The present application claims the benefit of Chinese Patent Application No. 201610276100.6, filed on Apr. 29, 2016, the entire disclosure of which is incorporated herein by reference.
The present disclosure generally relates to the field of display technology, and more particularly to an array substrate, a display panel comprising the array substrate and a display device, as well as a manufacturing method of the array substrate.
When manufacturing an array substrate of a display device, a metal pattern such as a signal line, a source/a drain, or the like is usually made of a metal such as aluminum or copper, and layers such as a gate insulating layer, an etching stop layer, a passivation layer, or the like are formed on the metal pattern, and then dry etching is performed on the respective layers on the metal pattern at positions corresponding to the metal pattern using a gas such as oxygen to form connection holes for exposing the metal pattern so as to electrically connect the metal pattern from the outside. However, under the conditions of dry etching, the gas such as oxygen for drying etching may react with the metallic material of the metal pattern, resulting in occurrence of a bulge-like defect in the metal pattern. It has been found in the subsequent processes that the bulge-like defect may cause a series of problems such as pad erosion, failure in bonding, and the like. Unfortunately, the bulge-like defect is difficult to improve by changing the conditions of dry etching, which will seriously affect the quality of the final product and reduce the yield of the final product.
In view of the above, there is a need in the art for providing an improved array substrate of a display device.
It is an objective of the present disclosure to provide an array substrate, a display panel comprising the array substrate and a display device, as well as a manufacturing method of the array substrate, which can at least partially alleviating or eliminating one or more of the problems in the prior art as mentioned above.
According to a first aspect of the present disclosure, there is provided an array substrate comprising a base substrate, a metal layer arranged over the base substrate, a conductive material layer arranged on the metal layer, and a connection hole arranged over the conductive material layer to expose the conductive material layer.
In the above-described array substrate, by arranging the conductive material layer on the metal layer, during the process of etching the layers such as a gate insulating layer, a passivation layer and the like over the metal layer to form the connection hole, the conductive material layer protects the metal layer from being affected by etching, which consequently reduces or even avoids occurrence of a bulge-like defect in the metal layer, thereby improving the quality and yield of the final product.
In some embodiments, the conductive material layer may be in the same layer as the display driving electrode layer of the array substrate.
As compared to the prior art manufacturing process in which the display driving electrode layer is first formed and the metal layer is then formed, in this embodiment, the metal layer is first formed, and the display driving electrode layer and the conductive material layer are then formed in a same layer, so that occurrence of a bulge-like defect in the metal material of the metal layer can be avoided when the connection hole is being etched without increasing the layer number and thickness of the array substrate, thereby improving the quality of the final product.
In some embodiments, the array substrate comprises a thin film transistor, and the metal layer may comprise at least one of a source and a drain of the thin film transistor.
By forming the conductive material layer on the source and/or the drain of the thin film transistor, the source and/or the drain can be protected from quality degradation that results from being affected by etching during the process of etching the layers over the source and/or the drain to form the connection hole.
In some embodiments, the metal layer may comprise a signal line of the array substrate.
In some embodiments, the signal line may include a data line.
An array substrate of a display device generally comprises a plurality of mutually parallel gate lines and a plurality of mutually parallel data lines. The gate lines and the data lines intersect and define a plurality of pixel units. A thin film transistor TFT is arranged at each intersection of a gate line and a data line. By controlling turn-on and turn-off of the thin film transistor, it is possible to control the pixel unit corresponding to the thin film transistor to display a picture or not, thereby controlling the display device to display an image.
In some embodiments, the array substrate may further comprise a gate insulating layer arranged between the data line and the base substrate, and a passivation layer arranged over the conductive material layer, the connection hole being arranged in the passivation layer. In this case, the array substrate may be a bottom gate type array substrate, wherein a gate metal layer is located below a source/drain metal layer. The connection hole is used for electrically connecting the data line via the conductive material layer.
In some embodiments, the array substrate may further comprise a gate insulating layer and a passivation layer successively arranged over the conductive material layer, the connection hole being arranged in the gate insulating layer and the passivation layer. In such a case, the array substrate may be a top gate type array substrate, wherein a gate metal layer is located above a source/drain metal layer. Likewise, the connection hole is used for electrically connecting the data line via the conductive material layer.
In some embodiments, the conductive material layer may be in the same layer as a pixel electrode layer of the array substrate.
As compared to the prior art manufacturing process in which the pixel electrode layer is first formed and the data line is then formed, in this embodiment, the data line is first formed, and the pixel electrode layer and the conductive material layer are then formed in a same layer, so that occurrence of a bulge-like defect in the metal material of the data line can be avoided when the connection hole is being etched without increasing the layer number and thickness of the array substrate, thereby improving the quality of the final product.
