Patent Application
20220081033
The present invention relates to an automotive crashworthiness energy absorptive part and a method for manufacturing the same, and more particularly, to an automotive crashworthiness energy absorptive part configured to be axially crushed when crashworthiness load is input from a front side or a rear side of an automotive body to absorb crashworthiness energy, and a method for manufacturing the same.
There are many technologies to improve automotive crashworthiness energy absorptive properties, such as optimization of shape, structure, and material of automotive parts. Furthermore, in recent years, many technologies have been proposed to improve the crashworthiness energy absorptive properties of an automotive part and reduce the weight of automotive body by foaming and filling a resin (such as foamed resin) inside the automotive part with a closed cross section shape.
For example, Patent Literature 1 discloses the following technology of automotive structural parts. A closed space is formed inside automotive structural parts by aligning the directions of the top portions of hat-shaped cross section parts such as side sills, floor members, and pillars and overlapping the flanges. The structural parts are filled with a foam filler to improve the bending strength and torsional stiffness of the automotive structural parts with a minimum weight increase. This technology improves the rigidity and collision safety of the automotive body.
Furthermore, Patent Literature 2 discloses a technology for filling the internal space of a closed cross section shape such as a pillar with hat-shaped cross section parts facing each other and flanges together with a high-rigidity foam, in which the high-rigidity foam is fixed by compressive counterforce caused by filling and foaming. This technology improves the vibration isolating performance to suppress the transmission of vibration sound, as well as to improve the strength, rigidity, and impact energy absorption.
Patent Literature 1: Japanese Patent Application Laid-open No. 2006-240134
Patent Literature 2: Japanese Patent Application Laid-open No. 2000-318075
According to the technologies disclosed in Patent Literature 1 and Patent Literate 2, by filling the interior of an automotive part with a foam filler or foam, it is possible to improve the strength of the automotive part against bending deformation, impact energy absorption, and rigidity against torsional deformation, and the deformation of the automotive part can be suppressed.
However, for automotive parts such as front side members and crash boxes, which absorb crashworthiness energy by buckling deformation in a bellows-shaped manner when crashworthiness loads are input from the front or rear of the automotive body and cause axial crushing, there is a problem in that even if the technology to fill the interior of the automotive part with a foam filler or foam is applied, it is difficult to improve the crashworthiness energy absorptive properties.
Aspects of the present invention have been made in order to solve the above-mentioned problem, and it is an object thereof to provide an automotive crashworthiness energy absorptive part, which can improve crashworthiness energy absorptive effect by coating the inner surface with a resin and function as a damping material for absorbing vibration occurring in an automotive body, when crashworthiness load is input from the front side or the rear side of the automotive body such as a front side member or a crash box and causes axial crush, and a method for manufacturing the same.
To solve the problem and achieve the object, an automotive crashworthiness energy absorptive part according to aspects of the present invention to be provided at a front portion or a rear portion of an automotive body and configured to be axially crushed when crashworthiness load is input from a front side or a rear side of the automotive body to absorb crashworthiness energy, the automotive crashworthiness energy absorptive part includes: a tubular member configured to be axially crushed to absorb crashworthiness energy, the tubular member having a top portion and side wall portions continuous to the top portion; and a resin configured to coat or patch at least inner surfaces of the top portion and the side wall portions of the tubular member, wherein the coated or patched resin has a thickness of 8 mm or less after being heated and forms at least a part of a peripheral wall portion in a closed cross-sectional space, and adheres to the inner surfaces with an adhesive strength of 10 MPa or more.
Moreover, the automotive crashworthiness energy absorptive part according to aspects of the present invention further includes a release prevention member configured to cover a surface of the resin and join to the inner surface of the side wall portions, in order to prevent the resin from being released from the inner surface, wherein the resin adheres to the release prevention member with an adhesive strength of 10 MPa or more.
Moreover, a method for manufacturing an automotive crashworthiness energy absorptive part according to aspects of the present invention to be provided at a front portion or a rear portion of an automotive body and configured to be axially crushed when crashworthiness load is input from a front side or a rear side of the automotive body to absorb crashworthiness energy, the automotive crashworthiness energy absorptive part including a tubular member having a top portion and side wall portions continuous to the top portion, the method includes: a step of coating or patching an inner surface of the tubular member with a resin with a thickness of 8 mm or less; and a step of adhering the resin to the inner surface of the tubular member with an adhesive strength of 10 MPa or more by performing heat treatment, under a predetermined condition, on the tubular member coated or patched with the resin.
