Information
-
Patent Grant
-
5780405
-
Patent Number
5,780,405
-
Date Filed
Monday, March 18, 199628 years ago
-
Date Issued
Tuesday, July 14, 199826 years ago
-
Inventors
-
Original Assignees
-
Examiners
Agents
-
CPC
-
US Classifications
Field of Search
US
- 510 141
- 510 152
- 510 153
- 510 447
- 510 450
- 510 475
- 510 476
-
International Classifications
-
Abstract
The present invention is directed to synthetic bar compositions wherein relatively small amounts of specified polyoxyethylene-polypropylene nonionic polymer has been found to enhance mildness of bar compositions.
Description
FIELD OF THE INVENTION
The present invention relates to synthetic bar compositions (i.e., bars in which at least some fatty acid soap has been replaced by synthetic surfactants, such as anionic surfactants).
BACKGROUND
Traditionally, soap has been utilized as a skin cleanser. Notwithstanding its many advantages (e.g., inexpensive, easy to manufacture into bars, having good lathering properties), soap is a very harsh chemical. Irritated and cracked skin often result from the use of soap, especially in colder climates.
In order to maintain cleaning effectiveness and reduce harshness, the art has used synthetic surfactants to replace some or all of the soap. In particular, anionic surfactants have been used because these tend to most clearly mimic the lather generation which soap readily provides.
Anionic surfactants, however, are still harsh. One method of reducing the harshness of anionic surfactants is to utilize other surfactants such as nonionic or other mildness surfactants (e.g., amphoteric). The use of surfactants other than anionics, however, can introduce other problems. For example, nonionic surfactants generally do not generate creamy thick lather as do anionics; and both nonionics and amphoterics, for example can be sticky and introduce processing difficulties.
For this reason, the art is always searching for materials which are milder than anionic and/or which can be used to replace at least some of the anionic surfactants, yet, which do not simultaneously seriously compromise lather generation or processing efficiency. Further, even if the anionic is not substituted, the art is always searching for materials which can substitute for inerts and/or other fillers and produce enhanced mildness.
Unexpectedly, applicants have found that the use of relatively low levels of specific nonionic polymeric surfactants can be used to obtain these goals. That is, at levels no higher than 10% by wt. of the bar composition, the polymers provide enhanced mildness without sacrificing processability or lather. While not wishing to be bound by theory, it is believed that the copolymers may be interacting with anionic surfactant to form polymer-surfactant complexes thereby reducing free anionic surfactant (known for its harshness) from the bar.
The use of polyoxyethylene polyoxypropylene (EO-PO) nonionic polymeric surfactants in bar compositions per se is not new.
U.S. Pat. No. 3,312,627 to Hooker, for example, teaches bars substantially free of anionic detergents comprising 0 to 70% by weight EO-PO polymer, polyethylene glycol (PEG) or derivatives of these compounds as base; and 10 to 70% of a nonionic lathering component. In order to give these bars more "soap-like" characteristics, the reference contemplates use of 10%-80% lithium soap. It is clear that use of lithium soap is unique to the invention (column 8, lines 20-23) and that use of other soaps or anionic (other than fatty acid lithium soap) is not contemplated. Thus, this reference clearly differs from the composition of the invention which comprise 10 to 50% of a surfactant system of which at least 50% (though no more than 40% total of total composition) is anionic surfactant.
U.S. Pat. No. 3,766,097 to Rosmarin discloses the use of 30%-50% of a specified EO-PO copolymer (Pluronic F-127) in a bar using sodium cocoyl isethionate as primary anionic surfactant. Here again, the polymer is being used as a bar structurant at levels well above the 10% upper limit of the subject invention. There is no teaching or suggestion that the polymers can be used in combination with anionic at much lower levels to unexpectedly and remarkably enhance mildness (e.g., reduce irritation) at these low levels.
U.S. Ser. No. 08/213,287 to Chambers et al. (assigned to Lever Brothers) teaches that certain solid EO-PO polymers can be used as alternatives to solid polyethylene glycols (PEGs) as bar structurants for synthetic bar formulations. Once more, the polymers are contemplated for use as structurants, i.e., at much higher levels than the levels under 10% by wt. of the subject application. There is again no teaching or suggestion that the polymers can be used at much lower levels (both as total percentage of compositions and as ratio to total level of anionics) to provide enhanced mildness (i.e., reduced skin irritation).
