Patent Grant
8785589
1. Field of the Invention
The present invention relates to cross-linked, imide-based, photomechanical polymers derived from a multi(azobenzene-amine) cross-linker in conjunction with an aromatic amine and an aromatic dianhydride.
2. Description of the Related Art
Photomechanical polymers are a special class of smart (stimuli-responsive) polymers that are responsive to light and are capable of generating photo-directed motions and dimensional or shape alteration at the macro-scale level. These motions and/or alterations are driven by the collective molecular-volume change brought about by the chromophoric units upon appropriate irradiation. The chromophoric units in photoresponsive polymers are photochromic and have the unique ability to reversibly interconvert between two structural isomers (each with distinctly different optical and physical properties) under appropriate excitation conditions. Examples of chromophoric units can be found in photo-isomerizable molecules such as azobenzenes, spiropyrans, spirooxazines, diarylethylenes, and fulgides. However, with respect to photomechanical polymers, azobenzene is the most commonly used molecularly-actuating moiety because of its excellent thermal stability and resolved isomeric forms, as well as its ability to form surface gradient reliefs when subjected to conventional or polarization holography.
The resulting photomechanical output of a polymeric material depends not only on its optical properties (absorption wavelength, wavelength of exposure, polarization of exposure), but also on its molecular architecture and morphology (amorphous, crystalline, liquid crystalline). In addition, the photomechanical output is dependent on the polymeric material's thermomechanical properties, as well as the geometrical properties of the device, e.g. thickness of a cantilever.
Polyimides (PIs) represent an important class of heat-resistant polymers that have found utility in a wide spectrum of applications, ranging from structural components to electronic and photonic devices. The widespread application of polyimides is mainly the result of their excellent combination of physical properties, thermal stability, and processability. For example, polyimides containing azobenzene in the backbone or side-chain have been investigated for photo-induced alignment in liquid crystal display (LCD) as well as nonlinear optical applications. More recently, an azobenzene-containing poly(amic acid) (a PI precursor) was crosslinked by a triamine in N,N-dimethylformamide (DMF) and the resulting sol-gels showed a two-fold increase in the storage modulus after irradiation with 405 nm light. Another closely related aromatic poly(amic acid) was reported to be photomechanically active.
In accordance with the present invention, there is provided a composition of matter comprising non-liquid-crystalline, amorphous polyimides containing a photo-active tris(azobenzene) crosslinker. Cantilevers comprising these polyimides demonstrate large-amplitude, photo-directed, bidirectional bending. The general formula for the subject cross-linked polyimides is provided below:
In the general formula, “n,m,l” denote the degrees of polymerization (DP) of each of the three branches of the crosslinked polyimide. In one embodiment, n, m, and l are equal. In another embodiment, one or more of n, m, and l is not equal with respect to one another. In a further embodiment, the DP range is about 2 to about 20. In another embodiment, the DP range is about 3 to about 15. The linking group R′ is one or more of the following moieties: —C(CF3)2—, —O—, —SO2—, >C(═O), —OPh-C(CH3)2-PhO-, or -(Ph)C(CF3)—. In other embodiments, one or more of the linking groups R′ may simply be a direct bond (—) between the two phthalimido moieties.
The present invention further includes a method for making the crosslinked polyimides comprising the following steps: dissolving 1,3-bis(3-aminophenoxy)benzene and a bis(phthalic anhydride) compound in N,N-dimethylacetamide (DMAc) to form a solution, with the bis(phthalic anhydride) compound having the general formula of:
stirring the solution under a nitrogen atmosphere at room temperature to form a poly(amic acid) oligomer (PAA) solution in which the PAA oligomers further comprise terminal anhydride groups;—adding a tris(azobenzene-amine) cross-linker to the poly(amic acid) oligomer solution, wherein the tris(azobenzene-amine) cross-linker has a general structure:
wherein for the cross-linker, for meta-azo substitution, R is equal to H, and for para-azo substitution, R is selected from the group consisting of H, F, Cl, CF3, and CH3; allowing the tris(azobenzene-amine) cross-linker to dissolve in the poly(amic acid) oligomer solution to form a poly(amic acid) sol-gel precursor; and curing the poly(amic acid) sol-gel precursor to crosslink and imidize the poly(amic acid) sol-gel precursor to form the crosslinked polyimide.
In one embodiment of the method, the molar ratio of the bis(phthalic anhydride) compound to the 1,3-bis(3-aminophenoxy)benzene ranges, respectively, from about 1.00:0.92 to about 1.00:0.55. In various alternative embodiments of the method, the bis(phthalic anhydride) compound may be 2,2-bis(phthalic anhydride)-1,1,1,3,3,3-hexafluoroisopropane; 4,4′-oxydiphthalic anhydride; 3,3′,4,4′-benzophenonetetracarboxylic dianhydride; 3,3′,4,4′-diphenylsulfone tetracarboxylic dianhydride; 2,2-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane dianhydride; 4,4′-(2,2,2-trifluoro-1-phenylethylidene)diphthalic anhydride; or 3,3′,4,4′-biphenyl-tetracarboxylic dianhydride.
It has been estimated that the mechanical work per polymer chain based on the azobenzene isomerization process is only 10% efficient, meaning that only 10% of the incident photon energy (4×10−19 J) is converted to mechanical work (−4.5×10−20 J). As a way to improve the transduction efficiency via increasing the effective number density of azobenzene-actuating units in a polyimide (PI) network structure, the presently disclosed crosslinker is designed to contain three azobenzenes per molecule, via a trifunctional monomer, which can promote polyimide network formation under appropriate fabricating and curing conditions.