Moreover, a method for manufacturing the automotive crashworthiness energy absorptive part according to aspects of the present invention includes: a step of coating or patching the inner surface of the tubular member with a resin with a thickness of 8 mm or less; a step of joining, to the inner surface of the side wall portions, the release prevention member for preventing the resin that is coating or patching the inner surface from being released from the inner surface, by disposing the release prevention member so as to cover the surface of the resin; and a step of adhering the resin to the inner surface of the tubular member and to the release prevention member, with an adhesive strength of 10 MPa or more by performing heat treatment, under a predetermined condition, on the tubular member coated or patched with the resin.
Moreover, a method for manufacturing the automotive crashworthiness energy absorptive part according to aspects of the present invention includes: a step of coating or patching a release prevention member with a resin with a thickness of 8 mm or less, the release prevention member being configured to prevent the resin from being released from the inner surfaces of the top portion of the tubular member and the side wall portions continuous to the top portion; a step of joining the release prevention member to the inner surface of the side wall portions by disposing the resin that is coating or patching the release prevention member such that the resin contacts the inner surface of the tubular member; and a step of adhering the resin to the inner surface and to the release prevention member, with an adhesive strength of 10 MPa or more by performing heat treatment, under a predetermined condition, on the tubular member having the inner surface to which the release prevention member is joined.
According to aspects of the present invention, in the process of compressive deformation of a tubular member that absorbs crashworthiness energy by axially crushing when crashworthiness load is input from the front or rear of the automotive body, the buckling strength of the tubular member can be increased and buckling deformation can be generated in a bellows shape without reducing the deformation resistance of the tubular member, and a fracture in a bending portion of the buckling deformation of the tubular member can be prevented, thus improving crashworthiness energy absorptive properties. Furthermore, according to aspects of the present invention, vibrations from the automotive engine and vibrations input to the automotive body from various directions during driving a car can be absorbed, thereby improving vibration-damping properties.
Automotive crashworthiness energy absorptive parts and methods for manufacturing the same according to first and second embodiments of the present invention are described below with reference to
As exemplified in
The tubular member 3 is configured to be axially crushed to absorb crashworthiness energy, and has a top portion and side wall portions continuous to the top portion. For example, as illustrated in
The closed cross-sectional space refers to a space formed by a continuous closed cross-section along the axial direction in the tubular member 3 illustrated in
The tubular member 3 having such a closed cross-sectional space is used for automotive parts having a closed cross section shape, such as front side members extending in the front and rear directions of the automotive body at the left and right positions of the front part of the automotive body and forming part of the automotive body frame, and crash boxes installed at the front or rear ends of the automotive body frame. The automotive parts are disposed in the automotive body such that the axial direction (longitudinal direction) of the tubular member 3 coincides with the front and rear directions of the automotive body.
Examples of the types of metal sheets used for the tubular member 3 used as automotive parts include a cold rolled steel sheet, a hot rolled steel sheet, a stainless steel sheet, a zinc-based coating steel sheet, a zinc alloy coating steel sheet, an aluminum alloy coating steel sheet, and an aluminum alloy sheet.
As illustrated in
Examples of the type of the resin 9 in the automotive crashworthiness energy absorptive part 1 according to the first embodiment include a thermoplastic resin, a thermoset resin, and an elastomer resin. Examples of the thermoplastic resin include a vinyl resin (such as vinyl acetate and vinyl chloride), an acrylic resin, a polyamide resin, a polystyrene resin, and a cyanoacrylate resin. Examples of the thermoset resin include an epoxy resin, a urethane resin, an ester resin, a phenolic resin, a melamine resin, and a urea resin. Examples of the elastomer resin include a nitro rubber resin, a styrene butadiene rubber resin, a modified silicone resin, a butyl rubber resin, a urethane rubber resin, and an acrylic rubber resin.
As the resin 9, a foamed resin is preferred in view of the weight reduction of the automotive crashworthiness energy absorptive part 1. Note that, when a foamed resin is used as the resin 9, the foaming ratio is not particularly limited.
Note that the adhesive strength between the resin 9 and the tubular member 3 may be a maximum sheared stress or a mean sheared stress acting on an interface between the metal sheet and the resin. For example, the maximum sheared stress or the mean sheared stress can be determined by crashworthiness analysis of a double-layered square column in which a metal sheet (such as steel sheet) and a resin adhere to each other.
The adhesive strength between the resin 9 and the tubular member 3 may be determined in a manner that a part of the resin 9 and the tubular member 3 after adhesion is cut out, the cut resin 9 and tubular member 3 are placed in a tensile testing machine, and the resin 9 on one side and the tubular member 3 on the other side are pulled. Alternatively, the adhesive strength between the resin 9 and the tubular member 3 may be measured in a manner that a part of the tubular member 3 and the resin 9 after adhesion is cut out and placed in a tensile testing machine, and one part grasps the resin 9 while the other part grasps a gripping part (not shown) formed by bending the tubular member 3 made of metal sheet and pulls the same, or a gripping part is joined to the tubular member 3 and the gripping part grasped by the tensile testing machine and pulled.
