Patent Application
20160233356
The present invention relates to a back-surface bridge type contact electrode of a crystalline silicon solar battery and a preparation method therefor, and falls within the technical field of solar batteries.
At present, local back surface field batteries are an important research and development direction of efficient crystalline silicon solar batteries, and by means of a back surface passivation technique and a local back surface field structure, the recombination in the back surface of a solar battery can be remarkably reduced, the back reflection within long-wave bands is improved, and the absorption of free carriers in the back surface is reduced, such that the conversion efficiency of the battery is improved. At present, in order to reduce the process for preparing a back passivation battery, a back surface passivation film is locally opened using a laser or chemical slurry erosion method, then an aluminium layer is formed on the back surface using a silk screen printing or evaporation method, and then aluminium atoms instead of silicon atoms enter the silicon crystal lattice in a high temperature process to form a p-type heavily-doped region, i.e. a local back surface field, below the open film region.
However, when using a conventional method of full back surface printing or aluminium layer depositing, it is easy to form voids in the contact region in the high temperature process due to the difference of diffusion coefficients between aluminium and silicon, which causes: 1. a local back surface field cannot be formed, and severe recombinations in the back surface are caused; 2. the contact area between the local back surface field and the aluminium-silicon alloy layer becomes small, and the fill factor is reduced; and 3. due to the void effect, the thickness of the local back surface field is insufficient, and the formation of the voids restricts current local back surface field batteries, particularly the efficiency improvement of back point contact batteries.
The technical problem to be solved by the present invention is to overcome the deficiencies in the prior art, and provide a back-surface bridge type contact electrode of a crystalline silicon solar battery, which can inhibit the formation of voids in the local back surface field, increase the thickness of the local back surface field, reduce the resistance loss due to the fact that a minority of carriers pass through the local back surface field to the contact region to be recombined, and improve the conversion efficiency of the back passivation battery.
The technical solution used in the present invention to solve the above-mentioned technical problems is: a back-surface bridge type contact electrode of a crystalline silicon solar battery, which comprises a local electrode connected to a local back surface field and a back surface electrode which is covered with a back surface passivation film on a contact surface with a silicon wafer substrate, at least one bridge electrode is provided between the local electrode and the back surface electrode, the contact surface of the bridge electrode and the silicon wafer substrate is also covered with the back surface passivation film, the local electrode is connected to the back surface electrode via the bridge electrode, and the back surface passivation film is also provided, besides at the connection region of the bridge electrode, between the local electrode and the back surface electrode.
Further, the width of the bridge electrode is 0.1-50,000 μm, and the length is 0.1-1,000 μm. By controlling the width and length of the bridge electrode, the total amount of silicon which diffuses into the aluminium-silicon liquid alloy in the high temperature process can be controlled.
Further, the material of the back surface passivation film is selected from one or more of aluminium oxide, silicon oxide, silicon nitride and titanium oxide.
Further, the materials of the local electrode, the back surface electrode and the bridge electrode contain aluminium.
Further, the cross section of the local electrode is in a line or dot shape, and the dot shape includes a circle, parallelogram or regular polygon.
Further, when the cross section of said local electrode is in a line shape, the width of the local electrode is not less than 1 μm, and the spacing between the centres of the local electrodes is not less than 100 μm.
Further, when the cross section of said local electrode is in a dot shape, the size of the local electrode is not less than 1 μm, and the spacing between the centres of the local electrodes is not less than 50 μm.
The present invention further provides a method for preparing the back-surface bridge type contact electrode of a crystalline silicon solar battery, which comprises the following steps:
1) providing a screen plate for silk screen printing, wherein the screen plate provides a gauze in the back surface electrode region and an array region composed of a plurality of local electrodes and bridge electrodes in the back-surface bridge type contact electrode of a crystalline silicon solar battery, through which a slurry can pass, and the other part is composed of a membrane which is impermeable to the slurry;
2) providing a silicon wafer substrate on which a back surface passivation film is deposited, and locally opening the film with a laser;
3) printing a metal slurry on the back surface of the silicon wafer substrate using the screen plate in step 1) by a silk screen printing method; and
4) the local electrodes and the silicon wafer substrate forming a local back surface field in a process of high temperature sintering.
The present invention further provides a method for preparing the back-surface bridge type contact electrode of a crystalline silicon solar battery, which comprises the following steps:
1) providing a silicon wafer substrate on which a back surface passivation film is deposited, and locally opening the film with a laser;
2) depositing a unit formed by the arrangement of a back surface electrode and a plurality of local electrodes and bridge electrodes in the back-surface bridge type contact electrode of a crystalline silicon solar battery on the back surface passivation film of the silicon wafer substrate by a CVD or PVD method; and
3) the local electrodes and the silicon wafer substrate forming a local back surface field in a process of high temperature sintering.
