Articles subject to ice formation comprising a repellent surface

Abstract

Articles subject to ice formation during normal use are described. The article comprises a repellent surface such that the receding contact angle of the surface with water ranges from 90 degrees to 135 degrees. The repellent surface comprises a fluorochemical material, typically in combination with a non-fluorinated organic polymeric binder. The fluorochemical material is prefer-ably a compound having the formula: (Rf-L-P)nA Rf is a fluorinated group; L is independently an organic divalent linking group; P is a catenary, divalent heteroatom-containing carbonyl moiety, such as —C(O)O—; A is hydrocarbon moiety; and n typically ranges from 1 to 3. Also described are methods of making an article comprising providing an article subject to ice formation during normal use and providing a liquid repellent surface, as described herein, on at least a portion of the article.

Description

SUMMARY

In one embodiment, an article subject to ice formation during normal use is described. The article comprises a repellent surface such that the receding contact angle of the surface with water ranges from 90 degrees to 135 degrees. The repellent surface comprises a fluorochemical material, typically in combination with a non-fluorinated organic polymeric binder. The fluorochemical material is preferably a compound having the formula:(R_f-L-P)_nAR_f is a fluorinated group;L is independently an organic divalent linking group;P is a catenary, divalent heteroatom-containing carbonyl moiety, such as —C(O)O—;A is hydrocarbon moiety;and n typically ranges from 1 to 3.

Also described are methods of making an article comprising providing an article subject to ice formation during normal use and providing a liquid repellent surface, as described herein, on at least a portion of the article.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is cross-sectional view of an embodied substrate comprising a repellent surface layer.

FIG. 2 is cross-sectional view of another embodiment of an article comprising a repellent surface;

DETAILED DESCRIPTION

Presently described are articles or components thereof that are subject to ice formation during their normal use. The term “ice” includes any form of frozen water including frost, freezing rain, sleet and snow.

Representative articles include sign faces, signal transmission lines (e.g., telephone and electrical cables), satellite dishes, antennas, solar panels, wind turbine blades, automobiles, railroad cars, aircraft, watercraft, navigation equipment, heat pumps and exchangers or components thereof, ice manufacturing facilities and articles including ice-cube trays and other “ice maker” components; commercial and residential refrigerators and freezers; cryogenic and supercomputer storage facilities; buildings, transportation signs, roofing, dams (especially near a lock), oil drilling platforms, outdoor sporting equipment; recreational vehicles such as snowmobiles, and snow removal equipment.

A heat exchanger is an article used to transfer heat between one or more fluids. The fluids may be separated by a solid wall to prevent mixing or they may be in direct contact. They are widely used in space heating, refrigeration, air conditioning, power stations, chemical plants, petrochemical plants, petroleum refineries, natural-gas processing, and sewage treatment. The classic example of a heat exchanger is found in an internal combustion engine in which a circulating fluid known as engine coolant flows through radiator coils and air flows past the coils, which cools the coolant and heats the incoming air.

Types of heat exchangers include: shell and tube heat exchanger, plate heat exchangers, plate and shell heat exchanger, adiabatic wheel heat exchanger, plate fin heat exchanger, pillow plate heat exchanger, fluid heat exchanger, waste heat recovery units, dynamic scraped surface heat exchanger, phase-change heat exchangers, direct contact heat exchangers, microchannel heat exchangers.

One of the widest uses of heat exchangers is for air conditioning of buildings and vehicles. This class of heat exchangers is commonly called air coils, or just coils due to their often-serpentine internal tubing. Liquid-to-air, or air-to-liquid HVAC (i.e. heating, ventilation and air conditioning) coils are typically of modified crossflow arrangement. In vehicles, heat coils are often called heater cores.

On the liquid side of these heat exchangers, the common fluids are water, a water-glycol solution, steam, or a refrigerant. For heating coils, hot water and steam are the most common, and this heated fluid is supplied by boilers, for example. For cooling coils, chilled water and refrigerant are most common. Chilled water is supplied from a chiller that is potentially located very far away, but refrigerant must come from a nearby condensing unit. When a refrigerant is used, the cooling coil is the evaporator in the vapor-compression refrigeration cycle. HVAC coils that use this direct-expansion of refrigerants are commonly called DX coils. Some DX coils are “microchannel” type.

On the air side of HVAC coils a significant difference exists between those used for heating, and those for cooling. Air that is cooled often has moisture condensing out of it, except with extremely dry air flows. Heating some air increases that airflow's capacity to hold water. Thus, heating coils need not consider moisture condensation on their air-side. However, cooling coils are designed and selected to handle latent (moisture) as well as the adequate (cooling) loads. The water that is removed is called condensate.

With reference to FIG. 1, article 200 comprises substrate 210 comprising a (e.g. liquid and ice) repellent surface layer (e.g. layer) 251 disposed on a substrate. The repellent surface layer can comprise a (e.g. non-fluorinated) organic polymeric binder and a fluorochemical material. The concentration of fluorochemical material at the outer exposed surface 253 is typically higher than the concentration of fluorochemical material within the (e.g. non-fluorinated) organic polymeric binder layer 251 proximate substrate 210. The (e.g. liquid) repellent surface layer can be provided by coating substrate 210 with a coating composition comprising an organic solvent, a (e.g. non-fluorinated) organic polymeric binder, and a fluorochemical material; as will subsequently be described.

With reference to FIG. 2, article 300 comprises substrate 310 comprising a (e.g. liquid) repellent surface (e.g. layer) 353 that comprises a fluorochemical material. The concentration of fluorochemical material at the outer exposed surface (e.g. layer) 353 is typically higher than the concentration of fluorochemical material proximate the center of the substrate 310. In one embodiment, the (e.g. liquid) repellent surface 353 can be provided by including a fluorochemical material, such as a fluorochemical compound, as a melt additive in a polymeric material that is thermally processed to form substrate 310 into a component or a surface layer thereof.

The repellent surface repels ice and typically also repels liquids such as water, aqueous solutions and mixtures including paint. The repellent surface also typically repels hydrophobic liquids such as hexadecane.

In some embodiments, the inclusion of the repellent surface can aid in the removal of ice accumulation from the repellent surface. For example, the inclusion of the repellent surface may reduce the force required to remove the ice from the repellent surface.

Further, the article may be capable of repeatedly releasing ice from the repellent surface.

In other embodiments, the inclusion of the repellent coating may reduce or prevent ice build-up on the repellent surface. The repellent coating or surface may also reduce the time required to remove ice which has formed on a substrate when the substrate is thawed/defrosted.

Ice repellency can be measured by various known methods, such as Centrifugal Testing (as conducted by AMIL) according to the test method described in the examples. In some embodiments, the repellent surface has an ice reduction factor (ARF) of at least 2 or 2.5. The ice reduction factor may range up to about 5 or greater. In some embodiments, the ice adhesion on bare aluminum is less than 325, 300, 275, 250, or 200 kPa. The ice adhesion may be at least 50 or 100 kPa.

