Patent Application
20230010461
The present invention relates to articles with thin, durable anti-reflection coatings with extended infrared transmission.
The disclosure relates to articles with thin, durable anti-reflective structures with extended infrared (IR) transmission, and more particularly to articles with thin, multi-layer anti-reflective coatings with such properties.
Cover articles are often used to protect devices and components within electronic products, to provide a user interface for input and/or display, protect a camera cover and/or sensor, and/or for many other functions. Such products include mobile devices, for example smart phones, smart watches, mp3 players and computer tablets. Cover articles also include architectural articles, transportation articles (e.g., interior and exterior display and non-display articles used in automotive applications, trains, aircraft, sea craft, etc.), appliance articles, or any article that may benefit from some transparency, scratch-resistance, abrasion resistance or a combination thereof. These applications often demand scratch-resistance and strong optical performance characteristics, in terms of maximum light transmittance and minimum reflectance. In some display, camera and sensor applications, the article that covers one or more of these elements should provide mechanical protection, as well as high visible light transmission (e.g., over cameras and displays) and high transmission in IR wavelengths (e.g., 940 nm) (e.g., for sensor applications, such as proximity, light-detection and ranging (LIDAR), and time-of-flight sensors).
Furthermore, for some cover applications it is beneficial that the color exhibited or perceived, in reflection and/or transmission, does not change appreciably as the viewing angle is changed. In display applications, this is because, if the color in reflection or transmission changes with viewing angle to an appreciable degree, the user of the product will perceive a change in color or brightness of the display, which can diminish the perceived quality of the display. In other applications, changes in color may negatively impact the aesthetic appearance or other functional aspects of the device.
These display and non-display articles are often used in applications (e.g., mobile devices) with packaging constraints. In particular, many of these applications can significantly benefit from reductions in overall thickness, even reductions of a few percent. In addition, many of the applications that employ such display and non-display articles benefit from low manufacturing cost, e.g., through the minimization of raw material costs, minimization of process complexity and yield improvements. Smaller packaging with optical and mechanical property performance attributes comparable to existing display and non-display articles can also serve the desire for reduced manufacturing cost (e.g., through less raw material costs, through reductions in the number of layers in an anti-reflective structure, etc.).
The optical performance of cover articles can be improved by using various anti-reflective coatings; however, known anti-reflective coatings are susceptible to wear or abrasion. Such abrasion can compromise any optical performance improvements achieved by the anti-reflective coating. Abrasion damage can include reciprocating sliding contact from counter face objects (e.g., fingers). In addition, abrasion damage can generate heat, which can degrade chemical bonds in the film materials and cause flaking and other types of damage to the cover glass. Since abrasion damage is often experienced over a longer term than the single events that cause scratches, the coating materials disposed experiencing abrasion damage can also oxidize, which further degrades the durability of the coating.
Accordingly, there is a need for new cover articles which are abrasion resistant, have acceptable or improved optical performance, including IR transmission, and are thinner optical structures.
According to some aspects of the disclosure, an article is provided that includes: a substrate having opposing major surfaces including a first major surface and a second major surface; and an optical film structure in direct contact with the first major surface of the substrate, the optical film structure comprising a physical thickness from about 50 nm to less than 500 nm, a plurality of alternating high refractive index (RI) and low RI layers with a first low RI layer directly on and in contact with the first major surface, and a capping low RI layer. The capping low RI layer and the plurality of alternating high RI and low RI layers total three (3) layers to nine (9) layers, wherein each low RI layer and the capping low RI layer comprises a silicon-containing oxide and each high RI layer comprises a silicon-containing nitride or a silicon-containing oxynitride. The article exhibits a maximum hardness of 8 GPa or greater measured over an indentation depth of about 50 nm or greater, the maximum hardness measured by a Berkovich Indenter Hardness Test. Further, the article exhibits a two-side average transmittance that is greater than 85% at infrared wavelengths from 840 nm to 860 nm and greater than 85% at infrared wavelengths from 930 nm to 950 nm at 0° incidence.
According to some aspects of the disclosure, an article is provided that includes: a substrate having opposing major surfaces including a first major surface and a second major surface; and an optical film structure in direct contact with the first major surface of the substrate, the optical film structure comprising a physical thickness from about 50 nm to less than 500 nm, a plurality of alternating high refractive index (RI) and low RI layers with a first low RI layer directly on and in contact with the first major surface, and a capping low RI layer. The capping low RI layer and the plurality of alternating high RI and low RI layers total three (3) layers to nine (9) layers, wherein each low RI layer and the capping low RI layer comprises a silicon-containing oxide and each high RI layer comprises a silicon-containing nitride or a silicon-containing oxynitride. The article exhibits a maximum hardness of 8 GPa or greater measured over an indentation depth of about 50 nm or greater, the maximum hardness measured by a Berkovich Indenter Hardness Test. In addition, a combined physical thickness of the high RI layers is from about 40% to 60% of the physical thickness of the optical film structure. Further, the article exhibits a two-side average transmittance that is greater than 85% at infrared wavelengths from 840 nm to 860 nm and greater than 85% at infrared wavelengths from 930 nm to 950 nm at 0° incidence.
According to some aspects of the disclosure, an article is provided that includes: a substrate having opposing major surfaces including a first major surface and a second major surface; and an optical film structure in direct contact with the first major surface of the substrate, the optical film structure comprising a physical thickness from about 50 nm to less than 500 nm, a plurality of alternating high refractive index (RI) and low RI layers with a first low RI layer directly on and in contact with the first major surface, and a capping low RI layer. The capping low RI layer and the plurality of alternating high RI and low RI layers total three (3) layers to nine (9) layers, wherein each low RI layer and the capping low RI layer comprises a silicon-containing oxide and each high RI layer comprises a silicon-containing nitride or a silicon-containing oxynitride. The article exhibits a maximum hardness of 8 GPa or greater measured over an indentation depth of about 50 nm or greater, the maximum hardness measured by a Berkovich Indenter Hardness Test. In addition, the thickest high RI layer has a physical thickness from 120 nm to 180 nm, the first low RI layer directly on and in contact with the first major surface has a physical thickness from 15 nm to 35 nm, and the capping low RI layer has a thickness from 80 nm to 100 nm. Further, the article exhibits a two-side average transmittance that is greater than 85% at infrared wavelengths from 840 nm to 860 nm and greater than 85% at infrared wavelengths from 930 nm to 950 nm at 0° incidence.
Additional features and advantages will be set forth in the detailed description which follows, and in part will be readily apparent to those skilled in the art from that description or recognized by practicing the embodiments as described herein, including the detailed description which follows, the claims, as well as the appended drawings.
It is to be understood that both the foregoing general description and the following detailed description are merely exemplary, and are intended to provide an overview or framework to understanding the nature and character of the claims.
The accompanying drawings are included to provide a further understanding, and are incorporated in and constitute a part of this specification. The drawings illustrate one or more embodiment(s) and, together with the description, serve to explain, by way of example, principles and operation of the disclosure. It is to be understood that various features of the disclosure disclosed in this specification and in the drawings can be used in any and all combinations. By way of non-limiting examples, the various features of the disclosure may be combined with one another according to the following embodiments.
These and other features, aspects and advantages of the present disclosure are better understood when the following detailed description of the disclosure is read with reference to the accompanying drawings, in which:
In the following detailed description, for purposes of explanation and not limitation, example embodiments disclosing specific details are set forth to provide a thorough understanding of various principles of the present disclosure. However, it will be apparent to one having ordinary skill in the art, having had the benefit of the present disclosure, that the present disclosure may be practiced in other embodiments that depart from the specific details disclosed herein. Moreover, descriptions of well-known devices, methods and materials may be omitted so as not to obscure the description of various principles of the present disclosure. Finally, wherever applicable, like reference numerals refer to like elements.
Ranges can be expressed herein as from “about” one particular value, and/or to “about” another particular value. As used herein, the term “about” means that amounts, sizes, formulations, parameters, and other quantities and characteristics are not and need not be exact, but may be approximate and/or larger or smaller, as desired, reflecting tolerances, conversion factors, rounding off, measurement error and the like, and other factors known to those of skill in the art. When the term “about” is used in describing a value or an end-point of a range, the disclosure should be understood to include the specific value or end-point referred to. Whether or not a numerical value or end-point of a range in the specification recites “about,” the numerical value or end-point of a range is intended to include two embodiments: one modified by “about,” and one not modified by “about.” It will be further understood that the end-points of each of the ranges are significant both in relation to the other end-point, and independently of the other end-point.
The terms “substantial,” “substantially,” and variations thereof as used herein are intended to note that a described feature is equal or approximately equal to a value or description. For example, a “substantially planar” surface is intended to denote a surface that is planar or approximately planar. Moreover, “substantially” is intended to denote that two values are equal or approximately equal. In some embodiments, “substantially” may denote values within about 10% of each other, for example within about 5% of each other, or within about 2% of each other.
Directional terms as used herein—for example “up,” “down,” “right,” “left,” “front,” “back,” “top,” “bottom”—are made only with reference to the figures as drawn and are not intended to imply absolute orientation.
Unless otherwise expressly stated, it is in no way intended that any method set forth herein be construed as requiring that its steps be performed in a specific order. Accordingly, where a method claim does not actually recite an order to be followed by its steps, or it is not otherwise specifically stated in the claims or descriptions that the steps are to be limited to a specific order, it is in no way intended that an order be inferred, in any respect. This holds for any possible non-express basis for interpretation, including: matters of logic with respect to arrangement of steps or operational flow; plain meaning derived from grammatical organization or punctuation; the number or type of embodiments described in the specification.
As used herein, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to a “component” includes embodiments having two or more such components, unless the context clearly indicates otherwise.
Embodiments of the disclosure relate to articles with thin, durable anti-reflective structures, and more particularly to articles with thin, multi-layer anti-reflective coatings exhibiting abrasion resistance, low reflectivity, color less transmittance, color less reflectance, and/or high transmittance in the IR spectrum. Embodiments of these articles possess anti-reflective optical structures with a total physical thickness of about 50 nm to less than 500 nm, while maintaining the hardness, abrasion resistance and optical properties associated with the intended applications for these articles (e.g., as display, camera and sensor covers, housings and substrates for display devices, interior and exterior automotive components, etc.).
