Patent Application
20200072265
The present application relates to artificial aluminum layers. More specifically, the present application relates to artificial aluminum layers for fastening magnesium castings in self-pierce riveting (SPR) applications.
Self-pierce riveting (SPR) is a high-speed mechanical fastening process for joining two or more sheets of material without a predrilled or punched hole. Typically, SPR processes are conducted by driving a semi-tubular rivet through top layers of material and upsetting the rivet in a lower layer (without completely piercing the lower layer) to form a durable mechanical joint. Attempts have been made to use existing SPR technologies to fasten an aluminum alloy top layer or a steel top layer to a cast magnesium alloy bottom layer. This rivet structure has suffered from limited integrity due to cracking of the magnesium alloy casting. The cracking of the magnesium alloy casting is related to the low formability of magnesium and its alloys. In addition, when magnesium casting is pre-coated (e.g., using electrophoretic coating or with a powder coat), the coating is damaged when forming the buttons on the die. Thus, while lightweight magnesium alloy die castings offer the potential for weight reduction in automotive technologies, mechanical properties of magnesium alloys limit its use in SPR processes.
It would be advantageous to provide an improved artificial aluminum layer for fastening magnesium castings in self-piercing rivet (SPR) applications that overcomes the foregoing challenges. These and other advantageous features will be apparent to those reviewing the present disclosure.
An exemplary embodiment relates to a self-piercing rivet (SPR) joint includes a top layer including at least one steel material or at least one aluminum material, a middle layer including at least one magnesium material, and a bottom artificial aluminum layer including at least one aluminum material.
The present disclosure describes artificial aluminum layers for fastening magnesium castings in self-piercing rivet (SPR) applications.
In one exemplary embodiment as illustrated schematically in
In one embodiment, the at least two different layers of steel of the top layer includes a first layer of steel of a first steel material and a second layer of steel of a second steel material, the first steel material and the second steel material being different from each other.
The steel layer(s) may have a variety of different compositions. For example, in one embodiment, the steel may be a low carbon steel having iron alloyed with about 0.25 wt. % carbon. In another embodiment, the steel may be a high carbon steel having iron alloyed with up to about 2.5 wt. % carbon. In other embodiments, the steel may be a stainless steel having iron alloyed with chromium and nickel. According to other embodiments, any steel may be used comprising at least one of iron, carbon, manganese, chromium, nickel, tungsten, molybdenum, boron, titanium, vanadium, cobalt, niobium, or a combination thereof. For example, the steel layer may comprise CR3 steel, which includes about 0.10% carbon (C), about 0.45% manganese (Mn), at most 0.03% sulfur (S), at most 0.04% phosphorus (P), balance iron (Fe), and trace impurities and/or ferrite-martensite dual phase (DP) 600 steel, which includes about 0.10% carbon (C), about 1.4% manganese (Mn), about 0.14% silicon (Si), balance iron (Fe), and trace impurities.
According to an exemplary embodiment, the top layer includes at least two different layers of steel, at least one of which is a high-strength steel, for example, a high-strength steel comprising at least one of weathering steel, control-rolled steels, pearlite-reduced steels, acicular ferrite steels, dual-phase steels, or microalloyed steels. Weathering steels (i.e. ASTM A242, ASTM A588) exhibit increased resistance to atmospheric corrosion due by forming a corrosion-retarding protective layer on its surface under the influence of external conditions. Control-rolled steels (i.e. hot-rolled steels), which have a highly deformed austenite structure that transforms to a fine equiaxed ferrite structure upon cooling, exhibit improved toughness and strength, ductility, resistance to vibration and shock, formability, and weldability. Pearlite-reduced steels, which have low carbon content and little or no pearlite, have a very fine grain ferrite matrix and are strengthened by precipitation hardening. Acicular ferrite steels are characterized by having a very fine, high strength acicular ferrite structure, a very low carbon content, and good hardenability. Dual-phase steel (i.e. FF 280 DP, DP450, DP500, DP600, DP780 (and derivatives), DP980 (and derivatives), DP1180) is a high-strength steel having a ferritic microstructure and small, uniformly distributed sections of martensite. Typically, this microstructure gives the steels a low yield strength, high rate of work hardening, and good formability. Microalloyed steels, which contain very small additions of niobium, vanadium, and/or titanium, have a refined grain size and/or precipitation hardening.