BRIEF SUMMARY OF THE INVENTION
Applicants have now found that the use of relatively small amounts of defined polyoxyethylene-polyoxypropylene nonionic polymer surfactants in bar compositions comprising primarily anionic surfactant systems remarkably and unexpectedly enhances the mildness of these bars.
More specifically, applicants' invention relates to bar compositions comprising:
(a) 10% to 70% by wt. total composition of a surfactant system selected from the group consisting of anionic surfactants, nonionic surfactants (other than the nonionic EO-PO polymer), cationic surfactants, amphoteric surfactants and mixtures thereof;
wherein the anionic surfactant comprises at least 50%, preferably at least 60% of said surfactant system and wherein the anionic component further comprises no more than about 40% by wt. of total composition;
(b) 20% to 85% by wt., preferably 30 to 70% total composition of a bar structurant selected from the group consisting of alkylene oxide compounds having a molecular weight of from about 2000 to about 25,000, preferably 3,000 to 10,000; C.sub.8 -C.sub.22 free fatty acids, paraffin waxes; water soluble starches (e.g., maltodextrin); and C.sub.8 -C.sub.20 alkanols; and
(c) 3% to 10% by wt. total composition of a polyoxyethylene-polyoxypropylene nonionic polymer surfactant (EO-PO polymer);
wherein ratio of anionic surfactant to EO-PO polymer is between 2.5:1 to 10:1, preferably 4:1 to 7:1.
The composition may optionally comprise 0% to 25%, preferably 2% to 15% by wt. solvent such as ethylene oxide or propylene oxide.
FIG. 1 shows the Zein % dissolved by acyl isethionate/cocoamidopropyl betaine as a function of Pluronic (EO-PO polymer) concentration. In contrast to PEG 8000, Pluronic F88 and 25R8 significantly reduced the Zein % dissolved at even quite low levels, such as 0.3 wt. % (at sodium acyl isethionate (SAI) to EO-PO weight ratio at 1:0.15, this is equivalent to about 4% EO-PO in the bar of Formulation (a) in Table 2, Example 1). Therefore the irritation potential of a personal washing bar can be further reduced by including relatively low levels (i.e. 10% and under in a full bar composition; this would correspond to about 0.74% in the liquor as shown in FIG. 1) of Pluronics in the bar formulation. The data also showed that EO-terminated Pluronic F88 is potentially a better mildness enhancer than the PO-terminated Pluronic 25R8.
FIG. 2 shows the EO-PO polymer of the invention significantly reduces skin irritation caused by DEFI.
DETAILED DESCRIPTION OF THE INVENTION
The present invention relates to synthetic bar compositions wherein the majority of the surfactant system of the bar comprises anionic surfactant; and to specific nonionic copolymers which can be used in such bar compositions to significantly enhance bar mildness.
More specifically, the bar compositions comprise
(a) 10% to 70% by weight total composition of a surfactant system wherein said surfactant system is selected from the group consisting of anionic surfactants, nonionic surfactants (other than the EO-PO polymer), amphoteric surfactants, cationic surfactants and mixtures thereof, wherein the anionic comprises 50% or more, preferably 60% or more, of the surfactant system and the anionic further comprises no more than 40% of the total composition;
(b) 20% to 85% by wt. total composition of a bar structurant selected from the group consisting of polyalkylene glycols having a MW of from about 2,000 to 25,000 (which may optionally include 1% to 5% higher molecular weight polyalkylene glycols having MW from 50,000 to 500,000, especially around 100,000); C.sub.8 to C.sub.24, preferably C.sub.12 to C.sub.24 fatty acids; paraffin waxes; water soluble starches (e.g., maltodextrin); and C.sub.8 to C.sub.20 alkanols (e.g., cetyl alcohol); and
(c) 3% to 10% by weight total composition of a polyoxyethylene, polyoxypropylene nonionic polymer surfactant
wherein ratio of anionic surfactant to EO-PO polymers is between 2.5:1 to 10:1, preferably 4:1 to 7:1.