As an example, a representative synthesis of a photo-active, multi-(azobenzene-amine) cross-linker according to the present invention (compound 6) is shown in Scheme 1 below.
In Scheme 1,1,1,1,-tris(4-hydroxyphenyl)ethane (compound 1) was treated with 1-fluoro-4-nitrobenzene in presence of potassium carbonate to make 1,1,1-tris[4-(4-nitrophenoxy)phenyl]ethane (compound 2), which was reduced to 1,1,1-tris[4-(4-aminophenoxy)phenyl]ethane (compound 3) by catalytic hydrogenation. The reaction of compound 3 and 4-nitrosoacetanilide (compound 4) in acetic acid yielded the tris(azobenzene-amide) as compound 5. The tris(azobenzene-amine) monomer (compound 6) was generated after the deprotection of compound 5 via alkaline deacetylation reaction. By end-capping compound 6 with phthalic anhydride, a tris(azobenzene-N-phthalimide) model compound (compound 7) was obtained (see Scheme 1 above), which was useful in validating and semi-quantifying the kinetics of photoisomerization process in the cross-linked azo-polyimide system.
The crosslinked polyimides of the present invention may be made using the following general method. The method begins by dissolving 1,3-bis(3-aminophenoxy)benzene and a bis(phthalic anhydride) compound in N,N-dimethylacetamide (DMAc) to form a solution, with the bis(phthalic anhydride) compound having the general formula of:
Next, the solution is stirred under a nitrogen atmosphere at room temperature to form a poly(amic acid) oligomer (PAA) solution in which the PAA oligomers further comprise terminal anhydride groups. A tris(azobenzene-amine) cross-linker having the following general structure is then added to the poly(amic acid) oligomer solution:
In the cross-linker, for meta-azo substitution, R is equal to H, and for para-azo substitution, R is selected from the group consisting of H, F, Cl, CF3, and CH3. The azo linkage is para to phenoxy group. As described in more detail with respect to Scheme 2, an excess amount of the bis(phthalic anhydride) compound is required to prepare the desired poly(amic acid) oligomers (PAA) with terminal anhydride groups, and the added amount of crosslinker ranges from 5 to 30 mol % in accordance to ⅓ of the calculated total molar amount of the terminal anhydride groups of PAA to form a PAA sol-gel precursor. The method continues with allowing the tris(azobenzene-amine) cross-linker to dissolve in the poly(amic acid) oligomer solution to form a poly(amic acid) sol-gel precursor; and curing the poly(amic acid) sol-gel precursor to crosslink and imidize the poly(amic acid) sol-gel precursor to form a crosslinked polyimide with the following general structure:
The tris(azobenzene-amine) cross-linker crosslinker creates crosslinked polyimides containing three branches, with varying degrees of polymerization (DP) for each branch, which are denoted as “n,m,l.” The DP represents the number of repeat units (contained in the brackets in the general structure above) that each branch contains. The DP values may be the same or different for each branch, with even spacing between the repeat units. Where the DP values are all equal, the resulting polymer network is uniform. In one embodiment, the DP may be between about 2 and about 20. In another embodiment, the DP may be between about 3 and about 15. The infinity symbol (∞) is used to denote an infinite network structure for a crosslinked polymer. The linking group R′ may be one or more of the following moieties: —C(CF3)2—, —O—, —SO2—, >C(═O), —OPh-C(CH3)2-PhO-, or -(Ph)C(CF3)—. In other embodiments, one or more of the linking groups R′ may simply be a direct bond (—) between the two phthalimido moieties.
The bis(phthalic anhydride) compound may be 2,2-bis(phthalic anhydride)-1,1,1,3,3,3-hexafluoroisopropane; 4,4′-oxydiphthalic anhydride; 3,3′,4,4′-benzophenonetetracarboxylic dianhydride; 3,3′,4,4′-diphenylsulfone tetracarboxylic dianhydride; 2,2-bis[4-(3,4-dicarboxyphenoxy)phenyl]propane dianhydride; 4,4′-(2,2,2-trifluoro-1-phenylethylidene)diphthalic anhydride; or 3,3′,4,4′-biphenyl-tetracarboxylic dianhydride. In one embodiment of the method, the molar ratio of the bis(phthalic anhydride) compound to the 1,3-bis(3-aminophenoxy)benzene ranges from about 1.00:0.92 to about 1.00:0.55.
More specifically, the crosslinked polyimides of the present invention are related to a well-known low-color, space-grade polyimide commonly known as CP2 (LaRC™-CP2, originally developed by NASA Langley Research Center). CP2 may be derived from 2,2-bis(phthalic anhydride)-1,1,1,3,3,3-hexafluoroisopropane (6FDA) and 1,3-bis(3-aminophenoxy)benzene (APB). Scheme 2 outlines the synthesis of an exemplary azobenzene containing CP2 (azo-CP2) polyimide. 6FDA (compound 8) and APB (compound 9) were dissolved under nitrogen atmosphere in N,N-dimethylacetamide (DMAc) (5 wt % concentration) at room temperature for 24 hours with excess 6FDA for the preparation of poly(amic acid) oligomers (PAA oligomers, compound 10) with terminal anhydride groups. Subsequently, the tris(azobenzene-amine) crosslinker (compound 6) was added to the solution of anhydride-terminated PAA oligomers with a stoichiometric ratio of the amino group to the terminal acid anhydride. After the crosslinker had completely dissolved, the resulting PAA sol-gel precursor/DMAc (compound 11, structure not shown) was poured onto glass slides and cured in an oven up to 300° C. to crosslink and imidize the polymer films to form a azobenzene-containing CP2 polyimide network (compound 12).
