Patent Application
20120196188
The invention relates to membrane in an acidic electrolyte flow battery. More specifically, the invention is related to an aromatic polymer ion exchange membrane and its composite membrane and their applications in acidic electrolyte flow batteries.
Flow batteries with an acidic electrolyte is a new technology in the field of electrochemical energy storage. The advantages include high conversion efficiency, flexible system design, large storage capacity, flexibility in site selection, deep discharge, safe and environmentally friendly, and low maintenance cost, etc. It is one of the preferred technologies for the large scale and high efficiency energy storage. In particular, since the vanadium redox flow battery (VRB) has the advantages of high security, strong stability, high efficiency, long operating life (above 15 years) and low cost, etc., it has been considered as the most promising and representative among flow batteries.
The ion exchange membrane is the key component in a flow battery. It separates the positive and negative electrolytes while serves as the conduit for transporting ions between the positive and the negative electrolyte. Therefore, the ion exchange membrane is required to have a high ionic conductivity, ion selectivity and good chemical stability. After evaluating some commercial membranes, Skyllas-kazacos et al. found that with the exception that the comprehensive property of some perfluorosulfonic polymers is stable enough, other membranes (such as Selemion CMV, CMS, AMV, DMV, ASS and DSV etc.) are not stable enough in acid vanadium solution (J. Appl Electrochem, 2004, 34 (2): 137). However, studies found that even though the commercial perfluorosulfonic polymer possesses high mechanical strength and chemical stability, the permeation rate of vanadium ions when used in VRB is high. There is also obvious water migration between the anode and cathode during charge-discharge cycles. Moreover, the complex production technology, severe preparation conditions and high cost in making perfluorosulfonic polymers have severely limited the application and commercialization of VRB.
Since the aromatic polymer ion exchange membrane with nitrogen heterocycles has excellent mechanical stability, thermal stabilty and chemical stability, it has received wide-spread attention in different fields.
The present invention relates to a class of aromatic polymer ion exchange membrane and its composite membranes in the acidic electrolyte flow battery applications, particularly their applications in VRBs. This type of polymer has aromatic nitrogen heterocycles that can interact with acid and form a donor—acceptor mesh structure. The network structure can transport protons and maintain the ionic conductivity of the membrane. This type of membrane materials has excellent thermal stability, chemical stability and good ionic conductivity. It can be used in many applications, particularly suitable for use as the ion-exchange membrane in the acidic electrolyte flow battery.
The present invention discloses nitrogen heterocyles aromatic polymers that are aromatic polymers containing nitrogen heterocycles, including one or more homopolymers or copolymers of benzimidazole, vinyl imidazole, pyridine, vinyl pyridine, pyrazole, pyrimidine, thiazole, benzothiazole, oxazole, benzoxazole, oxadiazole, quinoline, quinoxaline, thiadiazole, and purine. The following are the structures of some of the polymers:
wherein n is a positive integer, 10≦n≦200, R1 is one of the following structures.
R2 is chosen from hydrogen, saturated C1-C4 alkyl groups, or C2-C4 alkenyl groups.
The above-described aromatic polymers containing nitrogen heterocycles in this invention include both homopolymers and copolymers. The present invention uses polybenzimidazole (PBI) as an example and explain its structure in details.
Said homopolymer of PBI has the following structural formula:
Said copolymer of PBI has the following structural formula:
wherein x is a positive integer, 10≦x≦200; R1, R3 and R4 refer to one of the following structures:
R2 and R5 are selected from hydrogen, C1-C4 alkyl groups, or C2-C4 alkenyl groups. wherein m and n are molar fractions of corresponding units, 0<n≦0.8, 0.2≦m<1, m+n=1.