The outer exposed surface 253 is preferably (e.g. ice, liquid) repellent such that the advancing and/or receding contact angle of the surface with water is least 90, 95, 100, 105, 110, or 115 degrees. The advancing and/or receding contact angle is typically no greater than 135, 134, 133, 132, 131 or 130 degrees and in some embodiments, no greater than 129, 128, 127, 126, 125, 124, 123, 122, 121, or 120 degrees. The difference between the advancing and/or receding contact angle with water of the (e.g. ice, liquid) repellent surface layer can be at least 5, 10, 15, 20, 25, 30, 35, 40, 45, or 50 degrees. In some embodiments, the difference between the advancing and receding contact angle with water of the surface layer is no greater than 15, 14, 13, 12, 11, 10, 9, 8, 7, 6, 5, 4, 3, 2, or 1 degree. As the difference between the advancing and receding contact angle with water increases, the tilt angle needed to slide or roll off a (e.g. water) droplet from a planar surface increases. One of ordinary skill appreciates that deionized water is utilized when determining contact angles with water.

In some embodiments, the outer exposed surface 253 exhibits a contact angle in the ranges just described after soaking in water for 24 hours at room temperature (25° C.). The contact angle of the (e.g. ice, liquid) repellent surface can also be evaluated with other liquids instead of water such as hexadecane or a solution of 10% by weight 2-n-butoxyethanol and 90% by weight deionized water. In some embodiments, the advancing contact angle with such 2-n-butoxyethanol solution is at least 60, 61, 62, 63, 64, 65, 66, 67, 68, 69, 70 degrees and in some embodiments at least 75 or 80 degrees. In some embodiments, the receding contact angle with such 2-n-butoxyethanol solution is at least 40, 45, 50, 55, 60, 65, or 70 degrees. In some embodiments, the advancing and/or receding contact angle of the (e.g. ice, liquid) repellent surface with such 2-n-butoxyethanol solution is no greater than 100, 95, 90, 85, 80, or 75 degrees.

In another embodiment, the outer exposed surface 253 is preferably (e.g. ice, liquid) repellent such that the receding contact angle of the surface with hexadecane is at least 45, 46, 47, 48, 49, 50, 55, 60, 65, 70, or 75 degrees. The advancing contact angle with hexadecane is typically at least 45, 50, 55, 60, 65, 70, 75, 80, or 84 degrees. In typical embodiments, the receding or advancing contact angle with hexadecane is no greater than 85 or 80 degrees. In some embodiments, the outer exposed surface 253 exhibits a contact angle in the ranges just described after soaking in water for 24 hours at room temperature (25° C.).

The surface layer is not a lubricant impregnated surface. Rather the outer exposed surface is predominantly a solid (e.g. ice, liquid) repellent material. In this embodiment, less than 50, 45, 40, 35, 30, 25, 20, 15, 10, 5, 4, 3, 2, 1, 0.5, 0.1, 0.005, 0.001% of the surface area is a liquid lubricant. Rather, at least 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, 96, 97, 98, 99, 99.5%, or greater of the outer exposed surface is a solid repellent material, as described herein. Thus, a liquid (e.g. water, oil, paint) or solid (e.g. ice) that is being repelled comes in contact with and is repelled by the solid repellent material.

The repellent material is generally a solid at the use temperature of the coated substrate or article, which can be as low as −60° F. (−51.1° C.) or −80° F. (−62.2° C.), yet more typically ranges from −40° F. (−40° C.) to 120° F. (48.9° C.). For outdoor usage in moderate climates, the typical use temperature may be at least −20° F. (−28.9° C.), −10° F. (−23.3° C.), 0° F. (−17.8° C.), or 10° F. (−12.2° C.). In typical embodiments, the repellent material is a solid at room temperature (e.g. 25° C.) and temperatures ranging from 40° F. (4.44° C.) to 130° F. (54.4° C.). In typical embodiments the repellent material has a melting temperature (peak endotherm as measured by DSC) of greater than 25° C. and also typically greater than 130° F. (54.4° C.). In some embodiments, the repellent material has a melting temperature no greater than 200° C. In typical embodiments, a single solid repellent material is utilized. However, the coating composition may contain a mixture of solid repellent materials.

The repellent material has no solubility or only trace solubility with water, e.g., a solubility of 0.01 g/l or 0.001 g/l or less.

The (e.g. liquid, ice) repellent surface layer comprises a fluorochemical material and a (e.g. non-fluorinated) organic polymeric binder. In typical embodiments, a major amount of non-fluorinated polymeric binder is combined with a sufficient amount of fluorochemical material that provides the desired ice and liquid repellency properties, as previously described.

In typical embodiments, the amount of fluorochemical material is at least about 0.005, 0.10, 0.25, 0.5, 1.5, 2.0, or 2.5 wt.-% and in some embodiments, at least about 3.0, 3.5, 4.0, 4.5, or 5 wt.-%. The amount of fluorochemical material is typically no greater than 50, 45, 40, 35, 30, 25, 20, or 15 wt.-% of the sum of the fluorochemical material and (e.g., non-fluorinated) polymeric binder. Thus, the fluorine content of such fluorochemical material-containing polymeric (e.g. binder) materials is significantly less than the fluorine content of fluoropolymers, such as Teflon™ PTFE. The Teflon™ PTFE materials are polytetrafluoroethylene polymers prepared by the polymerization of the monomer tetrafluoroethylene (“TFE” having the structure CF₂═CF₂). It has been found that Teflon™ PTFE does not provide a highly repellent surface such that the receding contact angle with water is at least 90 degrees and/or difference between the advancing contact angle and the receding contact angle of water is less than 10. It is therefore a surprising result that materials containing such low fluorine content can provide comparable or better repellency than fluoropolymers such as Teflon™ PTFE having a substantially higher fluorine content.

In some embodiments, the fluorochemical material comprises a compound or a mixture of compounds represented by the formula:(R_f-L-P)_nAR_f is a fluorinated group;L is independently an organic divalent linking group;P is independently a catenary, divalent heteroatom-containing a carbonyl moiety;A is hydrocarbon moiety;and n typically ranges from 1 to 3.

In some embodiments, n is preferably 2 or averages at least 2. When the fluorochemical material comprises a mixture of compounds, the concentration by weight of the fluorochemical compound wherein n is 2 is typically greater than each of the fractions wherein n is not 2 (e.g. n=1 or n=3). Further, the concentration wherein n is 2 is typically at least 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, or 95% by weight or greater of the mixture of compounds.

The fluorinated group, R_f, is typically a fluoroalkyl group that contains at least 3 or 4 carbon atoms and typically no greater than 12, 8, or 6 carbon atoms. The fluoroalkyl group can be straight chain, branched chain, cyclic or combinations thereof. In typical embodiments, the fluoroalkyl group is preferably free of olefinic unsaturation. In some embodiments, each terminal fluorinated group contains at least 50, 55, 60, 65, or 70% to 78% fluorine by weight. Such terminal groups are typically perfluorinated. In some embodiments, R_f is CF₃(CF₂)₃— or in other words C₄F₉— for at least 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90%, or 95% by weight or greater of the mixture of compounds. In another embodiment, the fluorinated group, R_f, is a perfluoroheteroalkyl group, such as a perfluoroether or perfluoropolyether.

