Atomic oxygen protective coating with resistance to undercutting at defect sites

Abstract

Structures composed at least partially of an organic substrate may be protected from oxidation by applying a catalyst onto said substrate for promoting the combination of atomic oxygen to molecular oxygen. The structure may also be protected by applying both a catalyst and an atomic oxygen shielding layer onto the substrate. The structures to be protected include spacecraft surfaces.

Description

FIELD OF THE INVENTION

The present invention pertains to protective coatings or shielding layers for retarding oxidation of polymeric and other organic surfaces by atomic oxygen. In particular the invention pertains to coatings and shielding layers used to protect spacecraft surfaces in low earth orbit from developing large oxidized cavities caused by atomic oxygen which may cause structural failure of materials.

BACKGROUND

Atomic oxygen protective coatings typically include SiO.sub.x (where x is between 1.9 and 2.0), fluoropolymer-filled silicon dioxide films, and Al.sub.2 O.sub.3. These coatings may be deposited as thin films by ion beam sputtering, electron beam evaporation, chemical vapor deposition, RF magnetron deposition, reactive DC magnetron sputter deposition and the like. Protective coatings for atomic oxygen have been applied over polyimides, graphite epoxy, fluorinated ethylene propylene, and various forms of carbon (such as pyrolytic graphite and carbon-carbon composites).

Abrasion and flexure however, of these protective coatings lead to defects which are susceptible to oxidation. In addition, defects occur as a result of particulate contaminants contacting the surface of the organic material; microscopic roughness and undulations on the protective coating surface; and micrometeoroids or other debris which impact on the protective coating in low earth orbit. These defects enable atomic oxygen to react with the underlying organic, polymeric, substrate.

Atomic oxygen gradually undercuts at defect sites in protective coatings thus oxidizing the underlying polymer. A cavity is formed with portions of the protective coating overhanging this cavity.

For typical spacecraft materials such as polyimide, only about 14% of the incident atomic oxygen will react with the polymer at the bottom of each defect site. Most of the unreacted atomic oxygen that leaves the organic surface is ejected out of the defect opening and back into space. However, as the undercut cavity grows larger around each defect, more and more atomic oxygen, which does not react upon first impact, scatters off the bottom of the atomic oxygen shielding layer. As the atomic oxygen scatters, it again has an opportunity to react with the polymeric material.

U.S. Pat. Nos. 4,560,577, 4,604,181 (Mirtich et al.) and 4,664,980 (Sovey et al.) disclose coating a polymeric substrate with metal oxide to provide protection from oxidation in low earth orbits. Such metal oxide coatings are, however, subject to undercut cavities caused by atomic oxygen.

Protective coatings such as the coating disclosed in the '577, '181 and '980 patents do not recombine atomic oxygen. Consequently, the undercut cavities which inevitably form are continuously exposed to atomic oxygen, which results in a dramatic reduction in the functional lifetime of the underlying structure. Unchecked undercutting ultimately leads to structural failure of protected organic substrates. In the case of solar arrays, this could lead to limiting the duration of the mission or the useful life of the solar array.

U.S. Pat. No. 3,682,100 (Lindberg, Jr.) discloses using a heat-dissociable material for layers which alternate with metal layers in a space vehicle nose cone. The heat dissociable material is selected from hydrides and silver oxide. The outer layer is preferably constructed of ceramic so that upon dissociation of silver oxide, the oxygen does not oxidize the carrier material, but rises to the surface of the nose cone.

U.S. Pat. No. 3,378,411 (Bergen) discloses inhibiting stress corrosion cracking in austenitic stainless steel, particularly upon exposure to chloride, by coating the steel surfaces with an oxide film containing silver, lead and/or cobalt ions.

U.S. Pat. No. 4,757,512 (Macken) discloses silver oxide as a catalyst for oxidizing carbon monoxide to carbon dioxide. There is however, no suggestion of protective coatings for aircraft.

SUMMARY OF THE INVENTION

The present invention protects a structure from oxidation by providing at least one catalyst on a first surface of an organic substrate and at least one atomic oxygen shielding layer.

The present invention protects a structure containing two opposing surfaces from oxidation by providing an atomic oxygen shielding layer on each of said surfaces and a catalyst on each of the atomic oxygen shielding layers. The catalyst is dispersed in at least one atomic oxygen shielding layer or is provided as a discrete layer on at least one of the atomic oxygen shielding layers or alternatively provides for the catalyst to be dispersed in one atomic oxygen shielding layer while it exists as a discrete layer next to the second atomic oxygen shielding layer.

The present invention also protects a polymeric substrate from oxidation by providing an atomic oxygen shielding layer on a catalytic layer coated on said polymer.