According to the principle of polymerization, the amount of crosslinker added must generally be such that the functionality molar ratio of all of the amine groups (three from the crosslinker and two from the diamine APB) to all of the anhydride groups (two from 6FDA) is 1:1; i.e. amine:anhydride is 1:1. Because the initial PAA oligomers were synthesized using excess dianhydride (e.g. 6FDA), the amount of crosslinker that was added must contain a balancing amount of amine groups to react with all the anhydride end-groups (i.e. two per PAA chain). For example, to generate the Azo-CP2-03 sample that contains 3 mol % of crosslinker (see Table 1), the dianhydride-terminated PAA oligomers were first prepared from 100 mol % of the dianhydride, 6FDA, and 95.5 mol % of the diamine, APB. Because there are two anhydride endgroups, there are a total of 2×(100-95.5) 9 mol % of anhydride. Because each molecule of crosslinker (three amines) can react with three anhydride endgroups, the molar amount of crosslinker required is ⅓ of 9 mol % of the total anhydride endgroups.
The concentration of azobenzene may be varied in the azo-CP2 films by adding various amounts (i.e. 5, 10, 20 and 30 mol %) of the tris(azobenzene-amine) monomer to the respective PAA/DMAc solutions. The molar ratios of the three monomer mixtures, 6FDA: APB: crosslinker, are listed in Table 1. The film thickness for the azo-CP2 sample, as an example of photo-mobile cantilever for this series of crosslinked azo-polyimides, is 20 μm.
The following examples and methods are presented as illustrative of the present invention or methods of making or carrying out the invention and are not restrictive or limiting of the scope of the invention in any manner. The crosslinked, azobenzene-containing polyimides according to the present invention may be synthesized following the procedures given in the following examples.
Into a 250 mL three-necked flask equipped with a magnetic stir bar and nitrogen inlet and outlet were placed 1,1,1,-tris(4-hydroxyphenyl)ethane (10.0 g, 33.0 mmol), 1-fluoro-4-nitrobenzene (15.4 g, 109 mmol), potassium carbonate (15.1 g, 109 mmol) and DMF (100 mL). The mixture was stirred at room temperature for 24 hours and filtered. The filtrate was diluted with ethyl acetate (400 mL) and the organic layer was separated. The organic layer was washed with water 3 times. It was dried over anhydrous magnesium sulfate and filtered. The filtrate was concentrated to 75 mL on a rotary evaporator, and then stored in refrigerator for several days to afford 11.2 g (51%) of off-white crystals, m.p. 98-99° C. MS (m/e): 669 (M+). Anal. Calcd. for C38H27N3O9: C, 68.18%; H, 4.06%; N, 6.27%; O, 21.50%. Found: C, 67.69%; H, 4.26%; N, 6.21%; O, 21.22%. FT-IR (KBr, cm−1): 3076, 2979, 1586, 1513, 1486, 1344, 1248, 1165, 1107, 874, 846. 1H-NMR (DMSO-d6, δ in ppm): 2.26 (s, 3H, CH3), 7.17-7.27 (m, 18H, Ar—H), 8.28-8.31 (d, 6H, Ar—H).
1,1,1-Tris[4-(4-nitrophenoxy)phenyl]ethane (Example 1; 3; 5.0 g, 7.5 mmol), THF (50 mL) and 5% palladium on activated carbon (0.50 g) were added to a hydrogenation bottle. The bottle was secured on a Parr hydrogenation apparatus, flushed three times with hydrogen, and then pressurized to 55 psi. After the mixture had been agitated at room temperature for 24 hours under the hydrogen pressure of 55 psi, it was filtered through Celite. The filter cake was washed with THF, and then the filtrate was evaporated to dryness on a rotary evaporator to afford a 4.25 g (98%) of yellow crystal, which was used without further purification, m.p. 220-221° C. MS (m/e): 579 (M+). Anal. Calcd. for C38H33N3O3: C, 78.73%; H, 5.74%; N, 7.25%. Found: C, 78.17%; H, 5.78%; N, 7.04%. FT-IR (KBr, cm−1): 3441, 3361 (NH2), 3035, 2970, 1617, 1581, 1497, 1384, 1232, 1173, 1117, 1010, 871, 842. 1H-NMR (DMSO-d6, δ in ppm): 2.02 (s, 3H, CH3), 4.99 (s, 6H, NH2), 6.53-6.58 (d, 6H, Ar—H), 6.68-6.74 (m, 12H, Ar—H), 6.88-6.93 (d, 6H, Ar—H).
After oxone (potassium peroxymonosulfate, from Sigma-Aldrich®; 12.28 g, 20.0 mmol) had dissolved completely in water (100 mL), potassium carbonate (4.14 g, 30 mmol) was added slowly to neutralize the solution to a weak acidity. The solution was added quickly into a solution of 4′-aminoacetanilide (from Sigma-Aldrich®; 1.50 g, 10.0 mmol) in water (150 mL). The mixture immediately turned green, and greenish-gray solids started to fall out of solution. After the mixture had been stirred for another 10 minutes, the precipitates were collected on a filter funnel, air dried, and recrystallized from hot ethanol. Two batches of products were collected to give a total yield of 1.06 g (65%) greenish crystals, mp 179-180° C. (lit. 179-180° C.).
