the results of CHNS elemental analysis before and after oxidation of kraft lignin. Before the analysis, the samples were heat treated at 160° C. to remove adsorbed ammonia. The analysis showed that a certain amount of nitrogen became a part of the structure of the oxidised lignin during the oxidation process.
During testing in batch experiments, it was determined that it is beneficial for the oxidation to add the entire amount of hydrogen peroxide during small time interval contrary to adding the peroxide in small portions over prolonged time period. In the present example 2.0 wt.-% of H2O2 based on the total reaction weight was used.
The oxidation is an exothermic reaction and increase in temperature is noted upon addition of peroxide. In this example, temperature was kept at 60° C. during three hours of reaction.
After the oxidation, the amount of lignin functional groups per gram of sample increased as determined by 31P NMR and aqueous titration. Sample preparation for 31P NMR was performed by using 2-chloro-4,4,5,5-tetramethyl-1,3,2-dioxaphospholane (TMDP) as phosphitylation reagent and cholesterol as internal standard. NMR spectra of kraft lignin before and after oxidation were made and the results are summarized in table IA3.
The change in COOH groups was determined by aqueous titration and utilization of the following formula:
Where V2s and V1s are endpoint volumes of a sample while V2b and V1b are the volume for the blank. Cacid is 0.1M HCl in this case and ms is the weight of the sample. The values obtained from aqueous titration before and after oxidation are shown in table IA4.
The average COOH functionality can also be quantified by a saponification value which represents the number of mg of KOH required to saponify 1 g lignin. Such a method can be found in AOCS Official Method Cd 3-25.
Average molecular weight was also determined before and after oxidation with a PSS PolarSil column (9:1 (v/v) dimethyl sulphoxide/water eluent with 0.05 M LiBr) and UV detector at 280 nm. Combination of COOH concentration and average molecular weight also allowed calculating average carboxylic acid group content per lignin macromolecule and these results are shown in table IA5.
Lignin oxidation with hydrogen peroxide is an exothermic process and even in lab-scale significant temperature increases were seen upon addition of peroxide. This is a natural concern when scaling up chemical processes since the amount of heat produced is related to dimensions in the 3rd power (volume) whereas cooling normally only increase with dimension squared (area). In addition, due to the high viscosity of the adhesive intermediates process equipment has to be carefully selected or designed. Thus, the scale up was carefully engineered and performed in several steps.
The first scale up step was done from 1 L (lab scale) to 9 L using a professional mixer in stainless steel with very efficient mechanical mixing The scale-up resulted only in a slightly higher end temperature than obtained in lab scale, which was attributed to efficient air cooling of the reactor and slow addition of hydrogen peroxide
The next scale up step was done in a closed 200 L reactor with efficient water jacket and an efficient propeller stirrer. The scale was this time 180 L and hydrogen peroxide was added in two steps with appr. 30 minute separation. This up-scaling went relatively well, though quite some foaming was an issue partly due to the high degree reactor filling. To control the foaming a small amount of food grade defoamer was sprayed on to the foam. Most importantly the temperature controllable and end temperatures below 70° C. were obtained using external water-cooling.
The pilot scale reactions were performed in an 800 L reactor with a water cooling jacket and a twin blade propeller stirring. 158 kg of lignin (UPM LignoBoost™ BioPiva 100) with a dry-matter content of 67 wt.-% was de-lumped and suspended in 224 kg of water and stirred to form a homogenous suspension. With continued stirring 103 kg of 25% ammonia in water was pumped into the reactor and stirred another 2 hours to from a dark viscous solution of lignin.
To the stirred lignin solution 140 kg of 7.5 wt.-% at 20-25° C. hydrogen peroxide was added over 15 minutes. Temperature and foam level was carefully monitored during and after the addition of hydrogen peroxide and cooling water was added to the cooling jacket in order to maintain an acceptable foam level and a temperature rise less than 4° C. per minute as well as a final temperature below 70° C. After the temperature increase had stopped, cooling was turned off and the product mixture was stirred for another 2 hours before transferring to transport container.
