Patent Grant
9457496
The invention relates to the manufacture of thermally and dimensionally stable transparent polymer films. More particularly, the invention relates to the manufacture and use of aromatic polyamides, which have a rigid backbone with a glass transition temperature higher than 300° C., yet are still soluble in conventional organic solvents without the need for the presence of inorganic salts. The polymer films can be prepared by solution casting, and cured at elevated temperatures. The cured films show a high optical transparency over a range of 400˜750 nm, (transmittance >80%), a low coefficient of thermal expansion (CTE <20 ppm/° C.), and good solvent resistance.
Organic Light Emitting Diode (OLED) displays were a $1.25 billion market in 2010, which is projected to grow annually at a rate of 25%. The high efficiency and high contrast ratio of OLED displays make them a suitable replacement for liquid crystal displays (LCDs) in the mobile phone display, digital camera, and global positioning system (GPS) market segments. These applications place a premium on high electrical efficiency, compact size, and robustness. This has increased the demand for active matrix OLEDs (AMOLEDs) which consume less power, have faster response times, and higher resolutions. AMOLED innovations that improve these properties will further accelerate AMOLED adoption into portable devices and expand the range of devices that use them. These performance factors are largely driven by the processing temperature of the electronics. AMOLEDs have a thin-film transistor (TFT) array structure which is deposited on the transparent substrate. Higher TFT deposition temperatures can dramatically improve the electrical efficiency of the display. Currently, glass plates are used as AMOLED substrates. They offer high processing temperatures (>500° C.) and good barrier properties, but are relatively thick, heavy, rigid, and are vulnerable to breaking, which reduces product design freedom and display robustness. Thus, there is a demand by portable device manufacturers for a lighter, thinner, and more robust replacement. Flexible substrate materials would also open new possibilities for product design, and enable lower cost roll-to-roll fabrication.
Many polymer thin films have excellent flexibility, transparency, are relatively inexpensive, and are lightweight. Polymer films are excellent candidates for substrates for flexible electronic devices, including flexible displays and flexible solar cell panels, which are currently under development. Compared to rigid substrates like glass, flexible substrates offer some potentially significant advantages in electronic devices, including:
To facilitate these inherent advantages of a polymeric substrate for the flexible display application, several issues must be addressed including:
Several polymer films have been evaluated as transparent flexible substrates, including: polyethylene terephthalate (PET), polyethylene naphthalate (PEN), polycarbonate (PC), polyethersulfone (PES), cyclic olefin polymer (COP), polyarylates (PAR), polyimides (PI), and others. However, no one film can meet all the requirements. Currently, the industrial standard for this application is PEN film, which meets part of the requirements (Transmittance >80% between 400 nm ˜750 nm, CTE <20 ppm/° C.), but has a limited use temperature (<200° C.). A transparent polymer film with a higher thermal stability (Tg>300° C.) and a lower CTE (<20 ppm/° C.) is desirable.
Conventional aromatic polyimides are well known for their excellent thermal and mechanical properties, but their films, which must be cast from their polyamic acid precursors, are usually dark yellow to orange. Some aromatic polyimides have been prepared that can be solution cast into films that are colorless in the visible region, but such films do not display the required low CTE (For example, F. Li. F. W. Harris, and S. Z. D. Cheng, Polymer, 37, 23, pp 5321 1996). The films are also not solvent resistant. Polyimide films based on part or all alicyclic monomers, such as those described in patents JP 2007-063417 and JP 2007-231224, and publication by A. S. Mathews et al (J. Appl. Polym. Sci., Vol. 102, 3316-3326, 2006), show improved transparency. Although Tgs of these polymers can be higher than 300° C., at these temperatures the polymers do not show sufficient thermal stability due to their aliphatic units.
Fiber reinforced polymer composite films, such as reported by H. Ito (Jap. J. Appl. Phys., 45, No. 58, pp 4325, 2006), combine the dimensional stability of fiber glass in a polymer film, offering an alternative way to achieve a low CTE. However, in order to maintain a high transparency, the refractive indices of the matrix polymer and the fiber must be precisely matched, which greatly limits the choice of the matrix polymer within an organic silicon resin. By using nanoparticles as filler, the effect of lowering CTE is not significant (J M Liu, et al, J. SID, Vol. 19, No. 1, 2011)
Although most aromatic polyamides are poorly soluble in organic solvents and cannot be solution cast into films, a few polymers have been prepared that are soluble in polar aprotic solvents containing inorganic salts. Some of these have been investigated for use as flexible substrates. For example, JP 2009-79210A describes a thin film prepared from a fluorine containing aromatic polyamide that displays a very low CTE (<0 ppm/° C.), good transparency (T %>80 between 450˜700 nm), and excellent mechanical properties. However, the maximum thickness of films made from this polymer is 20 μm, because a dry-wet method where the salt is removed must be used for the film preparation. Most importantly, the film also displays poor resistance to strong organic solvents.