The organic divalent linking group, L, can be a covalent bond, a heteroatom (e.g., O or S), or an organic moiety. The organic divalent linking group typically contains no greater than 20 carbon atoms, and optionally contains oxygen-, nitrogen-, or sulfur-containing groups or a combination thereof. L is typically free of active hydrogen atoms. Examples of L moieties include straight chain, branched chain, or cyclic alkylene, arylene, aralkylene, oxy, thio, sulfonyl, amide, and combinations thereof such as sulfonamidoalkylene. Below is a representative list of suitable organic divalent linking groups.—SO₂N(R′)(CH₂)_k——CON(R′)(CH₂)_k——(CH₂)_k——(CH₂)_kO(CH₂)_k——(CH₂)_kS(CH₂)_k——(CH₂)_kSO₂(CH₂)_k——(CH₂)_kOC(O)NH——(CH₂)SO₂N(R′)(CH₂)_k——(CH₂)_kNR′——(CH₂)_kNR′C(O)NH—

For the purpose of this list, each k is independently an integer from 1 to 12. R′ is hydrogen, phenyl, or an alkyl of 1 to about 4 carbon atoms (and is preferably methyl). In some embodiments, k is no greater than 6, 5, 4, 3, or 2. In some embodiments, the linking group has a molecular weight of at least 14 g/mole, in the case of —CH₂—, or at least 20, 25, 30, 40, 50, 60, 70, 80, 90, 100, or 110 g/mole. The molecular weight of the linking group is typically no greater than 350 g/mole and in some embodiments no greater than 300, 250, 200, or 150 g/mole.

The aforementioned moiety, A, can be a straight chain, branched chain, or cyclic hydrocarbon, or a combination thereof. Typical A moieties include alkylene, alkene, arylene, and aralkylene having 4-50 carbon atoms. In some embodiments, A is preferably a saturated hydrocarbon moiety or in other words an alkylene group (i.e. when n is 2 or 3) or alkyl group (i.e. when n is 1) averaging at least 4, 6, 8, 10, 12, 14, 16, or 18 carbon atoms. In some embodiments, the alkylene or alkyl group averages no greater than 45, 40, 35, 30, 25, or 20 carbon atoms. In typical embodiments, A is a hydrocarbon portion of a dicarboxylic acid or fatty acid.

The divalent carbonyl moiety, P, is typically a residue of a dicarboxylic or fatty acid and thus carbonyloxy (—C(O)O—) or in other words an ester group.

The fluorochemical compound can be prepared by various methods known in the art such as described in U.S. Pat. No. 6,171,983. The fluorochemical is most typically prepared by esterifying a fluorinated alcohol with a dicarboxylic acid or a fatty acid. Particularly when a fatty acid is utilized as a starting material the resulting fluorochemical material typically contains a mixture of compounds.

Suitable dicarboxylic acids include adipic acid, suberic acid, azelaic acid, dodecanedioic acid, octadecanedioic acid, eicosanedioic acid, and the like that provide the A group as previously described. Derivatives of dicarboxylic acid can also be employed such as halides and anhydrides.

Suitable unsaturated fatty acids include for example—palmitoleic acid, linoleic acid, linolenic acid, oleic acid, rinoleic acid, gadoleic acid, eracic acid or mixtures thereof. Polymerized fatty acids can contain a higher number of carbon atoms such that the fluorochemical compound averages 30, 35, 40, 45 or 50 carbon atoms.

Suitable saturated fatty acids include caprylic acid, CH₃(CH₂)₆COOH; capric acid, CH₃(CH₂)₈COOH; lauric acid, CH₃(CH₂)₁₀COOH; myristic acid, CH₃(CH₂)₁₂COOH; palmitic CH₃(CH₂)₁₄COOH; stearic acid CH₃(CH₂)₁₆COOH; arachidic acid, CH₃(CH₂)₁₈COOH; behenic acid CH₃(CH₂)₂₀COOH; lignoceric acid, CH₃(CH₂)₂₂COOH; and cerotic acid CH₃(CH₂)₂₄COOH.

Representative examples of useful fluorine-containing monoalcohols include the following wherein R_f is a fluorinated group as previously described.

RfSO2N(CH3)CH2CH2OH,            CF3(CF2)3SO2N(CH3)CH2CH2OH,
CF3(CF2)3SO2N(CH3)CH(CH3)CH2OH, CF3(CF2)3SO2N(CH3)CH2CH(CH3)OH,
C3F7CH2OH,                      RfSO2N(H)(CH2)2OH,
RfSO2N(CH3)(CH2)4OH,            C4F9SO2N(CH3)(CH2)4OH
C6F13SO2N(CH3)(CH2)4OH,         RfSO2N(CH3)(CH2)11OH,
RfSO2N(C2H5)CH2CH2OH,           CF3(CF2)3SO2N(C2H5)CH2CH2OH,
C6F13SO2N(C2H5)CH2CH2OH         RfSO2N(C2H5)(CH2)6OH,
C3F7CONHCH2CH2OH,               RfSO2N(C3H7)CH2OCH2CH2CH2OH,
RfSO2N(CH2CH2CH3)CH2CH2OH,      RfSO2N(C4H9)(CH2)4OH,
RfSO2N(C4H9)CH2CH2OH,

Other fluorine-containing monoalcohols are described in U.S. Pat. No. 6,586,522; incorporated herein by reference.

In some embodiments, the monofunctional fluoroaliphatic alcohols useful in preparing the fluorochemical compounds include the N-alkanol perfluoroalkylsulfonamides described in U.S. Pat. No. 2,803,656 (Ahlbrecht et al.), which have the general formula R_fSO₂N(R)R₁CH₂OH wherein R_f is a perfluoroalkyl group having 3 to 6 and preferably 4 carbon atoms, R₁ is an alkylene radical having 1 to 12 carbon atoms, and R is a hydrogen atom or an alkyl group containing 1 to 4 carbon atoms and is preferably methyl. In some embodiments, R₁ is an alkylene radical having no greater than 8, 7, 6, 5, 4, 3, or 2 carbon atoms. These monofunctional alcohols can be prepared by reactions of an acetate ester of halohydrin with a sodium or potassium salt of the corresponding perfluoroalkylsulfonamide.

In some embodiments, the fluorochemical compound has the following formulasC₄F₉SO₂N(CH₃)(CH₂)_kOC(O)-A-C(O)O(CH₂)_kN(CH₃)SO₂C₄F₉ orC₄F₉SO₂N(CH₃)(CH₂)_kOC(O)-Awherein k and A are the same as previously described.

In some typical embodiments, the fluorochemical compound comprises less than 2% of fluorinated groups having greater than 6 carbon atoms. Further, the fluorochemical compound typically comprises less than 25% of fluorinated groups having greater than 4 carbon atoms. In favored embodiments, the fluorochemical compound is free of fluorinated (e.g. fluoroalkyl) groups, R_f, having at least 8 carbon atoms. In some embodiments, the fluorochemical compound is free of fluorinated (e.g. fluoroalkyl) groups, R_f, having at least 5, 6, or 7 carbon atoms. In some embodiments, the repellent surface or repellent coating is free of fluorinated (e.g. fluoroalkyl) groups, R_f, having at least 8 carbon atoms. In some embodiments, the repellent surface or repellent coating is free of fluorinated (e.g. fluoroalkyl) groups, R_f, having at least 5, 6, or 7 carbon atoms.

Fluorochemical compounds according to the formulas described herein are not fluoroalkyl silsesquioxane materials having the chemical formula [RSiO_3/2]_n, wherein R comprises a fluoroalkyl or other fluorinated organic group. Fluorochemical compounds according to the formulas described herein are also not (e.g. vinyl terminated) polydimethylsiloxanes. In typical embodiments, the fluorochemical material is free of silicon atoms as well as siloxane linkages.