Surfactant System
The anionic detergent active which may be used may be aliphatic sulfonates, such as a primary alkane (e.g., C.sub.8 -C.sub.22) sulfonate, primary alkane (e.g., C.sub.8 -C.sub.22) disulfonate, C.sub.8 -C.sub.22 alkene sulfonate, C.sub.8 -C.sub.22 hydroxyalkane sulfonate or alkyl glycerol ether sulfonate (AGS); or aromatic sulfonates such as alkyl benzene sulfonate.
The anionic may also be an alkyl sulfate (e.g., C.sub.12 -C.sub.8 alkyl sulfate) or alkyl ether sulfate (including alkyl glycerol ether sulfates). among the alkyl ether sulfates are those having the formula:
RO(CH.sub.2 CH.sub.2 O).sub.n SO.sub.3 M
wherein R is an alkyl or alkenyl having 8 to 18 carbons, preferably 12 to 18 carbons, n has an average value of greater than 1.0, preferably greater than 3; and M is a solubilizing cation such as sodium, potassium ammonium or substituted ammonium. Ammonium and sodium lauryl ether sulfates are preferred.
The anionic may also be alkyl sulfosuccinates (including mono- and dialkyl, e.g., C.sub.6 -C.sub.22 sulfosuccinates); alkyl and acyl taurates, alkyl and acyl sarcosinates, sulfoacetates, C.sub.8 -C.sub.22 alkyl phosphates and phosphates, alkyl phosphate esters and alkoxyl alkyl phosphate esters, acyl lactates, C.sub.8 C.sub.22 monoalkyl succinates and maleates, sulphoacetates, alkyl glucosides and acyl isethionates.
Sulfosuccinates may be monoalkyl sulfosuccinates having the formula:
R.sup.4 O.sub.2 CCH.sub.2 CH(SO.sub.3 M)CO.sub.2 M;
and
amide-MEA sulfosuccinates of the formula:
R.sup.4 CONHCH.sub.2 CH.sub.2 O.sub.2 CCH.sub.2 CH(SO.sub.3 M)CO.sub.2 M
wherein R.sup.4 ranges from C.sub.8 -C.sub.22 alkyl and M is a solubilizing cation.
Sarcosinates are generally indicated by the formula:
R'CON(CH.sub.3)CH.sub.2 CO.sub.2 M,
wherein R ranges from C.sub.8 -C.sub.20 alkyl and M is a solubilizing cation.
Taurates are generally identified by formula:
R.sup.2 CONR.sup.3 CH.sub.2 CH.sub.2 SO.sub.3 M
wherein R.sup.2 ranges from C.sub.8 -C.sub.8 alkyl, R.sup.3 ranges from C.sub.1 -C.sub.4 a alkyl and M is a solubilizing cation.
Particularly preferred are the C.sub.8 -C.sub.18 acyl isethionates. These esters are prepared by reaction between alkali metal isethionate with mixed aliphatic fatty acids having from 6 to 18 carbon atoms and an iodine value of less than 20. At least 75% of the mixed fatty acids have from 12 to 18 carbon atoms and up to 25% have from 6 to 10 carbon atoms.
Acyl isethionates, when present, will generally range from about 10% to about 70% by weight of the total composition. Preferably, this component is present from about 30% to about 60%.
The acyl isethionate may be an alkoxylated isethionate such as is described in llardi et al., U.S. Pat. No. 5,393,466, hereby incorporated by reference. This compound has the general formula: ##STR1## wherein R is an alkyl group having 8 to 18 carbons, m is an integer from 1 to 4, X and Y are hydrogen or an alkyl group having 1 to 4 carbons and M.sup.+ is a monovalent cation such as, for example, sodium, potassium or ammonium.
The anionic surfactant comprises 50% or more of the total surfactant system, but should comprise no more than 40% by wt. of the total composition.
