Patent Application
20110117281
This invention relates to aqueous coating binders for corrosion protection, wood and concrete.
Aqueous binders based on cationically stabilised epoxy amine adducts have been known for application in cathodic electrodeposition coatings, such as described in EP 0 249 850 A1. These are usually cured by heating their mixtures with capped di- or polyfunctional isocyanates. Epoxy amine adducts that are dispersed in water after neutralisation can be chain-extended with further epoxy resin to yield high molar mass products that do not need an additional curing agent, but form coherent coating films upon drying (“physically drying”) on substrates such as metal and concrete which exhibit excellent adhesion and impart good corrosion protection. Such systems have been known from EP 1 207 187 B1, and also from copending EP application No. 07 001 858.5.
The corrosion resistance imparted to substrates covered by coatings based on such systems under high temperature and high humidity conditions (temperatures in excess of 30° C., relative humidity in excess of 50%) still needs to be improved.
It has been found that by adding a crosslinking agent such as an aminoplast resin, a phenol resol, a triazine tris-alkyl carbamate, or a mixture of such crosslinking agents provided that these are compatible, leads to aqueous binders that can be used to prepare coating compositions which show improved corrosion protection. By “compatible”, such mixtures are referred to which do not lead to phase separation in the presence of the other binder resins, and which improve curing so that the overall curing rate is at least not lower compared to the curing rate with each of the components alone. Such binders may be preferably used to formulate corrosion protection coatings for metals, and to formulate sealers for wood. It has been found that it is also possible to add a polyester having carboxyl groups and hydroxyl groups, which addition leads to better adhesion to substrates, and higher elasticity of the coating film.
An object of the invention are therefore aqueous binders comprising mass fractions of from 70% to 98% of a chain-extended epoxy amine adduct A and from 2% to 30% of at least one crosslinking agent C that is selected from the group consisting of aminoplast resins, phenol resols, triazine tris-alkyl carbamates, and mixtures of such crosslinking agents.
Another object of the invention is a process for the preparation of binder mixtures comprising mass fractions of from 70% to 98% of a chain-extended epoxy amine adduct A and from 2% to 30% of at least one crosslinking agent C that is selected from the group consisting of aminoplast resins, phenol resols, triazine tris-alkyl carbamates, and mixtures of such crosslinking agents, which process encompasses the following steps:
Binder mixtures of chain-extended epoxy amine adducts A and of crosslinking agents C according to the invention may be used to form coating films on substrates comprising mixing and homogenising the binder mixtures, optionally together with pigments or fillers, to form a coating composition, applying the said coating composition to a substrate, and subjecting the said coating composition to forced drying at a temperature of from 60° C. to 140° C.
Aqueous dispersions of A and C may be formed by dispersing the mixture of A and C in water as described supra, it is also possible to add C to the water charge used for dispersion, or to an aqueous dispersion of A.
A preferred embodiment are binder mixtures comprising mass fractions of from 50% to 96% of a chain-extended epoxy amine adduct A, from 2% to 30% of a carboxy functional polyester B that contains a limited amount of aromatic constituents in mass fractions of up to 15% and has an acid number of from 4 mg/g to 50 mg/g, and from 2% to 30% of a crosslinker C selected from the group consisting of aminoplast resins, phenol resols, triazine tris-alkyl carbamates, and mixtures of such crosslinking agents, with the proviso that the sum of the mass fractions of components A, B and C is always 100%.