Referring to
The anti-reflective coating 120 includes at least three (3) layers. The term “layer” may include a single layer or may include one or more sub-layers. Such sub-layers may be in direct contact with one another. The sub-layers may be formed from the same material or two or more different materials. In one or more alternative embodiments, such sub-layers may have intervening layers of different materials disposed therebetween. In one or more embodiments a layer may include one or more contiguous and uninterrupted layers and/or one or more discontinuous and interrupted layers (i.e., a layer having different materials formed adjacent to one another). A layer or sub-layers may be formed by a discrete deposition or a continuous deposition process. In one or more embodiments, the layer may be formed using only continuous deposition processes, or, alternatively, only discrete deposition processes.
As used herein, the term “dispose” includes coating, depositing and/or forming a material onto a surface. The disposed material may constitute a layer, as defined herein. The phrase “disposed on” includes the instance of forming a material onto a surface such that the material is in direct contact with the surface and also includes the instance where the material is formed on a surface, with one or more intervening material(s) between the disposed material and the surface. The intervening material(s) may constitute a layer, as defined herein.
According to one or more embodiments, the anti-reflective coating 120 of the article 100 (e.g., as shown and described in connection with
The anti-reflective coating 120 and the article 100 may be described in terms of a hardness measured by a Berkovich Indenter Hardness Test. Further, those with ordinary skill in the art can recognize that abrasion resistance of the anti-reflective coating 120 and the article 100 can be correlated to the hardness of these elements. As used herein, the “Berkovich Indenter Hardness Test” includes measuring the hardness of a material on a surface thereof by indenting the surface with a diamond Berkovich indenter. The Berkovich Indenter Hardness Test includes indenting the anti-reflective surface 122 of the article 100 or the surface of the anti-reflective coating 120 (or the surface of any one or more of the layers in the anti-reflective coating) with the diamond Berkovich indenter to form an indent to an indentation depth in the range from about 50 nm to about 500 nm (or the entire thickness of the anti-reflective coating or layer, whichever is less) and measuring the hardness from this indentation at various points along the entire indentation depth range, along a specified segment of this indentation depth (e.g., in the depth range from about 100 nm to about 500 nm), or at a particular indentation depth (e.g., at a depth of 50 nm, 100 nm, 150 nm, 200 nm, 250 nm, 300 nm, 350 nm, 400 nm, 450 nm, 500 nm, etc.) generally using the methods set forth in Oliver, W. C. and Pharr, G. M., “An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments”, J. Mater. Res., Vol. 7, No. 6, 1992, 1564-1583; and Oliver, W. C. and Pharr, G. M., “Measurement of Hardness and Elastic Modulus by Instrument Indentation: Advances in Understanding and Refinements to Methodology”, J. Mater. Res., Vol. 19, No. 1, 2004, 3-20. Further, when hardness is measured over an indentation depth range (e.g., in the depth range from about 50 nm to about 500 nm), the results can be reported as a maximum hardness within the specified range, wherein the maximum hardness is selected from the measurements taken at each depth within that range. As used herein, “hardness” and “maximum hardness” both refer to as-measured hardness values, not averages of hardness values. Similarly, when hardness is measured at an indentation depth, the value of the hardness obtained from the Berkovich Indenter Hardness Test is given for that particular indentation depth.
Typically, in nanoindentation measurement methods (such as by using a Berkovich indenter) of a coating that is harder than the underlying substrate, the measured hardness may appear to increase initially due to development of the plastic zone at shallow indentation depths and then increases and reaches a maximum value or plateau at deeper indentation depths. Thereafter, hardness begins to decrease at even deeper indentation depths due to the effect of the underlying substrate. Where a substrate having an increased hardness compared to the coating is utilized, the same effect can be seen; however, the hardness increases at deeper indentation depths due to the effect of the underlying substrate.
The indentation depth range and the hardness values at certain indentation depth range(s) can be selected to identify a particular hardness response of the optical film structures and layers thereof, described herein, without the effect of the underlying substrate. When measuring hardness of the optical film structure (when disposed on a substrate) with a Berkovich indenter, the region of permanent deformation (plastic zone) of a material is associated with the hardness of the material. During indentation, an elastic stress field extends well beyond this region of permanent deformation. As indentation depth increases, the apparent hardness and modulus are influenced by stress field interactions with the underlying substrate. The substrate influence on hardness occurs at deeper indentation depths (i.e., typically at depths greater than about 10% of the optical film structure or layer thickness). Moreover, a further complication is that the hardness response utilizes a certain minimum load to develop full plasticity during the indentation process. Prior to that certain minimum load, the hardness shows a generally increasing trend.
At small indentation depths (which also may be characterized as small loads) (e.g., up to about 50 nm), the apparent hardness of a material appears to increase dramatically versus indentation depth. This small indentation depth regime does not represent a true metric of hardness; but instead, it reflects the development of the aforementioned plastic zone, which is related to the finite radius of curvature of the indenter. At intermediate indentation depths, the apparent hardness approaches maximum levels. At deeper indentation depths, the influence of the substrate becomes more pronounced as the indentation depths increase. Hardness may begin to drop dramatically once the indentation depth exceeds about 30% of the optical film structure thickness or the layer thickness.
As noted above, those with ordinary skill in the art can consider various test-related considerations in ensuring that the hardness and maximum hardness values of the coating 120 and article 100 obtained from the Berkovich Indenter Hardness Test are indicative of these elements, rather than being unduly influenced by the substrate 110, for example. Further, embodiments of the articles of the disclosure surprisingly demonstrate high hardness values (e.g., a maximum hardness of 8 GPa or greater) associated with the anti-reflective coating 120 despite the relatively low thickness of the coating 120 (i.e., <500 nm). Indeed, as evidenced by the Examples detailed below in subsequent sections, the hardness of the high refractive index (RI) layer(s) 130B within an anti-reflective coating (see, e.g.,
In some embodiments, the anti-reflective coating 120 of the article 100 may exhibit a hardness or a maximum hardness of greater than about 8 GPa, as measured on the anti-reflective surface 122, by a Berkovich Indenter Hardness Test at an indentation depth of about 50 nm or greater. The antireflective coating 120 may exhibit a hardness or maximum hardness of about 8 GPa or greater, about 9 GPa or greater, about 10 GPa or greater, about 11 GPa or greater, about 12 GPa or greater, about 13 GPa or greater, about 14 GPa or greater, about 15 GPa or greater, or about 16 GPa or greater by a Berkovich Indenter Hardness Test at an indentation depth of about 50 nm or greater. The article 100, including the anti-reflective coating 120 and any additional coatings, as described herein, may exhibit a hardness or maximum hardness of about 8 GPa or greater, about 9 GPa or greater, about 10 GPa or greater, about 11 GPa or greater, about 12 GPa or greater, about 13 GPa or greater, or about 14 GPa or greater, as measured on the anti-reflective surface 122 by a Berkovich Indenter Hardness Test at an indentation depth of about 50 nm or greater. Such measured hardness and maximum hardness values may be exhibited by the anti-reflective coating 120 and/or the article 100 over an indentation depth of about 50 nm or greater, about 100 nm or greater (e.g., from about 100 nm to about 300 nm, from about 100 nm to about 400 nm, from about 100 nm to about 500 nm, from about 100 nm to about 600 nm, from about 200 nm to about 300 nm, from about 200 nm to about 400 nm, from about 200 nm to about 500 nm, or from about 200 nm to about 600 nm).
The anti-reflective coating 120 may have at least one layer made of material itself having a maximum hardness (as measured on the surface of such a layer, e.g., a surface of the second high RI layer 130B of
Optical interference between reflected waves from the interface between the anti-reflective coating 120 and air, and from the interface between the anti-reflective coating 120 and substrate 110, can lead to spectral reflectance and/or transmittance oscillations that create apparent color in the article 100. As used herein, the term “transmittance” is defined as the percentage of incident optical power within a given wavelength range transmitted through a material (e.g., the article, the substrate or the optical film or portions thereof). The term “reflectance” is similarly defined as the percentage of incident optical power within a given wavelength range that is reflected from a material (e.g., the article, the substrate, or the optical film or portions thereof). In one or more embodiments, the spectral resolution of the characterization of the transmittance and reflectance is less than 5 nm or 0.02 eV. The color may be more pronounced in reflection. The angular color shifts in reflection with viewing angle due to a shift in the spectral reflectance oscillations with incident illumination angle. Angular color shifts in transmittance with viewing angle are also due to the same shift in the spectral transmittance oscillation with incident illumination angle. The observed color and angular color shifts with incident illumination angle are often distracting or objectionable to device users, particularly under illumination with sharp spectral features, for example, under fluorescent lighting and some LED lighting. Angular color shifts in transmission may also play a factor in angular color shifts in reflection and vice versa. Factors in angular color shifts in transmission and/or reflection may also include angular color shifts due to viewing angle or color shifts away from a certain white point that may be caused by material absorption (somewhat independent of angle) defined by a particular illuminant or test system.
The oscillations may be described in terms of amplitude. As used herein, the term “amplitude” includes the peak-to-valley change in reflectance or transmittance. The phrase “average amplitude” includes the peak-to-valley change in reflectance or transmittance averaged within the optical wavelength regime. As used herein, the “optical wavelength regime” includes the wavelength range from about 400 nm to about 800 nm (and more specifically from about 450 nm to about 650 nm). According to some embodiments, the optical wavelength range further includes the infrared spectrum from 800 nm to 1000 nm.
The embodiments of this disclosure include an anti-reflective coating (e.g., anti-reflective coating 120 or optical film structure 120) to provide improved optical performance, in terms of colorlessness and/or smaller angular color shifts when viewed at varying incident illumination angles from normal incidence under different illuminants.
