The present application claims priority to Chinese patent application No. CN201610910232.X, filed on Oct. 19, 2016, which is incorporated herein by reference in its entirety.
The present disclosure relates to the field of battery, and particularly relates to a battery module.
In existing structure of a battery module, a side plate has a composite structure consisting of aluminum alloy and an insulating membrane, adjacent mono-batteries directly contact with each other or space apart from each other via a compact plate (such as rubber pad, insulating plastic). When one mono-battery suffers thermal runaway, a temperature of the one mono-battery even reaches 500° C., at this time, heat generated by the one mono-battery may be massively transferred to mono-batteries adjacent to the one mono-battery respectively via adjacent compact plates and the side plate of metal (such as aluminum alloy), therefore the mono-batteries adjacent to the one mono-battery are also runaway. However, using an aerogel blanket to space apart the adjacent mono-batteries will cost too much.
In view of the problems existing in the background of the present disclosure, an object of the present disclosure is to provide a battery module, in which a through-hole of each isolating plate can form air thermal resistance, thereby preventing heat generated by one runaway mono-battery from massively and quickly transferring to large surfaces of mono-batteries adjacent to the runaway mono-battery, so as to achieve the purpose of thermal isolation.
In order to achieve the above object, the present disclosure provides a battery module, which comprises: a plurality of mono-batteries arranged along an arrangement direction; and a frame receiving and fixing the plurality of mono-batteries. The battery module further comprises a plurality of isolating plates, each isolating plate is interposed between two adjacent mono-batteries, each isolating plate is provided with a through hole penetrating along the arrangement direction. Each isolating plate is configured to be capable of self-foaming to make a volume of each isolating plate expanded when each isolating plate is heated and a temperature of each isolating plate is more than 200° C.
Compared to the prior art, the present disclosure has following beneficial effects: in the battery module of the present disclosure, the through-hole of each isolating plate can form air thermal resistance, because air has a low thermal conductivity, therefore the isolating plate of the present disclosure can prevent heat generated by the runaway mono-battery from massively and quickly transferring to the large surfaces of the adjacent mono-batteries, so as to achieve the purpose of thermal isolation. At the same time, when the temperature rises and the temperature of each isolating plate is more than 200° C., each isolating plate can self-foam so as to develop pores in the inside of each isolating plate, meanwhile, the volume of each isolating plate is expanded, thereby further increasing the air thermal resistance, preventing heat generated by the runaway mono-battery from transferring to the large surfaces of the adjacent mono-batteries, and avoiding the battery module from being runaway.
The battery module of the present disclosure is especially suitable for application in a power battery and an energy storage battery.
The reference numerals are as follows:
Hereinafter a battery module according to the present disclosure will be described in detail.
Referring to
Each isolating plate 3 won't self-foam under normal use (the temperature of each isolating plate 3 is not more than 200° C.), structural integrity of each isolating plate 3 is maintained and an interval between the two adjacent mono-batteries 1 is maintained. When one mono-battery 1 is runaway and the temperature rises, because air has a low thermal conductivity, the through hole of the isolating plate 3 can form air thermal resistance, thereby preventing heat generated by the runaway mono-battery 1 from massively and quickly transferring to large surfaces of the mono-batteries 1 adjacent to the runaway mono-battery 1, so as to achieve the purpose of thermal isolation. At the same time, when the temperature rises and the temperature of each isolating plate 3 is more than 200° C., each isolating plate 3 can self-foam so as to develop pores in the inside of each isolating plate 3, meanwhile, the volume of each isolating plate 3 is expanded, thereby increasing the interval between the two adjacent mono-batteries 1, further increasing the air thermal resistance, preventing heat generated by the runaway mono-battery 1 from transferring to the large surfaces of the mono-batteries 1 adjacent to the runaway mono-battery 1, and avoiding the battery module from being runaway.
In the battery module according to the present disclosure, a main component of each isolating plate 3 is thermosetting resin which is capable of self-foaming to make a volume thereof expanded when heated. It should be noted that, “a main component of the isolating plate 3” means that in all components of the isolating plate 3, besides the thermosetting resin which is capable of self-foaming to make the volume thereof expanded when heated is included, other materials, for example conventional resin, polymer, inorganic filler and the like, can also be included. Of course, the isolating plate 3 may also only be consisted of the thermosetting resin which is capable of self-foaming to make the volume thereof expanded when heated.