The present invention is directed toward transparent films prepared from aromatic copolyamides with Tgs greater than 300° C. that have CTEs less than 20 ppm/° C. The films are cast using solutions of the polyamides in N,N-dimethylacetamide (DMAc), N-methyl-2-pyrrolidinone (NMP), or other polar solvents. The present invention can be produced in the absence of an inorganic salt. Surprisingly, it was discovered that the incorporation of a few free, pendant carboxyl groups along the polyamide backbones allowed the films to be thermally cured at elevated temperatures, which greatly increased their solvent resistance.
According to one embodiment of this invention, a process is provided for manufacturing a thermally and dimensionally stable transparent aromatic copolyamide film comprising the steps of: (A) forming a mixture of two or more aromatic diamines wherein at least one of the diamines contains one or more free carboxylic acid groups, such that the amount of the carboxylic acid containing diamine is greater than approximately 1 mole percent and less than approximately 10 mole percent of the total diamine mixture; (B) dissolving the aromatic diamine mixture in a polar solvent; (C) reacting the diamine mixture with at least one aromatic diacid dichloride, wherein hydrochloric acid and a polyamide solution is generated; (D) eliminating the hydrochloric acid with a reagent; (E) casting the polyamide solution into a film; and (F) curing the film at a temperature, wherein the temperature is at least 90% of the glass transition temperature of the film. The curing process involves heating the polymer films containing a free acid group near the Tg for several minutes under an inert atmosphere or under reduced pressure. After the curing process, the film resists dissolution and/or swelling in commonly used organic solvents, including NMP, DMAc, dimethylsulfoxide (DMSO), etc. The word “eliminating” is defined to mean physically trapping, neutralizing, and/or chemically reacting the hydrochloric acid.
According to another embodiment of this invention, a transparent aromatic copolyamide film is produced having at least two repeat units of a general formula (I) and (II):
wherein n=1 to 4 (including, without limitation, 1, 2, 3, and 4), wherein Ar1 is selected from the group of aromatic units which form aromatic diacid chlorides:
wherein p=4, q=3, and wherein R1, R2, R3, R4, R5 are selected from the group comprising hydrogen, halogen (fluoride, chloride, bromide, and iodide), alkyl, substituted alkyl such as halogenated alkyls, nitro, cyano, thioalkyl, alkoxy, substituted alkoxy such as halogenated alkoxy, aryl, or substituted aryl such as halogenated aryls, alkyl ester and substituted alkyl esters, and combinations thereof. It is to be understood that each R1 can be different, each R2 can be different, each R3 can be different, each R4 can be different, and each R5 can be different. G1 is selected from a group comprising a covalent bond; a CH2 group; a C(CH3)2 group; a C(CF3)2 group; a C(CX3)2 group, wherein X is a halogen; a CO group; an O atom; a S atom; a SO2 group; a Si (CH3)2 group; 9,9-fluorene group; substituted 9,9-fluorene; and an OZO group, wherein Z is a aryl group or substituted aryl group, such as phenyl group, biphenyl group, perfluorobiphenyl group, 9,9-bisphenylfluorene group, and substituted 9,9-bisphenylfluorene. Ar2 is selected from the group of aromatic units which form diamines:
wherein p=4, wherein R6, R7, R8 are selected from the group comprising hydrogen, halogen (fluoride, chloride, bromide, and iodide), alkyl, substituted alkyl such as halogenated alkyls, nitro, cyano, thioalkyl, alkoxy, substituted alkoxy such as halogenated alkoxy, aryl, substituted aryl such as halogenated aryls, alkyl ester, and substituted alkyl esters, and combinations thereof. It is to be understood that each R6 can be different, each R7 can be different, and each R8 can be different. G2 is selected from a group comprising a covalent bond; a CH2 group; a C(CH3)2 group; a C(CF3)2 group; a C(CX3)2 group, wherein X is a halogen; a CO group; an O atom; a S atom; a SO2 group; a Si (CH3)2 group; 9,9-fluorene group; substituted 9,9-fluorene; and an OZO group, wherein Z is a aryl group or substituted aryl group, such as phenyl group, biphenyl group, perfluorobiphenyl group, 9,9-bisphenylfluorene group, and substituted 9,9-bisphenylfluorene. Ar3 is selected from the group of aromatic units which form diamines containing free carboxylic acid group:
wherein t=1 to 3, wherein R9, R10, R11 are selected from the group comprising hydrogen, halogen (fluoride, chloride, bromide, and iodide), alkyl, substituted alkyl such as halogenated alkyls like trifluoromethyl, nitro, cyano, thioalkyl, alkoxy, substituted alkoxy such as a halogenated alkoxy, aryl, substituted aryl such as halogenated aryls, alkyl ester, and substituted alkyl esters, and combinations thereof. It is to be understood that each R9 can be different, each R10 can be different, and each R11 can be different. G3 is selected from a group comprising a covalent bond; a CH2 group; a C(CH3)2 group; a C(CF3)2 group; a C(CX3)2 group, wherein X is a halogen; a CO group; an O atom; a S atom; a SO2 group; a Si (CH3)2 group; 9,9-fluorene group; substituted 9,9-fluorene; and an OZO group, wherein Z is a aryl group or substituted aryl group, such as phenyl group, biphenyl group, perfluorobiphenyl group, 9,9-bisphenylfluorene group, and substituted 9,9-bisphenylfluorene. It should be understood that the copolymer may contain multiple repeat units with structures (I) and (II) where Ar1, Ar2, and Ar3 may be the same or different.
