ASSEMBLY OF WET ELECTROSTATIC PRECIPITATOR

Abstract

Wet electrostatic precipitator (WESP) collector tube bundles are formed by a procedure in which strips of conductive material are corrugated, intended abutting surfaces of the corrugated strips are abraded, adhesive is applied to the abraded surfaces, multiple ones of the corrugated strips are assembled with corrugation in abutting relationship, and outer panels are assembled with the resulting hexagonal tube bundle.

Description

FIELD OF THE INVENTION

This invention relates to the assembly of a wet electrostatic precipitator (WESP), in particular collector tube bundles therefor.

BACKGROUND TO THE INVENTION

Wet electrostatic precipitators (WESP) have been used for many years to remove dust, acid mist and other particulates from water-saturated air and other gases by electrostatic means. In a WESP, particulates and/or mist laden water-saturated air flows in a region of the precipitator between discharge and collecting electrodes, where the particulates and/or mist is electrically charged by corona emitted from the high voltage discharge electrodes. As the water-saturated gas flows further within the WESP, the charged particulates matter and/or mist is electrostatically attracted to grounded collecting plates or electrodes where it is collected. The accumulated materials are continuously washed off by both an irrigating film of water and periodic flushing.

This type of system is used to remove pollutants from gas streams exhausting from various industrial sources, such as incinerators, coke ovens, glass furnaces, non-ferrous metallurgical plants, coal-fired generation plants, forest product facilities, food drying plants and petrochemical plants.

The electrodes used in WESPs are commonly formed of stainless steel. In International Patent Application Publication No. WO 2008/154,735 and International Patent Application No. PCT/CA2010/000377 assigned to the assignee hereof and the disclosures of which are incorporated herein by reference, we have described the provision of WESP parts constructed of electrically-conductive corrosion and spark-resistant carbon composites. Such materials show comparable or superior properties to stainless steel and permit WESPs to be constructed at lower cost.

SUMMARY OF INVENTION

We provide herein a procedure for assembly of WESP electrode bundles from conductive carbon composites. The present invention uses a so-called “stacked panel” method of forming hexagonal tubes.

In such a procedure, conductive carbon composite material is molded into corrugated form, the corrugations of mating surfaces of adjacent panels are abraded to expose carbon fibres, adjacent corrugated strips are adhered at their abutting corrugations to form a hexagonal tube bundle, and the corrugated tube bundle is assembled with outer structural panels.

The procedure described herein allows for carbon-carbon contact required for conduction. The procedure is flexible, providing the ability to manufacture one stock generic panels for different size tube bundles with low capital and operating costs. The composite material is light weight yet able to withstand sparking and corrosion.

BRIEF DESCRIPTION OF DRAWING

FIG. 1 is a perspective view of a WESP electric bundle product according to one embodiment of the invention;

FIG. 2 is a perspective view of stacked panels according to one embodiment of the invention;

FIG. 3 is a schematic perspective view of the panel molding step;

FIG. 4 is a schematic perspective view of abrasion of the bonding areas of the panel;

FIG. 5 is a schematic perspective view of the application of bonding material to the abraded areas of the panel;

FIG. 6 is a perspective view of an outer panel with hexagonal corrugation;

FIG. 7 is a perspective view of the outer panel with V corrugation;

FIG. 8 is a perspective view of an inner panel constructed of conductive carbon composite material with hexagonal corrugation; and

FIGS. 9 to 15 illustrate the sequence of assembly of the electrode stack.

DESCRIPTION OF PREFERRED EMBODIMENT

Referring to the drawings, the first step in the assembly procedure is the formation of elongate strips of conductive carbon material which are molded into a corrugated shape (FIGS. 2 and 3).

Any desired molding procedure may be used which enables corrugated strips of carbon composite material to be formed, including vacuum assisted resin transfer molding, as schematically illustrated in FIG. 3 and/or resin infusion.

The conductive composite material utilized herein is a conductive hybrid composite material designed for highly corrosive operating conditions including dry and saturated mist environments with elevated temperatures. The hybrid composite material is a blend of glass and/or carbon fibres and thermosetting resins developed for applications subjected to corona voltage flash over, spark, erosion, corrosion and power arc, including wet electrostatic precipitation. Such resins include thermosetting polyvinyl ester resin.

In particular, the composite material comprises carbon fiber woven roving and/or carbon fibres within a thermosetting resin where extremely strong molecular building blocks form totally cross-linked structures bonded to each other and at interconnects. Carbon fibres are used as the reinforcing material in areas of the strips required to be conductive while a glass fibre wrap can be used to improve the structural strength of the panel assembly (tube bundle).

The surface of the formed strips then are abraded at the raised portions of the corrugations to expose the conductive carbon fibres for fibre-fibre contact with adjacent mated panels. This abrasion provides for stronger bonding and proper electrical conductivity in the bonded areas. Bonding resin then is applied to the abraded mating surface of the corrugated strips (FIGS. 4 and 5).

Another panel then is stacked with the first panel with the corrugations abutting one another to become adhered together (FIG. 2). This procedure is repeated until a stack of hexagonal tubes of the desired size has been prepared.

The outer panels are the main structural components of the tube bundles and holds the dead and earthquake loads of both the upper equipment and the lower tube bundles.

The outer panels are broken down into two corrugation forms. One corrugation form is a “Hat” section corrugation having a hexagonal-shaped ‘H’ corrugation (FIG. 6) and the other is a hex-shaped V corrugation (FIG. 7). These panels, including flanges and stiffening ribs can be constructed of glass-fibre reinforced materials.

The panels may be assembled into the final tube bundles (FIG. 1) utilizing a stack clamp/jig table. The assembly steps are shown in FIGS. 9 to 15.

SUMMARY OF THE DISCLOSURE

In summary of this disclosure, the present invention provides a method of assembly of conductive tube bundles using conductive carbon composite materials. Modifications are possible within the scope of this invention.

Claims

1. A method of forming a hexagonal tube bundle, which comprises: forming strips of conductive material into corrugated strips,abrading intended abutting portion of the corrugated strips,applying adhesive the abraded mating surface(s), andassembling multiple ones of the corrugated strips with corrugations in abutting relationship until the desired bundle size has been achieved.

2. The method of claim 1, wherein said conductive material is a conductive carbon composite material.

3. The method of claim 3, wherein the conductive carbon composite material is a hybrid composite material comprising a blend of carbon fibreglass and/or carbon fibres and thermosetting resin.

4. The method of claim 1 further comprising assembling outer panels with the hexagonal tube bundles.