Based on the scale up runs it could be concluded that even though the reactions are exothermic a large part of the reaction heat is actually balanced out by the heat capacity of the water going from room temperature to about 60° C., and only the last part has to be removed by cooling. It should be noted that due to this and due to the short reaction time this process would be ideal for a scale up and process intensification using continuous reactors such as in-line mixers, tubular reactors or CSTR type reactors. This would ensure good temperature control and a more well-defined reaction process.
Tests of the scale up batches indicated the produced oxidised lignin had properties in accordance to the batches produced in the lab.
In the following examples, several oxidised lignins were prepared.
The following properties were determined for the oxidised lignins:
Component Solids Content:
The content of each of the components in a given oxidised lignin solution is based on the anhydrous mass of the components or as stated below.
Kraft lignin was supplier by UPM as BioPiva100™ as dry powder. NH4OH 25% was supplied by Sigma-Aldrich and used in supplied form. H2O2, 30% (Cas no 7722-84-1) was supplied by Sigma-Aldrich and used in supplied form or by dilution with water. PEG 200 was supplied by Sigma-Aldrich and were assumed anhydrous for simplicity and used as such. PVA (Mw 89.000-98.000, Mw 85.000-124.000, Mw 130.000, Mw 146.000-186.000) (Cas no 9002-89-5) were supplied by Sigma-Aldrich and were assumed anhydrous for simplicity and used as such. Urea (Cas no 57-13-6) was supplied by Sigma-Aldrich and used in supplied form or diluted with water. Glycerol (Cas no 56-81-5) was supplied by Sigma-Aldrich and was assumed anhydrous for simplicity and used as such.
Oxidised Lignin Solids
The content of the oxidised lignin after heating to 200° C. for 1 h is termed “Dry solid matter” and stated as a percentage of remaining weight after the heating. Disc-shaped stone wool samples (diameter: 5 cm; height 1 cm) were cut out of stone wool and heat-treated at 580° C. for at least 30 minutes to remove all organics. The solids of the binder mixture were measured by distributing a sample of the binder mixture (approx. 2 g) onto a heat treated stone wool disc in a tin foil container. The weight of the tin foil container containing the stone wool disc was weighed before and directly after addition of the binder mixture. Two such binder mixture loaded stone wool discs in tin foil containers were produced and they were then heated at 200° C. for 1 hour. After cooling and storing at room temperature for 10 minutes, the samples were weighed and the dry solids matter was calculated as an average of the two results.
COOH Group Content
The change in COOH group content was also determined by aqueous titration and utilization of the following formula:
Where V2s and V1s are endpoint volumes of a sample while V2b and V1b are the volume for a blank sample. Cacid is 0.1M HCl in this case and ms,g is the weight of the sample.
Method of Producing an Oxidised Lignin:
Oxidised Lignin Compositions
In the following, the entry numbers of the oxidised lignin example correspond to the entry numbers used in Table II.
71.0 g lignin UPM Biopiva 100 was dissolved in 149.0 g water at 20° C. and added 13.3 g 25% NH4OH and stirred for 1 h by magnetic stirrer, where after 16.8 g H2O2 30% was added slowly during agitation. The temperature was increased to 60° C. in the water bath. After 1 h of oxidation, the water bath was cooled and hence the reaction was stopped. The resulting material was analysed for COOH, dry solid matter, pH, viscosity and density.
71.0 g lignin UPM Biopiva 100 was dissolved in 88.8 g water at 20° C. and added 13.3 g 25% NH4OH and stirred for 1 h by magnetic stirrer. PEG 200, 22.8 g was added and stirred for 10 min, where after 16.7 g H2O2 30% was added slowly during agitation. The temperature was increased to 60° C. in the water bath. After 1 h of oxidation, the water bath was cooled and hence the reaction was stopped. The resulting material was analysed for COOH, dry solid matter, pH, viscosity and density.