Said homopolymer of PBI is poly(aryl ether benzimidazoles), whose structural formula is as follows:
wherein R1 is one of the following:
wherein R2 represents one of the following:
The above-described copolymer of PBI is an ion exchange membrane of PBI containing pyridine groups, whose structural formula is as follows:
The polymer is a random copolymer, wherein x is a positive integer, 10≦x≦200; wherein m and n respectively are molar percentage of different structural units, 0<n≦0.8, 0.2≦x<1, m+n=1. The weight average molecular weight of this type of polymer is between 5,000 to 800,000. Wherein R1 represents one of the followings:
R2 represents one of the followings:
Wherein R3 and R4 are selected from hydrogen, C1-C4 alkyl groups, or C2-C4 alkenyl groups, R3 and R4 can be the same or different.
In addition, the copolymer disclosed in this invention can be random copolymers or block copolymers. Furthermore, the copolymer disclosed herein can also be copolymers of nitrogen heterocycles, such as the copolymer of poly-oxadiazole and PBI, or the copolymer of poly-triazole and PBI, etc, but not limited to the following structures:
wherein n is a positive integer, 10≦n≦200, R1 represents one of the followings:
R2 is selected from hydrogen, C1-C4 alkyl groups, or C2-C4 alkenyl groups.
The nitrogenous heterocyclic aromatic polymers disclosed in this invention are obtainable by nucleophilic polycondensation reaction [Progress in Polymer Science 34 (2009) 449-477].
The ion-exchange membranes are obtained using above-described polymer by solution casting. Its method of preparation can be found in the relevant patents or in the literature. Appropriate solvents are selected for various polymers according to their solubility. Dissolving the polymer to form a polymer solution then casting the solution directly on a glass plate or other flat-panel, drying and evaporation at a certain temperature to obtain an aromatic polymer ion exchange membrane. Immersing the aromatic polymer ion exchange membrane in an strong acid solution with a concentration of 0.1-25 mol/L, soaking time 0.05-1000 h, the solution temperature at 5-100° C., the thickness of aromatic polymer ion exchange membrane is 0.1 to 200 microns. After acid doping, each repeating unit in the polymer comprises one or more acid molecules.
Said organic-inorganic composite ion exchange membrane, wherein the organic phase is a PBI type polymer, whose structural formula is as follows:
n is a positive integer, 10≦n≦200, R represents one of the followings:
wherein R1 and R2 respectively are selected from hydrogen, C1-C4 alkyl groups, or C2-C4 alkenyl groups, R1 and R2 can be the same or different.
The organic-inorganic composite membrane is obtainable by common solution casting wherein the inorganic particles can be obtained by direct blending or by in situ sol-gel method, but not limited to these two methods.
In addition to having a polymer containing nitrogen heterocycles, the organic-inorganic composite membrane also contains another class of polymer that comprises sulfonic acid, such as one or more among perfluorinated sulfonic acid polymer, sulfonated polysulfone, sulfonated polypropylene, sulfonated poly (ether sulfone), sulfonated poly (ether sulfone), sulfonated poly aryl sulfone, sulfonated polyphenylene ether, sulfonated polyether ether ketone, sulfonated poly (aryl ether ketone). The sulfonated polymer accounts for 0.1 to 50% of the aromatic polymer, which is used in preparing organic-inorganic ion exchange membrane. Immersing the ion exchange membrane in a strong acid solution having a concentration of 0.1-25 mol/L, soaking for 0.05-1000 h, solution temperature of 5-100° C., and the thickness of the aromatic polymer ion exchange membrane is 0.1 to 200 microns. After acid doping, each repeating unit in the polymer has one or more acid molecules. The unique feature of this composite membrane is that it utilizes the interaction between the sulfonic groups and nitrogen heterocycles, effectively avoiding the permeation of ions and therefore improving the selectivity of the membrane particles.
The beneficial effects of the present invention include:
1) The present invention discloses using aromatic polymer membrane as the ion exchange membrane in the acidic electrolyte flow battery. The membrane uses acidic electrolyte as a conductive medium, acid and nitrogen heterocycles in the polymer form the structure of the receptor, and directional hopping mechanism (Grotthuss hopping mechanism) to conduct protons (see Scheme 1). It has very low water migration and very high ion selective permeability in the proton transfer process, which greatly reduces the uneven distribution of the positive and negative electrolyte and the self-discharge phenomenon, effectively extending the life of the electrolyte. The ion exchange membrane material prepared according to this invention can be easily made into membranes.