One aspect of this disclosure pertains to an article that exhibits colorlessness in reflectance and/or transmittance even when viewed at different incident illumination angles under an illuminant. In one or more embodiments, the article exhibits an angular color shift in reflectance and/or transmittance of about 5 or less, or about 2 or less, between a reference illumination angle and any incidental illumination angles, in the ranges provided herein. As used herein, the phrase “color shift” (angular or reference point) refers to the change in both a* and b*, under the International Commission on Illumination (CIE) L*, a*, b* colorimetry system in reflectance and/or transmittance. It should be understood that unless otherwise noted, the L* coordinate of the articles described herein are the same at any angle or reference point and do not influence color shift. For example, angular color shift may be determined using the following Equation (1):
√((a*2−a*1)2+(b*2−b*1)2) (1)
with a*1, and b*1 representing the a* and b* coordinates of the article when viewed at a reference illumination angle (which may include normal incidence) and a*2, and b*2 representing the a* and b* coordinates of the article when viewed at an incident illumination angle, provided that the incident illumination angle is different from the reference illumination angle and in some cases differs from the reference illumination angle by about 1 degree or more, 2 degrees or more, about 5 degrees or more, about 10 degrees or more, about 15 degrees or more, or about 20 degrees or more. In some instances, an angular color shift in reflectance and/or transmittance of about 10 or less, 9 or less, 8 or less, 7 or less, 6 or less, 5 or less, 4 or less, 3 or less, or even 2 or less is exhibited by the article when viewed at various incident illumination angles from a reference illumination angle, under an illuminant. In some instances the angular color shift in reflectance and/or transmittance is about 1.9 or less, 1.8 or less, 1.7 or less, 1.6 or less, 1.5 or less, 1.4 or less, 1.3 or less, 1.2 or less, 1.1 or less, 1 or less, 0.9 or less, 0.8 or less, 0.7 or less, 0.6 or less, 0.5 or less, 0.4 or less, 0.3 or less, 0.2 or less, or 0.1 or less. In some embodiments, the angular color shift may be about 0. The illuminant can include standard illuminants as determined by the CIE, including A illuminants (representing tungsten-filament lighting), B illuminants (daylight simulating illuminants), C illuminants (daylight simulating illuminants), D series illuminants (representing natural daylight), and F series illuminants (representing various types of fluorescent lighting). In specific examples, the articles exhibit an angular color shift in reflectance and/or transmittance of about 2 or less when viewed at an incident illumination angle from the reference illumination angle under a CIE F2, F10, F11, F12 or D65 illuminant or more specifically under a CIE F2 illuminant.
The reference illumination angle may include normal incidence (i.e., 0 degrees), or 5 degrees from normal incidence, 10 degrees from normal incidence, 15 degrees from normal incidence, 20 degrees from normal incidence, 25 degrees from normal incidence, 30 degrees from normal incidence, 35 degrees from normal incidence, 40 degrees from normal incidence, 50 degrees from normal incidence, 55 degrees from normal incidence, or 60 degrees from normal incidence, provided that the difference between the reference illumination angle and the difference between the incident illumination angle and the reference illumination angle is about 1 degree or more, 2 degrees or more, about 5 degrees or more, about 10 degrees or more, about 15 degrees or more, or about 20 degrees or more. The incident illumination angle may be, with respect to the reference illumination angle, in the range from about 5 degrees to about 80 degrees, from about 5 degrees to about 75 degrees, from about 5 degrees to about 70 degrees, from about 5 degrees to about 65 degrees, from about 5 degrees to about 60 degrees, from about 5 degrees to about 55 degrees, from about 5 degrees to about 50 degrees, from about 5 degrees to about 45 degrees, from about 5 degrees to about 40 degrees, from about 5 degrees to about 35 degrees, from about 5 degrees to about 30 degrees, from about 5 degrees to about 25 degrees, from about 5 degrees to about 20 degrees, from about 5 degrees to about 15 degrees, and all ranges and sub-ranges therebetween, away from normal incidence. The article may exhibit the angular color shifts in reflectance and/or transmittance described herein at and along all the incident illumination angles in the range from about 2 degrees to about 80 degrees, or from about 5 degrees to about 80 degrees, or from about 10 degrees to about 80 degrees, or from about 15 degrees to about 80 degrees, or from about 20 degrees to about 80 degrees, when the reference illumination angle is normal incidence. In some embodiments, the article may exhibit the angular color shifts in reflectance and/or transmittance described herein at and along all the incident illumination angles in the range from about 2 degrees to about 80 degrees, or from about 5 degrees to about 80 degrees, or from about 10 degrees to about 80 degrees, or from about 15 degrees to about 80 degrees, or from about 20 degrees to about 80 degrees, when the difference between the incident illumination angle and the reference illumination angle is about 1 degree or more, 2 degrees or more, about 5 degrees or more, about 10 degrees or more, about 15 degrees or more, or about 20 degrees or more. In one example, the article may exhibit an angular color shift in reflectance and/or transmittance of 2 or less at any incident illumination angle in the range from about 2 degrees to about 60 degrees, from about 5 degrees to about 60 degrees, or from about 10 degrees to about 60 degrees away from a reference illumination angle equal to normal incidence. In other examples, the article may exhibit an angular color shift in reflectance and/or transmittance of 2 or less when the reference illumination angle is 10 degrees and the incident illumination angle is any angle in the range from about 12 degrees to about 60 degrees, from about 15 degrees to about 60 degrees, or from about 20 degrees to about 60 degrees away from the reference illumination angle.
In some embodiments, the angular color shift may be measured at all angles between a reference illumination angle (e.g., normal incidence) and an incident illumination angle in the range from about 20 degrees to about 80 degrees. In other words, the angular color shift may be measured and may be less than about 5, or less than about 2, at all angles in the range from about 0 degrees to about 20 degrees, from about 0 degrees to about 30 degrees, from about 0 degrees to about 40 degrees, from about 0 degrees to about 50 degrees, from about 0 degrees to about 60 degrees, or from about 0 degrees to about 80 degrees.
In one or more embodiments, the article 100 exhibits a color in the CIE L*, a*, b* colorimetry system in reflectance and/or transmittance such that the distance or reference point color shift between the transmittance color or reflectance coordinates from a reference point is less than about 10, less than about 8, less than about 6, less than about 5, less than about 4, less than about 3, or less than about 2, under an illuminant (which can include standard illuminants as determined by the CIE, including A illuminants (representing tungsten-filament lighting), B illuminants (daylight simulating illuminants), C illuminants (daylight simulating illuminants), D series illuminants (representing natural daylight), and F series illuminants (representing various types of fluorescent lighting)). In specific examples, the articles exhibit a color shift in reflectance and/or transmittance of about 2 or less when viewed at an incident illumination angle from the reference illumination angle under a CIE F2, F10, F11, F12 or D65 illuminant or more specifically under a CIE F2 illuminant. Stated another way, the article may exhibit a transmittance color (or transmittance color coordinates) and/or a reflectance color (or reflectance color coordinates) measured at the anti-reflective surface 122 having a reference point color shift of less than about 2 from a reference point, as defined herein. Unless otherwise noted, the transmittance color or transmittance color coordinates are measured on two surfaces of the article including at the anti-reflective surface 122 and the opposite bare surface of the article (i.e., 114). Unless otherwise noted, the reflectance color or reflectance color coordinates are measured on only the anti-reflective surface 122 of the article.
In one or more embodiments, the reference point may be the origin (0, 0) in the CIE L*, a*, b* colorimetry system (or the color coordinates a*=0, b*=0), color coordinates (a*=−2, b*=−2) or the transmittance or reflectance color coordinates of the substrate. It should be understood that unless otherwise noted, the L* coordinate of the articles described herein are the same as the reference point and do not influence color shift. Where the reference point color shift of the article is defined with respect to the substrate, the transmittance color coordinates of the article are compared to the transmittance color coordinates of the substrate and the reflectance color coordinates of the article are compared to the reflectance color coordinates of the substrate.
In one or more specific embodiments, the reference point color shift of the transmittance color and/or the reflectance color may be less than 1 or even less than 0.5. In one or more specific embodiments, the reference point color shift for the transmittance color and/or the reflectance color may be 1.8, 1.6, 1.4, 1.2, 0.8, 0.6, 0.4, 0.2, 0 and all ranges and sub-ranges therebetween. Where the reference point is the color coordinates a*=0, b*=0, the reference point color shift is calculated by Equation (2):
reference point color shift=√((a*article)2+(b*article)2) (2)
In some embodiments, the article 100 may exhibit a transmittance color (or transmittance color coordinates) and a reflectance color (or reflectance color coordinates) such that the reference point color shift is less than 2 when the reference point is any one of the color coordinates of the substrate, the color coordinates a*=0, b*=0 and the color coordinates a*=−2, b*=−2.
In some embodiments, the article 100 may exhibit a first-surface reflected color given by Equation (3) below of less than 5, less than 4, less than 3, less than 2, or even less than 1 for 6° and 20° incidence. In some implementations, the article 100 may exhibit a first-surface reflected color given by Equation (3) below of less than 10, less than 9, less than 8, less than 7, less than 6, less than 5, or even less than 4 for all angles from 0° to 60° incidence.
first-surface reflected color=√((a*article)2+(b*article)2) (3)
where the reflected color coordinates in the CIE L*, a*, b* colorimetry system are measured at one or more angles of incidence.
In some embodiments, the article 100 may exhibit a two-surface transmitted color given by Equation (4) below of less than 2, less than 1.8, less than 1.6, less than 1.4, less than 1.2, less than 1.0, or even less than 0.8 for 0° or near-normal incidence.
two-surface transmitted color=√((a*article)2+(b*article)2) (4)
where the transmitted color coordinates in the CIE L*, a*, b* colorimetry system are measured at 0° or near-normal incidence.
The article 100 of one or more embodiments, or the anti-reflective surface 122 of one or more articles, may exhibit a two-surface (e.g., through both major surfaces 112, 114 and one of these surfaces has an anti-reflective coating 120) photopic average light transmittance of about 93% or greater, of about 94% or greater (e.g., about 94% or greater, about 95% or greater, about 96% or greater, about 96.5% or greater, about 97% or greater, about 97.5% or greater, about 98% or greater, about 98.5% or greater or about 99% or greater) at 0° or near-normal incidence.
