Patent Grant
8419850
The present invention relates to an aqueous composition comprising a carbonate of zirconium and of an alkali metal salt and an ammonium halide, and to the use of the said composition as insolubilizing agent in coating baths for paper or board.
It is known that aqueous compositions of ammonium zirconium carbonate (AZC) can be used to render insoluble, in aqueous solution, natural binders, such as starch, casein or carboxymethylcellulose (CMC), or synthetic binders, such as latexes or polyvinyl alcohol, and to form insoluble films, thus improving the resistance to water, to friction, to heat and to solvents.
These zirconium carbonate solutions are used in numerous technological fields, in particular in aqueous ink and paint formulations and more particularly in coating baths intended for the coating or impregnation of paper or board in order to improve the appearance, the wet abrasion resistance, the picking, the strength and the ability to receive printing.
However, the use of these solutions has the disadvantage of releasing a strong smell of ammonia when the latter are employed.
One solution provided is the use of aqueous solutions of zirconium carbonate and of an alkali metal salt, such as of sodium or potassium. However, the use of these compositions does not give satisfactory results, particularly as regards the resistance of the coating to wet rub.
U.S. Pat. No. 6,113,989 indicates that aqueous alkaline solutions of sodium, potassium or ammonium and zirconium carbonate used in compositions for preventing the colouring of wood can be modified by the addition of anionic entities, such as Cl ions.
FR 1 378 117 teaches that the addition of a small amount of ammonium chloride to aqueous solutions of ammonium zirconium carbonate appears to improve the performance of the said solution in compositions for the coating of paper.
Surprisingly, it has now been found that the addition of an ammonium halide to an aqueous solution of carbonate of zirconium and of an alkali metal salt makes it possible to obtain resistances to wet rub which are comparable to aqueous AZC solutions, this being the case even for coating baths having high pH values.
A subject-matter of the present invention is thus an aqueous composition comprising a carbonate of zirconium and of an alkali metal salt, prepared from a zirconium compound and from an alkali metal bicarbonate with a bicarbonate to zirconium molar ratio equal to or greater than 4:1, and an ammonium halide with a halide to zirconium molar ratio equal to or greater than 2:1.
The term “zirconium compound” denotes basic zirconium carbonate, also known as BZC or ZBC, zirconium oxychloride (ZrOCl2), also known as ZOC, and basic zirconium sulphate, also known as BZS, basic zirconium carbonate being preferred.
The term “alkali metal bicarbonate” denotes sodium bicarbonate or potassium bicarbonate, potassium bicarbonate being preferred.
The ammonium halide can be chosen from ammonium chloride, ammonium bromide, ammonium fluoride, ammonium iodide or their mixtures. Ammonium chloride (NH4Cl) is preferred.
The halide to zirconium molar ratio in the aqueous composition is equal to or greater than 2:1, preferably between 2:1 and 5:1, preferentially between 2.5:1 and 3.5:1 and very particularly equal to 3:1.
The bicarbonate to zirconium molar ratio during the preparation of the carbonate of zirconium and of an alkali metal salt is equal to or greater than 4:1, preferably between 4:1 and 6:1, and preferably equal to 4:1.
The aqueous compositions of the present invention have a pH of greater than 7 and of less than 10, preferably of between 8 and 9, a concentration of 4 to 12% by weight, expressed as ZrO2, preferably a concentration of 7 to 10% by weight, expressed as ZrO2, and a solids content of 11 to 42%, preferably of 30 to 36%.
The basic zirconium carbonate, the zirconium oxychloride and the basic zirconium sulphate which can be used according to the invention are commercial products generally available in the solid and hydrate form. Advantageously, the basic zirconium carbonate will be used in the powder form as sold by Astron.
Typically, the compositions of the present invention are prepared by reaction of the zirconium compound with an aqueous solution of alkali metal bicarbonate, followed by addition of the ammonium halide.
Another subject-matter of the invention is a process for the preparation of an aqueous composition comprising a carbonate of zirconium and of an alkali metal salt, prepared from a zirconium compound and from an alkali metal bicarbonate, and an ammonium halide, as described above, comprising a stage consisting in reacting the zirconium compound with an aqueous solution of alkali metal bicarbonate, with a bicarbonate to zirconium molar ratio equal to or greater than 4:1, and a stage of addition of the ammonium halide, with a halide to zirconium molar ratio equal to or greater than 2:1.
The reaction of the zirconium compound with the alkali metal bicarbonate can be carried out at ambient temperature but it is facilitated by heating.