71.0 g lignin UPM Biopiva 100 was dissolved in 57.1 g water at 20° C. and added 13.3 g 25% NH4OH and stirred for 1 h by mechanical stirrer, where after 16.6 g H2O2 30% was added slowly during agitation. The temperature was increased to 60° C. in the water bath. After 1 h of oxidation, the water bath was cooled and hence the reaction was stopped. The resulting material was analysed for COOH, dry solid matter, pH, viscosity and density.
71.0 g lignin UPM Biopiva 100 was dissolved in 57.1 water at 20° C. and added 13.3 g 25% NH4OH and stirred for 1 h by mechanical stirrer. PEG 200, 19.0 g was added and stirred for 10 min, where after 16.6 g H2O2 30% was added slowly during agitation. The temperature was increased to 60° C. in the water bath. After 1 h of oxidation, the water bath was cooled and hence the reaction was stopped. The resulting material was analysed for COOH, dry solid matter, pH, viscosity and density.
8.5 l hot water (50° C.) and 1.9 l NH4OH (24.7%) was mixed, where after 9.0 kg lignin (UPM biopiva 100) was added slowly over 10 minutes at high agitation (660 rpm, 44 Hz).
The temperature increased by high shear forces. After 30 minutes, 4 l of hot water was added, and the material was stirred for another 15 minutes before adding the remaining portion of hot water (5 l). Samples were taken out for analyses of un-dissolved lignin by use of a Hegman Scale and pH measurements.
This premix was then transferred to a rotor-stator device and a reaction device where the oxidation was made by use of H2O2 (17.5 vol %). The reaction device used in this case has at least partially a reaction tube and a reaction vessel. Dosage of the premixture was 150 l/h and the H2O2 was dosed at 18 l/h. In the present case, a Cavitron CD1000 rotor-stator device was used to carry out the mixing/oxidation step. The rotor-stator device was run at 250 Hz (55 m/s circumferential speed) with a counter pressure at 2 bar. The dwell time in the reaction tube was 3.2 minutes and in the reaction vessel 2 hours.
Temperature of the premixture was 62° C., and the oxidation step increased the temperature to 70° C.
The final product was analysed for the COOH group content, dry solid matter, pH, viscosity and remaining H2O2.
484 l hot water (70° C.) and 47.0 l NH4OH (24.7%) was mixed, where after 224.0 kg lignin (UPM biopiva 100) was added slowly over 15 minutes at high agitation. Samples were taken out for analyses of un-dissolved lignin by use of a Hegman Scale and pH measurements.
This premixture was then transferred to a static mixer and a mixer/heat-exchanger, where the oxidation was made by use of H2O2 (35 vol %). Dosage of the premixture was 600 l/h and the H2O2 was dosed at 17.2 l/h. The dwell time in the mixer/heat-exchanger was 20 minutes.
The temperature of the mixture increased during the oxidation step up to 95° C.
The final product was analysed for the COOH group content, dry solid matter, pH, viscosity and remaining H2O2.
A binder was made based on this AOL: 49.3 g AOL (19.0% solids), 0.8 g primid XL552 (100% solids) and 2.4 g PEG200 (100% solids) were mixed with 0.8 g water to yield 19% solids; and then used for test of mechanical properties in bar tests.
Bar Tests
The mechanical strength of the binders was tested in a bar test. For each binder, 16 bars were manufactured from a mixture of the binder and stone wool shots from the stone wool spinning production.
A sample of this binder solution having 15% dry solid matter (16.0 g) was mixed well with shots (80.0 g). The resulting mixture was then filled into four slots in a heat resistant silicone form for making small bars (4×5 slots per form; slot top dimension: length=5.6 cm, width=2.5 cm; slot bottom dimension: length=5.3 cm, width=2.2 cm; slot height=1.1 cm). The mixtures placed in the slots were then pressed with a suitably sized flat metal bar to generate even bar surfaces. 16 bars from each binder were made in this fashion. The resulting bars were then cured at 200° C. The curing time was 1 h. After cooling to room temperature, the bars were carefully taken out of the containers. Five of the bars were aged in a water bath at 80° C. for 3 h.
