Patent Grant
11607569
This application is a National Stage entry under § 371 of International Application No. PCT/EP2019/050791, filed on Jan. 14, 2019, and which claims the benefit of European Application No. 18153209.4, filed on Jan. 24, 2018. The content of each of these applications is hereby incorporated by reference in their entirety.
The present invention relates to an assembly having a plurality of fire protection profiles and to a method for producing a fire protection profile.
Fire protection insulation materials such as fire protection cushions and fire protection bricks are used to insulate wall and ceiling feedthroughs. Said materials often consist of polyurethane.
These block- or pillow-shaped materials are layered to form a fire stop in an aperture to be sealed.
The disadvantage here is that usually a large number of said units have to be joined to form a fire stop and that the units have to be cut to size in order to adapt to line feedthroughs. Additional sealants are often used in order to reduce cutting, but this is also complex.
A lower density would simplify the installation process, but is disadvantageous in relation to fire resistance. The units usually have a density of 200-400 kg/m3.
Another disadvantage is that the units are produced in a single-mold production method, which is not very effective.
A problem addressed by the present invention is therefore that of providing fire protection that is reliable and is simple to install. A further problem addressed by the invention is that of providing a simplified method for producing fire protection profiles.
This problem is solved by an assembly comprising at least two fire protection profiles which have a hose that is made of a composite material and is filled with a fire protection material, the composite material having an inorganic fiber material which is connected to a film, the fire protection profiles being designed such that they bake together in the event of a fire. In this context, baking means that the fire protection material of a first fire protection profile expands through the composite material of an immediately contiguous second fire protection profile in the direction of the interior of the second fire protection profile and partially penetrates the composite material, and, vice versa, the fire protection material of the second fire protection profile expands in the direction of the interior of the first fire protection profile, which allows a connection between the two fire protection profiles.
The hose made of composite material forms a thermally resistant sleeve, which has the positive effect that a stable ash crust is formed, in particular by compressing the fire protection material. The stable ash crust and the composite material also improve the properties during the hose stream test.
Owing to these positive effects, particularly good fire properties can be achieved at a reduced density. In addition, fewer intumescent additives than usual are required.
For example, the density of the fire protection material in the hardened state can be between 100 kg/m3 and 200 kg/m3, in particular 150 kg/m3. This has the particular advantage that the fire protection profiles can be compressed at least to some extent. This means that there is no need for complex cutting when sealing apertures. For example, a straight cut can be sufficient in order to adapt the fire protection profile to a line feedthrough. In addition, at a lower density, the amount of material used is reduced.
An individual design is possible by means of the film in the composite material, for example by printing on the film. Depending on the selection of the film, the film can also be painted over. For food sectors, a film that has a surface that is easy to clean or a disinfectable film can be selected. In addition, the film can contribute to an improvement in the sealing properties, for example a better seal against smoke, air, sound and odors. Furthermore, the film can be used as a carrier material for the inorganic fiber material.
The film can have or comprise a plastics material, such as a composite film, including composite films having a metal layer, for example aluminum composite films, or can consist of a plastics material.
The fire protection material is, for example, an intumescent material. This ensures particularly reliable fire protection.
According to one embodiment, the fire protection material can comprise polyurethane. Fire protection additives may also be contained in the fire protection material.
The inorganic fiber material can be a woven fabric, a knitted fabric or a non-woven fabric. It is advantageous here that these fiber materials are permeable at least to some extent. In the event of a fire, the fire protection material can therefore intumesce through the fiber material. This allows the fire protection profiles, which are in contact with one another, to bake together. Furthermore, fiber materials of this type are flexible and are easy to handle when producing a fire protection profile.
Glass fibers, basalt fibers, ceramic fibers, metal fibers or threads or wires, or a fiber material made of different materials, such as inorganic composite materials, for example glass fibers having metal wire, are particularly suitable for the fiber material.
The fiber material preferably has a plurality of holes. The fire protection material can intumesce through the holes such that baking of the individual fire protection profiles is promoted. A hole size of approximately 3 mm×3 mm has proven to be particularly advantageous. At this size, sufficient fire protection material can intumesce through the holes; at the same time, there is sufficient dimensional stability of the fire protection profile. However, the hole size can also vary, for example it can be between 1 mm×1 mm and 5 mm×5 mm.
Alternatively or in addition, the fiber material can have combustible fibers and non-combustible fibers. This has the advantage that the fiber material is sufficiently dense during production in order to hold the fire protection material within the hose. However, in the event of a fire, when the combustible fibers are burned, intumescence of the fire protection material through the fiber material is simplified, as a result of which baking of fire protection profiles in contact with one another is facilitated.
A fire protection profile preferably has a rectangular cross section. As a result, the fire debris profiles can be stacked, particularly simply and without gaps, in a wall or ceiling aperture.
Furthermore, the problem is solved according to the invention by a method for producing a fire protection profile, the method comprising the following steps:
A production method of this type is particularly efficient; in particular, fully automated manufacturing involving little manual effort is possible, which leads to lower production costs.
The fire protection profile pieces can be cut to a length of 80 cm, for example, in order to allow easy handling during packaging and transport. Before installation, the profile pieces can be cut into shorter pieces by a user if required.
