Patent Application
20230392515
The present invention relates to turbomachine or gas turbine parts between which sealing must be achieved by means of at least one sealing tongue present in grooves or housings at the connecting edges of adjacent parts.
The invention relates for example, but not exclusively, to a turbine ring set for a turbomachine, which set comprises a plurality of ring sectors of composite material with a ceramic matrix. Sealing between adjacent ring sectors is achieved by one or more sealing tongues housed in grooves machined in the connecting edges of the sectors.
Composite materials with a ceramic matrix, or CMC, are known for their good mechanical properties which make them suitable for constituting structural elements, and for their ability to retain these properties at high temperatures. The use of CMC for various hot portions of aeronautical engines has already been considered, especially since CMCs have a lower density than that of refractory metals conventionally used.
The production of a turbine ring set from CMC ring sectors is described in particular in document WO 2017/060604. Sealing between adjacent ring sectors is achieved by one or more sealing tongues housed in grooves machined in the connecting edges of the sectors.
The CMC material developed for turbines is generally based on silicon carbide (SiC) fibers and on SiC matrix. However, due to its manufacturing range, the material still contains silicon in metallic form, called “free silicon”.
The tongues currently used for sealing between the sectors are made of nickel based or cobalt based alloys (for example: HA188). These alloys are chosen for their mechanical strength at high temperature and their resistance to oxidation.
The free silicon can react at high temperature with the Nickel or the Cobalt of the alloy, typically above 700° C. In addition to the temperature activated solid phase diffusion, there may be the formation of a low melting point eutectic which will strongly degrade the CMC and the metal. These reactions are called “CMC/Metal interaction”. However, the metal tongues housed in the sealing grooves are potentially subjected to temperatures above 700° C. and will thus react with the CMC in the machined housing.
There is therefore a need to achieve a sealing between parts of a sectorized set without the risk of chemical reaction or diffusion at high temperature.
To this end, the invention proposes an assembly for a turbine comprising a plurality of sectors which are adjacent to one another, each sector comprising at least one connecting edge of composite material with a ceramic matrix (CMC), each connecting edge comprising at least one groove or a housing and a sealing tongue present in each groove or housing, characterized in that each sealing tongue has a laminated structure comprising a plurality of strips, the upper strip and the lower strip of the laminated structure each being formed by a film of monolithic ceramic material.
The portions of the sealing tongue(s) intended to be in contact with the CMC of the sectors of the assembly, namely the lower and upper faces, formed by a film of ceramic material which is chemically inert with respect to CMC material. This avoids any risk of chemical reaction or diffusion at high temperature between the sealing tongues and the CMC material of the sectors.
Furthermore, each sealing tongue has a laminated structure which gives it greater flexibility and, therefore, good resistance to deformations encountered in operation and/or to adapt to the shape of the groove in which it is intended to be housed (for example angled groove) and thus optimize the sealing.
According to a particular characteristic of the assembly of the invention, the film of monolithic ceramic material has a thickness less than or equal to 50 μm.
According to one embodiment of the assembly of the invention, each sealing tongue comprises one or more intermediate strips present between the lower strip and the upper strip of the laminated structure, each intermediate strip being formed by a film of monolithic ceramic material. According to a particular aspect of this embodiment.
The film of monolithic ceramic material constituting each intermediate strip may have a thickness less than or equal to 50 μm.
According to another embodiment of the assembly of the invention, each sealing tongue comprises one or more intermediate metallic material strips present between the lower strip and the upper strip of the laminated structure. According to a particular aspect of this embodiment, the intermediate metallic material strip(s) are made of a nickel or cobalt based alloy.
According to another particular characteristic of the assembly of the invention, the films of monolithic ceramic material are made of a material selected from: SiC, Si3N4 and any type of oxide ceramic material of the Al2O3, YSZ or silicalate type.
According to another particular characteristic of the assembly of the invention, a fugitive binder is present between the adjacent strips of the laminated structure.