Amphoteric detergents which may be used in this invention include at least one acid group. This may be a carboxylic or a sulphonic acid group. They include quaternary nitrogen and therefore are quaternary amido acids. They should generally include an alkyl or alkenyl group of 7 to 18 carbon atoms. They will usually comply with an overall structural formula. ##STR2## where R.sup.1 is alkyl or alkenyl of 7 to 18 carbon atoms; R.sup.2 and R.sup.3 are each independently alkyl, hydroxyalkyl or carboxyalkyl of 1 to 3 carbon atoms;
m is 2 to 4;
n is O to 1;
X is alkylene of 1 to 3 carbon atoms optionally substituted with hydroxyl, and
Y is --CO.sub.2 --or--SO.sub.3 --
Suitable amphoteric detergents within the above general formula include simple betaines of formula: ##STR3## and amido betaines of formula: ##STR4## wherein m is 2 or 3.
In both formulae R.sup.1, R.sup.2, and R.sup.3 are as defined previously. R.sup.1 may in particular be a mixture of C.sub.12 and C.sub.14 alkyl groups derived from coconut so that at least half, preferably at least three quarters of the groups R.sup.1 are preferably methyl.
A further possibility is that the amphoteric detergent is a sulphobetaine of formula ##STR5## wherein m is 2 or 3, or variants of these in which -(CH.sub.2).sub.3 SO.sub.3 -is replaced by ##STR6## in these formulae R.sup.1, R.sup.2 and R.sup.3 are as discussed previously.
The nonionic which may be used includes in particular the reaction products of compounds having a hydrophobic group and a reactive hydrogen atom, for example aliphatic alcohols, acids, amides or alkyl phenols with alkylene oxides, especially ethylene oxide either alone or with propylene oxide. Specific nonionic detergent compounds are alkyl (C.sub.6 -C.sub.22) phenols-ethylene oxide condensates, the condensation products of aliphatic (C.sub.8 C.sub.18) primary or secondary linear or branched alcohols with ethylene oxide, and products made by condensation of ethylene oxide with the reaction products of propylene oxide and ethylenediamene Other so-called nonionic detergent compounds include long chain tertiary amine oxides, long chain tertiary phosphine oxides and dialkyl sulphoxides.
The nonionic may also be a sugar amide, such as a polysaccharide amide. Specifically, the surfactant may be one of the lactobionamides described in U.S. Pat. No. 5,389,279 to Au et al. which is hereby incorporated by reference or it may be one of the sugar amides described in U.S. Pat. No. 5,009,814 to Kelkenberg, hereby incorporated into the subject application by reference.
Other surfactants which may be used are described in U.S. Pat. No. 3,723,325 to Parran Jr. which is also incorporated into the subject application by reference.
Nonionic and cationic surfactants which may be used include any one of those described in U.S. Pat. No. 3,761,418 to Parran, Jr. hereby incorporated by reference into the subject application. Those included are the aldobionamides taught in U.S. Pat. No. 5,389,279 to Au et al. and the polyhydroxy fatty acid amides as taught in U.S. Pat. No. 5,312,934 to Letton, both of which are incorporated by reference into the subject application.
The surfactants generally comprise 10 to 50% of the total composition except, as noted that anionic comprises 50% or more of the surfactant system and no more than 40% total.
A preferred surfactant system is one comprising acyl isethionate and a amphoteric, i.e., betaine, as co-surfactant.
Structurant
The structurant of the invention can be a water soluble or water insoluble structurant.
Water soluble structurants include moderately high molecular weight polyalkylene oxides of appropriate melting point (e.g., 40.degree. to 100.degree. C., preferably 50.degree. to 90.degree.) and in particular polyethylene glycols or mixtures thereof.
Polyethylene glycols (PEG's) which are used may have a molecular weight in the range 2,000 to 25,000, preferably 3,000 to 10,000. However, in some embodiments of this invention it is preferred to include a fairly small quantity of polyethylene glycol with a molecular weight in the range from 50,000 to 500,000, especially molecular weights of around 100,000. Such polyethylene glycols have been found to improve the wear rate of the bars. It is believed that this is because their long polymer chains remain entangled even when the bar composition is wetted during use.
If such high molecular weight polyethylene glycols (or any other water soluble high molecular weight polyalkylene oxides) are used, the quantity is preferably from 1% to 5%, more preferably from 1% or 1.5% to 4% or 4.5% by weight of the composition. These materials will generally be used jointly with a large quantity of other water soluble structurant such as the above mentioned polyethylene glycol of molecular weight 2,000 to 25,000, preferably 3,000 to 10,000.