1,1,1-Tris(4-(4-aminophenoxy)phenyl)ethane (Example 2; 0.580 g, 1.00 mmol), N-(4-nitrosophenyl)acetamide (Example 3; 0.985 g, 6 mmol) and acetic acid (20 mL) were charged into a 150 mL round-bottomed flask equipped with a magnetic stir bar. The mixture was stirred at room temperature for 48 hours. The mixture was at first turned into a greenish solution, and then yellow particles started to precipitate out of the solution. The mixture was diluted by deionized water (100 mL). Solids were collected and washed with water (500 mL), followed by ethanol (200 mL) to remove most of the unreacted nitroso reagent. The solid was then extracted by hot acetone (100 mL) four times. The acetone extract was concentrated on a rotary evaporator to give yellow solids as raw product. The raw product was slurried in hot ethanol (50 mL) and filtered twice after cooling to room temperature in between to give 0.62 g (61%) of yellow solids, mp 220° C. (dec.). 1H-NMR (d6-DMSO, δ in ppm): 2.09 (s, 9H, COCH3), 2.15 (s, 3H, CCH3) 7.03-7.15 (m, 18H), 7.79-7.87 (m, 18H) 10.28 (s, 3H, NHCO). 13C-NMR (d6-DMSO, δ in ppm): 24.16, 30.28, 51.00, 118.50, 118.86, 119.18, 123.42, 124.35, 129.99, 142.09, 144.50, 147.38, 147.77, 153.78, 159.07, 168.06.
To a 100 mL round-bottomed flask with a stir-bar and a condenser, 1,1,1-tris[4-(4-(4-acetamidophenyldiazenyl)phenoxy)phenyl]ethane (Example 4; 0.50 g, 0.49 mmol), 6 M HCl (20 mL) and 95% ethanol (20 mL) were charged and heated to 80° C. The mixture was stirred at 80° C. for 3 days. After the mixture was allowed to cool to room temperature, water (60 mL) added. The resulting red solid was collected by filtration and washed with dilute sodium bicarbonate solution, followed by deionized water (300 mL). After being air dried, the crude product was purified by column chromatography (silica gel, ethyl acetate as eluent). The solvent was removed by a rotary evaporator to afford 0.23 g (52.5%) of orange red solid, mp >300° C. MS (m/e): 892 (M+). Anal. Calcd. for C56H45N9O3: C, 75.40%; H, 5.08%; N, 14.13%. Found: C, 75.44%; H, 5.08%; N, 13.98%. 1H-NMR (d6-DMSO, δ in ppm): 2.12 (s, 3H, CCH3), 6.03 (s, 6H, NH2), 6.67-6.70 (d, 6H, J=8.7 Hz), 6.99-7.02 (d, 6H, J=8.7 Hz), 7.09-7.13 (m, 12H), 7.62-7.66 (d, 6H, J=8.7 Hz), 7.75-7.78 (d, 6H, J=8.7 Hz). 13C-NMR (d6-DMSO, δ in ppm): 30.34, 51.91, 113.41, 118.44, 118.69, 123.52, 124.96, 129.93, 142.92, 144.25, 148.41, 152.56, 154.21, 157.75.
1,3-Bis(3-aminophenoxy)benzene (APB; 0.4093 g, 1.400 mmol) and DMAc (8 mL) were added to a 50 mL 3-necked flask equipped with a magnetic stirrer and a nitrogen inlet and outlet and stirred under dry nitrogen at room temperature for 30 minutes. 2,2-Bis(phthalic anhydride)-1,1,1,3,3,3-hexafluoroisopropane (6FDA; 0.8885, 2.000 mmol) was then introduced to the resulting solution. The light yellow solution was agitated at room temperature for 24 hours to afford a poly(amic acid) solution. Then, the tris(azobenzene-amine) cross-linker (Example 5; 0.3568 g, 0.400 mmol) was added to this solution. After the crosslinker had completely dissolved in DMAc, the mixture was poured into a glass petri dish, followed by vacuum evaporation of DMAc at 50° C., and heat-treated according to following schedule: 100° C./2 hrs, 150° C./2 hrs, 175° C./1 hr, 200° C./2 hrs, 250° C./1 hr and 300° C./1 hr to form polyimide films. The film thickness was approximately 20 μm. To prepare a polyimide with (ax100) mol % of the crosslinker, this procedure was followed with variation in the mole ratio of APB: 6FDA:crosslinker=(1-3a/2):1:a, where a can be varied from 0.05 to 0.50. In the designation, azo-CP2-XX, the “XX” corresponds to the mol % of the azobenzene-containing crosslinker, ranging from 5-30 mol %
Table 1 below summarizes the composition and properties of polyimide films made according to the present invention.
In Table 1, the measured thickness of the azo-CP2 films are as follows: 18 μm (azo-CP2-05), 21 μm (azo-CP2-10), 21 μm (azo-CP2-20) and 20 μm (azo-CP2-30). The cantilevers were uniform in thickness with variation less than 0.5 μm. Tg is measured from the peak of tan delta (DMA) as an average value taken from four measurements. The modulus (E) is determined in tension at 25° C. as an average from five specimens per sample. Mc denotes the average molecular weight of the linear segment between two cross-linked sites, calculated from the following equation Mc=350.27×Xn+295.32×2, where 350.27 is one-half the formula weight of a CP2 repeat unit, the number-average degree of polymerization Xn=(1+r)/(1−r), the stoichiometric imbalance factor (r) is the molar ratio of diamine to dianhydride, and 295.32 is one-third value of the formula weight of cross-linker segment (from methyl-end to imide-nitrogen) in CP2 network. α442 is the measured absorption coefficient for the materials at 442 nm. Azo-CP2-03 and Azo-CP2-40 were extrapolated cross-linked polyimide compositions to define the range of degrees of polymerization (DP, which is indicated by n,m,l in the generic structure for Azo-CP2-XX) for linear CP2 segments. Because the molecular weight for a CP2 repeat unit is ˜700 Da, the calculated DP values are (from top to bottom): 23, 14, 7, 4, and 3.