In some embodiments, the (e.g. starting materials of the fluorochemical compound are selected such that the) fluorochemical compound has a molecular weight (Mw) no greater than 1500, 1400, 1300, 1200, 1100, or 1000 g/mole. In some embodiments the molecular weight is at least 250, 300, 350, 400, 450, 500, 550, 600, or 700 g/mole.

In some embodiments, the (e.g. starting materials of the fluorochemical compound are selected such that the) fluorochemical compound has a fluorine content of at least 25 wt.-%. In some embodiments, the fluorine content of the fluorochemical material is at least 26, 27, 28, 29, 30, 31, 32, 33, or 34 wt.-% and typically no greater than 58, 57, 56, 55, 54, 53, 52, 51, or 50 wt.-%.

Various organic polymeric binders can be utilized. Although fluorinated organic polymeric binders can also be utilized, fluorinated organic polymeric binders are typically considerably more expensive than non-fluorinated binders. Further, non-fluorinated organic polymeric binders can exhibit better adhesion to non-fluorinated polymeric, metal, or other substrates.

Suitable non-fluorinated binders include for example polystyrene, atactic polystyrene, acrylic (i.e. poly(meth)acrylate), polyester, polyurethane (including polyester type thermoplastic polyurethanes “TPU”), polyolefin (e.g. polyethylene), and polyvinyl chloride. Many of the polymeric materials that a substrate can be thermally processed from, as will subsequently be described, can be used as the non-fluorinated organic polymeric binder of the organic solvent coating composition. However, in typical embodiments, the non-fluorinated organic polymeric binder is a different material than the polymeric material of the substrate. In some embodiments, the organic polymeric binder typically has a receding contact angle with water of less than 90, 80, or 70 degrees. Thus, the binder is typically not a silicone material.

In some embodiments, the (e.g. non-fluorinated) organic polymeric binder is a film-grade resin, having a relatively high molecular weight. Film-grade resins can be more durable and less soluble in the liquid/solid (e.g. water, oil, paint, ice) being repelled. In other embodiments, the (e.g. non-fluorinated) organic polymeric binder can be a lower molecular weight film-forming resin. Film-forming resins can be more compliant and less likely to affect the mechanical properties of the substrate. Viscosity and melt flow index are indicative of the molecular weight. Mixtures of (e.g. non-fluorinated) organic polymeric binders can also be used.

In some embodiments, the film-grade (e.g. non-fluorinated) organic polymeric binder typically has a melt flow index of at least 1, 1.5, 2, 2.5, 3, 4, or 5 g/10 min at 200° C./5 kg ranging up to 20, 25, or 30 g/10 min at 200° C./5 kg. The melt flow index can be determined according to ASTM D-1238. The tensile strength of the (e.g. non-fluorinated) organic polymeric binder is typically at least 40, 45, 50, 55, or 60 MPa. Further, the (e.g. non-fluorinated) organic polymeric binder can have a low elongation at break of less than 10% or 5%. The tensile and elongation properties can be measured according to ASTM D-638.

In other embodiments, the (e.g. non-fluorinated) organic polymeric binders have a lower molecular weight and lower tensile strength than film-grade polymers. In one embodiment, the melt viscosity of the (e.g. non-fluorinated) organic polymeric binders (as measured by ASTM D-1084-88) at 400° F. (204° C.) ranges from about 50,000 to 100,000 cps. In another embodiment, the molecular weight (Mw) of the (e.g. non-fluorinated) organic polymeric binder is typically at least about 1000, 2000, 3000, 4000, or 5000 g/mole ranging up to 10,000; 25,000; 50,000; 75,000; 100,000; 200,000; 300,000; 400,000, or 500,000 g/mole. In some embodiments, the (e.g. non-fluorinated) organic polymeric binder has a tensile strength of at least 5, 10, or 15 MPa ranging up to 25, 30, or 35 MPa. In other embodiments, the (e.g. non-fluorinated) organic polymeric binder has a tensile strength of at least 40, 45, or 50 MPa ranging up to 75 or 100 MPa. In some embodiments, the (e.g. non-fluorinated) organic polymeric binder has an elongation at break ranging up to 25, 50, 100, 200, 300, 400, 500, 600, 700, 800, 900, 1000% or higher. In some embodiments, the (e.g. non-fluorinated) organic polymeric binder has a Shore A hardness of at least 50, 60, 70, or 80 ranging up to 100.

In some embodiments, the (e.g. non-fluorinated) organic polymeric binder is selected such that it is compliant at the use temperature of the coated substrate or article.

In this embodiment, the (e.g. non-fluorinated) organic polymeric binder has a glass transition temperature (Tg) as can be measured by DSC of less than 0° C. or 32° F. In some embodiments, the (e.g. non-fluorinated) organic polymeric binder has a glass transition temperature (Tg) of less than 20° F. (−6.7° C.), 10° F. (−12.2° C.), 0° F. (−17.8° C.), −10° F. (−23.3° C.), −20° F. (−28.9° C.), −30° F. (−34.4° C.), −40° F. (−40° C.), −50° F. (−45.6° C.), −60° F. (−51.1° C.), −70° F. (−56.7° C.), or −80° F. (−62.2° C.). The (Tg) of many (e.g. non-fluorinated) organic polymeric binders is at least −130° C.

The selection of (e.g. non-fluorinated) organic polymeric binder contributes to the durability of the repellent surface.

In typical embodiments, the non-fluorinated organic polymeric binder does not form a chemical (e.g. covalent) bond with the fluorochemical material as this may hinder the migration of the fluorochemical material to the outermost surface layer.

In some embodiments, the (e.g. non-fluorinated) organic polymeric binder is not curable, such as in the case of alkyd resins. An alkyd resin is a polyester modified by the addition of fatty acids and other components, derived from polyols and a dicarboxylic acid or carboxylic acid anhydride. Alkyds are the most common resin or “binder” of most commercial “oil-based” paints and coatings.

In some embodiments, the selection of the non-fluorinated polymeric binder can affect the concentration of fluorochemical material that provides the desired (e.g. liquid, ice) repellency properties. For example when the binder is atactic polystyrene, having a molecular weight of 800-5000 kg/mole, or polystyrene available under the trade designation “Styron 685D”, the concentration of fluorochemical material was found to exceed 2.5 wt.-% in order to obtain the desired repellency properties. Thus, for some non-fluorinated polymeric binders, the concentration of fluorochemical material may be at least 3, 3.5, 4, or 5 wt.-% of the total amount of fluorochemical material and (e.g. non-fluorinated) polymeric binder.

Further, when the binder is PMMA, i.e. polymethylmethacrylate, (available from Alfa Aesar) 50 wt.-% of fluorochemical material resulted in a receding contact angle with water of 86 degrees. However, lower concentrations of fluorochemical material resulted in a receding contact angle with water of greater than 90 degrees. Thus, for some non-fluorinated polymeric binders, the concentration of fluorochemical material may be less than 50 wt.-% of the total amount of fluorochemical material and (e.g. non-fluorinated) polymeric binder.

