Patent Application
20100011949
This invention relates to armor panels, in particularly composite armor panels comprising one or more protective layers.
A standard armor panel of the kind to which the present invention particularly refers, comprises a multitude of layers, designed to gradually absorb the kinetic energy of the impact, delivered to the panel by an incoming projectile and finally to completely avoid penetration of the projectile or its fragments to the body to be protected.
The layers used in such armor panels may be divided into two groups: hard layers, e.g. steel or ceramic, and soft layers, e.g. Aramid or UHMW HDPE (Ultra High Molecular Weight High Density PolyEthylene). The harder layers are usually positioned facing the expected threat and absorb most of its kinetic energy thereof, thereby slowing it down and shattering and/or deforming it substantially. The softer layers absorb the remains of the kinetic energy of the projectile, stopping it and its fragments, thereby preventing them from deforming/coming in contact with the body to be protected or at least from penetrating it.
It is known in the art to use armor panels having several hard layers of different materials in order to better absorb the kinetic energy of the incoming projectile.
The choice between various materials that may constitute the hard and/or soft layers of the armor panel is affected by the required end properties of the panel, such as ballistic properties, weight, etc. Thus, for example, a hard ceramic layer may be light-weight, yet brittle, while a hard steel layer having similar ballistic properties, may be very heavy, though easy to work with.
According to the present invention, there is provided an armor panel for protecting a body from an incoming projectile having an expected impact direction, said armor panel comprising at least an armor layer made of cemented carbide in the form of metal-carbide aggregate embedded within a metal binder matrix.
The armor panel may be adapted to protect the human body, i.e. be in the form of personal armor such as a vest, or alternatively, be designed to protect a structure, mobile or immobile, adapted to house individuals to be protected, e.g. a vehicle.
The ‘metal-carbide aggregate’ should be understood as being in the form of granular/powder material, and ‘embedded within a metal binder matrix’ should be understood as being homogenously spread throughout the metal binder matrix.
It should be noted that cemented carbide may be divided into two major groups, a first group in which the cemented carbide comprises a carbide aggregate embedded within a binder matrix, and a second group in which the cemented carbide comprises an aggregate without a binder.
For the purpose of simplicity, the metal of said metal-carbide will be referred herein as ‘carbide metal’ and the metal used for said metal binder matrix will be referred herein as ‘binder metal’.
Said carbide metal and said binder metal may differ in their inherent characteristics. More particularly, the properties of said carbide and said binder metal may differ from one another. The metal of said carbide metal may be chosen from a group of refractory metals, in order to provide said cemented carbide with high hardness, high fracture toughness and a high melting point. The metal of the binder metal may be a metal having a lower hardness than that of the metal of the metal-carbide, in order to reduce the brittleness of the cemented carbide and provide it with high fracture toughness.
Cemented carbide may be manufactured by a variety of processes in solid, liquid and vapor phases as known per se, for example hot isostatic pressing (HIP) or sintering. During manufacture, binder metal and carbide are heated up until the binder metal is melted down while the aggregate remains in solid phase, thereby providing the cemented carbide with its desired morphology. This is due to the carbide having a higher melting point than that of the binder metal.
The carbide metals are so chosen as to provide the metal-carbide with relatively high density, high toughness and hardness. Thus, the metal-carbides described above may have a density ranging from 4.93÷15.8 gr/cc, a toughness ranging from 240÷550 MPa, hardness ranging from 1400÷3000 HV50and a melting point ranging from 1800÷3990° C. Fracture toughness of the above metal-carbides is relatively not high, e.g. up to about 12 Mpa*(m1/2), Some examples of such metal-carbides may be WC, TiC, TaC, NbC, ZrC, HfC, VC, Cr3C2, Mo2C etc. The cemented carbide may comprise several carbide metals forming several kinds of aggregates while using the same metal binder. Some examples of such cemented carbides may be WC—Co, WC—TiC—TaC—NbC—Co, WC—Cr3C2—Co, WC—TiC—TaC—NbC—Cr3C2—Co, TiCN—WC—TiC—TaC—NbC—Ni—Co—Mo2C—VC.