According to yet another embodiment of this invention, a method of preparing a transparent film having a CTE less than 20 ppm/° C. that is stable for at least one hour at 300° C. comprising the steps of:
(A) reacting a mixture of aromatic diamines, in a polar solvent, wherein at least one of the diamines includes a pendant carboxylic acid group of the general formula (III):
wherein m=1 or 2, wherein t=1 to 3, wherein R9, R10, R11 are selected from the group comprising hydrogen, halogen (fluoride, chloride, bromide, and iodide), alkyl, substituted alkyl such as halogenated alkyls, nitro, cyano, thioalkyl, alkoxy, substituted alkoxy such as a halogenated alkoxy, aryl, substituted aryl such as halogenated aryls, alkyl ester, and substituted alkyl esters, and combinations thereof. It is to be understood that each R9 can be different, each R10 can be different, and each R11 can be different. G3 is selected from a group comprising a covalent bond; a CH2 group; a C(CH3)2 group; a C(CF3)2 group; a C(CX3)2 group, wherein X is a halogen; a CO group; an O atom; a S atom; a SO2 group; a Si (CH3)2 group; 9,9-fluorene group; substituted 9,9-fluorene; and an OZO group, wherein Z is a aryl group or substituted aryl group, such as phenyl group, biphenyl group, perfluorobiphenyl group, 9,9-bisphenylfluorene group, and substituted 9,9-bisphenylfluorene; with aromatic diacid chlorides to afford a copolyamide containing pendant carboxyl groups;
(B) solution casting the resulting copolyamide into a film; and,
(C) curing the film to induce solvent resistance.
Polyamides containing free pendant carboxylic groups have been prepared using 3,5-diaminobenzoic acid (DAB) or 4,4′-diaminodiphenic acid (DADP). In U.S. Pat. No. 5,160,619, polyamides containing small amounts of DAB (less than 1 mol %) useful for reverse osmosis membranes are described. In U.S. Pat. No. 5,039,785, polyamides containing more than 10 mol % DADP useful for high performance fibers are described. However, there has been no attempt to crosslink films of these polymers by heating them to temperatures near their Tgs. Even if the inventors had attempted to crosslink them in this unexpected manner, in the case of the polymers containing DAB, the carboxylic acid content would have been too low to affect cross linking, and in the case of the DADP polymers, the degree of cross linking would have been so high that the films would have been extremely brittle and unsuitable for flexible substrates.
Thus, it was surprising to find that the incorporation of about 1 mole % to about 10 mole % of a diamine, containing free carboxyl groups, in the copolyamides in this invention could allow the polymers to be crosslinked within a short period of time (minutes) when their films were heated at temperatures close to their Tgs. For example, the incorporation of these amounts of DADP or DAB resulted in films resistant to solvents commonly used in the microelectronic industry that had retained their transparency through the crosslinking process. The crosslinked films displayed high glass transition temperatures (Tg>300° C.), and low coefficients of thermal expansion (<20 ppm/° C.). Thus, the crosslinked films can be used as flexible substrates that will enable the high temperature fabrication of thin film transistors needed for a wide range of microelectronic applications, particularly for ruggedized or flexible organic light emitting diode (OLED) displays. No available material exhibits all of these properties.
The polymer substrate films in the present invention expand the utilization of AMOLEDs in portable devices by improving device electrical efficiency and the consumer experienced robustness of the display. In addition to the standard OLED display market, the substrate of the present invention will enable the development of the flexible display market. These displays can be used for conformable displays that can be integrated onto clothing, flexible e-paper and e-book displays, displays for smartcards, and a host of other new applications. For example, the polymer substrate films in the present invention can be used for flexible sensors. The new devices produced from the polymer substrate films in the present invention can dramatically impact daily life, by decreasing the cost and increasing accessibility and portability of information.
Additionally, the polymers in the present invention can be prepared in a common organic solvent at room temperature (approximately 15° C. to approximately 25° C.). These polymers can be produced in the absence of an inorganic salt. The resulting colorless and homogenous polymer solution can be used directly for subsequent film casting. No special polymerization reactor and no polymer isolation procedure is required. However, after the polymers are heated at temperatures near their Tgs for several minutes, the polymer films are inherently insoluble and chemically resistant to swelling when exposed to inorganic or organic solvents. Thus, the process is amenable to scale-up to metric ton quantities.