As described above, in the automotive crashworthiness energy absorptive part 1 according to the first embodiment, the inner surface of the tubular member 3 is coated with the resin 9, but in accordance with aspects of the present invention, the inner surface of the tubular member may be patched with a plate-shaped resin having a thickness of 8 mm or less with an adhesive. Furthermore, the inner surface of the tubular member may be patched with a film-shaped resin having a thickness of about 100 μm, similarly to a laminate in a laminated steel sheet. The adhesive strength between the plate-shaped resin or the film-shaped resin and the inner surface of the tubular member needs to be 10 MPa or more.
<Method for Manufacturing Automotive Crashworthiness Energy Absorptive Part>
Next, a method for manufacturing an automotive crashworthiness energy absorptive part according to the first embodiment is described.
As exemplified in
At the step of coating the inner surface of the tubular member 3 with the resin 9, the tubular member 3 in which an outer part 5 having a hat-shaped cross section and made of a metal sheet and an inner part 7 having a plate shape and made of a metal sheet are joined may be formed and then the inner surface of the tubular member 3 may be coated with the resin 9 with a thickness of 8 mm or less, or alternatively, sites of the outer part 5 and the inner part 7 corresponding to the inner surface of the tubular member 3 may be coated with the resin with a thickness of 8 mm or less and then the outer part 5 and the inner part 7 may be joined to form the tubular member 3.
Specific examples of the method for coating with the resin 9 include a method for coating the inner surface of the tubular member 3 by spraying the resin 9 with a spray nozzle, a method for coating the inner surface of the tubular member 3 with the resin 9 by use of a brush or the like, and a method for coating the inner surface of the tubular member 3 with the resin 9 by impregnating the tubular member 3 in a tank in which paint containing the resin 9 is stored. Note that a part of the peripheral wall portion in the closed cross-sectional space in the tubular member 3 was coated with the resin in consideration of the weight increased by the resin.
At the step of performing heat treatment, the tubular member 3 coated with the resin 9 is subjected to heat treatment under predetermined conditions to cause the resin 9 to adhere to the inner surface of the tubular member 3 with an adhesive strength of 10 MPa or more. In this case, the resin 9 and the tubular member 3 can adhere to each other by the adhesive capacity of the resin 9 itself or by an adhesive.
In the case of adhesion by the adhesive capacity of the resin 9 itself, heat treatment may be performed after the inner surface of the tubular member 3 is coated with the resin 9, and temperature and time of the heat treatment may be appropriately adjusted depending on the type of the coating resin 9 such that the adhesive strength becomes 10 MPa or more. In the case of adhesion with an adhesive, on the other hand, heat treatment may be performed after the resin 9 and the inner surface of the tubular member 3 adhere to each other with an adhesive, and temperature and time of the heat treatment may be appropriately adjusted such that the adhesive strength of the adhesive becomes 10 MPa or more. The step of performing heat treatment in accordance with aspects of the present invention may serve also as, for example, a step of performing baking finish by painting the outer surface of the tubular member 3 with paint.
Note that, as described above, the adhesive strength between the resin 9 and the inner surface of the tubular member 3 can be determined by crashworthiness analysis of a double-layered square column in which a metal sheet (such as steel sheet) and a resin adhere to each other, or by measurement using a tensile testing machine.
As described above, in the method for manufacturing an automotive crashworthiness energy absorptive part according to the first embodiment, the inner surface of the tubular member 3 is coated with the resin 9, but in accordance with aspects of the present invention, the inner surface of the tubular member may be patched with a plate-shaped resin having a thickness of 8 mm or less with an adhesive. Furthermore, the inner surface of the tubular member may be patched with a film-shaped resin having a thickness of about 100 μm, similarly to a laminate in a laminated steel sheet. At the step of performing heat treatment, the adhesive strength between the plate-shaped resin or the film-shaped resin and the inner surface of the tubular member should be adjusted to be 10 MPa or more.
Next, the reason why crashworthiness energy absorptive properties improve in the process of axial crush of the automotive crashworthiness energy absorptive part 1 according to the first embodiment is described below.
In conventional automotive crashworthiness energy absorptive parts having a tubular member made of a metal sheet such as a steel sheet, the tubular member absorbs the crashworthiness energy by repeatedly generating buckling deformation in a bellows shape, in the process in which crashworthiness load is input at the axial end of the automotive crashworthiness energy absorptive part and exceeds the buckling strength of the tubular member, leading to axial crush of the tubular part.