The present invention also protects a polymeric substrate from oxidation by applying a first atomic oxygen shielding layer to one surface of the substrate and a second atomic oxygen shielding layer on the second surface of said substrate and providing a catalyst on at least one of the atomic oxygen shielding layers in the form of a dispersion in the shielding layer or a discrete layer.

The present invention further provides a method for retarding oxidation in an atomic oxygen shielding layer protective coating by applying a film of catalytic material on said protective coating, which causes atomic oxygen to combine into diatomic oxygen.

The present invention is also directed to a method for retarding oxidation of an organic substrate in contact with an atomic oxygen shielding layer.

The protective coatings of the present invention retard the growth of undercut cavities produced by atomic oxygen contacting organic surfaces. The protective coatings in accordance with the invention prolong the lifetime of structural surfaces exposed to atomic oxygen by causing atomic oxygen to recombine into diatomic oxygen.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention will be more completely understood by one of ordinary skill in the art with reference to the drawings, wherein:

FIG. 1 shows an organic substrate coated successively with a catalyst and an atomic oxygen shielding layer;

FIG. 2 illustrates a preferred location for the catalyst layer;

FIG. 3 shows a typical atomic oxygen defect site in a protective coating having a concentration of catalytic material at the protective coating-organic substrate interface;

FIG. 4 shows how the growth of an undercut cavity is retarded by applying a protective coating to both sides of a polymeric sheet; and

FIG. 5 is a plot of the mass erosion of a polyimide protected by a recombinative coating in accordance with the invention versus atomic oxygen recombination probability;

FIG. 6 shows a reel-to-reel coating system which provides a silver oxide interface followed by an SiO.sub.x protective coating, wherein RF magnetron sputter sources are used to apply the protective coating to a sheet material.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The present invention provides for protecting a structure containing an organic substrate, having at least two opposing surfaces, from oxidation. The structure may be constructed of any type of material so long as a portion of the structure contains an organic substrate.

Referring to FIGS. 1, an oxidation-protected structure comprises an organic substrate 10. The substrate has at least two surfaces 12 and 14, wherein at least one of the surfaces 12 contains a catalyst 20 which promotes combination of atomic oxygen to form molecular oxygen. The organic substrate 10 is comprised of a polymer. Examples of polymers suitable for use as the organic substrate of the present invention include, but are not limited to a polyimide, a fluoropolymer, graphite epoxy or fluorinated ethylene propylene. Fluorinated ethylene propylene is preferred.

Catalysts useful in the present invention for promoting combination of atomic oxygen to form molecular oxygen are comprised of a metal. Examples of metals useful as catalysts in the present invention include but are not limited to silver, hafnium, gold, rhenium, platinum and irridium. Preferably, the catalyst is a precious metal or precious metal oxide. Examples of metal oxide catalysts useful in the present invention include, but are not limited to, silver oxide, hafnium oxide, rhenium oxide and platinum oxide.

According to FIG. 1, the structure of the present invention can further comprise a first atomic oxygen shielding layer 15 on the surface 12 of the organic substrate which contains the catalyst 20. Examples of materials from which first atomic oxygen shielding layer 15 can be comprised include, but are not limited to, aluminum oxide, silicon oxide, magnesium oxide, aluminum, germanium, indium, tin oxide or other metal or metal oxide which is atomic oxygen durable.

The catalyst can be in the form of a layer 20 distinct from the atomic oxygen shielding layer 15 which interfaces with organic substrate 10 as shown in FIG. 1. Alternatively, the catalyst can be dispersed in the organic substrate layer 10 itself or within the atomic oxygen shielding layer 15.

Catalyst layer 20 has a thickness of about 100 to about 300 .ANG.. First atomic oxygen shielding layer 15 has a thickness of about 600 to about 1 .mu.m, preferably from about 1000 .ANG. to about 1500 .ANG..

FIG. 2 shows a preferred location for the catalyst wherein the catalyst is in the form of a layer 75 distinct from the atomic oxygen shielding layer 70, and which interfaces with substrate 80.

FIG. 3 illustrates the present invention in accordance with FIG. 1 wherein a defect 65 in the oxygen protective coating 45 has been cut away by atomic oxygen to form undercut cavity 60 and thereby expose a part of the polymer substrate 55. While, atomic oxygen entering into this undercut cavity 60 may initially react with the underlying polymer substrate 55, it can be deflected off the polymer to either exit the undercut cavity 60 through the defect 65 or to contact catalyst layer 50. The atomic oxygen reacts with the catalyst layer 50 on the overhanging portion 47 of the atomic oxygen shielding layer 45. Once the atomic oxygen strikes the concentrated layer of catalyst 50, it reassociates with other atomic oxygen to be ejected from the cavity 60 through defect 65 as diatomic oxygen.