The compositions comprising a fluorochemical material and a (e.g., non-fluorinated organic) polymeric binder can be dissolved, suspended, or dispersed in a variety of organic solvents to form a coating composition suitable for use in coating the compositions onto a substrate. The organic solvent coating compositions typically contain at least about 70%, 80%, 90%, 91%, 92%, 93%, 94%, 95%, 96%, 97%, 98%, 99% organic solvent or greater, based on the total weight of the coating composition. The coating compositions typically contain at least about 0.01%, 0.1%, 0.5%, 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 15% or greater solids of the (e.g. non-fluorinated organic) polymeric binder and fluorochemical material, based on the total weight of the coating composition. However, the coating composition can be provided with an even higher amount of solids, e.g. 20, 30, 40, or 50 wt.-% solids. Suitable organic solvents include for example alcohols, esters, glycol ethers, amides, ketones, hydrocarbons, chlorohydrocarbons, hydrofluorocarbons, hydrofluoroethers, chlorocarbons, and mixtures thereof.

The coating composition may contain one or more additives provided the inclusion of such does not detract from the (e.g. liquid, ice) repellent properties.

The coating compositions can be applied to a substrate or article by standard methods such as, for example, spraying, padding, dipping, roll coating, brushing, or exhaustion (optionally followed by the drying of the treated substrate to remove any remaining water or organic solvent). The substrate can be in the form of sheet articles that can be subsequently thermally formed into a substrate or component. When coating flat substrates of appropriate size, knife-coating or bar-coating may be used to ensure uniform coating of the substrate.

The moisture content of the organic coating composition is preferably less than 1000, 500, 250, 100, 50 ppm. In some embodiments, the coating composition is applied to the substrate at a low relative humidity, e.g. of less than 40%, 30% or 20% at 25° C.

The coating compositions can be applied in an amount sufficient to achieve the desired repellency properties. Coatings as thin as 250, 300, 350, 400, 450, or 500 nm ranging up to 1, 1.5, 2, 2.5, 3, 3.5, 4, 4.5, or 5 microns can provide the desired repellency. However, thicker coatings (e.g., up to about 10, 15, 20 microns or more) can also be used. Thicker coatings can be obtained by applying to the substrate a single thicker layer of a coating composition that contains a relatively high solids concentration. Thicker coatings can also be obtained by applying successive layers to the substrate.

In another embodiment, the fluorochemical material can be combined with a thermally processible (e.g. thermoplastic) polymer and then melt processed into an article, substrate thereof, or surface layer thereof. In this embodiment, the fluorochemical material typically migrates to the surface forming a surface layer with a high concentration of fluorochemical material relative to the total amount of fluorochemical material and thermally processible polymer.

In typical embodiments, the amount of fluorochemical material melt additive is at least about 0.05, 0.1, 0.25, 0.5, 1.5, 2.0 or 2.5 wt.-% and in some embodiments, at least about 3.0, 3.5, 4.0, 4.5 or 5 wt.-%. The amount of fluorochemical material is typically no greater than 25, 20, 15, or 10 wt.-% of the sum of the fluorochemical material melt additive and thermally processible polymer.

To form a polymer blend by melt processing, the fluorochemical material can be, for example, mixed with pelletized, granular, powdered or other forms of the thermally processible polymer and then melt processed by known methods such as, for example, molding or melt extrusion. The fluorochemical material can be mixed directly with the polymer or it can be mixed with the polymer in the form of a “master batch” (concentrate) of the fluorochemical material in the polymer. If desired, an organic solution of the fluorochemical material can be mixed with powdered or pelletized polymer, followed by drying (to remove solvent) and then melt processing. Alternatively, the fluorochemical composition can be added to the polymer melt to form a mixture or injected into a molten polymer stream to form a blend immediately prior to extrusion or molding into articles.

In some embodiments, the melt processible (e.g. thermoplastic) polymer is a polyolefin, polyester, polyamide, polyurethane, or polyacrylate.

The fluorochemical (e.g. melt additive) materials are generally a solid at room temperature (e.g. 25° C.) and at the use temperature of the spray application system component, which commonly ranges from 40° F. (4.4° C.) to 120° F. (48.9° C.). The fluorochemical material and thermally processible polymer are selected such that the fluorochemical material and/or siloxane material is typically molten at the melt processing temperature of the mixture. In some embodiments, the fluorochemical material has a melt temperature no greater than 200, 190, 180, 170, or 160° C.

Extrusion can be used to form polymeric films. In film applications, a film forming polymer is simultaneously melted and mixed as it is conveyed through the extruder by a rotating screw or screws and then is forced out through a slot or flat die, for example, where the film is quenched by a variety of techniques known to those skilled in the art. The films optionally are oriented prior to quenching by drawing or stretching the film at elevated temperatures. Adhesive can optionally be coated or laminated onto one side of the extruded film in order to apply and adhere the (liquid, ice) repellent film onto a substrate.

Molded articles are produced by pressing or by injecting molten polymer from a melt extruder as described above into a mold where the polymer solidifies. Typical melt forming techniques include injection molding, blow molding, compression molding and extrusion, and are well known to those skilled in the art. The molded article is then ejected from the mold and optionally heat-treated to effect migration of the polymer additives to the surface of the article.

After melt processing, an annealing step can be carried out to enhance the development of repellent characteristics. The annealing step typically is conducted below or above the melt temperature of the polymer for a sufficient period of time. The annealing step can be optional.

The (e.g. liquid, ice) repellent coating composition can be provided on a wide variety of organic or inorganic substrates.

Suitable polymeric materials for substrates include, but are not limited to, polyesters (e.g., polyethylene terephthalate or polybutylene terephthalate), polycarbonates, acrylonitrile butadiene styrene (ABS) copolymers, poly(meth)acrylates (e.g., polymethylmethacrylate, or copolymers of various (meth)acrylates), polystyrenes, polysulfones, polyether sulfones, epoxy polymers (e.g., homopolymers or epoxy addition polymers with polydiamines or polydithiols), polyolefins (e.g., polyethylene and copolymers thereof or polypropylene and copolymers thereof), polyvinyl chlorides, polyurethanes, fluorinated polymers, cellulosic materials, derivatives thereof, and the like. In some embodiments, where increased transmissivity is desired, the polymeric substrate can be transparent. The term “transparent” means transmitting at least 85 percent, at least 90 percent, or at least 95 percent of incident light in the visible spectrum (wavelengths in the range of 400 to 700 nanometers). Transparent substrates may be colored or colorless.

Suitable inorganic substrates include metals and siliceous materials such as glass. Suitable metals include pure metals, metal alloys, metal oxides, and other metal compounds. Examples of metals include, but are not limited to, chromium, iron, aluminum, silver, gold, copper, nickel, zinc, cobalt, tin, steel (e.g., stainless steel or carbon steel), brass, oxides thereof, alloys thereof, and mixtures thereof.

The coating composition can be used to impart or enhance (e.g. ice, aqueous liquid and/or oil) repellency of a variety of substrates and articles. The term “ice” includes any form of frozen water as previously described.