Another preferred embodiment is a process for the preparation of binder mixtures comprising mass fractions of from 50% to 96% of a chain-extended epoxy amine adduct A, of 2% to 30% of a crosslinking agent C, and from 2% to 30% of a carboxy functional polyester B that contains a limited amount of aromatic constituents in a mass fraction of from 0% to 15% and has an acid number of from 4 mg/g to 50 mg/g, which process encompasses the following steps:
The epoxy resins A1 have at least one, preferably two, 1,2-epoxide groups per molecule, and are of aromatic or aliphatic nature. Glycidyl ethers of monohydric aliphatic or mixed aliphatic-aromatic alcohols, or glycidyl esters of aliphatic or aromatic monocarboxylic acids are preferred as monoepoxides. The alcohols preferably have from 4 to 20 carbon atoms and are particularly preferably selected from the group consisting of 2-ethyl hexanol, decanol, tridecanol, stearyl alcohol, and benzyl alcohol. The acids are preferably selected from the group consisting of branched aliphatic monocarboxylic acids having from 5 to 11 carbon atoms, particularly preferably, of the group consisting of glycidyl neopentanoate, glycidyl 2-ethyl hexanoate, glycidyl neodecanoate, and the mixtures of such acids which are commercially available under the trade names of ®Versatic acids. Mixtures of such ethers and such esters can likewise be used. Other aliphatic epoxides can be formed by epoxidation of olefins or diolefins, such as hexene-1,1,3-butadiene, 1,5-hexadiene, or by reaction of epichlorohydrin with dihydric alcohols such as 1,4-butane diol, 1,6-hexanediol, or oligomeric ethylene and propylene glycols. Aromatic diepoxides may be formed by reaction of epichlorohydrin with dihydroxyaromatic compounds such as resorcinol, dihydroxy diphenyl, dihydroxydiphenyl sulphone, or dihydroxy benzophenone. Particularly preferred are reaction products of epichlorohydrin with Bisphenol A (2,2-bis-(4-hydroxyphenyl) propane), and Bisphenol F (bis-(4-hydroxyphenyl)methane). In addition to these diepoxides mentioned, glycidyl ethers of tri- or polyhydric alcohols such as trimethylol ethane and propane, ditrimethylol ethane and ditrimethylol propane, pentaerythritol, and dipentaerythritol, as well as ethoxylation or propoxylation products of the said alcohols may also be used, with an average of from two to twenty oxyalkylene groups per one hydroxyl group of the said alcohols are preferred. Glycidyl esters of dibasic or polybasic organic acids can also be used, preference being given to those of succinic acid, adipic acid, phthalic acid, isophthalic acid, terephthalic acid, trimellithic acid, trimesic acid, and benzophenone tetracarboxylic acid. It is preferred to use such epoxy resins A1 having a specific epoxide group content e (e=n(EP)/m, the ratio of the amount of substance n(EP) of epoxide groups in the resin, and the mass in of the resin) of from 0.5 mol/kg to 8 mol/kg, particularly preferred of from 1 mol/kg to 6 mol/kg.
As amines A2, aliphatic linear, branched or cyclic amines having from 2 to 40 carbon atoms are preferred. These amines A2 may be selected from the group consisting of amines A21 having at least one primary amino group and optionally, one or more further non-primary amino groups, and amines A22 having at least one secondary amino group and optionally, one or more hydroxyl groups.
In addition to the at least one primary amino group, the amines A21 may have one or more further amino groups selected from the group consisting of secondary and tertiary amino groups. Particularly preferred are diamines, triamines, and tetramines with two primary amino groups, such as ethylene diamine, 1,2- and 1,3-propylene diamine, 1,4-diaminobutane, 1,6-diaminohexane, diethylene triamine, triethylene tetramine, 1,2-, 1,3-, and 1,4-diaminocyclohexane, isophorone diamine, and 1,3-bisaminomethyl cyclohexane, or mixtures of such amines. It is also possible to use oligomeric diamino ethylene imines. Among the primary mono- and diamines having further tertiary amino groups, preference is given to those having at least one primary and at least one tertiary amino groups, and from 4 to 20 carbon atoms, the alkyl residues attached to the tertiary amino group having from 1 to 4 carbon atoms, viz., methyl, ethyl, n-propyl, iso-propyl, n-butyl, sec.-butyl, iso-butyl, and tert.-butyl groups. Such amines are 3-(N,N-dimethylamino)-propylamine, 3-(N,N-diethylamino)-propylamine, N-(2-aminoethyl)-morpholine, N,N′-bis-(2-aminoethyl)-piperazine. Among the suitable triamines, tris-2-aminoethyl-amine is mentioned. Particularly preferred are ethylene diamine, diethylene triamine, and 1,4-diaminobutane, as well as 3-(N,N-dimethylamino)-propylamine, and 3-(N,N-diethylamino)-propylamine.
