Patent Grant
10563959
The present invention relates to a ballistic protective textile structure and a method for making it.
More specifically, the present invention relates to a personal ballistic protective textile structure which is usually called “soft armor”.
As is known, the capability of a fabric material to reject a bullet or a penetration of a knife or pointed implement, essentially depends on the nature of the textile fibers used, the fabric material weave and the fabric material weight per surface unit, or fabric areal density.
A demand of improved small weight and comfortable fabric materials for the above applications is a main market requirement in several fields of ballistic protective garments.
At present, the main reinforcement fibers forming the ballistic protective fabrics substantially comprise para-aramid and ultra-high-molecular-weight polyethylene (UHMWPE) fibers, which, owing to their peculiar mechanical characteristics, are adapted to efficiently adsorb forces applied thereon.
In the so-called “UD” or unidirectional products, the reinforcement fibers, which are arranged with a parallel arrangement, are coupled to a suitable film or resin material, substantially operating as a glue for said fibers, to allow the fiber layer to be handled in making the protective device or garment, without causing the parallel arrangement of the fibers to be changed.
In this connection, it should be pointed out that the fiber weight/matrix ratio, jointly to the yarn and support material features, control the ballistic performance of the product.
The UD ballistic protective garments usually have a flexibility and draping capability less than that of textile approaches, thereby the garment comfort conditions are very poor.
In fact, the UD article parallel fiber arrangement and, mainly, the take-up of the weave, that is a straddling of the warp and weft yarns, are design parameters providing the textile material with a maximum resistance against bullets, fragments, knives, pointed implements and so on, since said fibers are all arranged with a parallel arrangement and aligned in a single axial direction.
Because of the above mentioned taking-up of the warp and weft yarns, and consequently because of an offset of the fibers away from their axis at warp and weft yarn overlapping points, the article mechanical strength values are usually less than those of the same fibers in an UD construction.
Using high toughness fibers, such as para-aramid and UHMWPE fibers, to provide overlapped unidirectional products is already known for applications in textile structures, both flexible and stiff.
The above structures can be further subjected to impregnating processes, to improve their impact resistance, while partially modifying their bending characteristics.
Conventional methods for making the above textile articles comprise an opening step of mechanically opening the fibers and a stabilizing step, by different thermoplastic matrix arrangements.
The above process, while allowing to properly exploit the yarns and reduce the finished product weight, on the other hand greatly reduces the mechanical characteristics of the yarns.
In this connection, it should be pointed out that different commercial approaches are at present available, of a non-monolithic nature, that is different from homogeneous fabrics, to meet different related standards, and providing articles resisting against conventional bullets, but not against those of military guns, in which case an improved protective capability is required, usually achieved by additional reinforcement plates (for example of ceramics and UHMWPE materials).
Accordingly, the aim of the present invention is to provide such a composite construction textile product and a method for making it, for the ballistic protective field, overcoming the above mentioned problems of prior textile constructions, while preserving the typical bending properties of fabric materials.
Within the scope of the above mentioned aim, a main object of the invention is to provide such a textile product, and a method for making it, providing an alternative textile structure for UD products, while overcoming the limitations of the latter.
Actually, in many industrial applications, the protective garment comprising open fibers unidirectionally (UD) arranged on a thin resin or thermoplastic film layer, replaces fabric materials by providing a smaller areal density value while preserving a high ballistic performance, the garment weight being the same, since the UD products are not made by textile methods, but by other processes typical of other industrial fields.
Within the above mentioned aim, a main object of the invention is to provide such a composite textile garment or construction including warp yarns preferably consisting of a para-aramid or ultra high molecular polyethylene (UHMPE), glass, polybenzoxazole (PBO) fibers, and weft yarns of a thermoplastic material such as polyethylene terephthalate (PET), polypropylene (PP), polyethylene (PE), UHMWPE, polyurethane (PU) and so on, in a para-aramid film or yarn strip form.
The construction thus made is moreover processed by a suitable laminating method, to partially soften or melt the weft yarn thermoplastic material and provide warp fibers made rigid with one another by the unidirectional weft yarn thermoplastic material operating as a binding material.
This solution, if used in combination with a set number of other layers of the same type or even of different textile structures and materials, allows, the areal density being the same, to provide a quick dissipation of the penetrating bullet energy, thereby stopping the movement and penetration of the bullet.
The hereinbelow disclosed construction and method are mainly used for making ballistic protective garments or products, either of a hybrid or a monolithic type, for the above so-called soft protection applications.
According to one aspect of the present invention, the above mentioned aim and objects, as well as yet other objects, which will become more apparent hereinafter, are achieved by a ballistic protective textile structure or construction and a method for making it, as claimed in the enclosed claims.
Further characteristics and advantages of the present invention will become more apparent hereinafter from the following detailed disclosure of a preferred, though not exclusive, embodiment of the invention, which is illustrated, by way of an indicative but not limitative example, in the accompanying drawings, where:
With reference to the number references of the above mentioned figures, the method according to the present invention comprises a first flat or plain weaving step, in which a first element, generally indicated by the reference number 1, comprising unidirectional warp fibers or flat strips is made.
Said flat strips are arranged on suitable creels and are interleaved in a warp arrangement with a second element 2, consisting of like unidirectional thread flat strips, or a thermoplastic matrix film.