The term “aqueous” means a liquid medium that contains at least 50, 55, 60, 65, or 70 wt-% of water. The liquid medium may contain a higher amount of water such as at least 75, 80, 85, 90, 95, 96, 97, 98, 99, or 100 wt-% water. The liquid medium may comprise a mixture of water and one or more water-soluble organic cosolvent(s), in amounts such that the aqueous liquid medium forms a single phase. Examples of water-soluble organic cosolvents include for example methanol, ethanol, isopropanol, 2-methoxyethanol, (2-methoxymethylethoxy)propanol, 3-methoxypropanol, 1-methoxy-2-propanol, 2-butoxyethanol, ethylene glycol, ethylene glycol mono-2-ethylhexylether, tetrahydrofuran, 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, tetraethylene glycol di(2-ethylhexoate), 2-ethylhexylbenzoate, and ketone or ester solvents. The amount of organic cosolvent does not exceed 50 wt-% of the total liquids of the coating composition. In some embodiments, the amount of organic cosolvent does not exceed 45, 40, 35, 30, 25, 20, 15, 10 or 5 wt-% organic cosolvent. Thus, the term aqueous includes (e.g. distilled) water as well as water-based solutions and dispersions such as paint. Water-based solutions and dispersions may be used as test liquids for evaluating contact angles.

Objects and advantages of this invention are further illustrated by the following examples, but the particular materials and amounts thereof recited in these examples, as well as other conditions and details, should not be construed to unduly limit this invention. These examples are for illustrative purposes only and are not meant to be limiting on the scope of the appended claims.

Material
designation	Description	Obtained from
MEK	Methyl ethyl ketone	Avantor Performance
MIBK	Methyl isobutyl ketone	Materials, Center Valley,
		PA
Acetone	Acetone	VWR International,
		Radnor, PA
MDI	Methylene diphenyldiisocyanate	Bayer, Germany
DMF	Dimethylformamide	VWR International,
		Radnor, PA
Capa 2100	Linear polyester diol under trade	Perstorp Holding AB,
	designation “CAPA 2100”	Malmo, Sweden
1,4-butane diol	1,4-butane diol	Sigma-Aldrich Chemical
		Company, St. Louis, MO
PS	Atactic polystyrene beads with	Alfa Aesar, Ward Hill,
	formula weights of 800-5000 g/mol	MA
	(PS5) or 125-250 kg/mol (PS250),
Styron 685D	Polystyrene resin beads	American Styrenics, The
		Woodlands, TX
PMMA	Poly(methyl methacrylate)	Alfa Aesar, Ward Hill,
	(PMMA) powder with a melting	MA
	point >150° C.
PVC	Poly(vinylchloride)with an inherent	Aldrich Chemical Co.,
	viscosity of 1.115 dL/g.	Milwaukee, WI
Elvacite 1010	Acrylic resin, under trade	Lucite International,
	designation “ELVACITE 1010”	Mississauga, Ontario,
		Canada
TPU2	Polyurethane resin, under trade	Lubrizol Advanced
	designation “ESTANE 5703”	Materials, Inc., Cleveland,
		OH
TPU3	Polyurethane resin, under trade	Lubrizol Advanced
	designation “ESTANE ALR CL87A”	Materials, Inc.,
Unicid 350	Long chain, linear primary carboxylic	Baker Hughes Inc.,
	acid, under trade designation “UNICID	Houston, TX
	350”

Synthesis of Fluorochemical Material 1 (FC-1)

MEFBSE (C₄F₉SO₂N(CH₃)C₂H₄OH), a fluorochemicai alcohol having an equivalent weight of 357, was made in two stages by reacting perfluorobutanesulfonyl fluoride (PBSF) with methylamine to form MEFBSA (C₄F₉SO₂N(CH₃)H), followed by reaction with ethylenechlorohydrin, using a procedure essentially as described in Example 1 of U.S. Pat. No. 2,803,656 (Ahlbrecht, et al.).

Fluorochemical 1 was then prepared using the protocol described in U.S. Pat. No. 7,396,866 (Jariwala et al.) by esterifying the MEFBSE with octadecanedioic acid at a molar ratio of 2:1 as follows: to a three-necked round bottom flask was added 25 g (0.0793 moles) of Emerox 118 (available from Cognis Corporation, Cincinnati, Ohio), 56.7 g (0.159 moles) of MEFBSE, 100 g toluene and 1 g (0.007 moles) of 70 wt % solution of methanesulfonic acid. The contents of the flask were refluxed using a Dean-Stark trap and a condenser at 112° C. for 12 h. The solution was then cooled to 80° C. To this solution was added 1.08 g (0.007 moles) of triethanol amine and the solution was stirred at 80° C. for 1 h. This toluene solution was then washed with 75 g hot water (80° C.) three times. After the last wash the organic bottom layer was distilled to remove the toluene. The residue remaining the flask was the diester product, which was poured into a jar and allowed to crystallize on cooling to room temperature.

Synthesis of Fluorochemical Material 2 (FC-2)

Fluorochemical 2 was made by the esterification of a long chain hydrocarbon acid (Unicid 350, C25 average), and MEFBSE (C₄F₉SO₂N(CH₃)C₂H₄OH) in the same manner as the synthesis of Fluorochemical 1.

Synthesis of Polyurethane TPU1

100 g Capa 2100 was mixed with 50.02 g MDI in a 500 mL round-bottomed flask and heated up to 70° C. for 2 h. Next, 200 g of DMF and 8.11 g of 1,4-butane diol were added. The reactants were heated for an additional 3 h to obtain the thermoplastic urethane polymer. The polymer mixture is approximately 44% solids in DMF. Prior to coating, the mixture was diluted to 20% solids with DMF, then further diluted to either 4 or 5% solids with MEK, as noted in the Tables, below.

Methods

Method for Contact Angle Measurements

Water and hexadecane contact angles were measured using a Ramé-Hart goniometer (Rama-Hart Instrument Co., Succasunna, N.J.). Advancing (θ_adv) and receding (θ_rec) angles were measured as the test liquid (e.g. water or hexadecane) was supplied via a syringe into or out of sessile droplets (drop volume ˜5 μL). Measurements were taken at 2 different spots on each surface, and the reported measurements are the averages of the four values for each sample (a left-side and right-side measurement for each drop).

Preparative Examples 1-39 (PE1-PE39)

PE1-PE39 were mixed to prepare coating solutions containing polymeric binder and fluorinated additives to be used in the Examples and Comparative Examples described below.

To prepare PE1-PE39 coating solutions, 2 g of FC-1 or FC-2 powder and 48 g of solvent (one of MEK, MIBK, DMF or mixtures thereof) were added to a jar. This mixture was stirred and heated to 60° C. until the solid powder dissolved and was no longer visible. This hot coating solution was mixed at the appropriate ratio with a 60° C. solution of binder polymer in solvent (one of MEK, MIBK, DMF or mixtures thereof). The polymeric binder/fluorinated additive solutions were then cooled to room temperature. The compositions of coating solutions of PE1-PE39 are summarized in Table 1, below. Note: Teflon AF was purchased, not made.