The at least two different layers of aluminum of the top layer include a first layer of aluminum of a first aluminum material and a second layer of aluminum of a second aluminum material.
In one embodiment, at least one layer of aluminum may be a 1000 series aluminum alloy, a 2000 series aluminum alloy, a 3000 series aluminum alloy, a 4000 series aluminum alloy, a 5000 series aluminum alloy, a 6000 series aluminum alloy, a 7000 series aluminum alloy, or an 8000 series aluminum alloy.
The 1000 series aluminum alloy (i.e. 1050, 1060, 1070, 1100, 1145, 1199, 1350, etc.) is essentially pure aluminum with a minimum 99 wt. % aluminum content and may be work hardened. The 2000 series aluminum alloy (i.e. 2011, 2014, 2024, 2036, 2048, 2090, 2091, 2099, 2124, 2195, 2218, 2219, 2319, 2618, etc.) is alloyed with copper and may be precipitation hardened to strengths comparable to steel. The 3000 series aluminum alloy (i.e. 3003, 3004, 3005, 3102, 3103, 3105, 3303, etc.) is alloyed with manganese and may be work hardened. The 4000 series aluminum alloy (i.e. 4006, 4007, 4015, 4032, 4043, etc.) is alloyed with silicon. The 5000 series aluminum alloy (i.e. 5005, 5010, 5019, 5026, 5050, 5052, 5056, 5059, 5083, 5086, 5154, 5182, 5252, 5254, 5356, 5454, 5456, 5457, 5652, 5657, 5754, Al3Mg, etc.) is alloyed with magnesium and offer enhanced corrosion resistance. The 6000 series aluminum alloy (i.e. 6005, 6009, 6010, 6060, 6061, 6063, 6063A, 6065, 6066, 6070, 6081, 6082, 6101, 6105, 6151, 6162, 6201, 6205, 6262, 6351, 6463, etc.) is alloyed with magnesium and silicon and is machinable, weldable, and may be precipitation hardened. The 7000 series aluminum alloy (i.e. 7005, 7039, 7049, 7050, 7068, 7072, 7075, 7079, 7116, 7129, 7175, 7178, 7475, etc.) is alloyed with zinc and may be precipitation hardened to the highest strengths of any aluminum alloy, with a tensile strength up to 700 MPa. The 8000 series aluminum alloy (i.e. 8011, 8090, etc.) is alloyed with elements which are not covered by 1000-7000 series aluminum alloys.
In one embodiment, the first aluminum material of the top layer and the second aluminum material of the top layer are 6000 series aluminum alloys. In one embodiment, the bottom artificial aluminum layer comprises at least two different layers of aluminum alloy. In one embodiment, the at least two different layers of aluminum alloy of the bottom layer include at least one layer of 5000 series aluminum alloy. According to an exemplary embodiment, the bottom artificial aluminum layer may comprise 5052 aluminum, which includes about 2.2-2.8% magnesium (Mg), at most about 0.15-0.35% chromium (Cr), at most 0.1% copper (Cu), at most 0.4% iron (Fe), at most 0.1% manganese (Mn), at most 0.25% silicon (Si), at most 0.1% zinc (Zn), balance aluminum (Al), and trace amount of other impurities and/or Al3Mg aluminum, which includes.
The middle layer includes at least one magnesium layer, such as a magnesium alloy. In one embodiment, the at least one layer of magnesium alloy may be AE42, AE44, AM20, AM40, AM50, AM60, AM60B, AS21, AS41, AZ31, AZ61, AZ63, AZ80, AZ81, AZ91, Elektron 21, Elektron 675, EZ33, HK31, HM21, HZ32, K1A, LA141, LA103, LAZ43, M1, M1A, QE22, QH21, WE43, WE54, ZC63, ZC71, ZE41, ZK10, ZK20, ZK30, ZK40, ZK51, ZK60, ZK61, ZM21, ZMC711, any alloys with magnesium contents of 80% of higher, or a combination thereof. According to an exemplary embodiment, the magnesium layer may comprise AM60B magnesium alloy, which includes about 5.5-6.5% aluminum (Al), about 0.24-0.6% manganese (Mn), at most about 0.22% zinc (Zn), at most about 0.1% silicon (Si), at most about 0.01% copper (Cu), at most about 0.005% iron (Fe), at most about 0.002% nickel (Ni), balance magnesium (Mg), and trace impurities.