According to a preferred embodiment, after having added, at ambient temperature, the zirconium compound to the aqueous solution of alkali metal bicarbonate, the solution obtained is brought with stirring to a temperature of between 30 and 80° C., preferably to 70° C., for 1 h to 24 h, preferably 4 h.
Conventionally, the ammonium halide is added to the solution obtained above at ambient temperature and then stirring is allowed to take place until the ammonium halide has completely dissolved.
The stability of the aqueous compositions of the present invention can be improved by the addition of a stabilizing agent as described in FR-A-2 088 550. Mention may be made, by way of example, of tartaric acid or gluconic acid, which is advantageously added in the proportion of 1 to 2% approximately with respect to the weight of the final solution. The tartaric or gluconic acid can be added before the reaction between the zirconium compound and the alkali metal bicarbonate or after the addition of the ammonium halide, preferably before the reaction.
The compositions obtained according to the invention are stable over time and exhibit advantageous properties when they are introduced into compositions for the treatment of cellulose-based products, in particular into coating baths.
They make it possible in particular to improve the wet abrasion resistance, the wet pick resistance and the inertia with regard to water of the substrates treated, such as paper or board, such as, for example, paper of the type for the printing of writing, newsprint, recycled paper, wrapping paper, paper of test liner type, the backing for self-adhesive labels or board in the flat.
Another subject-matter of the invention is thus the use of these compositions as insolubilizing agent in an aqueous composition for the treatment of a cellulose-based product, preferably paper or board.
In the present invention, the coating bath can be:
In particular, another subject-matter of the invention is a method for treating a cellulose-based product, preferably paper or board, in which a coating bath comprising at least one binder, an insolubilizing agent and optionally a pigment is applied at the surface of the said cellulose-based product, characterized in that the insolubilizing agent is an aqueous composition comprising a carbonate of zirconium and of an alkali metal salt and an ammonium halide, as described above.
According to another aspect, the invention is also targeted at a method for treating a cellulose-based product, preferably paper or board, in which a coating bath comprising at least one binder, an insolubilizing agent and optionally a pigment is brought into contact with the said cellulose-based product, characterized in that that the insolubilizing agent is an aqueous composition comprising a carbonate of zirconium and of an alkali metal salt and an ammonium halide, as described above.
According to a preferred aspect for implementing the invention, the insolubilizing agent is an aqueous composition comprising a potassium zirconium carbonate and ammonium chloride.
A coating bath is an aqueous mixture comprising at least one binder, an insolubilizing agent and optionally a pigment, and also, optionally, functional additives. Generally, the pigments used are chosen from kaolin, calcium carbonate, titanium dioxide and their mixtures. Other pigments, such as alumina hydrate, satin white, silicates or synthetic pigments, can also be used for specific applications.
The binders can be of natural or synthetic origin.
Mention may be made, among natural binders, of starch, modified starch (for example oxidized or modified by enzymes), soy protein and casein.
More commonly, use is made of synthetic binders, such as styrene/butadiene latexes, polyvinyl acetate latexes, acrylate latexes or polyvinyl alcohol.
According to a preferred aspect, the binders used in the present invention can be chosen from functionally modified latexes, for example latexes modified with hydroxyl groups, particularly with carboxyl groups, in particular sodium carboxylate groups. Mention may be made, by way of example, of the styrene/butadiene DL 950 latex sold by Dow.
The coating baths which can be used in the present invention can also comprise additives, such as dispersants, viscosity modifiers (carboxymethylcellulose or hydroxyethylcellulose, for example), lubricating agents, bactericides, pH control agents, repellants, gloss agents, dyes or antifoaming agents.
The pH of the said coating baths is generally between 7 and 9, preferably between 7 and 8.6.
Generally, the amount of insolubilizing agent of the present invention in the coating bath is between 1 and 20 parts as is per 100 parts of binder under dry conditions, preferably between 3 and 15 parts as is per 100 parts of binder under dry conditions.
The coating bath is applied by methods known per se. Mention may be made, by way of example, of the process with an applicator roll, size press or premetering size press.
The invention is illustrated without implied limitation by the following examples.
Preparation of a potassium zirconium carbonate solution comprising 8.5% of dry ZrO2 with regard to the solution as is and 4 mol of bicarbonate per mole of zirconium.
0.78 g of tartaric acid is added to 41.32 g of water with stirring and at ambient temperature. Subsequently, 26.70 g of potassium bicarbonate are added, followed by 20.50 g of basic zirconium carbonate (38 to 42% of ZrO2; Astron). When the addition is complete, the solution is heated at 70° C. for 3 hours.