Water insoluble structurants also have a melting point in the range 40.degree.-100.degree. C., more preferably at least 50.degree. C., notably 50.degree. C. to 90.degree. C. Suitable materials which are particularly envisaged are fatty acids, particularly those having a carbon chain of 12 to 24 carbon atoms. Examples are lauric, myristic, palmitic, stearic, arachidic and behenic acids and mixtures thereof. Sources of these fatty acids are coconut, topped coconut, palm, palm kernel, babassu and tallow fatty acids and partially or fully hardened fatty acids or distilled fatty acids. Other suitable water insoluble structurants include alkanols of 8 to 20 carbon atoms, particularly cetyl alcohol. These materials generally have a water solubility of less than 5 g/litre at 20.degree. C.
Soaps (e.g., sodium stearate) can also be used at levels of about 1% to 15%. The soaps may be added neat or made in situ by adding a base, e.g., NaOH, to convert free fatty acids.
The relative proportions of the water soluble structurants and water insoluble structurants govern the rate at which the bar wears during use. The presence of the water-insoluble structurant tends to delay dissolution of the bar when exposed to water during use and hence retard the rate of wear.
The structurant is used in the bar in an amount of 20% to 85%, preferably 30% to 70% by wt.
EO-PO Polymer The polyoxyethylene polyoxypropylene nonionic copolymers (EO-PO copolymers) of the subject invention are generally commercially available polymers having a broad molecular weight range and EO/PO ratio and a melting temperature of from about 25.degree. to 85.degree. C., preferably 40.degree. to 65.degree. C.
Generally, the polymers will be selected from one of two classes of polymers, i.e., (1) (EO).sub.m (PO).sub.n (EO).sub.m type copolymers or (PO).sub.n (EO).sub.m (PO).sub.n type copolymers of defined m/n ratio and optional hydrophobic moieties (e.g., decyltetradecanol ether) attached to either EO or PO compounds (such products are commercially available for example, from BASF under the Trademark Pluronic.RTM. or Pluronic-R.RTM., respectively); or (2) EO-PO polymers with amine constituents such as N.sub.2 C.sub.2 H.sub.4 (PO).sub.4n (EO).sub.4m or N.sub.2 C.sub.2 H.sub.4 (EO).sub.4m (PO).sub.4n with defined values of m and n and optional hydrophobic moieties �for example?! attached to either EO or PO components (such products are commercially available, for example from BASF as Tetronic.RTM. and Tetronic-R.RTM., respectively).
Specifically, examples of various Pluronic and Tetronic EO-PO polymers are set forth in Table 1 below wherein T.sub.m (.degree.C.) and Ross Miles foam height data (measured at 0.1% and 50.degree. C.) were digested from literature from BASF.
TABLE 1______________________________________ Foam EO and PO T.sub.m Heights NumberPolymer (.degree.C.) (ml) m/n______________________________________Pluronic: (EO).sub.m --(PO).sub.n --(EO).sub.m F38 48 35 46/16 F68 52 35 75/30 F77 48 47 52/35 F87 49 44 62/39 F88 54 48 97/39 F98 58 43 122/47 F108 57 41 128/54 F127 56 41 98/67Pluronic-R: (PO.sub.n --(EO).sub.m --(PO).sub.n 10R8 46 20 90/9 17R8 53 2 155/15 25R8 54 15 227/21Tetronic: N.sub.2 C.sub.2 H.sub.4 --(PO).sub.4n (EO).sub.4m 707 46 60 35/12 1107 51 50 64/20 908 58 40 85/16 1307 54 40 78/25 1508 60 40 159/30Tetronic-R: N.sub.2 C.sub.2 H.sub.4 --(EO).sub.4m (PO).sub.4n 90R8 47 0 90/17 110R7 47 0 64/21 150R8 53 0 12/29______________________________________
In general, the molecular weight of the copolymers used ranges from 2,000 to 25,000 (preferably 3,000 to 10,000). The EO-terminated polymers (Pluronic and Tetronic) are preferred to the PO-terminated ones (Pluronic-R and Tetronic-R) for the advantages of mildness enhancement and lather generation. To ensure water solubility, we prefer that the portion of ethylene oxide moiety per mole is between 50% to 90% wt., more preferably 60-85% wt. In other words, 2m:n (for Pluronic) or m:n (for Tetronic) ranges from 1.32 to 11.9, preferably 2.0 to 7.5.