In the battery module according to the present disclosure, the thermosetting resin is one selected from a group consisting of bisphenol-A cyanate ester resin (BCE), complex cyanate ester resin of phenol novolac cyanate ester and bisphenol-A cyanate ester and allyl compound modified bismaleimide resin.
In the battery module according to the present disclosure, the allyl compound may be allylphenol. Preferably, the allyl compound may be 2,2′-diallylbisphenol A (DABPA).
In the battery module according to the present disclosure, a compressive strength of each isolating plate 3 is larger than an expansion pressure of the mono-battery 1 adjacent to each isolating plate 3.
In the battery module according to the present disclosure, the compressive strength of each isolating plate 3 is 20 MPa-150 Mpa. When the compressive strength of each isolating plate 3 is 20 MPa-150 MPa, even if the mono-battery 1 adjacent to each isolating plate 3 is expanded, each isolating plate 3 won't be compressed, therefore the interval between the two adjacent mono-batteries 1 won't be decreased. Preferably, the compressive strength of each isolating plate 3 is 50 MPa-150 Mpa.
In the battery module according to the present disclosure, the through hole may be provided as one or multiple in number. Preferably, the through hole is provided as multiple in number.
In the battery module according to the present disclosure, a shape of the through hole is not limited. Preferably, the shape of the through hole is circular or rectangular.
In the battery module according to the present disclosure, a total plane area of the through hole in each isolating plate 3 is 30%-80% of a total plane area of each isolating plate 3. The proportion of the total plane area of the through hole in each isolating plate 3 is larger, heat transfer effect of each isolating plate 3 is worse, thermal isolation effect of each isolating plate 3 is better, but structural strength of each isolating plate 3 is also worse. Preferably, the total plane area of the through hole in each isolating plate 3 is 60%-70% of the total plane area of each isolating plate 3. It should be noted that, “a total plane area of each isolating plate 3” refers to the total plane area of each isolating plate 3 before the through hole is provided.
In the battery module according to the present disclosure, a thickness of each isolating plate 3 is 0.5 mm-5 mm. Preferably, the thickness of each isolating plate 3 is 2 mm.
In the battery module according to the present disclosure, each isolating plate 3 is the same as a large surface of the mono-battery 1 in both length and width.
In the battery module according to the present disclosure, when the battery module is under normal use, due to restriction of inherent characteristics of a material of each isolating plate 3, a porosity in the inside of each isolating plate 3 is close to 0, and generally is not more than 5%. When each isolating plate 3 is heated and the temperature of each isolating plate 3 is more than 200° C. and each isolating plate 3 has been self-foamed, the porosity in the inside of each isolating plate 3 is 10%-90%. It should be noted that, “a porosity in the inside of each isolating plate 3” refers to the porosity in the inside of a solid portion (that is a portion of each isolating plate 3 except the through hole) of each self-foamed isolating plate 3.
In the battery module according to the present disclosure, referring to
In the battery module according to the present disclosure, the two side plates 22 each are a L-type side plate. Referring to
In the battery module according to the present disclosure, sum of contact areas between the two horizontal portions 221 of the two L-type side plates and the bottom portion of each mono-battery 1 is 5%-95% of the area of the bottom portion of each mono-battery 1. Preferably, sum of contact areas between the two horizontal portions 221 of the two L-type side plates and the bottom portion of each mono-battery 1 is 40% of the area of the bottom portion of each mono-battery 1.
In the battery module according to the present disclosure, the two vertical portions 220 of the two side plates 22 and the two end plates 21 are fixed together via bolts S and/or a structural adhesive.
In the battery module according to the present disclosure, the vertical portion 220 of each side plate 22 is provided with a plurality of mounting holes 222; each end plate 21 is provided with a plurality of threaded holes 211 corresponding to positions of the plurality of mounting holes 222 of the two vertical portions 220 of the two side plates 22; each bolt S passes through the corresponding mounting hole 222 and is screwed into the corresponding threaded hole 211, therefore the two vertical portions 220 of the two side plates 22 and the two end plates 21 are fixed together. Referring to
In the battery module according to the present disclosure, a distance from the mounting hole 222 to a corresponding side edge of the side plate 22 is not less than 4 mm. Preferably, the distance from the mounting hole 222 to the corresponding side edge of the side plate 22 is 5 mm-10 mm.