The polymers of the present invention are soluble in polar aprotic solvents without the need for the presence of inorganic salts. They can be solution cast in a batch process, or continuously cast directly from their polymerization mixtures and cured using a roll-to-roll process to yield free standing transparent films with thickness greater than 20 μm. Alternatively, the polymer solutions may be solution cast onto a reinforcing substrate like thin glass or a microelectronic device and cured to form films less than 20 μm. The films display high Tgs (>300° C.), low CTEs (<20 ppm/° C.), high transparencies (T>80% between 400 to 750 nm), excellent mechanical properties (tensile strengths>200 MPa), and low moisture absorptions (<2% @ 100% humidity at room temperature). Furthermore, the films show excellent chemical resistance after they are heated to temperatures of at least 90% that of their Tgs for short periods of time.
The copolyamides were prepared by polymerizing one or more aromatic diacid dichlorides as shown in the following general structures:
wherein p=4, q=3, and wherein R1, R2, R3, R4, R5 are selected from the group comprising hydrogen, halogen (fluoride, chloride, bromide, and iodide), alkyl, substituted alkyl such as halogenated alkyls, nitro, cyano, thioalkyl, alkoxy, substituted alkoxy such as a halogenated alkoxy, aryl, or substituted aryl such as halogenated aryls, alkyl ester and substituted alkyl esters, and combinations thereof. It is to be understood that each R1 can be different, each R2 can be different, each R3 can be different, each R4 can be different, and each R5 can be different. G1 is selected from a group comprising a covalent bond; a CH2 group; a C(CH3)2 group; a C(CF3)2 group; a C(CX3)2 group, wherein X is a halogen; a CO group; an O atom; a S atom; a SO2 group; a Si (CH3)2 group; 9,9-fluorene group; substituted 9,9-fluorene; and an OZO group, wherein Z is a aryl group or substituted aryl group, such as phenyl group, biphenyl group, perfluorobiphenyl group, 9,9-bisphenylfluorene group, and substituted 9,9-bisphenylfluorene.
and two or more aromatic diamines as shown in the following general structures:
wherein p=4, m=1 or 2, and t=1 to 3, wherein R6, R7, R8, R9, R10, R11 are selected from the group comprising hydrogen, halogen (fluoride, chloride, bromide, and iodide), alkyl, substituted alkyl such as halogenated alkyls, nitro, cyano, thioalkyl, alkoxy, substituted alkoxy such as a halogenated alkoxy, aryl, substituted aryl such as halogenated aryls, alkyl ester, and substituted alkyl esters, and combinations thereof. It is to be understood that each R6 can be different, each R7 can be different, each R8 can be different, each R9 can be different, each R10 can be different, and each R11 can be different. G2 and G3 are selected from a group comprising a covalent bond; a CH2 group; a C(CH3)2 group; a C(CF3)2 group; a C(CX3)2 group, wherein X is a halogen; a CO group; an O atom; a S atom; a SO2 group; a Si (CH3)2 group; 9,9-fluorene group; substituted 9,9-fluorene; and an OZO group, wherein Z is a aryl group or substituted aryl group, such as phenyl group, biphenyl group, perfluorobiphenyl group, 9,9-bisphenylfluorene group, and substituted 9,9-bisphenylfluorene.
The present invention is directed toward transparent films prepared from aromatic copolyamides. A polyamide is prepared via a condensation polymerization in a solvent, where the hydrochloric acid generated in the reaction is trapped by a reagent like propylene oxide (PrO). The film can be made directly from the reaction mixture, without the need for isolating and re-dissolving the polyamide. Colorless films can be prepared by casting procedures directly from the polymerization solutions. The product of the reaction of the hydrochloric acid with the PrO is eliminated during the removal of the solvent. These films display low CTEs as cast and do not need to be subjected to stretching. By carefully manipulating the ratio of the monomers used to prepare the copolyamides, the CTEs and Tgs of the resulting copolymers and the optical properties of their solution cast films can be controlled. It is particularly surprising that a film can be cured at an elevated temperature when free carboxylic acid side groups exist along the polymer chains. If the reaction of the reagent with the hydrochloric acid does not form volatile products, the polymer is isolated from the polymerization mixture by precipitation and re-dissolved by a polar solvent (without the need for inorganic salts) and cast in the film. If the reaction of the reagent with the hydrochloric acid does form volatile products, the film can be directly cast. One example, above, of a reagent that forms volatile products is PrO.
Representative and illustrative examples of the useful aromatic diacid dichlorides in the invention are:
Terephthaloyl dichloride (TPC);
Isophthaloyl dichloride (IPC);
2,6-Naphthaloyl dichloride (NDC);
4,4′-Biphenyldicarbonyl dichloride (BPDC)
Representative and illustrative examples of the useful aromatic diamines in the invention are:
4,4′-Diamino-2,2′-bistrifluoromethylbenzidine (PFMB)
9,9-Bis(4-aminophenyl)fluorene (FDA)
9,9-Bis(3-fluoro-4-aminophenyl)fluorene (FFDA)
4,4″-Diaminodiphenic acid (DADP)
3,5-Diaminobenzoic acid (DAB)
4,4′-Diamino-2,2′-bistrifluoromethoxylbenzidine (PFMOB)
4,4′-Diamino-2,2′-bistrifluoromethyldiphenyl ether (6FODA)
Bis(4-amino-2-trifluoromethylphenyloxyl)benzene (6FOQDA)
Bis(4-amino-2-trifluoromethylphenyloxyl) biphenyl (6FOBDA)
This Example illustrates the general procedure for the preparation of a copolymer from TPC, IPC and PFMB (70%/30%/100% mol) via solution condensation.