The amines A22 have at least one secondary amino group and optionally, one or more hydroxyl groups, examples for these being diethanolamine, diisopropanolamine, n-hydroxyethyl piperazine, and 2-methylamino ethanol.
If mixtures of A21 and A22 are used, it is preferred to choose the quantities thereof such that the number of aminic hydrogen atoms in A22 is between 50% and 150%, particularly preferred from 75% to 125%, of the number of aminic hydrogen atoms in A21.
It is preferred to use organic monobasic acids to neutralise the adducts A12, such as formic acid, acetic acid, lactic acid, or tartaric acid. Inorganic polybasic acids such as boric acid, phosphoric acid, or their partial esters may also be used.
The epoxy resins A3 have at least two 1,2-epoxide groups, and may be aliphatic or aromatic. Aliphatic diepoxides may be formed by epoxidation of diolefins, such as 1,3-butadiene, 1,5-hexadiene, or by reaction of epichlorohydrin with dihydric alcohols such as 1,4-butane diol, 1,6-hexanediol, or oligomeric ethylene and propylene glycols. Aromatic diepoxides may be formed by reaction of epichlorohydrin with dihydroxyaromatic compounds such as resorcinol, dihydroxy diphenyl, dihydroxydiphenyl sulphone, or dihydroxy benzophenone. Particularly preferred are reaction products of epichlorohydrin with Bisphenol A (2,2-bis-(4-hydroxyphenyl) propane), and Bisphenol F (bis-(4-hydroxyphenyl)methane). In addition to these diepoxides mentioned, glycidyl ethers of tri- or polyhydric alcohols such as trimethylol ethane and propane, ditrimethylol ethane and propane, pentaerythritol, and dipentaerythritol, as well as ethoxylation or propoxylation products of the said alcohols may also be used, with an average of from two to twenty oxyalkylene groups per one hydroxyl group of the said alcohols are preferred. Glycidyl esters of dibasic or polybasic organic acids can also be used, preference being given to those of succinic acid, adipic acid, phthalic acid, isophthalic acid, terephthalic acid, trimellithic acid, trimesic acid, and benzophenone tetracarboxylic acid. It is preferred to use such epoxy resins A3 having a specific epoxide group content of from e=0.6 mol/kg to e=10 mol/kg, particularly preferred of from e=1.2 mol/kg to e=6 mol/kg. It is further preferred to choose such epoxy resins A3 with a specific epoxide group content e(A3) which is higher than that of the epoxy resins A1, particularly such that the ratio e(A3):e(A1) is from 1.2 to 5, preferably from 1.5 to 4.
The epoxy amine adducts A have preferably an amine number of from 40 mg/g to 150 mg/g, and hydroxyl numbers of from 30 mg/g to 150 mg/g, in each case in relation to the mass of solid resin. Their Staudinger index is preferably from 30 cm3/g to 100 cm3/g, as measured on solutions in N-methyl pyrrolidone at room temperature (23° C.).