In some embodiments, the signal line may comprise a common electrode line, and the array substrate may further comprise a gate insulating layer and a passivation layer arranged successively over the conductive material layer, the connection hole being arranged in the gate insulating layer and the passivation layer. In such a case, the array substrate may be a bottom gate type array substrate, wherein a gate metal layer is located below a source/drain metal layer. The connection hole is used for electrically connecting the common electrode line via the conductive material layer.
In some embodiments, the conductive material layer may be in the same layer as the common electrode layer of the array substrate.
As compared to the prior art manufacturing process in which the common electrode layer is first formed and the common electrode line is then formed, in this embodiment, the common electrode line is first formed, and the common electrode layer and the conductive material layer are then formed in a same layer, so that occurrence of a bulge-like defect in the metal material of the common electrode line can be avoided when the connection hole is being etched without increasing the layer number and thickness of the array substrate, thereby improving the quality of the final product.
In some embodiments, the conductive material layer may be made of a conductive oxide. For example, the conductive oxide may include one or more of an indium tin oxide (ITO), an aluminum-doped zinc oxide (AZO), an indium-doped zinc oxide (IZO), and an indium-doped cadmium oxide, wherein the indium tin oxide or the tin-doped indium oxide is currently known as the best and the most widely used transparent conductive oxide, which has been widely used due to its simplicity of being deposited as a thin film.
In some embodiments, the metal layer may be made of copper and/or aluminum.
To make a balance between the cost and the conductivity, aluminum is primarily used as a metal interconnect material in the conventional semiconductor manufacturing process. However, as the size of the transistor becomes smaller and smaller, devices manufactured using aluminum lines are beginning to be problematic in terms of reliability. Using a metal with smaller resistivity as the interconnection material and selecting a dielectric material with smaller dielectric constant are two main directions for reducing signal delay and improving the clock frequency. Since copper just has a resistivity of 1.67 μΩ-cm, much smaller than 2.66 μΩ-cm of aluminum, and can reduce the thickness of the interconnect layer, the effect of reducing signal delay is achieved by decreasing the capacitance. Therefore, if a low-K dielectric material is used in cooperation, the coupling capacitance between signal lines can be decreased, while the signal conversion speed is also increased, i.e. further reducing the signal delay. As a result, copper interconnect process comes into being. Nowadays, the copper interconnect technology has become a standard process for products of 90 nm or less.
According to a second aspect of the present disclosure, there is provided a display panel comprising the array substrate described in any one of the above embodiments.
According to a third aspect of the present disclosure, there is provided a display device comprising the above display panel.
In the above-described display panel and display device, by arranging the conductive material layer on the metal layer, during the process of etching the layers such as a gate insulating layer, a passivation layer and the like over the metal layer to form a connection hole, the conductive material layer protects the metal layer from being affected by etching, which consequently reduces or even avoids occurrence of a bulge-like defect in the metal layer, thereby improving the quality and yield of the final product.
According to a fourth aspect of the present disclosure, there is provided a manufacturing method of an array substrate. The method may comprise forming a metal layer over a base substrate, forming a conductive material layer on the metal layer, and forming a connection hole over the conductive material layer to expose the conductive material layer.
In the above-described manufacturing method of an array substrate, by forming the conductive material layer on the metal layer, during the subsequent process of etching the layers such as the gate insulating layer, the passivation layer and the like over the metal layer to form a connection hole, the conductive material layer protects the metal layer from being affected by etching, which consequently reduces or even avoids occurrence of a bulge-like defect in the metal layer, thereby improving the quality and yield of the final product.
In some embodiments, the conductive material layer and a display driving electrode layer of the array substrate may be simultaneously formed during one patterning process.
In some embodiments, the array substrate may comprise a thin film transistor, and the metal layer comprises at least one of a source and a drain of the thin film transistor.
In some embodiments, the metal layer may comprise a signal line of the array substrate. For example, the signal line includes a data line.
In some embodiments, the manufacturing method of an array substrate may further comprise forming a gate insulating layer over the base substrate prior to forming the conductive material layer, and forming a passivation layer over the conductive material layer, wherein the connection hole is formed in the passivation layer. The resulting array substrate may be a bottom gate type array substrate in which a gate metal layer is located below a source/drain metal layer. The connection hole is used for electrically connecting the data line via the conductive material layer.
In some embodiments, the manufacturing method of an array substrate may further comprise: forming a gate insulating layer and a passivation layer successively over the conductive material layer, wherein the connection hole is formed in the gate insulating layer and the passivation layer. The resulting array substrate may be a top gate type array substrate in which a gate metal layer is located above a source/drain metal layer. Likewise, the connection hole is used for electrically connecting the data line via the conductive material layer.
In some embodiments, the conductive material layer and a pixel electrode layer of the array substrate may be formed simultaneously during one patterning process.
In some embodiments, the signal line includes a common electrode line, and the manufacturing method of an array substrate may further comprise: forming a gate insulating layer and a passivation layer successively over the conductive material layer, wherein the connection hole is formed in the gate insulating layer and the passivation layer. The resulting array substrate may be a bottom gate type array substrate in which a gate metal layer is located below a source/drain metal layer. The connection hole is used for electrically connecting the common electrode line via the conductive material layer.