2) The ion exchange membrane prepared according to this invention has excellent thermal stability, mechanical stability and oxidation stability.
3) The membrane used in this invention has good structural stability, low cost, suitable for long and stable application in acidic electrolyte flow battery and large-scale commercial development.
4) The ion-exchange membrane prepared according to this invention has excellent ion conductivity.
5) The ion-exchange membrane prepared according to this invention has a good ion-selectivity and can avoid cross-contamination between the positive and negative electrolyte in acid flow battery.
6) The organic-inorganic composite ion-exchange membrane prepared according to this invention can effectively improve the ionic conductivity, and to maintain high ion selectivity.
7) The organic-organic composite ion-exchange membrane prepared according to this invention can effectively improve the mechanical and chemical stability of the membrane.
The following embodiments further illustrate this invention and do not limit scope the invention.
Dupont's Nafion 115 membrane was used to assemble a VBR. Activated carbon felt was the electrode and graphite plates were used as bipolar plates. The active area of the membrane was 9 cm2, the current density was 80 mA/cm2. Vanadium concentration in the electrolyte was 1.50 mol/L, H2SO4 concentration was 3 mol/L. The coulombic efficiency of the flow battery was 94.8% and the voltage efficiency was 88.9%. The energy efficiency was 84.5%.
1 g PBI (Mw=˜50,000) with the following structure was dissolved in N,N-dimethylacetamide (DMAc) to form 5 wt. % polymer solution. The solution was cast on a glass substrate and passed through a coating knife. After heated at 80° C. for 20 hours, the membrane was peeled from the glass substrate. The dried membrane was soaked in 4M H2SO4 solution for 5 hours at room temperature. The membrane was assembled in a VRB single cell with carbon felt electrodes and graphite current collectors. The concentrations of vanadium ions and H2SO4 in the electrolyte solution were 1.5 M and 3 M, respectively. The active area of the membrane was 9 cm2 and the testing current density was 80 mA cm−2. The coulombic efficiency (CE), voltage efficiency (VE) and energy efficiency (EE) were 99.34%, 82.17% and 81.6%, respectively. As shown in
In this example, n represents the structural unit amounts of polymer, 10≦n≦200.
3.4 g P2O5 was dissolved in 34 g phosphoric acid. The solution was poured into a 500 mL three-neck round-bottom flask and kept stirring as temperature increased. After the solution became transparent, 6 mmol 3,3′,4,4′-biphenyltetramine and 6 mmol 4,4′-dicarboxydiphenyl ether (DPE) were added into the solution. The temperature of the solution was increased to 200° C. After 20 hours, the polymer solution was cooled and poured into 5 wt. % NaOH aqueous solution. In the alkali solution, the polymer was precipitated and the acid was neutralized for 24 hours. Afterward, the polymer resin was washed with deionized water to remove the residual alkali. The polymer resin was then dried and dissolved in DMSO to form 4 wt. % solution. The solution was cast on a glass substrate and passed through a coating knife. After heating at 80° C. for 20 hours, the membrane was peeled from the substrate. The dried membrane was soaked in 4M H2SO4 solution for 5 hours at room temperature. The obtained ion exchange membrane had a thickness of about 35 μM. The chemical structure of the as-prepared polymer PBI is illustrated as follow:
In this example, n is the degree of polymerization, 10≦n≦200.
The IR spectrum of PBI is shown in
The PBI membrane was assembled in a VRB single cell with carbon felt electrodes and graphite current collectors. The concentrations of vanadium ions and H2SO4 in the electrolyte solution were 1.5 M and 3 M, respectively. The active area of the membrane was 9 cm2 and the testing current density was 80 mA cm−2. The CE, VE and EE were 99.2%, 80.6% and 80.2%, respectively. As shown in
Same as in Example 2 except that: 1) The polymer was the following and its weight average molecular weight was about 50,000; 2) The solvent used in the polymerization reaction is methansulfonic acid; and 3) cast solution was heated at 140° C. to form the membrane.