By using the above-mentioned technical solutions, the present invention has the following beneficial effects:
(1) the local electrode is used in the present invention to greatly reduce the probability of voids appearing in the local back surface field, and improve the open circuit voltage and the fill factor of the battery; and the formation of the local electrode in the open film region in the present invention restricts the transversal transmission of silicon in the electrode in the high temperature process, and if each electrode contains aluminium, it can enable the concentration of silicon in the aluminium-silicon liquid alloy to rapidly reach the saturation value, and silicon is rapidly precipitated from the aluminium silicon liquid in a temperature decreasing process and solidified at the aluminium-silicon interface to form a local back surface field, which greatly inhibits the generation of voids;
(2) the bridge electrode is used to conduct the electric current collected in the local electrode to the back surface electrode, and using the bridge electrode and the back surface electrode reduces the resistance of the back surface electrode, thereby reducing the resistance loss of the battery; and
(3) the process of the present invention is simple, can achieve the structure of the present invention by only printing once with regard to conventional silk screen printing, and is suitable for use in large-scale production.
In order to more easily and clearly understand the contents of the present invention, the present invention is further illustrated below in detail according to particular embodiments in combination with the drawings.
As shown in
The material of the back surface passivation film 2 may be selected from one or more of aluminium oxide, silicon oxide, silicon nitride and titanium oxide. The materials of the local electrode 3, the back surface electrode 1 and the bridge electrodes 4 contain aluminium.
This embodiment provides a circular hole-shaped array of back-surface bridge type contact electrodes of a crystalline silicon solar battery, which is prepared through silk screen printing, and after the deposition of an Al2O3/SiNx: H passivation film on the back surface is complete, the film is opened using a chemical slurry. Through a screen plate design, the use of silk screen printing and a well designed back surface screen plate, an aluminium slurry is printed on the back surface to make it form a pattern formed by an array of a plurality of circular holes, wherein the spacing between the circular hole contacts is 500 μm, the pattern of a single circular hole point contact is as shown in
As shown in
The material of the back surface passivation film 2 may be selected from one or more of aluminium oxide, silicon oxide, silicon nitride and titanium oxide.
The materials of the local electrode 3, the back surface electrode 1 and the bridge electrodes 4 contain aluminium.
This embodiment provides a square hole-shaped array of back-surface bridge type contact electrodes of a crystalline silicon solar battery, which is prepared through silk screen printing, and after the deposition of an Al2O3/SiNx: H passivation film 2 on the back surface and the local opening of the film with a laser are complete, through a screen plate design, an aluminium slurry is printed on the back surface using silk screen printing to make it form a pattern formed by the array of square holes. The spacing between the centres of the square holes is 400 μm, the pattern of a single square hole point contact is as shown in
As shown in
The material of the back surface passivation film 2 may be selected from one or more of aluminium oxide, silicon oxide, silicon nitride and titanium oxide. The materials of the local electrode 3, the back surface electrode 1 and the bridge electrodes 4 contain aluminium.
This embodiment provides a back-surface bridge type contact electrode of a crystalline silicon solar battery, which is prepared through silk screen printing, wherein a screen plate required for the silk screen printing is designed first, and after the deposition of an Al2O3/SiNx: H passivation film on the back surface and the local opening of the film with a laser are complete, silk screen printing and a well designed back surface screen plate are used and an aluminium slurry is printed on the back surface, so as to make it form a pattern formed by a line-shaped array. The spacing between the lines is 1200 μm, and a part of the line-shaped array on the back surface is as shown in
As shown in
The material of the back surface passivation film 2 may be selected from one or more of aluminium oxide, silicon oxide, silicon nitride and titanium oxide.
The materials of the local electrode 3, the back surface electrode 1 and the bridge electrode 4 contain aluminium.
The cross section of the local electrode 3 can be in a line or dot shape, and the dot shape includes a circle, parallelogram or regular polygon.
When the cross section of the local electrode 3 is in a line shape, the width of the local electrode 3 is not less than 1 μm, and the spacing between the centres of the local electrodes 3 is not less than 100 μm.
When the cross section of the local electrode 3 is in a dot shape, the size of the local electrode 3 is not less than 1 μm, and the spacing between the centres of the local electrodes 3 is not less than 50 μm.
A method for preparing the back-surface bridge type contact electrode of a crystalline silicon solar battery is provided, which comprises the following steps:
1) providing a silicon wafer substrate 6 on which a back surface passivation film 2 is deposited, and locally opening the film with a laser;
2) depositing a unit formed by the arrangement of a back surface electrode 1 and a plurality of local electrodes 3 and bridge electrodes 4 in the back-surface bridge type contact electrode of a crystalline silicon solar battery on the back surface passivation film 2 of the silicon wafer substrate 6 by a CVD or PVD method; and
3) the local electrodes 3 and the silicon wafer substrate 6 forming a local back surface field 5 in a process of high temperature sintering.
The above-mentioned particular embodiments further illustrate the solved technical problems, the technical solutions and the beneficial effects of the present invention in detail; and it is to be understood that the above description is merely particular embodiments of the present invention and is not used to limit the present invention, and any modifications, equivalent alternatives, improvements, etc. that are made within the spirit and principle of the present invention should be included within the scope of protection of the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201310440907.5 | Sep 2013 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2014/083399 | 7/31/2014 | WO | 00 |