In some embodiments, the conductive material layer and a common electrode layer of the array substrate may be simultaneously formed during one patterning process.
It is to be noted that the second, third and fourth aspects of the present disclosure have similar or the same example implementations and benefits as the first aspect of the present disclosure, which are not described here for simplicity.
These and other aspects of the present disclosure will be apparent from and will be elucidated with reference to the embodiments described below.
Exemplary embodiments of the present disclosure will be described in detail below with reference to the accompanying drawings. The drawings are illustrative and not drawn to scale, which are merely used to illustrate the embodiments of the present disclosure and are not intended to limit the scope of the present disclosure. In the drawings, like reference numerals denote the same or similar parts. In order to make the technical solution of the present disclosure clearer, the process steps and device structures well known in the art are omitted here.
In the array substrate shown in
In the array substrate shown in
As compared to the prior art manufacturing process in which the display driving electrode layer is first formed and the metal layer is then formed, in this embodiment, the metal layer is first formed, and the display driving electrode layer and the conductive material layer are then formed in the same layer, so that occurrence of a bulge-like defect in the metal material of the metal layer can be avoided when the connection hole is being etched without increasing the layer number and thickness of the array substrate, thereby improving the quality of the final product.
The metal layer 102 may comprise a signal line of the array substrate. For example, the signal line may include a data line.
In the array substrate shown in
The inventive concept of the present disclosure is further applicable to a top gate type array substrate.
In the array substrate shown in
In the array substrates shown in
In the array substrate shown in
In the array substrate shown in
The array substrate shown in
In the array substrate shown in
In one or more of the above embodiments, the conductive material layer is made of a conductive oxide. For example, the conductive oxide may include one or more of an indium tin oxide, an aluminum-doped zinc oxide, an indium-doped zinc oxide, and an indium-doped cadmium oxide. In addition, one or more of the metal layer 102, the data lines 202, 302, the common electrode line 402, and the source/the drain 502 may be made of copper and/or aluminum.
In step S601, as shown in
In step S602, as shown in
In step S603, as shown in
In step S604, as shown in
In the above-described manufacturing method of an array substrate, by forming the conductive material layer on the metal layer, during the subsequent process of etching the layers such as the gate insulating layer, the passivation layer and the like over the metal layer to form the connection hole, the conductive material layer protects the metal layer from being affected by etching, which consequently reduces or even avoids occurrence of a bulge-like defect in the metal layer, thereby improving the quality and yield of the final product.
Optionally, the conductive material layer and a display driving electrode layer of the array substrate are formed simultaneously during one patterning process.
Optionally, the metal layer comprises a data line, and the manufacturing method of an array substrate may further comprise: forming a gate insulating layer over the base substrate prior to forming the conductive material layer, and forming a passivation layer over the conductive material layer, wherein the connection hole is formed in the passivation layer. The resulting array substrate may be a bottom gate type array substrate in which a gate metal layer is located below a source/drain metal layer. The connection hole is used for electrically connecting the data line via the conductive material layer.
Optionally, the manufacturing method of an array substrate may further comprise: forming a gate insulating layer and a passivation layer successively over the conductive material layer, wherein the connection hole is formed in the gate insulating layer and the passivation layer. The resulting array substrate may be a top gate type array substrate in which the gate metal layer is located over the source/drain metal layer. Likewise, the connection hole is used for electrically connecting the data line via the conductive material layer.
Optionally, the conductive material layer and a pixel electrode layer of the array substrate are formed simultaneously during one patterning process.
Optionally, the metal layer comprises a common electrode line, and the manufacturing method of an array substrate further comprises: forming a gate insulating layer and a passivation layer successively over the conductive material layer, wherein the connection hole is formed in the gate insulating layer and the passivation layer. The resulting array substrate may be a bottom gate type array substrate in which the gate metal layer is located below the source/drain metal layer. The connection hole is used for electrically connecting the common electrode line via the conductive material layer.
Optionally, the conductive material layer and a common electrode layer of the array substrate are simultaneously formed during one patterning process.
The present disclosure further provides a display panel and a display device comprising the array substrate described in any one of the above embodiments.
The concept of the present disclosure can be widely applied to any system having display function, including a desktop computer, a laptop computer, a mobile phone, a tablet computer, and the like. In addition, although several embodiments have been described in detail above, other modifications are possible. For example, the flow chart described above does not require a desired result to be achieved in the particular order or sequence as described. Other steps may be provided, or steps may be removed from the described flow, and other components may be added to the described system or removed from the described system. Other embodiments may be within the scope of the present disclosure. Numerous variations and modifications may be made by those skilled in the art without departing from the spirit and scope of the present disclosure in view of the teachings of the present disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201610276100.6 | Apr 2016 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2017/070286 | 1/5/2017 | WO | 00 |