After drying for 1-2 days, the aged bars as well as five unaged bars were broken in a 3 point bending test (test speed: 10.0 mm/min; rupture level: 50%; nominal strength: 30 N/mm2; support distance: 40 mm; max deflection 20 mm; nominal e-module 10000 N/mm2) on a Bent Tram machine to investigate their mechanical strengths. The bars were placed with the “top face” up (i.e. the face with the dimensions length=5.6 cm, width=2.5 cm) in the machine.
Oxidised Lignin Component (AOL)
8.5 l hot water (50° C.) and 1.9 l NH4OH (24.7%) was mixed, where after 9.0 kg lignin (UPM biopiva 100) was added slowly over 10 minutes at high agitation (660 rpm, 44 Hz).
The temperature increased by high shear forces. After 30 minutes, 4 l of hot water was added, and the material was stirred for another 15 minutes before adding the remaining portion of hot water (5 l).
This premix was then transferred to a rotor-stator device and a reaction device where the oxidation was made by use of H2O2 (17.5 vol %). The reaction device used in this case has at least partially a reaction tube and a reaction vessel. Dosage of the premixture was 150 l/h and the H2O2 was dosed at 18 l/h.
In the present case, a Cavitron CD1000 rotor-stator device was used to carry out the mixing/oxidation step. The rotor-stator device was run at 250 Hz (55 m/s circumferential speed) with a counter pressure at 2 bar. The dwell time in the reaction tube was 3.2 minutes and in the reaction vessel 2 hours.
Temperature of the premixture was 62° C., and the oxidation step increased the temperature to 70° C.
To a mixture of 18.3% aq. AOL made as above (100 g, thus efficiently 18.3 g AOL) stirred at room temperature, is added 5.0 g polyethyleneglycol 300 and 2.5 g aliphatic carbodiimide.
The binder solids are 21.2%.
For mechanical tests (15% binder solids, 0.5% silane of binder solids), the mixture is diluted with water (0.402 g/g binder mixture) and 10% aq. Silane (0.011 g/g binder mixture, Momentive A1871, prehydrolysed in acetic conditions with 10% acetic acid, diluted with water). The final binder mixture for mechanical tests have pH=10.2.
Bar Tests
The mechanical strength of the binders is tested in a bar test. For each binder, 16 bars are manufactured from a mixture of the binder and stone wool shots from the stone wool spinning production.
A sample of this binder solution having 15% dry solid matter (16.0 g) is mixed well with shots (80.0 g). The resulting mixture is then filled into four slots in a heat resistant silicone form for making small bars (4×5 slots per form; slot top dimension: length=5.6 cm, width=2.5 cm; slot bottom dimension: length=5.3 cm, width=2.2 cm; slot height=1.1 cm). The mixtures placed in the slots is then pressed with a suitably sized flat metal bar to generate even bar surfaces. 16 bars from each binder are made in this fashion. The resulting bars are then cured typically at 200° C.
The curing time is 1 h. After cooling to room temperature, the bars are carefully taken out of the containers. Five of the bars are aged in a water bath at 80° C. for 3 h.
After drying for 1-2 days, the aged bars as well as five unaged bars are broken in a 3 point bending test (test speed: 10.0 mm/min; rupture level: 50%; nominal strength: 30 N/mm2; support distance: 40 mm; max deflection 20 mm; nominal module 10000 N/mm2) on a Bent Tram machine to investigate their mechanical strengths. The bars are placed with the “top face” up (i.e. the face with the dimensions length=5.6 cm, width=2.5 cm) in the machine.
The binder of Example 1 shows excellent binder properties in the bar tests.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2020/059670 | 4/3/2020 | WO |