According to FIG. 4, the structure can further comprise a second atomic oxygen shielding layer 46 on a second surface 56 of substrate 55 which contains a catalyst. The catalyst 50 can be applied to opposing sides 56 and 58 of an organic substrate as shown in FIG. 4. The atomic oxygen shielding layers 46 are provided on opposing sides 56 and 58 of an organic substrate 55, and a catalyst layer 50 is disposed between the organic substrate 55 and each atomic oxygen shielding layer. Thus, the catalyst may comprise a layer distinct from the atomic oxygen shielding layers on both opposing surfaces. Alternatively, the catalyst may be dispersed in both atomic oxygen shielding layers. In addition, it is possible to have the catalyst dispersed in the first atomic oxygen shielding layer and in the form of a discrete layer adjacent to the second atomic oxygen shielding layer.

The advantage of having a protective coating on each opposing surface of the organic substrate as illustrated in FIG. 4 is that, after atomic oxygen etches through the first atomic oxygen shielding layer 45, it begins to form an undercut cavity 60 through the organic substrate 55 by etching through the polymer. The catalyst 50 on the second atomic oxygen shielding layer 46 in combination with the catalyst 50 on portions 47 of first atomic oxygen shielding layer 45 which overhang the undercut cavity 60 dramatically increase the probability of diatomic oxygen being formed on first impact within the cavity 60. Here the initial erosion reaction occurs only until the polymer 55 is completely eroded to the second oxygen shielding layer 46. As a result, the growth of the undercut cavity is greatly reduced, thereby extending the functional lifetime of a spacecraft blanket or solar array made of this material.

The second atomic oxygen shielding layer 46 has a thickness of about 600 .ANG. to about 1 .mu.m, preferably from about 1000 .ANG. to about 1500 .ANG..

FIG. 5 illustrates the relationship between erosion and the probability of atomic oxygen recombining to form molecular oxygen. The ordinate (y axis) represents erosion as measured in mass after 15 years in orbit over the original mass before erosion and the abscissa (x axis) represents the probability of oxygen recombination. As shown, a 20% chance of recombination of atomic oxygen to molecular oxygen as for example is seen with the present invention, results in 90% of the mass of the protected structure remaining after 15 years. By contrast, only about 45% of a surface without an oxygen recombination catalyst, will remain over the same period of time.

The present invention also comprises a method for retarding oxidation of an organic substrate having at least two surfaces. The method comprises applying to the substrate a catalyst which causes atomic oxygen to combine into diatomic oxygen upon impact with said catalyst. The organic substrate upon which the catalyst is applied is comprised of a polymer which is preferably a polyimide or a fluoropolymer. The catalyst is a metal preferably selected from the group consisting of silver, hafnium, gold, rhenium, platinum and irridium and is most preferably a metal oxide selected from the group consisting of silver oxide, hafnium oxide, rhenium and platinum oxide.

The method according to the present invention can further comprise the step of applying a first atomic oxygen shielding layer on the surface of the catalyst.

The catalyst is deposited by ion beam sputtering, electron beam evaporation, magnetron sputtering, chemical vapor deposition, reactive sputtering or any combination thereof. The catalyst layer is preferably deposited to a thickness of about 100 to about 300 .ANG..

The first atomic oxygen shielding layer is deposited by ion beam sputtering, electron beam evaporation, magnetron sputtering, chemical vapor deposition, reactive sputtering or any combination thereof. The first atomic oxygen shielding layer is preferably deposited to a thickness of about 1000 to about 1500 .ANG..

The method according to the present invention can further comprise adding a second atomic oxygen shielding layer on a second surface of the substrate which contains a catalyst. The second atomic oxygen shielding layer can be deposited to a thickness of about 600 .ANG. to about 1 .mu.m.

FIG. 6 shows a reel-to-reel coating system for applying a catalyst interface and a silicon oxide shielding layer. An example of a typical reel-to-reel coating system is disclosed in U.S. Pat. No. 4,604,181 to Mirtich et al., the disclosure of which is hereby incorporated in its entirety by reference.

According to FIG. 6, two RF magnetron sources 35 and 36 are used--one to deposit the silicon oxide, and one to deposit the catalyst oxide. A single RF magnetron may be used to deposit both the catalyst and the silicon oxide onto the organic sheet 32 which is fed between reels 30 and 25 if the target contains a mixture of silicon oxide and catalysts. When the protective coating is deposited by electron beam evaporation a separate crucible of silver oxide is first evaporated, followed by silicon dioxide or silicon monoxide evaporation.