In this process, if the tubular member buckles and deforms without fracturing, the crashworthiness energy is most easily absorbed. However, if fractures occur on the outer surface of the tip of the bellows-shaped bend portion where the tubular member is buckled and deformed in a bellows shape, the crashworthiness energy absorption is insufficient and the original capability cannot be achieved. Because the bellows-shaped bend portion caused by the buckling deformation of the tubular member has a small bending radius inherent to the metal sheet, stress concentrates on the outer surface of the bend and fractures are likely to occur.
In the shape of the tubular member, the part that has a high capacity to absorb crashworthiness energy is the part that connects the top portion and the side wall portion, but it is also the part that is most susceptible to work-hardening when the tubular member is pressed. As a result, fractures are likely to occur at the tip of the bellows-shaped bend portion connecting the top portion and the side wall portion due to the decrease in ductility caused by work-hardening.
In particular, high-strength steel sheet, which has recently been adopted for automotive parts to achieve both crash worthiness and weight reduction, has less ductility than conventional strength steel sheet. According to the relation between the strength level of the steel sheet and the fracture limit for bending radius R/thickness t of the steel sheet (see Reference 1 below) illustrated in Table 1 and
(Reference 1) Kohei Hasegawa, Shinjiro Kaneko, Kazuhiro Seto, “High-strength Cold-Rolled and Alloyed Hot-Dip Galvanized (GA) Steel Sheet Contributing to Weight Reduction of Body Parts around Cabin,” JFE Technical Report, No. 30 (August 2012), p. 6-12.
As a result, when applying high-strength steel sheets to automotive crashworthiness energy absorptive parts, the above was a factor that hindered the progress of further increasing the strength of steel sheets. In accordance with aspects of the present invention, the inventors have focused on the fact that the bellows-shaped bend portion of the tubular member has a small bending radius inherent in the metal sheet described above, and conceived the idea that if the bending radius can be increased, fractures at the bend tip of the bellows shape caused by buckling deformation during axially crushing can be prevented.
In other words, when the tubular member 3 made of metal sheets is buckled and deformed in the early stage of the axial crushing impact, the bending radius of the convex bending portion can be held large by compressing the convexly deformed bending portion with an intervening object between the metal sheets. However, the addition of an intervening object between the metal sheets leads to an increase in the weight of the part, and hence the intervening object needs to be as light as possible.
Therefore, in accordance with aspects of the present invention, a resin is caused to adhere to the inner surface of the tubular member, and the resin is sandwiched between the metal sheets as the intervening object in the convex bending portion. As a result, the bending radius of the convex bending portion can be made larger than the fracture limit for bending radius inherent in the metal sheets with the resin intervening, and fractures are prevented from occurring in the bellows-shaped bending portion of the tubular member. As a result, the crashworthiness energy absorptive properties can be prevented from deteriorating.
However, if the adhesive strength between the resin coating the inner surface of the tubular member of an automotive crashworthiness energy absorptive part and the inner surface of the tubular member is small, the resin coating the inner surface of the tubular member is released and falls from the tubular member in the process from immediately after the buckling deformation starts due to the input of crashworthiness load to the axial end of the automotive crashworthiness energy absorptive part to the end of the axial crushing deformation. As a result, fractures occur during buckling deformation, and the crashworthiness energy absorptive properties cannot be improved.
In contrast, in the automotive crashworthiness energy absorptive part 1 according to the first embodiment, the resin 9 coating and adhering to the inner surface of the tubular member 3 with an adhesive strength of 10 MPa or more compressively deforms with the tubular member 3 without being released and falling from the inner surface of the tubular member 3 in the process of axial crushing.
This improves the buckling strength of the tubular member 3 and also allows the tubular member 3 to undergo repeated buckling deformation in a bellows shape manner without reducing the deformation resistance of the tubular member 3, resulting in improved crashworthiness energy absorptive properties.
Furthermore, by making the thickness of the resin 9 after coating and heated 8 mm or less, when the tubular member 3 made of the metal sheet is buckled and deformed in the initial stage of the axial crushing impact, the resin is sandwiched between the metal sheets in the convexly deformed bending portion. This prevents the bending radius of the convex bending portion from becoming smaller than the fracture limit for bending radius inherent in the metal sheet, and prevents fracture of the metal sheet from occurring. As a result, the crashworthiness energy absorptive properties can be prevented from deteriorating.
Unlike the conventional cases, it is not necessary to fill the entire closed cross-sectional space of the tubular member 3 with a resin. This is because, for the reason described above, it is only necessary to make the resin present at the tip of the bellows-shaped bend portion due to buckling deformation during axially crushing. Therefore, in order for the resin to be present with buckling deformation, the resin needs to adhere to the part connecting the top portion and the side wall portions of the tubular member 3.