In some embodiments, the article 100, or the anti-reflective surface 122 of one or more articles, may exhibit an average light reflectance of about 1% or less (e.g., 1%, 0.9%, 0.8%, 0.75%, 0.6%, 0.5% or less, or 0.25% or less) over the optical wavelength regime in the range from about 400 nm to about 800 nm. These light transmittance and light reflectance values may be observed over the entire optical wavelength regime or over selected ranges of the optical wavelength regime (e.g., a 100 nm wavelength range, a 150 nm wavelength range, a 200 nm wavelength range, a 250 nm wavelength range, a 280 nm wavelength range, or a 300 nm wavelength range, within the optical wavelength regime). In some embodiments, these light reflectance and transmittance values may be a total reflectance or total transmittance (taking into account reflectance or transmittance on both the anti-reflective surface 122 and the opposite major surface 114). Unless otherwise specified, the average reflectance or transmittance is measured at an incident illumination angle of 0 degrees (however, such measurements may be provided at incident illumination angles of 45 degrees or 60 degrees).
The article 100 of one or more embodiments, or the anti-reflective surface 122 of one or more articles, may exhibit a two-surface average light transmittance of about 93% or greater, about 94% or greater, or about 95% or greater over the optical wavelength regime in the infrared spectrum from about 800 nm to about 1000 nm, from about 900 nm to 1000 nm, from 840 nm to 860 nm, or from 930 nm to 950 nm at 0° or near-normal incidence. In other implementations, the article 100 may exhibit a two-surface average light transmittance of about 85% or greater, about 87% or greater, about 89% or greater, about 91% or greater, about 93% or greater, or about 95% or greater over the optical wavelength regime in the infrared spectrum from about 800 nm to about 1000 nm, from about 900 nm to 1000 nm, from 840 nm to 860 nm, or from 930 nm to 950 nm at 0° or near-normal incidence. In some embodiments, the article 100, or the anti-reflective surface 122 of one or more articles, may exhibit an average light reflectance of about 3% or less, 2.5% or less, 2% or less, 1.5% or less, 1% or less, 0.75% or less, or even about 0.5% or less over the infrared spectrum from about 800 nm to about 1000 nm, from about 900 nm to 1000 nm, from 840 nm to 860 nm, or from 930 nm to 950 nm at 6° incidence. These light transmittance and light reflectance values may be observed over the entire optical wavelength regime or over selected ranges of the optical wavelength regime (e.g., a 100 nm wavelength range, a 150 nm wavelength range, a 200 nm wavelength range, a 250 nm wavelength range, a 280 nm wavelength range, or a 300 nm wavelength range, within the optical wavelength regime). In some of these embodiments, the light reflectance and transmittance values may be a total reflectance or total transmittance (taking into account reflectance or transmittance on both the anti-reflective surface 122 and the opposite major surface 114). Unless otherwise specified, the average reflectance or transmittance of these embodiments is measured at an incident illumination angle of 0 degrees (however, such measurements may be provided at incident illumination angles of 45 degrees or 60 degrees).
In some embodiments, the article 100 of one or more embodiments, or the anti-reflective surface 122 of one or more articles, may exhibit a visible photopic average reflectance of about 1% or less, about 0.9% or less, about 0.8% or less, about 0.7% or less, about 0.6% or less, about 0.5% or less, about 0.4% or less, about 0.3% or less, or about 0.2% or less, over the optical wavelength regime at 6° and 20° incidence. These photopic average reflectance values may be exhibited at incident illumination angles in the range from about 0° to about 20°, from about 0° to about 40°, or from about 0° to about 60°. As used herein, “photopic average reflectance” mimics the response of the human eye by weighting the reflectance versus wavelength spectrum according to the human eye's sensitivity. Photopic average reflectance may also be defined as the luminance, or tristimulus Y value of reflected light, according to known conventions for example CIE color space conventions. The photopic average reflectance is defined in Equation (5) as the spectral reflectance, R(λ), multiplied by the illuminant spectrum, I(λ), and the CIE's color matching function,
In some embodiments, the anti-reflective surface 122 of one or more articles (i.e., when measuring the anti-reflective surface 122 only through a single-sided measurement) may exhibit a visible photopic average reflectance of about 1% or less, about 0.9% or less, about 0.7% or less, about 0.5% or less, about 0.45% or less, about 0.4% or less, about 0.35% or less, about 0.3% or less, about 0.25% or less, or about 0.2% or less. In such “single-sided” measurements as described in this disclosure, the reflectance from the second major surface (e.g., surface 114 shown in
Substrate
The substrate 110 may include an inorganic oxide material and may include an amorphous substrate, a crystalline substrate or a combination thereof. In one or more embodiments, the substrate exhibits a refractive index in the range from about 1.45 to about 1.55, e.g., 1.45, 1.46, 1.47, 1.48, 1.49, 1.50, 1.51, 1.52, 1.53, 1.54, 1.55, and all refractive indices therebetween.
Suitable substrates 110 may exhibit an elastic modulus (or Young's modulus) in the range from about 30 GPa to about 120 GPa. In some instances, the elastic modulus of the substrate may be in the range from about 30 GPa to about 110 GPa, from about 30 GPa to about 100 GPa, from about 30 GPa to about 90 GPa, from about 30 GPa to about 80 GPa, from about 30 GPa to about 70 GPa, from about 40 GPa to about 120 GPa, from about 50 GPa to about 120 GPa, from about 60 GPa to about 120 GPa, from about 70 GPa to about 120 GPa, and all ranges and sub-ranges therebetween. The Young's modulus values for the substrate itself as recited in this disclosure refer to values as measured by a resonant ultrasonic spectroscopy technique of the general type set forth in ASTM E2001-13, titled “Standard Guide for Resonant Ultrasound Spectroscopy for Defect Detection in Both Metallic and Non-metallic Parts.”
In one or more embodiments, the amorphous substrate may include glass, which may be strengthened or non-strengthened. Examples of suitable glass include soda lime glass, alkali aluminosilicate glass, alkali containing borosilicate glass and alkali aluminoborosilicate glass. In some variants, the glass may be free of lithia. In one or more alternative embodiments, the substrate 110 may include crystalline substrates, for example, glass-ceramic, or ceramic, substrates (which may be strengthened or non-strengthened), or may include a single crystal structure, for example, sapphire. In one or more specific embodiments, the substrate 110 includes an amorphous base (e.g., glass) and a crystalline cladding (e.g., sapphire layer, a polycrystalline alumina layer and/or or a spinel (MgAl2O4) layer).
The substrate 110 may be substantially planar or sheet-like, although other embodiments may utilize a curved or otherwise shaped or sculpted substrate. The substrate 110 may be substantially optically clear, transparent and free from light scattering. In such embodiments, the substrate may exhibit an average light transmission over the optical wavelength regime of about 85% or greater, about 86% or greater, about 87% or greater, about 88% or greater, about 89% or greater, about 90% or greater, about 91% or greater or about 92% or greater. In one or more alternative embodiments, the substrate 110 may be opaque or exhibit an average light transmission over the optical wavelength regime of less than about 10%, less than about 9%, less than about 8%, less than about 7%, less than about 6%, less than about 5%, less than about 4%, less than about 3%, less than about 2%, less than about 1%, or less than about 0%. In some embodiments, these light reflectance and transmittance values may be a total reflectance or total transmittance (taking into account reflectance or transmittance on both major surfaces of the substrate) or may be observed on a single side of the substrate (i.e., on the anti-reflective surface 122 only, without taking into account the opposite surface). Unless otherwise specified, the average reflectance or transmittance is measured at an incident illumination angle of 0 degrees (however, such measurements may be provided at incident illumination angles of 45 degrees or 60 degrees). The substrate 110 may optionally exhibit a color, for example white, black, red, blue, green, yellow, orange, etc.
Additionally or alternatively, the physical thickness of the substrate 110 may vary along one or more of its dimensions for aesthetic and/or functional reasons. For example, the edges of the substrate 110 may be thicker as compared to more central regions of the substrate 110. The length, width and physical thickness dimensions of the substrate 110 may also vary according to the application or use of the article 100.
The substrate 110 may be provided using a variety of different processes. For instance, where the substrate 110 includes an amorphous substrate, for example, glass, various forming methods can include float glass processes, rolling processes, updraw processes, and down-draw processes, for example fusion draw and slot draw.
Once formed, a substrate 110 may be strengthened to form a strengthened substrate. As used herein, the term “strengthened substrate” may refer to a substrate that has been chemically strengthened, for example through ion-exchange of larger ions for smaller ions in the surface of the substrate. However, other strengthening methods known in the art, for example thermal tempering, or utilizing a mismatch of the coefficient of thermal expansion between portions of the substrate to create compressive stress and central tension regions, may be utilized to form strengthened substrates.
Where the substrate is chemically strengthened by an ion exchange process, the ions in the surface layer of the substrate are replaced by—or exchanged with—larger ions having the same valence or oxidation state. Ion exchange processes are typically carried out by immersing a substrate in a molten salt bath containing the larger ions to be exchanged with the smaller ions in the substrate. It will be appreciated by those skilled in the art that parameters for the ion exchange process, including, but not limited to, bath composition and temperature, immersion time, the number of immersions of the substrate in a salt bath (or baths), use of multiple salt baths, and any additional steps (e.g., annealing, washing, and the like) are generally determined by the composition of the substrate, the desired compressive stress (CS), and the desired depth of compressive stress (CS) layer (or depth of layer) of the substrate that result from the strengthening operation. By way of example, ion exchange of alkali metal-containing glass substrates may be achieved by immersion in at least one molten bath containing a salt for example, but not limited to, nitrates, sulfates, and chlorides of the larger alkali metal ion. The temperature of the molten salt bath typically is in a range from about 380° C. up to about 450° C., while immersion times range from about 15 minutes up to about 40 hours. However, temperatures and immersion times different from those described above may also be used.
In addition, non-limiting examples of ion exchange processes in which glass substrates are immersed in multiple ion exchange baths, with washing and/or annealing steps between immersions, are described in U.S. patent application Ser. No. 12/500,650, filed Jul. 10, 2009, by Douglas C. Allan et al., entitled “Glass with Compressive Surface for Consumer Applications”, claiming priority from U.S. Provisional Patent Application No. 61/079,995, filed Jul. 11, 2008, in which glass substrates are strengthened by immersion in multiple, successive, ion exchange treatments in salt baths of different concentrations; and U.S. Pat. No. 8,312,739, by Christopher M. Lee et al., issued on Nov. 20, 2012, and entitled “Dual Stage Ion Exchange for Chemical Strengthening of Glass,” claiming priority from U.S. Provisional Patent Application No. 61/084,398, filed Jul. 29, 2008, in which glass substrates are strengthened by ion exchange in a first bath diluted with an effluent ion, followed by immersion in a second bath having a smaller concentration of the effluent ion than the first bath. The contents of U.S. patent application Ser. No. 12/500,650 and U.S. Pat. No. 8,312,739 are incorporated herein by reference in their entirety.