EXAMPLES

Example 1

A fluorinated ethylene propylene substrate of 0.025 to 0.127 mm thickness is coated with hafnium oxide using sputter deposition until the layer is 100 to 300 .ANG. thick. Then, a layer of SiO.sub.2 is deposited by sputter deposition to a thickness of between 1000-1500 .ANG..

Example 2

The process of Example 1 is used to coat a polyimide substrate using gold as the catalyst layer and SiO.sub.1.9-2.0 as the thin-film protective coating.

Example 3

Silicon oxide, in which gold is dispersed, is deposited on both sides of a fluorinated ethylene propylene substrate to form a layer of 100 to 300 .ANG. thick.

Example 4

Silicon oxide containing gold dispersed therein is deposited on an organic substrate to form a layer of 100 to 300 .ANG. thick. Then a layer of SiO.sub.2 is deposited by sputter deposition to a thickness of between 1000 to 1500 .ANG..

Although the present invention has been described in connection with preferred embodiments, it will be apparent to those skilled in the art that numerous modifications and substitutions are possible without departing from the spirit and scope of the invention defined by the following claims.

Claims

1. An oxidation-protected polymer structure comprising an organic substrate having at least two surfaces wherein at least one of said surfaces supports a metal catalyst which promotes combination of atomic oxygen to form molecular oxygen.

2. The structure of claim 1, wherein said organic substrate is comprised of a polymer.

3. The structure of claim 2, wherein said polymer is a polyimide or a fluoropolymer.

4. The structure of claim 1, wherein said metal catalyst is selected from the group consisting of silver, hafnium, gold, rhenium, platinum and irridium.

5. An oxidation-protected polymer structure comprising an organic substrate having at least two surfaces wherein at least one of said surfaces supports a metal oxide catalyst selected from the group consisting of silver oxide, hafnium oxide, rhenium oxide, and platinum oxide which promotes combination of atomic oxygen to form molecular oxygen.

6. An oxidation-protected polymer structure comprising

an organic substrate having at least two surfaces wherein at least one of said surfaces supports a catalyst layer which promote combination of atomic oxygen to form molecular oxygen, and

an atomic oxygen shielding layer on said catalyst layer.

7. The structure of claim 6, wherein said catalyst layer has a thickness of about 100 to about 300 .ANG..

8. The structure of claim 6, wherein said atomic oxygen shielding layer is comprised of a material selected from the group consisting of aluminum oxide, silicon oxide, magnesium oxide, aluminum, germanium, indium, and tin oxide.

9. The structure of claim 6, wherein said atomic oxygen shielding layer has a thickness of about 1000 to about 1500 .ANG..

10. An oxidation-protected polymer structure comprising,

an organic substrate having at least two surfaces, each of which contains a catalyst which promotes combination of atomic oxygen to form molecular oxygen,

a first atomic oxygen shielding layer on one of said surfaces, and

a second atomic oxygen shielding layer on the other of said surfaces of said substrate.

11. The structure of claim 6, wherein said catalyst layer is formed of a metal selected from the group consisting of silver, hafnium, gold, rhenium, platinum and irridium.

12. The structure of claim 10, wherein said second atomic oxygen shielding layer has a thickness of about 600 .ANG. to about 1 .mu.m.

13. A structure protected from oxidation, comprising:

i) an organic substrate;

ii) an atomic oxygen shielding layer; and

iii) at least one catalyst supported by a surface of said substrate which promotes combination of atomic oxygen to form molecular oxygen selected from the group consisting of a metal and metal oxide, said catalyst being in the form of an independent layer between said substrate and said atomic oxygen shielding layer.

14. The structure of claim 13, wherein said catalyst is selected from the group consisting of silver, hafnium, silver oxide, and hafnium oxide.

15. A structure protected from oxidation comprising:

i) an organic substrate;

ii) a first atomic oxygen shielding layer;

iii) first catalyst on a first surface of said substrate which promotes combination of atomic oxygen to form molecular oxygen selected from the group consisting of a metal and a metal oxide, said first catalyst being in the form of an independent layer between said substrate and said first atomic oxygen shielding layer; and

iv) a second catalyst which promotes combination of atomic oxygen to form molecular oxygen on a second surface of said substrate opposite to said first surface of said substrate.

16. The structure of claim 15, wherein said second catalyst is in the form of an independent layer further comprising a second atomic oxygen shielding layer on said second surface, said independent layer of said second catalyst being interposed between said second surface and said second atomic oxygen shielding layer.