To a 250 ml, three necked, round bottom flask, equipped with a mechanical stirrer, a nitrogen inlet and an outlet, are added PFMB (12024 g, 0.01 mol) and dried DMAc (45 ml). After the PFMB dissolves completely, IPC (0.6395 g 0.003 mol) is added to the solution at room temperature under nitrogen, and the flask wall is washed with DMAc (1.5 ml). After 15 minutes, TPC (1.4211 g, 0.007 is added to the solution, and the flask wall is again washed with DMAc (1.5 ml). The viscosity of the solution increases until the mixture forms a gel. After adding PrO (1.4 g, 0.024 mol), the gel is broken up under stirring to form a viscous, homogenous solution. After stirring at room temperature for another 4 hours, the resulting copolymer solution can be directly cast into film.
This Example illustrates the general procedure for the preparation of a copolymer from TPC, PFMB, and FDA (100%/80%/20% mol) via solution condensation.
To a 100 ml, four necked, round bottom flask, equipped with a mechanical stirrer, a nitrogen inlet and outlet, are added PFMB (1.0247 g, 3.2 mmol), FDA (0.02788 g, 0.8 mmol), and dried DMAc (20 ml) at room temperature under nitrogen. After the PFMB dissolves completely, TPC (0.8201 g 4.04 mmol) is added to the solution, and the flask wall is washed with DMAc (5.0 ml). The viscosity of the solution increases until the mixture forms a gel. After adding PrO (0.5 g, 8.5 mmol), the gel is broken up under stirring to form a viscous, homogenous solution. After stirring for another 4 hours at room temperature, the resulting copolymer solution can be directly cast into film.
This Example illustrates the general procedure for the preparation of a copolymer from TPC, IPC, DADP, and PFMB (70%/30%/3%/97% mol) via solution condensation.
To a 250 ml, three necked, round bottom flask, equipped with a mechanical stirrer, a nitrogen inlet and outlet, are added PFMB (3.1060 g, 0.0097 mol), DADP (0.0817 g, 0.0003 mol), and dried DMAc (45 ml) at room temperature under nitrogen. After the PFMB dissolves completely, IPC (0.6091 g 0.003 mol) is added to the solution, and the flask wall is washed with DMAc (1.5 ml). After 15 minutes, TPC (1.4211 g, 0.007 mol) is added, and the flask wall is again washed with DMAc (1.5 ml). The viscosity of the solution increases until the mixture forms a gel. After adding PrO (1.4 g, 0.024 mol), the gel is broken up under stirring to form a viscous, homogenous solution. After stirring for another 4 hours at roam temperature, the resulting copolymer solution can be directly cast into film.
This Example illustrates the general procedure for the preparation of a copolymer from TPC, IPC, DAB, and PFMB (75%/25%/5%/95% mol) via solution condensation.
To a 250 ml, three necked, round bottom flask, equipped with a mechanical stirrer, a nitrogen inlet and outlet, are added PFMB (10423 g, 0.0095 mol), DAB (0.0761 g, 0.0005 mol), and dried DMAc (45 ml) at room temperature under nitrogen. After the PFMB dissolves completely, IPC (0.5076 g 0.0025 mol) is added to the solution, and the flask wall is washed with DMAc (1.5 ml). After 15 minutes, TPC (1.5227 g, 0.0075 mol) is added, and the flask wall is again washed with DMAc (1.5 ml). The viscosity of the solution increases until the mixture forms a gel. After adding PrO (1.4 g, 0.024 mol), the gel is broken up under stirring to form a viscous, homogenous solution. After stirring for another 4 hours at room temperature, the resulting copolymer solution can be directly cast into film.
It is to be understood, although the temperature provided in the examples is room temperature, the temperature range can be between approximately −20° C. to approximately 50° C., and in some embodiments from approximately 0° C. to approximately 30° C.
Preparation and Characterization of the Polymer Films
The polymer solution can be used directly for the film casting after polymerization. For the preparation of small films in a batch process, the solution is poured on a flat glass plate or other substrate, and the film thickness is adjusted by a doctor blade. After drying on the substrate, under reduced pressure, at 60° C. for several hours, the film is further dried at 200° C. under protection of dry nitrogen flow for 1 hour. The film is cured by heating at or near the polymer Tg under vacuum or in an inert atmosphere for several minutes. Mechanical removal from the substrate yields a free standing film greater than approximately 10 μm thick. The thickness of the free standing films can be adjusted by adjusting the solids content and viscosity of the polymer solution. It is to be understood that the film can be cured at any temperature between approximately 90% and approximately 110% of the Tg. It is also understood that the batch process can be modified so that it can be carried out continuously by a roll-to-roll process by techniques known to those skilled in the art.