Therefore, even if a punch shoulder R portion 5b of the outer part 5 is coated with a resin 17 as in an automotive crashworthiness energy absorptive part 15 illustrated in
As illustrated in
Furthermore, in the automotive crashworthiness energy absorptive part 1 according to the first embodiment, the resin 9 coating the inner surface of the tubular member 3 also functions as a damping material to absorb vibrations. For example, when the automotive crashworthiness energy absorptive part 1 is used as a front side member, which absorbs crashworthiness energy by axial crushing, the resin 9 can absorb the vibration of the automotive engine mounted on the front side member, thereby improving vibration-damping properties. This point is demonstrated in the example described below.
Note that, in the above description, the tubular member 3 is formed by joining the outer part 5 having a hat-shaped cross section and the plate-shaped inner part 7 by spot welding or the like. The tubular member 3 is not limited thereto. For example, the tubular member 3 may be formed by joining members of hat-shaped cross section or U-shaped cross section to form a tubular shape, or may be formed by forming a cylindrical member or the cross section of a cylindrical member into a polygonal shape, or combining flange surfaces of a plurality of members to form a polygonal shape.
Furthermore, the above description is about the automotive crashworthiness energy absorptive part 1 in which the inner surface of the tubular member 3 is coated with the resin 9, but the same functions and effects as in the automotive crashworthiness energy absorptive part 1 according to the first embodiment can be obtained even when the inner surface of the tubular member is patched with a plate-shaped or film-shaped resin and the adhesive strength thereof is 10 MPa or more.
In the automotive crashworthiness energy absorptive part 1 according to the above-mentioned first embodiment, in order to reliably secure an adhesive strength of 10 MPa or more between the inner surface of the tubular member 3 and the resin 9 and prevent the case where the resin 9 adhering to the inner surface of the tubular member 3 is released in the process of axial crush and crashworthiness energy absorptive properties are not improved, the inventors of the present invention have considered a unit for preventing the release of the resin 9.
As illustrated in
The release prevention member 23 is made of a metal sheet (such as steel sheet). As illustrated in
Similarly to the above-mentioned first embodiment, the adhesive strength between the resin 9 and the tubular member 3 and between the resin 9 and the release prevention member 23 may be determined by crashworthiness analysis of a double-layered square column in which a metal sheet (such as steel sheet) and a resin adhere to each other, or may be determined by measurement by a tensile testing machine after cutting out a part of the resin, the tubular member, and the release prevention member after adhesion.
As described above, in the automotive crashworthiness energy absorptive part 21 according to the second embodiment, the inner surface of the tubular member 3 is coated with the resin 9, but in accordance with aspects of the present invention, the inner surface of the tubular member may be patched with a plate-shaped resin having a thickness of 8 mm or less with an adhesive. Furthermore, the inner surface of the tubular member may be patched with a film-shaped resin having a thickness of about 100 μm, similarly to a laminate in a laminated steel sheet. The adhesive strength between the plate-shaped resin or the film-shaped resin and the inner surface of the tubular member only needs to be 10 MPa or more.
<Method for Manufacturing Automotive Crashworthiness Energy Absorptive Part>
Next, a method for manufacturing an automotive crashworthiness energy absorptive part according to the second embodiment is described.
As illustrated in
At the step of coating the inner surface of the tubular member 3 with the resin 9, after the tubular member 3 is formed by joining the outer part 5 having a hat-shaped cross section and made of a metal sheet and the inner part 7 having a plate shape and made of a metal sheet, the inner surface of the tubular member 3 is coated with the resin 9 with a thickness of 8 mm or less. At this time, the inner surface of the tubular member 3 may be coated with a liquid resin 9 with a thickness of 8 mm or less, or a plate resin 9 having a thickness of 8 mm or less may be caused to adhere to the inner surface of the tubular member 3 with an adhesive.
At the step of joining the release prevention member 23 to the inner surface of the tubular member 3, the release prevention member 23 is caused to patch, or adhere to with an adhesive, the resin coating the inner surface of the tubular member 3, and is joined to the inner surfaces of the side wall portions 5c of the outer part 5 by spot welding or the like.
At the step of performing heat treatment, the tubular member 3 coated with the resin 9 and provided with the release prevention member 23 is subjected to heat treatment under predetermined conditions, and the resin 9 and the inner surface of the tubular member 3 and the release prevention member 23 are caused to adhere to one another with an adhesive strength of 10 MPa or more.
Alternatively, in the case where the resin 9 is caused to adhere the inner surface of the tubular member 3 with an adhesive, heat treatment is performed after the resin 9 adhere to the inner surface of the tubular member 3, and the temperature and time of the heat treatment may be adjusted appropriately such that the adhesive strength of the adhesive is 10 MPa or more. The step of performing heat treatment in accordance with aspects of the present invention may also be, for example, a step of painting the outer surface of the tubular member 3 with paint and performing baking finish.