The quantity formerly referred to as “limiting viscosity number”, called “Staudinger index” Jg in accordance with DIN 1342, part 2.4, is the limiting value of the Staudinger function. Jv measured with decreasing concentration and shear stress, wherein Jv is the ratio of the relative change in viscosity ηr−1, divided by the mass concentration βB=mB/V of the solute B (mass mB of the solute in a volume V of the solution), given by Jv=(ηr−1)/βB·ηr−1 stands for the relative change in dynamic viscosity, according to ηr−1=(η−ηs)/ηs. The relative viscosity ηr is the ratio of the dynamic viscosity η of the solution under consideration and the dynamic viscosity ηs of the pure solvent. The physical significance of the Staudinger index is that of a specific hydrodynamic volume of the solvated polymer coil at infinite dilution and at rest. The unit conventionally used for J is “cm3/g”; formerly also “dl/g”.
The acid number is defined according to DIN EN ISO 3682 as the ratio of the mass mKOH of potassium hydroxide needed to neutralise the sample under consideration, and the mass mB of that sample (mass of solids in the sample in the case of solutions or dispersions); its conventional unit is “mg/g”.
The amine number is defined according to DIN 53 176 as being the ratio of that mass mKOH of potassium hydroxide which consumes the same quantity of acid as the sample under consideration, and the mass mB of the said sample (mass of solids in the sample in the case of solutions or dispersions); its conventional unit is “mg/g”.
The hydroxyl number is defined according to DIN EN ISO 4629 as the ratio of the mass mKOH of potassium hydroxide which has the same number of hydroxyl groups as the sample under consideration, and the mass mB of that sample (mass of solids in the sample in the case of solutions or dispersions); its conventional unit is “mg/g”.
Dispersions of the adducts A in water usually have a mass fraction of solids of from 20% to 60%.
Although such epoxy resins A are physically drying, that means, they do not need the addition of a crosslinker to form a stable and mechanically resistant film on a substrate, it has been found in the present invention that the addition of cosslinkers C that react with functional groups, in this case hydroxyl groups, present in the binder resin leads to largely enhanced properties, particularly with regard to corrosion resistance, surprisingly without sacrifice of elasticity. The elasticity can be further improved by addition of a polyester B, such addition also unexpectedly improves the adhesion to substrates such as metals, wood, and also concrete.
Such crosslinkers C that can react with hydroxyl groups are preferably
The amount of crosslinking agents C is preferably chosen in a way that at least 10% of the hydroxyl groups present in the chain-extended epoxy amine adduct A are consumed by reaction with the crosslinking agent to form a cured coating film on the surface of a substrate.
It has further been found in the present invention that the corrosion protection performance of coatings prepared from mixtures of these dispersions of epoxy resins A and crosslinking agents C can still be improved, particularly under what is referred to as “tropical conditions” at temperatures of 30° C. or more, and relative humidity of more than 50%, by adding carboxy functional polyesters B. Addition of these polyester also leads to improved adhesion of the coating films on substrates such as metals, wood, and concrete, and also to increased elasticity of the coating films.
The polyesters B are characterised by a limited amount of aromatic constituents, where the mass fraction of aromatic constituents, viz. the ratio of the mass m(B22) of aromatic acids B22, to the sum of the masses of all hydroxy functional and acid functional constituents, m(B1)+m(B2), is up to 15%, preferably from 1% to 12.5%, and in particular, from 2% to 10%.
The polyesters are condensation products of hydroxy functional components B1 and acid functional components B2. It is preferred that at least one of B1 and B2 comprises compounds with a functionality of more than 2, i.e. either a trihydric or polyhydric alcohol, or a tribasic or polybasic acid, or both. In this context, “poly” refers to functionality of 4 or more. Preferably, at least the acid component B2 comprises a compound with a functionality of three or more.
It is also preferred that in the reaction mixture of components B1 and B2, the ratio of the amount of substance of hydroxyl groups to the amount of substance of acid groups is between 0.8 mol/mol and 1.7 mol/mol, particularly preferred, between 0.9 mol/mol and 1.6 mol/mol. The acid number of the polyesters B preferably lies in the range of from 4 mg/g to 50 mg/g, and its hydroxyl number is preferably from 80 mg/g to 280 mg/g, particularly preferable from 100 mg/g to 270 mg/g. The Staudinger index of the polyesters, measured in a solution in dimethyl formamide at 23° C., is preferably from 10 cm3/g to 25 cm3/g, particularly preferred from 12 cm3/g to 20 cm3/g, and especially preferred, from 15 cm3/g to 18 cm3/g.