TABLE 1
			Polymeric
			Binder/Fluorinated
Preparative		Fluorinated	Additive Weight		Weight %
Example	Polymeric Binder	Additive	Ratio	Solvent	Solids
PE1	Styron 685D	—	100/0	MEK	4
PE2	Styron 685D	FC-1	97.5/2.5	MEK	4
PE3	Styron 685D	FC-1	95/5	MEK	4
PE4	Styron 685D	FC-1	90/10	MEK	4
PE5	Styron 685D	FC-1	85/15	MEK	4
PE6	Styron 685D	FC-1	95/5	MIBK	4
PE7	PS5	FC-1	99/1	MEK	4
PE8	PS5	FC-1	97.5/2.5	MEK	4
PE9	PS5	FC-1	95/5	MEK	4
PE10	PS5	FC-1	90/10	MEK	4
PE11	PS5	FC-1	85/15	MEK	4
PE12	PS250	FC-1	95/5	MEK	4
PE13	PS250	FC-2	95/5	MEK	4
PE14	PMMA	FC-1	95/5	MEK	4
PE15	Elvacite 1010	FC-1	95/5	MEK	4
PE16	PVC	FC-1	95/5	MEK	4
PE17	TPU2	FC-1	95/5	MEK	5
PE18	Teflon ® AF	—	100/0	3M FC40	1
PE19	Comparative	—	100/0	MEK	4
	Binder - PS250
PE20	Comparative	—	100/0	MEK	4
	Binder - PS5
PE21	Comparative	—	100/0	MEK	4
	Binder - PMMA
PE22	Comparative	—	100/0	MEK	4
	Binder -
	Elvacite 1010
PE23	Comparative	—	100/0	MEK	4
	Binder - PVC
PE24	Comparative	—	100/0	MEK	4
	Binder -
	TPU2
PE25	PS250	FC-2	90/10	MEK	4
PE26	PS250	FC-2	85/15	MEK	4
PE27	—	FC-1	0/100	MEK	4
PE28	—	FC-2	0/100	MEK	4
PE29	PMMA	FC-2	95/5	MEK	4
PE30	PMMA	FC-2	90/10	MEK	4
PE31	Elvacite 1010	FC-2	95/5	MEK	4
PE32	PVC	FC-2	95/5	MEK	4
PE33	TPU1	FC-2	95/5	MEK/DMF	4
PE34	TPU1	FC-1	95/5	MEK/DMF	4
PE35	TPU1	FC-2/FC-1	94/3/3	MEK/DMF	4.5
PE36	TPU2	—	100/0	MEK	5
PE37	TPU2	FC-1	97.5/2.5	MEK	4
PE38	TPU2	FC-1	99/1	MEK	4
PE39	TPU2	FC-1	92.5/7.5	MEK	4

Examples 1-30 (EX1-EX30) and Comparative Examples 1-11 (CE1-CE11)

Glass microscope slides (7.5×5.0 cm with a thickness of 0.1 cm, obtained from Fisher) were cleaned with acetone and wiped dry with a WYPALL paper towel. The cleaned glass slides were place on a flat surface and approximately 0.5 mL of each coating composition was evenly coated onto the cleaned glass microscope slide by means of a #52 Mayer rod and dried for approximately 2 h at 21° C. This process provides a coating that is about 133 microns initially and about 5 microns after evaporation of the solvent.

CE8 was a bare PTFE sheet obtained from ePlastics (San Diego, Calif.) and was used as the substrate without any coating.

Water contact angles were evaluated as summarized in Table 2, below.

	TABLE 2
	Water Contact Angles
	in Degrees
	Preparative Example of			CAH
Example	Previous Table	θadv	θrec	(θadv − θrec)
CE1	PE1	93	74	19
EX1	PE2	110	103	7
EX2	PE3	112	105	7
EX3	PE4	114	106	8
EX4	PE5	114	112	2
EX5	PE6	116	110	6
EX6	PE7	103	93	10
EX7	PE8	117	116	1
EX8	PE9	114	106	8
EX9	PE10	116	108	8
EX10	PE11	116	108	8
EX11	PE12	118	112	6
EX12	PE13	120	112	8
EX13	PE14	115	107	8
EX14	PE15	117	109	8
EX15	PE16	120	119	1
EX16	PE17	120	111	9
EX17	PE18	116	107	9
CE2	PE19	103	82	21
CE3	PE20	91	72	19
CE4	PE21	74	57	17
CE5	PE22	71	55	16
CE6	PE23	87	64	23
CE7	PE24	86	45	41
EX18	PE25	121	102	19
EX19	PE26	121	109	12
CE8	PTFE Sheet	111	87	24
CE9	PE27	—	—	—
CE10	PE28	136°	87°	49°
EX20	PE29	119°	111°	8°
EX21	PE30	121°	115°	6°
EX23	PE31	119°	114°	5°
EX25	PE32	121°	117°	4°
EX29	PE33	120°	114°	6°
EX30	PE35	119°	112°	7°
CE11	PE36	67°	<20°	>47°

The CE9 sample prepared from PE27 (neat FC-1) dried into a powder that did not continuously cover the surface of the glass microscope slide and, consequently, it was not possible to measure water contact angles.

The CE10 sample prepared from PE28 (neat FC-2) was characterized by a large hysteresis of 49°, and contacting water droplets did not readily move on the coating surface. Furthermore, the coated CE10 material was readily removed from the substrate by gentle abrasion. These results for the neat FC-1 and FC-2 demonstrate that these fluorochemical materials are not, by themselves, useful for repellent coatings. The organic polymeric binder coatings alone were also not highly repellent, as shown in CE11 (PE36), which is a thermoplastic polyurethane with no fluorochemical additive (for water, a θ_rec of <20° and CAH of >47°).

Examples 31-34 (EX31-EX34)

EX31-EX34 were prepared by coating PE33-PE35 and PE17 coating solutions, respectively on aluminum substrates 1 inch×4 inches (about 2.5 cm×10 cm) in dimension. The aluminum substrates were removed from their package, rinsed with isopropanol, and wiped dry with a WYPALL paper towel. Then the aluminum coupon substrates were dip coated at a controlled speed by lowering them into the desired coating solutions, leaving a small top portion of the substrate uncoated to clamp and hold the sample. Upon maximum immersion depth of the substrate, the coupon was raised up and out of the solution at controlled speed using a standard dip-coating procedure with a KSV NIMA dip-coater [available from Biolin Scientific]. The coated samples were dried at room temperature for a few minutes and then heated at 110° C. for 15 minutes providing a coating that is about 500 nm to 1 micron after evaporation of the solvent.

Advancing and receding contact angles of droplets of water and hexadecane on the coated substrates were measured. Then, to probe the durability of the repellency of the dried coatings, the coated aluminum samples were soaked (fully submerged) overnight in deionized water in a sealed glass jar. After 24 hours, the samples were removed from the water and allowed to air dry overnight at room temperature. The advancing and receding contact angles of water and hexadecane were then measured again to look for changes and probe the durability of the coating repellency after an overnight water soak of the coating. The data are summarized in Tables 3 and 4, below.

	TABLE 3
	Water θadv	Water θrec
Example	Coating Solution	Initial	After Soak	Initial	After Soak
EX31	PE33	123	106	93	71
EX32	PE34	122	124	110	96
EX33	PE35	125	119	108	91
EX34	PE17	121	115	115	106

	TABLE 4
	Hexadecane	Hexadecane
	θadv	θrec
Example	Coating Solution	Initial	After Soak	Initial	After Soak
EX31	PE33	38	43	<20	<20
EX32	PE34	84	83	66	47
EX33	PE35	80	78	62	52
EX34	PE17	79	76	76	57

The contact angle of the (e.g. ice, liquid) repellent surface can also be evaluated with other liquids instead of water or hexadecane, such as a solution of 10% by weight 2-n-butoxyethanol and 90% by weight deionized water. Advancing and receding contact angles of droplets of a solution of 10% by weight 2-n-butoxyethanol and 90% by weight deionized water on the coated substrates were measured. The data is summarized in Table 5.