While the crosslinking density increases as the crosslinker concentration increases, the calculated average molecular weights between crosslinked sites (Mc), on the other hand, follows an opposite trend (see Table 1 above). The glass transition temperature (Tg) of neat polyimide (CP2) is 214° C. by DMA. Comparatively, the Tg values (220-284° C.) of the azobenzene-containing polyimide networks (i.e. azo-CP2-XX, increase with the concentration of tris(azobenzene) crosslinker, especially with concentrations >5 mol %. The tensile moduli (E) of the azo-CP2 films initially decrease with the presence of crosslinker concentration (0-5 mol %) as compared to that of unmodified CP2, before subsequently increasing by ˜0.2-0.3 GPa per 5 mol % of crosslinker added. It is speculated that at the crosslinker concentration of <5 mol % the tripod geometry of the crosslinker may be disrupting the chain-packing regularity of the CP2 polyimide, resulting in softening of the azo-CP2 networks. However, in the azo-CP2 systems, increasing crosslink density (and the corresponding decrease in Mc between the azobenzene net points) causes the increase in modulus with each addition of 5 mol % crosslinker.
The photomechanical response of the azo-CP2-20 cantilevers is depicted in
Linearly polarized blue-green (440-510 nm) light induces what has been referred to as trans-cis-trans reorientation (also known as the Weigert effect). This phenomenon has been extensively employed in glassy azobenzene polymers to form both conventional volume gratings as well as surface relief gratings. Fundamental to this mechanism is the simultaneous and repeated trans-cis and cis-trans isomerization cycles of azobenzene induced by light in this wavelength regime. The repeated trans-cis and cis-trans isomerizations of azobenzene, due to the dichroic absorption of azobenzene (in addition to the rotational freedom of the azo bond when photo-excited) results in a statistical buildup of trans azobenzene rotated orthogonal to the incident linear polarization of the light source. Due to the large absorption coefficient of azo-CP2-20 at 442 nm (see Table 1), light is absorbed nonuniformly across the thickness of the film. When light is polarized parallel to the long axis of the cantilever, the reorientation of azobenzene results in a contraction along this long axis, which yields bending towards the light source. Conversely, when light is polarized orthogonal to the long axis of the cantilever, the reorientation of azobenzene causes an expansion along the long axis, which yields bending away from the laser source. The fact that bending is not observed to light polarized 45° to the long axis confirms that a) the mechanism is not photothermal in nature, and b) it is the expected result of a reorientation mechanism (no net change in reorientation). Calculations indicate that only a small percentage of the azobenzene mesogens need to rotate to generate the strain required to drive bending of this magnitude in this glassy system.
The photoresponse of glassy poly-domain azobenzene liquid-crystalline network (azo-LCN), when exposed to 442 nm laser, exhibits slight larger magnitude bending, identical polarization dependence, and retains the bent shape for an extended (months) period of time (known as photo-fixing effect). As shown in
To further understand the relationship between azobenzene/crosslinker concentration and the resulting photoresponse of the azo-CP2 materials,
Although specific embodiments have been described in detail in the foregoing description and illustrated in the drawings, various other embodiments, changes, and modifications to the disclosed embodiment(s) will become apparent to those skilled in the art. All such other embodiments, changes, and modifications are intended to come within the spirit and scope of the appended claims.
This application claims the benefit of U.S. Provisional Patent Application No. 61/636,134, filed on Apr. 20, 2012, by inventor Loon-Seng Tan, et al., entitled “Multi(Azobenzene-Amine) Photo-Active Crosslinkers,” and U.S. Provisional Patent Application No. 61/636,170, filed Apr. 20, 2012, by inventor Loon-Seng Tan, et al., entitled “Azobenzene-Containing Glassy Polyimides Capable of Photo-Induced Large-Angle Bending,” both of which are incorporated herein by reference in their entirety.