The degree of chemical strengthening achieved by ion exchange may be quantified based on the parameters of central tension (CT), peak CS, depth of compression (DOC, which is the point along the thickness wherein compression changes to tension), and depth of ion layer (DOL). Peak CS, which is a maximum observed compressive stress, may be measured near the surface of the substrate 110 or within the strengthened glass at various depths. A peak CS value may include the measured CS at the surface (CSs) of the strengthened substrate. In other embodiments, the peak CS is measured below the surface of the strengthened substrate. Compressive stress (including surface CS) is measured by a surface stress meter (FSM) using commercially available instruments such as the FSM-6000, manufactured by Orihara Industrial Co., Ltd. (Japan). Surface stress measurements rely upon the accurate measurement of the stress optical coefficient (SOC), which is related to the birefringence of the glass. SOC in turn is measured according to Procedure C (Glass Disc Method) described in ASTM standard C770-16, entitled “Standard Test Method for Measurement of Glass Stress-Optical Coefficient,” the contents of which are incorporated herein by reference in their entirety. As used herein, DOC means the depth at which the stress in the chemically strengthened alkali aluminosilicate glass article described herein changes from compressive to tensile. DOC may be measured by FSM or a scattered light polariscope (SCALP) depending on the ion exchange treatment. Where the stress in the glass article is generated by exchanging potassium ions into the glass article, FSM is used to measure DOC. Where the stress is generated by exchanging sodium ions into the glass article, SCALP is used to measure DOC. Where the stress in the glass article is generated by exchanging both potassium and sodium ions into the glass, the DOC is measured by SCALP, since it is believed the exchange depth of sodium indicates the DOC and the exchange depth of potassium ions indicates a change in the magnitude of the compressive stress (but not the change in stress from compressive to tensile); the exchange depth of potassium ions in such glass articles is measured by FSM. Maximum CT values are measured using a scattered light polariscope (SCALP) technique known in the art. Refracted near-field (RNF) method or SCALP may be used to measure (graph, depict visually, or otherwise map out) the complete stress profile. When the RNF method is utilized to measure the stress profile, the maximum CT value provided by SCALP is utilized in the RNF method. In particular, the stress profile measured by RNF is force balanced and calibrated to the maximum CT value provided by a SCALP measurement. The RNF method is described in U.S. Pat. No. 8,854,623, entitled “Systems and methods for measuring a profile characteristic of a glass sample”, which is incorporated herein by reference in its entirety. In particular, the RNF method includes placing the glass article adjacent to a reference block, generating a polarization-switched light beam that is switched between orthogonal polarizations at a rate of from 1 Hz to 50 Hz, measuring an amount of power in the polarization-switched light beam and generating a polarization-switched reference signal, wherein the measured amounts of power in each of the orthogonal polarizations are within 50% of each other. The method further includes transmitting the polarization-switched light beam through the glass sample and reference block for different depths into the glass sample, then relaying the transmitted polarization-switched light beam to a signal photodetector using a relay optical system, with the signal photodetector generating a polarization-switched detector signal. The method also includes dividing the detector signal by the reference signal to form a normalized detector signal and determining the profile characteristic of the glass sample from the normalized detector signal.
In some embodiments, a strengthened substrate 110 can have a peak CS of 250 MPa or greater, 300 MPa or greater, 400 MPa or greater, 450 MPa or greater, 500 MPa or greater, 550 MPa or greater, 600 MPa or greater, 650 MPa or greater, 700 MPa or greater, 750 MPa or greater, or 800 MPa or greater. The strengthened substrate may have a DOC of 10 μm or greater, 15 μm or greater, 20 μm or greater (e.g., 25 μm, 30 μm, 35 μm, 40 μm, 45 μm, 50 μm, or greater) and/or a CT of 10 MPa or greater, 20 MPa or greater, 30 MPa or greater, 40 MPa or greater (e.g., 42 MPa, 45 MPa, or 50 MPa or greater) but less than 100 MPa (e.g., 95, 90, 85, 80, 75, 70, 65, 60, 55 MPa or less). In one or more specific embodiments, the strengthened substrate has one or more of the following: a peak CS greater than 500 MPa, a DOC greater than 15 μm, and a CT greater than 18 MPa.
Example glasses that may be used in the substrate may include alkali aluminosilicate glass compositions or alkali aluminoborosilicate glass compositions, though other glass compositions are contemplated. Such glass compositions are capable of being chemically strengthened by an ion exchange process. One example glass composition comprises SiO2, B2O3 and Na2O, where (SiO2+B2O3)≥66 mol. %, and Na2O≥9 mol. %. In some embodiments, the glass composition includes about 6 wt. % aluminum oxide or more. In some embodiments, the substrate includes a glass composition with one or more alkaline earth oxides, such that a content of alkaline earth oxides is about 5 wt. % or more. Suitable glass compositions, in some embodiments, further comprise at least one of K2O, MgO, or CaO. In some embodiments, the glass compositions used in the substrate can comprise 61-75 mol. % SiO2; 7-15 mol. % Al2O3; 0-12 mol. % B2O3; 9-21 mol. % Na2O; 0-4 mol. % K2O; 0-7 mol. % MgO; and 0-3 mol. % CaO.
A further example glass composition suitable for the substrate comprises: 60-70 mol. % SiO2; 6-14 mol. % Al2O3; 0-15 mol. % B2O3; 0-15 mol. % Li2O; 0-20 mol. % Na2O; 0-10 mol. % K2O; 0-8 mol. % MgO; 0-10 mol. % CaO; 0-5 mol. % ZrO2; 0-1 mol. % SnO2; 0-1 mol. % CeO2; less than 50 ppm As2O3; and less than 50 ppm Sb2O3; where 12 mol. %≤(Li2O+Na2O+K2O)≤20 mol. % and 0 mol. %≤(MgO+CaO)≤10 mol. %.
A still further example glass composition suitable for the substrate comprises: 63.5-66.5 mol. % SiO2; 8-12 mol. % Al2O3; 0-3 mol. % B2O3; 0-5 mol. % Li2O; 8-18 mol. % Na2O; 0-5 mol. % K2O; 1-7 mol. % MgO; 0-2.5 mol. % CaO; 0-3 mol. % ZrO2; 0.05-0.25 mol. % SnO2; 0.05-0.5 mol. % CeO2; less than 50 ppm As2O3; and less than 50 ppm Sb2O3; where 14 mol. %≤(Li2O+Na2O+K2O)≤18 mol. % and 2 mol. %≤(MgO+CaO)≤7 mol. %.
In some embodiments, an alkali aluminosilicate glass composition suitable for the substrate 110 comprises alumina, at least one alkali metal and, in some embodiments, greater than 50 mol. % SiO2, in other embodiments 58 mol. % SiO2 or more, and in still other embodiments 60 mol. % SiO2 or more, wherein the ratio (Al2O3+B2O3)/Σmodifiers (i.e., sum of modifiers) is greater than 1, wherein the ratio of these components are expressed in mol. % and the modifiers are alkali metal oxides. This glass composition, in particular embodiments, comprises: 58-72 mol. % SiO2; 9-17 mol. % Al2O3; 2-12 mol. % B2O3; 8-16 mol. % Na2O; and 0-4 mol. % K2O, wherein the ratio (Al2O3+B2O3)/Σmodifiers (i.e., sum of modifiers) is greater than 1.
In some embodiments, the substrate 110 may include an alkali aluminosilicate glass composition comprising: 64-68 mol. % SiO2; 12-16 mol. % Na2O; 8-12 mol. % Al2O3; 0-3 mol. % B2O3; 2-5 mol. % K2O; 4-6 mol. % MgO; and 0-5 mol. % CaO, wherein: 66 mol. %≤SiO2+B2O3+CaO≤69 mol. %; Na2O+K2O+B2O3+MgO+CaO+SrO>10 mol. %; 5 mol. %≤MgO+CaO+SrO≤8 mol. %; (Na2O+B2O3)—Al2O3≤2 mol. %; 2 mol. %≤Na2O—Al2O3≤6 mol. %; and 4 mol. %≤(Na2O+K2O)—Al2O3≤10 mol. %.
In some embodiments, the substrate 110 may comprise an alkali aluminosilicate glass composition comprising: 2 mol. % or more of Al2O3 and/or ZrO2, or 4 mol. % or more of Al2O3 and/or ZrO2.
Where the substrate 110 includes a crystalline substrate, the substrate may include a single crystal, which may include Al2O3. Such single crystal substrates are referred to as sapphire. Other suitable materials for a crystalline substrate include polycrystalline alumina layer and/or spinel (MgAl2O4).
Optionally, the crystalline substrate 110 may include a glass-ceramic substrate, which may be strengthened or non-strengthened. Examples of suitable glass-ceramics may include Li2O—Al2O3—SiO2 system (i.e., LAS-System) glass-ceramics, MgO—Al2O3—SiO2 system (i.e., MAS-System) glass-ceramics, and/or glass-ceramics that include a predominant crystal phase including β-quartz solid solution, β-spodumene ss, cordierite, and lithium disilicate. The glass-ceramic substrates may be strengthened using the chemical strengthening processes disclosed herein. In one or more embodiments, MAS-System glass-ceramic substrates may be strengthened in Li2SO4 molten salt, whereby an exchange of 2Li+ for Mg2+ can occur.