Note that the adhesive strength between the resin 9 and the inner surface of the tubular member 3 can be determined by crashworthiness analysis of a double-layered square column in which a metal sheet (such as steel sheet) and a resin adhere to each other, or by measurement using a tensile testing machine, as described above.
In the above description, in the method for manufacturing an automotive crashworthiness energy absorptive part according to the second embodiment, the inner surface of the tubular member 3 is coated with the resin 9, and then the release prevention member 23 is disposed inside the tubular member 3 and patches the surface of the resin 9 and is joined to the inner surface of the tubular member 3. However, the order of the coating with the resin 9 and the disposition of the release prevention member 23 are not limited to the above-mentioned order.
In other words, as another aspect of the method for manufacturing an automotive crashworthiness energy absorptive part 21 according to the second embodiment, the method may include a step of coating or patching, with a resin 9 with a thickness of 8 mm or less, a release prevention member 23 for preventing the resin 9 from being released from the inner surface of the tubular member 3, a step of bringing the resin 9 coating the release prevention member 23 into contact with the inner surface of the tubular member 3, and joining the release prevention member 23 to the inner surface of the tubular member 3, and a step of causing the resin 9 to adhere to the inner surface of the tubular member 3 and the release prevention member 23 with an adhesive strength of 10 MPa or more by performing heat treatment under predetermined condition.
In the automotive crashworthiness energy absorptive part 21 according to the second embodiment, similarly to the automotive crashworthiness energy absorptive part 1 according to the above-mentioned first embodiment, the resin 9 is prevented from being released from the inner surface of the tubular member 3 in the process of buckling deformation of the tubular member 3 into a bellows shape and axial crushing. As a result, the automotive crashworthiness energy absorptive part 21 according to the present embodiment can prevent the fracture in the tubular member 3 in the early stage of the axial crushing by effectively preventing the bending radius of the buckling deformation portion from becoming less than the fracture limit for bending radius due to the resin 9 being trapped inside the buckling deformation portion when the tubular member 3 is buckled and deformed, thereby further improving the crashworthiness energy absorptive properties.
In the automotive crashworthiness energy absorptive part 21, the resin 9 is coating across the top portion 5a of the outer part 5 to include the punch shoulder R portion 5b. However, in accordance with aspects of the present invention, a resin 17 may be coating only the punch shoulder R portion 5b of the outer part 5, as in an automotive crashworthiness energy absorptive part 25 illustrated in
In this way, even if the resin 17 is coating only the punch shoulder R portion 5b of the outer part 5 and adhered to the outer part 5 and to the release prevention member 23 with an adhesive strength of 10 MPa or more, the resin 17 is prevented from being released from the outer part 5 in the early stage of the axial crush impact, which improves the buckling strength and can improve the crashworthiness energy absorptive properties. When the punch shoulder R portion 5b, which has undergone work hardening in the press forming process of the outer part 5, buckles and deforms in the axial crushing process, the resin 17 is sandwiched inside the bending portion of the buckling deformation and prevents the punch shoulder R portion 5b from being bent below the fracture limit for bending radius, thereby preventing fracture from occurring.
Also in the automotive crashworthiness energy absorptive part 21 according to the second embodiment, the resin 9 coating the inner surface of the tubular member 3 also functions as a damping material to absorb vibrations.
For example, when the automotive crashworthiness energy absorptive part 21 is used as a front side member, which is a component that absorbs crashworthiness energy by axial crushing, the vibration of the automotive engine mounted on the front side member can be absorbed by the resin 9, thus improving vibration-damping properties.
Furthermore, although the above description refers to the automotive crashworthiness energy absorptive part 21 with the inner surface of the tubular member 3 coated with the resin 9, the same functions and effects as in the automotive crashworthiness energy absorptive part 21 according to the second embodiment can be obtained even if the inner surface of the tubular member is patched with a plate-shaped or film-shaped resin with an adhesive strength of 10 MPa or more.
Experiments for confirming the effects of the automotive crashworthiness energy absorptive parts according to aspects of the present invention were performed, and the results are described below.
In the present example, an automotive crashworthiness energy absorptive part according to aspects of the present invention was used as a test specimen to evaluate the absorptive properties of crashworthiness energy by axial crushing test and the damping characteristics by measuring the frequency response function and calculating the character frequency in the impact vibration test.