As noted, melting temperature of the compounds must be about 25.degree.-85.degree. , preferably 40.degree. to 65.degree. C., the latter being more favorable for processing (e.g., chips form more easily and logs plod more readily).
Bars of the invention may comprise 0% to 25%, preferably 2% to 15% by wt. of an emollient such as ethylene glycol, propylene glycol and/or glycerine.
Other Ingredients
Bar compositions of this invention will usually contain water, but the amount of water is only a fairly small proportion of the bar. Larger quantities of water reduce the hardness of the bars. Preferred is that the quantity of water is not over 15% by weight of the bars, preferably 1% to about 10%, more preferably 3% to 9%, most preferably 3% to 8%.
Bars of this invention may optionally include so-called benefit agents - materials included in relatively small proportions which confer some benefit additional to the basic cleansing action of the bars. Examples of such agents are: skin conditioning agents, including emollients such as fatty alcohols and vegetable oils, essential oils, waxes, phospholipids, lanolin, anti-bacterial agents and sanitizers, opacifiers, pearlescers, electrolytes, perfumes, sunscreens, fluorescers and coloring agents. Preferred skin conditioning agents comprise silicone oils, mineral oils and/or glycerol.
The examples below are intended to better illustrate the invention, but are not intended to be limiting in any way.
All percentages, unless otherwise noted, are intended to be percentages by weight.
EXAMPLES
Methodology
Mildness Assessments
Zein dissolution test was used to preliminarily screen the irritation potential of the formulations studied. In an 8 oz. jar, 30 mLs of an aqueous dispersion of a formulation were prepared. The dispersions sat in a 45.degree. C. bath until fully dissolved. Upon equilibration at room temperature, 1.5 gms of zein powder were added to each solution with rapid stirring for one hour. The solutions were then transferred to centrifuge tubes and centrifuged for 30 minutes at approximately 3,000 rpms. The undissolved zein was isolated, rinsed and allowed to dry in a 60.degree. C. vacuum oven to a constant weight. The percent zein solubilized, which is proportional to irritation potential, was determined gravimetrically.
The Protocol of 3-Day Patch Test
Patch test was used to evaluate skin mildness of aqueous dispersions containing 1% DEFI active (sodium cocoyl isethionate) and different levels of the structurant/coactives. Patches (Hilltop.RTM. Chambers, 25 mm in size) were applied to the outer upper arms of the panelists under bandage type dressings (Scanpor.RTM. tape). After each designated contact periods (24 hrs. for the first patch application, 18 hrs. for the second and third applications), the patches were removed and the sites were visually ranked in order of severity (erythema and dryness) by trained examiners under consistent lighting.
Formulation Processing
Bar formulations were prepared in a 2-liter Patterson mixer with a sigma type blade. The components were mixed together at .about.95.degree. C., and the water level was adjusted to approximately 8-10 wt. %. The batch was covered to prevent moisture loss, and mixed for about 15 minutes. Then the cover was removed and the mixture was allowed to dry. The moisture content of the samples taken at different times during the drying stage was determined by Karl Fisher titration with a turbo titrator. At the final moisture level (.about.5%), the formulation was dropped onto a heated applicator roll and then was chipped over a chill roll. The chill roll chips were plodded under vacuum in a Weber Seelander duplex refiner with screw speed at .about.20 rpm. The nose cone of the plodder was heated to 45.degree.-50.degree. C. The cut billets were stamped into bars using a Weber Seelander L4 hydraulic press with a nylon, pillow-shaped die in place.
Bars were also prepared by a cast-melt process. First, the components were mixed together at 80.degree.-120.degree. C. in a 500 ml beaker, and the water level was adjusted to approximately 10-15 wt. %. The batch was covered to prevent moisture loss and was mixed for about 15 minutes. Then the cover was removed, and the mixture was allowed to dry. The moisture content of the samples taken at different times during the drying stage and was determined by Karl Fisher titration with a turbo titrator. At the final moisture level (.about.5%), the mixture in the beaker (in the form of a free-flow liquid) was dropped into bar-molds and was allowed to be cooled at room temperature for four hours. Upon solidification, the mixture was casted in the bar mold into a bar.