According to another particular characteristic of the assembly of the invention, the sectors are turbine ring sectors each comprising an annular base having an internal face intended to define the internal face of a turbine ring when the ring sector is mounted to a ring support structure and an external face from which extends one or more portions for hooking the ring sector to the ring support structure, each ring sector further comprising two inter-sector connecting edges of composite material with a ceramic matrix present at the circumferential ends of the sector, each inter-sector connecting edge being intended to face a neighboring ring sector when the ring sector is mounted on the ring support structure, each inter-sector connecting edge including one or more grooves in which a sealing tongue is partially housed.
According to another particular characteristic of the assembly of the invention, the sectors are distributor sectors comprising a sector structural body including an aerodynamic profile extending in a radial direction between a lower platform and an external platform and, along a axial direction, between a leading edge and a trailing edge, said sector further comprising two inter-platform connecting edges of composite material with a ceramic matrix present at the circumferential ends of each platform, each inter-platform connecting edge being intended to be opposite a platform of a neighboring sector, each inter-platform connecting edge including one or more grooves in which a sealing tongue is partially housed.
The invention applies generally to any set or assembly for a turbine comprising a plurality of sectors which are adjacent to one another by connecting edges of composite material with a ceramic matrix or CMC, each connecting edge including at least one groove or housing and a sealing tongue present in each groove.
In accordance with the invention, the lower and upper strips are each formed by a film of monolithic ceramic material. This avoids any chemical reaction or diffusion between the CMC material of the connecting edge and the sealing tongue because the contact surfaces of the tongue are made of a material that is chemically inert with respect to the CMC material.
The monolithic ceramic material film of the upper strip 101 and of the lower strip 110 preferably has a thickness EP101, EP110 of less than or equal to 50 μm so as to give the upper and lower strips good flexibility with respect to modes of biasing the sealing tongues which correspond to deformations mainly in bending. The film of monolithic ceramic material may for example have a thickness comprised between 10 μm and 50 μm.
In the example described here, the sealing tongue 100 also comprises several intermediate strips 102 to 109 present between the lower strip 101 and the upper strip 110 of the laminated structure. The intermediate strips here each formed by a film of monolithic ceramic material, for example of the same type as the ceramic material of the films of the lower and upper strips. As for the lower strip 101 and the upper strip 110, the constituent films of the intermediate strips 102 to 109 have a thickness EP102 to EP109 less than or equal to 50 μm, for example comprised between 10 μm and 50 μm.
The juxtaposition of several independent thin strips made of monolithic ceramic material allows to obtain the necessary flexibility for the sealing tongue which cannot be obtained with a sealing tongue being formed by a single thick strip made of monolithic ceramic material due to the fragile nature of monolithic ceramics. In other words, the use of a plurality of independent thin strips made of monolithic ceramic material allows to obtain the flexibility necessary to adapt to the deformations encountered in operation without risk of breakage and/or to adapt to the shape of the groove in which it is intended to be housed (for example angled groove) and thus optimize sealing.
According to an optional characteristic of the invention, layers of fugitive binder 120 can be interposed between the adjacent strips 101 to 110 of the laminated structure as illustrated in
The lower strip 201 constitutes the lower face of the tongue 200 which is intended to contact a lower portion of a groove present on a connecting edge of a sector of an assembly for a turbine, while the upper strip 203 constitutes the upper face of the tongue 200 which is intended to contact an upper portion of a groove present on a connecting edge of a sector of a turbine assembly.
The film of monolithic ceramic material of the upper strip 201 and of the lower strip 203 preferably has a thickness EP201, EP203 of less than or equal to 50 μm so as to give the upper and lower strips good flexibility with respect to modes of biasing the sealing tongues which correspond to deformations mainly in bending. The film of monolithic ceramic material may for example have a thickness of between 10 μm and 50 μm.