The substrate 110, according to one or more embodiments, can have a physical thickness ranging from about 50 μm to about 5 mm. Example substrate 110 physical thicknesses range from about 50 μm to about 500 μm (e.g., 50, 100, 200, 300, 400 or 500 μm). Further example substrate 110 physical thicknesses range from about 500 μm to about 1000 μm (e.g., 500, 600, 700, 800, 900 or 1000 μm). The substrate 110 may have a physical thickness greater than about 1 mm (e.g., about 2, 3, 4, or 5 mm). In one or more specific embodiments, the substrate 110 may have a physical thickness of 2 mm or less or less than 1 mm. The substrate 110 may be acid polished or otherwise treated to remove or reduce the effect of surface flaws.
Anti-Reflective Coating
As shown in
The physical thickness of the anti-reflective coating 120 may be in the range from about 50 nm to less than 500 nm. In some instances, the physical thickness of the anti-reflective coating 120 may be in the range from about 10 nm to less than 500 nm, from about 50 nm to less than 500 nm, from about 75 nm to less than 500 nm, from about 100 nm to less than 500 nm, from about 125 nm to less than 500 nm, from about 150 nm to less than 500 nm, from about 175 nm to less than 500 nm, from about 200 nm to less than 500 nm, from about 225 nm to less than 500 nm, from about 250 nm to less than 500 nm, from about 300 nm to less than 500 nm, from about 350 nm to less than 500 nm, from about 400 nm to less than 500 nm, from about 450 nm to less than 500 nm, from about 200 nm to about 450 nm, and all ranges and sub-ranges therebetween. For example, the physical thickness of the anti-reflective coating 120 may be from: 10 nm to 490 nm, from 10 nm to 480 nm, from 10 nm to 475 nm, from 10 nm to 460 nm, from 10 nm to 450 nm, from 10 nm to 430 nm, from 10 nm to 425 nm, from 10 nm to 420 nm, from 10 nm to 410 nm, from 10 nm to 400 nm, from 10 nm to 350 nm, from 10 nm to 300 nm, from 10 nm to 250 nm, from 10 nm to 225 nm, from 10 nm to 200 nm, from 15 nm to 490 nm, from 20 nm to 490 nm, from 25 nm to 490 nm, from 30 nm to 490 nm, from 35 nm to 490 nm, from 40 nm to 490 nm, from 45 nm to 490 nm, from 50 nm to 490 nm, from 55 nm to 490 nm, from 60 nm to 490 nm, from 65 nm to 490 nm, from 70 nm to 490 nm, from 75 nm to 490 nm, from 80 nm to 490 nm, from 85 nm to 490 nm, from 90 nm to 490 nm, from 95 nm to 490 nm, from 100 nm to 490 nm, from 10 nm to 485 nm, from 15 nm to 480 nm, from 20 nm to 475 nm, from 25 nm to 460 nm, from 30 nm to 450 nm, from 35 nm to 440 nm, from 40 nm to 430 nm, from 50 nm to 425 nm, from 55 nm to 420 nm, from 60 nm to 410 nm, from 70 nm to 400 nm, from 75 nm to 400 nm, from 80 nm to 390 nm, from 90 nm to 380 nm, from 100 nm to 375 nm, from 110 nm to 370 nm, from 120 nm to 360 nm, from 125 nm to 350 nm, from 130 nm to 325 nm, from 140 nm to 320 nm, from 150 nm to 310 nm, from 160 nm to 300 nm, from 170 nm to 300 nm, from 175 nm to 300 nm, from 180 nm to 290 nm, from 190 nm to 280 nm, from 200 nm to 275 nm, from 275 nm to 350 nm. Further, in some implementations of the article 100 shown in
In one or more embodiments, as shown in
As shown in
In the embodiments of the article 100 shown in
In the embodiments of the article 100 shown in
As used herein, the terms “low RI” and “high RI” refer to the relative values for the RI of each layer relative to the RI of another layer within the anti-reflective coating 120 (e.g., low RI<high RI). In one or more embodiments, the term “low RI” when used with the first low RI layer 130A or with the capping layer 131, includes a range from about 1.3 to about 1.8. In one or more embodiments, the term “high RI” when used with the high RI layer 130B, includes a range from greater than about 1.8 to about 2.5, e.g., about 1.9, 2.0, 2.1, 2.2, 2.3, 2.4 or 2.5.
Exemplary materials suitable for use in the anti-reflective coating 120 include: SiO2, Al2O3, GeO2, SiOx, AlOxNy, AlN, oxygen-doped SiNx, SiNx, SiOxNy, SiuAlvOxNy, TiO2, ZrO2, TiN, MgO, HfO2, Y2O3, ZrO2, diamond-like carbon, and MgAl2O4.
Some examples of suitable materials for use in the low RI layer(s) 130A include SiO2, Al2O3, GeO2, SiOx, AlOxNy, SiOxNy, SiuAlvOxNy, MgO, and MgAl2O4. The nitrogen content of the materials for use in the first low RI layer 130A (i.e., the layer 130A in contact with the substrate 110) may be minimized (e.g., in materials, for example, Al2O3 and MgAl2O4). In some embodiments, the low RI layer(s) 130A and the capping layer 131 in the anti-reflective coating 120 can comprise one or more of a silicon-containing oxide (e.g., silicon dioxide), a silicon-containing nitride (e.g., an oxide-doped silicon nitride, silicon nitride, etc.), and a silicon-containing oxynitride (e.g., silicon oxynitride). In some embodiments of the article 100, the low RI layer(s) 130A and the capping layer 131 comprise a silicon-containing oxide, e.g., SiO2 or SiOx.
Some examples of suitable materials for use in the high RI layer(s) 130B include SiuAlvOxNy, AlN, oxygen-doped SiNx, Si3N4, AlOxNy, SiOxNy, HfO2, TiO2, ZrO2, Y2O3, ZrO2, Al2O3, and diamond-like carbon. The oxygen content of the materials for the high RI layer(s) 130B may be minimized, especially in SiNx or AlNx materials. The foregoing materials may be hydrogenated up to about 30% by weight. In some embodiments, the high RI layer(s) 130B in the anti-reflective coating 120 can comprise one or more of a silicon-containing oxide (e.g., silicon dioxide), a silicon-containing nitride (e.g., an oxide-doped silicon nitride, silicon nitride, etc.), and a silicon-containing oxynitride (e.g., silicon oxynitride). In some embodiments of the article 100, the high RI layer(s) 130B comprise a silicon-containing nitride or a silicon-containing oxynitride, e.g., Si3N4 or SiOxNy. The hardness of the high RI layer may be characterized specifically. In some embodiments, the maximum hardness of the high RI layer(s) 130B, as measured by the Berkovich Indenter Hardness Test over an indentation depth of about 50 nm or greater (i.e., as on a hardness test stack with a 2 micron thick layer of the material of the layer 130B disposed on a substrate 110), may be about 18 GPa or greater, about 20 GPa or greater, about 22 GPa or greater, about 24 GPa or greater, about 26 GPa or greater, and all values therebetween.
As used herein, the “AlOxNy,” “SiOxNy,” and “SiuAlxOyNz” materials in the disclosure include various aluminum oxynitride, silicon oxynitride and silicon aluminum oxynitride materials, as understood by those with ordinary skill in the field of the disclosure, described according to certain numerical values and ranges for the subscripts, “u,” “x,” “y,” and “z”. That is, it is common to describe solids with “whole number formula” descriptions, for example Al2O3. It is also common to describe solids using an equivalent “atomic fraction formula” description, for example Al0.4O0.6, which is equivalent to Al2O3. In the atomic fraction formula, the sum of all atoms in the formula is 0.4+0.6=1, and the atomic fractions of Al and O in the formula are 0.4 and 0.6, respectively. Atomic fraction descriptions are described in many general textbooks and atomic fraction descriptions are often used to describe alloys. See, for example: (i) Charles Kittel, Introduction to Solid State Physics, seventh edition, John Wiley & Sons, Inc., NY, 1996, pp. 611-627; (ii) Smart and Moore, Solid State Chemistry, An introduction, Chapman & Hall University and Professional Division, London, 1992, pp. 136-151; and (iii) James F. Shackelford, Introduction to Materials Science for Engineers, Sixth Edition, Pearson Prentice Hall, New Jersey, 2005, pp. 404-418.
Again referring to the “AlOxNy,” “SiOxNy,” and “SiuAlxOyNz” materials in the disclosure, the subscripts allow those with ordinary skill in the art to reference these materials as a class of materials without specifying particular subscript values. To speak generally about an alloy, for example aluminum oxide, without specifying the particular subscript values, we can speak of AlvOx. The description AlvOx can represent either Al2O3 or Al0.4O0.6. If v+x were chosen to sum to 1 (i.e., v+x=1), then the formula would be an atomic fraction description. Similarly, more complicated mixtures can be described, for example SiuAlvOxNy, where again, if the sum u+v+x+y were equal to 1, we would have the atomic fractions description case.
Once again referring to the “AlOxNy,” “SiOxNy,” and “SiuAlxOyNz” materials in the disclosure, these notations allow those with ordinary skill in the art to readily make comparisons to these materials and others. That is, atomic fraction formulas are sometimes easier to use in comparisons. For instance, an example alloy consisting of (Al2O3)0.3(AlN)0.7 is closely equivalent to the formula descriptions Al0.448O0.31N0.241 and also Al367O254N198. Another example alloy consisting of (Al2O3)0.4(AlN)0.6 is closely equivalent to the formula descriptions Al0.438O0.375N0.188 and Al37O32N16. The atomic fraction formulas Al0.448O0.31N0.241 and Al0.438O0.375N0.188 are relatively easy to compare to one another. For instance, Al decreased in atomic fraction by 0.01, O increased in atomic fraction by 0.065 and N decreased in atomic fraction by 0.053. It takes more detailed calculation and consideration to compare the whole number formula descriptions Al367O254N198 and Al37O32N16. Therefore, it is sometimes preferable to use atomic fraction formula descriptions of solids. Nonetheless, the use of AlvOxNy is general since it captures any alloy containing Al, O and N atoms.