The hydroxy functional components B1 are aliphatic linear, branched or cyclic compounds having at least two primary hydroxyl groups. It is preferred to have at least one linear difunctional hydroxy compound B11 and at least one further hydroxy compound B12 in the hydroxy functional components B1 used for the synthesis of the polyester B, where the compounds B12 comprise at least one trifunctional or polyfunctional hydroxy compound B121 or at least one branched difunctional hydroxy compound B122.
In another preferred embodiment, it is possible to add hydroxy functional polylactones such as polycaprolactone diols or triols, which can lower the glass temperature of the resulting polyester and thus modify the adhesion to the substrate.
Compounds B11 are difunctional linear aliphatic alcohols having preferably from 2 to 40 carbon atoms, particularly preferably from 4 to 12 carbon atoms. Suitable compounds are ethylene glycol, 1,3-propylene glycol, 1,4-butane diol, 1,6-hexane diol, and 1,12-dodecane diol, and ether diols such as diethylene glycol or triethylene glycol.
Trifunctional alcohols B121 have at least two primary hydroxyl groups, and at least one more hydroxyl group which can be primary or secondary. They preferably have from 3 to 12 carbon atoms. Suitable compounds include glycerol, diglycerol, trimethylol ethane, trimethylol propane, ditrimethylol ethane, ditrimethylol propane, pentaerythritol, dipentaerythritol, mannitol, and sorbitol.
Branched difunctional alcohols B122 have at least one tertiary or at least one quaternary carbon atom and from 3 to 10 carbon atoms. Suitable compounds are 1,2-propane diol, 2-methyl-1,3-propane diol, neopentyl glycol, 2,2,4-trimethyl-1,6-hexane diol and 2,4,4-trimethyl-1,6-hexane diol.
It is preferred to have a ratio of the amount of substance of compounds B12 to the amount of substance of compounds B11 of from 3% to 25%, particularly preferred from 5% to 20%.
The acids B2 comprise at least one aliphatic acid B21 and at least one aromatic acid B22. Preferably, at least 80% of the mass of the aromatic acid B22 is constituted by a tri- or polyfunctional acid, polyfunctional again referring to acids with a functionality of four or more. Suitable acids B22 comprise di-, tri- and polyfunctional aromatic acids such as the isomeric phthalic acids, sulphoisophthalic acid, trimellithic acid, trimesic acid, hemimellithic acid, pyromellithic acid, and benzophenone tetracarboxylic acid, as well as anhydrides thereof. The aliphatic acids B21 are preferably linear and have from 4 to 40 carbon atoms. Suitable compounds are succinic acid, sulphosuccinic acid, glutaric acid, adipic acid, dodecanedioic acid, and dimeric fatty acids which are preferably linear.
The binder mixtures of the invention comprising chain-extended epoxy amine adducts A and crosslinking agents C provide exceptionally good corrosion protection for metals. Metal coating compositions are usually formulated with defoamers, thixotropy agents, thickeners and also dispersing agents for the pigments and fillers used, which are usually iron oxide pigments, zinc phosphate pigments, and optionally fillers such as those based on kaolin or talc, or mixtures thereof. It has also been found that the binder mixtures of the present invention are particularly useful as sealers for wood. Such coating compositions may be formulated without fillers (as a clear coat), or with fillers such as kaolin or talc, and provide a surprisingly pronounced sealing effect. Addition of polyesters B improves the elasticity of the coating film formed from the binder mixtures, and its adhesion to substrates.