The solution is cooled to 30° C. and 10.70 g of ammonium chloride are added with stirring. Stirring is maintained until the ammonium chloride has completely dissolved.
100 g of a clear colourless solution having a slight smell of ammonia, a pH of approximately 8.2, a solids content of 32.8% and an NTU turbidity of 6 are obtained.
Use was made of a calcium carbonate sold by Omya (Hydrocarb® 90), a kaolin sold by Huber Engineered Materials (Hydragloss®), a styrene/butadiene latex sold by Dow (DL 950), and carboxymethylcellulose (CMC) sold by Noviant (Finfix® 10).
Various formulations C1 to C4 were prepared, the compositions of which are given in Table 1 below. The amounts are given as dry parts.
The formulation C1 does not comprise an insolubilizing agent.
The formulation C2 corresponds to the use of an insolubilizing composition according to the invention (Example 1).
The formulation C3 corresponds to the use of a commercial aqueous ammonium zirconium carbonate composition comprising 19% of dry ZrO2 with regard to the solution as is, a solids content of 30.85% and a pH of 9.5.
The formulation C4 corresponds to the use of an aqueous potassium zirconium carbonate solution prepared according to the procedure of Example 1 but without addition of ammonium chloride, comprising 11% of dry ZrO2 with regard to the solution as is, a solids content of 53.7% and a pH of 9.
In the examples, use was made of uncoated paper exhibiting a grammage of 80 g/m2.
The paper was coated with the formulations C1 to C4 with a deposition of approximately 26 g/m2 using a threaded rod, followed by oven drying at 105° C. in an oven for 2 minutes.
The Taber wet abrasion was subsequently determined on the coated paper.
The Taber wet abrasion was carried out according to amended French Standard Q 03-055, with annular test specimens with outer and inner diameters of 120 and 7 mm respectively, with 10 revolutions, CS O wheels, under a pressure of 1N, in the presence of 10 ml of water, followed by rinsing with 10 ml of water; these 20 ml of water are collected and made up to 25 ml with water and then the turbidity of these 25 ml of water is determined with a Hach turbidimeter. The turbidity found is expressed in NTU units (the lower the turbidity values, the better the resistance) and the results obtained are reported in Table 2 below.
The analysis of the results mentioned in Table 2 shows that, with respect to the coating slips prepared according to the techniques of the prior art, with an equivalent dose of ZrO2 as dry part, the insolubilizing composition C2 according to the invention makes it possible to obtain a coated paper exhibiting a better wet abrasion resistance.
Other advantages of the present invention are a very rapid preparation and only a very slight smell of ammonia in comparison with an aqueous ammonium zirconium carbonate solution.
| Number | Date | Country | Kind |
|---|---|---|---|
| 07 56550 | Jul 2007 | FR | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2008/059169 | 7/14/2008 | WO | 00 | 7/2/2010 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2009/010490 | 1/22/2009 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3298957 | Gens | Jan 1967 | A |
| 3741782 | Stewart et al. | Jun 1973 | A |
| 4021398 | Gilman et al. | May 1977 | A |
| 4061720 | Phillips | Dec 1977 | A |
| 4360507 | McArthur et al. | Nov 1982 | A |
| 4737491 | Leppavuori | Apr 1988 | A |
| 4844970 | Goldstein et al. | Jul 1989 | A |
| 5733666 | Sinko | Mar 1998 | A |
| 5759705 | Sinko | Jun 1998 | A |
| 6113989 | Sinko | Sep 2000 | A |
| 20100227074 | Trouve | Sep 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| 0004403 | Oct 1979 | EP |
| 1378117 | Nov 1964 | FR |
| 2088550 | Jan 1972 | FR |
| 2156879 | Jun 1973 | FR |
| 1001997 | Aug 1965 | GB |
| 1373634 | Nov 1974 | GB |
| Entry |
|---|
| PCT International Search Report for PCT/EP2008/059169, Jan. 23, 2009. |
| PCT International Preliminary Report on Patentability for PCT/EP2008/059169, Oct. 23, 2009. |
| PCT International Search Report for PCT/EP2008/052940, Jun. 19, 2008. |
| Written Opinion of the International Searching Authority for PCT/EP2008/052940, Jun. 19, 2008. |
| Aqueous Chemistry of Zirconium(IV) in Carbonate Media, Helvetica Chimica Acta, 83, 414-427, (2000). |
| Number | Date | Country | |
|---|---|---|---|
| 20100263573 A1 | Oct 2010 | US |