In one embodiment of this invention, the polymer solution may be solution cast onto a reinforcing substrate like thin glass, silica, or a microelectronic device. In this case, the process is adjusted so that the final polyamide film thickness is greater than approximately 5 μm.
The CTE and Tg are measured with a thermal mechanical analyzer (TA Q 400 TMA). The sample film has a thickness of approximately 20 μm, and the load strain is 0.05N. In one embodiment, the free standing film thickness is between approximately 20 μm and approximately 125 μm. In one embodiment, the film is adhered to a reinforcing substrate and the film thickness is <20 μm. In one embodiment, the CTE is less than approximately 20 ppm/° C., but it is understood that in other embodiments, the CTE is less than approximately 15 ppm/° C., less than approximately 10 ppm/° C., and less than approximately 5 ppm/° C. It is to be understood that within these embodiments the CTE can be less than approximately 19, 18, 17, 16, 15, 14, 13, 12, 11, 10, 9, 8, 7, 6, or 5 ppm/° C. The experimentally derived CTEs are the average of the CTE obtained from room temperature to about 250° C.
Film transparency is measured by determining the transmittance of a 10 μm thick film from 400 to 750 nm with a UV-Visible spectrometer (Shimadzu UV 2450).
The solvent resistance of the film is determined by immersing it in a selected solvent for 30 minutes at room temperature. The film is considered solvent resistant if it is substantially free of surface wrinkles, swelling, or any other visible damage after immersion. The films are useful as substrates for flexible electronic devices.
To determine the ratio of reactants necessary to obtain a soluble copolyamide that can be solution cast into a colorless film with a Tg>300 C, a CTE <20 ppm, and a transmittance >80% from 400 to 750 nm, a preliminary study can be conducted where the amount of reactants that do not contain free carboxyl groups are varied in a systematic manner. The properties of the films of the copolymers obtained are measured in order to determine suitable copolymer candidates (base polymers) for the incorporation of free carboxyl groups. Such studies are well understood by those skilled in the art. The following tables show comparative examples of the such studies used to determine some on the base polymers utilized in the present invention.
To determine the minimum amount of carboxyl groups necessary to thermally crosslink the copolymer without significantly changing the properties, a second preliminary study can be conducted where various amounts of a reactant containing free carboxyl groups are copolymerized with the mixture of reactants used to prepare the base polymer. Films of the copolymers obtained and their properties determined. For example, various amounts of DADP were copolymerized with the reactants used in the preparation of the base polymer made from a mixture of TPC, IPC and PFMB in a 70/30/100 ratio (Example 1). The films of the copolymers obtained containing DADP were thermally treated at 330° C. for 5 minutes. After curing, the film resistance to NMP was evaluated. The results are shown in Table 3.
The properties of polymer films based on Example 3 after curing are shown in Table 4. The composition of a copolymer containing DAB (Example 4), which was determined in an analogous manner, is also shown in Table 4 along with the properties of cured films of this polymer.
The cured films of this invention are resistant to both inorganic and organic solvents. The film solvent resistance can be evaluated quickly by analyzing the resistance to NMP, a commonly used strong solvent. It has been found that films resistant to this solvent are also resistant to other polar solvents.
The following are exemplary polymers that can be used in this invention—1) about 50 to about 70 mol % TPC, about 30 to about 50 mol % IPC, about 90 to about 99 mol % PFMB, and about 1 to about 10 mol % 4,4′-Diaminodiphenic acid (DADP); 2) about 50 to about 70 mol % TPC, about 25 to about 50 mol % IPC, about 90 to about 96 mol % PFMB, and about 4 to about 10 mol % 3,5-diaminobenzoic acid (DAB); 3) about 100 mol % TPC, about 25 to about 85 mol % PFMB, about 15 to about 50 mol % 9,9-Bis(4-aminophenyl)fluorine (FDA), and about 1 to about 10 mol % DADP; and 4) about 100 mol % TPC, about 50 to about 85 mol % PFMB, about 15 to about 50 mol % FDA, and about 4 to about 10 mol % DAB.
The embodiments have been described, hereinabove. It will be apparent to those skilled in the art that the above methods and apparatuses may incorporate changes and modifications without departing from the general scope of this invention. It is intended to include all such modifications and alterations insofar as they come within the scope of the appended claims or the equivalents thereof. Although the description above contains much specificity, this should not be construed as limiting the scope of the invention, but as merely providing illustrations of some of the embodiments of this invention. Various other embodiments and ramifications are possible within its scope.
Furthermore, notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contain certain errors necessarily resulting from the standard deviation found in their respective testing measurements.