Example 1
Components as listed in Table 2 below were melted together at 80.degree. C.-120.degree. C. to produce a material consisting predominantly of a liquid phase. All amounts are provided in percentage by weight. On cooling to 10.degree. C.-50.degree. C. by a chill-roll, the formulations formed plastic-like solids that were plodded using the extrusion equipment described above (i.e., formulation processing section) and pressed into bars using the single bar press. Identical formulations were also formed into bars by using the casting process from the hot melt. These bars contain a major DEFI active and an optional cocoamidopropyl betaine coactive. These bars provided rich, creamy and slippery lather; the skin-feel of the bars were found to be smooth and non-tacky.
TABLE 2______________________________________Formulation A B C D______________________________________Sodium acyl isethionate 27.8% 27.0% 27.0% 27.8%(from DEFI*)Cocoamidopropyl 5.2 5.0 5.0 5.2betainePEG 8000** 32.1 29.5 35.0 45.1PEG 4000*** 3.1 0.0 0.0 0Stearic-palmitic acid 11.6 8.6 9.0 11.6Maltodextrin 10.3 10.0 0.0 4.4Pluronic F88 4.0 5 10 0.0Tetronic 1107 0 5 0 0Perfume 0 0.3 0.3 0Sodium Stearate 0 0 5.0 0Titanium Dioxide 0 0 0.5 0EHDP 0 0.1 0.1 0EDTA 0 0.1 0.1 0Misc. Salts 0 2.9 2.9 0Water 5.9 6.5 5.1 5.9______________________________________ *DEFI: directly esterified fatty acid isethionate, which is a mixture containing about 74% by weight of fatty acyl isethionate, 23% stearicpalmitic acid and small amounts of other materials, manufactured b Lever Brothers Co., U.S. **PEG 8000: polyoxyethylene glycol with mean molecular weigh at 8000; PEG 4000: polyoxyethylene glycol with mean molecular weight at 4000.
Example 2
Components as listed in Table 3 below were preferably processed using a cast-melt approach described in the methodology section. All amounts are given in percentage of weight. These bars used sodium lauryl sarcosinate (formulation E, G) and sodium lauryl sulphate (formulation F) as the major anionic detergent with optional cocoamidopropyl betaine as a coactive. These bars provided rich, creamy and slippery lather and smooth skin feel.
TABLE 3______________________________________Formulation (E) (F) (G)______________________________________Sodium Lauryl Sarcosinate 15 0.0 27.0Cocoamidopropyl Betaine 5.0 5.0 5.0SLES (3EO) 5.0 20.0 0.0Stearic-palmitic Acid 5.0 5.0 5.0PEG 8000 25.0 44.0 39.0PEG 6000 27.0 8.0 5.0Pluronic F88 10.0 10.0 10.0Paraffin Wax 2.0 2.0 3.0Perfumes 1.0 1.0 1.0Water 5.0 5.0 5.0______________________________________
Example 3
The irritation reduction potential of Pluronics was investigated using Zein dissolution experiments. As indicated in Tables 4 and 5, Pluronic surfactants, as a class, are significantly more effective than PEG in reducing the Zein % dissolved by a 1% aqueous DEFI suspension (DEFI is a sodium acyl isethionate/fatty acid mixture defined in the Table 2 of Example 1). The data in Tables 4 and 5 also showed that EO terminated Pluronic F127 is potentially a better mildness enhancer than the PO-terminated Pluronic 25R8. Table 6 showed that EO-PO can significantly reduce the Zein % dissolved by even a quite mild detergency system (DEFI/cocoamidopropyl betaine): Tables 4, 5 and 6 are set forth below.