In the battery module according to the present disclosure, a thread depth of the threaded hole 211 is 3 mm-30 mm. Preferably, the thread depth of the threaded hole 211 is 5 mm-10 mm.
In the battery module according to the present disclosure, the structural adhesive is one or more selected from a group consisting of epoxy resin, acrylic acid and polyurethane. Preferably, the structural adhesive is acrylic acid.
In the battery module according to the present disclosure, a coating thickness of the structural adhesive is 0.2 mm-2 mm. Preferably, the coating thickness of the structural adhesive is 0.5 mm.
In the battery module according to the present disclosure, a thickness of each side plate 22 is 1 mm-5 mm. Preferably, the thickness of each side plate 22 is 2 mm.
In the battery module according to the present disclosure, a material of each of the two side plates 22 is fiber-reinforced thermosetting resin.
In the battery module according to the present disclosure, in the fiber-reinforced thermosetting resin, the fiber is one or more selected from a group consisting of glass fiber, carbon fiber, ceramic fiber and Kevlar fiber. Preferably, the fiber is glass fiber.
In the battery module according to the present disclosure, in the fiber-reinforced thermosetting resin, the fiber is one or more selected from a group consisting of chopped fiber, fibrous mat and fibrous fabric. Preferably, the fiber is fibrous fabric.
In the battery module according to the present disclosure, in the fiber-reinforced thermosetting resin, the thermosetting resin is one or more selected from a group consisting of cyanate ester resin, epoxy resin, epoxy vinyl ester resin and unsaturated polyester resin. Preferably, the thermosetting resin is epoxy vinyl ester resin.
In the battery module according to the present disclosure, a thermal conductivity of the fiber-reinforced thermosetting resin is not more than 0.5 W/(mK).
In the battery module according to the present disclosure, referring to
Length×width×thickness of each mono-battery was 150 mm×100 mm×2 mm, a nominal capacity of each mono-battery was 42 Ah, positive materials of each mono-battery were NCM, then the three mono-batteries were assembled as a 1P3S battery module, each isolating plate was made from allyl compound modified bismaleimide resin, and each isolating plate was provided with a plurality of penetrating through holes, a total plane area of the through holes in each isolating plate was 30% of a total plane area of each isolating plate. Nail penetration test was conducted on the battery module until a puncturing depth of the nail in the first mono-battery was 50% of a thickness of the first mono-battery.
The highest temperature of the first mono-battery was 500° C.
The explosion-proof vent of the second mono-battery was not opened, the voltage remained stable, and the highest temperature was not more than 249.6° C.
The highest temperature of the third mono-battery was not more than 60° C.
Length×width×thickness of each mono-battery was 150 mm×100 mm×2 mm, a nominal capacity of each mono-battery was 42 Ah, positive materials of each mono-battery were NCM, then the three mono-batteries were assembled as a 1P3S battery module, each isolating plate was a compact plate made from silicone rubber (each isolating plate was not provided with the through hole penetrating along the up-down direction). Nail penetration test was conducted on the battery module until a puncturing depth of the nail in the first mono-battery was 50% of a thickness of the first mono-battery.
The highest temperature of the first mono-battery was 550° C.
The explosion-proof vent of the second mono-battery was opened after 11 min, then the voltage was down to 0 V, and the highest temperature was 580.5° C.
The explosion-proof vent of the third mono-battery was opened after 22 min, then the voltage was down to 0 V, the highest temperature was 600.2° C.
Length×width×thickness of each mono-battery was 150 mm×100 mm×2 mm, a nominal capacity of each mono-battery was 42 Ah, positive materials of each mono-battery were NCM, then the three mono-batteries were assembled as a 1P3S battery module, each isolating plate was a compact plate made from allyl compound modified bismaleimide resin (each isolating plate was not provided with the through hole penetrating along the up-down direction). Nail penetration test was conducted on the battery module until a puncturing depth of the nail in the first mono-battery was 50% of a thickness of the first mono-battery.
The highest temperature of the first mono-battery was 542.3° C.
The explosion-proof vent of the second mono-battery was opened after 19 min, then the voltage was down to 0 V, and the highest temperature was 561.1° C.
The explosion-proof vent of the third mono-battery was opened after 37 min, the voltage was down to 0 V, the highest temperature was 564.5° C.