TABLE 5
		90/10	90/10
		water/butoxyethanol	water/butoxyethanol
Example	Coating Solution	θadv	θrec
CE7	PE24	45	<20
EX31	PE33	82	79
EX32	PE34	81	76
EX33	PE35	80	75
EX34	PE17	80	78

All the examples just described are believed to reduce the force required to remove ice from the repellent surface, and may delay the formation of ice on the surface of the treated substrates under icing conditions. However, due to the cost, all of such examples were not subject to testing at the Anti-icing Materials International Laboratory (AMIL, Chicoutimi, Quebec, Canada).

Preparation of the Melt Blend

The melt blend was mixed using a C.W. Brabender® Instruments Brabender® Bowl Mixer Drive Unit. The brabender was heated to 180° C. The base resins (i.e. Estane ALR CL87A) was measured and put into the brabender. Then the specified fluorochemical material additive (i.e. 4 wt.-% FC-2) was put into the base resin. 50 grams of solids were initially added to the brabender in the specified weight ratios. If the brabender bowl was not full, material would be added in 5 gram increments until the bowl was full enough to mix properly. Once all of the material was in the brabender, it was left to mix for approximately 5 mins or until all of the additive had been thoroughly mixed with the polymeric binder.

Preparation of Films—Hot Pressed

A Carver 4-post manual Hydraulic press was used to flatten the blends out into films. The press was heated to 300° F. The blends were placed between 2 sheets of PTFE film which were placed between 2 silicone pads. Force was applied until the material reached a desired thickness. The film (i.e. Estane ALR CL87A with 4 wt-% FC-2) was annealed in an 80° C. oven for 30 minutes.

Centrifugal Testing at AMIL:

Pieces of the hot pressed films (i.e. Estane ALR CL87A with 4 wt-% FC-2) that were approximately 10 cm×4 cm were adhered to the end of an aluminum beam (length=34 cm, width 3.18 cm, thickness 0.63 cm) such that the major surface in the direction of the width and surfaces in the thickness direction were covered with the film.

Ice was deposited simultaneously on three test films and three bare aluminum controls at the AMIL facility by exposing them to an impinging spray of supercooled water at −10° C. These conditions yielded approximately 5 mm thick heavy rime ice with a density of 0.88 g/cm³. Following icing, the beams are balanced and placed into a centrifuge specially adapted to measure ice adhesion. All measurements are performed at −10° C. The rotational speed of the beam is progressively increased until the centrifugal force detaches the ice. The detachment of the ice is picked up by piezoelectric cells that are sensitive to vibrations and the rotational speed at detachment is recorded by the computer. The specific ice adhesion strength is calculated using the speed of detachment, the mass of the ice, and the beam length. AMIL commonly reports the results as adhesion reduction factors (ARFs) that are defined as

$\mathrm{ARF}=\frac{\mathrm{Mean}\mathrm{ice}\mathrm{adhesion}\mathrm{on}\mathrm{bare}\mathrm{aluminum}}{\mathrm{Mean}\mathrm{ice}\mathrm{adhesion}\mathrm{on}\mathrm{candidate}\mathrm{coating}}$

The average ice adhesion strength of the film (i.e. Estane ALR CL87A with 4 wt-% FC-2) was 304 kPa. In comparison, the average ice adhesive strength of bare aluminum control was 675 kPa. This is an ice adhesion reduction factor of 2.2.

Contact angle measurement were conducted on melt extruded and annealed films of the Estane ALR CL87A with various concentration of FC-2 as a melt additive. The results are in Table 6 as follows:

TABLE 6
	Extruded		Annealed
Wt. %	Films		Extruded Films
FC-2	θadv	θrec	θadv	θrec
0	86	73	106	82
2	106	84	115	99
4	109	87	115	113
6	109	84	118	115
10	114	95	117	113

Ice adhesion testing was carried out on solution cast coatings at AMIL, in addition to the melt processed film described above. The samples were prepared by dip coating the solutions onto the aluminum substrates provided by AMIL. The solutions are as described above, except that in some cases cyclohexanone (Avantor Performance Chemicals, PA) was substituted for about 40 wt. % of the MEK. Results obtained by AMIL are summarized in Table 7.

TABLE 7
		Ice Adhesion	Std.
		kPA	Deviation
Example	Coating Solution	AMIL	AMIL	ARF
CE11	PE36	342	23	1.8
EX31	PE33	211	25	2.2
EX34	PE17	134	12	4.6

Claims

1. An article subject to ice formation during normal use comprising a repellent surface such that the receding contact angle of the surface with water ranges from 90 degrees to 135 degrees; wherein the repellent surface comprises a non-fluorinated organic polymeric binder and a fluorochemical compound having the formula: (Rf-L-P)nARf is a fluorinated group;L is independently an organic divalent linking group;P is a catenary, divalent heteroatom-containing carbonyl moiety;A is hydrocarbon moiety comprising 4 to 40 carbon atoms;and n typically ranges from 1 to 3.

2. The article of claim 1 wherein L is the group SO2N(CH3)(CH2)n— wherein n ranges from 1-4.

3. The article of claim 1 wherein Rf comprises less than 2% of fluorinated groups having greater than 6 carbon atoms.

4. The article of claim 1 wherein Rf comprises less than 25% of fluorinated groups having greater than 4 carbon atoms.

5. The article of claim 1 wherein Rf is CF3(CF2)3— for at least 50 wt.-% of the fluorochemical material.

6. The article of claim 1 wherein the hydrocarbon moiety is a saturated alkylene moiety.

7. The article of claim 1 wherein the fluorochemical material has a fluorine content of at least 25 wt-%.

8. The article of claim 1 wherein n of the formula of claim 4 averages at least 2.

9. The article of claim 1 wherein the non-fluorinated polymeric binder is selected from polystyrene, acrylic, polyester, polyurethane, polyolefin, and polyvinyl chloride.

10. The article of claim 1 wherein the fluorochemical material does not form a covalent bond with the non-fluorinated polymeric binder.

11. The article of claim 1 wherein the repellent surface exhibits a difference between the advancing contact angle and receding contact angle with water of less than 15 degrees.

12. The article of claim 1 wherein the repellent surface exhibits a receding contact angle with water of at least 90 degrees after soaking in water for 24 hours.

13. The article of claim 1 wherein the repellent surface exhibits a receding contact angle with hexadecane of at least 60 degrees.

14. The article of claim 1 wherein the repellent surface exhibits a receding contact angle with hexadecane of at least 50 degrees after soaking in water for 24 hours.

15. The article of claim 1 wherein the fluorochemical material is not a fluoroalkyl silsesquioxane.

16. The article of claim 1 wherein the repellent surface comprises a thermally processable polymer and a fluorochemical material melt additive.

17. The article of claim 1 wherein the article is a heat exchanger.

18. The article of claim 1 wherein the repellent surface reduces the force of ice adhesion in comparison to the same article without the repellent surface.

19. The article claim 1 wherein the repellent surface or coating is free of fluoroalkyl groups with 8 or more carbon atoms.

20. The article of claim 1 wherein the repellent surface or coating exhibits a receding contact angle with a solution containing 10% by weight of 2-n-butoxyethanol and 90% by weight deionized water is at least 45 degrees.