Said binder metal may have a density ranging from 7.8÷8.9 gr/cc, fracture toughness ranging up to 400 Mpa*(m1/2) which is considerably higher than that of the metal-carbides, and a melting point ranging from 1450÷1536° C. Some examples of such binder metals may be Co, Ni, Fe etc.
The binder metals listed above have an atomic weight essentially lower than that of the carbide metals, providing the cemented carbide used for the armor panel with an essentially lower overall density than a similar cemented carbide in which the metal (such as W, Ti, Nb etc.) is of an atomic weight close to that of the carbide metals.
In the cemented carbide layer, the metal-carbide aggregate may be in the form of grains homogenously spread throughout the binder. The grain size of the metal-carbide aggregate may be such that it does not exceed 20 μm per grain. For example, for grains of tungsten carbide (WC), the grain size may range between about 0.5 μm÷2.3 μm, more particularly between 0.7 μm÷2.1 μm, and still more particularly between 0.9 μm÷1.9 μm, and having an average grain size of about 1.3 μm. For grains of titanium carbide (TiC), the grain size may range between about 2.5 μm÷6.2 μm, more particularly between 2.7 μm÷6 μm, and still more particularly between 2.9 μm÷5.8 μm, and having an average grain size of about 2.7 μm.
The composition of the cemented carbide may be such that, by weight percentage, the metal carbide aggregate does not exceed 80%. The metal carbide aggregate may constitute between about 80÷96%, more particularly between about 85÷94%, and still more particularly between about 90÷92%. The metal binder matrix may be such that, by weight, does not exceed 80%. The metal binder matrix may constitute between about 4%÷20%, more particularly between about 6%÷15%, and still more particularly between about 8%÷10%.
The composition of the cemented carbide may also be such that, by volume percentage, the metal carbide aggregate does not exceed 70%. The metal carbide aggregate may constitute between about 82÷96%, more particularly between about 86÷92%, and still more particularly between about 88÷90%. The metal binder matrix may be such that, by volume, does not exceed 30%. The metal binder matrix may constitute between about 4%÷18%, more particularly between about 8%÷14%, and still more particularly between about 10%÷12%.
It should be appreciated that the cemented carbide may comprise metal carbide aggregates of various metal, for example both titanium carbide (TiC) aggregates and tungsten carbide (WC) aggregates. In this case, the composition of the cemented carbide may be such that, by weight, WC ranges between 70%÷85%, more particularly between 74%÷80%, and still more particularly between 76%÷79%. The weight percentage of the titanium carbide (TiC) may range between 10%÷20%, more particularly between 12%÷18%, and still more particularly between 14%÷16%. The weight percentage of the binder may range between 4%÷20%, more particularly between 6%÷15%, and still more particularly between 8%÷10%.
In the above case, the composition of the cemented carbide may be such that, by volume, WC may range between 50%÷65%, more particularly between 53%÷62%, and still more particularly between 56%÷60%. The volume percentage of the titanium carbide (TiC) may range between 24%÷40%, more particularly between 27%÷36%, and still more particularly between 30%÷33%. The volume percentage of the binder may range between 4%÷16%, more particularly between 6%÷14%, and still more particularly between 9%÷12%.
The said cemented carbide may have an overall density ranging from 5.5÷15.5 gr/cc, a toughness ranging from 1.7÷4.1 GPa, hardness ranging from 87÷93 HRa, and fracture toughness up to 20 Mpa*(m1/2), i.e. lower than that of the binder metal yet higher that of the metal-carbide.
It should also be understood that the above compositions are chosen specifically in order to provide the cemented carbide, on the one hand, with high hardness due to the metal-carbide aggregate, and on the other hand, high fracture toughness due to the metal-binder matrix. In particular, since the cemented carbide is used in an armor panel, the composition is chosen such that it may be adapted to withstand a high impact during a short time interval.
It should be noted that the armor panel may also comprise a layer which is partially made of cemented carbide, for example, containing cemented carbide pellets and/or tiles. The term ‘pellets’ should be understood to refer to armor elements adapted to be incorporated within the armor panel, and usually having a polygonal/cylindrical shape extending along a central axis. The design of the armor panel may be such that the pellets/tiles are incorporated within a matrix which is of different characteristics than that of the metal-binder matrix, for example, made of a light weight metal (e.g. aluminum) or a thermoplastic/thermosetic polymer (e.g. resin).