As understood by those with ordinary skill in the field of the disclosure with regard to any of the foregoing materials (e.g., AlN) for the anti-reflective coating 120, each of the subscripts, “u,” “x,” “y,” and “z,” can vary from 0 to 1, the sum of the subscripts will be less than or equal to one, and the balance of the composition is the first element in the material (e.g., Si or Al). In addition, those with ordinary skill in the field can recognize that “SiuAlxOyNz” can be configured such that “u” equals zero and the material can be described as “AlOxNy”. Still further, the foregoing compositions for the anti-reflective coating 120 exclude a combination of subscripts that would result in a pure elemental form (e.g., pure silicon, pure aluminum metal, oxygen gas, etc.). Finally, those with ordinary skill in the art will also recognize that the foregoing compositions may include other elements not expressly denoted (e.g., hydrogen), which can result in non-stoichiometric compositions (e.g., SiNx vs. Si3N4). Accordingly, the foregoing materials for the optical film can be indicative of the available space within a SiO2—Al2O3—SiNx—AlN or a SiO2—Al2O3—Si3N4—AlN phase diagram, depending on the values of the subscripts in the foregoing composition representations.
In one or more embodiments, one or more of the layers of the anti-reflective coating 120 of the article 100 (e.g., as shown in
As noted earlier, embodiments of the article 100 are configured such that the physical thickness of one or more of the layers of the anti-reflective coating 120 are minimized. In one or more embodiments, the physical thickness of the high RI layer(s) 130B and/or the low RI layer(s) 130A are minimized such that they total from about 50 nm to less than about 500 nm. In one or more embodiments, the combined physical thickness of the high RI layer(s) 130B, the low RI layer(s) 130A and any capping layer 131 may be from: 10 nm to 490 nm, from 10 nm to 480 nm, from 10 nm to 475 nm, from 10 nm to 460 nm, from 10 nm to 450 nm, from 10 nm to 430 nm, from 10 nm to 425 nm, from 10 nm to 420 nm, from 10 nm to 410 nm, from 10 nm to 400 nm, from 10 nm to 350 nm, from 10 nm to 300 nm, from 10 nm to 250 nm, from 10 nm to 225 nm, from 10 nm to 200 nm, from 15 nm to 490 nm, from 20 nm to 490 nm, from 25 nm to 490 nm, from 30 nm to 490 nm, from 35 nm to 490 nm, from 40 nm to 490 nm, from 45 nm to 490 nm, from 50 nm to 490 nm, from 55 nm to 490 nm, from 60 nm to 490 nm, from 65 nm to 490 nm, from 70 nm to 490 nm, from 75 nm to 490 nm, from 80 nm to 490 nm, from 85 nm to 490 nm, from 90 nm to 490 nm, from 95 nm to 490 nm, from 100 nm to 490 nm, from 10 nm to 485 nm, from 15 nm to 480 nm, from 20 nm to 475 nm, from 25 nm to 460 nm, from 30 nm to 450 nm, from 35 nm to 440 nm, from 40 nm to 430 nm, from 50 nm to 425 nm, from 55 nm to 420 nm, from 60 nm to 410 nm, from 70 nm to 400 nm, from 75 nm to 400 nm, from 80 nm to 390 nm, from 90 nm to 380 nm, from 100 nm to 375 nm, from 110 nm to 370 nm, from 120 nm to 360 nm, from 125 nm to 350 nm, from 130 nm to 325 nm, from 140 nm to 320 nm, from 150 nm to 310 nm, from 160 nm to 300 nm, from 170 nm to 300 nm, from 175 nm to 300 nm, from 180 nm to 290 nm, from 190 nm to 280 nm, from 200 nm to 275 nm, from 275 nm to 350 nm. Further, in some implementations of the article 100 shown in
In one or more embodiments, the combined physical thickness of the high RI layer(s) 130B of the anti-reflective coating 120 of the article 100 shown in
In one or more embodiments of the articles 100 shown in
The article 100 (e.g., as shown in exemplary form in
The additional coating 140 may include a scratch resistant coating. Exemplary materials used in the scratch resistant coating may include an inorganic carbide, nitride, oxide, diamond-like material, or combination of these. Examples of suitable materials for the scratch resistant coating include metal oxides, metal nitrides, metal oxynitride, metal carbides, metal oxycarbides, and/or combinations thereof. Exemplary metals include B, Al, Si, Ti, V, Cr, Y, Zr, Nb, Mo, Sn, Hf, Ta and W. Specific examples of materials that may be utilized in the scratch resistant coating may include Al2O3, AlN, AlOxNy, Si3N4, SiOxNy, SiuAlvOxNy, diamond, diamond-like carbon, SixCy, SixOyCz, ZrO2, TiOxNy and combinations thereof.
In some embodiments, the additional coating 140 includes a combination of easy-to-clean material and scratch resistant material. In one example, the combination includes an easy-to-clean material and diamond-like carbon. Such additional coatings 140 may have a physical thickness in the range from about 5 nm to about 20 nm. The constituents of the additional coating 140 may be provided in separate layers. For example, the diamond-like carbon material may be disposed as a first layer and the easy-to-clean material can be disposed as a second layer on the first layer of diamond-like carbon. The physical thicknesses of the first layer and the second layer may be in the ranges provided above for the additional coating. For example, the first layer of diamond-like carbon may have a physical thickness of about 1 nm to about 20 nm or from about 4 nm to about 15 nm (or more specifically about 10 nm) and the second layer of the easy-to-clean material may have a physical thickness of about 1 nm to about 10 nm (or more specifically about 6 nm). The diamond-like coating may include tetrahedral amorphous carbon (Ta—C), Ta—C:H, and/or Ta—C—H.
A further aspect of this disclosure pertains to a method for forming the articles 100 described herein (e.g., as shown in
In one or more embodiments, the method may include loading the substrate on carriers which are then used to move the substrate in and out of different coating chambers, under load lock conditions so that a vacuum is preserved as the substrate is moved.
The anti-reflective coating 120 (e.g., including layers 130A, 130B and capping layer 131) and/or the additional coating 140 may be formed using various deposition methods, for example, vacuum deposition techniques, chemical vapor deposition (e.g., plasma enhanced chemical vapor deposition (PECVD), low-pressure chemical vapor deposition, atmospheric pressure chemical vapor deposition, and plasma-enhanced atmospheric pressure chemical vapor deposition), physical vapor deposition (e.g., reactive or nonreactive sputtering or laser ablation), thermal or e-beam evaporation and/or atomic layer deposition. Liquid-based methods may also be used for example spraying or slot coating. Where vacuum deposition is utilized, inline processes may be used to form the anti-reflective coating 120 and/or the additional coating 140 in one deposition run. In some instances, the vacuum deposition can be made by a linear PECVD source. In some implementations of the method, and articles 100 made according to the method, the anti-reflective coating 120 can be prepared using a sputtering process (e.g., a reactive sputtering process), chemical vapor deposition (CVD) process, plasma-enhanced chemical vapor deposition process, or some combination of these processes. In one implementation, an anti-reflective coating 120 comprising low RI layer(s) 130A, high RI layer(s) 130B and capping layer 131 can be prepared according to a reactive sputtering process. According to some embodiments, the anti-reflective coating 120 (including low RI layer 130A, high RI layer 130B and capping layer 131) of the article 100 is fabricated using a metal-mode, reactive sputtering in a rotary drum coater. The reactive sputtering process conditions were defined through careful experimentation to achieve the desired combinations of hardness, refractive index, optical transparency, low color and controlled film stress.
In some embodiments, the method may include controlling the physical thickness of the anti-reflective coating 120 (e.g., including its low RI layer(s) 130A, high RI layer(s) 130B and capping layer 131) and/or the additional coating 140 so that it does not vary by more than about 4% along about 80% or more of the area of the anti-reflective surface 122 or from the target physical thickness for each layer at any point along the substrate area. In some embodiments, the physical thickness of the anti-reflective layer coating 120 and/or the additional coating 140 is controlled so that it does not vary by more than about 4% along about 95% or more of the area of the anti-reflective surface 122.
The articles 100 disclosed herein (e.g., as shown in
According to some embodiments, the articles 100 (e.g., as shown in
According to some embodiments, the articles 100 (e.g., as shown in
Various embodiments will be further clarified by the following examples.
The as-fabricated samples of Example 1A (“Ex. 1A”) were formed by providing a glass substrate having a nominal composition of 69 mol. % SiO2, 10 mol. % Al2O3, 15 mol. % Na2O, and 5 mol. % MgO and disposing an anti-reflective coating having five (5) layers on the glass substrate, as shown in
Referring now to
Referring now to Tables 2A-2C below, optical properties were measured on the samples of this Example (i.e. Exs. 1A-1C) and reported in these tables. In Tables 2A-2C, reflectance and transmittance values are reported as polarization averages, that is, average values combining both s- and p-polarization values into a single average. Photopic averages (Y), L*, a*, and b* values were calculated from measured sample data using known methods according to the CIE 1964 standards with 10° observer and D65 illuminant. These create weighted values according to the human eye's response to visible light. Specular reflectance was measured in an angular range of +/−2.5 degrees using an Agilent Cary 5000 UV-Vis-NIR spectrophotometer. 1st-surface reflectance values were obtained by using an index matching oil to couple the back surface of the glass sample to a light absorber.
Referring now to
Referring now to
Referring now to
Referring now to
Referring now to
Referring now to
Referring now to
Referring now to
Referring now to
Referring now to
Referring now to
Embodiment 1. An article is provided that includes: a substrate having opposing major surfaces including a first major surface and a second major surface; and an optical film structure in direct contact with the first major surface of the substrate, the optical film structure comprising a physical thickness from about 50 nm to less than 500 nm, a plurality of alternating high refractive index (RI) and low RI layers with a first low RI layer directly on and in contact with the first major surface, and a capping low RI layer. The capping low RI layer and the plurality of alternating high RI and low RI layers total three (3) layers to nine (9) layers, wherein each low RI layer and the capping low RI layer comprises a silicon-containing oxide and each high RI layer comprises a silicon-containing nitride or a silicon-containing oxynitride. The article exhibits a maximum hardness of 8 GPa or greater measured over an indentation depth of about 50 nm or greater, the maximum hardness measured by a Berkovich Indenter Hardness Test. Further, the article exhibits a two-side average transmittance that is greater than 85% at infrared wavelengths from 840 nm to 860 nm and greater than 85% at infrared wavelengths from 930 nm to 950 nm at 0° incidence.
Embodiment 2. The article of Embodiment 1 is provided, wherein the article exhibits a maximum hardness of 10 GPa or greater measured over an indentation depth of about 50 nm or greater.