It is also possible to modify the epoxy amine adducts A further by including in the reaction leading to these epoxy amine adducts A to the said educts, or starting components, viz. the epoxy resins A1, the aliphatic amines A2, and the further epoxy resins A3, at least one fatty acid A4 as a further component. This fatty acid A4 is preferably unsaturated, having at least one olefinic unsaturation, and has from 6 to 30, preferably from 8 to 26, and particularly preferred, from 16 to 22, carbon atoms. Preferred fatty acids A4 are palmoleic acid, oleic acid, and erucic acid, linolic acid, linoleic acid, elaostearic acid, arachidonic acid and clupanodonic acid as well as the fatty acids obtained from natural oils such as linseed fatty acid, soy bean oil fatty acid, tall oil fatty acid, cotton seed oil fatty acid, isomerised sunflower fatty acid, rape seed oil fatty acid, and fatty acid mixtures derived from dehydrated castor oil. The fatty acid A4 may be reacted in any sequence with the epoxy resins A1 and the amines A2, before further reaction with the epoxy resin A3, such as first reacting A1 and A2, and then reacting the product from this reaction with A4, or first reacting A1 and A4, and then reacting the product from this reaction with A2, or reacting A1 concurrently with A4 and A2.
The invention is further illustrated by the following examples. In these examples as well as in the whole specification, all quantities measured in “%” relate to mass fractions or mass ratios, as measured in cg/g or g/hg, except where specifically denoted otherwise.
The epoxy amine adduct solution of Example 1 was heated to 150° C., and the solvent was removed by distillation under reduced pressure. The resin was allowed to cool to 120° C. 142 g of lactic acid (85% strength solution in water) were slowly added, and the neutralised resin was cooled to 90° C. and then diluted to a mass fraction of solids of about 40% by addition of desalinated water. Under stirring, 130 g of bisphenol A diglycidyl ether were added thereto at 90° C., and the mixture was continued to stir until no more epoxy groups were detectable. After cooling to room temperature, further water was added to dilute to a mass fraction of solids of about 38%.
The solution of Example 2 was used to formulate a cationic primer. In a mixture of 88 g of fully desalinated water and 22 g of a commercial dispersing agent (®Additol VXW 6208, Cytec Surface Specialties Austria GmbH), 3 g of a commercial defoamer (®Surfynol SE-F, E. I. DuPont de Nemours Company), 6 g of a thixotropy agent (®Luwothix HT, Lehmann & Voss), and 3 g of an acrylate thickener (®Acrysol RM 8/12, Rohm & Haas Company), 62 g of an iron oxide pigment (®Bayferrox, Lanxess AG), 106 g of a modified zinc phosphate pigment (Heucophos ZPO, Heubach GmbH), 55 g of a kaolin filler (®ASP 600, Engelhardt GmbH), and 55 g of a talc filler (®Talkum AT1, Norwegian Talc AS) were dispersed. A mixture of 480 g of the binder resin solution of Example 2 and 47.6 g of a high imino type partially methyl etherified melamine formaldehyde based crosslinker (®Cymel 328, Cytec Industries Inc.) and further 117 g of desalinated water were added thereto. The primer composition P1 thus obtained had an efflux time of approximately thirty seconds, measured in a 4 mm cup according to DIN EN ISO 2431, or DIN 53 211.
Example 3 was repeated, and the melamine formaldehyde based crosslinker was replaced by 65.5 g of 2,4,6-tris-(butoxycarbonylamino)-1,3,5-triazin to yield primer composition P2.
Example 3 was repeated, and the melamine formaldehyde based crosslinker was replaced by 78 g (mass of solids) of a butylated phenol-based resol to yield primer composition P3.
Example 3 was repeated, without addition of a crosslinker to yield primer composition P4.
A corrosion test was conducted according to DIN 50 021 using untreated steel sheets, spraying with each of the primer compositions to obtain a 30 μm dry film after forced drying at 100° C. for thirty minutes. The results are listed in Table 1.