The invention described herein may be manufactured and used by or for the Government of the United States for all governmental purposes without the payment of any royalty.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3455879 | Gay et al. | Jul 1969 | A |
| 3600361 | Heacock et al. | Aug 1971 | A |
| 3732200 | Bach | May 1973 | A |
| 3835120 | Bach et al. | Sep 1974 | A |
| 4107125 | Lovejoy | Aug 1978 | A |
| 4271288 | Woo | Jun 1981 | A |
| RE30922 | Heilman et al. | May 1982 | E |
| 4394499 | Robinson et al. | Jul 1983 | A |
| 4728697 | Bolon et al. | Mar 1988 | A |
| 4981497 | Hayes | Jan 1991 | A |
| 5101005 | Vora et al. | Mar 1992 | A |
| 5175234 | Lubowitz et al. | Dec 1992 | A |
| 5300559 | Sheehan et al. | Apr 1994 | A |
| 5344894 | Lubowitz et al. | Sep 1994 | A |
| 5516876 | Lubowitz et al. | May 1996 | A |
| 5585217 | Oba | Dec 1996 | A |
| 5599582 | Adamopoulous et al. | Feb 1997 | A |
| 5670651 | Tan et al. | Sep 1997 | A |
| 5965687 | Jensen | Oct 1999 | A |
| 6001277 | Ichimura et al. | Dec 1999 | A |
| 6184333 | Gray | Feb 2001 | B1 |
| 6262223 | Meador et al. | Jul 2001 | B1 |
| 6307008 | Lee et al. | Oct 2001 | B1 |
| 6509094 | Shah et al. | Jan 2003 | B1 |
| 7582722 | Tan et al. | Sep 2009 | B1 |
| 7678873 | Tan et al. | Mar 2010 | B1 |
| 8173763 | Tan et al. | May 2012 | B1 |
| 8389619 | Tan et al. | Mar 2013 | B1 |
| 8546614 | Tan et al. | Oct 2013 | B1 |
| 20030064235 | Okawa et al. | Apr 2003 | A1 |
| 20040233377 | Utsumi et al. | Nov 2004 | A1 |
| 20050080229 | Deets et al. | Apr 2005 | A1 |
| 20060217482 | Lukehart et al. | Sep 2006 | A1 |
| 20060235194 | Kato | Oct 2006 | A1 |
| 20060270825 | Angermeier et al. | Nov 2006 | A1 |
| 20070106056 | Itatani | May 2007 | A1 |
| 20070270562 | Yamada et al. | Nov 2007 | A1 |
| 20080025905 | Wang et al. | Jan 2008 | A1 |
| 20080311303 | Naiki et al. | Dec 2008 | A1 |
| 20090220722 | Wang | Sep 2009 | A1 |
| 20100048745 | Yamada et al. | Feb 2010 | A1 |
| 20110009513 | Chaudhary et al. | Jan 2011 | A1 |
| 20110136061 | Itatani | Jun 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 2 380 867 | Oct 2011 | EP |
| 2005023151 | Jan 2005 | JP |
| 2005154643 | Jun 2005 | JP |
| 2007051217 | Feb 2007 | JP |
| Entry |
|---|
| Jenekhe, Samson A., et al., Nonlinear Optical Properties of Poly(p-phenylenebenzobisoxazole), Chem. Mater. 1992, 4, 683-687. |
| Kannan, Ramamurthi, et al., Diphenylaminofluorene-Based Two-Photon Absorbing Chromophores with Various π-Electron Acceptors, Chem. Mater. 2001, 13, 1896-1904. |
| Pyun, Eumi, et al., “Kinetics and mechanisms of thermal imidization of a polyamic acid studied by ultraviolet-visible spectroscopy”, Macromolecules (1989), 22(3), 1174-83. |
| Natansohn, A., et al., “Photoinduced Motions in Azo-Containing Polymers,” Chemical Reviews (Washington, DC, United States) (2002), 102(11), 4139-4175. |
| Hugel, Thorsten, et al., “Single-molecule optomechanical cycle”, Science (2002), 296(5570), 1103-1106. |
| Hosono, Nobuhiko, et al., “Photochemical control of network structure in gels and photo-induced changes in their viscoelastic properties” Colloids and Surfaces, B: Biointertaces (2007), 56(1-2), 285-289. |
| Zhang, Chaohui, et al., “Rapid bending of a nonliquid crystal azobenzene polymer film and characteristics of surface relief grating” Journal of Applied Polymer Science (2009), 113(2), 1330-1334. |
| Kannan, Ramamurthi, et al., “Toward Highly Active Two-Photon Absorbing Liquids: Synthesis and Characterization of 1,3,5-Triazine-Based Octupolar Molecules,” Chem. Mater. 2004, 16, 185-194. |
| He, Guang S., et al., “Degenerate Two-Photon-Absorption Spectral Studies of Highly Two-Photon Active Organic Chromophores,” J. Chem. Phys., vol. 120 No. 11 (2004) 5275-5284. |
| Wang, David H., et al., “Photomechanical Response of Glassy Azobenzene Polyimide Networks” Macromolecules 2011, 44, pp. 3840-3846. |
| Hrozhyk, Uladzimir, et al., “Bidirectional Photoresponse of Surface Pretreated Azobenzene Liquid Crystal Polymer Networks,” Optics Express, vol. 17, Issue 2, pp. 716-722 (2009). |
| Usami, Kiyoaki, et al., “Photo-Aligned Blend Films of Azobenzene-Containing Polyimides with and without Side-Chains for Inducing Inclined Alignment of Liquid Crystal Molecules,” Journal of Applied Physics (2011), 110(4), 043522/1-043522/6. |
| Makita, Shonei, et al., “Synthesis of Alkaline-Developable, Photosensitive Hyperbranched Polyimides through the Reaction of Carboxylic Acid Dianhydrides and Trisamines,” Journal of Polymer Science Part A: Polymer Chemistry, vol. 42, 3697-3707 (2004). |
| Lendlein Andreas et al., “Shape-Memory Polymers,” Angewandte Chemie, International Edition, vol. 41, 2034-2057 (2002). |