This application claims priority to a provisional patent application Ser. No. 61/466,751, entitled AROMATIC POLYAMIDE FILMS FOR TRANSPARENT FLEXIBLE SUBSTRATES, filed Mar. 23, 2011, the contents of which are incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3386965 | Huffman et al. | Jun 1968 | A |
| 4461886 | Rogers et al. | Jul 1984 | A |
| 5026819 | Irwin | Jun 1991 | A |
| 5039785 | Irwin | Aug 1991 | A |
| 5160619 | Yamaguchi et al. | Nov 1992 | A |
| 5189141 | Irwin | Feb 1993 | A |
| 5189538 | Arakawa | Feb 1993 | A |
| 5212258 | Irwin | May 1993 | A |
| 5290887 | Hefner et al. | Mar 1994 | A |
| 5292856 | Irwin | Mar 1994 | A |
| 5387657 | Hefner et al. | Feb 1995 | A |
| 5396355 | Wada et al. | Mar 1995 | A |
| 5427712 | Nakamura et al. | Jun 1995 | A |
| 5529818 | Tsuda et al. | Jun 1996 | A |
| 5532322 | Kadono et al. | Jul 1996 | A |
| 5580950 | Harris et al. | Dec 1996 | A |
| 5677390 | Dadgar et al. | Oct 1997 | A |
| 5698676 | Dhaon | Dec 1997 | A |
| 6115095 | Suzuki et al. | Sep 2000 | A |
| 6175400 | Duncan et al. | Jan 2001 | B1 |
| 6881454 | Taguchi | Apr 2005 | B2 |
| 7037443 | Shuto et al. | May 2006 | B2 |
| 7061081 | Yano et al. | Jun 2006 | B2 |
| 7135211 | Shuto et al. | Nov 2006 | B2 |
| 7227602 | Jeon et al. | Jun 2007 | B2 |
| 7236221 | Ishikawa et al. | Jun 2007 | B2 |
| 8664335 | Koros et al. | Mar 2014 | B2 |
| 20020041352 | Kazuhara et al. | Apr 2002 | A1 |
| 20040051831 | Su Yu et al. | Mar 2004 | A1 |
| 20050057714 | Jeon et al. | Mar 2005 | A1 |
| 20050105027 | Wada et al. | May 2005 | A1 |
| 20050200792 | Jeon et al. | Sep 2005 | A1 |
| 20050270458 | Ishikawa et al. | Dec 2005 | A1 |
| 20060062935 | Murakami | Mar 2006 | A1 |
| 20060106193 | Toray | May 2006 | A1 |
| 20060114383 | Kobayashi et al. | Jun 2006 | A1 |
| 20070020407 | Umemoto et al. | Jan 2007 | A1 |
| 20070046870 | Murakami et al. | Mar 2007 | A1 |
| 20080239491 | Zheng et al. | Oct 2008 | A1 |
| 20080241565 | Germroth et al. | Oct 2008 | A1 |
| 20090318660 | Bos et al. | Dec 2009 | A1 |
| 20110034666 | Bos et al. | Feb 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 101511938 | Aug 2009 | CN |
| 06 103 79 | Jul 1998 | EP |
| 1 506 991 | Feb 2005 | EP |
| 04 215 602 | Aug 1992 | JP |
| 2000 273 168 | Oct 2000 | JP |
| 2005206846 | Aug 2005 | JP |
| 2007 046 059 | Feb 2007 | JP |
| 2007-063417 | Mar 2007 | JP |
| 2007-231224 | Sep 2007 | JP |
| 2009-067834 | Apr 2009 | JP |
| 2009-079210 | Apr 2009 | JP |
| I287030 | Jan 2006 | TW |
| 2008-044 851 | Apr 2008 | WO |
| 2008 121 584 | Oct 2008 | WO |
| 2010005734 | Jan 2010 | WO |
| Entry |
|---|
| José M. García, Félix C. García, Felipe Serna, José L. de la Peña, High-performance aromatic polyamides, Progress in Polymer Science, vol. 35, Issue 5, May 2010, pp. 623-686, ISSN 0079-6700, http://dx.doi.org/10.1016/j.progpolymsci.2009.09.002. |
| Zhang, D., et al., “Mesogen-Jacketed Liquid Crystal Polymers with Mesogens of Aromatic Amide Structure” Polymers for Advanced Technologies, Wiley & Sons, Bognor Regis, GB, vol. 18, No. 4, Apr. 1, 1997, pp. 227-233, XP000691535. |
| Zhang, et al., “Synthesis of a New Side-Chain Type Liquid Crystal Polymer Poly[dicyclohexyl vinylterephtalate]” Macromolecules, ACS, Washington, DC, U.S., vol. 32, Jan. 1, 1999, pp. 4494-4496, XP002495422, ISSN: 0024-9297. |
| Zhao, et al., Synthesis and Characterization of Diblock Copolymers Based on Crystallizable Poly(e-caprolactone) and Mesogen-Jacketed Liquid Crystalline Polymer Block: Polymer, Elsevier Science Publishers B.V., GB, vol. 46, No. 14, Jun. 27, 2005, pp. 5396-5405, XP004924379, ISSN: 0032-3861. |
| Li, et al., “Hierarchical Assembly of a Series of Rod-Coil Block Copolymers: Supramolecular LC Phase in Nanoenvironment” Macromolecules 2004, vol. 37, No. 8, pp. 2854-2860. |