According to one embodiment, the continuous hose can be glued or welded at a seam. This prevents the continuous hose from being pushed open when the fire protection material is foamed. However, it is also conceivable that fixation be omitted and the hose be glued by the fire protection material during foaming.
In order to give the fire protection profile its shape, the continuous hose can be held, when the fire protection material is foamed, by means of support elements which abut on all sides.
Further advantages and features of the invention can be found in the following description and the drawings to which reference is made. In the drawings:
The fire protection profiles 12 have a hose 18 that is made of a composite material 19 and is filled with a fire protection material 20. A detailed sectional view of a fire protection profile 12 is shown schematically in
The fire protection material 20 is preferably an intumescent material.
The composite material 19 is composed of a film 22 and an inorganic fiber material 24. In
The film 22 forms an outer surface of the fire protection profile 12. This has the advantage that the fire protection profile 12 can be given an individual design by printing on the film 22. Depending on the selection of the film 22, the fire protection profile 12 can also be painted over or easy to clean.
The fiber material 24 can be a woven fabric, a knitted fabric or a non-woven fabric, in particular made of glass fibers, basalt fibers or ceramic fibers, metal fibers or threads or wires, or a fiber material made of different materials, such as inorganic composite materials, for example glass fibers having metal wire.
If a particular temperature is exceeded, for example in the event of a fire, the fire protection material 20 expands and can escape out from the hose 18 through the composite material 19.
In the case of an assembly 10 comprising a plurality of fire protection profiles 12, as shown in
The fire protection material 20 preferably has a low density, for example between 100 kg/m3 and 200 kg/m3. The solids content of the hardened fire protection material is preferably between 20 g and 30 g, in particular 27 g, in each case based on one liter of hardened fire protection material. As a result, the fire protection profile 12 is compressible and can be adapted particularly well to the line feedthrough 16.
A fire protection profile 12 has, for example, a height of 35 mm, a width of 150 mm and a length of 800 mm. In the mounted state, the width extends in a depth direction of the aperture 14 to be sealed. The optimal width therefore depends on the desired fire resistance duration. However, a sufficient fire resistance duration can generally be ensured at a width of 150 mm.
In comparison with fire protection bricks, the fire protection profile 12 has the advantage that, due to its length, only a few profiles are required to seal an aperture 14. In particular, a fire protection profile 12 can extend across an entire width of an aperture 14, as shown in
In one embodiment, the fiber material 24 has combustible fibers 28 and non-combustible fibers 30. In the illustration in
The fiber material 24 also facilitates the formation of a stable ash crust.
First, a composite material 19 is provided, for example in the form of strips, which is formed into a continuous hose 32 by being folded over.
This creates a material overlap, in particular a seam 34, along which the continuous hose 32 can be glued or welded.
A liquid fire protection material 36 is then filled into the continuous hose 32 and foamed. The solids content of the liquid fire protection material 36 is, for example, 18 wt. %.
During the foaming, the continuous hose 32 is stabilized in order to obtain a desired shape of the fire protection profile 12, for example a profile having a substantially rectangular cross section. The stabilization is carried out, for example, by means of conveyor belts which abut on all sides.
After the fire protection material 20 has hardened, the resulting continuous profile can be divided into individual fire protection profiles 12 in a desired length, as shown, for example, in
| Number | Date | Country | Kind |
|---|---|---|---|
| 18153209 | Jan 2018 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2019/050791 | 1/14/2019 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2019/145175 | 8/1/2019 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4015386 | Cook | Apr 1977 | A |
| 9637915 | Hensley | May 2017 | B1 |
| 9833646 | Forg | Dec 2017 | B2 |
| 20030079425 | Morgan | May 2003 | A1 |
| 20040045234 | Morgan | Mar 2004 | A1 |
| 20040157012 | Miller | Aug 2004 | A1 |
| 20060006611 | Foerg | Jan 2006 | A1 |
| 20120251762 | Forg | Oct 2012 | A1 |
| 20140227160 | Olbert | Aug 2014 | A1 |
| 20140360118 | Hensley | Dec 2014 | A1 |
| 20160097197 | Pilz | Apr 2016 | A1 |
| 20220080235 | Sobol | Mar 2022 | A1 |
| Number | Date | Country |
|---|---|---|
| 4139375 | Jun 1993 | DE |
| 43 25 966 | Feb 1995 | DE |
| 10303943 | Jun 2004 | DE |
| 202015002895 | Jul 2015 | DE |
| 0544600 | Jun 1993 | EP |
| 1429436 | Jun 2004 | EP |
| 3628789 | Apr 2020 | EP |
| 2216220 | Oct 1989 | GB |
| WO-9922107 | May 1999 | WO |
| 2017194588 | Nov 2017 | WO |
| Entry |
|---|
| Rectorseal, “Rectorseal Flamesafe Bags”, Sep. 16, 2009, XP055490429, 6 pages. |
| International Search Report dated Feb. 4, 2019 in PCT/EP2019/050791, with English translation, 6 pages. |
| Written Opinion dated Feb. 4, 2019 in PCT/EP2019/050791. |
| Number | Date | Country | |
|---|---|---|---|
| 20210146173 A1 | May 2021 | US |