| Liu C. et al., “Review of Progress in Shape-Memory Polymers,” Journal of Materials Chemistry, vol. 17, 1543-1558 (2007). |
| Fay, Catherine C. et al., “Molecularly Oriented Polymeric Thin Films for Space Applications,” High Performance Polymers, vol. 11, 145-156 (1999). |
| SRS Technologies and Mantech Materials, “Polyimides: CP1 and CP2 Film Properties,” printed Jul. 9, 2012, 1 page, available at <http://www.mantechmaterials.com/—images/documents/3—8—doc.pdf>. |
| St. Clair, Anne K., et al. “Synthesis and Characterization of Essentially Colorless Polyimide Films,” J. Polym. Mater. Sci Eng., vol. 51, pp. 62-66 (1984). |
| Miner, Gilda A., et al., “The Wettability of LaRC Colorless Polyimide Resins on Casting Surfaces,” J. Polym. Mater. Sci Eng., vol. 76, pp. 381-382 (1997). |
| Straub, Daniel, “Lewis Structures of Boron Compounds Involving Multiple Bonding,” J. Chem. Ed. 72(6) 494-497 (1995). |
| Chao, Tsung-Yi, et al., “Nonlinear Optical Polyimide/Montmorillonite/Nanocomposites Consisting of Azobenzene Dyes,” Dyes and Pigments, 77 (2008) 515-524. |
| Agolini, F., et al., “Synthesis and Properties of Azoaromatic Polymers,” Macromolecules (May-Jun. 1970), vol. 3, No. 3, 349-351. |
| Lovrien, R., “The Photoviscosity Effect,” Proc. Natl. Acad. Sci. U.S. A. 1967 (57) 236-242. |
| Cojocariu, C., et al., “Light-induced motions in azobenzene-containing polymers,” Pure Appl. Chem. 2004, 76, 1479-1497. |
| Tabiryan, N., et al., “Polymer film with optically controlled form and actuation,” T. Optics Express 2005, 13, 7442-7448. |
| White, T.J., et al., “A high frequency photodriven polymer oscillator,” J. Soft Matter 2008,4, 1796-1798. |
| Barrett, C.J., et al., “Photo-mechanical effects in azobenzene-containing soft materials,” Soft Matter 2007, 3, 1249-1261. |
| Park, C., et al., “Actuating Single Wall Carbon Nanotube—Polymer Composites: Intrinsic Unimorphs,” Adv. Mater. 2008, 20, 2074-2079. |
| Van Oosten, C.L., et al., “Bending Dynamics and Directionality Reversal in Liquid Crystal Network Photoactuators,” Macromolecules 2008,41,8592-8596. |
| Irie, M., “Photochromism and Molecular Mechanical Devices,” Bull. Chem. Soc. Jpn. 2008, 81 (8), 917-926. |
| Serak, S.V., et al., “Azobenzene liquid crystal polymer-based membrane and cantilever optical systems,” Optics Express, vol. 17, No. 18 (Aug. 31, 2009), 15736-15746. |
| Hogan, P.M., et al., “UV-Manipulation of Order and Macroscopic Shape in Nematic Elastomers,” Phys. Rev. E: Stat., Nonlinear, Soft Matter Phys. 2002, 65, 041720/1-041720110. |
| Eisenbach, C.D., “Isomerization of aromatic azo chromophores in poly(ethyl acrylate) networks and photomechanical effect,” Polymer 1980, 21, 1175-1179. |
| Viswanathan, N.K., et al., “Surface relief structures on azo polymer films,” J. Mater. Chem. 1999, 9, 1941-1955. |
| Harris, K.D., et al., Large amplitude light-induced motion in high elastic modulus polymer actuators, J. Mater. Chem. 2005, 15, 5043-5048. |
| Van Oosten, C.L., et al., “Glassy photomechanical liquid-crystal network actuators for microscale devices,” Eur. Phys. J. E, 2007, 23, 329-336. |
| White, T.J., et al., “Polarization-controlled, photodriven bending in monodomain liquid crystal elastomer cantilevers,” J. Mater. Chem. 2009, 19, 1080-1085. |
| Lee, K.M., et al., “Relationship between the Photomechanical Response and the Thermomechanical Properties of Azobenzene Liquid Crystalline Polymer Networks,” Macromolecules 2010, 43, 8185-8190. |
| Finkelmann, H., et al., “A New Opto-Mechanical Effect in Solids,” Phys. Rev. Lett. 2001, 87, 01550111-01550114. |
| Sroog, C.E., “Polyimides,” Prog. Polym. Sci. 1991, 16, 561-694. |
| Koshiba, Y., et al., “Photo-induced alignment behavior of azobenzene compound in thin film,” Thin Solid Films 2009, 518, 805-809. |
| Koerner, H., et al., “Photogenerating work from polymers,” Mater. Today (Oxford, U. K.) 2008, 11, (7-8), 34-42. |
| Wang, D.H., et al., “Nanocomposites Derived from a Low-Color Aromatic Polyimide (CP2) and Amine-Functionalized Vapor-Grown Carbon Nanofibers: In Situ Polymerization and Characterization,” Macromolecules 2007, 40, 6100-6111. |
| Yu, Y., et al., “Photomechanical Effects of Ferroelectric Liquid-Crystalline Elastomers Containing Azobenzene Chromophores,” Angew. Chem., Int. Ed. 2007, 46, 881-883. |
| Arlen, M., et al., “Thermal-Electrical Character of in Situ Synthesized Polyimide-Grafted Carbon Nanofiber Composites,” Macromolecules 2008, 41, 8053-8062. |
| Chen, J.P., et al., “Highly Stable Optically Induced Birefringence and Holographic Surface Gratings on a New Azocarbazole-Based Polyimide,” Macromolecules 1999, 32, 8572-8579. |