Referring to
In the embodiment of
Conventional SPR joints often suffer from structural defects to the bottom magnesium layer due to severe cracks occurring at the joint buttons of the magnesium layer (
As utilized herein, the terms “approximately,” “about,” “substantially”, and similar terms are intended to have a broad meaning in harmony with the common and accepted usage by those of ordinary skill in the art to which the subject matter of this disclosure pertains. It should be understood by those of skill in the art who review this disclosure that these terms are intended to allow a description of certain features described and claimed without restricting the scope of these features to the precise numerical ranges provided. Accordingly, these terms should be interpreted as indicating that insubstantial or inconsequential modifications or alterations of the subject matter described and claimed are considered to be within the scope of the invention as recited in the appended claims.
References herein to the positions of elements (e.g., “top,” “bottom,” “above,” “below,” etc.) are merely used to describe the orientation of various elements in the FIGURES. It should be noted that the orientation of various elements may differ according to other exemplary embodiments, and that such variations are intended to be encompassed by the present disclosure.
The construction and arrangement of the elements of the SPR joint as shown in the exemplary embodiments are illustrative only. Although only a few embodiments of the present disclosure have been described in detail, those skilled in the art who review this disclosure will readily appreciate that many modifications are possible (e.g., variations in sizes, dimensions, structures, shapes and proportions of the various elements, values of parameters, mounting arrangements, use of materials, colors, orientations, etc.) without materially departing from the novel teachings and advantages of the subject matter recited. For example, elements shown as integrally formed may be constructed of multiple parts or elements, the position of elements may be reversed or otherwise varied, and the nature or number of discrete elements or positions may be altered or varied.
Additionally, the word “exemplary” is used to mean serving as an example, instance, or illustration. Any embodiment or design described herein as “exemplary” is not necessarily to be construed as preferred or advantageous over other embodiments or designs (and such term is not intended to connote that such embodiments are necessarily extraordinary or superlative examples). Rather, use of the word “exemplary” is intended to present concepts in a concrete manner. Accordingly, all such modifications are intended to be included within the scope of the present disclosure. Other substitutions, modifications, changes, and omissions may be made in the design, operating conditions, and arrangement of the preferred and other exemplary embodiments without departing from the scope of the appended claims.
Other substitutions, modifications, changes and omissions may also be made in the design, operating conditions and arrangement of the various exemplary embodiments without departing from the scope of the present invention. For example, any element disclosed in one embodiment may be incorporated or utilized with any other embodiment disclosed herein. Also, for example, the order or sequence of any process or method steps may be varied or re-sequenced according to alternative embodiments. Any means-plus-function clause is intended to cover the structures described herein as performing the recited function and not only structural equivalents but also equivalent structures. Other substitutions, modifications, changes and omissions may be made in the design, operating configuration, and arrangement of the preferred and other exemplary embodiments without departing from the scope of the appended claims.
While this specification contains many specific implementation details, these should not be construed as limitations on the scope of any inventions or of what may be claimed, but rather as descriptions of features specific to particular embodiments of particular inventions. Certain features that are described in this specification in the context of separate embodiments can also be implemented in combination in a single embodiment. Conversely, various features that are described in the context of a single embodiment can also be implemented in multiple embodiments separately or in any suitable sub-combination. Moreover, although features may be described above as acting in certain combinations and even initially claimed as such, one or more features from a claimed combination can in some cases be excised from the combination, and the claimed combination may be directed to a sub-combination or variation of a sub-combination.
Similarly, while operations are depicted in the drawings in a particular order, this should not be understood as requiring that such operations be performed in the particular order shown or in sequential order, or that all illustrated operations be performed, to achieve desirable results. In certain circumstances, multitasking and parallel processing may be advantageous. Moreover, the separation of various system components in the embodiments described above should not be understood as requiring such separation in all embodiments, and it should be understood that the described program components and systems can generally be integrated together in a single software product or packaged into multiple software products.
Thus, particular embodiments of the subject matter have been described. In some cases, the actions recited herein can be performed in a different order and still achieve desirable results. In addition, the processes depicted in the accompanying figures do not necessarily require the particular order shown, or sequential order, to achieve desirable results. In certain implementations, multitasking and parallel processing may be advantageous.