Claims
- 1. A coating composition comprising a mixture of
- a) 5-40 percent by total weight of a crosslinkable co-vehicle comprising a polymer which is the polymerization product of monomers selected from the group consisting of acrylate and methacrylate hydroxyl functional monomers and other vinyl monomers, said polymer having a glass transition temperature between about -3.degree. C. to about 35.degree. C. (using the Fox method of Tg calculation), a weight average molecular weight of 1,000 to 7,000 and a hydroxyl value of between 75 and 175 mg KOH/g,
- b) 10 to 50 percent by total weight of an organic solvent,
- c) 1 to 60 percent by total weight of a reactive urea-urethane compound comprising reactive functionality other than --NCO groups thereon and consisting of the reaction product of alkanolamine, di- or poly-isocyanate and aliphatic alcohol,
- d) 0 to 30 percent by total weight of a reactive diluent,
- e) 10 to 50 percent by total weight of isocyanate cross linker,
- f) 0 to 10 percent by total weight of additives, selected from the group consisting of rheology control additives, flow modifiers, curing catalysts, accelerators, anti-settling agents, wetting agents, dispersing agents, mar and slip agents and mixtures thereof,
- h)10 to 60 percent by total weight of pigments.
- 2. The coating composition of claim 1 wherein the crosslinkable covehicle is an acrylic polymer further comprising glycidyl groups and the polymer is subsequently reacted to a fatty acid through said glycidyl groups.
- 3. The coating composition of claim 1 wherein the crosslinkable covehicle comprising an acrylic polymer comprises the polymerization product of ethylenically unsaturated acrylate and methacrylate monomers containing hydroxyl groups and other vinyl monomers, wherein the resulting acrylic polymer is subsequently esterified by means of reaction with natural or synthetic fatty acids.
- 4. The coating composition of claim 1 wherein the reactive urea/urethane compound consists of the reaction product of a polyisocyanate selected from the group consisting of the isocyanurate of isophorone diisocyante and the isocyanurate of hexamethylene diisocyanate and an alkanolamine with structure ##STR2## where R.sub.1 is selected from the group consisting of alkyl, cycloaliphatic and benzylic moieties, each containing a hydroxyl group,
- R.sub.2 is selected from the group consisting of hydrogen, alkyl, cycloaliphatic and benzylic moieties, each with or without a hydroxyl group, and where R.sub.1 and R.sub.2 combined comprise up to 12 carbon atoms.
- 5. The coating composition of claim 4 wherein the reactive urea/urethane compound has a weight average molecular weight between 2050 and 6000, as measured by gel permeation chromatography relative to polystyrene standards.
- 6. The coating composition of claim 1 wherein the crosslinkable covehicle is an acrylic polymer further comprising organic acid groups and the polymer is subsequently reacted to an oxirane functional compound through said organic acid groups on the polymer.
- 7. A method for improving dry time of an ambient cure pigmented coating composition comprising the steps of
- (A) applying over a primer coated substrate a pigmented coating composition to a thickness of between 1.1 to 1.3 mils, said coating comprising
- a) 5-40 percent by total weight of a crosslinkable covehicle comprising a polymer which is the polymerization product of monomers selected from the group consisting of acrylate and methacrylate hydroxyl functional monomers and other vinyl monomers, said polymer having a glass transition temperature between about -3.degree. C. to about 35.degree. C. (using the Fox method of Tg calculation), a weight average molecular weight of 1,000 to 7,000 and a hydroxyl value of between 75 and 175 mg KOH/g,
- b) 10 to 50 percent by total weight of an organic solvent,
- c) 1 to 60 percent by total weight of a reactive urea/urethane compound, comprising reactive functionality other than --NCO groups and comprising the reaction product of an alkanolamine with structure ##STR3## where R.sub.1 is selected from the group consisting of alkyl, cycloaliphatic and benzylic moieties, each containing a hydroxyl group,
- R.sub.2 is selected from the group consisting of hydrogen, alkyl, cycloaliphatic and benzylic moieties, each with or without a hydroxyl group, and
- where R.sub.1 and R.sub.2 combined comprise up to 12 carbon atoms,
- d) 0 to 30 percent by weight of a reactive diluent,
- e) 10 to 50 percent by total weight of isocyanate crosslinker,
- f) 0 to 10 percent by total weight of additives, selected from the group consisting of rheology control additives, flow modifiers, curing catalysts, accelerators, anti-settling agents, wetting agents, dispersing agants, mar and slip agents and mixtures thereof, and
- g)10 to 60 percent by total weight of pigments,
- B) flash drying the pigmented coating for between 10 and 30 minutes at 140.degree. F.,
- C) applying a non-pigmented coating composition wet on wet to the pigmented coating,
- D) heating the substrate at 140.degree. for 30 minutes,
- E) air drying the coating at ambient temperatures to achieve a reduction in dust free dry time as measured on a Byk Recorder of between 57% to 70% when compared to an identical coating composition without component (c).
Parent Case Info
This is a continuation of application Ser. No. 08/475,477 filed on Aug. 7, 1995, now abandoned which is a continuation of appliacation Ser. No. 08/382,732, filed on Feb. 2, 1995, now abandoned.
US Referenced Citations (4)
Number |
Name |
Date |
Kind |
3975457 |
Chang et al. |
Aug 1976 |
|
4180489 |
Andrew et al. |
Dec 1979 |
|
4555535 |
Bednarek et al. |
Nov 1985 |
|
5063091 |
Martorano |
Nov 1991 |
|
Continuations (2)
|
Number |
Date |
Country |
Parent |
475477 |
Aug 1995 |
|
Parent |
382732 |
Feb 1995 |
|