| Kumar, G.S., et al., “Photochemistry of Azobenzene-Containing Polymers,” Chem. Rev. 1989, 89, 1915-25. |
| Yu, Y., et al., “Effect of Cross-linking Density on Photoinduced Bending Behavior of Oriented Liquid-Crystalline Network Films Containing Azobenzene,” Chem. Mater. 2004, 16, 1637-1643. |
| Kondo, M., et al., “Effect of concentration of photoactive chromophores on photomechanical properties of crosslinked azobenzene liquid-crystalline polymers,” J. Mater. Chem. 2010, 20, 117-122. |
| Li, M.-H., et al., “Light-Driven Side-On Nematic Elastomer Actuactors,” Adv. Mater. 2003, 15, 569-572. |
| U.S. Patent and Trademark Office, Non-Final Office Action mailed Sep. 26, 2012, U.S. Appl. No. 13/557,326, 9 pages. |
| U.S. Patent and Trademark Office, Non-Final Office Action mailed Mar. 27, 2013, U.S. Appl. No. 13/557,326, 5 pages. |
| U.S. Patent and Trademark Office, Non-Final Office Action mailed Nov. 7, 2013, U.S. Appl. No. 13/546,439, 9 pages. |
| Meador, Mary Ann B., et al., “Synthesis and Properties of Nanoporous Polyimide Aerogels Having a Covalently Bonded Network Structure,” Polymer Preprints 2010, 51(1), 265. |
| Japanese Patent Office, Machine Translation of JP 2005154643A, 39 pages. |
| Meador, Mary Ann B., et al., “Improvements to the Synthesis of Polyimide Aerogels,” ACS Spring National Meeting 2011, Anaheim, CA; Mar. 20-26, 2011, 34 pages. |
| Usami, K. et al., “Improvement in photo-alignment efficiency of azobenzene-containing polyimide films,” Thin Solid Films 2009, 518, 729-734. |
| Usami, Kiyoaki, et al., “Pretilt Angle Control of Liquid Crystal Molecules by Photoaligned Films of Azobenzene-Containing Polyimide with Different Content of Side-Chain,” Journal of Applied Phyics 104, 113528 (2008). |
| Lee, Kyung Min, and White, Timothy J., “Photomechanical Response of Composite Structures Built from Azobenzene Liquid Crystal Polymer Networks,” Polymers (2011), 3, 1447-1457. |
| Georgiev, A., et al, “Polyimide Coatings Containing Azo-Chromophores as Structural Units,” Journal of Physics, Conference Series vol. 113 No. 1 (2008) 012032. |
| Sakamoto, Kenji, et al., “Highly Polarized Polymer-Based Light Emitting Diodes Fabricated by Using Very Thin Photoaligned Polyimide Layers,” Journal of Applied Physics 107, 113108 (2010). |
| Sakamoto, Kenji, et al., “Light Exposure Dependence of Molecular Orientation of Glassy Polyfluorene Layers Formed on Photo-Aligned Polyimide Films,” Colloids and Surfaces B: Biointerfaces 56, pp. 260-264 (2007). |
| Usami, K., et al., “Stability of Photo-Induced Alignment of Azobenzene-Containing Polyimides,” Molecular Crystals and Liquid Crystals (2005) 438:1, 227/[1791]-236[1800]. |
| Park, B., et al., “Thermal and Optical Stabilities of Photoisomerizable Polyimide Layers for Nematic Liquid Crystal Alignments,” Jpn. J. Appl. Phys. vol. 37 (1998) pp. 5663-5668. |
| Cain, J. C., “Para- and Meta-nitrosoacetanilide,” J. Chem. Soc., Trans. 1908, 93, 681-684. |
| Yu, Y., et al., “Precisely Direction-Controllable Bending of Cross-Linked Liquid-Crystalline Polymer Films by Light,” Mol. Cryst. Liq. Cryst., vol. 436, pp. 281/[1235]-290/[1244], 2005. |
| Si, J., et al., “Thermosetting enhancement of the light-induced polar orientation stability of molecules in polymers,” J. Appl. Phys. 85, 8018 (1999); doi: 10.1063/1.370637. |
| Eisenbach, C. D., “Relation between Photochromism of Chromophores and Free vol. Theory in Bulk Polyers,” Ber. Bunsenges. Phys. Chem. 1980, 84, 680. |
| Pieroni, O., et al., “Photoresponsive Polymeric Materials,” Trends Polym. Sci. (Cambridge, U.K.) 1995, 3, 282-287. |
| Mathisen, R., et al., “Imidization studies of polyamic acids by dye-labeling technique,” Polymer Preprints (American Chemical Society, Division of Polymer Chemistry) (1987), 28(1), 82-83. |
| Hergenrother, P.M., “Recent Developments in High Temperature Organic Polymers,” Polyimides and Other High-Temperature Polymers, Abadie, M.J.M. and Sillion, B., Eds., Elsevier: New York, 1991, pp. 1-18. |
| Yager, K. G., et al., “Azobenzene Polymers as Photomechanical and Multifunctional Smart Materials,” Intelligent Materials, Shahinpoor, M. and Schneider, H.-J., Eds., Royal Society of Chemistry: Cambridge, UK, 2008; pp. 424-446. |
| Irie, M, et al., “Photoresponsive Polymers,” Functional Monomers and Polymers, 2nd ed., Takemoto, K., et al., Eds., Dekker: New York, 1997, pp. 65-116. |
| Tan, Loon-Seng, et al., U.S. Appl. No. 13/557,326, filed Jul. 25, 2012. |
| Tan, Loon-Seng, et al., U.S. Appl. No. 13/546,439, filed Jul. 11, 2012. |
| Tan, Loon-Seng, et al., U.S. Appl. No. 13/661,194, filed Oct. 26, 2012. |
| Number | Date | Country | |
|---|---|---|---|
| 61636134 | Apr 2012 | US | |
| 61636170 | Apr 2012 | US |