In this example, n is the degree of polymerization, 10≦n≦200.
Same as in Example 3 except that the chemical structure of the PBI polymer was as follows, the weight average molecular weight was 70000, the polymer solution was in methansulfonic acid, and the evaporation temperature was 140° C.:
In this example, n is the degree of polymerization, 10≦n≦200.
Same as in Example 3 except that the chemical structure of the PBI polymer was as follows, the weight average molecular weight was 40000, the polymer solution was in methansulfonic acid, and the evaporation temperature was 140° C.:
In this example, n is the degree of polymerization, 10≦n≦200.
3.4 g P2O5 was dissolved in 34 g phosphoric acid (PPA). The solution was poured into a 500 mL three-neck round-bottom flask and kept stirring as temperature increased. After the solution became transparent, 6 mmol 3,3′,4,4′-biphenyltetramine, 1.2 mmol 2,6-pyridine dicarboxylic acid and 4.8 mmol 4,4′-oxybisbenzoic acid were added into the solution. The temperature of the solution was increased to 200° C. After 20 hours, the polymer solution was cooled and poured into 5 wt. % NaOH aqueous solution. In the alkali solution, the polymer was precipitated and the acid was neutralized for 24 hours. Afterward, the polymer resin was washed with deionized water to remove the residual alkali. The polymer resin was then dried and dissolved in DMSO to form 4 wt. % solution. The solution was cast on a glass substrate and passed through a coating knife. After heating at 80° C. for 20 hours, the membrane was peeled from the glass substrate. The dried membrane was soaked in 4M H2SO4 solution for 5 hours at room temperature. The obtained PBI ion exchange membrane contained 20 wt % pyridine and had a thickness of about 35 μm and a weight average molecular weight of about 60,000.
The IR spectrum of PBI is shown in
In this example, m and n are the molar ratios of corresponding chemical units (0<n≦0.8, 0.2≦m<1, m+n=1).
The PBI membrane was assembled in a VRB single cell with carbon felt electrodes and graphite current collectors. The concentrations of vanadium ions and H2SO4 in the electrolyte solution were 1.5 M and 3 M, respectively. The efficient area of the membrane was 9 cm2 and the testing current density was 80 mA cm−2. The CE, VE and EE were 99.3%, 86.2% and 85.6%, respectively. As shown in
Same as in Example 6 except that the chemical structure of the polymer was as follows:
In the example, m and n are the molar ratios of corresponding chemical units (0<n≦0.8, 0.2≦m<1, m+n=1).
Same as in Example 7 except that the polymer was a PBI copolymer having a structure as follows:
In the example, m and n are the molar ratios of corresponding chemical units (0<n≦0.8, 0.2≦m<1, m+n=1).
Same as in Example 8 except that the polymer was a PBI copolymer having a structure as follows:
In the example, m and n are the molar ratios of corresponding chemical units (0<n≦0.8, 0.2≦m<1, m+n=1).