It can be seen from this table that the addition of a crosslinker in a physically drying primer system according to the invention brings about a marked improvement in corrosion protection, while there is no improvement in conventional alkyd resin-based physically drying primer systems.
Into a three neck vessel equipped with a stirrer and a reflux condenser, 531 g (4.5 mol) of hexane diol-1,6, 67 g (0.5 mol) of trimethylol propane, 438 g (3.0 mol) of adipic acid, and 58 g (0.3 mol) of trimellithic anhydride were charged. The charge was heated to 200° C. by 10 K/h, under stirring and a nitrogen blanket. Water formed in the condensation reaction was separated, and reaction was continued until the acid number had decreased below 25 mg/g. The Staudinger index of the polyester PE1 as measured in a dimethyl formamide solution at 23° C. was 16.5 cm3/g. A hydroxyl number of 209 mg/g was determined on a sample. Finally, the polyester PE1 was diluted to a mass fraction of solids of 80% by adding further methoxypropanol.
The epoxy amine adduct solution of Example 1 was heated to 150° C., and the solvent was removed by distillation under reduced pressure. 147 g of the polyester solution of Example 8 (PE1) were added, the mixture was stirred for one further hour at 150° C. whereafter the mixture was allowed to cool to 110° C. 60 mmol of lactid acid per 100 g of solid resins were added, and the neutralised resin mixture was diluted to a mass fraction of solids (=non-volatiles) of 40% by addition of fully desalinated water. Within one further hour, 130 g of bisphenol A diglycidylether were added to this aqueous solution at 90° C., and the resulting mixture was kept at this temperature under stirring until the epoxide groups were completely consumed. Further water was added to adjust the solution to a mass fraction of solids of 38%.
The solution of Example 9 was used to formulate a cationic primer. In a mixture of 88 g of fully desalinated water and 22 g of a commercial dispersing agent (®Additol VXW 6208, Cytec Surface Specialties Austria GmbH), 3 g of a commercial defoamer (®Surfynol SE-F, E. I. DuPont de Nemours Company), 6 g of a thixotropy agent (®Luwothix HT, Lehmann & Voss), and 3 g of an acrylate thickener (®Acrysol RM 8/12, Rohm & Haas Company), 62 g of an iron oxide pigment (®Bayferrox, Lanxess AG), 106 g of a modified zinc phosphate pigment (Heucophos ZPO, Heubach GmbH), 55 g of a kaolin filler (®ASP 600, Engelhardt GmbH), and 55 g of a talc filler (®Talkum AT1, Norwegian Talc AS) were dispersed. 480 g of the binder solution of Example 9 and further 117 g of desalinated water were added thereto. The primer composition thus obtained had an efflux time of approximately thirty seconds, measured in a 4 mm cup according to DIN EN ISO 2431, or DIN 53 211.
The procedure of Example 10 was repeated, with the binder solution of Example 9 being replaced by a mixture of 480 g of the binder resin solution of Example 9 and 47.6 g of a high imino type partially methyl etherified melamine formaldehyde based crosslinker (®Cymel 328, Cytec Industries Inc.)
Corrosion testing at room temperature and at increased temperature (45° C., 50% relative humidity) gave the same improvement as without the addition of polyester, but it was found that the coating layer had better elasticity (T-bend and Erichsen cupping tests), and better adhesion than that prepared with primers P1, P2 and P3. When used as a sealer for wood, it was found that addition of polyester led to a decrease in discolouration upon extendend storage of sealed wood panels at elevated temperatures (40° C. over 6 weeks).
The optimum range for the mass fraction of the polyester in the binder mixture to improve adhesion and elasticity without impairing the corrosion results was found to be from 5% to 15%.
| Number | Date | Country | Kind |
|---|---|---|---|
| 08160844.0 | Jul 2008 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP09/58485 | 7/6/2009 | WO | 00 | 1/19/2011 |