Embodiment 3. The article of Embodiment 1 or Embodiment 2 is provided, wherein the article exhibits a single-side average reflectance that is less than 1.5% at infrared wavelengths from 840 nm to 860 nm and less than 3% at infrared wavelengths from 930 nm to 950 nm at 6° incidence.
Embodiment 4. The article of any one of Embodiments 1-3 is provided, wherein the article exhibits a two-side average transmittance that is greater than 92% at infrared wavelengths from 840 nm to 860 nm and greater than 89% at infrared wavelengths from 930 nm to 950 nm at 0° incidence.
Embodiment 5. The article of any one of Embodiments 1˜4 is provided, wherein the article exhibits a single-side photopic average reflectance that is less than 1% at 6° incidence and 20° incidence and a two-surface photopic average transmittance of greater than 93% at 0° incidence.
Embodiment 6. The article of any one of Embodiments 1-5 is provided, wherein the article exhibits a first-surface reflected color (√(a*2+b*2)) of less than 5 at 6° and 20° incidence, a first-surface reflected color (√(a*2+b*2)) of less than 10 for all angles from 0° to 60° incidence, and a two-surface transmitted color (√(a*2+b*2)) of less than 2 at 0° incidence.
Embodiment 7. The article of any one of Embodiments 1-6 is provided, wherein the substrate is a glass substrate or a glass-ceramic substrate.
Embodiment 8. The article of any one of Embodiments 1-7 is provided, wherein the capping low RI layer and the plurality of alternating high RI and low RI layers total five (5) layers to (7) layers.
Embodiment 9. The article of any one of Embodiments 1-8 is provided, wherein the optical film structure comprises a physical thickness from 275 nm to 350 nm, each high RI layer is SiNx, each low RI layer is SiO2 and the capping low RI layer is SiO2.
Embodiment 10. A consumer electronic product is provided which includes: a housing comprising a front surface, a back surface and side surfaces; electrical components at least partially within the housing, the electrical components comprising a controller, a memory, and a display, the display at or adjacent to the front surface of the housing; and a cover substrate disposed over the display. At least one of a portion of the housing or the cover substrate comprises the article of any one of Embodiments 1-9.
Embodiment 11. An article is provided that includes: a substrate having opposing major surfaces including a first major surface and a second major surface; and an optical film structure in direct contact with the first major surface of the substrate, the optical film structure comprising a physical thickness from about 50 nm to less than 500 nm, a plurality of alternating high refractive index (RI) and low RI layers with a first low RI layer directly on and in contact with the first major surface, and a capping low RI layer. The capping low RI layer and the plurality of alternating high RI and low RI layers total three (3) layers to nine (9) layers, wherein each low RI layer and the capping low RI layer comprises a silicon-containing oxide and each high RI layer comprises a silicon-containing nitride or a silicon-containing oxynitride. The article exhibits a maximum hardness of 8 GPa or greater measured over an indentation depth of about 50 nm or greater, the maximum hardness measured by a Berkovich Indenter Hardness Test. In addition, a combined physical thickness of the high RI layers is from about 40% to 60% of the physical thickness of the optical film structure. Further, the article exhibits a two-side average transmittance that is greater than 85% at infrared wavelengths from 840 nm to 860 nm and greater than 85% at infrared wavelengths from 930 nm to 950 nm at 0° incidence.
Embodiment 12. The article of Embodiment 11 is provided, wherein the article exhibits a maximum hardness of 10 GPa or greater measured over an indentation depth of about 50 nm or greater.
Embodiment 13. The article of Embodiment 11 or Embodiment 12 is provided, wherein the article exhibits a single-side average reflectance that is less than 1.5% at infrared wavelengths from 840 nm to 860 nm and less than 3% at infrared wavelengths from 930 nm to 950 nm at 6° incidence.
Embodiment 14. The article of any one of Embodiments 11-13 is provided, wherein the article exhibits a two-side average transmittance that is greater than 89% at infrared wavelengths from 840 nm to 860 nm and greater than 92% at infrared wavelengths from 930 nm to 950 nm at 0° incidence.
Embodiment 15. The article of any one of Embodiments 11-14 is provided, wherein the article exhibits a single-side photopic average reflectance that is less than 1% at 6° incidence and 20° incidence and a two-surface photopic average transmittance of greater than 93% at 0° incidence.
Embodiment 16. The article of any one of Embodiments 11-15 is provided, wherein the article exhibits a first-surface reflected color (√(a*2+b*2)) of less than 5 at 6° and 20° incidence, a first-surface reflected color (√(a*2+b*2)) of less than 10 for all angles from 0° to 60° incidence, and a two-surface transmitted color (√(a*2+b*2)) of less than 2 at 0° incidence.
Embodiment 17. The article of any one of Embodiments 11-16 is provided, wherein the substrate is a glass substrate or a glass-ceramic substrate.
Embodiment 18. The article of any one of Embodiments 11-17 is provided, wherein the capping low RI layer and the plurality of alternating high RI and low RI layers total five (5) layers to (7) layers.
Embodiment 19. The article of any one of Embodiments 11-18 is provided, wherein the optical film structure comprises a physical thickness from 275 nm to 350 nm, each high RI layer is SiNx, each low RI layer is SiO2 and the capping low RI layer is SiO2.
Embodiment 20. The article of any one of Embodiments 11-19 is provided, wherein the combined physical thickness of the high RI layers is from about 45% to 55% of the physical thickness of the optical film structure.
Embodiment 21. A consumer electronic product is provided which includes: a housing comprising a front surface, a back surface and side surfaces; electrical components at least partially within the housing, the electrical components comprising a controller, a memory, and a display, the display at or adjacent to the front surface of the housing; and a cover substrate disposed over the display. At least one of a portion of the housing or the cover substrate comprises the article of any one of Embodiments 11-20.
Embodiment 22. An article is provided that includes: a substrate having opposing major surfaces including a first major surface and a second major surface; and an optical film structure in direct contact with the first major surface of the substrate, the optical film structure comprising a physical thickness from about 50 nm to less than 500 nm, a plurality of alternating high refractive index (RI) and low RI layers with a first low RI layer directly on and in contact with the first major surface, and a capping low RI layer. The capping low RI layer and the plurality of alternating high RI and low RI layers total three (3) layers to nine (9) layers, wherein each low RI layer and the capping low RI layer comprises a silicon-containing oxide and each high RI layer comprises a silicon-containing nitride or a silicon-containing oxynitride. The article exhibits a maximum hardness of 8 GPa or greater measured over an indentation depth of about 50 nm or greater, the maximum hardness measured by a Berkovich Indenter Hardness Test. In addition, the thickest high RI layer has a physical thickness from 120 nm to 180 nm, the first low RI layer directly on and in contact with the first major surface has a physical thickness from 15 nm to 35 nm, and the capping low RI layer has a thickness from 80 nm to 100 nm. Further, the article exhibits a two-side average transmittance that is greater than 85% at infrared wavelengths from 840 nm to 860 nm and greater than 85% at infrared wavelengths from 930 nm to 950 nm at 0° incidence.
Embodiment 23. The article of Embodiment 22 is provided, wherein the article exhibits a maximum hardness of 10 GPa or greater measured over an indentation depth of about 50 nm or greater.
Embodiment 24. The article of Embodiment 22 or Embodiment 23 is provided, wherein the article exhibits a single-side average reflectance that is less than 1.5% at infrared wavelengths from 840 nm to 860 nm and less than 3% at infrared wavelengths from 930 nm to 950 nm at 6° incidence.
Embodiment 25. The article of any one of Embodiments 22-24 is provided, wherein the article exhibits a two-side average transmittance that is greater than 89% at infrared wavelengths from 840 nm to 860 nm and greater than 92% at infrared wavelengths from 930 nm to 950 nm at 0° incidence.
Embodiment 26. The article of any one of Embodiments 22-25 is provided, wherein the article exhibits a single-side photopic average reflectance that is less than 1% at 6° incidence and 20° incidence and a two-surface photopic average transmittance of greater than 93% at 0° incidence.
Embodiment 27. The article of any one of Embodiments 22-26 is provided, wherein the article exhibits a first-surface reflected color (√(a*2+b*2)) of less than 5 at 6° and 20° incidence, a first-surface reflected color (√(a*2+b*2)) of less than 10 for all angles from 0° to 60° incidence, and a two-surface transmitted color (√(a*2+b*2)) of less than 2 at 0° incidence.
Embodiment 28. The article of any one of Embodiments 22-27 is provided, wherein the substrate is a glass substrate or a glass-ceramic substrate.
Embodiment 29. The article of any one of Embodiments 22-28 is provided, wherein the capping low RI layer and the plurality of alternating high RI and low RI layers total five (5) layers to (7) layers.
Embodiment 30. The article of any one of Embodiments 22-29 is provided, wherein the optical film structure comprises a physical thickness from 275 nm to 350 nm, each high RI layer is SiNx, each low RI layer is SiO2 and the capping low RI layer is SiO2.
Embodiment 31. The article of any one of Embodiments 22-30 is provided, wherein the thickest high RI layer has a physical thickness from 125 nm to 160 nm, the first low RI layer directly on and in contact with the first major surface has a physical thickness from 20 nm to 30 nm, and the capping low RI layer has a thickness from 85 nm to 95 nm.
Embodiment 32. A consumer electronic product is provided which includes: a housing comprising a front surface, a back surface and side surfaces; electrical components at least partially within the housing, the electrical components comprising a controller, a memory, and a display, the display at or adjacent to the front surface of the housing; and a cover substrate disposed over the display. At least one of a portion of the housing or the cover substrate comprises the article of any one of Embodiments 22-31.
Many variations and modifications may be made to the above-described embodiments of the disclosure without departing substantially from the spirit and various principles of the disclosure. All such modifications and variations are intended to be included herein within the scope of this disclosure and protected by the following claims. For example, the various features of the disclosure may be combined according to the following embodiments.
This application claims the benefit of priority under 35 U.S.C. § 119 of U.S. Provisional Application No. 63/217,967, filed on Jul. 2, 2021, the contents of which are relied upon and incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 63217967 | Jul 2021 | US |