In the example described here, the sealing tongue 100 also comprises an intermediate metallic material strip 202 present between the lower strip 201 and the upper strip 203 of the laminated structure. The intermediate metallic material strip 202 may have a thickness EP202 greater than 50 μm, for example between 100 μm and 400 μm. The intermediate strip 202 can be made of a nickel- or cobalt-based alloy.
Chemical reactions or diffusion between the metallic material of the intermediate strip and the CMC of the connecting edge are avoided with the sealing tongue 200 because the intermediate strip 202 is covered by the lower strip 201 and the upper strip 203 which form the surfaces of contact of the tongue with the CMC material of the connecting edge, the lower and upper strips being made of a material that is chemically inert with respect to the CMC material.
According to an optional characteristic of the invention, layers of fugitive binder 220 can be interposed between the adjacent strips 201 to 203 of the laminated structure as illustrated in
According to a variant embodiment, the sealing tongue 200 can comprise several intermediate metallic material strips.
The films of monolithic ceramic material used to form the lower and upper strips as well as the intermediate strips as in the sealing tongues 100 and 200 described previously can be made in particular with a monolithic ceramic material selected from: SiC, Si3N4, and any oxide ceramic material of the Al2O3, YSZ (yttria-stabilized zirconia) or silicalate type.
The sealing tongues which have just been described are used to produce a sealing between the sectors of an assembly for a turbine, the assembly possibly corresponding in particular to a turbine ring or a sectorized distributor.
The turbine ring sector 40 is made of composite material with a ceramic matrix (CMC) and includes two inter-sector connecting edges 42 and 43 present respectively at the circumferential ends of the sector 40. The connecting edge 42 includes a first groove 420 receiving a portion of a first sealing tongue 150, a second groove 421 receiving a portion of a second sealing tongue 151 and a third groove 422 receiving a portion of a third sealing tongue 152. The connection edge 43 also includes three grooves, not shown in
In the example described here, the sealing tongues 150 to 155 have a laminated structure comprising a plurality of strips each being formed by a film of monolithic ceramic material as for the sealing tongue 100 described above. However, the sealing tongues 150 to 155 can also have a laminated structure with a metal core as for the sealing tongue 200 described above.
The laminated structure of the tongues 150 to 155 gives them a flexibility which allows to conform the tongues to the shape of the grooves without risk of breakage. Indeed, with its laminated structure, the tongue according to the invention has a very good resistance against the stresses encountered during its use which are mainly in bending and torsion. In particular, the tongues 152 and 155 can be shaped in a bent shape so as to adapt to the shape respectively of the groove 422 present on the connecting edge 42 and to the shape of the groove (not shown in
The turbine ring sector 80 further comprises at the lower platform 83 two inter-platform connecting edges 830 and 831 present respectively at the circumferential ends of the lower platform 83. Similarly, the turbine ring sector 80 comprises at the external platform 84 two inter-platform connecting edges 840 and 841 present respectively at the circumferential ends of the external platform 84.
The connecting edges 830 and 831 respectively include a groove 8300 and a groove 8310, the groove 8300 receiving a portion of a first sealing tongue 290 while the groove 8310 receives a portion of a second sealing tongue 291. The connecting edge 840 includes two grooves 8400 and 8401 respectively receiving a portion of a third and fourth sealing tongues 292 and 293. The connecting edge 841 also includes two grooves 8410 and 8411 respectively receiving a portion of a fourth sealing tongue 294 and a portion of a fifth sealing tongue 295.
In the example described here, the sealing tongues 290 to 295 have a laminated structure comprising a metal core being formed by one or more metallic material strips and lower and upper strips each being formed by a film of monolithic ceramic material as for the sealing tongue 200 described above. However, the sealing tongues 290 to 295 can also have a laminated structure comprising a plurality of strips formed by a film of monolithic ceramic material as for the sealing tongue 100 described above.
The laminated structure of the tongues 209 to 295 gives them a flexibility which allows to conform the tongues to the shape of the grooves without risk of breakage.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2011153 | Oct 2020 | FR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/FR2021/051890 | 10/27/2021 | WO |