TABLE 4______________________________________Component % Zein Dissolved______________________________________1% DEFI 23.91% DEFI + 0.8% PLU.F127* 17.8Water 9.0______________________________________
TABLE 5______________________________________Component % Zein Dissolved______________________________________PEG 8K 20.85% PLU.25R8** 8.95% PLU.F127* 4.1______________________________________
TABLE 6***______________________________________Component % Zein Dissolved______________________________________5% PEG 17.45% PLU.F127 3.6______________________________________ *Structure of PLU F127 is EO.sub.98 PO.sub.67 EO.sub.98 **Structure of PLU 25R8 is PO.sub.21 EO.sub.227 PO.sub.21 ***Components tested in mild system comprising 1% DEFI/0.8% cocoamidopropyl betaine
Example 4
Three day skin patch tests showed that Pluronic F88 significantly reduced the skin irritation caused by DEFI, even at low levels of addition. As shown in FIG. 2, at a Sodium acyl isethionate (SAI) Pluronic F88 weight ratio around 1:0.37 (equivalent to 10% EO-PO in the bar of Formulation (B) or (C) in Table 2 of Example 1), Pluronic F88 reduced the skin irritation of a DEFI/betaine liquor significantly. In contrast, even at SAI/PEG 8000 weight ratio as low as 1:1.67 (effectively 45% PEG 8000 in the bar of formulation D, Table 2) PEG 8000 made no measurable mildness contribution to the SAI/CAP betaine aqueous liquor.
Example 5
Zein dissolution experiments (Table 7 below) revealed that Pluronic F88 can significantly reduce the amount of Zein dissolved by many different types of anionic surfactants commonly used in personal washing products. Thus inclusion of EO-POs in the bar formulations containing the anionic surfactants listed in Table 7 can effectively enhance the mildness of the bars.
TABLE 7______________________________________ Zein % DissolvedFormulation (in distilled water) (w/w)Anionic Surfactant Pluronic F88 (Standard dev. 2%)______________________________________1% Sodium Lauryl Sarcosinate 0.73% 37.1%1% Sodium Lauryl Sarcosinate 0 43.81% SLES (3EO) 0.73% 28.61% SLES (3EO) 0 35.81% Sodium Lauryl Sulfate 0.73% 59.01% Sodium Lauryl Sulfate 0 66.91% Sodium Soap (82:18 0.73% 49.7Tallowate/Cocoate)1% Sodium Soap 0 59.71% Sodium Lauryl Isethionate 0.73% 38.51% Sodium Lauryl Isethionate 0 46.5______________________________________
Claims
- 1. A bar composition comprising
- (a) 10% to 70% by weight of total composition of a surfactant system selected from the group consisting of anionic surfactants, nonionic surfactants other than the nonionic polymer surfactant of item (c) below, cationic surfactants, amphoteric surfactants and mixtures thereof, wherein the anionic surfactant comprises 50% or greater of the surfactant system, and wherein anionic comprises no more than about 40% by wt. of the total composition.
- (b) 20% to 85% by wt. of the composition of a bar structurant selected from the group consisting of alkylene oxide components having a molecular weight of from about 2,000 to about 25,000; and C.sub.8 -C.sub.22 free fatty acids; C.sub.2 to C.sub.20 alkanols, paraffin waxes; water-soluble starches; and
- (c) 3% to 10% by wt. total composition of a polyoxyethylene polyoxypropylene nonionic polymer surfactant (EO-PO polymer) wherein ratio by weight total composition of anionic surfactant to EO-PO polymer is between 2.5:1 to 10:1.
- 2. A composition according to claim 1 wherein surfactant system comprises anionic, amphoteric or mixtures thereof.
- 3. A composition according to claim 1, wherein surfactant comprises acyl isethionate and betaine.
- 4. A composition according to claim 1, wherein structurant (b) comprises 30% to 70% of the bar.
- 5. A composition according to claim 1, wherein molecular wt. of structurant (b) is 3,000 to 10,000.
- 6. A composition according to claim 1, wherein melting temperature of (c) is 25.degree. C to 85.degree. C.
- 7. A composition according to claim 1, additionally comprising a polyol.
- 8. A composition according to claim 7, wherein said polyol is selected from the group consisting of ethylene glycol, propylene glycol, glycerol and mixtures thereof.
US Referenced Citations (4)
Foreign Referenced Citations (1)
Number |
Date |
Country |
9530737 |
Nov 1995 |
WOX |