| Luo, et al., “Conduction Mechanism in a Novel Oxadiazole Derivative: Effects of Temperature and Hydrostatic Pressure” J. Phys. D: Appl. Phys. vol. 38, 2005, pp. 1132-1135, IOP Publishing Ltd. Printed in the UK. |
| Ito, H.; Oka, W.; Goto, H.; Umeda, H.; Plastic Substrates for Flexible Displays, JP Journal of Applied Physics, vol. 45, No. 5B, 2006, pp. 4325-4329. |
| Li, F.; Harris, F.W.; Cheng, S.Z.D.; Polyimide Films as Negative Birefringent Compensators for Normally White Twisted Nematic Liquid Crystal Displays, Polymer vol. 37, No. 23, 1996, pp. 5321-5325. |
| Matthews, A. S.; Kim, I.; Ha, C.S.; Fully Aliphatic Polyimides From Adamantane-Based Diamines For Enhanced Thermal Stability, Solubility, Transparency, and Low Dielectric Constant, Dept. of Polymer Science and Engineering, Pusan National University, Busan, 2006, pp. 609-735, Korea. |
| Mehdipour-Antaei, S.; Babanzadeh, S.; New Types of Heat-Resistant, Flame-Retardant Ferrocene-Based Ployamides With Improved Solubility, Iran Polymer and Petrochemical Institute, P.O. Box 14965/115, Tehran, Iran (Available at ScienceDirect, Reactive & Functional Polymers 67, 2007, pp. 883-892. |
| Liou, G.S.; Hsiao, S.H.; Ishida, M.; Kakimoto, M.; Imai, Y.; Synthesis and Characterization of Novel Soluble Triphenylamine-Containing Aromatic Polyamides Based on N,N′-BIS(4-Aminophenyl)-N,N′-Diphenyl-1,4-Phenylenediamine; Journal of Polymer Science; Part A: Polymer Chemistry, vol. 40, 2002, pp. 2810-2818. |
| Phillips, R.E.; Soulen, R.L.; Propylene Oxide Addition to Hydrochloric Acid, Journal of Chemical Education, vol. 72, No. 7, Jul. 1995, pp. 624-625. |
| Seo, K.B.; Jeong, J.K.; Choi, S.J.; Hong, Y.T.; Suh, D.H.; Synthesis and Characterization of Novel Aromatic-Aliphatic Poly(Amide-Imide-Imide)S (PAII), Die Angewandte Makromolekulare Chemic 264, 1999, oo, pp. 30-38, (Mr 4590). |
| Ebadi, H.; Mehdipour-Ataei, S.; Heat-Resistant, Pyridine-Based Polyamides Containing Ether and Ester Units With Improved Solubility, Chinese Journal of Polymer Science, vol. 28, No. 1, 2010, pp. 29-37. |
| Mehdipour-Ataei, S.; Hatami M.; Mosslemin, M.H.; Organosoluble, Thermally Stable Polyamides Containing Sulfone and Sulfide Units, Chinese Journal of Polymer Science, vol. 27, No. 6, 2009, pp. 781-787. |
| Chai, C.; Wang, J.; Fan, X.; Chen, X.; Zhou, Q.; Synthesis and Characterization of Mesogen Jacketed Liquid Crystalline Polymer Containing 1, 3, 4-Oxadiazole, Beijing National Laboratory for Molecular Science, Key Laboratory of Polymer Chemistry and Physics of Ministry of Education College of Chemistry and Molecular Engineering, Peking University, Beijing, 2006, 532-535. |
| Liu, J.M.; Lee, T.M.; Wen, C.H.; Leu, C.M.; High Performance Organic-Inorganic Hybrid Plastic Substrate for Flexible Display and Electronics, MCL, Industrial Technology Research Institute, Chutung, Hsinchu, 310 Taiwan, ROC, SID 10 Digest, pp. 913-916. |
| Office Action issued on Aug. 13, 2014 at Taiwan Patent Office, pp. 1-5. |
| Kratochvil, AM; Koros, WJ, “Decarboxylation-Induced Cross-Linking of a Polyimide for Enhanced CO2 Plasticization Resistance”, pp. 7920-7927, Macromolecules, 2008. Amer. Chem. Society. |
| Chien-Chiang, et al “Plasticization-resistant hollow fiber membranes for CO2/CH4 separation based on a thermally crosslinkable polyimide”, pp. 212-221, Journal of Membrane Science 382 (2011). |
| Chien-Chang, et al. “Characterization of Thermally Cross-Linkable Hollow Fiber Membranes for Natural Gas Separation”, pp. 1015-1022, ACS Publications, American Chemical Society (2012). |
| SIPO of P.R. China—Notification of First Office Action dated Jul. 15, 2015 from CN application No. 201280022302.8, filed Mar. 22, 2012, pp. 1-4. |
| Number | Date | Country | |
|---|---|---|---|
| 20120244330 A1 | Sep 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61466751 | Mar 2011 | US |