The warp components can comprise either warp yarns or flat strips made of a para-aramid matrix, such as KEVLAR® (poly-paraphenylene terephthalamide), TWARON® (p-phenylene terephthalamide) or the like, as commercially available, or warp yarns or flat strips of a ultra-high-molecular-weight polyethylene (UHMWPE) matrix, such as SPECTRA® (gel-spun UHMWPE), DYNEEMA® (gel-spun UHMWPE), TENSYLON® (UHMWPE material), or the like as commercially available.
The weft yarns advantageously comprises high toughness yarns.
In this connection, it should be pointed out that the yarns used do not have any linear density limitations.
The weft yarns, in turn, comprise flat strip elements of a para-aramid matrix, such as KEVLAR®, TWARON® or other commercially available para-aramid matrix arrangements, as suitably processed by glue, adhesive or thermoplastic materials, or further flat strip elements of a UHMWPE matrix, such as SPECTRA®, DYNEEMA®, TENSYLON®, or other commercially available arrangements, or further thermoplastic films such as PE, PU, PP, polyamide (PA), ethylene-vinyl acetate (EVA), or, in principle, any desired or target thermoplastic material suitable for extruding a film.
The most suitable condition for holding such a yarn/thermoplastic material ratio without negatively affecting the end energy or power dispersion properties, is achieved by using, as a weft pick or yarn arrangements, flat strip elements of a height less than or equal to 2 cm.
The material thus made is subject to a further stabilizing process, comprising partially melting the thermoplastic matrix by hot calendering or laminating, or by “IR” lamps, operating under operative conditions varying depending on the thermoplastic material used.
The stabilizing method can be carried out both in-line on the loom, and in parallel on dedicated systems.
The above material combination can be further impregnated by additional elements, indicated by the reference number 3, such as thermoplastic matrixes based on rubber or elastomeric polymers or a combination thereof, or being laminated by different thermoplastic films such as PE, PU, PP, PA, EVA or, in principle, by any thermoplastic materials providing an extruded film.
The above mentioned additional components facilitate an impact energy distribution through the underlying support, owing to a viscoelastic fiber deforming, breaking or fibrillating.
The thermoplastic impregnation moreover properly compacts either one or more support layers, including the above mentioned elements 1 and 2, by a molding method.
With reference to
Ballistic data show that the above structure does not provide results like those which can be achieved by individual layers.
In fact, the presence of a gap or discontinuity, facilitates a reduction of traumas deriving from a bullet impact, and an improved energy distribution.
Said discontinuity or gap can comprise air, or any other desired materials, such as different density and thickness felt or foamed materials.
The examples mentioned hereinbelow have been achieved by experimental tests performed by the Applicant and are herein shown only by way of an illustrative and not limitative purpose.
The tests shown, in particular, are related to packages having a weight from 5.10 kg/m2 and 5.2 kg/m2, depending on the individual layer weights.
The packages have been applied to a plasticine block designed to verify traumas of bullets fired with a firing speed according to the NIJ standard, that is Cal. 9 mm FMJ RN and 44 Mag. JHC bullets, to measure the VO value.
For each package three shots have been fired.
28 layers of a 0°/90° crossed unidirectional fabric comprising a 930 dtex multifilament para-aramid fiber warp (element 1) and a middle toughness 2 cm TENSYLON® flat strip (element 2) being stabilized by a PE base thermoplastic film.
The speed and trauma data are shown in the following table:
38 layers of a 0°/90° crossed unidirectional fabric comprising a 930 dtex multifilament para-aramid fiber warp (element 1) and a 2 cm ionomeric polyethylene film flat strip (element 2).
The speed and trauma data are shown in the following table:
54 layers of a 0°/90° crossed unidirectional fabric comprising a 670 dtex multifilament para-aramid fiber warp (element 1) and a 2 cm ionomeric polyethylene film flat strip (element 2).
The speed and trauma data are shown in the following table:
It has been found that the invention fully achieves the intended aim and objects.
In practicing the invention, the chosen details may be different both with respect to the individual constructional layer of the package, and with respect to the individual layer component elements.
| Number | Date | Country | Kind |
|---|---|---|---|
| MI2012A2085 | Dec 2012 | IT | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2013/002657 | 11/28/2013 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2014/087212 | 6/12/2014 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6642159 | Bhatnagar | Nov 2003 | B1 |
| 20060040576 | Citterio | Feb 2006 | A1 |
| 20110269359 | Tam | Nov 2011 | A1 |
| 20110283875 | Citterio | Nov 2011 | A1 |
| 20120189804 | Chiou | Jul 2012 | A1 |
| 20130059494 | Tam | Mar 2013 | A1 |
| 20130101787 | Bhatnagar | Apr 2013 | A1 |
| 20140072758 | Arvidson | Mar 2014 | A1 |
| 20140083285 | Marissen | Mar 2014 | A1 |
| 20140087125 | Ardiff | Mar 2014 | A1 |
| 20140302274 | Tam | Oct 2014 | A1 |
| 20160122909 | Ardiff | May 2016 | A1 |
| Number | Date | Country |
|---|---|---|
| 2388549 | Nov 2011 | EP |
| 2009151484 | Dec 2009 | WO |
| 2011082201 | Jul 2011 | WO |
| 2011156577 | Dec 2011 | WO |
| Entry |
|---|
| International Search report dated Feb. 21, 2014. |
| Number | Date | Country | |
|---|---|---|---|
| 20150323290 A1 | Nov 2015 | US |