Hydrazide Sulfate (HS) was dissolved in PPA at a molar ratio of 1:10. The solution was poured into a 500 mL three-neck round-bottom flask and heated to 160° C. DPE was then added in the solution (molar ratio nHS:nDPE=1:1.2). The polymerization reaction proceeded for 4 hours. After cooling, the polymer solution was poured into 5 wt. % NaOH aqueous solution. In the alkali solution, the polymer precipitated and the acid was neutralized for 24 hours. The obtained polymer resin was washed with deionized water to remove the residual alkali. The polymer resin was filtered and dried. The average molecular weight of the polymer obtained was about 100,000. The polymer was dissolved in N-methyl-2-pyrrolidone (NMP) to form 5 wt. % solution. The solution was cast on a glass substrate and passed through a coating knife. After heated at 80° C. for 20 hours, the membrane was peeled up from the substrate. The dried membrane was soaked in 4M H2SO4 solution for 5 hours at room temperature. The ion exchange membrane of poly (4,4′-diphenylether-1,3,4-oxadiazole) (POD-DPE) thus obtained had a thickness of about 25 μm. The 1H NMR spectrum of POD-DPE is shown in
The POD-DPE membrane was assembled in a VRB single cell with carbon felt electrodes and graphite current collectors. The concentrations of vanadium ions and H2SO4 in the electrolyte solution were 1.5 M and 3 M, respectively. The active area of the membrane was 6 cm2 and the testing current density was 50 mA cm−2. The CE, VE and EE were 97.9%, 83.6% and 81.9%, respectively. As shown in
In this example, n is the degree of polymerization, 10≦n≦200.
Same as in Example 10 except that the polymer was polyvinyl imidazole.
Same as in Example 11 except that the polymer was the copolymer of poly-oxadizole and PBI.
In this example, m and n are the molar ratios of corresponding chemical units (0<n≦0.8, 0.2≦m<1, m+n=1).
0.2 g SiO2 nano particles were dissolved in 20 ml DMSO and poured into a 250 ml conical flask. 1 ml Tween 80 was added in the solution, followed by stirring for 1 hour to obtain a transparent solution. 2 g PBI resin, with the structure described in Example 2, was added in the solution and kept stirring at 50-100° C. until the solution turned clear. The solution was cast on a glass substrate and passed through a coating knife. After heating at 80° C. for 20 hours, the membrane was peeled from the substrate. The dried composite membrane was soaked in 4M H2SO4 solution for 5 hours at room temperature. The obtained a composite ion exchange membrane had a thickness of about 35 μm.
The composite membrane was assembled in a VRB single cell with carbon felt electrodes and graphite current collectors. The concentrations of vanadium ions and H2SO4 in the electrolyte solution were 1.5 M and 3 M, respectively. The active area of the membrane was 9 cm2 and the testing current density was 80 mA cm−2. The CE, VE and EE were 99.3%, 83.6% and 84.2%, respectively. As shown in
Same as in Example 13 except that the inorganic particles were TiO2.
Same as in Example 14 except that the inorganic particles were ZrO2.
PBI was dissolved in DMAc to form a 10 wt. % polymer solution, followed by blending it with Nafion® resin of Na+ form. The blends solution was evaporated at 60° C. to obtain a polymer membrane. The polymer membrane was heated at 160° C. in vacuum oven for 3 hours. The heat-treated membrane was peeled off and soaked in deionized water for 100 hours to remove impurities. Then the membrane was soaked in 5M H2SO4 solution for 48 hours at room temperature.
Same as in Example 16 except that the sulfonated resin used was poly(aromatic ether ketone).
Same as in Example 17 except that the sulfonated resin was sulfonated poly(aromatic ether sulfone). Same as in Example 17 except that the sulfonated resin was sulfonated poly(phenylene oxide).
Same as in Example 16 except that the sulfonated resin was poly(propylene).
The structural feature of the ion exchange membrane of this invention lies in the aromatic polymer with nitrogen heterocycles, especially polybenzimidazole type polymer. The nitrogen heterocycles in the structure interact with acid in the electrolyte to form donor-receptor proton transport network, so as to maintain the proton transport performance of the membrane. The preparation condition for such ion exchange membranes is mild and the process is simple. The preparation method is suitable for mass production. The invention in particular relates to the application of such membranes in acidic electrolyte flow battery, especially in VRB. The prepared membrane has excellent mechanical stability and thermostability. In VRB, the membrane has excellent proton conduction and excellent resistance to the permeation of vanadium ions.
| Number | Date | Country | Kind |
|---|---|---|---|
| 200910187902.X | Oct 2009 | CN | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/CN2010/074501 | 6/25/2010 | WO | 00 | 3/14/2012 |