In the axial crush test, as illustrated in
On the other hand, in the impact vibration test, as illustrated in
The outer parts 5 and the inner parts 7 used for the test specimen 31, the test specimen 33, and the test specimen 35 illustrated in
In the test specimen 31, the test specimen 33, and the test specimen 35, the resin 9 and the resin 27 were epoxy or urethane foamed resins. The thickness of the coating or patching resin 9 or resin 27 was 0.1 mm, 1 mm, 3 mm, or 8 mm or less (see
Furthermore, in the present example, a test specimen 41 (
The first example to the seventh example are those in which the adhesive strength of the resin was within the range according to aspects of the present invention (10 MPa or more). The first example to the fifth example and the seventh example are those in which the test specimen 31 or the test specimen 33 provided with the release prevention member 23 was used, and the sixth example used the test specimen 35 without a release prevention member. On the other hand, the first comparative example to the fourth comparative example are those coated or patched with no resin, and the fifth comparative example to the seventh comparative example are those in which the adhesive strength of the resin was outside the range according to aspects of the present invention (less than 10 MPa).
In the first comparative example illustrated in
In the fourth comparative example illustrated in
Example 1 illustrated in
In this manner, in the first example, it is understood that the buckling strength in the axial crushing process increased and the deformation resistance increased without the resin 9 stripped and released, resulting in bellows-shaped compressive deformation and improved crashworthiness energy absorption.
In the third example illustrated in
Next, the structure and test specimen weight of the test specimens, as well as the results of the absorption energy when the axial crushing test was performed and the results of the character frequency obtained by the impact vibration test, are illustrated in Table 2 above. The test specimen weight illustrated in Table 2 is the sum of the weights of the outer part 5, the inner part 7, the release prevention member 23, and the resin 9 or the resin 17 for the test specimen 31 or the test specimen 33 coated with the resin 9 or the resin 17, and the sum of the weights of the outer part 5, the inner part 7, and the release prevention member 23 for the test specimen 41 coated or patched with no resin.
In the first comparative example, the test specimen 41 (
In the second comparative example, in the test specimen 41 coated with no resin similarly to the first comparative example, the plate thickness of the outer part 5 was changed from 1.2 mm to 1.4 mm, and the test specimen weight was 1.17 kg. The absorption energy was 7.9 kJ, and the character frequency was 175 Hz.
The third comparative example used a test specimen 41 with the same shape as in the first comparative example, but the outer part 5 was made of 980 MPa class high-strength steel sheet, and the test specimen weight was 1.06 kg. The absorption energy was 8.1 kJ, which was an increase over the first comparative example, but a fracture occurred in the tubular member 3. The character frequency was 155 Hz.
The fourth comparative example used a test specimen 41 with the same shape as in the first comparative example, but the outer part 5 was made of 1180 MPa class high-strength steel sheet, and the test specimen weight was 1.07 kg. The absorption energy was 8.5 kJ, which was higher than in the third comparative example, but a fracture occurred in the tubular member 3. The character frequency was 155 Hz.
The fifth comparative example used a test specimen with the same shape as the test specimen 31 according to aspects of the present invention, but the resin 9 with a thickness of 1 mm was not cased to adhere to the outer part 5 and the release prevention member 23, and the adhesive strength was set to 0 MPa. The test specimen weight was 1.15 kg. Furthermore, the absorption energy was 8.7 kJ, and a fracture occurred in the tubular member 3. The character frequency was a low value of 255 Hz.
The sixth comparative example used a test specimen with the same shape as the test specimen 33 according to aspects of the present invention, in which the resin 17 with a thickness of 3 mm was coating only the punch shoulder R portion 5b of the outer part 5, but the adhesive strength between the resin 17 and the outer part 5 and the release prevention member 23 was 4.0 MPa outside the range of the present invention. The test specimen weight was 1.13 kg. Furthermore, the absorption energy was 7.6 kJ, and a fracture occurred in the tubular member 3. The character frequency was as low as 285 Hz.
The seventh comparative example used a test specimen with the same shape as the test specimen 31 according to aspects of the present invention, but the adhesive strength between the resin 9 and the outer part 5 and the release prevention member 23 was set to 9.0 MPa outside the range of the present invention. The test specimen weight was 1.17 kg. Furthermore, the absorption energy was 8.3 kJ, and a fracture occurred in the tubular member 3. The character frequency was slightly low at 295 Hz.
The eighth comparative example used a test specimen with the same shape as the test specimen 35 according to aspects of the present invention, but the adhesive strength between the resin 9 and the outer part 5 was set to 4.0 MPa outside the range of the present invention. The test specimen weight was 0.96 kg. Furthermore, the absorption energy was 8.8 kJ, and a fracture occurred in the tubular member 3. The character frequency was as low as 265 Hz.
The ninth comparative example used a test specimen with the same shape as the test specimen 31 according to aspects of the present invention, but the thickness of the resin 9 was 9 mm outside the range of the present invention. The test specimen weight was 1.33 kg, and the absorption energy per unit weight was 6.6 kJ. The character frequency was as low as 275 Hz.