One of surprising properties that may be obtained in the cemented carbide armor layer as defined above, is that this layer, on the one hand, exhibits uniform mechanical properties as in known, and widely used in the field of armor, ceramic tiles, and on the other hand, may be essentially less brittle then these tiles (due to the inherent ductile properties of the binder metal), due to which the armor layer may have a high multi-hit capability compatible to that of an armor layer made of metal carbide pellets or armor elements within a matrix, and the ability to be processed, in particular cut, without causing its fracture, e.g. using CNC tools, to have a desired design.
Tests carried out on an armor panel having an armor layer of cemented carbide as described above, in comparison with a reference armor panel having a steel armor layer of a greater thickness than that of the cemented carbide layer and otherwise being of a design similar to that of the cemented carbide panel, exhibits penetration resistance properties similar to that of the reference panel, though at an essentially lower weight. The armor panel may comprise two or more layers which may be made of the same or different cemented carbides.
Said armor panel may comprise in addition to the at least one layer of cemented carbide, a complementary armor layer positioned in front or behind said cemented carbide layer, and/or an optional a backing layer. The additional layers may be made of any appropriate ballistic materials, such as steel, metal, ceramic or any other ballistic material.
In order to understand the invention and to see how it may be carried out in practice, embodiments will now be described, by way of non-limiting examples only, with reference to the accompanying drawings, in which:
In embodiments described below, examples of different designs of an armor panel according to the present invention are presented, including a cemented carbide layer either alone or with additional layers. Examples of materials and processes that may be used for the manufacture of the cemented carbide layer are generally presented in the Summary of Invention, whilst for the purpose of the present detailed description, one specific non-limiting example of the cemented carbide will be referred to, which is a cemented carbide produced from tungsten carbide as a metal-carbide aggregate with cobalt as a binder metal, by a process including heating up both the binder metal and the carbide to high temperatures of about 1600° C. Since the melting point of the carbide, in this case tungsten-carbide (≅1800° C.), is higher than that of the cobalt binder (≅1550° C.), the cobalt binder is melted to assume a liquid phase while the tungsten-carbide aggregate remains in solid state. This manufacturing process provides even dispersion of the aggregate within the binder and causes the resulting cemented carbide to have extremely low porosity, e.g. about 2%.
In the example shown in
For the purpose of illustrating the performance of armor panels described below, they will be compared with that of a reference armor panel RP (shown
With reference to
To compare the ballistic performance of the armor panel 1 with that of the above reference panel RP, the armor panel 1 has been produced with a thickness t of 10 mm and an areal weight w approx. 69 Kg/m2. Namely, the armor panel 1 is essentially lighter and thinner than the reference armor panel RP, the respective weight and thickness ratios m and d between the armor panels 2 and 1 being
Surprisingly, despite the above essential thickness and weight ratios d and m, respectively, the armor panel 1 has appeared to provide the same level of protection (level 3 threats according to STANAG 4569), as that of the armor panel 1 and withstand AP rounds and FSP. It should also be appreciated that the armor panel 1 may provide protection against hollow charges as well.
Turning now to
It should be noted that the terms ‘first’ and ‘second’ are used with reference to an expected impact direction of incoming projectiles, i.e. among the two layer the ‘first’ layer meets an incoming projectile before the ‘second’ layer. Hereinafter, arrow 100 denotes the expected impact direction.
The panel 1′ may for example, be produced with a thickness t′ of the first, cemented carbide layer 10 being 4 mm and a thickness T′ of the second, steel layer 20 being 5 mm. Such an armor panel 1′ has appeared to withstand the same threats as those withstood by the reference armor panel 1, whilst being essentially thinner and lighter.
With reference to
Turning now to
It should be obvious from the above test tables that the armor panel according to the present invention is capable to provide at least the same ballistic protection as the reference armor panel RP, however, with reduced overall weight and thickness.
Those skilled in the art to which this invention pertains will readily appreciate that numerous changes, variations, and modifications can be made without departing from the scope of the invention.