The first example used a test specimen 31 (
The second example is a test specimen 31 (
In the third example, the outer part 5 was made of a high-strength steel sheet with a strength of 1180 MPa class in a test specimen 31 having the same shape as in the second example. The absorption energy in the third example was 12.3 kJ, which was slightly lower than that in the first example, but much higher than that in the first comparative example, and no fracture occurred in the tubular member 3. The test specimen weight in the third example was 1.15 kg, which was lighter than that of the first example. The absorption energy per unit weight in the third example was 10.7 kJ/kg, which was higher than that in the first example (=10.0 kJ/kg) and the first comparative example (=6.1 kJ/kg). In the fourth comparative example (
In the fourth example, the outer part 5 was a steel sheet with a strength of 590 MPa class, and a test specimen 33 with a resin 9 coating only the punch shoulder R portion 5b of the outer part 5 with a thickness of 3 mm was used. The absorption energy in the fourth example was 9.0 kJ, which was much higher than the absorption energy of 6.5 kJ in the first comparative example (
In the fifth example, the thickness of the resin 9 was set to 3 mm in a test specimen 31 of the same shape as in the first example (
In the sixth example, a test specimen 35 with a resin 9 of 1 mm thickness coating the outer part 5 without a release prevention member was used, and the test specimen weight was 0.96 kg. The absorption energy in the sixth example was 11.2 kJ, and the absorption energy per unit weight was 11.7 kJ/kg. The energy absorptive properties were equivalent to or more than that in the first example, and no fracture occurred in the tubular member 3. The character frequency in the sixth example was 345 Hz, which was significantly higher than that in the eighth comparative example, in which the adhesive strength was outside the range of the present invention in the test specimen 35 of the same shape.
In the seventh example, the thickness of the resin 9 was set to 0.1 mm, which was the same level as that of a laminate in an ordinary laminated steel sheet, and the test specimen weight was 1.08 kg in a test specimen 31 of the same shape as in the first example. The absorption energy in the seventh example was 11.8 kJ, and the absorption energy per unit weight was 10.9 kJ/kg. The energy absorptive properties were equivalent to or more than that in the first example, and no fracture occurred in the tubular member 3. The character frequency in the seventh example was 300 Hz, which was significantly higher than that in the fifth comparative example, in which the resin 9 with a thickness of 1 mm was coating the outer part 5 in the test specimen 31 of the same shape, and the adhesive strength was outside the range of the present invention.
From the above, it was revealed that the automotive crashworthiness energy absorptive parts according to aspects of the present invention can efficiently improve the crashworthiness energy absorptive properties while minimizing the increase in weight when crashworthiness load is input in the axial direction and causes axial crushing, and can also improve the vibration-damping properties by increasing the character frequency when impact is applied.
The reason why the vibration-damping properties are improved by increasing the character frequency is as follows. When the character frequency of the tubular member 3, which is a crashworthiness member such as the front side member described above, enters the frequency range of the vibration of the engine mounted on the member, the tubular member 3 resonates (sympathetic vibration) and the vibration increases. For example, when the engine rotates at 4000 rpm, which is the high rpm range for normal driving, the crankshaft turns at the same rpm, and in a four-cycle engine, the crankshaft explodes and vibrates once every two revolutions, so the frequency of vibration is 133 Hz for a four-cylinder engine, 200 Hz for a six-cylinder engine, and 267 Hz for an eight-cylinder engine. Therefore, a character frequency of about 300 Hz or more in accordance with aspects of the present invention reliably prevents the above-mentioned sympathetic vibration and improve vibration-damping properties.
According to aspects of the present invention, the automotive crashworthiness energy absorptive part, which can improve crashworthiness energy absorptive effect by coating the inner surface with a resin and function as a damping material for absorbing vibration occurring in an automotive body, when crashworthiness load is input from the front side or the rear side of the automotive body such as a front side member or a crash box and causes axial crush, and the method for manufacturing the same can be provided.
1 automotive crashworthiness energy absorptive part
3 tubular member
5 outer part
5
a top portion
5
b punch shoulder R portion
5
c side wall portion
7 inner part
9 resin
11 automotive crashworthiness energy absorptive part
13 resin
15 automotive crashworthiness energy absorptive part
17 resin
21 automotive crashworthiness energy absorptive part
23 release prevention member
25 automotive crashworthiness energy absorptive part
27 resin
31 test specimen (example)
33 test specimen (example)
35 test specimen (example)
41 test specimen (comparative example)
| Number | Date | Country | Kind |
|---|---|---|---|
| 2018-238021 | Dec 2018 | JP | national |
This is the U.S. National Phase application of PCT/JP2019/035182, filed Sep. 6, 2019, which claims priority to Japanese Patent Application No. 2018-238021, filed Dec. 20, 2018, the disclosures of these applications being incorporated herein by reference in their entireties for all purposes.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2019/035182 | 9/6/2019 | WO | 00 |